WO2012108766A2 - Procédé de fabrication d'une cellule solaire et cellule solaire - Google Patents
Procédé de fabrication d'une cellule solaire et cellule solaire Download PDFInfo
- Publication number
- WO2012108766A2 WO2012108766A2 PCT/NL2012/050067 NL2012050067W WO2012108766A2 WO 2012108766 A2 WO2012108766 A2 WO 2012108766A2 NL 2012050067 W NL2012050067 W NL 2012050067W WO 2012108766 A2 WO2012108766 A2 WO 2012108766A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- semiconductor substrate
- diffusion
- substrate
- layer
- region
- Prior art date
Abstract
Selon l'invention, dans la fabrication d'une cellule solaire, une couche de résistance à la diffusion (22A) de matériau isolant électriquement est disposée sur le premier côté (11) d'un substrat semi-conducteur (10), et mise sous forme de motifs selon un motif prédéterminé de régions émettrices sélectives (30) devant être appliquées dans le substrat semi-conducteur ; des espèces dopantes sont disposées dans le substrat semi-conducteur (10) pour former les régions émettrices sélectives (30) comprenant des porteurs de charge de type p. Par la suite, des régions de diffusion de dopant sélectives (31) sont créées à travers une diffusion contrôlée d'autres espèces dopantes à travers la couche de résistance à la diffusion (22a), les régions émettrices sélectives (30) et les régions de diffusion (31) fonctionnant de manière conjointe en tant qu'émetteur. La couche de résistance à la diffusion (22) s'étendra également dans n'importe quel trou traversant (20) dans le substrat (10).
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
NL2006161 | 2011-02-08 | ||
NL2006161A NL2006161C2 (en) | 2011-02-08 | 2011-02-08 | Method of manufacturing a solar cell and solar cell thus obtained. |
NL2006160A NL2006160C2 (en) | 2011-02-08 | 2011-02-08 | A method of manufacturing a solar cell and a solar cell. |
NL2006160 | 2011-02-08 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2012108766A2 true WO2012108766A2 (fr) | 2012-08-16 |
WO2012108766A3 WO2012108766A3 (fr) | 2013-01-17 |
Family
ID=45755470
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/NL2012/050067 WO2012108766A2 (fr) | 2011-02-08 | 2012-02-08 | Procédé de fabrication d'une cellule solaire et cellule solaire |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2012108766A2 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014082152A1 (fr) * | 2012-11-30 | 2014-06-05 | União Brasileira De Educação E Assistência, Mantenedora Da Pucrs | Procédé de diffusion de dopants dans des plaques de silicium pour la fabrication de cellules solaires |
WO2014179368A1 (fr) * | 2013-04-29 | 2014-11-06 | Solexel, Inc. | Réalisation de motifs par laser sans dommages de couches transparentes en vue de former des régions dopées sur un substrat de cellule solaire |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3903428A (en) | 1973-12-28 | 1975-09-02 | Hughes Aircraft Co | Solar cell contact design |
EP0985233A1 (fr) | 1997-05-30 | 2000-03-15 | Interuniversitair Micro-Elektronica Centrum Vzw | Cellule solaire et procede de fabrication de celle-ci |
WO2009050639A1 (fr) | 2007-10-16 | 2009-04-23 | Nxp B.V. | Particule comprenant un cœur et une enveloppe et ses applications |
WO2009064183A1 (fr) | 2007-11-13 | 2009-05-22 | Stichting Energieonderzoek Centrum Nederland | Procédé de fabrication de cellules solaires en silicium cristallin utilisant la codiffusion du bore et du phosphore |
WO2009067005A1 (fr) | 2007-11-19 | 2009-05-28 | Stichting Energieonderzoek Centrum Nederland | Procédé de fabrication d'une cellule photovoltaïque à contact arrière, et cellule photovoltaïque à contact arrière fabriqué par un tel procédé |
WO2010018490A2 (fr) | 2008-08-12 | 2010-02-18 | Nxp B.V. | Cellule photovoltaïque et son procédé de fabrication |
WO2010049268A1 (fr) | 2008-10-31 | 2010-05-06 | Bosch Solar Energy Ag | Cellule solaire et procédé de fabrication |
WO2010052565A2 (fr) | 2008-11-07 | 2010-05-14 | Centrotherm Photovoltaics Technology Gmbh | Procédé permettant de fabriquer une photopile à dopage à deux étapes |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060060238A1 (en) * | 2004-02-05 | 2006-03-23 | Advent Solar, Inc. | Process and fabrication methods for emitter wrap through back contact solar cells |
DE102006003283A1 (de) * | 2006-01-23 | 2007-07-26 | Gp Solar Gmbh | Verfahren zur Herstellung eines Halbleiterbauelements mit unterschiedlich stark dotierten Bereichen |
DE102007036921A1 (de) * | 2007-02-28 | 2008-09-04 | Centrotherm Photovoltaics Technology Gmbh | Verfahren zur Herstellung von Siliziumsolarzellen |
-
2012
- 2012-02-08 WO PCT/NL2012/050067 patent/WO2012108766A2/fr active Application Filing
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3903428A (en) | 1973-12-28 | 1975-09-02 | Hughes Aircraft Co | Solar cell contact design |
EP0985233A1 (fr) | 1997-05-30 | 2000-03-15 | Interuniversitair Micro-Elektronica Centrum Vzw | Cellule solaire et procede de fabrication de celle-ci |
WO2009050639A1 (fr) | 2007-10-16 | 2009-04-23 | Nxp B.V. | Particule comprenant un cœur et une enveloppe et ses applications |
WO2009064183A1 (fr) | 2007-11-13 | 2009-05-22 | Stichting Energieonderzoek Centrum Nederland | Procédé de fabrication de cellules solaires en silicium cristallin utilisant la codiffusion du bore et du phosphore |
WO2009067005A1 (fr) | 2007-11-19 | 2009-05-28 | Stichting Energieonderzoek Centrum Nederland | Procédé de fabrication d'une cellule photovoltaïque à contact arrière, et cellule photovoltaïque à contact arrière fabriqué par un tel procédé |
WO2010018490A2 (fr) | 2008-08-12 | 2010-02-18 | Nxp B.V. | Cellule photovoltaïque et son procédé de fabrication |
WO2010049268A1 (fr) | 2008-10-31 | 2010-05-06 | Bosch Solar Energy Ag | Cellule solaire et procédé de fabrication |
WO2010052565A2 (fr) | 2008-11-07 | 2010-05-14 | Centrotherm Photovoltaics Technology Gmbh | Procédé permettant de fabriquer une photopile à dopage à deux étapes |
Non-Patent Citations (1)
Title |
---|
J. SZLUFCIK ET AL., OPTO-ELECTR. REV., vol. 8, 2000, pages 299 - 305 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014082152A1 (fr) * | 2012-11-30 | 2014-06-05 | União Brasileira De Educação E Assistência, Mantenedora Da Pucrs | Procédé de diffusion de dopants dans des plaques de silicium pour la fabrication de cellules solaires |
WO2014179368A1 (fr) * | 2013-04-29 | 2014-11-06 | Solexel, Inc. | Réalisation de motifs par laser sans dommages de couches transparentes en vue de former des régions dopées sur un substrat de cellule solaire |
Also Published As
Publication number | Publication date |
---|---|
WO2012108766A3 (fr) | 2013-01-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7776727B2 (en) | Methods of emitter formation in solar cells | |
US9412895B2 (en) | Method of manufacturing photoelectric device | |
US20180277701A1 (en) | Method of Manufacturing of a Solar Cell and Solar Cell Thus Obtained | |
US7888168B2 (en) | Solar cell contact formation process using a patterned etchant material | |
WO2018147739A1 (fr) | Procédé de fabrication d'une cellule solaire passivée et cellule solaire passivée ainsi obtenue | |
US7838400B2 (en) | Rapid thermal oxide passivated solar cell with improved junction | |
TW201528344A (zh) | 使用離子佈植製造的太陽電池射極區域 | |
CN104769725A (zh) | 使用氧离子注入法形成太阳能电池中的间隔物 | |
US20180277693A1 (en) | Method of Manufacturing a Solar Cell | |
TW201826556A (zh) | 具有背側多晶矽鈍化接觸件的太陽能電池的製造方法 | |
KR20100019522A (ko) | 태양 전지를 제조하기 위한 보호층 | |
JP2012516567A (ja) | コンタクトを製造する方法、コンタクト、およびコンタクトを含む太陽電池 | |
WO2014098982A1 (fr) | Réalisation de régions émettrices de cellules solaires à l'aide de nanoparticules de silicium dopé de type n | |
US8338275B2 (en) | Methods of forming a metal contact on a silicon substrate | |
WO2012108766A2 (fr) | Procédé de fabrication d'une cellule solaire et cellule solaire | |
WO2012031649A1 (fr) | Procédé de fabrication d'une cellule solaire à contact en face arrière | |
US20120108003A1 (en) | Method for producing a solar cell | |
KR100995654B1 (ko) | 태양전지 및 그 제조방법 | |
WO2014137284A1 (fr) | Procédé de fabrication d'une cellule solaire | |
NL2021449B1 (en) | A method of manufacturing a passivated solar cell and resulting passivated solar cell | |
NL2006161C2 (en) | Method of manufacturing a solar cell and solar cell thus obtained. | |
NL2006160C2 (en) | A method of manufacturing a solar cell and a solar cell. | |
US20110036398A1 (en) | Method for manufacturing a semiconductor component | |
KR101397024B1 (ko) | 광전소자의 제조방법 | |
EP3550611A1 (fr) | Procédé de fabrication d'un dispositif photovoltaïque |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 12705490 Country of ref document: EP Kind code of ref document: A2 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 12705490 Country of ref document: EP Kind code of ref document: A2 |