CN102534848A - Production method of coffee polyester multifunctional fiber - Google Patents
Production method of coffee polyester multifunctional fiber Download PDFInfo
- Publication number
- CN102534848A CN102534848A CN2010106053983A CN201010605398A CN102534848A CN 102534848 A CN102534848 A CN 102534848A CN 2010106053983 A CN2010106053983 A CN 2010106053983A CN 201010605398 A CN201010605398 A CN 201010605398A CN 102534848 A CN102534848 A CN 102534848A
- Authority
- CN
- China
- Prior art keywords
- coffee
- fiber
- polyester
- master batch
- polyester fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a production method of coffee polyester multifunctional fiber. The method comprises the steps of: preparing coffee polyester masterbatch, blending purpose-made coffee polyester masterbatch with polyester chips in weight percentage, and producing coffee fiber by adopting a polyester fiber production process. With good adsorptivity and antibacterial activity, the coffee fiber can be made into towels a beauty function, medical protective clothing, masks, infant protective clothing, pregnant woman protective clothing and stockings, can adsorb odor and bacteria, and has an antitoxic effect.
Description
Technical field
The present invention relates to textile industry, relate in particular to the manufacturing approach of a kind of coffee multifunctional polyester of synthetic fiber production field fiber.
Background technology
Now, " environmental protection ", energy shortage are all being paid close attention in the whole world; Air pollution is serious, have only one when we more and more recognize the earth, and we injures heavyly more to it; Last all can retribution when the mankind on one's body, we begin to do a thing for environmental protection to full capacity.The progress of science and technology has produced great influence for people's life and consumption mode, and " green consumption " that when being particular about comfortable life, has the environmental protection notion concurrently is that the mankind move towards the inevitable of civilization and economic development.Coffee multifunctional polyester fiber is exactly this outstanding representative on the one hand.Coffee multifunctional polyester fiber has moisture absorption, deodorizing, multi-efficiency such as antibiotic.Weaving industry high-technicalization, final purpose are exactly to be human service, promote people's quality of life; When global greenhouse effect temperature warms up, the enterprise of prediction thinking is arranged, smell the business opportunity of paying attention to environmental protection and resource circulation utilization theory for a long time; This is a trend; Also be the following function property textiles most favored by customers of expection, if add the composition of coffee multifunctional polyester fiber, fabric has moisture absorption, deodorizing, antibiotic effect in the fabric; If can be on dress ornament extensively utilization, believe the ripple business opportunity of purchasing on a barter basis.Coffee multifunctional polyester fiber selects to utilize coffee grounds in addition after the micronizing, selects special process to be processed into coffee carbon master batch, design special spinnerets, breaks through drying, spinning and drawing-off key production technology thereof, the multifunctional fibre of exploitation.
Summary of the invention
The object of the present invention is to provide a kind of manufacturing approach of coffee multifunctional polyester fiber.
The present invention at first wants special coffee master batch; Coffee master batch production process is: earlier coffee grounds is dewatered; Be heated in 550 ℃～650 ℃ the temperature and give charing; Be heated to again in 900 ℃～1200 ℃ high temperature and calcine, grind to form 200～500 nanometer grade powders then, be processed into the coffee master batch that is applicable to that polyester fiber is produced through special process again.Special coffee master batch and polyester slice blend are made into the coffee fiber through the polyester fiber production technology.
Coffee fibre manufacturing technique flow process is: with percentage by weight 5%～20% and polyester slice blend, after vacuumize, fusion, spinning machine spinning, reeling, fall to up-coiler through the path barrel obtains as-spun fibre with the coffee master batch.Before this, spin in the process, spinning temperature is 265 ℃～288 ℃, with 275 ℃～280 ℃ be good, spinning speed is 1000～1400 meters/minute.Again through after spin and be about to some barrels of as-spun fibres through the creel boundling, and carry out drawing-off, curl, cut off and make the coffee fiber.Drafting multiple of the present invention is 3.0～3.7 times.
Coffee of the present invention fibre section can be any cross section of known melt spinning, as circle, triangle, trilobal cross, hollow shape, pancake,, L shaped, T shape, W shape, polygon, dog bone shape or the like.Its monofilament fineness was 0.8 dawn～10 dawn.
The present invention has significant good effect:
1. the coffee grounds material has countless holes, and surface area is huge, and adsorption capacity is extremely strong, and adsorbable various organic compounds are like infringement health or pathogenic refuses such as remains of pesticide, heavy metal, various pathogenic bacteria and mycins; Can produce far infrared, can increase the microvascular blood circulation of human body surface, enhance metabolism.
2. the coffee fiber can be made towel, medical protection clothes, mouth mask, baby children and pregnant woman's protective clothing, socks with cosmetology function owing to its good adsorption property, biocidal property, adsorbable foul smell and bacterium, and have anti-toxic action.
3. adopt the coffee grounds material, environmental protection and resources circulation are utilized very big meaning again.
The specific embodiment
Embodiment 1
The production fiber number is the coffee fiber of 1.33 DENIERs (dtex).
Is that 10% ratio is added in the polyester slice with special coffee master batch with percentage by weight, carries out vacuumize, and first constant temperature was 60 ℃ of insulations 1 hour; Be warming up to 80 ℃ of insulations 1 hour again; Be warming up to 100 ℃ of insulations 2 hours, be warming up to 120 ℃ of insulations 2 hours, be warming up to 160 ℃ of insulations 3 hours; Progressively be warming up to 200 ℃ of insulations to obtaining dry crystallization section, dry run generally needs 14 hours.Use existing spinning equipment, i.e. spinning on the LHV451 spinning machine, coiling and molding is an as-spun fibre again; Spinning temperature is 278 ℃, and winding speed is 1050m/min, and as-spun fibre is through boundling; Drawing-off on LHV903 first break draft machine, drafting multiple is 3.5 times, obtains 1.33dtex coffee fiber.
Embodiment 2
The production fiber number is the hollow coffee fiber of 4.44 DENIERs (dtex).
Is that 12% ratio is added in the polyester slice with special coffee master batch with percentage by weight; Carry out vacuumize, first constant temperature is warming up to 100 ℃ of insulations 2 hours again 60 ℃ of insulations 1 hour; Be warming up to 120 ℃ of insulations 2 hours; Be warming up to 160 ℃ of insulations 3 hours, progressively be warming up to 200 ℃ of insulations to obtaining dry crystallization section, dry run generally needs 14 hours.Use existing spinning equipment, i.e. spinning on the LHV451 spinning machine, used spinning spinneret is the hollow spray filament plate; Coiling and molding is an as-spun fibre again, and spinning temperature is 275 ℃, and winding speed is 1050m/min; As-spun fibre is through boundling; Drawing-off on LHV903 first break draft machine, drafting multiple is 3.2 times, obtains 8.89dtex hollow coffee fiber.
Embodiment 3
The production fiber number is the coffee fiber of 6.67 DENIERs (dtex).
Is that 12% ratio is added in the polyester slice with special coffee master batch with percentage by weight; Carry out vacuumize, first constant temperature is warming up to 80 ℃ of insulations 1 hour again 60 ℃ of insulations 1 hour; Be warming up to 120 ℃ of insulations 2 hours; Be warming up to 160 ℃ of insulations 3 hours, progressively be warming up to 200 ℃ of insulations to obtaining dry crystallization section, dry run generally needs 14 hours.Use existing spinning equipment, i.e. spinning on the LHV451 spinning machine, coiling and molding is an as-spun fibre again; Spinning temperature is 272 ℃, and winding speed is 1000m/min, and as-spun fibre is through boundling; Drawing-off on LHV903 first break draft machine, drafting multiple is 3.4 times, obtains 6.67dtex coffee fiber.
The manufacturing approach of a kind of coffee multifunctional polyester fiber of the present invention is not limited to above embodiment.
Claims (3)
1. the manufacturing approach of a coffee multifunctional polyester fiber; It is characterized in that special coffee master batch; Coffee master batch production process is: earlier with the coffee grounds dehydration, be heated in 550 ℃～650 ℃ the temperature and give charing, be heated in 900 ℃～1200 ℃ high temperature again and calcine; Grind to form 200～500 nanometer grade powders then, process the coffee master batch that is applicable to that polyester fiber is produced through certain processes again.
2. the manufacturing approach of a kind of coffee multifunctional polyester fiber according to claim 1 is characterized in that: described special coffee master batch is made into the coffee fiber with percentage by weight and polyester slice blend through the polyester fiber production technology.
3. the manufacturing approach of a kind of coffee multifunctional polyester fiber according to claim 1 is characterized in that: said coffee master batch is with percentage by weight 5%～20% and polyester slice blend.