CN101838939B - 耐洗耐磨的后焙烘棉弹力面料整理工艺 - Google Patents

耐洗耐磨的后焙烘棉弹力面料整理工艺 Download PDF

Info

Publication number
CN101838939B
CN101838939B CN2010101660481A CN201010166048A CN101838939B CN 101838939 B CN101838939 B CN 101838939B CN 2010101660481 A CN2010101660481 A CN 2010101660481A CN 201010166048 A CN201010166048 A CN 201010166048A CN 101838939 B CN101838939 B CN 101838939B
Authority
CN
China
Prior art keywords
washable
postcure
dyeing
elastic fabric
cotton elastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2010101660481A
Other languages
English (en)
Other versions
CN101838939A (zh
Inventor
甄峤源
潘文英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yixing Lucky G&L Denim Co., Ltd.
Original Assignee
YIXING XINLEQI TEXTILE PRINTING AND DYEING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIXING XINLEQI TEXTILE PRINTING AND DYEING CO Ltd filed Critical YIXING XINLEQI TEXTILE PRINTING AND DYEING CO Ltd
Priority to CN2010101660481A priority Critical patent/CN101838939B/zh
Publication of CN101838939A publication Critical patent/CN101838939A/zh
Application granted granted Critical
Publication of CN101838939B publication Critical patent/CN101838939B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

耐洗耐磨的后焙烘棉弹力面料整理工艺，涉及棉弹力织物多功能后整理工艺，包括染色和后整理，染色时染色液中加入有防泳移剂；染色后采用红外线预烘干，再低温烘干固色，烘干温度为60-70℃，风速50-60％；后整理中，整理剂由渗透剂JFC、树脂Permafresh EFR-6C、环氧基改性硅柔软剂Advaansoft AV-920、聚氨酯BAYPRET NANO-PU、丙烯酸酯类粘合剂ACRYGEN61192配伍组成，获得的产品耐洗性(ColorBand)达到30次水洗变色为3.5级(AATCC135)；耐磨性15000转(BS EN ISO 12947 part 2，Martindale)，平整度(抗皱度)水洗30次后达到3.5级(AATCC 124)，裤缝水洗30次后达到4.0级(AATCC 88)。

Description

耐洗耐磨的后焙烘棉弹力面料整理工艺
技术领域
本发明涉及棉弹力织物多功能后整理工艺，尤其是指一种耐洗耐磨的后焙烘棉弹力面料整理工艺。
背景技术
现有的纺织物染色，在轧染后先用红外线预烘干，再进入烘房烘干固色(100-120℃，风速100％)，烘干时温度高，风速快，是一种快速染色的方式，所得的色布染色不透芯，不耐洗，一般洗3-5次就会出泛白(不耐洗)，不能满足现在的耐洗要求。
染色后的织物要达到免烫、抗皱等特点，须进行后整理，织物进行后整理的方法是将织物在拉幅机上用渗透剂、树脂、纤维保护剂、硅油柔软剂等浸渍、烘干，再预缩处理。这种后烘焙整理工艺中通常采用加树脂方法，但加入树脂会导致织物强力受损，其强力要降低40-50％。而对于弹力织物，由于纱中包覆有氨纶，较一般非弹力布强力要降低20-30％，若让弹力布采用后焙烘整理工艺，其强力受损更为严重，按照通常的方法后焙烘棉弹力面料强力是不能满足要求，并且织物十分不耐磨。此种后整理方法所得到棉弹力面料，树脂用量大，对纤维损伤大，因而影响耐磨性，耐磨性试验只有5000-6000转，不能满足现在高耐磨要求。
由于上述原因，面料多次水洗后产生退色，不够耐洗，水洗30次，平整度、裤缝达不到3级，成衣接缝及折边磨损现象严重，导致消费者经常投诉。
发明内容
本发明目的在于克服上述已有技术的不足，提供一种耐洗耐磨的后焙烘棉弹力面料整理工艺，所获产品平整度高，耐洗耐磨性能好。
本发明目的实现，主要改进是在染色液中增加防泳移剂(20-30g/l)，在烘干时采用低温慢速烘干(60-70℃，风速50-60％)，减少染料在烘干时的移动，从而提高染色的透染性，增强耐磨耐洗度；其次，在后整理的整理剂中加入聚氨酯和聚丙烯粘合剂，减少树脂用量，并使助剂附着于纱线表面，从而提高耐磨性以及抗皱性。
具体说，耐洗耐磨的后焙烘棉弹力面料整理工艺，包括染色和后整理，其特征在于染色时染色液中加入有防泳移剂；染色后采用红外线预烘干，再低温烘干固色，烘干温度为60-70℃，风速50-60％；后整理中，整理剂的各组分配方为：
渗透剂JFC                  5-10g/L
树脂Permafresh EFR-6C      240-250g/L环氧基改性硅柔软剂Advaansoft AV-920      60-70g/L
聚氨酯BAYPRET NANO-PU                   100-120g/L
丙烯酸酯类粘合剂ACRYGEN 61192           50-60g/L。
本工艺染色液中加入的防泳移剂通常为丙烯酸类防泳移剂，加入量为20-30g/l，主要作用是防止染料泳移，使其染透芯，提高水洗牢度，防退色；本工艺中加入的丙烯酸类防泳移剂浓度较高，是防泳移剂常规用量的一倍量以上。
本工艺的染色液还增加有盐(氯化钠)以提高染料的渗透固色效果，盐的加入量为20-30g/L。
烘干时，烘房温度及风量设定较低，是让布慢慢烘干，防止染料泳移，使纱线内外色差减少，提高耐洗性。
后整理采用的整理液配方中，环氧基改性硅柔软剂Advaansoft AV-920可使后面手感好；加入有BAYPRET NANO-PU(聚氨酯)和ACRYGEN 61192(丙烯酸酯类粘合剂)，通过减少原后整理液中树脂用量(减少20-30％)，BAYPRET NANO-PU(聚氨酯)和ACRYGEN61192(丙烯酸酯类粘合剂)形成薄膜附着于面料表面，提高了耐磨性，增加了平整度。所用BAYPRET NANO-PU(聚氨酯)是纳米级分散、自交联聚醚聚氨脂型高端整理剂，纳米级乳液具有最佳的分散和渗透性能，可以在纤维表面和纤维间形成一层膜，可以降低强力的损失，增加耐磨性。所用ACRYGEN 61192(丙烯酸酯类粘合剂)是丙烯酸酯类聚合物，增加织物耐磨性。
为降低织物中甲醛，整理液中加有4-8g/L的尿素。
通过该整理工艺，获得的产品耐洗性(ColorBand)达到30次水洗变色为3.5级(AATCC135)；耐磨性15000转(BS EN ISO 12947 part 2，Martindale)，平整度(抗皱度)水洗30次后达到3.5级(AATCC 124)，裤缝水洗30次后达到4.0级(AATCC 88)，是一种高级后焙烘工艺。
具体实施方式
实施例1，耐洗耐磨的后焙烘棉弹力面料整理工艺，包括染色和后整理：
染色时染色液中加入有丙烯酸类防泳移剂，含是为20g/l；
染色后采用红外线预烘干，再低温烘干固色，烘干温度为70℃，风速60％；
后整理中，整理剂的各组分配方为：
渗透剂JFC                             5g/L
Permafresh EFR-6C(树脂)               250g/L
环氧基改性硅柔软剂Advaansoft AV-920   70g/L
BAYPRET NANO-PU(聚氨酯)              120g/L
ACRYGEN 61192(丙烯酸酯类粘合剂)      60g/L。
实施例2，耐洗耐磨的后焙烘棉弹力面料整理工艺，包括染色和后整理：染色时染色液中加入有丙烯酸类防泳移剂，含是为30g/l；
染色后采用红外线预烘干，再低温烘干固色，烘干温度为60℃，风速55％；
后整理中，整理剂的各组分配方为：
渗透剂JFC                              8g/L
Permafre sh EFR-6C(树脂)               240g/L
环氧基改性硅柔软剂Advaansoft AV-920    68g/L
BAYPRET NANO-PU(聚氨酯)                110g/L
ACRYGEN 61192(丙烯酸酯类粘合剂)        50g/L。
尿素                                   4g/L
实施例3，耐洗耐磨的后焙烘棉弹力面料整理工艺，包括染色和后整理：
染色时染色液中加入有丙烯酸类防泳移剂，含是为25g/l，另加入有盐，含量为30g/L；
染色后采用红外线预烘干，再低温烘干固色，烘干温度为65℃，风速50％；
后整理中，整理剂的各组分配方为：
渗透剂JFC                             10g/L
Permafresh EFR-6C(树脂)               245g/L
环氧基改性硅柔软剂Advaansoft AV-920   65g/L
BAYPRET NANO-PU(聚氨酯)               100g/L
ACRYGEN 61192(丙烯酸酯类粘合剂)       55g/L。
尿素                                  6g/L
实施例4，耐洗耐磨的后焙烘棉弹力面料整理工艺，包括染色和后整理：
染色时染色液中加入有丙烯酸类防泳移剂，含是为28g/l，另加入有盐，含量为20g/L；
染色后采用红外线预烘干，再低温烘干固色，烘干温度为60℃，风速50％；
后整理中，整理剂的各组分配方为：
渗透剂JFC                            6g/L
Permafresh EFR-6C(树脂)              248g/L
环氧基改性硅柔软剂Advaansoft AV-920  60g/L
BAYPRET NANO-PU(聚氨酯)              115g/L
ACRYGEN 61192(丙烯酸酯类粘合剂)         52g/L。
尿素                                    8g/L
实施例1-实施例4获得的产品，耐洗性(ColorBand)达到30次水洗变色为3.5级(AATCC135)；耐磨性15000转(BS EN ISO 12947part 2，Martindale)，平整度(抗皱度)水洗30次后达到3.5级(AATCC 124)，裤缝水洗30次后达到4.0级(AATCC 88)。

Claims (5)

1.耐洗耐磨的后焙烘棉弹力面料整理工艺，包括染色和后整理，其特征在于染色时染色液中加入有防泳移剂；染色后采用红外线预烘干，再低温烘干固色，烘干温度为60-70℃，风速50-60％；后整理中，整理剂的各组分配方为：
渗透剂JFC                             5-10g/L
树脂Permafresh EFR-6C                 240-250g/L
环氧基改性硅柔软剂Advaansoft AV-920   60-70g/L
聚氨酯BAYPRET NANO-PU                 100-120g/L
丙烯酸酯类粘合剂ACRYGEN 61192         50-60g/L。
2.根据权利要求1所述的耐洗耐磨的后焙烘棉弹力面料整理工艺，其特征在于染色液中加入的防泳移剂为丙烯酸类防泳移剂。
3.根据权利要求1或2所述的耐洗耐磨的后焙烘棉弹力面料整理工艺，其特征在防泳移剂加入量为20-30g/l。
4.根据权利要求1所述的耐洗耐磨的后焙烘棉弹力面料整理工艺，其特征在于染色液中还加有盐，盐的加入量为20-30g/L。
5.根据权利要求1所述的耐洗耐磨的后焙烘棉弹力面料整理工艺，其特征在于整理液中加入有尿素，加入量为4-8g/L。
CN2010101660481A 2010-04-30 2010-04-30 耐洗耐磨的后焙烘棉弹力面料整理工艺 Active CN101838939B (zh)