WO2012140923A1 - 不等辺山形鋼の短辺端部の成形方法、及びその装置 - Google Patents
不等辺山形鋼の短辺端部の成形方法、及びその装置 Download PDFInfo
- Publication number
- WO2012140923A1 WO2012140923A1 PCT/JP2012/050668 JP2012050668W WO2012140923A1 WO 2012140923 A1 WO2012140923 A1 WO 2012140923A1 JP 2012050668 W JP2012050668 W JP 2012050668W WO 2012140923 A1 WO2012140923 A1 WO 2012140923A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- unequal
- forming
- short side
- roller
- rolling process
- Prior art date
Abstract
短辺端部成形装置は、不等辺山形鋼の熱間圧延工程において、中間圧延工程又は仕上圧延工程を経た不等辺山形鋼(200)の短辺(201)の端部(201b)を、外周面(21)に形成した成形部(22)上をその周方向に通過させながら、該成形部(22)により押圧し成形する成形ローラ(20)を有し、成形部(22)は、成形ローラ(20)の外周面(21)の全周にわたって凹形状をなして形成され、成形ローラ(20)の軸方向に沿う形状が、円弧形状及び該円弧形状の部位(22a)に隣接する直線形状とされ、直線形状の部位(22b)は、円弧形状の部位(22a)における前記隣接する端部(22c)の接線(t)と一致する。
Description
本発明は、造船用に多用される不等辺不等厚山形鋼等の不等辺山形鋼の短辺の端部を成形する技術に関する。
従来から造船用に多用されている不等辺不等厚山形鋼は、熱間圧延によって製造されている。具体的には、熱間圧延工程において、加熱工程にて素材となる鋼片を加熱し、その後、粗圧延工程及び中間圧延工程にてそれぞれの圧延機で複数パスの成形圧延を行い、山形に近い断面形状に成形する。その後、仕上圧延工程にて、1パスの成形圧延を行い、所定の断面形状に仕上げている。
図9は、不等辺不等厚山形鋼200の形状を示す斜視図である。
図9に示すように、不等辺不等厚山形鋼200は、短辺(フランジ)201と長辺(ウエブ)202とからなり、断面が略L字形状をなしている。ここで、短辺は、長辺よりも厚くなっている。
このような不等辺不等厚山形鋼200に対して塗装を施す場合、短辺201の端部201bの端面201b1に対しても適切に塗装がなされる必要がある。
図9に示すように、不等辺不等厚山形鋼200は、短辺(フランジ)201と長辺(ウエブ)202とからなり、断面が略L字形状をなしている。ここで、短辺は、長辺よりも厚くなっている。
このような不等辺不等厚山形鋼200に対して塗装を施す場合、短辺201の端部201bの端面201b1に対しても適切に塗装がなされる必要がある。
ここで、図10A及び図10Bは、短辺の端部の形状を示す。
図10A(丸で囲んだ部位)に示すように、短辺201において、端面201b1と外側面201aとが不連続となりエッジが成形されると、塗装の際に塗装むらが発生し易くなる。なお、短辺201及び長辺202の外側面201a,202aとは、図9に示すように、曲がり部203の外側部203aを介して短辺201及び長辺202において隣接する側面である。
図10A(丸で囲んだ部位)に示すように、短辺201において、端面201b1と外側面201aとが不連続となりエッジが成形されると、塗装の際に塗装むらが発生し易くなる。なお、短辺201及び長辺202の外側面201a,202aとは、図9に示すように、曲がり部203の外側部203aを介して短辺201及び長辺202において隣接する側面である。
このような塗装むらが発生しないようにするために、図10B(丸で囲んだ部位)に示すように、短辺201において、端面201b1と外側面201aとが滑らかにつながりエッジの成形が抑制されること(好ましくはエッジが発生しないこと)が要求されている。
よって、山形鋼製品に対しては、短辺の端部の形状を厳しく管理することが要求されている。特に、短辺の端部のエッジの許容量が厳しい製品は、手入れラインに送り、冷間でエッジを許容量以下にするため、短辺の端部に対して全長にわたってグラインダ等の機械による手入れが行われている。
よって、山形鋼製品に対しては、短辺の端部の形状を厳しく管理することが要求されている。特に、短辺の端部のエッジの許容量が厳しい製品は、手入れラインに送り、冷間でエッジを許容量以下にするため、短辺の端部に対して全長にわたってグラインダ等の機械による手入れが行われている。
ここで、特許文献1に開示の耳出成形方法のように、冷間工程において研削加工により、耳出を除去する方法がある。
しかしながら、特許文献1に開示の方法では、エッジを除去するために、研削ヘッドや端部位置を検出するコントローラを有する大掛かりな装置が必要になる。
本発明の目的は、簡単な構成で、短辺の端面のエッジを滑らかに成形することである。
本発明の目的は、簡単な構成で、短辺の端面のエッジを滑らかに成形することである。
前記課題を解決するために、請求項1に係る発明は、不等辺山形鋼の熱間圧延工程において、中間圧延工程又は仕上圧延工程を経た前記不等辺山形鋼の短辺の端部を、成形ローラの外周面に形成した成形部上をその周方向に通過させながら、該成形部により押圧し成形しており、前記成形部は、前記成形ローラの外周面の全周にわたって凹形状をなして形成され、前記成形ローラの軸方向に沿う形状が、円弧形状及び該円弧形状の部位に隣接する直線形状とされ、前記直線形状の部位は、前記円弧形状の部位における前記隣接する端部の接線と一致することを特徴とする不等辺山形鋼の短辺端部の成形方法である。
また、請求項2に係る発明は、請求項1の記載において、前記中間圧延工程又は仕上圧延工程を経た前記不等辺山形鋼の前記成形ローラへの案内を、前記不等辺山形鋼の長辺の端部を拘束して、前記成形ローラによる前記短辺の端部の成形を行う前から行うことを特徴とする不等辺山形鋼の短辺端部の成形方法である。
また、請求項3に係る発明は、不等辺山形鋼の熱間圧延工程において、中間圧延工程又は仕上圧延工程を得た前記不等辺山形鋼の短辺の端部を、外周面に形成した成形部上をその周方向に通過させながら、該成形部により押圧し成形する成形ローラを有し、前記成形部は、前記成形ローラの外周面の全周にわたって凹形状をなして形成され、前記成形ローラの軸方向に沿う形状が、円弧形状及び該円弧形状の部位に隣接する直線形状とされ、前記直線形状の部位は、前記円弧形状の部位における前記隣接する端部の接線と一致することを特徴とする不等辺山形鋼の短辺端部の成形装置である。
また、請求項3に係る発明は、不等辺山形鋼の熱間圧延工程において、中間圧延工程又は仕上圧延工程を得た前記不等辺山形鋼の短辺の端部を、外周面に形成した成形部上をその周方向に通過させながら、該成形部により押圧し成形する成形ローラを有し、前記成形部は、前記成形ローラの外周面の全周にわたって凹形状をなして形成され、前記成形ローラの軸方向に沿う形状が、円弧形状及び該円弧形状の部位に隣接する直線形状とされ、前記直線形状の部位は、前記円弧形状の部位における前記隣接する端部の接線と一致することを特徴とする不等辺山形鋼の短辺端部の成形装置である。
また、請求項4に係る発明は、請求項3の記載において、前記中間圧延工程又は仕上圧延工程を経た前記不等辺山形鋼の搬送路において前記成形ローラに対して上流側に配置され、前記不等辺山形鋼の長辺の端部を拘束して前記不等辺山形鋼の前記成形ローラへの案内を行う案内部をさらに有することを特徴とする不等辺山形鋼の短辺端部の成形装置である。
本発明によれば、成形ローラの外周面の全周にわたって凹形状をなして形成され、成形ローラの軸方向に沿う形状が、円弧形状及び該円弧形状の部位に隣接する直線形状とされ、直線形状の部位が、円弧形状の部位における隣接する端部の接線と一致する成形部を有する成形ローラを、熱間圧延工程において、短辺の端部に押圧し成形するだけで、簡単な構成で、短辺の端面のエッジを滑らかに成形することができる。
(構成)
本実施形態は、不等辺不等厚山形鋼の短辺の端部成形装置(以下、単に短辺端部成形装置という。)である。
図1は、仕上圧延工程を実施するための仕上圧延装置100の後段に設置されている短辺端部成形装置10の構成を示す上面図である。
本実施形態は、不等辺不等厚山形鋼の短辺の端部成形装置(以下、単に短辺端部成形装置という。)である。
図1は、仕上圧延工程を実施するための仕上圧延装置100の後段に設置されている短辺端部成形装置10の構成を示す上面図である。
図1に示すように、短辺端部成形装置10は、短辺出側ガイド11、長辺出側ガイド12、成形ローラ(エッジ成形ローラ、成形ロール)20、及びガイドローラ30を有する。
短辺出側ガイド11及び長辺出側ガイド12は、仕上圧延工程(仕上圧延装置100)の出側において互いに対向するように配置されており、仕上圧延工程から搬送されてくる不等辺不等厚山形鋼の短辺及び長辺をそれぞれガイドする。
短辺出側ガイド11及び長辺出側ガイド12は、仕上圧延工程(仕上圧延装置100)の出側において互いに対向するように配置されており、仕上圧延工程から搬送されてくる不等辺不等厚山形鋼の短辺及び長辺をそれぞれガイドする。
成形ローラ20は、不等辺不等厚山形鋼の短辺の端部を成形する。成形ローラ20は、短辺出側ガイド11に回転自在として組み込まれている。ここで、成形ローラ20は、回転軸を垂直にして設置されている。
図2は、成形ローラ20の形状を示す正面図である。
図2に示すように、成形ローラ20は、外周が上端部から下端部近傍に向かって次第に径が小さくなっていくように縮径している(くびれている)。この成形ローラ20において、外周面21の縮径部位の下端部は、短辺の端面を成形するための成形部22をなしている。そして、成形ローラ20の下端部24は、縮径部位の下端部(成形部22)に対して拡径し、略円盤形状をなしている。この下端部24は、回転軸Oに向かって次第に厚さが増加して、その上面24aが傾斜している。
図2は、成形ローラ20の形状を示す正面図である。
図2に示すように、成形ローラ20は、外周が上端部から下端部近傍に向かって次第に径が小さくなっていくように縮径している(くびれている)。この成形ローラ20において、外周面21の縮径部位の下端部は、短辺の端面を成形するための成形部22をなしている。そして、成形ローラ20の下端部24は、縮径部位の下端部(成形部22)に対して拡径し、略円盤形状をなしている。この下端部24は、回転軸Oに向かって次第に厚さが増加して、その上面24aが傾斜している。
成形部22は、短辺の端部を成形するために、大きなラウンド形状を有する。具体的には、成形部22は、成形ローラ20の外周面21の全周にわたって凹形状をなして形成され、成形ローラ20の軸方向に沿う形状(外周面21の上下方向に沿う形状)が、円弧形状及び該円弧形状の部位(以下、円弧部という。)22aに隣接する直線形状とされている。そして、直線形状の部位(以下、平面部という。)22bは、円弧部22aにおいて隣接する端部22cの接線tと一致する。
ここで、円弧部22aは、成形する短辺の端面(201b1)が所望の形状になるように予め決められた半径を有する。また、平面部22bは、後述する不等辺不等厚山形鋼の拘束姿勢における短辺(短辺の外側面201a)の傾斜角度と略等しくなるように、予め決められた勾配(角度)を有する。なお、本実施形態では、平面部22bにおいて、円弧部22aの上端22cに対する近傍部位(下方部位)22b1は、短辺の端部の成形に実際に寄与する部位となり、その他の部位(上方部位)22b2は、短辺の端部の成形には実際に寄与せず、余裕をもって設けられた部位となる。
また、成形ローラ20の縮径部位における成形部22に隣接する上方部位(平面部22bに隣接する上方部位)は、予め決められた勾配(角度)をもって形成された逃げ部23をなしている。ここでいう予め決められた勾配とは、短辺の端部を成形する際に該短辺の外側面に逃げ部23が接触しないように逃げ角をもった勾配である。
以上のように、成形ローラ20の外周面には、円弧部22a、平面部22b、及び逃げ部23といったように、大きく分けて3つの異なる縮径部(くびれ部)が形成されている。
以上のように、成形ローラ20の外周面には、円弧部22a、平面部22b、及び逃げ部23といったように、大きく分けて3つの異なる縮径部(くびれ部)が形成されている。
一方、ガイドローラ30は、成形ローラ20が短辺の端部を成形する際の不等辺不等厚山形鋼をガイドする。ガイドローラ30は、成形ローラ20に対して搬送方向上流側に位置されるように長辺出側ガイド12に組み込まれている。このとき、ガイドローラ30は、長辺出側ガイド12に回転自在とされつつ組み込まれている。ここで、ガイドローラ30は、回転軸を垂直にして設置されている。
このように長辺出側ガイド12にガイドローラ30が組み込まれることで、このガイドローラ30と成形ローラ20とは、不等辺不等厚山形鋼の形状に応じて予め決められた距離だけ互いに離れて設置されている。
図3は、ガイドローラ30の形状を示す正面図である。
図3に示すように、ガイドローラ30は、外周が上下端それぞれから中央部に向かって径が次第に小さくなっていくように縮径されて、略鼓型又は砂時計型の形状をなしている。ガイドローラ30は、下側の略円柱形状をなす部位31の外周面31aで不等辺不等厚山形鋼の長辺の端部を拘束(支持)して、不等辺不等厚山形鋼をガイドする。
図3は、ガイドローラ30の形状を示す正面図である。
図3に示すように、ガイドローラ30は、外周が上下端それぞれから中央部に向かって径が次第に小さくなっていくように縮径されて、略鼓型又は砂時計型の形状をなしている。ガイドローラ30は、下側の略円柱形状をなす部位31の外周面31aで不等辺不等厚山形鋼の長辺の端部を拘束(支持)して、不等辺不等厚山形鋼をガイドする。
(作用、効果等)
図4は、短辺端部成形装置10が設置されている熱間圧延設備による熱間圧延工程の一例を示す。
図4に示すように、熱間圧延工程は、加熱工程(ステップS1)、粗圧延工程(ステップS2)、中間圧延工程(ステップS3)、及び仕上圧延工程(ステップS4)を有する。そして、本実施形態では、熱間圧延工程中において、仕上圧延工程(ステップS4)後に短辺の端部成形(ステップS5)を実施する。
熱間圧延工程では、加熱工程(ステップS1)にて素材となる鋼片を加熱し、その後、粗圧延工程(ステップS2)及び中間圧延工程(ステップS3)にてそれぞれの圧延機で複数パスの成形圧延を行い、山形に近い断面形状に成形する。その後、仕上圧延工程(ステップS4、図1に示す仕上圧延装置100)にて、1パスの成形圧延を行い、所定の断面形状に仕上げている。例えば、各成形圧延では、主に孔型ロールが用いられている。そして、仕上圧延工程(ステップS4)の後、短辺端部成形装置10により短辺の端部を成形する(ステップS5)。
図4は、短辺端部成形装置10が設置されている熱間圧延設備による熱間圧延工程の一例を示す。
図4に示すように、熱間圧延工程は、加熱工程(ステップS1)、粗圧延工程(ステップS2)、中間圧延工程(ステップS3)、及び仕上圧延工程(ステップS4)を有する。そして、本実施形態では、熱間圧延工程中において、仕上圧延工程(ステップS4)後に短辺の端部成形(ステップS5)を実施する。
熱間圧延工程では、加熱工程(ステップS1)にて素材となる鋼片を加熱し、その後、粗圧延工程(ステップS2)及び中間圧延工程(ステップS3)にてそれぞれの圧延機で複数パスの成形圧延を行い、山形に近い断面形状に成形する。その後、仕上圧延工程(ステップS4、図1に示す仕上圧延装置100)にて、1パスの成形圧延を行い、所定の断面形状に仕上げている。例えば、各成形圧延では、主に孔型ロールが用いられている。そして、仕上圧延工程(ステップS4)の後、短辺端部成形装置10により短辺の端部を成形する(ステップS5)。
図5A及び図5Bは、短辺端部成形装置10による短辺の端部の成形工程(ステップS5)を示す。
図5Aに示すように、先ず、ガイドローラ30は、不等辺不等厚山形鋼200の長辺202の端面202b(特に端面202b1)を拘束する。これにより、短辺出側ガイド11及び長辺出側ガイド12によるガイドも手伝って、不等辺不等厚山形鋼200の長辺202が拘束される。この結果、短辺201のパスラインが決定される。つまり、ガイドローラ30が長辺202の端部202bを拘束することで、短辺201の端部201bのパスラインが決定される。
図5Aに示すように、先ず、ガイドローラ30は、不等辺不等厚山形鋼200の長辺202の端面202b(特に端面202b1)を拘束する。これにより、短辺出側ガイド11及び長辺出側ガイド12によるガイドも手伝って、不等辺不等厚山形鋼200の長辺202が拘束される。この結果、短辺201のパスラインが決定される。つまり、ガイドローラ30が長辺202の端部202bを拘束することで、短辺201の端部201bのパスラインが決定される。
その後、図5Bに示すように、パスラインを搬送される不等辺不等厚山形鋼200は、短辺201の端部201bが、ガイドローラ30に対して搬送方向下流側にある成形ローラ20により拘束されるようになる。すなわち、不等辺不等厚山形鋼は、長辺202の端部202bがガイドローラ30により拘束されるとともに、短辺201の端部201bが成形ローラ20に拘束されるようになる。
そして、短辺201の端部201bが成形ローラ20に対して拘束されつつ通過する際に、図6に示すように、短辺201の端部201bは、成形ローラ20の円弧部22a及び平面部22bからなる成形部22により押圧されるため、円弧部22a及び平面部22b(具体的にはその下方部位22b1)に合致した形状になる。すなわち、短辺201の端面201b1は、全長において、R面として成形され、そのR面における外側面201aに隣接する端部の接線が該外側面201aと一致するようになる。つまり、短辺201の端面201b1は、全長にわたりエッジが発生せず滑らかな形状となる。
また、前述のように、本実施形態では、成形ローラ20に対して搬送路上流側にガイドローラ30を配置している。すなわち、仕上圧延工程を経た不等辺不等厚山形鋼200の成形ローラ20への案内を、成形ローラ20による短辺の端部の成形を行う前から行っている。
例えば、成形ローラ20に対して搬送路下流側にガイドローラ30を配置してしまうと、不等辺不等厚山形鋼のパスラインが不安定となり、端部の成形工程では、短辺の端部を安定して成形できなくなってしまう。このようなことから、本実施形態では、成形ローラ20に対して搬送路上流側にガイドローラ30を配置することで、短辺の端部を安定して成形することを実現している。
例えば、成形ローラ20に対して搬送路下流側にガイドローラ30を配置してしまうと、不等辺不等厚山形鋼のパスラインが不安定となり、端部の成形工程では、短辺の端部を安定して成形できなくなってしまう。このようなことから、本実施形態では、成形ローラ20に対して搬送路上流側にガイドローラ30を配置することで、短辺の端部を安定して成形することを実現している。
また、前述のように、成形ローラ20において、逃げ部23は、短辺の外側面に対して逃げ角をもつように形成されている。そのため、成形ローラ20の上方部位と短辺の外側面とが接触することによる短辺の端部の成形精度の低下を防止することができる。
また、本願発明者は、短辺の端部のエッジが熱間圧延工程で発生することを発見しており、本実施形態のように熱間圧延工程内に短辺の端部の成形工程を組み入れることで、すなわち、熱間圧延工程の一環として、仕上圧延成形後に引き続いて短辺の端部を成形するようにしたことで、エッジの発生を効率良く防止できる。
また、本願発明者は、短辺の端部のエッジが熱間圧延工程で発生することを発見しており、本実施形態のように熱間圧延工程内に短辺の端部の成形工程を組み入れることで、すなわち、熱間圧延工程の一環として、仕上圧延成形後に引き続いて短辺の端部を成形するようにしたことで、エッジの発生を効率良く防止できる。
また、仕上圧延後の不等辺不等厚山形鋼の圧延材料温度は700℃~800℃程度であるので、成形ローラ20と短辺の端面とが接する程度で、十分滑らかな端面形状に成形することができる。
図7及び図8は本実施形態に対する比較例(本実施形態のような前述の構成を有しない例)を示す。
図7及び図8は本実施形態に対する比較例(本実施形態のような前述の構成を有しない例)を示す。
図7は、成形ローラ20の円弧部22aだけで短辺201の端部201bを成形した場合である。この場合、短辺201の端部201bには、図10Aに示すようなエッジが発生してしまう。
図8は、成形ローラ20の上方部位25が短辺201の外側面201aに接触してしまう場合である。この場合、成形ローラ20の成形部22の形状をたとえ端部にエッジが発生しないような形状にしたとしても、そのような接触により所望の端面形状が得られなくなってしまう。
なお、本実施形態では、例えば、ガイドローラ30は案内部を実現している。
図8は、成形ローラ20の上方部位25が短辺201の外側面201aに接触してしまう場合である。この場合、成形ローラ20の成形部22の形状をたとえ端部にエッジが発生しないような形状にしたとしても、そのような接触により所望の端面形状が得られなくなってしまう。
なお、本実施形態では、例えば、ガイドローラ30は案内部を実現している。
(本実施形態の変形例)
本実施形態は、不等辺不等厚山形鋼に限らず、短辺の厚さと長辺の厚さとが等しい不等辺山形鋼にも適用することができる。
また、本実施形態では、短辺端部成形装置を仕上圧延装置の後段へ設置したが、それが困難な場合などでは、中間圧延工程の孔型の出側に設置してもよく、このような場合でも、仕上圧延装置の後段に設置した場合と同様な効果が得られる。
なお、一般に山形鋼は短辺および長辺の外側面(201a、202a)を上方として熱間圧延するため、以上の例では短辺端部成形装置10を図1に示す向きに設置しているが、圧延される山形鋼の向きに応じて短辺端部成形装置10が設置される向きを適宜調整することは自由である。
本実施形態は、不等辺不等厚山形鋼に限らず、短辺の厚さと長辺の厚さとが等しい不等辺山形鋼にも適用することができる。
また、本実施形態では、短辺端部成形装置を仕上圧延装置の後段へ設置したが、それが困難な場合などでは、中間圧延工程の孔型の出側に設置してもよく、このような場合でも、仕上圧延装置の後段に設置した場合と同様な効果が得られる。
なお、一般に山形鋼は短辺および長辺の外側面(201a、202a)を上方として熱間圧延するため、以上の例では短辺端部成形装置10を図1に示す向きに設置しているが、圧延される山形鋼の向きに応じて短辺端部成形装置10が設置される向きを適宜調整することは自由である。
断面形状における長辺寸法が350mm、短辺寸法が100mmの不等辺不等厚山形鋼を用いて本実施形態の成形方法により短辺の端部を成形した。
その結果、エッジの許容量が厳しい不等辺不等厚山形鋼製品を製造する際、手入れラインに送ることなく、全長にわたりエッジを許容量以下にすることができた。
その結果、エッジの許容量が厳しい不等辺不等厚山形鋼製品を製造する際、手入れラインに送ることなく、全長にわたりエッジを許容量以下にすることができた。
10 短辺端部成形装置
11 短辺出側ガイド
12 長辺出側ガイド
20 成形ローラ
21 外周面
22 成形部
22a 円弧部
22b 平面部
30 ガイドローラ
11 短辺出側ガイド
12 長辺出側ガイド
20 成形ローラ
21 外周面
22 成形部
22a 円弧部
22b 平面部
30 ガイドローラ
Claims (4)
- 不等辺山形鋼の熱間圧延工程において、中間圧延工程又は仕上圧延工程を経た前記不等辺山形鋼の短辺の端部を、成形ローラの外周面に形成した成形部上をその周方向に通過させながら、該成形部により押圧し成形しており、
前記成形部は、前記成形ローラの外周面の全周にわたって凹形状をなして形成され、前記成形ローラの軸方向に沿う形状が、円弧形状及び該円弧形状の部位に隣接する直線形状とされ、
前記直線形状の部位は、前記円弧形状の部位における前記隣接する端部の接線と一致することを特徴とする不等辺山形鋼の短辺端部の成形方法。 - 前記中間圧延工程又は仕上圧延工程を経た前記不等辺山形鋼の前記成形ローラへの案内を、前記不等辺山形鋼の長辺の端部を拘束して、前記成形ローラによる前記短辺の端部の成形を行う前から行うことを特徴とする請求項1に記載の不等辺山形鋼の短辺端部の成形方法。
- 不等辺山形鋼の熱間圧延工程において、中間圧延工程又は仕上圧延工程を得た前記不等辺山形鋼の短辺の端部を、外周面に形成した成形部上をその周方向に通過させながら、該成形部により押圧し成形する成形ローラを有し、
前記成形部は、前記成形ローラの外周面の全周にわたって凹形状をなして形成され、前記成形ローラの軸方向に沿う形状が、円弧形状及び該円弧形状の部位に隣接する直線形状とされ、
前記直線形状の部位は、前記円弧形状の部位における前記隣接する端部の接線と一致することを特徴とする不等辺山形鋼の短辺端部の成形装置。 - 前記中間圧延工程又は仕上圧延工程を経た前記不等辺山形鋼の搬送路において前記成形ローラに対して上流側に配置され、前記不等辺山形鋼の長辺の端部を拘束して前記不等辺山形鋼の前記成形ローラへの案内を行う案内部をさらに有することを特徴とする請求項3に記載の不等辺山形鋼の短辺端部の成形装置。