CN103012675A - 大孔弱碱性丙烯酸系阴离子交换树脂的制备方法 - Google Patents
大孔弱碱性丙烯酸系阴离子交换树脂的制备方法 Download PDFInfo
- Publication number
- CN103012675A CN103012675A CN201210489706XA CN201210489706A CN103012675A CN 103012675 A CN103012675 A CN 103012675A CN 201210489706X A CN201210489706X A CN 201210489706XA CN 201210489706 A CN201210489706 A CN 201210489706A CN 103012675 A CN103012675 A CN 103012675A
- Authority
- CN
- China
- Prior art keywords
- water
- exchange resin
- preparation
- warming
- following weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种大孔弱碱性丙烯酸系阴离子交换树脂的制备方法,在传统生产工艺基础上,本发明通过合理搭配悬浮保护剂、分散剂、致孔剂、络合剂,优化工艺参数,使得本方法制备的阴离子交换树脂,孔径分布均匀,交换容量提高的效果,本发明制得的离子交换树脂比表面积能达到60m2/g以上,大于2nm的中孔比例大于50%,全交换容量达到10.5mmol/g。
Description
技术领域
本发明属于一种离子交换树脂的制备方法,具体是一种大孔弱碱性丙烯酸系阴离子交换树脂的制备方法。
背景技术
阴、阳离子交换树脂广泛地用于水处理、物质的净化、浓缩、分离、物质离子组成的转变、物质的脱色以及催化剂等领域。虽然目前的阴、阳离子交换树脂的交换容量得到了有效的提高,但孔径分布不均,小孔比例过大,交换速度低。交换容量不足等问题,满足不了客户的要求。
发明内容
本发明的目的是提供一种大孔弱碱性丙烯酸系阴离子交换树脂的制备方法,本发明通过水相的改进,使得分散性、悬浮性提高,进而达到增加离子交换树脂的交换容量,孔径分布均匀的效果。
本发明的技术方案如下:
大孔弱碱性丙烯酸系阴离子交换树脂的制备方法,其特征在于包括以下步骤:
(1)、聚合反应制备A料
去离子水 320-350
明胶 10-12
古尔胶 5-8
甘油 15-20
羟甲基纤维素 30-35
三乙烯四胺 15-20
硫酸钠 40-45
三聚磷酸钠 20-25
过硫酸钾 1-2
用硫酸调水相PH为中性
丙烯酸甲酯 35-45
二乙烯苯 50-55
TAIC 210-220
丙烯酸甲酯 10-15
二茂铁 8-10
白油 115-125
偶氮二异丁腈 3-5
过氧化苯甲酰 1-2
缓慢升温至62-65℃,注意观察球体粒度及定型情况;
用20-40分钟,升温至82-85℃保温2-3h;
(2)、胺化反应制备B料
A料 380-420
三乙烯四胺 1500-1600
中控合格后,抽母液;
(3)、甲基化制备树指
将B料加入到下列重量份的混合原料中,开动搅拌;
甲酸1180-2200
水 200-240
甲醛 60-65
磺基水杨酸 10-15
本发明通过合理搭配悬浮保护剂、分散剂、致孔剂、络合剂,优化工艺参数,使得本方法制备的阴离子交换树脂,孔径分布不均,交换容量提高的效果,本发明制得的离子交换树脂比表面积能达到60m2/g 以上,大于2nm 的中孔比例大于50%,全交换容量达到10.5mmol/g。
具体实施方式
大孔弱碱性丙烯酸系阴离子交换树脂的制备方法,包括以下步骤:
(1)、聚合反应制备A料
去离子水 320
明胶 10
古尔胶 5
甘油 15
羟甲基纤维素 30
三乙烯四胺 15
硫酸钠 40
三聚磷酸钠 20
过硫酸钾 1
用硫酸调水相PH为中性
丙烯酸甲酯 35
二乙烯苯 50
TAIC 210
丙烯酸甲酯 10
二茂铁 8
白油 115
偶氮二异丁腈 3
过氧化苯甲酰 1
用20-40分钟,升温至82-85℃保温2-3h;
(2)、胺化反应制备B料
A料 380
三乙烯四胺 1500
(3)、甲基化制备树指
甲酸1180
水 200
甲醛 60
磺基水杨酸 10
抽干母液,大量水洗至中性,抽干,出料、干燥即得。
本发明制得的离子交换树脂比表面积能达到60m2/g 以上,大于2nm 的中孔比例大于50%,全交换容量达到10.5mmol/g。
Claims (1)
1.大孔弱碱性丙烯酸系阴离子交换树脂的制备方法,其特征在于包括以下步骤:
(1)、聚合反应制备A料
配好下列重量份水相,混合搅拌均匀;
去离子水 320-350
明胶 10-12
古尔胶 5-8
甘油 15-20
羟甲基纤维素 30-35
三乙烯四胺 15-20
硫酸钠 40-45
三聚磷酸钠 20-25
过硫酸钾 1-2
用硫酸调水相PH为中性
丙烯酸甲酯 35-45
二乙烯苯 50-55
TAIC 210-220
丙烯酸甲酯 10-15
二茂铁 8-10
白油 115-125
偶氮二异丁腈 3-5
过氧化苯甲酰 1-2
抽干水,烘干,分筛制得A料;
(2)、胺化反应制备B料
A料 380-420
三乙烯四胺 1500-1600
升温至130-135℃,保温反应15-18h,测中控交换大于8.5mmol/g合格;
(3)、甲基化制备树指
甲酸1180-2200
水 200-240
甲醛 60-65
磺基水杨酸 10-15
升温至45-50℃,保持30-50分钟;