WO2023054589A1 - 食品用油脂組成物、これを含む食品及び植物肉、オレオゲルの食感改善剤、並びに食品用油脂組成物の製造方法 - Google Patents

食品用油脂組成物、これを含む食品及び植物肉、オレオゲルの食感改善剤、並びに食品用油脂組成物の製造方法 Download PDF

Info

Publication number
WO2023054589A1
WO2023054589A1 PCT/JP2022/036452 JP2022036452W WO2023054589A1 WO 2023054589 A1 WO2023054589 A1 WO 2023054589A1 JP 2022036452 W JP2022036452 W JP 2022036452W WO 2023054589 A1 WO2023054589 A1 WO 2023054589A1
Authority
WO
WIPO (PCT)
Prior art keywords
oil
wax
fat composition
food
fatty acid
Prior art date
Application number
PCT/JP2022/036452
Other languages
English (en)
French (fr)
Inventor
哲史 有馬
Original Assignee
三菱ケミカル株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱ケミカル株式会社 filed Critical 三菱ケミカル株式会社
Priority to CN202280066013.1A priority Critical patent/CN118042937A/zh
Priority to JP2023551850A priority patent/JPWO2023054589A1/ja
Publication of WO2023054589A1 publication Critical patent/WO2023054589A1/ja

Abstract

本発明は、食品用途に好適なくちどけ等の食感等に優れている油脂組成物を提供することを課題とする。油脂、ワックス、及びショ糖脂肪酸エステルを含む、食品用油脂組成物により課題を解決する。

Description

食品用油脂組成物、これを含む食品及び植物肉、オレオゲルの食感改善剤、並びに食品用油脂組成物の製造方法
　本発明は、食品用油脂組成物、これを含む食品及び植物肉、オレオゲルの食感改善剤、並びに食品用油脂組成物の製造方法に関するものである。
　オレオゲルとは、液体の油と少量のゲル化剤とからなり、ゲル化剤が形成する網目構造に液体の油が取り込まれることにより、固化した油脂組成物である。オレオゲルはトランス脂肪酸を含まないため、不飽和脂肪酸への水素添加によって固化した硬化油に比べて、体への悪影響が少ないとされる。また、動植物油脂の固体脂や硬化油に比べて、オレオゲルは、飽和脂肪酸の含有率が低い。したがって、オレオゲルを摂取した際は、肥満や循環器疾患のリスクを高める飽和脂肪酸の摂取が過剰になり難い。これらの理由から、近年、オレオゲルは固体脂や硬化油の代替品として注目されている。
　特許文献１には、嚥下・咀嚼困難者に供されるキザミ食やペースト食と混合するためのオルガノゲルが記載されている。ここで、オルガノゲルは油脂と油脂ゲル化剤を含有し、油脂ゲル化剤としては、極度硬化油、乳化剤、ワックス等が挙げられている。
　特許文献２及び３には、油脂とワックスを混合することによって、ワックスオレオゲルを作製できることが記載されている。
国際公開第２０１２／１１４９９５号 米国特許出願公開第２００４／００５２９２１号明細書 国際公開第２０２１／０４６６４２号
　オレオゲルを食品用途に用いる場合、食感等に優れていることが好ましい。しかしながら、上述のオレオゲルは、食品用途に用いた場合の食感等について十分な検討がなされていない。そこで、本発明は、食品用途に好適なくちどけ等の食感等に優れている油脂組成物を提供することを課題とする。
　本発明者らは、上記課題を解決すべく研究を進めた。この結果、油脂及びワックスを含む油脂組成物に、さらに乳化剤としてショ糖脂肪酸エステルを含ませることによって、油脂組成物の性質を改良できることを見出し、本発明の完成に至った。
　即ち、本発明の要旨は以下の通りである。
［１］　油脂、ワックス、及びショ糖脂肪酸エステルを含む、食品用油脂組成物。
［２］　前記油脂、前記ワックス及び前記ショ糖脂肪酸エステルを合計３０～１００重量％含み、前記ワックスと前記ショ糖脂肪酸エステルの合計含有量が７．５重量％以上であり、前記ワックスに対する前記ショ糖脂肪酸エステルの含有量比（重量比）が０．０１以上５．０以下である、［１］に記載の食品用油脂組成物。
［３］　前記ショ糖脂肪酸エステルのＨＬＢが０以上５以下である、［１］又は［２］に記載の食品用油脂組成物。
［４］　前記ショ糖脂肪酸エステルを構成する脂肪酸の炭素数が１０～２４である、［１］～［３］のいずれかに記載の食品用油脂組成物。
［５］　前記ワックスが植物性ワックスである、［１］～［４］のいずれかに記載の食品用油脂組成物。
［６］　前記ワックスがライスブランワックス又はキャンデリラワックスである、［１］～［５］のいずれかに記載の食品用油脂組成物。
［７］　オレオゲルである、［１］～［６］のいずれかに記載の食品用油脂組成物。
［８］　前記食品が植物肉である、［１］～［７］のいずれかに記載の食品用油脂組成物。
［９］　ショ糖脂肪酸エステルからなる、ワックスオレオゲルの食感改善剤。
［１０］　［１］～［８］のいずれかに記載の食品用油脂組成物を含む食品。
［１１］　［１］～［８］のいずれかに記載の食品用油脂組成物及び植物性タンパク質を含有する植物肉であって、前記食品用油脂組成物を０．１～５０重量％含有し、前記植物性タンパク質を１０～９０重量％含有する、植物肉。
［１２］　更に結着剤を含有する、［１１］に記載の植物肉。
［１３］　油脂、ワックス及びショ糖脂肪酸エステルを含有する食品用油脂組成物の製造方法であって、前記ワックスと前記ショ糖脂肪酸エステルの合計含有量が７．５重量％以上であり、前記ワックスに対する前記ショ糖脂肪酸エステルの含有量比（重量比）が０．０１以上５．０以下となるように、前記油脂、前記ワックス及び前記ショ糖脂肪酸エステルを混合する工程、並びに前記工程により得られた混合物を加熱溶解後に冷却固化する工程を有する、食品用油脂組成物の製造方法。
［１４］　ワックスオレオゲルの食感改善のための、ショ糖脂肪酸エステルの使用。
　本発明により、食感等に優れた油脂組成物を提供することができる。
比較例１、２、３、５、６の顕微鏡画像である。（図面代用写真） 実施例１、３、４の顕微鏡画像である。（図面代用写真） 比較例７、８、１１、１２の顕微鏡画像である。（図面代用写真） 実施例５、７の顕微鏡画像である。（図面代用写真） 比較例１、２、３、５、６について、各歪値γにおける貯蔵弾性率Ｇ’及び損失弾性率Ｇ”を示すグラフである。 比較例１、実施例１、３、４について、各歪値γにおける貯蔵弾性率Ｇ’及び損失弾性率Ｇ”を示すグラフである。 比較例７、８、１１、１２について、各歪値γにおける貯蔵弾性率Ｇ’及び損失弾性率Ｇ”を示すグラフである。 比較例７、実施例５、７について、各歪値γにおける貯蔵弾性率Ｇ’及び損失弾性率Ｇ”を示すグラフである。 比較例１～３、５、６、実施例１、３、４について、ｔａｎδ＝１となる歪値γを示すグラフである。 比較例７、８、１１、１２、実施例５、７について、ｔａｎδ＝１となる歪値γを示すグラフである。 実施例８、９、１０の顕微鏡画像である。（図面代用写真）
　以下、本発明の実施形態を詳細に説明する。以下に記載する構成要件の説明は、本発明の実施形態の一例（代表例）であり、本発明はその要旨を超えない限り、これらの内容に限定されるものではない。また、本明細書において「～」という表現を用いる場合、その前後の数値又は物性値を含む表現として用いるものとする。
　本発明の一実施形態は、油脂、ワックス、及びショ糖脂肪酸エステルを含む、油脂組成物である。本実施形態の油脂組成物は、食品用途に好適に用いられる。すなわち、本実施形態の油脂組成物は、食品用油脂組成物であることが好ましい。本実施形態の油脂組成物は、ワックス（ゲル化剤）の網目構造に液体の油が取り込まれることにより固化したオレオゲルであることが好ましい。
　オレオゲルを構成する網目構造において、ワックスは、通常、結晶状態である。オレオゲル中のワックスの結晶は、通常粗大であり、硬い網目構造を形成する。結晶の大きさと形状は核形成と結晶成長の条件によって変化する。
　後述するとおり、本発明の一実施形態に係る油脂組成物は、口内でのくちどけが良好である。その理由は、ショ糖脂肪酸エステルがワックスと相互作用することにより、ワックスの結晶形状が変化し、粗大化が抑制され、微細なワックス結晶になったためと推定される。すなわち、微細な結晶により形成された網目構造は、常温では適度な硬さを有し、体温に近い温度では、外力により変形や崩壊しやすくなったと考えられる。
＜油脂＞
　本実施形態の油脂組成物に含まれる油脂は、食用油脂であることが好ましい。また、常温（本発明では、常温は２５℃とする。）で液体の油（以下、「液体油脂」と言う場合がある。）であることが好ましい。液体油脂としては、具体的には、菜種油、大豆油、ヒマワリ油、オリーブ油、パーム分別油（パームオレイン）、コーン油、コメ油、綿実油、ゴマ油、落花生油、アーモンド油、亜麻仁油、エゴマ油、魚油、中鎖脂肪酸トリグリセリドなどが挙げられる。これらのうち、菜種油、大豆油、ヒマワリ油、パーム分別油（パームオレイン）、コメ油、亜麻仁油及び中鎖脂肪酸トリグリセリドが好ましく、菜種油が特に好ましい。
　本実施形態の油脂組成物に含まれる油脂の融点は、１５℃以下であることが好ましく、５℃以下であることがさらに好ましい。
　本実施形態の油脂組成物に含まれる油脂に含まれる液体油脂の量は、５０重量％以上であることが好ましく、７５重量％以上であることがより好ましく、９０重量％以上であることがさらに好ましく、９５重量％以上であることが特に好ましい。
　本実施形態の油脂組成物に含まれる油脂は、１種類でも２種類以上の油脂の混合物でもよい。また、常温で固体の油脂（以下、「固体油脂」と言う場合がある。）が含有されていてもよい。固体油脂としては、具体的には、パーム油、ヤシ油、カカオ油、硬化油、牛脂、ラード、乳脂などが挙げられる。固体油脂が含まれる場合は、本実施形態の油脂組成物に含まれる油脂の５０重量％以下であることが好ましく、２５重量％以下であることがより好ましく、１０重量％以下であることがさらに好ましく、５重量％以下であることが特に好ましい。
　油脂に含まれる飽和脂肪酸の割合は、肥満や循環器疾患のリスクを低減する観点から低いことが好ましい。そこで、本実施形態の油脂組成物に含まれる油脂に含まれる飽和脂肪酸は、５０重量％以下であることが好ましく、２５重量％以下であることがより好ましく、１０重量％以下であることがさらに好ましく、５重量％以下であることが特に好ましい。
　本実施形態の油脂組成物に含まれる油脂、ワックス及びショ糖脂肪酸エステルの合計量に対する油脂の含有量は、通常５０重量％以上、好ましくは７０重量％以上、より好ましくは９０重量％以上である。また、通常９９．８９重量％以下、好ましくは９８重量％以下である。
＜ワックス＞
　本実施形態の油脂組成物に含まれるワックスは、合成ワックス、植物性ワックス、動物性ワックスのいずれでもよい。好ましくは植物性ワックスである。植物性ワックスは、特に限定されるものではないが、具体的にはライスブランワックス、カルナバワックス、ヒマワリワックス、キャンデリラワックス、ベリーワックス、コーンワックス、ミツロウ、ホホバワックス、オーリクリーワックスなどが挙げられる。これらのうち、ライスブランワックス及びキャンデリラワックスが好ましい。ワックスは、１種類のみを用いても、２種類以上を併用してもよい。
　ワックスの融点は、くちどけを改善する観点から、好ましくは９０℃以下である。また、下限は特に限定されないが、２５℃以上が好ましく、４０℃以上がさらに好ましい。
　ワックスは、ワックスエステル及び／又は炭化水素を含有する。ワックスに含有されるワックスエステル及び炭化水素の炭素数は、それぞれ２０以上７０以下であることが好ましい。
　ワックスエステルとは、脂肪酸と脂肪族アルコールがエステル結合した化合物である。ワックスエステルの炭素数は、３０以上がより好ましく、４０以上がさらに好ましく、また、６２以下がより好ましい。
　ワックスに含有される炭化水素の炭素数は６０以下が好ましく、４０以下がより好ましい。
　ワックスエステル及び炭化水素の炭素数が上記範囲内であると、ゲルを形成するための結晶ネットワークを形成しやすいため好ましい。また、炭化水素は鎖状炭化水素であることが好ましく、鎖状炭化水素は、直鎖であってもよく、分枝を有してもよい。
　ワックス中のワックスエステルの割合は、特に限定されないが、通常１５重量％以上、好ましくは８０重量％以上、より好ましくは９０重量％以上であり、一方、通常９８重量％以下である。ワックス中の炭化水素の割合は、通常０．１重量％以上、７５重量％以下である。
　本実施形態において、ワックス中には、ワックスエステルと炭化水素以外の成分が含有されていてもよい。その他の成分としては、具体的には、脂肪酸、脂肪族アルコール、樹脂、ヒドロキシ酸エステルなどが挙げられる。
　本実施形態の油脂組成物に含まれるワックスの結晶の大きさは、本実施形態の油脂組成物が常温で適度な硬さを有しやすい点では大きいことが好ましく、また、一方で、口内温度などの高温において外力により変形や崩壊しやすく、くちどけがよくなりやすい点では小さいことが好ましい。そこで、本実施形態の油脂組成物に含まれるワックスの結晶の大きさは、０．１μｍ以上であることが好ましく、１．０μｍ以上であることがより好ましい。また、一方で、２０μｍ以下であることが好ましく、１０μｍ以下であることがより好ましい。特に、本実施形態の油脂組成物に含まれるワックスが米ぬかワックス（ライスブランワックス）である場合の結晶の大きさは、１．０μｍ以上であることが好ましく、２．０μｍ以上であることがより好ましい。また、一方で、１５μｍ以下であることが好ましく、１０μｍ以下であることがより好ましい。また、本実施形態の油脂組成物に含まれるワックスがキャンデリラワックスである場合の結晶の大きさは、０．１μｍ以上であることが好ましく、１．０μｍ以上であることがより好ましい。また、一方で、７．０μｍ以下であることが好ましく、３．５μｍ以下であることがより好ましい。
　ワックスの結晶の大きさは、顕微鏡観察により、測定することができる。具体的には、油脂組成物を加熱溶解してスライドガラス上に薄く延ばした後に常温で偏光顕微鏡を用いて確認する。画像解析ソフト（ＷｉｎＲＯＯＦ２０１５）を用いて、結晶の長辺の長さを測定し、２０以上の結晶の平均値を算出する。
　本実施形態の油脂組成物に含まれる油脂、ワックス及びショ糖脂肪酸エステルの合計量に対するワックスの含有量は、通常０．１重量％以上であり、好ましくは０．５重量％以上であり、より好ましくは１．０重量％以上であり、一方、通常５０重量％以下、好ましくは２５重量％以下、より好ましくは１５重量％以下である。
＜ショ糖脂肪酸エステル＞
　本実施形態において、ショ糖脂肪酸エステルは、ワックスとの相互作用の観点から、親油性であることが好ましい。具体的には、ＨＬＢ値が０以上５以下であることが好ましく、０以上３以下であることがより好ましい。ＨＬＢ値は、通常、乳化剤の分野で使用される親水性、疎水性のバランスを表す指標である。ＨＬＢ値は、通常用いる計算式、例えばＧｒｉｆｆｉｎ、Ｄａｖｉｓ、川上式、有機概念図等の方法により求めることができる。また、カタログ等に記載されているＨＬＢの数値を使用してもよい。
　ショ糖脂肪酸エステルを構成する脂肪酸としては、ワックスとの相互作用の観点から、炭素数１０以上２４以下の脂肪酸が好ましく、１２以上２４以下がより好ましく、１４以上２４以下がさらに好ましい。具体的にはラウリン酸、パルミチン酸、ステアリン酸、ベヘン酸、オレイン酸、エルカ酸などが挙げられる。ショ糖脂肪酸エステルは、モノエステルであってもよく、ジエステル、トリエステル等のポリエステルであってもよい。また、２種類以上の脂肪酸から構成されるポリエステルであってもよい。ショ糖脂肪酸エステルは１種類のみを用いてもよく、２種類以上を併用してもよい。
　ショ糖脂肪酸エステルの市販品としては、「リョートーシュガーエステルＬ－１９５」、「リョートーシュガーエステルＰ－１７０」、「リョートーシュガーエステルＳ－０７０」、「リョートーシュガーエステルＳ－１７０」、「リョートーシュガーエステルＳ－２７０」、「リョートーシュガーエステルＳ－３７０」、「リョートーシュガーエステルＳ－５７０」、「リョートーシュガーエステルＯ－１７０」、「リョートーシュガーエステルＢ－３７０」、「リョートーシュガーエステルＥＲ－２９０」、「リョートーシュガーエステルＰＯＳ－１３５」（以上、三菱ケミカル社製、商品名）；「ＤＫエステルＦ－１０」、「ＤＫエステルＦ－２０Ｗ」、「ＤＫエステルＦ－５０」（以上、第一工業製薬社製、商品名）；等が挙げられる。
　本実施形態の油脂組成物に含まれる油脂、ワックス及びショ糖脂肪酸エステルの合計量に対するショ糖脂肪酸エステルの含有量は、好ましくは０．０１重量％以上、より好ましくは０．０５重量％以上であり、一方、通常１０重量％以下、好ましくは５重量％以下、より好ましくは２.５重量％以下である。
　また、ワックスに対するショ糖脂肪酸エステルの含有量比（重量比）は、０．０１以上であることが好ましく、０．０５以上であることがより好ましく、また、一方で、５．０以下であることが好ましく、２．０以下であることがより好ましく、１．０以下であることがさらに好ましい。ワックスに対するショ糖脂肪酸エステルの含有量比が上記範囲内であると、ワックス結晶の大きさや形が好適に制御され、油脂組成物の食感がより良好になりやすい。
　本実施形態の油脂組成物は、ショ糖脂肪酸エステル以外の乳化剤を含有していてもよい。但し、ワックス結晶とは別に、乳化剤が結晶を形成することを防ぐ観点から、乳化剤の含有量は少ないことが好ましい。
　本実施形態の油脂組成物において、ショ糖脂肪酸エステルは、ワックスと共にオレオゲルの網目構造を形成していると考えられる。そこで、本実施形態の油脂組成物に含まれるワックスとショ糖脂肪酸エステルの合計含有量は、本実施形態の油脂組成物が常温で適度な硬さを有しやすい点では多いことが好ましい。また、一方で、口内温度などの高温において外力により変形、崩壊しやすく、くちどけがよくなりやすい点では少ないことが好ましい。そこで、本実施形態の油脂組成物に含まれるワックスとショ糖脂肪酸エステルの合計含有量は、７．５重量％以上であることが好ましく、８．０重量％以上であることがより好ましく、９．０重量％以上であることがさらに好ましく、１０重量％以上であることが特に好ましい。一方、３０．０重量％以下であることが好ましく、２５．０重量％以下であることがより好ましく、２０．０重量％以下であることがさらに好ましく、１５．０重量％以下であることが特に好ましい。
＜食感改善剤＞
　本実施形態の油脂組成物においては、ショ糖脂肪酸エステルにより、ワックスの結晶の大きさが小さくなっていると期待される。すなわち、ショ糖脂肪酸エステルは、油脂とワックスを含有するワックスオレオゲルの食感改善剤として用いることができる。
　本実施形態の油脂組成物（ショ糖脂肪酸エステル含有）におけるワックスの結晶の大きさは、本実施形態の油脂組成物からショ糖脂肪酸エステルを除いた場合におけるワックスの結晶の大きさに対し、０．４７以下であることが好ましく、０．３６以下であることがより好ましい。
＜その他の成分＞
　本実施形態の油脂組成物は、本発明の機能を損なわない範囲で、必要に応じて、甘味料、安定化剤、香料、抗酸化剤、塩類など食品に添加される成分を含有してもよい。
　甘味料としては、糖、糖アルコール、高甘味度甘味料などがあり、具体的には、例えば、以下の甘味料が挙げられる。
　糖：ぶどう糖、果糖、木糖、ソルボース、ガラクトース、異性化糖などの単糖類；ショ糖、麦芽糖、乳糖、異性化乳糖、パラチノースなどの二糖類；フラクトオリゴ糖、マルトオリゴ糖、イソマルトオリゴ糖、ガラクトオリゴ糖、カップリングシュガー、パラチノースなどのオリゴ糖類；など
　糖アルコール：エリスリトール、ソルビトール、キシリトール、マンニトール等の単糖アルコール類；マルチトール、イソマルチトール、ラクチトール等の２糖アルコール類；マルトトリイトール、イソマルトトリイトール、パニトール等の３糖アルコール類；オリゴ糖アルコール等の４糖以上アルコール類；粉末還元麦芽糖水飴；など
　高甘味度甘味料：アスパルテーム、ネオテーム、スクラロース、ステビアなど。
　安定化剤としては、ガラクトマンナン、キサンタンガム、カラギーナン、アラビアガム、タマリンドガム、ジェランガム、グルコマンナン、セルロースなどが挙げられる。
　抗酸化剤としては、ローズマリー抽出物、茶抽出物、生コーヒー豆抽出物、ブドウ種子抽出物、ヤマモモ抽出物などの植物抽出物、トコフェロール、トコトリエノール、アスコルビン酸パルミチン酸エステル、ジブチルヒドロキシトルエン、ブチルヒドロキシアニソールなどが挙げられる。
　塩類としては、例えば、食塩、塩化カリウム、塩化マグネシウム等の塩化物；炭酸ナトリウム、炭酸カリウム、炭酸カルシウム等の炭酸塩；重炭酸ナトリウム等の重炭酸塩；リン酸２ナトリウム、リン酸３ナトリウム、リン酸２カリウム、リン酸３カリウム等のリン酸塩；ポリリン酸ナトリウム；クエン酸ナトリウム等のクエン酸塩；乳酸ナトリウム；などが挙げられる。特にマグネシウムを含む塩類が好ましく、食品用途に使用できるものとして、乳清ミネラル、塩化マグネシウム、酸化マグネシウム、炭酸マグネシウム、硫酸マグネシウム、苦汁（粗製海水塩化マグネシウム）、ドロマイト、粗塩、ステアリン酸マグネシウム、リン酸一水素マグネシウム、リン酸三マグネシウム、ケイ酸マグネシウム、水酸化マグネシウム、酢酸マグネシウム、クエン酸マグネシウム、リンゴ酸マグネシウム、安息香酸マグネシウム、グルコン酸マグネシウム、Ｌ－グルタミン酸マグネシウム、セピオライト、タルク、フィチンなどが挙げられる。
＜油脂組成物の物理的性質＞
　本実施形態の油脂組成物の融点は、特に限定されないが、通常１５℃以上であり、２５℃以上が好ましく、３５℃以上がより好ましい。一方、通常９０℃以下であり、８０℃以下が好ましく、７５℃以下がより好ましい。上記範囲内であると、本実施形態の油脂組成物を食品用途に用いた場合に硬さやくちどけなどの食感が良好になりやすい。
　物質の粘弾性は貯蔵弾性率Ｇ’、損失弾性率Ｇ”、及びそれらの比である損失正接ｔａｎδによって表される。損失正接ｔａｎδが１よりも大きい、即ちＧ’＜Ｇ”であるとき、物質は固体的性質を示し、損失正接ｔａｎδが１よりも小さい、即ちＧ’＞Ｇ”であるとき、物質は液体的性質を示す。本実施形態の油脂組成物は、静置状態では、通常、損失正接ｔａｎδが１よりも大きくなる。また、歪値γが一定以上になると、通常、損失正接ｔａｎδが１よりも小さくなり、ゲルの構造が崩壊する。食品においては、構造崩壊が起こる歪値γが低いほど「くちどけが良い」とされる報告もある。
　本実施形態の油脂組成物は、口内温度付近である３５℃で歪値γが０．０１であるときの貯蔵弾性率Ｇ’は特に限定されないが、通常１０Ｐａ以上であり、２０Ｐａ以上であることが好ましく、１００Ｐａ以上であることがさらに好ましい。また、通常２０００００Ｐａ以下であり、１０００００Ｐａ以下であることが好ましく、５００００Ｐａ以下であることがさらに好ましく、２００００Ｐａ以下であることが特に好ましい。上記範囲内であると、保形性が良好で纏まりのあるゲルとしやすい。
　本実施形態の油脂組成物は、３５℃で歪値γが０．０１であるときの損失弾性率Ｇ”は、特に限定されないが、通常１０Ｐａ以上であり、１００Ｐａ以上であることが好ましい。また、通常１０００００Ｐａ以下であり、５００００Ｐａ以下であることが好ましく、２００００Ｐａ以下であることがより好ましく、７０００Ｐａ以下であることが特に好ましい。上記範囲内であると、保形性が良好で纏まりのあるゲルとしやすい。
　本実施形態の油脂組成物は、３５℃における損失正接ｔａｎδが１となるときの歪値γは、特に限定されないが、通常０．１以上１．０以下であり、０．１以上０．７以下であることが好ましく、０．１以上０．５以下であることがさらに好ましく、０．１以上０．４以下であることが特に好ましい。上記範囲内であると、本実施形態の油脂組成物を食品用途に用いた場合にくちどけが良好になりやすい。
　本実施形態の油脂組成物の動的粘弾性は、動的粘弾性測定装置を用いて測定する。
　本実施形態の油脂組成物の官能評価は、以下のようにして行うことができる。本実施形態の油脂組成物を舌の上に乗せ、舌と上あごで擦る様に咀嚼し、感じたザラザラ感（滑らかさ）と、口内への広がり方（口溶け）を評価することができる。滑らかさの評価は、本実施形態の油脂組成物からショ糖脂肪酸エステルを除いた組成物との相対的な滑らかさを評価すればよい。また、くちどけの評価は、より早く口内に広がるか、口の中に塊やザラつきが残らないかについて、本実施形態の油脂組成物からショ糖脂肪酸エステルを除いた組成物との相対評価で行えばよい。
＜油脂組成物の組成＞
　本実施形態の油脂組成物は、上述の物理的性質が発現しやすく、特に食品用途に用いた場合におけるくちどけが良好となりやすいことから、油脂、ワックス及びショ糖脂肪酸エステルの合計量が多いことが好ましい。そこで、本実施形態の油脂組成物に含有される油脂、ワックス及びショ糖脂肪酸エステルの合計量は、３０重量％以上であることが好ましく、６０重量％以上であることがより好ましく、８０重量％以上であることがさらに好ましい。なお、上限は１００重量％である。
＜油脂組成物の製造方法＞
　本実施形態の油脂組成物は、油脂、ワックス及びショ糖脂肪酸エステルを上記の割合で混合する工程、並びに前記工程により得られた混合物を加熱溶解後に、冷却固化する工程を有する方法により製造することができる。加熱温度は、ワックスとショ糖脂肪酸エステルを油脂に溶解させやすい点では高温が好ましく、また、一方で、各成分の反応や変質を防ぐためには低温が好ましい。そこで、加熱温度は、４０℃以上が好ましく、６０℃以上がより好ましく、また、一方で、１２０℃以下が好ましく、１００℃以下がより好ましい。加熱溶解後の冷却は、室温に徐冷してもよいし、急冷してもよい。冷却中に攪拌してもよい。
＜油脂組成物の用途＞
　本実施形態の油脂組成物は、種々の食品において固体脂や硬化油の代替品として用いることができる。具体的には、クリーム状食品、乳代替物等の飲食品；レトルト状の栄養補助食品；流動食、高カロリー食、乳児用栄養製品等の機能性食品；経口ワクチン；ファットスプレッドやフラワーペーストなどの油脂加工品；カレー、コーヒークリーマー、マヨネーズ、ドレッシング、ムース、パスタソース、シチュー、デミグラスソース、ホワイトソース、トマトソース等の各種ソース・スープ類；中華食品の素、どんぶりの素等などのレトルト食品や複合調味料；ヨーグルト類、チーズ、アイスクリーム類、クリーム類、キャラメル、キャンディ、チューインガム、チョコレート、クッキー・ビスケット、ケーキ、パイ、スナック、クラッカー、和菓子、米菓子、豆菓子、ゼリー、プリン等の菓子・デザート；ハンバーグ、ミートボール、味付け畜肉缶詰等の畜産加工品；水産加工品；代替肉；冷凍食品；冷蔵食品；即席麺、カップ麺、即席スープ・シチュー類等の即席食品；栄養強化食品；経管栄養製剤等が挙げられる。
　本実施形態の油脂組成物は、くちどけに優れることから、食品用途に用いることが好ましく、代替肉用途に用いることがより好ましい。すなわち、本実施形態の油脂組成物を含む食品は、食感に優れる点で好ましい。また、本実施形態の油脂組成物を含む代替肉は、食感に優れる点で好ましい。
＜植物肉＞
　本実施形態の油脂組成物は、既存の固体油脂に比べ、飽和脂肪酸やトランス脂肪酸が少ない。そこで、本実施形態の油脂組成物は、健康面にアピールできる点で植物肉に用いることが特に好ましい。すなわち、本実施形態の油脂組成物を含む植物肉（以下、「本実施形態の植物肉」と言う場合がある。）は、食感に優れ、ヘルシーである点で好ましい。
　本実施形態の植物肉は、動物肉の代替肉の一種であって、植物性タンパク質を用いた代替肉のことを言う。また、本発明において、植物肉は、ソーセージやハムなどの所謂加工肉に用いられる動物性タンパク質に代えて、植物性タンパク質を用いたものも含む。
　本実施形態の植物肉は、本発明の一実施形態の油脂組成物と植物性タンパク質を含有する。植物性タンパク質としては、エンドウ豆タンパク質、大豆タンパク質、緑豆タンパク質、ヒヨコ豆タンパク質、そら豆タンパク質、レンズ豆タンパク質等の豆タンパク質、しいたけタンパク質、小麦タンパク質などが挙げられる。これらのうち、アレルギー症状などを起こすことが少なく、栄養豊富なことから豆タンパク質が好ましい。本実施形態の植物肉に含有される油脂組成物及び植物性タンパク質の量は、植物肉の調理法や植物肉を用いた料理の種類などに応じて適宜調整すればよい。本実施形態の植物肉は、植物性タンパク質を１０～９０重量％含有し、油脂組成物を０．１～５０重量％含有することが好ましい。また、本実施形態の植物肉は、植物性タンパク質に対し、油脂組成物を０．１～８３重量％含有することが好ましい。
　本実施形態の植物肉は、結着剤を含有することが好ましい。結着剤とは、植物性タンパク質、油脂などの植物肉中の成分を結着させる剤のことを言う。具体的には、例えば、セルロース誘導体、増粘多糖類、でんぷんなどが挙げられる。本実施形態の植物肉が結着剤を含む場合の含有量は、植物肉の成形性の点では多いことが好ましいが、また、一方で、噛み応えなどの食感の点では少ないことが好ましい。そこで、具体的には、植物肉中に含まれる結着剤は、０．１重量％以上であることが好ましく、０．５重量％以上であることがより好ましく、１．０重量％以上であることが特に好ましく、また、一方で、１０．０重量％以下であることが好ましく、８．０重量％以下であることがより好ましく、５．０重量％以下であることが特に好ましい。
　本実施形態の植物肉は、更に砂糖などの甘味料、塩、醤油などの調味料、エキス類、食物繊維などを含有していてもよい。
　以下、実施例により本発明をさらに詳細に説明するが、本発明の範囲は、以下の実施例で示す態様に限定されないことは言うまでもない。また、以下の実施例において、「％」の記載は、特段の断りが無ければ「重量％」を意味する。
＜原料＞
　各実施例で用いた原料を以下に示す。
・菜種油：株式会社　Ｊ－オイルミルズ　さらさらキャノーラ油（飽和脂肪酸の割合：４～８％）
・ライスブランワックス（ＲＢＸ）：ボーソー油脂株式会社　ライスワックスＳＳ－２（ワックスエステルの炭素数：４０～５６）
・キャンデリラワックス（ＣＬＸ）：東亜化成株式会社　ＴＯＷＡＸ－４Ｆ３（ワックスエステルの炭素数：３４～５６、炭化水素の炭素数：２７～３３）
・ショ糖ベヘン酸エステル（Ｂ－３７０）：三菱ケミカル株式会社　リョートーシュガーエステル　Ｂ－３７０、ＨＬＢ＝約３
・ショ糖パルミチン酸エステル（Ｐ－１７０）：三菱ケミカル株式会社　リョートーシュガーエステル　Ｐ－１７０、ＨＬＢ＝約１
・ショ糖ラウリン酸エステル（Ｌ－１９５）：三菱ケミカル株式会社　リョートーシュガーエステル　Ｌ－１９５、ＨＬＢ＝約１
・グリセリンモノベヘン酸エステル（ＧＭＢ）：Ｄａｎｉｓｃｏ　Ｃｒｙｓｔａｌｌｉｚｅｒ　１１０Ｒ、ＨＬＢ＝約４
・プロピレングリコールモノベヘン酸エステル（ＰＧＭＢ）：Ｄａｎｉｓｃｏ　ＰＧＭＢ、ＨＬＢ＝約３
・ソルビタントリベヘン酸エステル（ＳＴＢ）：理研ビタミン株式会社　ポエム　Ｂ－１５０、ＨＬＢ＝約２．５
・大豆レシチン（レシチン、Ｌｅｃ．）：辻製油株式会社　ＳＬＰ－ホワイト、ＨＬＢ＝３
＜油脂組成物の製造＞
　表１及び２に記載された各組成（表中の添加量は重量％）となるように原料をガラス製容器中で混合し、９０℃のヒーターを用いて９０分間加熱した。加熱の際はＶＯＲＴＥＸ－２　ＧＥＮＩＥの強度５で混合物を攪拌し、各原料が完全に溶解していることを目視で確認した。その後、４℃の恒温水槽にガラス製容器を漬けて５℃／ｍｉｎ以上で６０分以上冷却することにより、実施例１～７及び比較例１～１２のオレオゲルを得た。これらは以下の測定において使用するまで室温（２５℃）で保管した。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
＜顕微鏡観察＞
　上記で得た油脂組成物を、ヒーターを用いて９０℃に加熱した。加熱により油脂組成物が完全に溶解したことを目視で確認した。少量をスライドガラス上に取り、その上にカバーガラスを載せて油脂組成物を薄く延ばした。スライドガラスを顕微鏡用冷却加熱ステージ（ＬＩＮＫＡＭ　ＴＨＭＳ６００）の上に載せ、５℃／ｍｉｎ以上で２５℃まで冷却した。偏光顕微鏡（オリンパス　ＢＸ－５３）を用いて、油脂組成物中のワックスの結晶の大きさを観察した。結果を図１～４に示す。
　また、画像解析ソフト（ＷｉｎＲＯＯＦ２０１５）を用いて、ワックス結晶の長辺の長さを測定した。２０以上の結晶の長辺の長さを計測し、その平均値を算出した。結果を表３に示す。
Figure JPOXMLDOC01-appb-T000003
　表３から明らかなように、比較例１の乳化剤を含まないライスブランワックスの結晶の長辺の長さは２０μｍ程度と大きかった。また、比較例２、３、５、６のグリセリンモノベヘン酸エステル、プロピレングリコールモノベヘン酸エステル、ソルビタントリベヘン酸エステル又は大豆レシチンを加えたライスブランワックスの結晶の長辺の長さは１０～１５μｍ程度であり、比較例１の約１／２～３／４であった。
　これに対し、実施例１、３及び４のショ糖脂肪酸エステルを加えたライスブランワックスの結晶の長辺の長さは３～９μｍ程度と小さかった。これは乳化剤を加えないライスブランワックスの結晶の長辺の長さの約１／１０～１／２の大きさであり、微細であると言える。
　比較例７の乳化剤を加えないキャンデリラワックスの結晶の長辺の長さは７μｍ程度であり大きな結晶が確認された。また、比較例８、９及び１２のグリセリンモノベヘン酸エステル、プロピレングリコールモノベヘン酸エステル又は大豆レシチンを加えたキャンデリラワックスの結晶の長辺の長さは６～９μｍ程度で、乳化剤を加えないキャンデリラワックスの結晶の長辺の長さと大きな違いは見られなかった。また、比較例１１のソルビタントリベヘン酸エステルを加えたキャンデリラワックスの結晶の長辺の長さは３．５μｍ程度であり、比較例７の約１／２の大きさであった。
　一方、実施例５及び７のショ糖脂肪酸エステルを加えたキャンデリラワックスの結晶の長辺の長さは１～２μｍ程度と、比較例７の約１／７～１／４の大きさであり、これらは比較例７～９、１１、１２に比べて顕著に微細であった。
　以上の結果から、ワックスにショ糖脂肪酸エステルを添加することにより、ワックスの結晶サイズを１／１０～１／２程度に微細化することが可能であることが裏付けられた。
＜動的粘弾性測定＞
　φ３５ｍｍ　１°のコーンプレートを動的粘弾性測定装置（ＨＡＡＫＥ　ＲｈｅｏＳｔｒｅｓｓ　６００）に設置した。実施例１、３、４及び比較例１～３、５、６の油脂組成物をプレート上に載せ、ギャップを０．０５２ｍｍに設定した。
　３５℃において、歪値γを０．０１から１０までとしたときの貯蔵弾性率Ｇ’、損失弾性率Ｇ”、及び損失正接ｔａｎδを測定した。結果を図５及び６に示す。また、各油脂組成物においてＧ’＝Ｇ”、ｔａｎδ＝１となる歪値γを算出した結果を図９に示す。
　コーンプレートをφ２０ｍｍのパラレルプレートとし、ギャップを０．０１ｍｍとした以外は上記と同様にして、実施例５、７及び比較例７、８、１１、１２の油脂組成物の貯蔵弾性率Ｇ’、損失弾性率Ｇ”、及び損失正接ｔａｎδを測定した。結果を図７及び８に示す。また、各油脂組成物においてＧ’＝Ｇ”、ｔａｎδ＝１となる歪値γを算出した結果を図１０に示す。
　図９に示されるように、ワックスとしてライスブランワックスを用いて、ショ糖脂肪酸エステルを添加した実施例１、３、４は、比較例１～３、５、６に比べてｔａｎδ＝１となる歪値γが低く、ショ糖脂肪酸エステルによるオレオゲルのくちどけ改善効果が裏付けられた。特に、炭素数１６～２２のショ糖脂肪酸エステルを添加した実施例１、３は、ｔａｎδ＝１となる歪値γが顕著に低かった。
　また、図１０に示されるように、ワックスとしてキャンデリラワックスを用いて、ショ糖脂肪酸エステルを添加した実施例５、７は、比較例７、８、１１、１２に比べてｔａｎδ＝１となる歪値γが低く、ショ糖脂肪酸エステルによるオレオゲルのくちどけ改善効果が確認された。
＜官能評価＞
　各油脂組成物を５ｍｍ×５ｍｍ×５ｍｍに切り出した。切り出した油脂組成物を舌の上に乗せ、舌と上あごで擦る様に咀嚼し、感じたザラザラ感（滑らかさ）と、口内への広がり方（口溶け）を評価した。
　滑らかさの評価は、ＢＬＡＮＫ（比較例１又は７）を３として、より滑らかでありザラつきを相対的に感じないものを４、５とし、ザラつきをより感じて滑らかではないものを２、１とした。
　また、くちどけの評価は、ＢＬＡＮＫ（比較例１又は７）を３として、より早く口内に広がるものを４、５とし、口の中で塊やザラつきが残るものを２、１と評価した。結果を表４に示す。
Figure JPOXMLDOC01-appb-T000004
　ワックスとしてライスブランワックスを用いて、乳化剤を用いない比較例１は、舌にザラつきを感じ滑らかではなく、口溶けも不良であった。ショ糖脂肪酸エステル以外の乳化剤を添加した比較例３～５は、比較例１と比較して滑らかさは同程度かより不良で、口溶けは比較例１と同程度であった。
　一方、ショ糖脂肪酸エステルを添加した実施例１、２、４は、滑らかさは比較例１と同等以上であり、特に実施例１は非常に滑らかであった。これらの結果より、本実施形態の油脂組成物は、咀嚼時に速やかに口の中に広がり、口溶けが良好であることが裏付けられた。
　ワックスとしてキャンデリラワックスを用いて、乳化剤を用いない比較例７は、舌に大きな塊が残り滑らかではなく、口溶けも不良であった。ショ糖脂肪酸エステル以外の乳化剤を添加した比較例９～１１は、比較例７と比較してやや大きな塊が口内に残り、口溶けは比較例７と同程度であった。
　一方、ショ糖脂肪酸エステルを添加した実施例５～７は、滑らかさは比較例７と同等以上であり、特に実施例７は非常に滑らかであった。これらの結果より、本実施形態の油脂組成物は、咀嚼時に速やかに口の中に広がり、口溶けが良好であることが裏付けられた。特に、実施例７は、口溶けが非常に良好であった。
　以上の結果から、ショ糖脂肪酸エステルを含有することにより、油脂組成物の滑らかさが向上（ザラついた食感を改善）し、口溶けが良好となること（咀嚼時に速やかに口内に広がる効果）が裏付けられた。これらの効果は、ショ糖脂肪酸エステルを含有することによって、ワックスの結晶が微細化したことに起因すると考えられる（顕微鏡観察の結果を参照）。
＜油脂組成物の製造＞
　表５に記載された各組成（表中の添加量は重量％）となるように原料をガラス製若しくはステンレス製容器中で混合し、９０℃のヒーター若しくは恒温水槽を用いて９０分間加熱した。加熱の際はＶＯＲＴＥＸ－２　ＧＥＮＩＥの強度５若しくは手攪拌で混合物を攪拌し、各原料が完全に溶解していることを目視で確認した。その後、４℃の恒温水槽にガラス製容器を漬けて５℃／ｍｉｎ以上で６０分以上冷却、若しくは加熱溶解した油脂組成物を４℃の冷蔵庫で放冷することにより、実施例８～１０のオレオゲルを得た。これらは以下の測定において使用するまで室温（２５℃）で保管した。
＜顕微鏡観察＞
　上記で得た油脂組成物を、ヒーターを用いて９０℃に加熱した。加熱により油脂組成物が完全に溶解したことを目視で確認した。少量をスライドガラス上に取り、その上にカバーガラスを載せて油脂組成物を薄く延ばした。スライドガラスを顕微鏡用冷却加熱ステージ（ＬＩＮＫＡＭ　ＴＨＭＳ６００）の上に載せ、５℃／ｍｉｎ以上で２５℃まで冷却した。偏光顕微鏡（オリンパス　ＢＸ－５３）を用いて、油脂組成物中のワックスの結晶の大きさを観察した。結果を図１１に示す。
　また、画像解析ソフト（ＷｉｎＲＯＯＦ２０１５）を用いて、ワックス結晶の長辺の長さを測定した。２０以上の結晶の長辺の長さを計測し、その平均値を算出した。結果を表５に示す。
Figure JPOXMLDOC01-appb-T000005
　表５から明らかなように、実施例８及び９のライスブランワックスとショ糖脂肪酸エステルの合計量が７．５重量％以上である油脂組成物は、これに含まれるワックスの結晶のサイズが特に微細となることが裏付けられた。
＜植物肉の製造＞
　油脂組成物を用いて、表６に記載された各組成（表中の添加量は重量％）となるように大豆タンパク質を用いた植物肉（畜肉様加工食品）を製造した。
　まず、攪拌機（株式会社愛工舎製作所製「ＫＭ３００」）を用いて、オニオンパウダー、濃口醤油、上白糖、酵母エキス、食塩、エマルションカード及び油脂組成物を均一に攪拌混合した。そこへ、３０分間水戻しを行った粒状の大豆タンパク質を加え、まとまりのある均一な生地状態になるまで更に攪拌混練を行った。まとまった生地を、直径６ｃｍ、厚さ２ｃｍとなるように成形し、２２０℃の鉄板を用いて、片面９０秒ずつ両面を焼いた後、コンベンクションオーブン（タニコー株式会社製「ＴＳＣＯ―６ＥＤＮ」）を用いて、１５０℃、蒸気１００％で更に１０分間焼き、植物肉を製造した。
Figure JPOXMLDOC01-appb-T000006
＜官能評価＞
　製造された植物肉について、咀嚼時の柔らかさ、纏まり感、しっとり感の３点について、以下の基準で４名のパネリストにより官能評価を行った。比較例１３を０と評価し、これに対する実施例１１と１２の評価結果の平均値を表７に示す。
［咀嚼時の柔らかさ］
　咀嚼を繰り返す中で柔らかさを強く感じた場合を＋２、やや強く感じた場合を＋１、比較例１３と同等な場合を０、やや弱く感じた場合を－１、弱く感じた場合を－２とした。
［纏まり感］
　咀嚼を繰り返し、植物肉が口の中でほぐれる中で、よく纏まりながら崩れる場合を＋２、やや良くまとまりながら崩れる場合を＋１、比較例１３と同等な場合を０、ややボロボロと崩れる場合を－１、ボロボロと崩れる場合を－２とした。
［しっとり感］
　喫食中にしっとり感を強く感じた場合を＋２、やや強く感じた場合を＋１、比較例１３と同等な場合を０、しっとり感がやや弱く少しパサパサと感じた場合を－１、しっとり感が弱くパサパサと感じた場合を－２とした。
Figure JPOXMLDOC01-appb-T000007
　実施例１１及び１２は、比較例１３と比較して、咀嚼時の柔らかさ、纏まり感及びしっとり感に優れることから、本発明の一実施形態に係る油脂組成物により植物肉の食感が改善されること、本発明の一実施形態に係る油脂組成物が優れた食感改善剤であること、及び本発明の一実施形態に係る植物肉が食感に優れることが裏付けられた。これらの優れた食感は、油脂組成物に含まれるワックス結晶の微細化や物性変化によりもたらされたと考えられる。
＜油脂組成物の製造＞
　表８に記載された各組成（表中の添加量は重量％）となるように原料をガラス製容器中で混合し、９０℃のヒーターを用いて９０分間加熱した。加熱の際はＶＯＲＴＥＸ－２　ＧＥＮＩＥの強度５で混合物を攪拌し、各原料が完全に溶解していることを目視で確認した。その後、４℃の恒温水槽にガラス製容器を漬けて５℃／ｍｉｎ以上で６０分以上冷却することにより、実施例１３のオレオゲルを得た。これを以下の測定において使用するまで室温（２５℃）で保管した。
Figure JPOXMLDOC01-appb-T000008
＜融点の測定＞
　示差走査熱量測定装置（日立ハイテクノロジーズ社製「ＤＳＣ－６００」）を用いて、油脂組成物に含まれるワックスと油脂、及び実施例３と１３及び比較例１の油脂組成物の融点を測定した。得られたＤＳＣカーブから読み取った、「融解開始温度～完了温度」を以下に示す。
・菜種油：株式会社　Ｊ－オイルミルズ　さらさらキャノーラ油；－３０～０℃。
・ライスブランワックス（ＲＢＸ）：ボーソー油脂株式会社　ライスワックスＳＳ－２；６０～８５℃。
・キャンデリラワックス（ＣＬＸ）：東亜化成株式会社　ＴＯＷＡＸ－４Ｆ３；４５～７５℃。
・比較例１；５０～７５℃。
・実施例３；５０～７５℃。
・実施例１３；５０～７５℃。

Claims (13)

  1. 　油脂、ワックス、及びショ糖脂肪酸エステルを含む、食品用油脂組成物。
  2. 　前記油脂、前記ワックス及び前記ショ糖脂肪酸エステルを合計３０～１００重量％含み、前記ワックスと前記ショ糖脂肪酸エステルの合計含有量が７．５重量％以上であり、前記ワックスに対する前記ショ糖脂肪酸エステルの含有量比（重量比）が０．０１以上５．０以下である、請求項１に記載の食品用油脂組成物。
  3. 　前記ショ糖脂肪酸エステルのＨＬＢが０以上５以下である、請求項１又は２に記載の食品用油脂組成物。
  4. 　前記ショ糖脂肪酸エステルを構成する脂肪酸の炭素数が１０～２４である、請求項１又は２に記載の食品用油脂組成物。
  5. 　前記ワックスが植物性ワックスである、請求項１又は２に記載の食品用油脂組成物。
  6. 　前記ワックスがライスブランワックス又はキャンデリラワックスである、請求項１又は２に記載の食品用油脂組成物。
  7. 　オレオゲルである、請求項１又は２に記載の食品用油脂組成物。
  8. 　前記食品が植物肉である、請求項１又は２に記載の食品用油脂組成物。
  9. 　ショ糖脂肪酸エステルからなる、ワックスオレオゲルの食感改善剤。
  10. 　請求項１又は２に記載の食品用油脂組成物を含む食品。
  11. 　請求項１又は２に記載の食品用油脂組成物及び植物性タンパク質を含有する植物肉であって、前記食品用油脂組成物を０．１～５０重量％含有し、前記植物性タンパク質を１０～９０重量％含有する、植物肉。
  12. 　更に結着剤を含有する、請求項１１に記載の植物肉。
  13. 　油脂、ワックス及びショ糖脂肪酸エステルを含有する食品用油脂組成物の製造方法であって、前記ワックスと前記ショ糖脂肪酸エステルの合計含有量が７．５重量％以上であり、前記ワックスに対する前記ショ糖脂肪酸エステルの含有量比（重量比）が０．０１以上５．０以下となるように、前記油脂、前記ワックス及び前記ショ糖脂肪酸エステルを混合する工程、並びに前記工程により得られた混合物を加熱溶解後に冷却固化する工程を有する、食品用油脂組成物の製造方法。
     
     
PCT/JP2022/036452 2021-09-29 2022-09-29 食品用油脂組成物、これを含む食品及び植物肉、オレオゲルの食感改善剤、並びに食品用油脂組成物の製造方法 WO2023054589A1 (ja)