WO2019151189A1 - ワイン用アルミニウム製容器 - Google Patents

ワイン用アルミニウム製容器 Download PDF

Info

Publication number
WO2019151189A1
WO2019151189A1 PCT/JP2019/002771 JP2019002771W WO2019151189A1 WO 2019151189 A1 WO2019151189 A1 WO 2019151189A1 JP 2019002771 W JP2019002771 W JP 2019002771W WO 2019151189 A1 WO2019151189 A1 WO 2019151189A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminum
wine
polyester resin
container
lid
Prior art date
Application number
PCT/JP2019/002771
Other languages
English (en)
French (fr)
Inventor
諭 鬼頭
信彦 永井
千晶 吉野
仁詩 竹治
悦子 八百井
Original Assignee
東洋製罐株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋製罐株式会社 filed Critical 東洋製罐株式会社
Priority to EP19748121.1A priority Critical patent/EP3747790A4/en
Priority to BR112020015645-0A priority patent/BR112020015645A2/pt
Priority to CA3089820A priority patent/CA3089820A1/en
Priority to US16/966,640 priority patent/US20210031981A1/en
Publication of WO2019151189A1 publication Critical patent/WO2019151189A1/ja

Abstract

本発明は、アルミニウム製缶体、及び該缶体の開口部を覆うアルミニウム製缶蓋とから成るワイン用アルミニウム製容器に関するものであり、前記アルミニウム製缶体の内面に、缶体の胴部において４μｍ以上の厚みを有するポリエステル樹脂被覆が形成されており、前記アルミニウム製缶蓋の内面に、６μｍ以上の厚みのポリエステル／フェノール系塗料から成る塗膜が形成されていることにより、亜硫酸を捕捉するための特別な捕捉剤を用いることなく、亜硫酸塩を含有するワインを充填・密封した場合であっても、容器の腐食の発生やワインのフレーバーを損なうことが有効に防止されている。

Description

ワイン用アルミニウム製容器
　本発明は、ワイン用アルミニウム製容器に関するものであり、より詳細には、酸化防止剤として亜硫酸塩を含有するワインを充填・密封した場合にも、容器の腐食や、ワインのフレーバーを損なうことが有効に抑制されたワイン用アルミニウム製容器に関する。
　ワインは酸化されやすく、酸化によりフレーバーが損なわれやすいことから、一般に酸素を透過しないガラス瓶に充填・密封されて保存・流通されている。その一方、ガラス瓶は重く、衝撃に弱いことから、ワインにおいても軽量で衝撃に強い容器に充填・密封されることが望まれている。
　金属製容器はガラス瓶と同様にガスバリア性に優れていると共に、遮光性を有することから、ワインを金属製容器に充填・密封することも提案されている。しかしながら、一般にワインには酸化防止剤として亜硫酸塩が含有されており、この亜硫酸が金属に対する腐蝕性が高いことから、金属に腐食を生じてしまうと共に、金属との反応により発生する硫化水素により、ワインのフレーバーが損なわれるという問題があった。
　このような金属製容器の問題を解決するために、下記特許文献１には、缶内面側に亜硫酸と反応する捕酸剤として炭酸カルシウムが添加された樹脂層が形成されたワイン缶詰用金属缶が提案されている。また下記特許文献２には、ポリエステル樹脂、フェノール樹脂及び酸化亜鉛を含有する缶胴及び缶蓋用の塗料樹脂組成物が提案されており、酸化亜鉛により亜硫酸系化合物を捕捉することにより、耐食性と内容物保持性を発揮できることが記載されている。特許文献３には、ワイン中の亜硫酸濃度を５０ｐｐｍ以下に低減することにより、金属缶の腐食やフレーバー劣化の生じないワイン缶詰が記載されている。
日本国特開２００６－６２６８８号公報 日本国特開２０１２－３１２２３号公報 日本国特開平２－７６５６５号公報
　上記特許文献１は樹脂層を透過した亜硫酸を樹脂層の接着剤層に含有させた炭酸カルシウムによって捕捉するものであるため、生産性や経済性の点において満足するものではなかった。
　また上記特許文献２記載の塗料組成物を用いる場合には、金属缶の成形後に塗膜を形成する必要があり、生産性の点で未だ十分満足するものではないと共に、上記特許文献１と同様に、亜硫酸を捕捉するための捕捉剤が必要であることから、経済性の点においても満足するものではなかった。
　上記特許文献３記載のワイン缶詰を用いる場合には、遊離亜硫酸濃度が５０ｐｐｍ以上のワインを充填できないという問題があった。
　従って本発明の目的は、亜硫酸を捕捉するための特別な捕捉剤を用いることなく、亜硫酸塩を含有するワインを充填・密封した場合であっても、容器の腐食の発生やワインのフレーバーを損なうことが有効に防止されたワイン用アルミニウム製容器を提供することである。
　本発明の他の目的は、品質低下がなく、軽量で取扱い性にも優れた容器詰めワインを提供することである。
　本発明によれば、アルミニウム製缶体、及び該缶体の開口部を覆うアルミニウム製缶蓋とから成るワイン用アルミニウム製容器において、前記アルミニウム製缶体の内面には、缶体の胴部において４μｍ以上の厚みを有するポリエステル樹脂被覆が形成されており、前記アルミニウム製缶蓋の内面には、６μｍ以上の厚みのポリエステル／フェノール系塗料から成る塗膜が形成されていることを特徴とするワイン用アルミニウム製容器が提供される。
　本発明のワイン用アルミニウム製容器においては、
１．前記ポリエステル樹脂被覆の胴部における厚みが、４～３０μｍの範囲にあること、
２．前記缶蓋の塗膜の厚みが、６～２０μｍの範囲にあること、
３．前記ポリエステル樹脂被覆が、エチレンテレフタレート系ポリエステル樹脂から成ること、
４．前記ポリエステル／フェノール系塗料が、ポリエステル樹脂を主剤、レゾール型フェノール樹脂を硬化剤とする塗料組成物から形成されていること、
５．前記缶体が、ポリエステル樹脂被覆アルミニウム板を、絞り加工・曲げ伸ばし加工及び／又はしごき加工により成形して成るシームレス缶であること、
６．前記缶蓋が、ステイオンタブ式のイージーオープン缶蓋であること、
が好適である。
　本発明によればまた、上記ワイン用アルミニウム製容器に、ワインを充填・密封して成ることを特徴とする容器詰めワインが提供される。
　本発明の容器詰めワインでは、亜硫酸塩を含有するワインが好適に充填・密封されている。
　本発明のワイン用アルミニウム製容器においては、特定の厚みのポリエステル樹脂フィルムから成る内面被覆を有するアルミニウム製缶体と、特定の厚みのポリエステル／フェノール系内面塗膜を有するアルミニウム製缶蓋とを組み合わせることにより、亜硫酸塩を含有するワインを充填・密封しても、亜硫酸がアルミニウム製缶体の樹脂被覆及びアルミニウム製缶蓋の塗膜を透過することが抑制されているため、長期に亘ってアルミニウムの腐食及びフレーバーの低下を有効に防止することが可能になる。
　しかも上記内面被覆には亜硫酸を捕捉するための捕捉剤を配合する必要がないと共に、絞りしごき加工等の過酷な加工によってもポリエステル樹脂被覆の密着不良を生じることなく、生産性や経済性にも優れており、軽量で破損のおそれがなく取扱い性に優れたワイン用アルミニウム製容器が提供できる。
　またポリエステル樹脂被覆アルミニウム製缶体は、被覆からの有機成分の溶出がほとんどなく耐溶出性に優れていることから、亜硫酸と金属との反応による硫化水素の発生が抑制されていることと相俟って、ワインのフレーバーを損なうことがない。
　本発明のワイン用アルミニウム製容器の上述した効果は、後述する実施例の結果からも明らかである。すなわち、本発明で用いるポリエステル樹脂被覆アルミニウム製缶体を用いても、エポキシ／アクリル系塗膜を有するアルミニウム製缶蓋を組み合わせて用いた場合には、塗膜厚みが上記範囲にある場合であっても、缶蓋に腐食を生じ（比較例１及び２）、ポリエステル樹脂被覆の厚みが上記範囲よりも薄い場合には、缶体の腐食は生じないが、ワインのフレーバーが低下した（比較例３）。また、缶体及び缶蓋共に、エポキシ／アクリル系塗膜を形成した場合には、ワインのフレーバーが大きく低下すると共に、缶体及び缶蓋の両方に腐食を生じた（比較例４）。本発明で用いるエポキシ／フェノール系塗膜を有するアルミニウム製缶蓋を用いても、エポキシ／アクリル製塗膜を有するアルミニウム製缶体を組み合わせで用いた場合には、ワインのフレーバーが大きく低下すると共に、缶体に腐食を生じている（比較例５）。これに対して、本発明で用いるポリエステル樹脂被覆アルミニウム製缶体とエポキシ／フェノール系塗膜を有するアルミニウム製缶蓋とを組み合わせで用いた場合には、官能評価（ワインのフレーバー性）、並びに缶体及び缶蓋の両方の耐食性において満足する結果が得られている（実施例１）。
実施例１のシームレス缶にワインを充填密封して２３℃の恒温条件下で６か月経過後の缶ネック部（Ａ）及び缶胴ストレート部（Ｂ）における内面の写真である。 比較例４のシームレス缶にワインを充填密封して２３℃の恒温条件下で６か月経過後の缶ネック部（Ａ）及び缶胴ストレート部（Ｂ）における内面の写真である。 実験例３に用いた装置を示す図である。 実験例３により測定された亜硫酸透過量を示す図である。
（ワイン用アルミニウム製容器）
　本発明のワイン用アルミニウム製容器は、アルミニウム製缶体、及び該缶体の開口部を覆うアルミニウム製缶蓋とから成り、前記アルミニウム製缶体の内面には、缶体の胴部において４μｍ以上、好適には４～３０μｍの範囲の厚みを有するポリエステル樹脂被覆が形成されており、前記アルミニウム製缶蓋の内面には、６μｍ以上、好適には６～２０μｍの範囲の厚みのポリエステル／フェノール系塗料から成る塗膜が形成されていることを特徴とする。
　アルミニウム製缶体の内面樹脂被覆の厚みが上記範囲よりも薄い場合には、亜硫酸の樹脂被覆の透過を抑制することができず、フレーバー性が低下する。一方アルミニウム製缶体の内面樹脂被覆の厚みが上記範囲よりも厚い場合には、経済性に劣るだけでなく、成形時に樹脂被覆の密着不良が生じるおそれがある。
　同様に、アルミニウム製缶蓋の内面塗膜の厚みが上記範囲よりも薄い場合には、耐食性が損なわれ、一方、アルミニウム製缶蓋の内面塗膜の厚みが上記範囲よりも厚いと経済性に劣るだけでなく、塗料だれや塗膜形成の際のブリスタの発生により、正常な塗膜を形成できず、結果として亜硫酸透過を抑制し得る塗膜を形成できないおそれがある。
［アルミニウム製缶体］
　本発明のワイン用アルミニウム製容器に使用されるアルミニウム製缶体は、缶体の胴部において４μｍ以上、好適には４～３０μｍの範囲の厚みのポリエステル樹脂被覆を有する限り、その形状や成形方法は特に限定されないが、特にポリエステル樹脂被覆アルミニウム金属板をポリエステル樹脂被覆が内面となるように成形されたシームレス缶であることが好適である。
　本発明で規定するポリエステル樹脂被覆の厚みは、缶体において樹脂被覆が最も薄い部分の厚みであり、絞り加工・しごき加工等により成形されるシームレス缶においては、ポリエステル樹脂被覆金属板が最も薄肉化されている缶体胴部における厚みであり、この部分はポリエステル樹脂被覆も過酷な成形加工により最も薄肉化されている。
　本発明のアルミニウム製缶体を成形するために用いる、ポリエステル樹脂被覆アルミニウム板は、アルミニウム板の少なくとも缶内面となる面に、後述するポリエステル樹脂を被覆して成るものである。
　アルミニウム板としては、純アルミニウム或いはアルミニウム合金から成るアルミニウム板（本明細書においては、アルミニウム合金板を含め「アルミニウム板」という）を使用することができる。
　アルミニウム板は、樹脂被覆との密着性及び耐食性を向上するために、従来公知の表面処理が施されていることが好ましく、これに限定されないが、リン酸クロメート処理、ジルコニウム含有の有機無機系表面処理等の表面処理が施されているアルミニウム板であることが好ましい。
　アルミニウム板の厚みは０．１５～０．４０ｍｍ、特に０．２０～０．３０ｍｍの厚みのものを使用することが望ましい。
　アルミニウム板に施されるポリエステル樹脂被覆を構成するポリエステル樹脂としては、芳香族カルボン酸成分の８０モル％以上、特に９０モル％以上がテレフタル酸成分から成り、アルコール成分の８０モル％以上、特に９０モル％以上がエチレングリコールから成るエチレンテレフタレート系のポリエステル樹脂（以下、単に「ＰＥＴ樹脂」ということがある）であることが好ましい。このポリエステル樹脂はホモポリエチレンテレフタレートでも、共重合ポリエステルでも、或いはこれらの２種以上のブレンド樹脂であってもよい。
　テレフタル酸成分以外のカルボン酸成分としては、イソフタル酸、ナフタレンジカルボン酸、ｐ－β－オキシエトキシ安息香酸、ビフェニル－４，４’－ジカルボン酸、ジフェノキシエタン－４，４’－ジカルボン酸、５－ナトリウムスルホイソフタル酸、ヘキサヒドロテレフタル酸、アジピン酸、セバシン酸、トリメリット酸、ピロメリット酸、ヘミメリット酸、１，１，２，２－エタンテトラカルボン酸、１，１，２－エタントリカルボン酸、１，３，５－ペンタントリカルボン酸、１，２，３，４－シクロペンタンテトロカルボン酸、ビフェニル－３，４，３’，４’－テトラカルボン酸、ダイマー酸等を挙げることができ、特にイソフタル酸、ダイマー酸を含有することが好適である。
　一方、エチレングリコール以外のアルコール成分としては、プロピレングリコール、１，４－ブタンジオール、ネオペンチルグリコール、１，６－へキシレングリコール、ジエチレングリコール、トリエチレングリコール、シクロヘキサンジメタノール、ビスフェノールＡエチレンオキサイド付加物、グリセロール、トリメチロールプロパン、ペンタエリスリトール、ジペンタエリスリトール、ソルビタン等のアルコール成分を挙げることができる。
　ポリエステル樹脂は、フィルム形成範囲の分子量を有するべきであり、溶媒としてフェノール／テトラクロロエタン混合溶媒を用いて測定した固有粘度（ＩＶ）が０．５５ｄＬ／ｇ以上、特に０．６～１．０ｄＬ／ｇの範囲にあることが腐食成分に対するバリア性や機械的性質の点でよい。
　ポリエステル樹脂被覆は、単層のみならず多層であってもよく、これに限定されないが、表層がイソフタル酸含有量が５モル％以下のホモＰＥＴ又は共重合ＰＥＴ、下層がイソフタル酸含有量が５～１５モル％、ダイマー酸含有量が１～６モル％の共重合ＰＥＴから成り、表層と下層の厚み比が２：８～８：２の範囲にある二層構成とすることもできる。
　また絞り加工・曲げ伸ばし加工及び／又はしごき加工から成形される場合には、ポリエステル樹脂被覆アルニムニウム板の状態において、ポリエステル樹脂被覆の厚みが８～３０μｍの範囲にあることが、成形後の缶体のポリエステル樹脂内面被覆の胴部における厚みを上記範囲に設定する上で好ましい。ポリエステル樹脂被覆を多層とする場合には、トータル厚みが上記厚み範囲にあることが好ましい。
　またアルミニウム板へのポリエステル樹脂の被覆は、従来公知の積層方法によって行うことができ、好適には、キャストフィルム（多層キャストフィルム）のラミネーション、または押出コート（共押出コート）により接着剤を用いることなく被覆することができるが、勿論、接着剤を用いることを制限するものではなく、アルミニウム板との接着に従来公知の接着用プライマーを用いることもできる。
　尚、ポリエステル樹脂被覆アルミニウム板の外面側は、従来公知の缶用塗料やポリエステル樹脂被覆を制限なく形成することができる。
　本発明においては、上述したポリエステル樹脂被覆アルミニウム板を、絞り加工・再絞り加工、絞り加工・曲げ伸ばし加工、絞り加工・曲げ伸ばし加工・しごき加工或いは絞り・しごき加工等の従来公知の手段に付すことによって製造することができ、特に、絞り加工・曲げ伸ばし加工及び／又はしごき加工から成形されることが好適である。缶体の薄肉化は、底部に比して胴部は曲げ伸ばし加工及び／又はしごき加工により、ポリエステル樹脂被覆アルミニウム板の素板厚の２０～９５％、特に３０～８５％の厚みになるように薄肉化されているのが好ましい。
　成形された缶体は、従来公知の方法により、トリミング加工、熱処理、ネックイン加工、フランジ加工、必要により缶体外面への印刷が施されて、後述する缶蓋巻締め用のシームレス缶とすることができる。
［アルミニウム製缶蓋］
　本発明のワイン用アルミニウム製容器に使用されるアルミニウム製缶蓋は、６μｍ以上、好適には６～２０μｍの範囲の厚みのポリエステル／フェノール系内面塗膜を有する限り、その形状や成形方法は特に限定されない。
　アルミニウム製缶蓋を成形するために用いる、ポリエステル／フェノール系塗膜を有する塗装アルミニウム板は、前述したアルミニウム製缶体の成形に用いるアルミニウム板に、主剤としてポリエステル樹脂、硬化剤としてフェノール樹脂を含有する塗料組成物を塗工して成るものである。
　本発明において、上記ポリエステル／フェノール系塗膜を形成可能な塗料組成物としては、主剤としてポリエステル樹脂、硬化剤としてフェノール樹脂を含有する塗料組成物であるかぎり、特に限定されない。
　例えば、これに限定されないが、日本国特開２００３－３２１６４６号公報に記載された、１０～３０ｍｇＫＯＨ／ｇの酸価と、３０００～１００００の数平均分子量とを有するカルボキシル基含有芳香族ポリエステル樹脂とメタクレゾールから誘導されるフェノール樹脂を含有する水性塗料組成物や、日本国特開２０１３－２４９３７６号公報に記載された、酸価が２～５０ｍｇＫＯＨ／ｇ、ガラス転移温度（Ｔｇ）が３５～１００℃であるポリエステル樹脂（Ａ）と、酸価が０～５０ｍｇＫＯＨ／ｇ、ガラス転移温度（Ｔｇ）が－２０～２５℃であるポリエステル樹脂（Ｂ）とを混合した混合ポリエステル樹脂と、該混合ポリエステル樹脂の樹脂固形分１００重量部当たり１～３０重量部のレゾール型フェノール樹脂と、全樹脂固形分１００重量部に対して１～３０重量部の量の硬化触媒とを含有する塗料組成物等、を好適に使用することができる。
　本発明においては、前述したとおり、この塗料組成物を塗膜厚が６μｍ以上、特に６～２０μｍとなるように、アルミニウム板に塗工する。用いるアルミニウム板は、アルミニウム製缶体に用いたものと同様のものを使用することができる。
　塗料組成物のアルミニウム板への塗装方法としては、特に制限はなく、従来公知の塗装方法、例えば、スプレー塗装、ロールコーター塗装、浸漬塗装等の何れの方法によっても塗装することができる。また塗膜の焼付条件としては、一般的には１００～３００℃で５秒～３０分間、好適には１５０～２７０℃で１５秒～１５分間であることが好ましい。
　本発明のアルミニウム製缶蓋は、前述した蓋素材を使用する点を除けば、それ自体公知の成形法で成形することができる。すなわち、塗装アルミニウム板を所定の形状及び寸法に打ち抜き、次いでプレス型で蓋の形に成形することができる。本発明に用いるアルミニウム製蓋は、これに限定されないが、ステイオンタブ（ＳＯＴ）式のイージーオープン蓋、フルオープンタイプのイージーオープン蓋等であり、特にＳＯＴ蓋であることが好適である。
（容器詰めワイン）
　本発明の容器詰めワインは、上述したアルミニウム製缶体及びアルミニウム製缶蓋から成る容器にワインを充填・密封して成るものであり、前述したとおり、亜硫酸塩を酸化防止剤として含有するワインであっても、容器の内面腐食がなく、ワインのフレーバーを長期に亘って損なうことがない。
　ワインは、赤、白、ロゼ等従来公知のワインを制限なく収納することができ、遊離亜硫酸濃度が５０ｐｐｍ以上であるワインも充填することができる。またスパークリングワインにも対応することができる。
（缶体の作製）
　アルミニウム板として、リン酸クロメート表面処理アルミニウム板（板厚０．２８ｍｍ）を使用した。
　この表面処理アルミニウム板を２５０℃に加熱し、その両面に、ポリエステル樹脂フィルムをラミネートロールを介して熱圧着した後、直ちに水冷することにより、ポリエステル樹脂被覆アルミニウム板を作製した。尚、缶内面側のポリエステル樹脂フィルムとしては、表１に示す厚みのイソフタル酸含有量が１０モル％の共重合ＰＥＴ樹脂フィルムを用い、缶外面側には、１０μｍ厚のイソフタル酸含有量が１２モル％の共重合ＰＥＴ樹脂フィルムを用いた。
　得られたポリエステル樹脂被覆アルミニウム板の両面に、パラフィンワックスを静電塗油した後、直径１５６ｍｍの円形に打ち抜き、浅絞りカップを作成した。次いで、この浅絞りカップを、再絞り－しごき加工及びドーミング成形を行い、開口端縁部のトリミング加工を行い、２０１℃で７５秒間、次いで２１０℃で８０秒間熱処理を施し、開口端をネッキング加工、フランジング加工を行い、缶胴２１１径でネック部２０６径の容量５００ｍｌのポリエステル樹脂被覆アルミニウム製シームレス缶を作製した。
　尚、シームレス缶は、缶体径：６６ｍｍ、缶体高さ：１６８ｍｍであり、元板厚に対する缶側壁部の平均板厚減少率：６０％である。
　また比較品として、上記表面処理アルミニウム板を、ポリエステル樹脂フィルムを被覆することなく、上記と同様にしてシームレス缶を作製した後、缶内面に表１に示す厚みのエポキシ／アクリル系塗膜を形成して、内面塗膜を有するアルミニウム製シームレス缶を作製した。
（缶蓋の作製）
　板厚０．２６ｍｍのＪＩＳ　Ａ５１８２Ｈ１９アルミニウム合金コイルに、ポリエステル／フェノール系塗料又はエポキシ／アクリル系塗料を、内面側となる面に乾燥塗膜として表１に記載した厚みとなるように、コイルコートした後、アルミニウム板のピーク温度が２６０℃で全加熱時間が２８秒となるようにガスオーブンで塗膜を焼付け、塗装アルミニウムコイルを得た。また、アルミニウム板の外面側には、内面側とは異なる種類のエポキシ／アクリル系塗料を乾燥膜厚が４μｍとなるように形成した。
　尚、ポリエステル／フェノール系塗料としては、日本国特開２０１３－２４９３７６号公報の実施例８に記載された塗料、すなわち、ガラス転移温度５０℃、酸価１５ｍｇＫＯＨ／ｇ、数平均分子量１７０００のポリエステル（Ａ）と、ガラス転移温度７℃、酸価１ｍｇＫＯＨ／ｇ、数平均分子量１８０００のポリエステル（Ｂ）とを、９０：１０の重量比で含有し、ポリエステル１００重量部に対して、架橋剤としてメタクレゾールから誘導されるレゾール型フェノール樹脂を１０重量部、硬化触媒としてアミンブロックドデシルベンゼンスルホン酸を１．０重量部で配合して成る塗料組成物を使用した。また、内面側となる面に使用したエポキシ／アクリル系塗料としては、国際公開第２０１０／０１３６５５号の実施例１に記載された塗料を使用した。
　前記塗装アルミニウムコイルを使用し、シェル（開封用タブ取付け用蓋）成形機にて、強化環状溝のラジアス部の中央パネルからの深さが２．５ｍｍ、およびラジアス部の曲率半径が０．５０ｍｍである２０６径シェルを成形した。これにリベット加工、蓋外面側からスコア加工（スコア残存厚み９５μｍ）、および開封用タブの取付けを行い、ＳＯＴ蓋を作製した。
Figure JPOXMLDOC01-appb-T000001
（実験例１）
　白ワイン（ｐＨ３．４、遊離亜硫酸濃度８０ｐｐｍ、総亜硫酸濃度２２５ｐｐｍ）を、表１に示す実施例１及び比較例４の容器にそれぞれに充填して密封した。この容器詰めワインを２３℃の恒温条件下で６ヶ月保管した後、缶内面を観察したところ、実施例１の容器では、明らかに腐食が抑えられた。
　６か月経過後の缶内面の写真（（Ａ）はネック部、（Ｂ）は缶胴ストレート部）を、図１（実施例１）及び図２（比較例４）に示す。
（実験例２）
　白ワイン（ｐＨ３．２、遊離亜硫酸濃度３０ｐｐｍ、総亜硫酸濃度１０５ｐｐｍ）を、実施例１で作製したシームレス缶に充填し、下記表２に示す内面塗膜が異なる３種のアルミニウム製缶蓋を用いて密封した。この容器詰めワインを２３℃または３７℃の恒温条件下で３ヶ月保管した後に缶蓋内面を観察したところ、ポリエステル／フェノール塗膜仕様の蓋では、明らかに腐食が抑えられた。５μｍでは３７℃恒温条件下で３か月経過後に腐食が発生し、８μｍでは２３℃および３７℃の恒温条件下で３か月経過後の腐食発生率がいずれも０であった。
Figure JPOXMLDOC01-appb-T000002
（実験例３）
　実施例１、比較例２、比較例４のシームレス缶の缶胴の内面樹脂皮膜を単離し、図３に示す球型のガラス製カラムクロマト管（アズワン社、ＯＦ－３０）を使用して、亜硫酸透過量の大小を比較した。
　フッ素ゴム製のパッキン２を介して内面樹脂被膜３をカラム１（Ａ）およびカラム１（Ｂ）で挟んで固定した後、カラム１（Ａ）に純水、カラム１（Ｂ）に亜硫酸ナトリウムを添加したクエン酸溶液（ｐＨ３．１、総亜硫酸量５００ｐｐｍに調製）を充填し、シリコンゴム製のセプタム４で封をした。
　２３℃の恒温条件下で１週間保管した後に、カラム１（Ａ）に充填された純水中の亜硫酸量を測定した。
　亜硫酸量測定には、イオンクロマトグラフ（サーモフィッシャーサイエンティフィック社、ＩＣＳ－２１００）を使用した。結果を図４に示す。
　３種の内面樹脂皮膜について評価を行ったところ、エポキシ／アクリル系塗膜を有する比較例４のシームレス缶に対して、最低膜厚が４μｍ以上のポリエステルフィルムを有する実施例１、比較例２では亜硫酸の透過を少なく抑えられた。
（実験例４）
　白ワイン（ｐＨ３．２、遊離亜硫酸濃度３０ｐｐｍ、総亜硫酸濃度１０５ｐｐｍ）を表１に示した実施例１、比較例１～５の容器に充填・密封した後、２３℃の恒温条件下で３ヶ月経時後のワインの官能評価を実施した。
　缶胴にポリエステルフィルムを使用し、その膜が厚いほど、ワインのフレーバーの低下を抑えられた。官能評価と耐食性評価の結果を表１に合わせて示した。
（実験例５）
　表１に示した実施例１と比較例４の容器に蒸留水を充填し、９０℃３０分の殺菌処理をした後に、内容液の過マンガン酸カリウム消費量を滴定法によって測定した。過マンガン酸カリウム消費量は、水中の有機物や還元性物質（被酸化性物質）を酸化させるのに必要な過マンガン酸カリウムの量であり、酸化されやすい（反応性の高い）成分の溶存量の目安となる。
　実施例１の容器では、過マンガン酸カリウム消費量が、０．１～０．２ｐｐｍであるのに対して、比較例４の容器では０．４～０．５ｐｐｍであった。比較例４のエポキシ／アクリル系塗膜を有するシームレス缶に対して、実施例１のポリエステル樹脂被覆を有するシームレス缶ではワインの風味を損なうおそれのある酸化されやすい（反応性の高い）有機成分の溶出が少ないことから、フレーバー性に優れていると考えられる。
　１（Ａ）、１（Ｂ）　カラム
　２　パッキン
　３　内面樹脂皮膜
　４　セプタム
　５　カラムクロマト管

Claims (9)

  1. 　アルミニウム製缶体、及び該缶体の開口部を覆うアルミニウム製缶蓋とから成るワイン用アルミニウム製容器において、
    　前記アルミニウム製缶体の内面には、缶体の胴部において４μｍ以上の厚みを有するポリエステル樹脂被覆が形成されており、前記アルミニウム製缶蓋の内面には、６μｍ以上の厚みのポリエステル／フェノール系塗料から成る塗膜が形成されていることを特徴とするワイン用アルミニウム製容器。
  2. 　前記ポリエステル樹脂被覆の胴部における厚みが、４～３０μｍの範囲にある請求項１記載のワイン用アルミニウム製容器。
  3. 　前記缶蓋の塗膜の厚みが、６～２０μｍの範囲にある請求項１又は２記載のワイン用アルミニウム製容器。
  4. 　前記ポリエステル樹脂被覆が、エチレンテレフタレート系ポリエステル樹脂から成る請求項１～３の何れかに記載のワイン用アルミニウム製容器。
  5. 　前記ポリエステル／フェノール系塗料が、ポリエステル樹脂を主剤、レゾール型フェノール樹脂を硬化剤とする塗料組成物から形成されている請求項１～４の何れかに記載のワイン用アルミニウム製容器。
  6. 　前記缶体が、ポリエステル樹脂被覆アルミニウム板を、絞り加工、曲げ伸ばし加工及び／又はしごき加工により成形して成るシームレス缶である請求項１～５の何れかに記載のワイン用アルミニウム製容器。
  7. 　前記缶蓋が、ステイオンタブ式のイージーオープン缶蓋である請求項１～６の何れかに記載のワイン用アルミニウム製容器。
  8. 　請求項１～７の何れかに記載のワイン用アルミニウム製容器に、ワインを充填・密封して成ることを特徴とする容器詰めワイン。
  9. 　前記ワインが亜硫酸塩を含有する請求項８記載の容器詰めワイン。
PCT/JP2019/002771 2018-02-02 2019-01-28 ワイン用アルミニウム製容器 WO2019151189A1 (ja)