CN109054663A - Adhesive is used in a kind of processing of palm mattress - Google Patents
Adhesive is used in a kind of processing of palm mattress Download PDFInfo
- Publication number
- CN109054663A CN109054663A CN201810910500.7A CN201810910500A CN109054663A CN 109054663 A CN109054663 A CN 109054663A CN 201810910500 A CN201810910500 A CN 201810910500A CN 109054663 A CN109054663 A CN 109054663A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- palm
- mattress
- polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to mattress processing and manufacturing technologies, disclose a kind of palm mattress processing adhesive, polyethylene-vinyl acetate is modified using modifying agent, it is good to the wetability of palm material, adhesion strength is improved, initial viscosity reaches 16500mpas, compression strength reaches 65MPa, flexibility, heat resistance, resistance to medium is all good, it is indeformable to be resistant to 150 DEG C of high temperature, strong operability, there is fabulous adhesive property to palm mattress, and no poisonous and harmful substance release, degradation recycles better performances, the adhesive comprehensive performance that the present invention efficiently solves the problems, such as that existing palm mattress processing uses is insufficient, intensity effect and environmental-protecting performance are taken into account, improve the development and utilization of mattress adhesive, it can be realized the realistic meaning of the sustainable development and the feature of environmental protection that improve adhesive, It is a kind of technical solution being extremely worth of widely use.
Description
Technical field
The invention belongs to mattress processing and manufacturing technologies, and in particular to adhesive is used in a kind of processing of palm mattress.
Background technique
Mattress be in order to guarantee consumer secure good health and comfortably sleep and use it is a kind of between human body and bed it
Between article, mattress material is various, different materials production mattress different sleeper effects can be brought to people.With material progress
With being constantly progressive for technical matters, the mattress type that modern people use gradually tends to diversification, mainly has: sping mattress, palm fibre
Palmitic acid mattress, latex bed mattress, water bed mattress, pneumatic mattress, magnetic mattress etc..
As to advocate natural cry higher and higher by people, and environmental problem is increasingly paid attention to, staple fibre exists
Occurs a series of problems in preparation process, for example energy consumption is excessively high, and more serious pollution, product cost are caused to environment
It is more expensive, not pro-skin etc..So that natural plant fibre occupies certain market again.Palm fiber mattress is palm mattress, hand
Shredded coconut meat (coconut palm palm fibre) fiber that work braiding can not use also can use binder and be bonded into brown pad.The primary raw material of palm fibre pad has Arenga engleri Beccari
Silk and shredded coconut meat, Arenga engleri Beccari silk are palm-bark rain cape (brown piece) fibers of palm (color is dark brown)；Shredded coconut meat is the fiber in the pericarp of coconut
(color is light yellow).Since the molding of palm mattress is more difficult, natural glue viscosity is not enough to maintain the stabilization of mattress, and shows
Containing harmfulness ingredients such as formaldehyde in somebody's work synthetic adhesive, it is harmful to human health, it is therefore desirable to which a kind of viscosity is good, together
When the dedicated adhesive harmless to environment and human body.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of palm mattress processing adhesive is provided, to palm bed
Pad has fabulous adhesive property, and discharges without poisonous and harmful substance, and degradation recycles better performances.
The present invention is achieved by the following technical solutions:
A kind of palm mattress processing adhesive, is made of following component: polyethylene-vinyl acetate 75- in parts by weight
80 parts, 25-35 parts of methacrylic acid, 25-30 parts of ethyl acetate, 10-12 parts of paraffin, 5-8 parts of filler, 1.5-1.7 parts of graphite powder,
1.0-1.2 parts of modifying agent；The preparation method for modifier the following steps are included: be according to mass ratio by coffee grounds and zeolite powder
The ratio of 4-6:1-2 mixes, and is placed in Muffle furnace, is warming up to 1000-1100 DEG C with 10-12 DEG C/min of speed, heat preservation calcining
3-4 hours, mixed crystal is obtained, is cooled to room temperature the powder for being ground to specification between 150-200 nanometers.
It further describes as to above scheme, is made in parts by weight of following component: polyethylene-vinyl acetate
76-78 parts, 29-31 parts of methacrylic acid, 26-28 parts of ethyl acetate, 11-12 parts of paraffin, 6-7 parts of filler, graphite powder 1.5-1.6
Part, 1.1-1.2 parts of modifying agent.
It is further described as to above scheme, quality shared by vinylacetate in the polyethylene-vinyl acetate
Percentage is 24-26%.
It is further described as to above scheme, the filler is made of following component in parts by weight: lightweight carbon
Sour calcium 18-20 parts, 14-16 parts of talcum powder, 10-12 parts of silica flour, 8-10 parts of zinc oxide, 4-7 parts of titanium dioxide.
It further describes as to above scheme, when the polyethylene-vinyl acetate is heated to molten condition, is added
Modifying agent is blended 2.5-3.5 hours.
The present invention has the advantage that comprehensive in order to solve the adhesive that existing palm mattress processing uses compared with prior art
The insufficient problem of energy, the present invention provides a kind of palm mattress processing adhesives, using modifying agent to polyethylene vinyl acetate
Ester is modified, good to the wetability of palm material, and adhesion strength is improved, and initial viscosity reaches 16500mpas, resistance to compression
Intensity reaches 65MPa, and flexibility, heat resistance, resistance to medium are all good, and it is indeformable to be resistant to 150 DEG C of high temperature, strong operability, to palm
Mattress has fabulous adhesive property, and discharges without poisonous and harmful substance, and degradation recycles better performances, and the present invention effectively solves
Existing palm mattress of having determined processes the problem of the adhesive comprehensive performance deficiency used, has taken into account intensity effect and environmental-protecting performance,
The development and utilization for improving mattress adhesive can be realized the reality meaning of the sustainable development and the feature of environmental protection that improve adhesive
Justice is a kind of technical solution being extremely worth of widely use.
Specific embodiment
To make the purpose of the present invention, technical solution and effect clearer, clear and definite, combined with specific embodiments below to this hair
It is bright to be described further, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, is not used to limit
Technical solution provided by the present invention.
Embodiment 1
A kind of palm mattress processing adhesive, is made of following component: polyethylene-vinyl acetate 75 in parts by weight
Part, 25 parts of methacrylic acid, 25 parts of ethyl acetate, 10 parts of paraffin, 5 parts of filler, 1.5 parts of graphite powder, 1.0 parts of modifying agent；It is described
Preparation method for modifier is placed in horse the following steps are included: by coffee grounds and zeolite powder according to the ratio mixing that mass ratio is 4:1
Not in furnace, 1000 DEG C are warming up to 10 DEG C/min of speed, heat preservation calcining 3 hours obtains mixed crystal, is cooled to room temperature and grinds
It is milled to powder of the specification between 150-200 nanometers.
It further describes as to above scheme, is made in parts by weight of following component: polyethylene-vinyl acetate 76
Part, 29 parts of methacrylic acid, 26 parts of ethyl acetate, 11 parts of paraffin, 6 parts of filler, 1.5 parts of graphite powder, 1.1 parts of modifying agent.
It is further described as to above scheme, quality shared by vinylacetate in the polyethylene-vinyl acetate
Percentage is 24%.
It is further described as to above scheme, the filler is made of following component in parts by weight: lightweight carbon
18 parts of sour calcium, 14 parts of talcum powder, 10 parts of silica flour, 8 parts of zinc oxide, 4 parts of titanium dioxide.
It further describes as to above scheme, when the polyethylene-vinyl acetate is heated to molten condition, is added
Modifying agent is blended 2.5 hours.
Embodiment 2
A kind of palm mattress processing adhesive, is made of following component: polyethylene-vinyl acetate 78 in parts by weight
Part, 30 parts of methacrylic acid, 28 parts of ethyl acetate, 11 parts of paraffin, 6 parts of filler, 1.6 parts of graphite powder, 1.1 parts of modifying agent；It is described
Preparation method for modifier is placed in the following steps are included: by coffee grounds and zeolite powder according to the ratio mixing that mass ratio is 5:1.5
In Muffle furnace, 1050 DEG C are warming up to 11 DEG C/min of speed, heat preservation calcining 3.5 hours obtains mixed crystal, is cooled to often
Temperature is ground to powder of the specification between 150-200 nanometers.
It further describes as to above scheme, is made in parts by weight of following component: polyethylene-vinyl acetate 77
Part, 30 parts of methacrylic acid, 27 parts of ethyl acetate, 11.5 parts of paraffin, 6.5 parts of filler, 1.55 parts of graphite powder, modifying agent 1.15
Part.
It is further described as to above scheme, quality shared by vinylacetate in the polyethylene-vinyl acetate
Percentage is 25%.
It is further described as to above scheme, the filler is made of following component in parts by weight: lightweight carbon
19 parts of sour calcium, 15 parts of talcum powder, 11 parts of silica flour, 9 parts of zinc oxide, 5.5 parts of titanium dioxide.
It further describes as to above scheme, when the polyethylene-vinyl acetate is heated to molten condition, is added
Modifying agent is blended 3.0 hours.
Embodiment 3
A kind of palm mattress processing adhesive, is made of following component: polyethylene-vinyl acetate 80 in parts by weight
Part, 35 parts of methacrylic acid, 30 parts of ethyl acetate, 12 parts of paraffin, 8 parts of filler, 1.7 parts of graphite powder, 1.2 parts of modifying agent；It is described
Preparation method for modifier is placed in horse the following steps are included: by coffee grounds and zeolite powder according to the ratio mixing that mass ratio is 6:2
Not in furnace, 1100 DEG C are warming up to 12 DEG C/min of speed, heat preservation calcining 4 hours obtains mixed crystal, is cooled to room temperature and grinds
It is milled to powder of the specification between 150-200 nanometers.
It further describes as to above scheme, is made in parts by weight of following component: polyethylene-vinyl acetate 78
Part, 31 parts of methacrylic acid, 28 parts of ethyl acetate, 12 parts of paraffin, 7 parts of filler, 1.6 parts of graphite powder, 1.2 parts of modifying agent.
It is further described as to above scheme, quality shared by vinylacetate in the polyethylene-vinyl acetate
Percentage is 26%.
It is further described as to above scheme, the filler is made of following component in parts by weight: lightweight carbon
20 parts of sour calcium, 16 parts of talcum powder, 12 parts of silica flour, 10 parts of zinc oxide, 7 parts of titanium dioxide.
It further describes as to above scheme, when the polyethylene-vinyl acetate is heated to molten condition, is added
Modifying agent is blended 3.5 hours.
Claims (5)
1. a kind of palm mattress processing adhesive, which is characterized in that be made in parts by weight of following component: polyethylene-
75-80 parts of vinylacetate, 25-35 parts of methacrylic acid, 25-30 parts of ethyl acetate, 10-12 parts of paraffin, 5-8 parts of filler, stone
1.5-1.7 parts of ink powder, 1.0-1.2 parts of modifying agent；The preparation method for modifier is the following steps are included: by coffee grounds and zeolite
Powder is mixed according to the ratio that mass ratio is 4-6:1-2, is placed in Muffle furnace, is warming up to 1000- with 10-12 DEG C/min of speed
1100 DEG C, heat preservation calcining 3-4 hours obtains mixed crystal, is cooled to room temperature the powder for being ground to specification between 150-200 nanometers
Body.
2. a kind of palm mattress processing adhesive, which is characterized in that be made in parts by weight of following component: polyethylene-
76-78 parts of vinylacetate, 29-31 parts of methacrylic acid, 26-28 parts of ethyl acetate, 11-12 parts of paraffin, 6-7 parts of filler, stone
1.5-1.6 parts of ink powder, 1.1-1.2 parts of modifying agent.
3. a kind of palm mattress processing adhesive as described in claim 1, which is characterized in that the polyethylene vinyl acetate
Mass percent shared by vinylacetate is 24-26% in ester.
4. a kind of palm mattress processing adhesive as described in claim 1, which is characterized in that the filler is in parts by weight
It is made of following component: 18-20 parts of precipitated calcium carbonate, 14-16 parts of talcum powder, 10-12 parts of silica flour, 8-10 parts of zinc oxide, titanium
4-7 parts of white powder.
5. a kind of palm mattress processing adhesive as described in claim 1, which is characterized in that the polyethylene vinyl acetate
When ester is heated to molten condition, modifying agent is added, is blended 2.5-3.5 hours.