CN102534848A - 一种咖啡聚酯多功能纤维的制造方法 - Google Patents

一种咖啡聚酯多功能纤维的制造方法 Download PDF

Info

Publication number
CN102534848A
CN102534848A CN2010106053983A CN201010605398A CN102534848A CN 102534848 A CN102534848 A CN 102534848A CN 2010106053983 A CN2010106053983 A CN 2010106053983A CN 201010605398 A CN201010605398 A CN 201010605398A CN 102534848 A CN102534848 A CN 102534848A
Authority
CN
China
Prior art keywords
coffee
fiber
polyester
master batch
polyester fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010106053983A
Other languages
English (en)
Other versions
CN102534848B (zh
Inventor
杨卫忠
闫吉付
冯忠耀
王企章
杨成
朱亚宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai defulun New Material Technology Co.,Ltd.
Original Assignee
SHANGHAI DEFULUN CHEMICAL FIBER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI DEFULUN CHEMICAL FIBER CO Ltd filed Critical SHANGHAI DEFULUN CHEMICAL FIBER CO Ltd
Priority to CN201010605398.3A priority Critical patent/CN102534848B/zh
Publication of CN102534848A publication Critical patent/CN102534848A/zh
Application granted granted Critical
Publication of CN102534848B publication Critical patent/CN102534848B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种咖啡聚酯多功能纤维的制造方法，本发明采用制成一种咖啡聚酯母粒，特制的咖啡母粒以重量百分比与聚酯切片共混，经聚酯纤维生产工艺制作成咖啡纤维。咖啡纤维由于其良好的吸附性、抑菌性，可以做成具有美容功能的毛巾、医疗防护服、口罩、婴幼及孕妇防护服、袜子，可吸附臭气及细菌，并具有防毒作用。

Description

一种咖啡聚酯多功能纤维的制造方法
技术领域
本发明涉及纺织行业，尤其涉及合成纤维生产领域一种咖啡聚酯多功能纤维的制造方法。
背景技术
现在，全世界都在关注“环保”，能源紧张，空气污染严重，当我们越来越意识到地球只有一个，而且我们对它伤害得越重，最后都会报应在人类自己身上的时候，我们都开始尽全力为环境保护做点事。科技的进步给人们的生活及消费模式产生了极大的影响，在讲究舒适生活的同时兼具环保概念的“绿色消费”是人类走向文明及经济发展的必然。咖啡聚酯多功能纤维就是这一方面的杰出代表。咖啡聚酯多功能纤维拥有吸湿、除臭、抗菌等多重功效。纺织产业高科技化，最终的目的就是为人类服务，提升人们的生活质量，正值地球温室效应气温暖化之际，有前瞻思维的企业，早就嗅到注重环境保护与资源循环利用理念的商机，这是趋势，也是预期未来最受消费者喜爱的机能性纺织品，织物中若添加咖啡聚酯多功能纤维之成份，织物会有吸湿、除臭、抗菌之功效，如能在服饰上广泛运用，相信是一波换购商机。咖啡聚酯多功能纤维选择利用咖啡渣加以微粉化后，选择特殊工艺加工成咖啡碳母粒，设计特别的喷丝板，突破干燥、纺丝和牵伸关键生产工艺，开发的多功能纤维。
发明内容
本发明的目的在于提供一种咖啡聚酯多功能纤维的制造方法。
本发明首先要特制咖啡母粒，咖啡母粒生产工序是：先将咖啡渣脱水，加热到550℃～650℃的温度中予以炭化，再加热到900℃～1200℃高温中煅烧，然后研磨成200～500纳米级粉体，再经特殊工艺加工制成适用于聚酯纤维生产的咖啡母粒。特制的咖啡母粒与聚酯切片共混，经聚酯纤维生产工艺制作成咖啡纤维。
咖啡纤维生产工艺流程是：将咖啡母粒以重量百分比5％～20％与聚酯切片共混，经真空干燥后，熔融、纺丝机纺丝、通过甬道到卷绕机卷绕、落桶得到初生纤维。在这前纺过程中，纺丝温度为265℃～288℃，以275℃～280℃为佳，纺丝速度为1000～1400米/分钟。再经后纺即将若干桶初生纤维通过集束架集束，并进行牵伸、卷曲、切断而制得咖啡纤维。本发明的牵伸倍数为3.0～3.7倍。
本发明的咖啡纤维截面可以是已知熔融纺丝的任何截面，如圆形、三角形、三叶型、中空形、扁平形、、L形、T形、W形、多边形、狗骨形等等。其单丝细度为0.8旦～10旦。
本发明具有显著的积极效果：
1.咖啡渣材料具有无数孔隙，表面积巨大，吸附能力极强，可吸附各种有机化合物，如残留农药、重金属、各种致病菌及霉素等损害人体健康或致病的废物；可产生远红外线，能够增加人体表面微血管的血液循环，促进新陈代谢。
2.咖啡纤维由于其良好的吸附性、抑菌性，可以做成具有美容功能的毛巾、医疗防护服、口罩、婴幼及孕妇防护服、袜子，可吸附臭气及细菌，并具有防毒作用。
3.采用咖啡渣材料，对环境保护与资源循环再利用有很大的意义。
具体实施方式
实施例1
生产纤度为1.33旦尼尔(dtex)的咖啡纤维。
将特制的咖啡母粒以重量百分比为10％比例加到聚酯切片中，进行真空干燥，先定温在60℃保温1小时，再升温至80℃保温1小时，升温至100℃保温2小时，升温至120℃保温2小时，升温至160℃保温3小时，逐步升温至200℃保温至得到干燥的结晶切片，干燥过程一般需要14小时。用现有的纺丝设备，即在LHV451纺丝机上纺丝，再卷绕成型为初生纤维，纺丝温度为278℃，卷绕速度为1050m/min，初生纤维经过集束，在LHV903后牵伸机上牵伸，牵伸倍数为3.5倍，得到1.33dtex咖啡纤维。
实施例2
生产纤度为4.44旦尼尔(dtex)的中空咖啡纤维。
将特制的咖啡母粒以重量百分比为12％比例加到聚酯切片中，进行真空干燥，先定温在60℃保温1小时，再升温至100℃保温2小时，升温至120℃保温2小时，升温至160℃保温3小时，逐步升温至200℃保温至得到干燥的结晶切片，干燥过程一般需要14小时。用现有的纺丝设备，即在LHV451纺丝机上纺丝，所用纺丝喷丝板为中空喷丝板，再卷绕成型为初生纤维，纺丝温度为275℃，卷绕速度为1050m/min，初生纤维经过集束，在LHV903后牵伸机上牵伸，牵伸倍数为3.2倍，得到8.89dtex中空咖啡纤维。
实施例3
生产纤度为6.67旦尼尔(dtex)的咖啡纤维。
将特制的咖啡母粒以重量百分比为12％比例加到聚酯切片中，进行真空干燥，先定温在60℃保温1小时，再升温至80℃保温1小时，升温至120℃保温2小时，升温至160℃保温3小时，逐步升温至200℃保温至得到干燥的结晶切片，干燥过程一般需要14小时。用现有的纺丝设备，即在LHV451纺丝机上纺丝，再卷绕成型为初生纤维，纺丝温度为272℃，卷绕速度为1000m/min，初生纤维经过集束，在LHV903后牵伸机上牵伸，牵伸倍数为3.4倍，得到6.67dtex咖啡纤维。
本发明的一种咖啡聚酯多功能纤维的制造方法不局限于以上实施例。

Claims (3)

1.一种咖啡聚酯多功能纤维的制造方法，其特征在于特制咖啡母粒，咖啡母粒生产工序是：先将咖啡渣脱水，加热到550℃～650℃的温度中予以炭化，再加热到900℃～1200℃高温中煅烧，然后研磨成200～500纳米级粉体，再经一定工艺加工制成适用于聚酯纤维生产的咖啡母粒。
2.根据权利要求1所述的一种咖啡聚酯多功能纤维的制造方法，其特征在于：所述的特制的咖啡母粒以重量百分比与聚酯切片共混，经聚酯纤维生产工艺制作成咖啡纤维。
3.根据权利要求1所述的一种咖啡聚酯多功能纤维的制造方法，其特征在于：所述咖啡母粒以重量百分比5％～20％与聚酯切片共混。
CN201010605398.3A 2010-12-21 2010-12-21 一种咖啡聚酯多功能纤维的制造方法 Active CN102534848B (zh)