WO2005049701A1 - 二軸延伸ポリエステルフィルム - Google Patents
二軸延伸ポリエステルフィルム Download PDFInfo
- Publication number
- WO2005049701A1 WO2005049701A1 PCT/JP2004/017087 JP2004017087W WO2005049701A1 WO 2005049701 A1 WO2005049701 A1 WO 2005049701A1 JP 2004017087 W JP2004017087 W JP 2004017087W WO 2005049701 A1 WO2005049701 A1 WO 2005049701A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- polyester
- film
- thickness
- melting point
- Prior art date
Abstract
Description
Claims