WO2011132456A1 - ポリアミド化合物 - Google Patents
ポリアミド化合物 Download PDFInfo
- Publication number
- WO2011132456A1 WO2011132456A1 PCT/JP2011/053918 JP2011053918W WO2011132456A1 WO 2011132456 A1 WO2011132456 A1 WO 2011132456A1 JP 2011053918 W JP2011053918 W JP 2011053918W WO 2011132456 A1 WO2011132456 A1 WO 2011132456A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- polyamide
- mol
- polyamide compound
- group
- Prior art date
Abstract
Description
一方、コバルト等の遷移金属を含有する酸素捕捉性樹脂組成物は、透明性が必要な包装容器にも適用可能である利点を有するが、遷移金属触媒によって樹脂組成物が着色されるため好ましくない。また、これらの樹脂組成物では、遷移金属触媒によって、酸素を吸収することで樹脂が酸化される。具体的には、遷移金属原子によるポリアミド樹脂のアリーレン基に隣接するメチレン鎖から水素原子の引き抜きに起因するラジカルの発生、前記ラジカルに酸素分子が付加することによるパーオキシラジカルの発生、パーオキシラジカルによる水素原子の引き抜き等の各反応により起こるものと考えられている。このような機構による酸素吸収により樹脂が酸化されるため、分解物が発生して容器内容物に好ましくない臭気が発生したり、樹脂の酸化劣化により容器の色調や強度等が損なわれるという問題がある。
<1>下記一般式(I)で表される脂環族ジアミン単位を50モル%以上含むジアミン単位25~50モル%と、下記一般式(II-1)で表される直鎖脂肪族ジカルボン酸単位及び/又は下記一般式(II-2)で表される芳香族ジカルボン酸単位を合計で50モル%以上含むジカルボン酸単位25~50モル%と、下記一般式(III)で表される構成単位0.1~50モル%とを含有する、ポリアミド化合物。
<2>上記<1>に記載のポリアミド化合物を含むポリアミド組成物。
本発明のポリアミド化合物は、下記一般式(I)で表される脂環族ジアミン単位を50モル%以上含むジアミン単位25~50モル%と、下記一般式(II-1)で表される直鎖脂肪族ジカルボン酸単位及び/又は下記一般式(II-2)で表される芳香族ジカルボン酸単位を合計で50モル%以上含むジカルボン酸単位25~50モル%と、3級水素含有カルボン酸単位(好ましくは下記一般式(III)で表される構成単位)0.1~50モル%とを含有する。
ただし、前記ジアミン単位、前記ジカルボン酸単位、前記3級水素含有カルボン酸単位の合計は100モル%を超えないものとする。本発明のポリアミド化合物は、本発明の効果を損なわない範囲で、前記以外の構成単位をさらに含んでいてもよい。
本発明の「ポリアミド樹脂」は、本発明のポリアミド化合物において、相対粘度が1.8以上の重合体を意味する。ポリアミド樹脂は、単独で成形加工可能な材料であり、包装材料や包装容器に加工することができる。本発明のポリアミド樹脂に、必要により、他の樹脂や添加剤を添加、混合してもよく、そのようにして得たポリアミド組成物を成型加工してもよい。本発明のポリアミド樹脂は、金属を含有せずとも十分な酸素吸収性能を発現し、かつ不快な臭気が発生せず、極めて良好な透明性を有する。
本発明の「ポリアミドオリゴマー」は、本発明のポリアミド化合物において、相対粘度が1.8未満の重合体を意味する。ポリアミドオリゴマーは、単独では通常成型加工できない材料である。一般的にはオリゴマーとは数平均分子量が1000以下の重合体を指すことが多いが、本発明のポリアミドオリゴマーには、そのような一般的なオリゴマーだけでなく、数平均分子量が10000未満の重合体も包含されうる。
ジアミン単位とジカルボン酸単位との含有量の割合は、重合反応の観点から、ほぼ同量であることが好ましく、ジカルボン酸単位の含有量がジアミン単位の含有量の±2モル%であることがより好ましい。ジカルボン酸単位の含有量がジアミン単位の含有量の±2モル%の範囲を超えると、ポリアミド化合物の重合度が上がりにくくなるため重合度を上げるのに多くの時間を要し、熱劣化が生じやすくなる。
本発明のポリアミド化合物中のジアミン単位は、ポリアミド化合物に優れたガスバリア性を付与することに加え、透明性や色調の向上や、成形性を容易にする観点から、前記一般式(I)で表される脂環族ジアミン単位をジアミン単位中に50モル%以上含み、当該含有量は、好ましくは70モル%以上、より好ましくは80モル%以上、更に好ましくは90モル%以上であり、また、好ましくは100モル%以下である。
本発明のポリアミド化合物中のジカルボン酸単位は、重合時の反応性、並びにポリアミド化合物の結晶性及び成形性の観点から、前記一般式(II-1)で表される直鎖脂肪族ジカルボン酸単位及び/又は前記一般式(II-2)で表される芳香族ジカルボン酸単位を、ジカルボン酸単位に合計で50モル%以上含み、当該含有量は、好ましくは70モル%以上、より好ましくは80モル%以上、更に好ましくは90モル%以上であり、また、好ましくは100モル%以下である。
本発明のポリアミド化合物は、ポリアミド化合物に適度なガラス転移温度や結晶性を付与することに加え、包装材料や包装容器として必要な柔軟性を付与する目的の場合、前記一般式(II-1)で表される直鎖脂肪族ジカルボン酸単位を含むことが好ましい。
前記一般式(II-1)中、nは2~18の整数を表し、好ましくは3~16、より好ましくは4~12、更に好ましくは4~8である。
前記一般式(II-1)で表される直鎖脂肪族ジカルボン酸単位を構成しうる化合物としては、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、1,10-デカンジカルボン酸、1,11-ウンデカンジカルボン酸、1,12-ドデカンジカルボン酸等を例示できるが、これらに限定されるものではない。これらは単独で又は2種以上を組み合わせて用いることができる。
本発明のポリアミド化合物は、ポリアミド化合物に更なるガスバリア性を付与することに加え、包装材料や包装容器の成形加工性を容易にする目的の場合、前記一般式(II-2)で表される芳香族ジカルボン酸単位を含むことが好ましい。
前記一般式(II-2)中、Arはアリーレン基を表す。前記アリーレン基は、好ましくは炭素数6~30、より好ましくは炭素数6~15のアリーレン基であり、例えば、フェニレン基、ナフチレン基などが挙げられる。
前記一般式(II-2)で表される芳香族ジカルボン酸単位を構成しうる化合物としては、テレフタル酸、イソフタル酸、2,6-ナフタレンジカルボン酸等を例示できるが、これらに限定されるものではない。これらは単独で又は2種以上を組み合わせて用いることができる。
本発明における3級水素含有カルボン酸単位は、ポリアミド化合物の重合の観点から、アミノ基及びカルボキシル基を少なくとも1つずつ有するか、又はカルボキシル基を2つ以上有する。具体例としては、下記一般式(III)、(IV)又は(V)のいずれかで表される構成単位が挙げられる。
なお、官能基が更に置換されている場合、上述した炭素数には、更なる置換基の炭素数は含まれないものとする。例えば、ベンジル基は、フェニル基で置換された炭素数1のアルキル基と見なし、フェニル基で置換された炭素数7のアルキル基とは見なさない。以降の炭素数に記載についても、特に断りが無い限り、同様に解するものとする。
好ましいRの具体例としては、メチル基、エチル基、n-プロピル基、イソプロピル基、n-ブチル基、t-ブチル基、1-メチルプロピル基、2-メチルプロピル基、ヒドロキシメチル基、1-ヒドロキシエチル基、メルカプトメチル基、メチルスルファニルエチル基、フェニル基、ナフチル基、ベンジル基、4-ヒドロキシベンジル基等を例示できるが、これらに限定されるものではない。これらの中でも、メチル基、エチル基、2-メチルプロピル基、及びベンジル基がより好ましい。
また、前記一般式(IV)で表される構成単位を構成しうる化合物としては、3-アミノ酪酸等のβ-アミノ酸を例示でき、前記一般式(V)で表される構成単位を構成しうる化合物としては、メチルマロン酸、メチルコハク酸、リンゴ酸、酒石酸等のジカルボン酸を例示できるが、これらに限定されるものではない。
これらはD体、L体、ラセミ体のいずれであってもよく、アロ体であってもよい。また、これらは単独で又は2種以上を組み合わせて用いることができる。
本発明のポリアミド化合物は、ポリアミド化合物に柔軟性等が必要な場合には、前記ジアミン単位、前記ジカルボン酸単位及び前記3級水素含有カルボン酸単位に加えて、下記一般式(A)で表されるω-アミノカルボン酸単位を更に含有してもよい。
前記ω-アミノカルボン酸単位の含有量は、ポリアミド化合物の全構成単位中、好ましくは0.1~49.9モル%、より好ましくは3~40モル%、更に好ましくは5~35モル%である。ただし、前記のジアミン単位、ジカルボン酸単位、3級水素含有カルボン酸単位、及びω-アミノカルボン酸単位の合計は100モル%を超えないものとする。
前記一般式(A)中、pは2~18の整数を表し、好ましくは3~16、より好ましくは4~14、更に好ましくは5~12である。
本発明のポリアミド化合物の重合度については、相対粘度が使われる。本発明のポリアミド化合物の好ましい相対粘度は、好ましくは1.01~4.2である。
本発明のポリアミド化合物がポリアミド樹脂である場合、相対粘度は、成形品の外観や成形加工性の観点から、好ましくは1.8~4.2、より好ましくは1.9~4.0、更に好ましくは2.0~3.8である。但し、本発明のポリアミド樹脂を他の熱可塑性樹脂への添加剤や改質剤等に使用する場合、この範囲に限定されない。
本発明のポリアミド化合物がポリアミドオリゴマーである場合、相対粘度は、取扱い性、反応性及び熱安定性等の観点から、好ましくは1.01以上1.8未満、より好ましくは1.1~1.75、更に好ましくは1.2~1.65、特に好ましくは1.3~1.6である。
なお、ここでいう相対粘度は、ポリアミド化合物1gを96%硫酸100mLに溶解し、キャノンフェンスケ型粘度計にて25℃で測定した落下時間(t)と、同様に測定した96%硫酸そのものの落下時間(t0)の比であり、次式で示される。
相対粘度=t/t0
ポリアミド化合物の酸素吸収速度、及び酸素吸収によるポリアミド化合物の酸化劣化は、ポリアミド化合物の末端アミノ基濃度を変えることで制御することが可能である。ポリアミド化合物がポリアミド樹脂である場合、酸素吸収速度と酸化劣化のバランスの観点から、末端アミノ基濃度は5~150eq/106gの範囲が好ましく、より好ましくは10~100eq/106g、さらに好ましくは15~80eq/106gである。
本発明のポリアミド化合物は、前記ジアミン単位を構成しうるジアミン成分と、前記ジカルボン酸単位を構成しうるジカルボン酸成分と、前記3級水素含有カルボン酸単位を構成しうる3級水素含有カルボン酸成分と、必要により前記ω-アミノカルボン酸単位を構成しうるω-アミノカルボン酸成分とを重縮合させることで製造することができ、重縮合条件等を調整することで重合度を制御することができる。重縮合時に分子量調整剤として少量のモノアミンやモノカルボン酸を加えてもよい。また、重縮合反応を抑制して所望の重合度とするために、ポリアミド化合物を構成するジアミン成分とカルボン酸成分との比率(モル比)を1からずらして調整してもよい。
反応押出法は、ジアミン成分及びジカルボン酸成分からなるポリアミド(本発明のポリアミド化合物の前駆体に相当するポリアミド)又はジアミン成分、ジカルボン酸成分及びω-アミノカルボン酸成分からなるポリアミド(本発明のポリアミド化合物の前駆体に相当するポリアミド)と、3級水素含有カルボン酸成分とを押出機で溶融混練して反応させる方法である。3級水素含有カルボン酸成分をアミド交換反応により、ポリアミドの骨格中に組み込む方法であり、十分に反応させるためには、反応押出に適したスクリューを用い、L/Dの大きい2軸押出機を用いるのが好ましい。少量の3級水素含有カルボン酸成分を含むポリアミド化合物を製造する場合に、簡便な方法であり好適である。
加圧塩法は、ナイロン塩を原料として加圧下にて溶融重縮合を行う方法である。具体的には、ジアミン成分と、ジカルボン酸成分と、3級水素含有カルボン酸成分と、必要に応じてω-アミノカルボン酸成分とからなるナイロン塩水溶液を調製した後、該水溶液を濃縮し、次いで加圧下にて昇温し、縮合水を除去しながら重縮合させる。缶内を徐々に常圧に戻しながら、ポリアミド化合物の融点+10℃程度まで昇温し、保持した後、更に、-0.02MPaG まで徐々に減圧しつつ、そのままの温度で保持し、重縮合を継続する。一定の撹拌トルクに達したら、缶内を窒素で0.3MPaG程度に加圧してポリアミド化合物を回収する。
加圧塩法は、揮発性成分をモノマーとして使用する場合に有用であり、3級水素含有カルボン酸成分の共重合率が高い場合には好ましい重縮合方法である、特に、3級水素含有カルボン酸成分がポリアミド化合物を構成する全成分中に15モル%以上含まれる場合に、好適である。加圧塩法を用いることで、3級水素含有カルボン酸成分の蒸散を防ぎ、さらには、3級水素含有カルボン酸成分同士の重縮合を抑制でき、重縮合反応をスムーズに進めることが可能であるため、性状に優れたポリアミド化合物が得られる。
常圧滴下法では、常圧下にて、ジカルボン酸成分と、3級水素含有カルボン酸成分と、必要に応じてω-アミノカルボン酸成分とを加熱溶融した混合物に、ジアミン成分を連続的に滴下し、縮合水を除去しながら重縮合させる。なお、生成するポリアミド化合物の融点よりも反応温度が下回らないように、反応系を昇温しながら重縮合反応を行う。
常圧滴下法は、前記加圧塩法と比較すると、塩を溶解するための水を使用しないため、バッチ当たりの収量が大きく、また、原料成分の気化・凝縮を必要としないため、反応速度の低下が少なく、工程時間を短縮できる。
加圧滴下法では、まず、重縮合缶にジカルボン酸成分と、3級水素含有カルボン酸成分と、必要に応じてω-アミノカルボン酸成分とを仕込み、各成分を撹拌して溶融混合し混合物を調製する。次いで、缶内を好ましくは0.3~0.4MPaG程度に加圧しながら混合物にジアミン成分を連続的に滴下し、縮合水を除去しながら重縮合させる。この際、生成するポリアミド化合物の融点よりも反応温度が下回らないように、反応系を昇温しながら重縮合反応を行う。設定モル比に達したらジアミン成分の滴下を終了し、缶内を徐々に常圧に戻しながら、ポリアミド化合物の融点+10℃程度まで昇温し、保持した後、更に、-0.02MPaGまで徐々に減圧しつつ、そのままの温度で保持し、重縮合を継続する。一定の撹拌トルクに達したら、缶内を窒素で0.3MPaG程度に加圧してポリアミド化合物を回収する。
加圧滴下法は、加圧塩法と同様に、揮発性成分をモノマーとして使用する場合に有用であり、3級水素含有カルボン酸成分の共重合率が高い場合には好ましい重縮合方法である。特に、3級水素含有カルボン酸成分がポリアミド化合物を構成する全成分中に15モル%以上含まれる場合に、好適である。加圧滴下法を用いることで3級水素含有カルボン酸成分の蒸散を防ぎ、さらには、3級水素含有カルボン酸成分同士の重縮合を抑制でき、重縮合反応をスムーズに進めることが可能であるため、性状に優れたポリアミド化合物が得られる。さらに、加圧滴下法は、加圧塩法に比べて、塩を溶解するための水を使用しないため、バッチ当たりの収量が大きく、常圧滴下法と同様に反応時間を短くできることから、ゲル化等を抑制し、黄色度が低いポリアミド化合物を得ることができる。
上記重縮合方法で製造されたポリアミド化合物は、そのまま使用することもできるが、更に重合度を高めるための工程を経てもよい。更に重合度を高める工程としては、押出機内での反応押出や固相重合等が挙げられる。固相重合で用いられる加熱装置としては、連続式の加熱乾燥装置やタンブルドライヤー、コニカルドライヤー、ロータリードライヤー等と称される回転ドラム式の加熱装置およびナウタミキサーと称される内部に回転翼を備えた円錐型の加熱装置が好適に使用できるが、これらに限定されることなく公知の方法、装置を使用することができる。特にポリアミド化合物の固相重合を行う場合は、上述の装置の中で回転ドラム式の加熱装置が、系内を密閉化でき、着色の原因となる酸素を除去した状態で重縮合を進めやすいことから好ましく用いられる。
本発明のポリアミド化合物の重縮合においては、アミド化反応を促進する観点から、リン原子含有化合物を添加することが好ましい。
リン原子含有化合物としては、ジメチルホスフィン酸、フェニルメチルホスフィン酸等のホスフィン酸化合物;次亜リン酸、次亜リン酸ナトリウム、次亜リン酸カリウム、次亜リン酸リチウム、次亜リン酸マグネシウム、次亜リン酸カルシウム、次亜リン酸エチル等のジ亜リン酸化合物;ホスホン酸、ホスホン酸ナトリウム、ホスホン酸カリウム、ホスホン酸リチウム、ホスホン酸カリウム、ホスホン酸マグネシウム、ホスホン酸カルシウム、フェニルホスホン酸、エチルホスホン酸、フェニルホスホン酸ナトリウム、フェニルホスホン酸カリウム、フェニルホスホン酸リチウム、フェニルホスホン酸ジエチル、エチルホスホン酸ナトリウム、エチルホスホン酸カリウム等のホスホン酸化合物;亜ホスホン酸、亜ホスホン酸ナトリウム、亜ホスホン酸リチウム、亜ホスホン酸カリウム、亜ホスホン酸マグネシウム、亜ホスホン酸カルシウム、フェニル亜ホスホン酸、フェニル亜ホスホン酸ナトリウム、フェニル亜ホスホン酸カリウム、フェニル亜ホスホン酸リチウム、フェニル亜ホスホン酸エチル等の亜ホスホン酸化合物;亜リン酸、亜リン酸水素ナトリウム、亜リン酸ナトリウム、亜リン酸リチウム、亜リン酸カリウム、亜リン酸マグネシウム、亜リン酸カルシウム、亜リン酸トリエチル、亜リン酸トリフェニル、ピロ亜リン酸等の亜リン酸化合物等が挙げられる。
これらの中でも特に次亜リン酸ナトリウム、次亜リン酸カリウム、次亜リン酸リチウム等の次亜リン酸金属塩が、アミド化反応を促進する効果が高くかつ着色防止効果にも優れるため好ましく用いられ、特に次亜リン酸ナトリウムが好ましい。なお、本発明で使用できるリン原子含有化合物はこれらの化合物に限定されない。
リン原子含有化合物の添加量は、ポリアミド化合物中のリン原子濃度換算で0.1~1000ppmであることが好ましく、より好ましくは1~600ppmであり、さらに好ましくは5~400ppmである。0.1ppm以上であれば、重合中にポリアミド化合物が着色しにくく透明性が高くなる。1000ppm以下であれば、ポリアミド化合物がゲル化しにくく、また、リン原子含有化合物に起因すると考えられるフィッシュアイの成形品中への混入も低減でき、成形品の外観が良好となる。
アルカリ金属化合物としては、アルカリ金属水酸化物やアルカリ金属酢酸塩、アルカリ金属炭酸塩、アルカリ金属アルコキシド等が好ましい。本発明で用いることのできるアルカリ金属化合物の具体例としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウム、水酸化ルビジウム、水酸化セシウム、酢酸リチウム、酢酸ナトリウム、酢酸カリウム、酢酸ルビジウム、酢酸セシウム、ナトリウムメトキシド、ナトリウムエトキシド、ナトリウムプロポキシド、ナトリウムブトキシド、カリウムメトキシド、リチウムメトキシド、炭酸ナトリウム等が挙げられるが、これらの化合物に限定されることなく用いることができる。なお、リン原子含有化合物とアルカリ金属化合物の比率(モル比)は、重合速度制御の観点や、黄色度を低減する観点から、リン原子含有化合物/アルカリ金属化合物=1.0/0.05~1.0/1.5の範囲が好ましく、より好ましくは、1.0/0.1~1.0/1.2、さらに好ましくは、1.0/0.2~1.0/1.1である。
本発明のポリアミド組成物は、本発明のポリアミド化合物を含有する組成物である。本発明のポリアミド組成物は、本発明のポリアミド樹脂やポリアミドオリゴマーに、種々の添加剤や種々の樹脂を添加、混合することで得られる混合物であり、当該混合物中において、ポリアミド樹脂やポリアミドオリゴマーは、添加した添加剤や樹脂と、反応していてもよい。
本発明のポリアミド化合物に、要求される用途や性能に応じて、滑剤、結晶化核剤、白化防止剤、艶消剤、耐熱安定剤、耐候安定剤、紫外線吸収剤、可塑剤、難燃剤、帯電防止剤、着色防止剤、酸化防止剤、耐衝撃性改良材等の添加剤を添加させてポリアミド組成物としてもよい。これらの添加剤は、本発明の効果を損なわない範囲で、必要に応じて添加することができる。
本発明のポリアミド組成物においては、熱水処理後や長時間の経時後の白化抑制として、ジアミド化合物及び/又はジエステル化合物をポリアミド化合物に添加することが好ましい。ジアミド化合物及び/又はジエステル化合物は、オリゴマーの析出による白化の抑制に効果がある。ジアミド化合物とジエステル化合物を単独で用いてもよいし、併用してもよい。
炭素数8~30の脂肪族ジカルボン酸と主としてエチレンジアミンから成るジアミンから得られるジアミド化合物、または、主としてモンタン酸から成る脂肪族ジカルボン酸と炭素数2~10のジアミンから得られるジアミド化合物が好ましく、特に好ましくは主としてステアリン酸から成る脂肪族ジカルボン酸と主としてエチレンジアミンから成るジアミンから得られるジアミド化合物である。
前記脂肪族ジカルボン酸としては、ステアリン酸(C18)、エイコサン酸(C20)、ベヘン酸(C22)、モンタン酸(C28)、トリアコンタン酸(C30)等が例示できる。前記ジオールとしては、エチレングリコール、プロパンジオール、ブタンジオール、ヘキサンジオール、キシリレングリコール、シクロヘキサンジメタノール等が例示できる。これらを組み合わせて得られるジエステル化合物が好ましい。
特に好ましくは主としてモンタン酸から成る脂肪族ジカルボン酸と主としてエチレングリコール及び/又は1,3-ブタンジオールから成るジオールから得られるジエステル化合物である。
本発明のポリアミド組成物は、透明性を改善する観点から、結晶化核剤を添加することが好ましい。透明性を改善するだけでなく、熱水処理後や長時間の経時後の結晶化による白化にも効果があり、結晶化核剤をポリアミド化合物に添加することにより、球晶サイズを可視光の波長の1/2以下にすることで抑制できる。また、ジアミド化合物および/またはジエステル化合物と結晶化核剤を併用すると、これらの相乗効果により、それぞれの白化抑制効果から予想される程度よりはるかに優れた白化抑制が得られる。
本発明のポリアミド組成物においては、ポリアミド化合物に、酢酸ナトリウム、酢酸カルシウム、酢酸マグネシウム、ステアリン酸カルシウム、ステアリン酸マグネシウム、ステアリン酸ナトリウムおよびそれらの誘導体から選択される1種以上のカルボン酸塩類を添加することが好ましい。ここで該誘導体としては、12-ヒドロキシステアリン酸カルシウム、12-ヒドロキシステアリン酸マグネシウム、12-ヒドロキシステアリン酸ナトリウム等の12-ヒドロキシステアリン酸金属塩等が挙げられる。前記カルボン酸塩類を添加することで、成形加工中に起こるポリアミド化合物のゲル化防止や成型体中のフィッシュアイを低減することができ、成形加工の適性が向上する。
本発明のポリアミド組成物は、酸素吸収性能を制御する観点や機械物性低下を抑える観点から酸化防止剤を含有することが好ましい。酸化防止剤としては、銅系酸化防止剤、ヒンダードフェノール系酸化防止剤、ヒンダードアミン系酸化防止剤、リン系酸化防止剤、チオ系酸化防止剤等を例示することができ、中でもヒンダードフェノール系酸化防止剤、リン系酸化防止剤が好ましい。
本発明のポリアミド化合物を含有するアミド組成物においては、耐衝撃性、フィルムの耐ピンホール性、柔軟性を改善するため耐衝撃性改良材を加えてもよい。耐衝撃性改良材としては、ポリオレフィン、ポリアミドエラストマー、スチレン-ブタジエン共重合樹脂の水素添加処理物、アイオノマー、エチレン-エチルアクリレート共重合樹脂、エチレン-エチルアクリレート共重合樹脂の無水マレイン酸変性品、エチレン-メタクリル酸共重合樹脂、ナイロン6,66,12、ナイロン12、ナイロン12エラストマー、エチレン-プロピレン共重合エラストマー、ポリエステルエラストマー等を添加することができる。耐衝撃性改良材の添加量は1~10質量%が好ましく、1~5質量%が更に好ましく、2~3質量%が特に好ましい。添加量が多いと、透明性、ガスバリア性が低下する。添加量が少ないと、耐衝撃性、フィルムの耐ピンホール性、柔軟性があまり改善されない。
本発明のポリアミド化合物を、要求される用途や性能に応じて、種々の樹脂と混合してポリアミド組成物としてもよい。本発明のポリアミド化合物と混合する樹脂としては、特に限定されないが、ポリオレフィン、ポリエステル、ポリアミド、ポリビニルアルコール及び植物由来樹脂からなる群から選ばれる少なくとも1種であることが好ましい。
これらの中でも、酸素吸収効果を効果的に発揮するためには、ポリエステル、ポリアミド及びポリビニルアルコールのような酸素バリア性の高い樹脂とのブレンドが好ましい。
ポリオレフィンの具体例としては、ポリエチレン、ポリプロピレン、ポリブテン-1、ポリ-4-メチルペンテン-1等のオレフィン単独重合体;エチレン-プロピレンランダム共重合体、エチレン-プロピレンブロック共重合体、エチレン-プロピレン-ポリブテン-1共重合体、エチレン-環状オレフィン共重合体等のエチレンとα-オレフィンとの共重合体;エチレン-α,β-不飽和カルボン酸共重合体、エチレン-α,β-不飽和カルボン酸エステル共重合体、エチレン-α,β-不飽和カルボン酸共重合体のイオン架橋物、エチレン-酢酸ビニル共重合体、エチレン-酢酸ビニル共重合体の部分又は完全鹸化物等のその他のエチレン共重合体;これらのポリオレフィンを無水マレイン酸等の酸無水物等でグラフト変性したグラフト変性ポリオレフィン等を挙げることができる。
前記ポリエステルとは、ジカルボン酸を含む多価カルボン酸およびこれらのエステル形成性誘導体から選ばれる一種又は二種以上とグリコールを含む多価アルコールから選ばれる一種又は二種以上とから成るもの、又はヒドロキシカルボン酸およびこれらのエステル形成性誘導体から成るもの、又は環状エステルから成るものをいう。
本発明で使用するポリアミド(ここで言う“ポリアミド”は、本発明の“ポリアミド化合物”と混合されるポリアミド樹脂を指すものであり、本発明の“ポリアミド化合物”自体を指すものではない)は、ラクタムもしくはアミノカルボン酸から誘導される単位を主構成単位とするポリアミドや脂肪族ジアミンと脂肪族ジカルボン酸から誘導される単位を主構成単位とする脂肪族ポリアミド、脂肪族ジアミンと芳香族ジカルボン酸から誘導される単位を主構成単位とする部分芳香族ポリアミド、芳香族ジアミンと脂肪族ジカルボン酸から誘導される単位を主構成単位とする部分芳香族ポリアミドなどが挙げられ、必要に応じて、主構成単位以外のモノマー単位を共重合してもよい。
ポリビニルアルコールの具体例としては、ポリビニルアルコール、エチレン-ビニルアルコール共重合体及びその部分若しくは完全鹸化物等を挙げることができる。さらに、その変性品を用いても構わない。
植物由来樹脂の具体例としては、上記樹脂と重複する部分もあるが、特に限定されることなく公知の種々の石油以外を原料とする脂肪族ポリエステル系生分解性樹脂が挙げられる。脂肪族ポリエステル系生分解性樹脂としては、例えば、ポリグリコール酸(PGA)、ポリ乳酸(PLA)等のポリ(α-ヒドロキシ酸);ポリブチレンサクシネート(PBS)、ポリエチレンサクシネート(PES)等のポリアルキレンアルカノエート等が挙げられる。
本発明のポリアミド化合物及びポリアミド組成物は、酸素バリア性や酸素吸収性能が要求されるあらゆる用途に利用できる。例えば、本発明のポリアミド化合物を単独で小袋などに充填して酸素吸収剤として利用してもよい。
本発明のポリアミド化合物及びポリアミド組成物の代表的な利用例としては包装材料や包装容器等の成型体が挙げられるが、これらに限定されるものではない。本発明のポリアミド化合物またはポリアミド組成物を、それら成型体の少なくとも一部として加工して使用することができる。例えば、本発明のポリアミド化合物またはポリアミド組成物をフィルム状又はシート状の包装材料の少なくとも一部として使用することができ、また、ボトル、トレイ、カップ、チューブ、平袋やスタンディングパウチ等の各種パウチ等の包装容器の少なくとも一部にとして使用することができる。なお、これら包装材料や包装容器の成型体の構造は、本発明のポリアミド化合物またはポリアミド組成物からなる層の単層構造であってもよく、当該層と他の熱可塑性樹脂からなる層を組み合わせた多層構造であってもよい。本発明のポリアミド化合物またはポリアミド組成物からなる層の厚みは、特に制限は無いが、1μm以上の厚みを有することが好ましい。
また、トレイやカップ等の容器は射出成形機から金型中に溶融したポリアミド化合物又はポリアミド組成物を射出して製造する方法や、シート状の包装材料を真空成形や圧空成形等の成形法によって成形して得ることができる。包装材料や包装容器は上述の製造方法によらず、様々な方法を経て製造することが可能である。
なお、以下の実施例において、ポリ(シクロヘキサン-1,3-ジメチレン)アジパミドを「N-1,3BAC6」(なおここで、「6」は脂肪族ジカルボン酸に由来する単位の炭素数である)という。
1H-NMR(400MHz,日本電子(株)製、商品名:JNM-AL400、測定モード:NON(1H))を用いて共重合体の成分組成の定量を実施した。具体的には、溶媒としてギ酸-dを用いてポリアミド化合物の5質量%の溶液を調製し、1H-NMR測定を実施した。
ペレット状サンプル0.2gを精秤し、96%硫酸100mlに20~30℃で撹拌溶解した。完全に溶解した後、速やかにキャノンフェンスケ型粘度計に溶液5mlを取り、25℃の恒温漕中で10分間放置後、落下時間(t)を測定した。また、96%硫酸そのものの落下時間(t0)も同様に測定した。t及びt0から次式により相対粘度を算出した。
相対粘度=t/t0
まず、ポリアミド化合物を精秤し、フェノール/エタノール=4/1容量溶液に20~30℃で撹拌溶解させ、完全に溶解した後、撹拌しつつ、メタノール5mlで容器内壁を洗い流し、0.01mol/L塩酸水溶液で中和滴定して末端アミノ基濃度〔NH2〕を求めた。
また、ポリアミド化合物を精秤し、ベンジルアルコールに窒素気流下160~180℃で撹拌溶解させ、完全に溶解した後、窒素気流下80℃以下まで冷却し、撹拌しつつメタノール10mlで容器内壁を洗い流し、0.01mol/L水酸化ナトリウム水溶液で中和滴定して末端カルボキシル基濃度〔COOH〕を求めた。
測定した末端アミノ基濃度〔NH2〕及び末端カルボキシル基濃度〔COOH〕から、次式によって数平均分子量を求めた。
数平均分子量=2/(〔NH2〕+〔COOH〕)
〔NH2〕:末端アミノ基濃度(当量/g)
〔COOH〕:末端カルボキシル基濃度(当量/g)
示差走査熱量計((株)島津製作所製、商品名:DSC-60)を用い、昇温速度10℃/分で窒素気流下にDSC測定(示差走査熱量測定)を行い、ガラス転移温度(Tg)及び融点(Tm)を求めた。
厚み約100μmのフィルムサンプルを400cm2に切り出し、アルミ箔積層フィルムからなる25cm×18cmの3方シール袋に、水10mlを含ませた綿と共に仕込み、袋内空気量が400mlとなるようにして密封した。袋内の湿度は100%RH(相対湿度)とした。40℃下で28日保存後に、袋内の酸素濃度を酸素濃度計(東レエンジニアリング(株)製、商品名:LC-700F)で測定し、この酸素濃度から酸素吸収量(cc/g)を計算した。数値が高いほど酸素吸収性能に優れ好ましい。
なお、実施例103、401~403及び比較例401~403では、上記フィルムサンプルに代えて、ポリアミド化合物のペレット又は粉砕物を粉砕機で細かくした粉状サンプル2gを薬包紙に包んだものを用いて、上記と同様に酸素吸収量を計算した。
ASTM D3985に準じた酸素透過率測定装置(Mocon社製、型式:OX-TRAN 2/21SH)を使用して100μmフィルムの23℃、60%RHにおける酸素透過率を測定し、酸素透過係数(cc・mm/(m2・day・atm))に換算した。数値が低いほど酸素の透過量が少なく好ましい。
フィルムサンプルを400cm2に切り出した試験片、又はポリアミド化合物のペレット若しくは粉砕物を粉砕機で細かくして得られた粉状サンプル2gを薬包紙に包んだものを、アルミ箔積層フィルム(最内層のシーラントは、無臭グレードを使用)からなる25cm×18cmの3方シール袋に、水10mlを含ませた綿と共に仕込み、袋内空気量が400mlとなるようにして密封した。袋内の湿度は100%RHとした。40℃下で28日保存後に、注射器で袋内の空気を取り出し、10人のパネラーが臭気を嗅いで評価した。比較用のブランクとして、フィルムサンプル及び粉状サンプルを入れないものも用意した。官能試験評価は以下の基準により実施され、10人の評価の平均値を算出した。数値が低いほどにおいが少なく好ましい。
(評価基準)
0:臭いを感じない(ブランク)。
1:ブランクとの差をわずかに感じる。
2:ブランクとの差を感じる。
3:ブランクとかなりの差を感じる。
40℃100%RHの恒温槽に厚み約100μmのフィルムサンプルを28日間保存して酸素を吸収させた後のフィルムを23℃50%RHにて、1週間調湿した。このフィルムサンプルを、幅10mm、長さ100mmにカットして、引張試験機(東洋精機(株)製、商品名:ストログラフ V1-C)にて、引張速度50mm/minにて引っ張り、フィルム破断時の荷重を測定し、下記式により引張破断強度を求めた。
引張破断強度(MPa)=切断時の荷重(N)/試料フィルムの断面積(mm2)
本試験から得られる引張破断強度を機械物性保持の指標とした。なお、比較として、未保存(酸素吸収前)のフィルムサンプルを23℃50%RHにて1週間調湿後、同様に引張試験を実施した。酸素吸収後の数値が高いほど樹脂の劣化が少なく好ましい。
JIS-K-7105に準じて、厚み約100μmのフィルムサンプルについて、曇値測定装置(日本電色工業(株)製、型式:COH-300A)にて測定し、100μmあたりのHazeとして換算した。数値が低いほど着色が少なく好ましい。
(ポリアミド化合物の常圧滴下法による溶融重合)
撹拌機、分縮器、全縮器、温度計、滴下ロート及び窒素導入管、ストランドダイを備えた内容積50リットルの反応容器に、精秤したアジピン酸(旭化成ケミカルズ(株)製)13000g(89.0mol)、DL-アラニン((株)武蔵野化学研究所製)880.56g(9.88mol)、次亜リン酸ナトリウム11.9g(0.11mol)、酢酸ナトリウム6.16g(0.075mol)を入れ、十分に窒素置換した後、さらに少量の窒素気流下で系内を撹拌しながら170℃まで加熱した。これにcis体/trans体比率が74/26(mol%)である1,3-ビス(アミノメチル)シクロヘキサン(三菱ガス化学(株)製)12433g(88.7mol)を撹拌下に滴下し、生成する縮合水を系外へ除きながら系内を連続的に昇温した。1,3-ビス(アミノメチル)シクロヘキサンの滴下終了後、内温を260℃として40分反応を継続した。その後、系内を窒素で加圧し、ストランドダイからポリマーを取り出してこれをペレット化し、約23kgのポリアミド化合物を得た。
次いで、窒素ガス導入管、真空ライン、真空ポンプ、内温測定用の熱電対を設けたジャケット付きのタンブルドライヤーに前記ポリアミド化合物を仕込み、一定速度で回転させつつ、タンブルドライヤー内部を純度が99容量%以上の窒素ガスで十分に置換した後、同窒素ガス気流下でタンブルドライヤーを加熱し、約150分かけてペレット温度を150℃に昇温した。ペレット温度が150℃に達した時点で系内の圧力を1torr以下に減圧した。さらに昇温を続け、約70分かけてペレット温度を190℃まで昇温した後、190℃で30分保持した。次いで、系内に純度が99容量%以上の窒素ガスを導入して、タンブルドライヤーを回転させたまま冷却してDL-アラニン共重合N-1,3BAC6(ポリアミド化合物101)を得た。
図1中には、0.70~1.95ppmの範囲にある1,3-BACの水素に由来する吸収ピークを全て積算した数値13.9802が示されている(この数値をaとする)。なお、1,3-BACの繰り返し単位中のシクロヘキサン環には水素が10個含まれる。また、2.5ppm付近にアジピン酸のカルボニル基に隣接するメチレン基由来の水素に由来する吸収ピークを積算した数値4.0000が示されている(この数値をbとする)。一方、図2中には、0.65~1.95ppmの範囲にあるDL-アラニンのメチル基の水素に由来する吸収ピーク及び1,3-BACの水素に由来する吸収ピーク全てを積算した数値14.2631が示されている(他の実施例を含めたアミノ酸組成が異なる各々の測定サンプルから得られるこの数値をcとする)。この場合、cからaを差し引いた残りの積分強度(c-a)は、ポリアミド化合物中のDL-アラニン中のメチル基に由来することとなる。また、2.5ppm付近にアジピン酸のカルボニル基に隣接するメチレン基由来の水素に由来する吸収ピークを積算した数値4.0000が示されている(この数値をdとする)。b及びdの数値が同じであるため、積分強度(c-a)は、ポリアミド化合物中のDL-アラニン中のメチル基に由来する値とすることが可能である。
以下の実施例及び比較例においても、同様の手法により、調製したポリアミド化合物の成分組成の定量を実施した。
ポリアミド化合物101のペレットを25mmφ単軸押出機により、押出温度260℃、スクリュー回転数60rpm、引き取り速度1.2m/minで製膜し、幅200mm、厚み95~105μmの無延伸フィルムを作製した。
DL-アラニンの添加量をポリアミド化合物中の含有率が11.1mol%となるように変更したこと以外は、実施例101と同様の方法でDL-アラニン共重合N-1,3-BAC6(ポリアミド化合物102:1,3-BAC単位/アジピン酸単位/DL-アラニン単位=44.4/44.5/11.1(mol%比))及び無延伸フィルムを得た。
DL-アラニンの添加量をポリアミド化合物中の含有率が25mol%となるように変更したこと以外は、実施例101と同様の方法でDL-アラニン共重合N-1,3-BAC6(ポリアミド化合物103:1,3-BAC単位/アジピン酸単位/DL-アラニン単位=37.4/37.6/25.0(mol%比))を得た。なお、重合において分子量が十分に上がらなかったため、前述の無延伸フィルムでの引張破断強度、Haze値の評価は行わなかった。
α-アミノ酸をDL-2-アミノ酪酸(DL-AABA、(株)日本ファインケム製、精製品)に変更したこと以外は、実施例101と同様の方法でDL-2-アミノ酪酸共重合N-1,3-BAC6(ポリアミド化合物104:1,3-BAC単位/アジピン酸単位/DL-2-アミノ酪酸単位=47.3/47.4/5.3(mol%比))及び無延伸フィルムを得た。
α-アミノ酸をDL-フェニルアラニン(DL-Phe、Sinogel Amino Acid Co.,Ltd製)に変更したこと以外は、実施例101と同様の方法でDL-フェニルアラニン共重合N-1,3-BAC6(ポリアミド化合物105:1,3-BAC単位/アジピン酸単位/DL-フェニルアラニン単位=47.3/47.4/5.3(mol%比))及び無延伸フィルムを得た。
1,3-ビス(アミノメチル)シクロヘキサンを1,4-ビス(アミノメチル)シクロへキサン(三菱ガス化学(株)製、「1,4-BAC」と略す)に変更したこと以外は、実施例101と同様の方法でDL-アラニン共重合N-1,4-BAC6(ポリアミド化合物106:1,4-BAC単位/アジピン酸単位/DL-アラニン単位=47.3/47.4/5.3(mol%比))及び無延伸フィルムを得た。
芳香族ジカルボン酸として、イソフタル酸(IA、エイ・ジイ・インタナショナル・ケミカル(株)製)を共重合比が4.7mol%となるようにさらに共重合させたこと以外は、実施例101と同様の方法でDL-アラニン、イソフタル酸共重合N-1,3-BAC6(ポリアミド化合物107:1,4-BAC単位/アジピン酸単位/イソフタル酸単位/DL-アラニン単位=47.3/42.7/4.7/5.3(mol%比))及び無延伸フィルムを得た。
アジピン酸をセバシン酸(伊藤製油(株)製)に変更したこと以外は、実施例101と同様の方法でDL-アラニン共重合N-1,3-BAC10(ポリアミド化合物108:1,3-BAC単位/セバシン酸単位/DL-アラニン単位=47.3/47.4/5.3(mol%比))及び無延伸フィルムを得た。
(ポリアミド化合物の常圧滴下法による溶融重合)
撹拌機、分縮器、全縮器、温度計、滴下ロート及び窒素導入管、ストランドダイを備えた内容積50リットルの反応容器に、精秤したアジピン酸(旭化成ケミカルズ(株)製)13000g(89.0mol)、次亜リン酸ナトリウム11.5g(0.11mol)、酢酸ナトリウム5.96g(0.073mol)を入れ、十分に窒素置換した後、さらに少量の窒素気流下で系内を撹拌しながら170℃まで加熱した。これに1,3-ビス(アミノメチル)シクロヘキサン(三菱ガス化学(株)製)12437g(88.7mol)を撹拌下に滴下し、生成する縮合水を系外へ除きながら系内を連続的に昇温した。1,3-ビス(アミノメチル)シクロヘキサンの滴下終了後、内温を260℃として40分反応を継続した。その後、系内を窒素で加圧し、ストランドダイからポリマーを取り出してこれをペレット化し、約23kgのポリアミド化合物を得た。
次いで、窒素ガス導入管、真空ライン、真空ポンプ、内温測定用の熱電対を設けたジャケット付きのタンブルドライヤーに前記ポリアミド化合物を仕込み、一定速度で回転させつつ、タンブルドライヤー内部を純度が99容量%以上の窒素ガスで十分に置換した後、同窒素ガス気流下でタンブルドライヤーを加熱し、約150分かけてペレット温度を150℃に昇温した。ペレット温度が150℃に達した時点で系内の圧力を1torr以下に減圧した。さらに昇温を続け、約70分かけてペレット温度を190℃まで昇温した後、190℃で30分保持した。次いで、系内に純度が99容量%以上の窒素ガスを導入して、タンブルドライヤーを回転させたまま冷却してN-1,3BAC6(ポリアミド化合物109)を得た。
ポリアミド化合物109のペレットを25mmφ単軸押出機により、押出温度260℃、スクリュー回転数60rpm、引き取り速度1.2m/minで製膜し、幅200mm、厚み95~105μmの無延伸フィルムを作製した。
アジピン酸をcis体/trans体比率=70/30(mol%)である1,4-ビス(アミノメチル)シクロへキサン(1,4-BAC)(三菱ガス化学(株)製)に変更したこと以外は、比較例101と同様の方法でN-1,4-BAC6(ポリアミド化合物110)及び無延伸フィルムを得た。
DL-アラニンをα位に2級水素を持つグリシン((株)東京化成工業製)に変更したこと以外は、実施例101と同様の方法でグリシン共重合N-1,3-BAC6(ポリアミド化合物111:1,3-BAC単位/アジピン酸単位/グリシン単位=47.3/47.4/5.3(mol%比))及び無延伸フィルムを得た。
DL-アラニンをα位に水素を持たない2-アミノイソ酪酸(2-アミノ-2-メチルプロパン酸、AIB、(株)日本ファインケム製、精製品)に変更したこと以外は、実施例101と同様の方法で2-アミノ-2-メチルプロパン酸共重合N-1,3-BAC6(ポリアミド化合物112:1,3-BAC単位/アジピン酸単位/2-アミノメチルプロパン酸単位=47.3/47.4/5.3(mol%比))及び無延伸フィルムを得た。
芳香族ジカルボン酸として、イソフタル酸(エイ・ジイ・インタナショナル・ケミカル(株)製)を共重合比が5mol%となるようにさらに共重合させたこと以外は、比較例101と同様の方法でイソフタル酸共重合N-1,3-BAC6(ポリアミド化合物113:1,3-BAC単位/アジピン酸単位/イソフタル酸単位=49.9/45.1/5.0(mol%比))及び無延伸フィルムを得た。
アジピン酸をセバシン酸(伊藤製油(株)製)に変更したこと以外は、比較例101と同様の方法でN-1,3-BAC10(ポリアミド化合物114)及び無延伸フィルムを得た。
ポリアミド化合物109に対し、ステアリン酸コバルトを、組成物中のコバルト含有量が400ppmとなるように添加し、ドライブレンドした。得られたブレンド物を、30mmφ2軸押出機により、押出温度260℃、スクリュー回転数60rpm、フィードスクリュー回転数12rpm、引き取り速度1.8m/minで製膜し、幅200mm、厚み95~105μmの無延伸フィルムを作製した。
ポリアミド化合物109の100質量部に対し、マレイン酸変性ポリブタジエン(PB)(日本石油化学(株)製、商品名:M-2000-20)5質量部、及びステアリン酸コバルトを、組成物中のコバルト含有量が400ppmとなるように添加し、ドライブレンドした。得られたブレンド物を、30mmφ2軸押出機により、押出温度260℃、スクリュー回転数60rpm、フィードスクリュー回転数14rpm、引き取り速度2.0m/minで製膜し、幅200mm、厚み95~105μmの無延伸フィルムを作製した。
ポリアミド化合物109に対し、DL-アラニン((株)武蔵野化学研究所製)を、組成物中のDL-アラニン含有量が5質量%となるように添加し、ドライブレンドした。得られたブレンド物同士が共重合しないように、15mmφの小型の単軸押出機を用いて、押出温度240℃、スクリュー回転数30rpm、フィードスクリュー回転数14rpm、引き取り速度1.0m/minで製膜し、幅110mm、厚み95~105μmの無延伸フィルムを作製した。
これらに対し、3級水素を有するα-アミノ酸を共重合したポリアミド化合物は、金属を用いることなく十分な酸素吸収性能を発現することができ、しかも不快な臭気を発生することがない(実施例101~108)。特に、フィルムサンプルの場合、フィルムの酸素透過係数も良好で、透明性も良好であり、更に酸素吸収後の機械物性も保持できている(実施例101~102及び104~108)。
(ポリアミド化合物の常圧滴下法による溶融重合)
実施例201~216及び比較例201~203のそれぞれにおいて、ポリアミド化合物を以下の通り作製した。撹拌機、分縮器、全縮器、温度計、滴下ロート及び窒素導入管、ストランドダイを備えた内容積50リットルの反応容器に、表2に記載の脂肪族ジカルボン酸、芳香族ジカルボン酸、アミノ酸、次亜リン酸ナトリウム、酢酸ナトリウムを仕込み、十分に窒素置換した後、さらに少量の窒素気流下で系内を撹拌しながら170℃まで加熱した。これにcis体/trans体比率が74/26(mol%)である1,3-ビス(アミノメチル)シクロヘキサン(1,3-BACと略する)を撹拌下に滴下し、生成する縮合水を系外へ除きながら系内を連続的に昇温した。1,3-BACの滴下終了後、内温を240℃として撹拌トルクの上昇度に注意しながら40~60分反応を継続した。その後、系内を窒素で加圧し、ストランドダイからポリマーを取り出してこれをペレット化し、約23kgのポリアミド化合物を得た。
実施例201~216及び比較例201~203の各々で得られたポリアミド化合物のペレットを120℃で6時間真空乾燥した後、25mmφ単軸押出機により、押出温度245℃、スクリュー回転数60rpm、引き取り速度1.2m/minで製膜し、幅200mm、厚み95~105μmの無延伸フィルムを作製した。
これらに対し、3級水素を有するα-アミノ酸を共重合したポリアミド化合物は、金属を用いることなく十分な酸素吸収性能を発現することができ、共重合されるα-アミノ酸のモル比によって酸素吸収能力を調整することができる。
(ポリアミドの常圧滴下法による溶融重合)
実施例301~316及び比較例301~303のそれぞれにおいて、ポリアミド化合物を以下の通り作製した。撹拌機、分縮器、全縮器、温度計、滴下ロート及び窒素導入管、ストランドダイを備えた内容積50リットルの反応容器に、表3に記載のジカルボン酸、アミノカルボン酸、アミノ酸、次亜リン酸ナトリウム、酢酸ナトリウムを仕込み、十分に窒素置換した後、さらに少量の窒素気流下で系内を撹拌しながら170℃まで加熱した。これにcis体/trans体比率が74/26(mol%)である1,3-ビス(アミノメチル)シクロヘキサン(1,3-BACと略する)を撹拌下に滴下し、生成する縮合水を系外へ除きながら系内を連続的に昇温した。1,3-BACの滴下終了後、内温を245℃として40分反応を継続した。その後、系内を窒素で加圧し、ストランドダイからポリマーを取り出してこれをペレット化し、約23kgのポリアミド化合物を得た。
実施例301~316及び比較例301~303の各々で得られたポリアミド化合物のペレットを120℃で6時間真空乾燥した後、25mmφ単軸押出機により、押出温度245℃、スクリュー回転数60rpm、引き取り速度1.2m/minで製膜し、幅200mm、厚み95~105μmの無延伸フィルムを作製した。
これらに対し、3級水素を有するα-アミノ酸を共重合したポリアミド化合物は、金属を用いることなく十分な酸素吸収性能を発現することができ、共重合されるα-アミノ酸のモル比によって酸素吸収能力を調整することができる。
(ポリアミドオリゴマーの常圧滴下法による溶融重合)
撹拌機、分縮器、全縮器、温度計、滴下ロート及び窒素導入管、ストランドダイを備えた内容積50リットルの反応容器に、表4に記載された種類及び配合量の脂肪族ジカルボン酸、芳香族ジカルボン酸、α-アミノ酸、ω-アミノカルボン酸、次亜リン酸ナトリウム、酢酸ナトリウムを仕込み、十分に窒素置換した後、さらに少量の窒素気流下で系内を撹拌しながら170℃まで加熱した。これに、表4に記載された配合量の脂環族ジアミンであるcis体/trans体比率が74/26(mol%)である1,3-ビス(アミノメチル)シクロヘキサン(1,3-BACと略する)を撹拌下に滴下し、生成する縮合水を系外へ除きながら系内を連続的に昇温した。ジアミンの滴下終了後、内温を240℃として撹拌トルクの上昇度に注意しながら40~60分反応を継続した。その後、系内を窒素で加圧し、ストランドダイからポリアミドオリゴマーを取り出した。ストランド状態で取り出せるものはペレタイズし、ペレット状のポリアミドオリゴマーを得た。また、分子量が低くストランド状態で取り出せないものは、別途、粉砕機にて粉砕し、ポリアミドオリゴマー粉砕物を得た。
Claims (9)
- 前記一般式(III)におけるRが、置換もしくは無置換の炭素数1~6のアルキル基又は置換もしくは無置換の炭素数6~10のアリール基である、請求項1に記載のポリアミド化合物。
- 前記直鎖脂肪族ジカルボン酸単位が、アジピン酸単位、セバシン酸単位、及び1,12-ドデカンジカルボン酸単位からなる群から選ばれる少なくとも1つを合計で50モル%以上含む、請求項1又は2に記載のポリアミド化合物。
- 前記芳香族ジカルボン酸単位が、イソフタル酸単位、テレフタル酸単位、及び2,6-ナフタレンジカルボン酸単位からなる群から選ばれる少なくとも1つを合計で50モル%以上含む、請求項1~3のいずれかに記載のポリアミド化合物。
- 前記ω-アミノカルボン酸単位が、6-アミノヘキサン酸単位及び/又は12-アミノドデカン酸単位を合計で50モル%以上含む、請求項5に記載のポリアミド化合物。
- 相対粘度が1.8以上4.2以下である、請求項1~6のいずれかに記載のポリアミド化合物。
- 相対粘度が1.01以上1.8未満である、請求項1~6のいずれかに記載のポリアミド化合物。
- 請求項1~8のいずれかに記載のポリアミド化合物を含むポリアミド組成物。