WO2008047626A1 - Method for producing resin for optical material - Google Patents
Method for producing resin for optical material Download PDFInfo
- Publication number
- WO2008047626A1 WO2008047626A1 PCT/JP2007/069659 JP2007069659W WO2008047626A1 WO 2008047626 A1 WO2008047626 A1 WO 2008047626A1 JP 2007069659 W JP2007069659 W JP 2007069659W WO 2008047626 A1 WO2008047626 A1 WO 2008047626A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- bis
- polymerizable composition
- mercaptomethylthio
- resin
- compound
- Prior art date
Description
Claims