WO2020262462A1 - Élément emballage externe destiné à élément calorifuge sous vide, élément calorifuge sous vide, et article muni d'un élément calorifuge sous vide - Google Patents

Élément emballage externe destiné à élément calorifuge sous vide, élément calorifuge sous vide, et article muni d'un élément calorifuge sous vide Download PDF

Info

Publication number
WO2020262462A1
WO2020262462A1 PCT/JP2020/024838 JP2020024838W WO2020262462A1 WO 2020262462 A1 WO2020262462 A1 WO 2020262462A1 JP 2020024838 W JP2020024838 W JP 2020024838W WO 2020262462 A1 WO2020262462 A1 WO 2020262462A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
vacuum heat
heat insulating
inorganic
outer packaging
Prior art date
Application number
PCT/JP2020/024838
Other languages
English (en)
Japanese (ja)
Inventor
琢 棟田
将博 今井
Original Assignee
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大日本印刷株式会社 filed Critical 大日本印刷株式会社
Priority to JP2020572558A priority Critical patent/JP7247235B2/ja
Publication of WO2020262462A1 publication Critical patent/WO2020262462A1/fr

Abstract

La présente invention concerne un élément emballage externe (10) destiné à un élément calorifuge sous vide, l'élément emballage externe ayant un film thermosoudable (1), et au moins deux couches inorganiques (4) comprenant une première couche inorganique et une seconde couche inorganique. L'élément emballage externe comprend en outre une couche de composé de type couche inorganique (5) qui contient un composé de type couche inorganique et un liant ; la première couche inorganique, la couche de composé de type couche inorganique et la seconde couche inorganique étant positionnées dans l'ordre indiqué, une couche métallique n'étant pas présente. En raison de la fourniture d'un tel élément emballage externe destiné à un élément calorifuge sous vide, la présente invention concerne : un élément emballage externe destiné à un élément calorifuge sous vide qui permet de fabriquer un élément calorifuge sous vide pouvant transmettre des ondes électriques et conserver une excellente fonction calorifuge ; et un élément calorifuge sous vide et un article muni d'un élément calorifuge sous vide dans lequel intervient l'élément emballage externe destiné à un élément calorifuge sous vide.
PCT/JP2020/024838 2019-06-24 2020-06-24 Élément emballage externe destiné à élément calorifuge sous vide, élément calorifuge sous vide, et article muni d'un élément calorifuge sous vide WO2020262462A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2020572558A JP7247235B2 (ja) 2019-06-24 2020-06-24 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-116573 2019-06-24
JP2019116573 2019-06-24

Publications (1)

Publication Number Publication Date
WO2020262462A1 true WO2020262462A1 (fr) 2020-12-30

Family

ID=74061737

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/024838 WO2020262462A1 (fr) 2019-06-24 2020-06-24 Élément emballage externe destiné à élément calorifuge sous vide, élément calorifuge sous vide, et article muni d'un élément calorifuge sous vide

Country Status (2)

Country Link
JP (2) JP7247235B2 (fr)
WO (1) WO2020262462A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015068484A (ja) * 2013-09-30 2015-04-13 旭有機材工業株式会社 真空断熱材用ラミネートシート及び真空断熱材
JP2017210986A (ja) * 2016-05-24 2017-11-30 大日本印刷株式会社 真空断熱材用外包材、真空断熱材、および真空断熱材付き機器

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015193141A (ja) 2014-03-31 2015-11-05 東レフィルム加工株式会社 ガスバリア性フィルムおよびそれを用いたガスバリア性ラミネート体
JP2018189163A (ja) * 2017-05-08 2018-11-29 大日本印刷株式会社 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP2019002442A (ja) * 2017-06-13 2019-01-10 大日本印刷株式会社 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP2018189227A (ja) * 2017-07-25 2018-11-29 大日本印刷株式会社 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015068484A (ja) * 2013-09-30 2015-04-13 旭有機材工業株式会社 真空断熱材用ラミネートシート及び真空断熱材
JP2017210986A (ja) * 2016-05-24 2017-11-30 大日本印刷株式会社 真空断熱材用外包材、真空断熱材、および真空断熱材付き機器

Also Published As

Publication number Publication date
JP2022000591A (ja) 2022-01-04
JP7247235B2 (ja) 2023-03-28
JPWO2020262462A1 (ja) 2021-09-13

Similar Documents

Publication Publication Date Title
CN110603403B (zh) 真空绝热材料用外包材料、真空绝热材料和带真空绝热材料的物品
WO2017146165A1 (fr) Matériau d'emballage externe de matériau d'isolation sous vide, matériau d'isolation sous vide, et article doté d'un matériau d'isolation sous vide
KR20140131112A (ko) 진공단열재용 외피재 및 이를 포함하는 고성능 진공단열재
JP2019002442A (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP2018189163A (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP7238566B2 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
WO2020262665A1 (fr) Matériau d'encapsulation externe pour matériau d'isolation thermique sous vide, matériau d'isolation thermique sous vide, et article doté de matériau d'isolation thermique sous vide
WO2020262462A1 (fr) Élément emballage externe destiné à élément calorifuge sous vide, élément calorifuge sous vide, et article muni d'un élément calorifuge sous vide
JP6149997B1 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP2016138638A (ja) 真空断熱材用積層体及びそれを用いた真空断熱材
JP2020008084A (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP2018189240A (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
WO2017159120A1 (fr) Matériau d'isolation thermique à vide et appareil domestique, mur de maison et équipement de transport comportant celui-ci
JP7155858B2 (ja) 複層ガラスの樹脂製スペーサ用ガスバリアフィルム、複層ガラス用樹脂製スペーサ、および複層ガラス
JP2018189227A (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP6662408B2 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP6187719B1 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP7334836B1 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP6369597B1 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP7305922B2 (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品
JP2017061956A (ja) 真空断熱材用外装材、およびそれを用いた真空断熱材、ならびに真空断熱材付き機器
CN114867599A (zh) 阻气膜、膜叠层体和真空隔热件
JPH11182780A (ja) 真空断熱材
WO2020175503A1 (fr) Matériau d'isolation à vide
JP2018189226A (ja) 真空断熱材用外包材、真空断熱材、および真空断熱材付き物品

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2020572558

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20831091

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20831091

Country of ref document: EP

Kind code of ref document: A1