WO2015051639A1 - 显示基板及其制造方法和柔性显示装置 - Google Patents
显示基板及其制造方法和柔性显示装置 Download PDFInfo
- Publication number
- WO2015051639A1 WO2015051639A1 PCT/CN2014/078013 CN2014078013W WO2015051639A1 WO 2015051639 A1 WO2015051639 A1 WO 2015051639A1 CN 2014078013 W CN2014078013 W CN 2014078013W WO 2015051639 A1 WO2015051639 A1 WO 2015051639A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- stress absorbing
- absorbing layer
- layer
- base substrate
- Prior art date
Abstract
Description
Claims