CN102922839B - Eva多功能复合棚膜 - Google Patents
Eva多功能复合棚膜 Download PDFInfo
- Publication number
- CN102922839B CN102922839B CN201210478570.2A CN201210478570A CN102922839B CN 102922839 B CN102922839 B CN 102922839B CN 201210478570 A CN201210478570 A CN 201210478570A CN 102922839 B CN102922839 B CN 102922839B
- Authority
- CN
- China
- Prior art keywords
- parts
- film
- plastic film
- layer film
- shed plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种农用棚膜及其制备方法,具体涉及一种EVA多功能复合棚膜,所述的EVA多功能复合棚膜,由内层、中层和外层三层薄膜复合而成,本发明采用母料法生产,在原有设备、工艺工序保持不变的情况下,按照配方中各层的组分配比单独混合,首先将少量的树脂粉料和各种助剂混合均匀,经螺杆挤出机制得各种功能性母料,该功能性母料为粒料,然后功能性母料再与剩余的树脂粒料混合均匀,最后经三层共挤吹塑薄膜机组按照厚度1:1:1挤出而成。由于棚膜中采用的树脂原料主要是高VA含量的EVA树脂,所以与其他功能性棚膜相比较透明度更高,透光性、保温性、和耐低温性显著提高,流滴和消雾的持效期以及使用寿命明显延长。
Description
技术领域
本发明涉及一种农用棚膜及其制备方法,具体涉及一种EVA多功能复合棚膜。
背景技术
塑料棚膜在我国农业生产中已被广泛应用,其在农田使用上所取得的保温保湿增产效果,已得到业界和农户的公认。目前广泛使用的农用塑料棚膜的基体树脂主要有PVC、PE、EVA,PVC虽然透明度高,耐寒性好,但密度高,同等重量的膜覆盖面积小;PE膜虽然密度小,但相比透明性和耐低温性能差一些,另外保温性和与助剂的相容性也比较差;而EVA膜兼有前两者的优点却没有二者的缺点,因此是比较理想的生产农用棚膜的基体树脂原料。用此树脂生产的高性能EVA多功能复合棚膜不仅具有良好的橡胶般的柔软性和弹性,在零下四五十度时仍具有较好的可挠性,透光性和表面光泽性好,化学稳定性好,耐老化和抗氧性好,环境友好性高,与功能性助剂的相容性和掺混性好,着色和成型加工性好。因此,特别适合高端棚膜对高透明度、高保温、超耐寒、大幅度提高流滴消雾持久性的要求。
发明内容
本发明的目的是提供一种EVA多功能复合棚膜,能够具有高透明度、高保温、超耐寒、大幅度提高流滴消雾持久性的优点。
本发明所述的EVA多功能复合棚膜,由内层、中层和外层三层薄膜复合而成,其中,内层、中层和外层薄膜分别由以下重量份数的原料制成:
内层:
EVA 100份 光稳定剂 1.15~1.3份
抗氧剂 0.3~0.4份 流滴剂 4.15~4.85份
消雾剂 0.21~0.31份
中层:
EVA 100份 光稳定剂 1.15~1.3份
抗氧剂 0.3~0.4份 流滴剂 4.15~4.85份
消雾剂 0.21~0.31份
外层:
LLDPE 100份 LDPE 55~65份
mLLDPE 55~65份 光稳定剂 1.05~1.2份
抗氧剂 0.3~0.4份 流滴剂 2.0~2.3份
其中,EVA的VA质量含量≥6%。
本发明中EVA、LLDPE、LDPE和mLLDPE均为聚烯烃类树脂,光稳定剂、抗氧剂、流滴剂和消雾剂均起到助剂的作用。
所述的光稳定剂优选用光稳定剂783,抗氧剂优选用抗氧剂B215。
本发明所使用的流滴剂和消雾剂均选用添加型,市售的流滴剂和消雾剂均可使用。
本发明采用母料法生产,在原有设备、工艺工序保持不变的情况下,按照配方中各层的组分配比单独混合,首先将少量的树脂粉料和各种助剂混合均匀,经螺杆挤出机制得各种功能性母料,该功能性母料为粒料,然后功能性母料再与剩余的树脂粒料混合均匀,最后经三层共挤吹塑薄膜机组按照厚度1:1:1挤出而成。
本发明的优点在于:由于棚膜中采用的树脂原料主要是高VA含量的EVA树脂,所以与其他功能性棚膜相比较透明度更高,透光性、保温性、和耐低温性显著提高,流滴和消雾的持效期以及使用寿命明显延长;且生产中不用额外增加生产设备,通过科学合理的配方设计即能达到棚膜使用的各种高功能性要求。
具体实施方式
以下结合实施例对本发明做进一步说明。
实施例1
本发明所述的多功能复合棚膜,由内层、中层和外层三层薄膜经挤出吹塑工艺复合而成,其中,内层、中层和外层薄膜分别由以下重量份数的原料制成:
内层:
EVA(VA=9%)100份 光稳定剂783 1.16份
抗氧剂B215 0.32份 流滴剂La12b 4.30份
消雾剂TS403 0.21份
中层:
EVA(VA=14%)100份 光稳定剂783 1.16份
抗氧剂B215 0.32份 流滴剂La12b 4.30份
消雾剂TS403 0.21份
外层:
LLDPE 100份 LDPE 57.11份
mLLDPE 58.42份 光稳定剂783 1.08份
抗氧剂B215 0.30份 流滴剂La12b 2.10份。
本例产品主要性能指标:
拉伸强度(MPa):28.5(纵向)、28.1(横向);断裂伸长率(%):633.1(纵向)、779.2(横向);直角撕裂强度(KN/m):118.9(纵向)、112.1(横向);透光率(%):90.4;雾度(%):11.72;初滴时间(s):285;流滴失效时间(d):12。
实施例2
本发明所述的多功能复合棚膜,由内层、中层和外层三层薄膜挤出吹塑复合工艺而成,其中,内层、中层和外层薄膜分别由以下重量份数的原料制成:
内层:
EVA(VA=9%)100份 光稳定剂783 1.16份
抗氧剂B215 0.32份 流滴剂KF650 4.45份
消雾剂AF-38 0.31份
中层:
EVA(VA=14%)100份 光稳定剂783 1.18份
抗氧剂B215 0.33份 流滴剂KF650 4.45份
消雾剂AF-38 0.31份
外层:
LLDPE 100份 LDPE 57.11份
mLLDPE 58.42份 光稳定剂783 1.08份
抗氧剂B215 0.30份 流滴剂KF650 2.20份。
本例产品主要性能指标:
拉伸强度(MPa):29.5(纵向)、28.6(横向);断裂伸长率(%):624.1(纵向)、749.3(横向);直角撕裂强度(KN/m):118.8(纵向)、110.9(横向);透光率(%):90.5;雾度(%):9.75;初滴时间(s):185;流滴失效时间(d):12。
实施例3
本发明所述的多功能复合棚膜,由内层、中层和外层三层薄膜挤出吹塑工艺复合而成,其中,内层、中层和外层薄膜分别由以下重量份数的原料制成:
内层:
EVA(VA=9%)100份 光稳定剂783 1.2份
抗氧剂B215 0.33份 流滴剂La12b 4.50份
消雾剂AF-38 0.31份
中层:
EVA(VA=14%)100份 光稳定剂783 1.15份
抗氧剂B215 0.3份 流滴剂La12b 4.50份
消雾剂AF-38 0.31份
外层:
LLDPE 100份 LDPE 57.11份
mLLDPE 58.42份 光稳定剂783 1.10份
抗氧剂B215 0.32份 流滴剂La12b 2.1份。
本例产品主要性能指标:
拉伸强度(MPa):30.8(纵向)、29.4(横向);断裂伸长率(%):657.1(纵向)、743.2(横向);直角撕裂强度(KN/m):102.0(纵向)、109.0(横向);透光率(%):90.9;雾度(%):11.52;初滴时间(s):243;流滴失效时间(d):12。
Claims (1)
1.一种EVA多功能复合棚膜,其特征在于由EVA树脂为主的内层、中层和外层三层薄膜复合而成,其中,内层、中层和外层薄膜分别由以下重量份数的原料制成:
内层:
EVA 100份 光稳定剂 1.15~1.3份
抗氧剂 0.3~0.4份 流滴剂 4.15~4.85份
消雾剂 0.21~0.31份
中层:
EVA 100份 光稳定剂 1.15~1.3份
抗氧剂 0.3~0.4份 流滴剂 4.15~4.85份
消雾剂 0.21~0.31份
外层:
LLDPE 100份 LDPE 55~65份
mLLDPE 55~65份 光稳定剂 1.05~1.2份
抗氧剂 0.3~0.4份 流滴剂 2.0~2.3份
所述的EVA的VA质量含量≥6%;
所述的光稳定剂选用光稳定剂783;
所述的抗氧剂选用抗氧剂B215。