WO2011086959A1 - 射出成形品およびその製造方法 - Google Patents
射出成形品およびその製造方法 Download PDFInfo
- Publication number
- WO2011086959A1 WO2011086959A1 PCT/JP2011/050070 JP2011050070W WO2011086959A1 WO 2011086959 A1 WO2011086959 A1 WO 2011086959A1 JP 2011050070 W JP2011050070 W JP 2011050070W WO 2011086959 A1 WO2011086959 A1 WO 2011086959A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- line segment
- injection
- thermoplastic resin
- resin member
- molded product
- Prior art date
Abstract
Description
(a)前記射出成形品の縦断面と前記接合面との交わりにより描かれる接合線が、前記射出成形品の表面から内側に延び内側に終端を有する第1の接合線分、前記射出成形品の裏面から内側に延び内側に終端を有する第2の接合線分、および、前記第1の接合線分の前記終端と前記第2の接合線分の前記終端とを結ぶ第3の接合線分からなり、かつ、
(b-1)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記各接合線分においてそれぞれ異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜している、あるいは、
(b-2)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記第1の接合線分と前記第2の接合線分において同じであり、前記第1の接合線分と前記第3の接合線分とにおいて異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜している射出成形品。
0.7>t1/t0>0.1、
0.8>t2/t0≧0、
0.7>t3/t0>0.1、および、
1.0>t2/L4≧0、
(ここで、t2=t0-t1-t3である)
の関係が満足されていることが好ましい。
0°≦R1≦80°、および、
0°≦R2≦80°
の関係が満足されていることが好ましい。
(a)前記射出成形品の縦断面と前記接合面との交わりにより描かれる接合線が、前記射出成形品の表面から内側に延び内側に終端を有する第1の接合線分、前記射出成形品の裏面から内側に延び内側に終端を有する第2の接合線分、および、前記第1の接合線分の前記終端と前記第2の接合線分の前記終端とを結ぶ第3の接合線分からなり、かつ、
(b-1)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記各接合線分においてそれぞれ異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜している、あるいは、
(b-2)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記第1の接合線分と前記第2の接合線分において同じであり、前記第1の接合線分と前記第3の接合線分とにおいて異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜しているように、
(c)前記一方の熱可塑性樹脂部材の厚みに適合したクリアランスを有する金型内に前記一方の熱可塑性樹脂部材を配置し、該一方の熱可塑性樹脂部材の前記側端面に対し、前記他方の熱可塑性樹脂部材を形成する樹脂を、射出成形してなる射出成形品の製造方法。
0.8>t2/t0≧0 ・・・(2)
0.7>t3/t0>0.1 ・・・(3)
1.0>t2/L4≧0 ・・・(4)
なお、t2の値は、(t0-t1-t3)の値に等しい関係にある。
図8は、電界シールド性の測定装置の概略縦断面図である。図8において、電界シールド性の測定装置81は、金属管85-eからなる測定筐体からなる。金属管85-eの内部空間は、外界から遮蔽されている。金属管85-eの内部空間には、信号発信用アンテナ85-bと信号受信用アンテナ85-cが設けられている。金属管85-eは、両アンテナの間に、測定試料85-aをその外側から挿入可能とされている。測定試料85-aは、測定試料厚み85-dを有する。
接合部曲げクラック発生荷重の測定方法:
次に示す試験装置、試験片、試験条件を用いて3点曲げ試験を行ない、曲げ荷重-歪み線図を採取する。その線図において破断挙動を示した時点の荷重を曲げクラック発生荷重とする。
支点間距離:30mm、支点の半径:2.0mm、圧子の半径:5.0mm、クロスヘッドスピード:1.0mm/分
接合部引張クラック発生荷重の測定方法:
次に示す試験装置、試験片、試験条件を用いて引張試験を行ない、荷重-歪み線図から破断挙動を示した時点の荷重を引張クラック発生荷重とする。
(b)試験片:前記接合部曲げクラック発生荷重の測定方法と同様にして試験片を作製する。
チャック間距離:30mm、クロスヘッドスピード:1.0mm/分
1b、4b:第2の接合線分
1ab、4ab:第3の接合線分
75、76:射出成形金型
75A、76B:射出成形機
81:電界シールド性の測定装置
85-a:測定試料
85-b:信号発信用アンテナ
85-c:信号受信用アンテナ
85-d:測定試料厚み
85-e:金属管
97:試験片
98:中心線
99:距離
103:抜き勾配
1110:補助中心線
1111、1112:領域
1113:中心
A:熱可塑性樹脂部材
A1:両部材の重なりがない領域
B:熱可塑性樹脂部材
B1:両部材の重なりがない領域
BS1、BS4:裏面
C:熱可塑性樹脂部材
C1:両部材の重なりがない領域
D:熱可塑性樹脂部材
D1:両部材の重なりがない領域
FS1、FS4:表面
IMA1、IMA2、IMA3、IMA4、IMA5、IMA6:射出成形品
JAB、JCD:接合面
JL1、JL4:接合線
L:試験片の長さ
LCS1、LCS4:縦断面
L4:第3の接合線分の法線方向の投影長さ
R:半径
R1、R2:角度
SEA、SEB、SEC、SED:側端面
t0、t1、t2、t3:厚み
W:試験片の幅
WJL1、WJL2、WJL3、WJL4、WJL5、WJL6:幅方向接合線
Claims (15)
- 一方の熱可塑性樹脂部材の側端面に対し他方の熱可塑性樹脂部材が射出成形されて双方の部材が双方の側端面において接合された接合面を有する射出成形品であって、
(a)前記射出成形品の縦断面と前記接合面との交わりにより描かれる接合線が、前記射出成形品の表面から内側に延び内側に終端を有する第1の接合線分、前記射出成形品の裏面から内側に延び内側に終端を有する第2の接合線分、および、前記第1の接合線分の前記終端と前記第2の接合線分の前記終端とを結ぶ第3の接合線分からなり、かつ、
(b-1)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記各接合線分においてそれぞれ異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜している、あるいは、
(b-2)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記第1の接合線分と前記第2の接合線分において同じであり、前記第1の接合線分と前記第3の接合線分とにおいて異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜している射出成形品。 - 前記第1の接合線分と前記第2の接合線分の少なくとも一方の接合線分の方向が、前記法線に実質的に平行である請求項1に記載の射出成形品。
- 前記第1の接合線分と前記第2の接合線分の双方の接合線分の方向が、前記法線に実質的に平行である請求項2に記載の射出成形品。
- 前記一方の熱可塑性樹脂部材と前記他方の熱可塑性樹脂部材とは、前記法線方向において、重なり合わない領域を有している請求項1に記載の射出成形品。
- 最大の傾斜角度を有する前記第3の接合線分が位置する前記接合面における前記射出成形品の厚みをt0、当該位置における前記第1の接合線分が位置する前記接合面における前記射出成形品の厚みをt1、当該位置における前記第2の接合線分が位置する前記接合面における前記射出成形品の厚みをt3、前記第3の接合線分を前記法線方向に投影したときの長さをL4としたとき、
0.7>t1/t0>0.1、
0.8>t2/t0≧0、
0.7>t3/t0>0.1、および、
1.0>t2/L4≧0
の関係が満足されている請求項1に記載の射出成形品。 - 前記第1の接合線分と前記一方の熱可塑性樹脂部材の表面の法線がなす角度をR1、前記第2の接合線分と前記一方の熱可塑性樹脂部材の裏面の法線がなす角度をR2としたとき、
0°≦R1≦80°、および、
0°≦R2≦80°
の関係が満足されている請求項1に記載の射出成形品。 - 前記一方の熱可塑性樹脂部材の前記他方の熱可塑性樹脂部材側に前記接合面を介して突出している部分を含む面が、意匠面である請求項1に記載の射出成形品。
- 前記一方の熱可塑性樹脂部材と前記他方の熱可塑性樹脂部材が、同一の樹脂成分を含んでいる請求項1に記載の射出成形品。
- 前記一方の熱可塑性樹脂部材のKEC法による周波数1GHz帯における電界シールド性が、0乃至10dBであり、前記他方の熱可塑性樹脂部材のそれが、30乃至120dBである請求項8に記載の射出成形品。
- 前記一方の熱可塑性樹脂部材が、非導電性繊維を含有し、前記他方の熱可塑性樹脂部材が、導電性繊維を含有している請求項8に記載の射出成形品。
- 一方の熱可塑性樹脂部材の側端面に対し他方の熱可塑性樹脂部材が射出成形されて双方の部材が双方の側端面において接合された接合面を有する射出成形品の製造方法であって、
(a)前記射出成形品の縦断面と前記接合面との交わりにより描かれる接合線が、前記射出成形品の表面から内側に延び内側に終端を有する第1の接合線分、前記射出成形品の裏面から内側に延び内側に終端を有する第2の接合線分、および、前記第1の接合線分の前記終端と前記第2の接合線分の前記終端とを結ぶ第3の接合線分からなり、かつ、
(b-1)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記各接合線分においてそれぞれ異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜している、あるいは、
(b-2)前記一方の熱可塑性樹脂部材の表面あるいは裏面の法線となす各接合線分の方向が、前記第1の接合線分と前記第2の接合線分において同じであり、前記第1の接合線分と前記第3の接合線分とにおいて異なるとともに、前記第3の接合線分の方向が、前記法線に対し傾斜しているように、
(c)前記一方の熱可塑性樹脂部材の厚みに適合したクリアランスを有する金型内に前記一方の熱可塑性樹脂部材を配置し、該一方の熱可塑性樹脂部材の前記側端面に対し、前記他方の熱可塑性樹脂部材を形成する樹脂を、射出成形してなる射出成形品の製造方法。 - 前記第1の接合線分と前記第2の接合線分の少なくとも一方の接合線分の方向が、前記法線に実質的に平行である請求項11に記載の射出成形品の製造方法。
- 前記第1の接合線分と前記第2の接合線分の双方の接合線分の方向が、前記法線に実質的に平行である請求項11に記載の射出成形品の製造方法。
- 前記一方の熱可塑性樹脂部材と前記他方の熱可塑性樹脂部材とは、前記法線方向において、重なり合わない領域を有している請求項11に記載の射出成形品の製造方法。
- 前記一方の熱可塑性樹脂部材と前記他方の熱可塑性樹脂部材が、同一の樹脂成分を含んでいる請求項11に記載の射出成形品の製造方法。