WO1997037076A1 - Composition hydrophobe et oleophobe - Google Patents
Composition hydrophobe et oleophobe Download PDFInfo
- Publication number
- WO1997037076A1 WO1997037076A1 PCT/JP1997/001059 JP9701059W WO9737076A1 WO 1997037076 A1 WO1997037076 A1 WO 1997037076A1 JP 9701059 W JP9701059 W JP 9701059W WO 9737076 A1 WO9737076 A1 WO 9737076A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- emulsion
- block isocyanate
- oil
- surfactant
- Prior art date
Description
Claims