WO2020162467A1 - ガラス板の成形装置 - Google Patents

ガラス板の成形装置 Download PDF

Info

Publication number
WO2020162467A1
WO2020162467A1 PCT/JP2020/004190 JP2020004190W WO2020162467A1 WO 2020162467 A1 WO2020162467 A1 WO 2020162467A1 JP 2020004190 W JP2020004190 W JP 2020004190W WO 2020162467 A1 WO2020162467 A1 WO 2020162467A1
Authority
WO
WIPO (PCT)
Prior art keywords
molding
glass plate
stage
glass
mold
Prior art date
Application number
PCT/JP2020/004190
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
祐司 井本
諭 金杉
Original Assignee
Ａｇｃ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ａｇｃ株式会社 filed Critical Ａｇｃ株式会社
Priority to JP2020571221A priority Critical patent/JP7463972B2/ja
Priority to CN202080010213.6A priority patent/CN113329977B/zh
Publication of WO2020162467A1 publication Critical patent/WO2020162467A1/ja

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B23/00—Re-forming shaped glass
    • C03B23/02—Re-forming glass sheets
    • C03B23/023—Re-forming glass sheets by bending
    • C03B23/03—Re-forming glass sheets by bending by press-bending between shaping moulds

Definitions

  • the present invention relates to a glass plate forming apparatus.
  • a molding apparatus has been proposed in which a plate-shaped glass material is sequentially conveyed to heating, pressing, and cooling stages provided in a chamber, and a press-molded product is continuously molded at each stage (Patent Document 1). ).
  • the glass material is maintained at a heating temperature sufficient for processing the glass material by setting the molding die to a specified temperature during pressing.
  • the glass material after molding is cooled and solidified, and finally cooled to a temperature of 200° C. or lower at which the molding die is not oxidized.
  • the shape of the mold is accurately transferred at the time of pressing, and by holding this molded shape by cooling and solidifying, it becomes a press-molded product with high shape accuracy.
  • An object of the present invention is to provide a glass plate forming apparatus capable of forming a molded product having a complicated shape with high shape accuracy and high throughput while reducing the equipment cost.
  • the present invention has the following configurations.
  • a glass plate forming apparatus for heating a glass plate to form a desired shape A first molding die in which a molding surface having a curved shape is formed in at least a part thereof, and the glass plate is supported on the molding surface; At least one second mold clamped to the first mold; At least one preheating stage for heating the glass plate supported by the first mold; At least one molding stage in which the second molding die is arranged so as to face the first molding die, and the heated glass plate is molded between the first molding die and the second molding die; At least one cooling stage for gradually cooling the glass plate after molding, A die conveying unit that conveys the first molding die in the order of the preheating stage, the molding stage, and the cooling stage, The glass plate has a glass central portion inside the glass-shaped outer peripheral edge, and a glass outer peripheral portion between the outer periphery of the glass central portion and the glass-shaped outer peripheral edge, A glass plate forming apparatus in which the second forming die of the forming stage makes contact with the glass plate
  • FIG. 1 is a schematic process drawing showing a procedure for forming a glass plate into a curved shape.
  • FIG. 2 is a schematic configuration diagram of the molding apparatus.
  • FIG. 3 is a sectional view of a plurality of lamp heaters.
  • FIG. 4 is a schematic plan view of the cross section along the line III-III shown in FIG. 2 as seen from above.
  • FIG. 5 is a schematic explanatory view showing how the lower die is conveyed along the conveying direction from the preheating stage to the cooling stage.
  • FIG. 6 is an enlarged sectional view of the molding stage.
  • 7A is a cross-sectional view of the upper mold
  • FIG. 7B is a cross-sectional view including the molding surface of the lower mold.
  • FIG. 8 is a rear view of the upper die viewed from the direction B in FIG. 7(A).
  • FIG. 9 is a plan view of the glass plate.
  • FIG. 10A is a schematic process explanatory view showing step by step how the lower mold and the upper mold shown in FIGS. 7A and 7B are brought close to each other to mold the glass plate.
  • FIG. 10B is a schematic process explanatory view showing stepwise how the lower die and the upper die shown in FIGS. 7A and 7B are brought close to each other to form the glass plate.
  • FIG. 10C is a schematic process explanatory view showing stepwise how the lower die and the upper die shown in FIGS. 7A and 7B are brought close to each other to form the glass plate.
  • FIG. 10A is a schematic process explanatory view showing step by step how the lower die and the upper mold shown in FIGS. 7A and 7B are brought close to each other to form the glass plate.
  • FIG. 10C is a schematic process explanatory view showing stepwise how the
  • FIG. 11 is a process explanatory view showing an outline of how a glass plate is formed by the second forming method.
  • FIG. 12 is a schematic configuration diagram of a molding apparatus including a plurality of preheating stages, a molding stage, and a plurality of cooling stages.
  • FIG. 13 is a graph showing an example of temperature changes of the lower mold and the glass plate in the preheating stage, the molding stage, and the cooling stage.
  • FIG. 14 is a schematic configuration diagram of a conventional molding apparatus as a reference example.
  • FIG. 15 is a schematic configuration diagram of a molding apparatus showing another configuration example of the molding apparatus shown in FIG. 16A is a schematic cross-sectional view showing the molded shapes of Test Examples 1 and 2,
  • FIG. 16B is the molded shape of Test Example 3, and
  • FIG. 16C is the molded shape of Test Example 4.
  • FIG. 1 is a schematic process diagram showing a procedure for forming a glass plate into a curved shape.
  • a preheating stage 11, a forming stage 13, and a cooling stage 15 are arranged in this order, and further, a loading unit 19 that carries in a glass sheet 17 before forming into the preheating stage 11, An unloading unit 21 that carries out the glass plate 17A after molding from the cooling stage 15.
  • the glass plate 17 carried in is heated to be softened.
  • the glass plate 17 which is heated and softened in the preheating stage 11 is subjected to press forming or the like to form a desired shape.
  • the glass plate 17 formed by the forming stage 13 is gradually cooled to a temperature at which deformation is suppressed.
  • the glass plate 17 is loaded and unloaded from the loading section 19 and the unloading section 21 to each of the above stages. That is, in the loading section 19, the glass plate 17 before molding is placed on the lower mold (first molding mold) 23.
  • the lower mold 23 on which the glass plate 17 is placed is conveyed to the preheating stage 11 and heated to a predetermined temperature in the preheating stage 11.
  • the heated glass plate 17 is conveyed to the molding stage 13 together with the lower mold 23.
  • the glass plate 17 is sandwiched between the upper mold (second molding mold) 25 and the lower mold 23 mounted on the molding stage 13, and the mold is clamped. As a result, the glass plate 17 is formed into a curved shape.
  • the upper mold 25 is separated from the lower mold 23, and the processed glass plate 17A remaining in the lower mold 23 is conveyed to the cooling stage 15 together with the lower mold 23.
  • the heated glass plate 17A is gradually cooled.
  • the glass plate 17A after the slow cooling is taken out from the lower mold 23 by the unloading section 21 and carried out.
  • the glass plate 17 in the molding stage 13, in addition to press molding in which the glass plate 17 softened by heating is pressed by the lower mold 23 and the upper mold 25, the glass plate is bent by its own weight (self-weight bending molding). Adsorption of the glass plate to the molding surface of the molding die (vacuum adsorption) and pressure bonding of the glass plate to the molding surface of the molding die (compressed air molding) are combined depending on the purpose. By selectively using such a plurality of pressure sources, curved surface molding with high shape accuracy is possible. Regarding the self-weight bending, if the glass plate 17 is placed on the lower die 23 and heated, the self-weight bending of the glass plate 17 occurs, but this can be given controllability.
  • Each of the above-mentioned molding methods is the following molding method.
  • Press molding means that a glass plate is placed between predetermined molding dies (lower mold, upper mold), the glass plate is softened, and a press load is applied between the upper and lower molding dies to obtain a glass plate. It is a method of bending the resin into a mold and molding it into a predetermined shape.
  • Self-weight bend forming means that after the plate-shaped glass is placed on a predetermined forming die, the glass plate is heated to soften it, and the glass plate is bent by gravity to conform to the forming die to have a predetermined shape. It is a method of molding into.
  • a glass plate is placed on a predetermined forming die, for example, a clamp forming die is placed on the glass plate to seal the periphery of the glass plate. Then, the closed space between the molding die and the glass plate is depressurized by a pump or the like to give a differential pressure to the front and back surfaces of the glass plate for molding.
  • a glass plate is placed on a predetermined mold, and for example, a clamp mold is placed on the glass plate to seal the periphery of the glass plate. Then, a positive pressure is applied to the upper surface of the glass plate by compressed air, and a differential pressure is applied to the front and back surfaces of the glass plate to form the glass plate.
  • the glass plate that is the molded object has a thickness of, for example, 0.5 mm or more, preferably 0.7 mm or more.
  • the thickness of the glass plate is 5 mm or less, preferably 3 mm or less, more preferably 2 mm or less. Within this range, the strength of the final product is less likely to break.
  • the glass composition of the glass plate alkali-free glass, soda lime glass, soda lime silicate glass, aluminosilicate glass, borosilicate glass, lithium aluminosilicate glass, borosilicate glass can be used.
  • the glass forming apparatus of this configuration is excellent when aluminosilicate or aluminoborosilicate is used for the glass plate.
  • These glass plates have a high Young's modulus and a high expansion coefficient, and high thermal stress is generated by heating the glass plates. For this reason, the deviation from the desired bent shape of the glass plate becomes large, and the value of the compressive stress may vary when the glass plate is further strengthened. In the glass forming apparatus of this configuration, since the glass plate has these glass compositions, it is possible to reduce the shape deviation even in the bent shape and suppress the variation in the compressive stress.
  • the composition is expressed in mol% based on the oxide, SiO 2 is 50 to 80%, Al 2 O 3 is 0.1 to 25%, Li 2 O+Na 2 O+K 2 O is 3 to A glass containing 30%, 0 to 25% of MgO, 0 to 25% of CaO and 0 to 5% of ZrO 2 can be mentioned, but it is not particularly limited. More specifically, the following glass compositions may be mentioned. Note that, for example, “containing 0 to 25% of MgO” means that MgO may be contained up to 25% although it is not essential.
  • the glass (i) is included in soda lime silicate glass, and the glasses (ii) and (iii) are included in aluminosilicate glass.
  • the glass (v) is included in the silicate glass of lithium aluminum.
  • (I) With a composition expressed in mol% based on oxide, 63 to 73% of SiO 2 , 0.1 to 5.2% of Al 2 O 3 , 10 to 16% of Na 2 O, and K 2 O of Glass containing 0-1.5%, Li 2 O 0-5%, MgO 5-13% and CaO 4-10%.
  • the composition expressed in mol% based on oxide is 50 to 74% for SiO 2 , 1 to 10% for Al 2 O 3 , 6 to 14% for Na 2 O, and 3 to 11% for K 2 O.
  • the composition expressed in mol% based on the oxide is 68 to 80% for SiO 2 , 4 to 10% for Al 2 O 3 , 5 to 15% for Na 2 O, and 0 to 1% for K 2 O.
  • the composition expressed in mol% based on oxide is 67 to 75% for SiO 2 , 0 to 4% for Al 2 O 3 , 7 to 15% for Na 2 O, and 1 to 9% for K 2 O. , Li 2 O 0 to 5%, MgO 6 to 14% and ZrO 2 0 to 1.5%, the total content of SiO 2 and Al 2 O 3 is 71 to 75%, Na 2 O And a glass having a total content of K 2 O of 12 to 20% and containing CaO of less than 1%.
  • (V) the composition viewed in mole percent on the oxide basis, of SiO 2 56 - 73%, the Al 2 O 3 10 ⁇ 24% , the B 2 O 3 0 ⁇ 6% , P 2 O 5 0 to 6%, Li 2 O 2-7%, Na 2 O 3-11%, K 2 O 0-2%, MgO 0-8%, CaO 0-2%, SrO 0-5% A glass containing 0 to 5% of BaO, 0 to 5% of ZnO, 0 to 2 % of TiO 2 , and 0 to 4% of ZrO 2 .
  • FIG. 2 is a schematic configuration diagram of the molding apparatus 100.
  • FIG. 3 is a schematic plan view of the cross section along the line III-III shown in FIG. 2 as seen from above.
  • the same reference numerals are given to members and parts that have the same effect, and the description thereof may be omitted or simplified.
  • the embodiments described in the drawings are schematically illustrated to clarify the description of the present configuration, and are not accurately represented according to the actual size and scale of the product.
  • the direction from the left side to the right side in the horizontal direction is the glass plate conveyance direction TD, and the preheating stage 11, the molding stage 13, and the cooling stage 15 are arranged in this order from the upstream side of the conveyance direction TD.
  • the preheating stage 11, the molding stage 13, and the cooling stage 15 are housed in the internal space of the chamber 27.
  • the inside of the chamber 27 is purged with an inert gas such as nitrogen gas to reduce the gas concentration of the gas that adversely affects the glass molding.
  • the chamber 27 has a carry-in port 29 for carrying the glass plate and the lower mold 23 into the chamber 27, and a carry-out port 31 for carrying out the glass plate and the lower mold 23 after molding.
  • the loading section 19 shown in FIG. 1 is connected to the carry-in port 29, and the unloading section 21 shown in FIG. 1 is connected to the carry-out port 31 (not shown).
  • shutters are provided at the carry-in port 29 and the carry-out port 31, and the atmosphere in the chamber 27 is kept constant by closing the shutters except when carrying in and carrying out the glass plate.
  • a plurality of openings 101 are formed in the chamber 27, and a support shaft 37 described below is inserted into each of the openings 101.
  • the support shaft 37 and the chamber 27 are sealed with a bellows structure (not shown).
  • the chamber 27 may have a closed structure for closing the inert gas, or a semi-closed structure for constantly supplying the inert gas to make the inside of the chamber 27 at a positive pressure.
  • an upper heater (heating part for heating) 35 that heats the glass plate and the lower mold 23 to a desired heating temperature is arranged above the glass plate transport surface.
  • the upper heater 35 is preferably arranged so as to face the lower mold 23 and includes a plurality of lamp heaters 36 supported by a fixed frame (not shown) as heat sources.
  • the lamp heater 36 for example, an infrared lamp heater is used.
  • the infrared lamp heater various known heaters such as carbon lamps and halogen lamps can be used, and any heating element capable of radiant heating can be used.
  • FIG. 3 is a sectional view of the plurality of lamp heaters 36.
  • the lamp heater 36 has a heating wire 36A that generates heat when energized, and a tube material 36B such as quartz that surrounds the heating wire 36A.
  • a ceramic coat layer 40 is formed on the inner peripheral surface or the outer peripheral surface of the pipe material 36B, leaving the irradiation window 38.
  • the opening angle (center angle) ⁇ of the irradiation window 38 with the heating wire 36A as the center is determined according to the distance Ld from the center of the lamp heater 36 to the lower mold 23 that is the object to be heated and the arrangement pitch Lc of the lamp heater 36.
  • the lower die 23 is uniformly irradiated with heat rays.
  • the opening angle ⁇ is set to 60°.
  • the heating region of the upper heater 35 (the region where the lamp heaters 36 are arranged) is preferably wider than the outer edge of the lower mold 23 in the horizontal plane, in which case the entire lower mold 23 can be heated uniformly.
  • the water cooling plate 39 supported by the support shaft 37 described above is arranged above. It is desirable that a reflective film is provided on the surface of the water cooling plate 39 facing the upper heater 35. A channel for cooling water is formed in the water cooling plate 39, and the cooling water supplied and discharged through the support shaft 37 is circulated.
  • the water cooling plate 39 suppresses unnecessary heating by the upper heater 35 to surrounding members other than the lower mold 23 and the glass plate.
  • a heat diffusion plate 41 is arranged below the lower mold 23 with a gap.
  • a lower heater (heating part for heating) 43 is disposed below the heat diffusion plate 41.
  • the heat diffusion plate 41 is made of a material having excellent heat conductivity and uniformly transfers the heat generated by the lower heater 43 to the lower mold 23.
  • As the material of the heat diffusion plate 41 for example, tungsten carbide, carbon, cemented carbide, copper, iron, stainless steel material or the like can be used.
  • As the lower heater 43 a contact heating type stage heater or the like can be used, but the same radiation heating type configuration as the upper heater 35 may be used.
  • a water cooling plate 47 is arranged below the lower heater 43.
  • the water cooling plate 47 is supported by a support body 45 fixed to the lower part of the chamber 27, and suppresses unnecessary heating of the peripheral members other than the heat diffusion plate 41 and the lower mold 23 by the lower heater 43.
  • the water cooling plate 47 has the same configuration as the water cooling plate 39 described above, and cooling water is supplied and discharged from the support body 45.
  • the gap between the lower mold 23 and the heat diffusion plate 41 in the cooling stage 15 is not particularly limited, but if it is too large, the heating efficiency decreases, and if it is too small, it becomes difficult to suppress the temperature deviation of the glass plate.
  • the lower limit of the gap is 1 mm.
  • the upper limit of the gap is 10 mm.
  • a heat insulating frame 51 is arranged so as to surround the upper surface side of the lower mold 23 on which the glass plate is placed and the outer periphery of the stage on the side of the upper heater 35, the water cooling plate 39 and the support shaft 37.
  • the heat insulating frame 51 covers the side of the glass plate placed on the lower mold 23 arranged in the stage.
  • the heat insulation frame 51 for example, a heat insulation board made of a material mainly containing calcium silicate can be used. Besides, for example, a metal plate such as a stainless steel material may be used.
  • the heat insulating frame is preferably a frame having a rectangular horizontal cross section that surrounds a wide range outside the outer periphery of the lower mold 23.
  • the heat insulating frame 51 may include a lid that covers the upper portion of the frame.
  • the heat insulating frames 53 and 55 having the same configuration are arranged also in the molding stage 13 and the cooling stage 15.
  • the outer sides of the heat insulating frames 51, 53, 55 are surrounded by the chamber 27, heat inflow and outflow with the outside do not easily occur in the heat insulating frame bodies 51, 53, 55, and a more uniform temperature distribution is obtained. can get. Thereby, the thermal efficiency is improved, the processing time in each stage can be shortened, and the temperature deviation of the glass plate in each stage can be reduced.
  • a lower mold 23 is arranged on each of the preheating stage 11, the molding stage 13, and the cooling stage 15.
  • Each of the lower molds 23 is provided with a pair of mold supporting rods 61 projecting outward on side surfaces 23a and 23b on both sides orthogonal to the transport direction TD.
  • the respective mold supporting rods 61 are supported by the mold conveying units 63A and 63B arranged on both sides of the lower mold 23.
  • the mold transfer units 63A and 63B use a walking beam transfer mechanism to move the plurality of lower molds 23 arranged along each stage along the transfer direction TD. Transport.
  • FIG. 5 is a schematic explanatory view showing how the lower die 23 is conveyed in the conveying direction TD from the preheating stage 11 to the cooling stage 15.
  • the mold transfer units 63A and 63B support the mold supporting rods 61 protruding from each of the plurality of lower molds 23, and move the plurality of lower molds 23 from the preheating stage 11 to the molding stage 13 by the walking beam method. From the sheet to the cooling stage 15 at the same time.
  • the vertical displacement of the lower mold 23 during the transportation is performed within a range that does not interfere with the fixed side members such as the heat insulating frames 51, 53, 55 and the heat diffusion plate 41.
  • the cooling stage 15 shown in FIG. 2 will be described.
  • a heat diffusion plate 65 Above the lower mold 23 of the cooling stage 15, a heat diffusion plate 65, an upper heater (heating unit for lowering temperature) 67 similar to the preheating stage 11, and a water cooling plate 59 are arranged in this order.
  • the heat diffusion plate 65 has the same configuration as the heat diffusion plate 41 described above.
  • the water cooling plate 59 is fixed to the upper part of the chamber 27 and is supported by a support shaft 71 having a flow path for cooling water formed therein.
  • a heat diffusion plate 73, a lower heater (heating unit for lowering temperature) 75, and a water cooling plate 77 are arranged below the lower mold 23 of the cooling stage 15.
  • the water cooling plate 77 is supported by a support 79 fixed to the lower part of the chamber 27, and suppresses unnecessary heating of the peripheral members other than the heat diffusion plate 73 and the lower mold 23 by the lower heater 75.
  • the water cooling plate 77 has the same configuration as the water cooling plate 39 described above, and cooling water is supplied and discharged from the support 79.
  • the lower mold 23 of the cooling stage 15 and the heat diffusion plate 65 and the lower mold 23 and the heat diffusion plate 73 may be closely contacted with each other, but a temperature distribution of the lower mold 23 is provided by providing a gap. It is preferable because it can be made more uniform.
  • FIG. 6 is an enlarged sectional view of the molding stage 13.
  • the upper mold 25 Above the lower mold 23 of the molding stage 13, the upper mold 25, the heat diffusion plate 81, the upper heater (heat retaining heating unit) 83, the heat insulating plate 85, and the water cooling plate 87 are arranged in this order.
  • the upper mold 25 is connected to a plunger (not shown), and is supported so as to be movable up and down between a molding position where the lower mold 23 is clamped and a retracted position above the molding position.
  • the upper mold 25 is arranged at the retracted position except when the lower mold 23 is being conveyed, such as when it is being molded. Further, the upper mold 25 may be fixed in the molding stage 13 and the lower mold 23 may be lifted during the conveyance of the lower mold 23 to clamp the mold. In that case, the upper die moving mechanism can be omitted, and the equipment cost can be reduced.
  • the water cooling plate 87 is supported by a support shaft 89 fixed to the upper part of the chamber 27, and suppresses unnecessary heating of peripheral members other than the upper mold 25 and the heat diffusion plate 81 by the upper heater 83.
  • the water cooling plate 87 has the same configuration as the water cooling plate 39 described above, and cooling water is supplied and discharged from the support shaft 89.
  • the heat insulating plate 85 a known heat insulating material such as ceramics, stainless steel, die steel, high speed steel (high speed steel) can be used.
  • a metal-based material it is preferable that the surface be coated with CrN, TiN, TiAlN or the like.
  • the surface of the heat insulating plate 85 may have a rough structure. In that case, a minute gap is generated between the water cooling plate 39 and a higher heat insulating effect.
  • a heat diffusion plate 91, a lower heater (heating unit for heating) 93, a heat insulating plate 85, and a water cooling plate 97 are arranged in this order below the lower mold 23 of the molding stage 13.
  • the water cooling plate 97 is supported by a support 99 fixed to the lower part of the chamber 27, and suppresses unnecessary heating of the peripheral members other than the heat diffusion plate 91 and the lower mold 23 by the lower heater 93.
  • the water cooling plate 97 has the same configuration as the water cooling plate 39 described above, and cooling water is supplied and discharged from the support body 99.
  • the upper die 25 of the molding stage 13 is attached to a cylinder (not shown) that is driven in the vertical direction, and is supported so as to be vertically movable by driving the cylinder.
  • a cylinder (not shown) that is driven in the vertical direction, and is supported so as to be vertically movable by driving the cylinder.
  • an air cylinder, a hydraulic cylinder, a servo cylinder using an electric servomotor, or the like can be used.
  • the upper die 25 of the molding stage 13 is in surface contact with the heat diffusion plate 81, and heat from the upper heater 83 is evenly transferred to the upper die 25.
  • the lower die 23 of the molding stage 3 is in surface contact with the heat diffusion plate 91 so that heat from the lower heater 93 is evenly transferred to the lower die 23.
  • the upper die 25 and the heat diffusion plate 81 may be separated from each other, and the lower die and the heat diffusion plate 91 may be separated from each other.
  • FIG. 7A is a sectional view of the upper die 25, and FIG. 7B is a sectional view including the molding surface 111 of the lower die 23.
  • FIG. 8 is a rear view of the upper die 25 seen from the direction B in FIG. 7(A).
  • the upper mold 25 has an annular protrusion 113.
  • the protrusion 113 is provided on the upper die 25 corresponding to the outer edge portion of the molding surface 111 of the lower die 23 shown in FIG. 7B so as to project toward the lower die 23.
  • the protruding portion 113 has an inclined surface 113 a whose amount of protrusion gradually increases from the outer periphery of the upper mold 25 toward the center.
  • the molding surface 111 has a shape that matches the molding shape of the glass plate.
  • the lower mold 23 has a plurality of suction holes 115 for vacuum forming which are opened in the forming surface 111.
  • the suction hole 115 is connected to a suction source such as a suction pump (not shown).
  • a suction pump By driving the suction pump, the gas in the space between the lower mold 23 and the glass plate 17 is sucked at a predetermined timing to bring the glass plate 17 into close contact with the molding surface 111.
  • the lower mold 23 and the upper mold 25 can be made of materials such as carbon, stainless steel, ceramics, and cemented carbide. In particular, it is preferable to use carbon from the viewpoint of making the heat distribution uniform.
  • the upper heaters 35, 67, 83 and the lower heaters 43, 75, 93 in the preheating stage 11, the molding stage 13, and the cooling stage 15 shown in FIG. 2 are all connected to a temperature control unit (not shown), and It is set to the individual set temperature.
  • the temperature control unit realizes heating, heat retention, and gradual cooling processing at each stage by control operations such as proportional control, PI control, and PID control.
  • the glass plate transport direction TD is horizontal, but it may be a direction inclined from the horizontal direction, such as the vertical direction.
  • the lower mold 23 and the upper mold 25 may not be arranged above and below, but by adjusting the heating temperature of the glass plate and not lowering the viscosity of the glass plate too much, the lower mold is suppressed while suppressing the influence of gravity. It can be molded between 23 and the upper mold 25.
  • the glass plate 17 before molding is placed on the lower mold 23 of the loading unit 19 shown in FIG. 1 by a transfer means such as a robot arm (not shown) or manually by an operator.
  • a transfer means such as a robot arm (not shown) or manually by an operator.
  • the lower mold 23 of the loading unit 19 is transferred to the preheating stage 11 while the glass plate 17 is placed by the mold transfer units 63A and 63B shown in FIG. It is preferable that the lower mold 23 is preheated to a temperature higher than room temperature before the glass plate 17 is placed, because the heating time in the preheating stage 11 can be shortened.
  • the temperature of the lower mold 23 when the glass plate 17 is placed is preferably 300° C. or higher, and more preferably 500° C. or higher.
  • the upper heater 35 and the lower heater 43 heat the glass plate 17 on the lower mold 23 to a target heating temperature (for example, 500° C. to 700° C.).
  • the temperature suitable for press-molding the glass plate 17 depends on the composition of the glass plate 17 itself, but if the temperature is too low, the glass plate 17 will not soften sufficiently. Therefore, in the preheating stage 11, heating is performed so that the glass transition point of the glass plate 17 is preferably Tg or higher, more preferably Tg+40° C. or higher, and further preferably Tg+80° C. or higher. On the other hand, if the temperature of the glass plate 17 is too high, the glass plate 17 is excessively softened and becomes unsuitable for maintaining its shape. Therefore, in the preheating stage 11, the glass plate 17 is heated to preferably Tg+200° C. or lower, more preferably Tg+150° C. or lower, and further preferably Tg+120° C. or lower.
  • the viscosity of the glass plate 17 is preferably 5.22 ⁇ 10 11 Pa ⁇ s or more, more preferably 1.97 ⁇ 10 10 Pa ⁇ s or more, further preferably Is heated to 1.81 ⁇ 10 9 Pa ⁇ s or more.
  • the viscosity of the glass plate 17 is preferably 5.94 ⁇ 10 6 Pa ⁇ s or less, more preferably 4.16 ⁇ 10 7 Pa ⁇ s or less, and further preferably 1.65 ⁇ 10 8 Pa. -Heating so that it becomes s or less.
  • the temperature deviation of the glass plate 17 during heating in the preheating stage 11 is preferably less than 30°C, more preferably less than 20°C, and even more preferably less than 10°C.
  • the temperature distribution of the region of the lower mold 23 in contact with the glass plate 17 during heating is preferably less than 30°C, more preferably less than 25°C, and even more preferably less than 20°C.
  • the glass plate 17 heated to the target heating temperature is conveyed to the molding stage 13 together with the lower mold 23.
  • an external force such as a press is applied to the heated glass plate 17 to mold it into a desired shape.
  • the upper mold 25 arranged at the retracted position is lowered, and the glass plate 17 is sandwiched between the upper mold 25 and the lower mold 23 to mold the glass plate 17. Details of this molding process will be described later.
  • the upper heater 83 and the lower heater 93 keep the temperature of the glass plate 17 heated by the preheating stage 11 constant.
  • the temperature of the glass plate 17 in the molding stage 13 is preferably suppressed to 20° C. or less from the above-mentioned heating temperature in the preheating stage 11. Further, from the viewpoint of the surface quality of the obtained glass plate molded body, it is preferable to uniformly heat the glass plate 17 on the molding stage 13. Specifically, it is preferable that the temperature deviation of the glass plate 17 being formed by the forming stage 13 is within 20°C.
  • the upper mold 25 moves up and returns to the retracted position. Then, the lower mold 23 is conveyed to the cooling stage 15 together with the molded glass plate 17A.
  • the set temperature of the upper heater 67 and the lower heater 75 is set to a temperature lower than the target heating temperature, and the glass plate 17A and the lower mold 23 are gradually cooled.
  • the glass plate 17 is gradually cooled until the shape of the heated and molded glass plate 17A becomes stable.
  • the glass plate 17A is gradually cooled while adjusting the heating temperature by the upper heater 67 and the lower heater 75. If the cooling speed in the cooling stage 15 is too fast, the glass plate 17A is likely to be deteriorated or have a temperature deviation. Therefore, the cooling rate of the glass plate 17A in the cooling stage 15 is preferably 30° C., 20° C., more preferably 30° C., and further preferably 40° C.
  • the temperature distribution of the glass plate 17A during cooling is preferably 30° C. or lower, more preferably 25° C. or lower, and further preferably 20° C. or lower.
  • the glass plate 17A After being gradually cooled, the glass plate 17A is transferred to the outside of the chamber 27 and then taken out by the unloading section 21 as shown in FIG.
  • the glass plate 17A which is placed on a lower mold having a temperature of 300° C. or higher, preferably 500° C. or higher, after molding and slow cooling is taken out from the mold surface.
  • the glass plate 17 may be taken out by a transfer means such as a robot arm (not shown) or manually by an operator.
  • the above-mentioned uniform temperature distribution of the glass plates 17 and 17A has the effect of confining heat by the heat insulating frames 51, 53 and 55, and the high heat shielding effect from the outside by the chamber 27 outside the heat insulating frames 51, 53 and 55. Further, the heat diffusion plates 41, 65, 73, 81, 91 achieve a uniform heating effect of the heater, and other synergistic effects. Further, the radiant heating by the upper heater 35 of the preheating stage 11, the heat transfer heating from the lower heater 43, the heat transfer heating from the upper heater 83 and the lower heater 93 of the molding stage 13, and the upper heater 67 and the upper heater 67 at the time of the cooling stage. Radiation heating via the heat diffusion plates 65 and 73 by the lower heater 75 causes each stage to have a different heating form. Further, the upper heater and the lower heater of each stage can be heated at their respective set temperatures, and fine temperature control is possible.
  • the temperature distribution of the glass plates 17, 17A can be made uniform at a high level. Also, fine adjustment according to the location becomes easy, and the heat treatment as designed can be realized accurately. Further, since the heating atmosphere is covered by the heat insulating frames 51, 53, 55 and the chamber 27, the heat outflow to the outside is suppressed, and as a result, the responsiveness of the heating control and the temperature lowering control is enhanced, and the desired temperature is increased. Can be uniformly reached in a short time.
  • the die transfer parts 63A and 63B are configured to transfer the lower die 23 by the walking beam method, the moving speed between the stages can be increased. Therefore, heat loss due to heat radiation between the stages is suppressed, and the temperature distribution can be made uniform.
  • the arrangement of the heat diffusion plates 41, 65, 73, 81, 91 may be omitted depending on the molding conditions. However, by providing the heat diffusion plate, the temperature deviation of the glass plates 17, 17A in each stage Can be kept small.
  • FIG. 9 is a plan view of the glass plate 17.
  • the glass plate 17 has a glass central portion 121 inside the glass-shaped outer peripheral edge 17a and a glass outer peripheral portion 123 between the central peripheral portion 121a of the glass central portion 121 and the outer peripheral edge 17a.
  • the outer peripheral portion 123 is hatched.
  • the molding step at least a part of the glass central part 121 is molded into a curved shape.
  • FIG. 10A, FIG. 10B, and FIG. 10C are schematic steps showing stepwise a process of forming the glass plate 17 by bringing the lower mold 23 and the upper mold 25 shown in FIGS. FIG.
  • the glass plate 17 is placed on the molding surface 111 of the lower mold 23 in a state where the outer peripheral edge 17 a of the glass plate 17 is in contact.
  • the protrusion 113 of the upper mold 25 comes into contact with the glass plate 17 placed on the lower mold 23.
  • the upper die 25 has a portion that comes into contact with the glass plate 17 and a portion that does not come into contact with it, and only the inclined surface 113 a of the protrusion 113 comes into contact with the glass outer peripheral portion 123 of the glass plate 17. Then, as shown in FIG. 10B, when the upper mold 25 is further lowered, the glass plate 17 is pressed into a shape protruding downward due to the inclination of the inclined surface 113a of the protrusion 113. That is, the upper mold 25 can deform the glass plate 17 toward the lower mold 23 only by contacting the glass plate 17 in an annular shape. Further, the glass plate 17 also bends downward due to its own weight and deforms along the molding surface 111 of the lower mold 23.
  • a negative pressure is supplied from the suction holes 115 so that the glass plate 17 is vacuum-sucked to the molding surface 111.
  • the glass plate 17 comes into close contact with the molding surface 111, and the curved shape of the molding surface 111 is transferred to the glass plate 17. Therefore, even a portion where the glass plate 17 and the molding surface 111 are difficult to be brought into close contact with each other only by press molding can be surely brought into close contact, and even a complicated shape which is difficult only by press molding can be easily formed.
  • the position, number, size, etc. of the suction holes 115 are not particularly limited, but it is preferable to form the suction holes 115 in the molding surface 111 where it is difficult to bring the glass plate 17 into close contact only by press molding. Further, the size of the suction hole 115 is preferably appropriately adjusted so that the trace of the suction hole 115 does not remain on the glass plate 17 or is not conspicuous even if it remains.
  • the entire surface of the glass plate is sandwiched and formed in contact with the mold. Therefore, in order to secure the surface quality of the obtained glass plate molded product, it is molded at a relatively low temperature. Therefore, it takes a relatively long time to deform the glass plate into a desired shape. Therefore, when molding a complicated shape, it has been difficult to mold in a low temperature range where surface quality can be secured. On the other hand, when molding is performed using the lower mold 23 and the upper mold 25 having the above configuration, the upper mold 25 does not come into contact with the glass central portion 121 of the glass plate 17.
  • a glass plate molded product having excellent surface quality can be obtained without adversely affecting the glass central portion 121 such as surface roughness due to contact with the molding die.
  • the molding stage 13 having this configuration can perform molding at a relatively high temperature, the molding can be completed in a short time. That is, by using the above-mentioned molding die, a glass plate molded product having excellent surface quality can be obtained in a short time.
  • the lower mold 23 and the upper mold 25 of this configuration are molds for obtaining a glass plate molded product in which the entire glass central portion 121 is bent with a constant curvature, but the shapes of the lower mold 23 and the upper mold 25 are The shape is not limited to the illustrated example. The shapes of the lower mold 23 and the upper mold 25 can be appropriately changed according to the target shape to be molded.
  • the lower mold 23 and the upper mold 25 of this configuration realize molding that combines press molding, vacuum molding, and gravity bending by gravity, but depending on the material, molding conditions, etc., press molding and weight excluding vacuum molding can be performed. It is possible to perform molding only by molding.
  • FIG. 11 is a process explanatory view showing an outline of how the glass plate 17 is formed by the second forming method.
  • the forming die in this case has the same configuration as the forming die of the first forming method except that the gas ejection holes 125 for compressed air forming are formed inside the annular projection 113 of the upper die 25A. ..
  • the gas ejection hole 125 is usually provided in a portion of the upper die 25A that does not contact the glass plate 17.
  • the number and size of the gas ejection holes 125 are not particularly limited.
  • the protrusion 113 of the upper mold 25A is brought into contact with the glass outer peripheral portion 123 of the glass plate 17, and then the gas ejection hole is formed. Gas is ejected from 125. Then, the glass plate 17 is pressed against the molding surface 111 of the lower mold 23. That is, since the protrusion 113 is formed in an annular shape and contacts the glass plate 17 in an annular shape, a closed space 129 is formed between the molding surface 111 of the lower mold 23 and the glass plate 17. Gas is supplied to the closed space 129, and the pressure in the closed space 129 becomes positive pressure. As a result, the glass plate 17 is pressed against the molding surface 111.
  • the above-described vacuum forming and forming by gravity are performed at the same time as the above-described pressure forming, so that the glass plate 17 can be made to follow the forming surface 111 more quickly and more reliably, and it is necessary to complete forming. You can save time.
  • press molding with at least one of vacuum molding, pressure molding, and gravity bending molding, molding of a complicated shape can be easily realized and the molding time can be further shortened.
  • the vacuum forming and the pressure forming can be performed at any timing during the execution of the press forming, and the order of execution may be the order of press forming, vacuum forming and pressure forming.
  • the order of vacuum forming may be used.
  • the glass plate forming apparatus 100 may include a plurality of preheating stages 11 and a plurality of cooling stages 15.
  • FIG. 12 is a schematic configuration diagram of a molding apparatus 200 including a plurality of preheating stages 11, a molding stage 13, and a plurality of cooling stages 15.
  • the preheating stages 11 are provided at four locations (PH1 to PH4) along the transport direction TD of the lower die 23, and the cooling stages 15 are provided at four locations (C1 to C4) along the transport direction TD of the lower die 23.
  • the molding stage 13 is provided at one location (PM1) between the preheating stage 11 and the cooling stage 15.
  • the heating temperature of PH1 to PH4 of the preheating stage 11 is set stepwise along the transport direction TD.
  • the lower mold 23 and the glass plate 17 are gradually heated as they are transported in the transport direction TD, and are heated until the target heating temperature, which is the molding temperature, is reached.
  • the heating temperatures of C1 to C4 of the cooling stage 15 are set gradually low along the transport direction TD.
  • the lower mold 23 and the glass plate 17 are gradually cooled as they are transported in the transport direction TD, and are gradually cooled from the target heating temperature.
  • FIG. 13 is a graph showing an example of temperature changes of the lower mold 23 and the glass plate 17 in the preheating stage 11, the molding stage 13, and the cooling stage 15.
  • the glass plate 17 supplied to the PH1 of the preheating stage 11 from the loading unit 19 (LD) shown in FIG. 12 is placed on the lower mold 23 that has been heated to a predetermined temperature Tc in advance, and is heated from the room temperature TRM .
  • the temperature of the lower mold 23 and the glass plate 17 increases as they are conveyed to PH2, PH3, and PH4, and reaches the target heating temperature T PM which is the molding temperature before being conveyed to the molding stage 13 (PM).
  • the glass plate 17 is formed while being held at a constant target heating temperature T PM .
  • the temperature of the lower mold 23 and the glass plate 17A after molding is conveyed to C1 to C4 of the cooling stage 15 and gradually decreases.
  • the glass plate 17A transported from C4 to the unloading unit 21 (ULD) shown in FIG. 12 is naturally cooled.
  • each stage of the preheating stage 11 and the cooling stage 15 the temperature is controlled so that the lower mold 23 and the glass plates 17 and 17A are uniformly set at the respective stages.
  • the larger the number of stages the wider the range of temperature change. From the viewpoint of takt time, it is preferable to reduce the number of stages.
  • the number of each stage is appropriately set according to the size of the glass plate to be processed, the processed shape, and the like. For example, when the size of the glass plate is large or when forming a complicated shape, it is preferable to increase the number of preheating stages 11 and cooling stages 15 in order to avoid a rapid temperature change.
  • FIG. 14 is a schematic view of a conventional molding apparatus as a reference example.
  • the glass plate 17 is entirely pressed by the lower die 131 and the upper die 135, and the heating temperature is set lower than the above-described molding temperature (target set temperature). Therefore, it is necessary to hold the glass plate 17 in the mold clamped state until the molding shape becomes stable. As a result, the molding time T PM2 becomes longer than the molding time T PM1 shown in FIG.
  • the glass plate 17 is molded by combining press molding in which only the outer circumference of the glass is contacted with vacuum molding, pressure molding, and gravity molding.
  • the temperature can be set to a high temperature, and due to the synergistic effect of each molding, the glass plate comes into close contact with the molding surface of the molding die and the molding shape stabilizes quickly. That is, springback of the glass plate is less likely to occur.
  • only one molding stage 13 is required, the equipment cost can be reduced, and the throughput can be improved.
  • the time required to reach the target set temperature can be further shortened and the takt time can be shortened.
  • FIG. 15 is a schematic view of a molding apparatus 300 showing another configuration example of the molding apparatus 200 shown in FIG.
  • the molding apparatus 300 having this configuration includes a plurality of molding lines including the preheating stage 11, the molding stage 13, and the cooling stage 15 shown in FIG.
  • the molding apparatus 300 is shown in FIG. 15 as having two lines, a first molding line 141 and a second molding line 143, but may have three or more lines.
  • the loading unit 19 of the first molding line 141 of the molding apparatus 300 is connected to the unloading unit 21 of the second molding line 143, and the unloading unit 21 of the first molding line 141 is the loading unit 19 of the second molding line 143.
  • the lower mold 23 of the first molding line 141 and the lower molds 23 of the second molding line 143 are commonly used and circulate in the respective lines.
  • the installation space of the molding device 200 can be reduced, which also reduces the equipment cost.
  • the pressure Pct applied to the glass central portion 121 by pressing is 0 to 0.1 MPa
  • the pressure Peg applied to the glass outer peripheral portion 123 is It is preferably 0.1 to 10 MPa. Then, the total pressure applied to the glass sheet 17 by the press forming and the vacuum forming is such that the pressure Peg of the glass outer peripheral portion 123 is higher than the pressure Pct of the glass central portion 121 (Peg>Pct).
  • the pressure Pct applied to the glass central portion 121 by pressing is 0 to 0.1 MPa
  • the glass outer peripheral portion 123 is The applied pressure Peg is preferably 0.1 MPa to 10 MPa.
  • the total pressure applied to the glass sheet 17 by press forming, vacuum forming and pressure forming is such that the pressure Peg at the glass outer peripheral portion 123 is higher than the pressure Pct at the glass central portion 121 (Peg>Pct).
  • pressure by pressure forming is also applied to the glass central portion 121, so that the pressure applied to the glass central portion is higher than in the case of only press forming and vacuum forming.
  • the above conditions may or may not include the bending effect due to self-weight forming before and after press forming.
  • the lower limit of the temperature during molding is preferably 400° C., more preferably Tg+40° C., further preferably Tg+80° C.
  • the upper limit of the temperature during molding is preferably 750°C, more preferably 680°C, and even more preferably 650°C.
  • the molding temperature within the above range, the molded shape of the glass plate 17 can be maintained in a short time, and the molding time can be shortened.
  • the viscosity of the glass plate 17 during molding varies depending grades like of the glass plate 17 as described above, 1 ⁇ 10 -5 Pa ⁇ s or less from the viewpoint of moldability Is preferred.
  • a glass plate molded body having excellent shape accuracy can be obtained.
  • an evaluation index of the shape quality of the glass plate molded body for example, an in-plane shape deviation compared with a design shape (design surface) can be mentioned.
  • the in-plane shape deviation is a curved surface approximation such that the absolute value of the distance from the design surface in the normal direction is the minimum in the surface when the normal is set along the design shape.
  • the deviation value of the deviation amount in the normal direction between the surface approximated to the curved surface and the design surface is defined as the in-plane shape deviation.
  • the in-plane shape deviation of the glass sheet molded body obtained by the manufacturing apparatus and the molding method of this configuration is preferably 0.6 mm or less, more preferably 0.4 mm or less.
  • Table 1 collectively shows the molding conditions of the glass plate and the molding results.
  • a glass plate material: Dragon Trail (registered trademark)
  • Molding was performed by only the edge-press molding for pressing the part, and a combination of press molding and vacuum molding.
  • the molded shape of the glass plate is the test examples 1 and 2 having a single radius of curvature shown in FIG. 16A, the S-shaped test example 3 shown in FIG. This is Test Example 4 having a J-shape shown in C).
  • the radius of curvature R of Test Example 1 is 2000 mm
  • the radius of curvature R of Test Example 2 is 800 mm.
  • the radius of curvature of the S-shaped test example 3 is 2000 mm for R1, 100 mm for R2, and 2000 mm for R3 in order from one end.
  • the J-shaped test example 4 has a shape in which a flat surface is connected to a curved surface having a radius of curvature R of 50 mm.
  • the molded product obtained by each molding method was evaluated with respect to the molding takt time, shape accuracy, and surface quality.
  • the evaluation criteria are as shown below.
  • ⁇ Tact time (time required for molding) ⁇ : Less than 30 s ⁇ : 30 s or more, less than 100 s ⁇ : 100 s or more, less than 200 s ⁇ : 200 s or more, less than 500 s ⁇ : 501 s or more
  • the takt time could not be shortened in any of the test examples.
  • full-face press molding since the entire surface of the glass plate comes into contact with the molding die, the surface roughness of the glass surface after molding increases and the surface quality deteriorates.
  • the single-curved test examples 1 and 2 have good takt time and shape accuracy, and particularly excellent surface quality.
  • the takt time, the shape accuracy, and the surface quality were all NG.
  • the present invention is not limited to the above-described embodiment, and those skilled in the art can modify and apply the invention based on a combination of the configurations of the embodiments with each other, a description in the specification, and a well-known technique. This is also the scope of the present invention and is included in the scope of protection required.
  • a glass plate forming apparatus for heating a glass plate to form a desired shape A first molding die in which a molding surface having a curved shape is formed in at least a part thereof, and the glass plate is supported on the molding surface; At least one second mold clamped to the first mold; At least one preheating stage for heating the glass plate supported by the first mold; At least one molding stage in which the second molding die is arranged so as to face the first molding die, and the heated glass plate is molded between the first molding die and the second molding die; At least one cooling stage for gradually cooling the glass plate after molding, A die conveying unit that conveys the first molding die in the order of the preheating stage, the molding stage, and the cooling stage, The glass plate has a glass central portion inside the glass-shaped outer peripheral edge, and a glass outer peripheral portion between the outer periphery of the glass central portion and the glass-shaped outer peripheral edge, A glass plate forming apparatus in which the second forming die of the forming stage makes contact with
  • the glass sheet forming apparatus since the glass sheet is pressed only between the first and second forming dies with the glass outer peripheral portion, the glass center portion on the second forming die side is in contact with the die surface. There is nothing to do. Therefore, the surface quality of the central portion of the glass can be improved and molding can be performed, and molding can be performed at a higher temperature than press molding in which the molding die is in full contact with the glass surface. Thereby, the molding can be completed in a short time, and the takt time can be shortened.
  • the second molding die has an annular protrusion that protrudes toward the first molding die, and a gas ejection hole that is disposed inside the annular protrusion and ejects gas for compressed air molding.
  • a heating unit provided on the preheating stage for heating the first mold and the glass plate to a desired heating temperature A heat-retaining heating unit which is provided on the molding stage, holds the temperature of the second mold and the first mold at the heating temperature, and holds the glass plate at a desired molding temperature; A temperature lowering heating unit which is provided on the cooling stage and sets the temperature of the first mold and the glass plate to a temperature lower than the heating temperature while heating the first mold and the glass plate.
  • the glass plate forming apparatus according to any one of 1) to (4). According to this glass plate forming apparatus, the temperature of each stage can be set with high accuracy by each heating unit.
  • At least one of the preheating stage, the forming stage, and the cooling stage surrounds the outer periphery of each stage and covers the side of the glass plate supported by the first forming die arranged in the stage.
  • the glass plate forming apparatus according to any one of (1) to (9), in which a heat insulating frame is arranged. According to this glass plate forming apparatus, the inside of the region surrounded by the heat insulating frame is maintained at a uniform temperature. In addition, since the heat flow in and out of the heat insulating frame is suppressed, the responsiveness of temperature control by heating is improved.
  • the heat insulating frame is arranged on all of the preheating stage, the molding stage, and the cooling stage,
  • the glass sheet forming apparatus according to (10) further including a chamber that accommodates the preheating stage, the forming stage, and the cooling stage in an internal space. According to this glass sheet forming apparatus, the temperature control in each stage can be accurately performed, and the quality of the formed glass sheet can be improved. Further, the heat inflow and outflow of each heat insulating frame is further suppressed by the chamber, and the temperature in the region surrounded by the heat insulating frame can be made more uniform.
  • a plurality of the preheating stages are arranged along the carrying direction of the first molding die, and the heating temperature of the preheating stage is set to be high stepwise along the carrying direction (1) to (13).
  • the glass plate forming apparatus according to any one of 1. According to this glass sheet forming apparatus, since heating can be advanced stepwise while maintaining a uniform temperature distribution state in each preheating stage, heating can be performed in comparison with heating to a desired target heating temperature in one preheating stage. The temperature unevenness on the way can be reduced.
  • a plurality of the cooling stages are arranged along the carrying direction of the first molding die, and the heating temperature of the cooling stage is set to be low stepwise along the carrying direction (1) to (14).
  • the glass plate forming apparatus according to any one of 1. According to this glass plate forming apparatus, since cooling can be progressed stepwise while maintaining a uniform temperature distribution state in each cooling stage, compared with the case of cooling to a desired temperature in one cooling stage, Temperature unevenness can be reduced.
  • a plurality of the first molding dies are arranged along the preheating stage, the molding stage, and the cooling stage,
  • the glass according to any one of (1) to (15), wherein the mold conveying unit simultaneously carries in and carries out the plurality of first molding dies to the preheating stage, the molding stage, and the cooling stage, respectively.
  • Plate forming equipment According to this glass plate forming apparatus, a plurality of first forming dies and the glass plate can be conveyed at a time, so that the forming efficiency can be increased and the throughput can be improved.
  • a plurality of molding lines including the preheating stage, the molding stage, and the cooling stage are provided, In each of the molding lines, a loading unit in which the first molding die and the glass sheet before molding are carried into the preheating stage, and the first molding die and the glass sheet after molding from the cooling stage are provided. And an unloading section to be carried out, The loading section of any one of the molding lines is connected to the unloading section of another molding line different from the molding line, and the first molding die is circulated and used in a plurality of the molding lines. (16) or the glass plate forming apparatus according to (17).
  • the first forming die can be circulated in common in a plurality of forming lines, whereby the equipment cost can be reduced, and the temperature of the first forming die can be prevented from being greatly reduced from the target heating temperature. it can. Thereby, the heat stress of the first mold can be reduced. In addition, an increase in heating energy can be suppressed and running cost can be reduced.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Re-Forming, After-Treatment, Cutting And Transporting Of Glass Products (AREA)
PCT/JP2020/004190 2019-02-08 2020-02-04 ガラス板の成形装置 WO2020162467A1 (ja)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2020571221A JP7463972B2 (ja) 2019-02-08 2020-02-04 ガラス板の成形装置
CN202080010213.6A CN113329977B (zh) 2019-02-08 2020-02-04 玻璃板的成形装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-021561 2019-02-08
JP2019021561 2019-02-08

Publications (1)

Publication Number Publication Date
WO2020162467A1 true WO2020162467A1 (ja) 2020-08-13

Family

ID=71948048

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/004190 WO2020162467A1 (ja) 2019-02-08 2020-02-04 ガラス板の成形装置

Country Status (4)

Country Link
JP (1) JP7463972B2 (zh)
CN (1) CN113329977B (zh)
TW (1) TWI830867B (zh)
WO (1) WO2020162467A1 (zh)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113387551A (zh) * 2021-06-30 2021-09-14 深圳大学 一种加热装置以及辊对板热压印设备
CN114133132A (zh) * 2021-09-29 2022-03-04 芜湖长信科技股份有限公司 一种3d曲面玻璃成型模具及其成型方法
CN114560623A (zh) * 2020-11-27 2022-05-31 Daeho科技株式会社 配备摩擦防止组件的大面积成形装置
KR20230153796A (ko) * 2022-04-29 2023-11-07 김근혜 유리패널 곡면부 열성형 금형모듈 및 이를 이용한 유리패널 곡면부 열성형 시스템

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5389362A (en) * 1977-01-18 1978-08-05 Tanaka Denshi Kizai Kk Method of producing braun tube
JPS6114148A (ja) * 1984-06-29 1986-01-22 Toshiba Ceramics Co Ltd 石英ガラスの成型方法
JPH01242428A (ja) * 1988-03-24 1989-09-27 Nippon Sheet Glass Co Ltd ガラス製品の成形方法
JPH03228840A (ja) * 1990-02-02 1991-10-09 Nippon Sheet Glass Co Ltd ガラス容器の成形方法
JPH08259240A (ja) * 1995-03-22 1996-10-08 Matsushita Electric Ind Co Ltd 光学素子の成形方法および製造装置
JPH08295522A (ja) * 1995-02-27 1996-11-12 Asahi Glass Co Ltd 石英ガラス製容器及びその製造方法、製造装置
JP2018525306A (ja) * 2015-06-26 2018-09-06 コーニング インコーポレイテッド シート材を再形成するための装置および方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4711653A (en) * 1986-12-29 1987-12-08 Ppg Industries, Inc. Innovative press bending of thermoplastic sheets
US20050172671A1 (en) * 2002-06-26 2005-08-11 Hoya Corporation Methods of manufacturing molded glass articles
WO2012176813A1 (ja) * 2011-06-20 2012-12-27 旭硝子株式会社 合わせガラスの製造方法、および合わせガラス
CN103974915B (zh) * 2012-01-05 2016-06-15 旭硝子株式会社 玻璃框体的成形装置以及成形方法
CN104556644B (zh) * 2013-10-23 2017-04-12 Daeho科技株式会社 玻璃成型品成型装置
JP6359855B2 (ja) * 2014-03-31 2018-07-18 Hoya株式会社 ガラス成形体のプレス成形装置
CN207581648U (zh) * 2016-09-29 2018-07-06 Daeho科技株式会社 包括保温单元的玻璃成型装置
CN107032585B (zh) * 2017-03-17 2019-09-27 四川旭虹光电科技有限公司 3d曲面玻璃板的成型方法、以及通过该成型方法得到的3d曲面玻璃板

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5389362A (en) * 1977-01-18 1978-08-05 Tanaka Denshi Kizai Kk Method of producing braun tube
JPS6114148A (ja) * 1984-06-29 1986-01-22 Toshiba Ceramics Co Ltd 石英ガラスの成型方法
JPH01242428A (ja) * 1988-03-24 1989-09-27 Nippon Sheet Glass Co Ltd ガラス製品の成形方法
JPH03228840A (ja) * 1990-02-02 1991-10-09 Nippon Sheet Glass Co Ltd ガラス容器の成形方法
JPH08295522A (ja) * 1995-02-27 1996-11-12 Asahi Glass Co Ltd 石英ガラス製容器及びその製造方法、製造装置
JPH08259240A (ja) * 1995-03-22 1996-10-08 Matsushita Electric Ind Co Ltd 光学素子の成形方法および製造装置
JP2018525306A (ja) * 2015-06-26 2018-09-06 コーニング インコーポレイテッド シート材を再形成するための装置および方法

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114560623A (zh) * 2020-11-27 2022-05-31 Daeho科技株式会社 配备摩擦防止组件的大面积成形装置
CN113387551A (zh) * 2021-06-30 2021-09-14 深圳大学 一种加热装置以及辊对板热压印设备
CN114133132A (zh) * 2021-09-29 2022-03-04 芜湖长信科技股份有限公司 一种3d曲面玻璃成型模具及其成型方法
KR20230153796A (ko) * 2022-04-29 2023-11-07 김근혜 유리패널 곡면부 열성형 금형모듈 및 이를 이용한 유리패널 곡면부 열성형 시스템
KR102626323B1 (ko) * 2022-04-29 2024-01-17 김근혜 유리패널 곡면부 열성형 금형모듈을 이용한 유리패널 곡면부 열성형 시스템

Also Published As

Publication number Publication date
TW202039379A (zh) 2020-11-01
TWI830867B (zh) 2024-02-01
JPWO2020162467A1 (ja) 2021-12-09
CN113329977A (zh) 2021-08-31
JP7463972B2 (ja) 2024-04-09
CN113329977B (zh) 2023-02-21

Similar Documents

Publication Publication Date Title
WO2020162467A1 (ja) ガラス板の成形装置
TWI551554B (zh) The forming device and forming method of glass frame body
JP6725582B2 (ja) 成形ガラス品を形成するための方法及び装置
CN104843976B (zh) 一种3d曲面超薄玻璃弯曲成型装置和制造方法
WO2020162468A1 (ja) ガラス板の成形方法
JP2012116705A (ja) 光学素子の成形装置及び成形方法
JP3608768B2 (ja) ガラス光学素子用プレス成形装置及びガラス光学素子の成形方法
WO2013011853A1 (ja) ガラス筐体の成形装置及び成形方法
JP2011136882A (ja) 光学素子の成形装置
JP3216100B2 (ja) 精密ガラス製品の製造方法
JP5953906B2 (ja) 光学素子の成形装置及び成形方法
JP2011184248A (ja) 光学素子の成形装置
JP2013252986A (ja) 光学素子の成形装置、成形型及び光学素子の成形方法
JP2598475B2 (ja) 板ガラスの曲げ成形装置
JP2013112592A (ja) 光学素子の成形装置及び成形方法
KR101632847B1 (ko) 모바일 디스플레이용 커버 글라스 성형 장치
TW201341321A (zh) 離型片材及玻璃成形品之成形方法
JP2004010404A (ja) ガラス光学素子の製造方法
JP2014139117A (ja) 光学素子の成形方法
JPH04149035A (ja) レンズ成形装置
JPH02275722A (ja) 光学素子の成形方法及び成形装置
JP2011230970A (ja) 光学素子の成形装置
JP2011132059A (ja) 光学素子の成形装置
JP2001335329A (ja) ガラスプリフォームの浮上搬送装置
JP2003054968A (ja) 光学素子の成形方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20752469

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020571221

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20752469

Country of ref document: EP

Kind code of ref document: A1