WO2001081658A1 - Procede electrolytique d'oxydation pour l'obtention d'un revêtement ceramique a la surface d'un metal - Google Patents
Procede electrolytique d'oxydation pour l'obtention d'un revêtement ceramique a la surface d'un metal Download PDFInfo
- Publication number
- WO2001081658A1 WO2001081658A1 PCT/FR2001/001269 FR0101269W WO0181658A1 WO 2001081658 A1 WO2001081658 A1 WO 2001081658A1 FR 0101269 W FR0101269 W FR 0101269W WO 0181658 A1 WO0181658 A1 WO 0181658A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- signal
- metal
- current
- voltage
- during
- Prior art date
Abstract
Description
Claims