WO1995012895A1 - Procede pour produire un element a semi-conducteurs, et feuille auto-adhesive pour coller des tranches - Google Patents
Procede pour produire un element a semi-conducteurs, et feuille auto-adhesive pour coller des tranches Download PDFInfo
- Publication number
- WO1995012895A1 WO1995012895A1 PCT/JP1994/001858 JP9401858W WO9512895A1 WO 1995012895 A1 WO1995012895 A1 WO 1995012895A1 JP 9401858 W JP9401858 W JP 9401858W WO 9512895 A1 WO9512895 A1 WO 9512895A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- compound
- wafer
- semiconductor device
- group
- Prior art date
Description
明 細 書
半導体素子の製造方法、 ウェハ貼付用粘着シート
〔技術分野〕
本発明は、 半導体素子の製造方法に関し、 詳しくは、 リードフレームに接続さ れた半導体チップを封止樹脂にて封止して、 樹脂封止型の半導体素子を製造する 方法の改良であって、 パッケージクラックの発生の少ない方法に関する。 また、 本発明は、 当該方法に使用しえるウェハ貼付用粘着シートに関する。
〔背景技術〕
従来の樹脂封止型の半導体パッケージ (半導体素子) は、 リードフレームと一 体になったタイパッド上に、 半導体ウェハから切断分離された半導体チップを銀 ペーストなどの接着手段によって固定した構造であった。 しかし、 近年、 例えば
D R AMなどのようにチップの大型化が進み、 従来の半導体パッケージ構造では 対応が困難となり、 チップ上にリードフレ一ムが設けられた L 0 C構造を採用す る例が増加している。
L O C構造においては、 従来の半導体パッケージ構造と異なり、 半導体チップ の裏面が封止樹脂に直接接している。 また、 従来の半導体パッケージ構造を含む 各種構造においても、 ダイパッドに開口部を設けるなどの手段によって、 ダイパ ッドの面積を半導体チップの面積よりも小さくする構造を採用する例が増加して いる。 このような構造においても、 ダイパッドの面積が半導体チップの面積より も小さいので、 半導体チップの裏面で封止樹脂に直接接する部分が存在する。 半導体ウェハは拈着シートに貼付され、 複数の半導体チップに切断 (ダイシン グ) された後、 粘着シートから個々の半導体チップが分雜 (ピックアップ) され て、 ダイパッド上にボンディングされる。 上記のように、 半導体チップの裏面 ( 粘着シートに接していた面、 以下同じ。 ) が封止樹脂に直接接する場合には、 封 止樹脂と半導体チップとの素材の線膨張係数の相違により、 または半導体チッブ の裏面に付着した粘着剤と封止樹脂との界面に水が溜まることにより、 封止樹脂 表面または内部にひびがはいり、 所謂パッケージクラックが発生するという問題 がある。
通常、 半導体チップの表面 (パターン形成面) には、 ポリイミ ド樹脂が被覆さ れており、 パッケージクラックの問題は生じないが、 半導体チップの裏面に対し てもポリイミ ド樹脂で被覆するならば、 煩雑な工程が増えることとなり、 また高 価なポリィミ ド樹脂を用いるために生産コストが上昇するという問題が生じる。 また、 放熱効果を高めるために、 リードフレームに銅フレームを用いる例が増 加しているが、 従来の 4 2ァロイなどに比較して、 ノ、'ッケージクラックが発生し 易いことが問題となっている。
さらに、 半導体封止樹脂の設計においても、 半導体チップの大型化に伴い、 成 形用金型からの剝雜性および半導体チップとの間の接着性を兼ね備えさせること が、 益々困難になっている。
〔発明の開示〕
本発明の目的は、 上記のような従来技術に伴う問題点を解決しょうとするもの であって、 煩雑な工程を必要とせずにパッケージクラックを防止し、 かつ封止樹 脂の設計が容易となる半導体素子の製造方法を提供することである。
また、 本発明は上記製造方法に、 好適に使用しえるウェハ貼付用粘着シートを 提供することである。
すなわち、 本発明の半導体素子の製造方法は、 反応性基を有する化合物 (但し、 下記の酸、 当該酸の酸成分となる置換基における誘導体は除く) 、 酸、 当該酸の 酸成分となる g換基における誘導体 (以下、 酸誘導体という) 〔但し、 酸および 酸誘導体中、 下記一般式 ( I ) で表される化合物に含まれるものは除く) 、 およ び下記一般式 ( I )
〔但し、 式中 R l、 R 2、 R 3および R 4は、 互いに同一または異なっていて もよい 1価の有機基であり、 nおよび mは、 それぞれ 0または 1以上の整数を示 し、 nと mとの和は、 1〜1 0 0 0である。 〕
で表されるシロキサン誘導体および該シロキサン誘導体をその構成中に含む数平
均分子量 1 0 0 0 0以下の化合物からなる群から選ばれる少なくとも一のパッケ ージクラック防止性化合物を用レ、て、 リードフレームおよびノまたは半導体ゥェ ハもしくは半導体チッブを処理する工程を含むことを特徵とする。
また、 本発明のウェハ貼付用粘着シートは、 上記少なくとも一のパッケージク ラック防止化合物を含有する拈着剤からなる層が、 基材面上に積層されてなるも のである。
〔図面の簡単な説明〕
図 1は、 本発明のウェハ貼付用拈着用シー卜の一実施例を示す断面図である。 図 2は、 本発明のゥェハ貼付用粘着用シートを用いたダイシング工程を示す断 面図である。
図 3は、 本発明のウェハ貼付用粘着用シートを用いたピックアップ工程を示す 断面図である。
図 4は、 チップの引張剝雜力の測定方法を示す説明図である。
図 5は、 パッケージの内部 示す説 ' .¾である。
図 6は、 リ一ドフレームの剪断接着力の測定方法を示す説明図である。
図 7は、 U V照射による接着シートとウェハとの接着力の経時変化を示すグラ フである。
図 8は、 U V照射によるパーティクル数の経時変化を示すグラフである。
本発明において 「反応性基を有する有機化合物 J とは、 ヒドロキシル基、 アミ ノ基、 カルボニル基 (エポキシ基を含む。 ) 、 ニトロ基、 ニトロソ基、 不飽和炭 化水素基 (ァルケニル、 アルカジエニル、 アルカトリェニル、 アルキニルなど) 、 イソシァネート基などを有する化合物をいい、 例えば架橋剤 (例:イソシァネー ト系架橋剤、 エポキシ系架橋剤、 メラミン系架橋剤など) 、 シランカップリング 剤 (例:イソシァネート系、 変性イソシァネート系、 変性アミノシラン系、 チタ ネート系、 エポキシ官能性シラン、 ォレフィン系シラン、 アクリル系シラン、 メ ルカプト系シラン、 イソシァネート系シラン、 エポキシ系シラン、 アミノ系シラ ン、 またはカルボキシル基を持つシラン類またはそのカルボキシル基における誘 導体など) が例示される。 「反応性基を有する有機化合物」 として好ましいもの
は、 水酸基と反応性の 「反応性基を有する有機化合物」 、 特にその分子量が 1000 以下の化合物が例示される。 「反応性基を有する有機化合物」 としては、 具体的 には、 次の化合物が例示される。
架橋剤:
下式で表されるスーパべッカミン J一 8 2 0、
などのメラミン系架橋剤。
下式で表されるテトラッド (:、
CH2-CH-CH20 0CH2-CH-CH5
\ /
0
CH2-CH-CH20 H2
等のエポキシ系架橋剤。
下式で表されるコロネート L、
ジメチル一ジフエニルメ夕ンジィソシァネート、 ジメ トキシ一ジフエ二ルジィ ソシァネート、 ジメ トキシービフエ二レンジイソシァネート、 テトラメチルーピ フエ二レンジィソシァネート等のィソシァネート系架橋剤。
シランカツプリング剤:
3—アミノブ口ピルトリエトキシシラン、 3—メタクリ口キシブ口ピルトリメ トキシシラン、 2— ( 3 , 4 —エポキシシクロへキシル) ェチルトリメ トキシシ
ラン、 N— 2— (アミノエチル) 3—アミノブ口ピルメチルジメ トキシシラン、
N— 2— (アミノエチル) 3—ァミノプロピルメチルジメ トキシシラン、 N—フ ェニルー 3—ァミノプロビルトリメ トキシシラン、 3—メルカブトプロピルトリ メ トキシンラン、 ァニリノブ口ビルトリメ トキシシラン、 メルカブトプロピルメ チルジメ トキシシラン、 3—ウレイ ドプロビルトリメ トキシシラン、 3—ァミノ プロピルートリス (2—メ トキシーエトキシーエトキシ) シラン、 N—メチルー
3—ァミノプロピルトリメ トキシシラン、 3— 4, 5ジヒドロイミダブールブロ ビルトリエトキシシラン、 下式で表される KBM— 403、 KBM- 903、 K
BM— 9 0 2、 KBM- 6 0 3 KBP- 44などのシリコーン性シランカップ リング剤が例示される。
KBM- 40 3 (CH30)3Si-(CH2)
KBM- 902 (CH30)2Si-NH2
CH3
KBM- 603 (CH30)3Si-(CH2)3NH-(CH2)2-NH2
また、 酸としては、 硫酸、 硝酸、 リン酸などの無機酸、 カルボキシル基、 スル ホン基を有する有機酸が例示される。 酸誘導体は、 酸成分となる置換基 (例えば、 カルボキシル基、 スルホン基) における誘導体 (例えば、 エステル、 アミ ド、 無 水物など) をいう。
有機酸および有機酸酸誘導体としては、 フタル酸などの芳香族ジカルボン酸類 フタル酸ァミ ドなどの芳香族ジカルボン酸誘導体;安息香酸などの芳香族モノ力 ルボン酸類:アルキル安息香酸類、 ァミノ安息香酸のごとき他の置換基をも有す る芳香族カルボン酸類:酢酸などの脂肪族モノカルボン酸類; コハク酸、 アジピ ン酸、 マレイン酸などの脂肪族ジカルボン酸類; クロトン酸、 テトロール酸、 ァ クリル酸、 メタクリル酸などの不飽和カルボン酸類;あるいはァミノ基のごとき その他の置換基をも有する脂肪族カルボン酸化合物;カルボキシル基を三つ以上 有する脂肪族、 芳香族カルボン酸化合物:上記の酸無水物、 例えば酢酸などの他 の酸との混合無水物あるいはエステル:上記の酸およびノまたは酸誘導体をその
構成要素の一部に持つオリゴマー (但し、 その有効性の点から上記酸および Zま たは酸誘導体を共重合体比で 1 o %以上含んでいるものが好ましい。 ) :上記の カルボキシル基をスルホン基に置換した化合物などが例示される。 スルホン基に 置換した化合物としては、 メタンスルホン酸、 エタンスルホン酸などの低級アル キルスルホン酸、 ェタンジスルホン酸、 プロパンジスルホン酸などの低級アルキ ルジスルホン酸、 ベンゼンスルホン酸、 トルエンスルホン酸などのァリルスルホ ン酸などが例示される。 特に、 リン酸などの無機酸、 および無水フタル酸、 無水 マレイン酸などの酸無水物が好ましい。
さらに、 酸誘導体としては、 後述する放射線重合性化合物として例示した化合 物中、 ァクリレート系化合物として例示した化合物が例示される。
また、 上記の酸誘導体には塩も包含され、 カリウム塩またはカルシウム塩のよ うなアルカリ金属またはアルカリ土類金属の塩:フッ化水素酸塩、 塩酸塩、 臭化 水素酸塩、 ョゥ化水素酸塩のようなハロゲン化水素酸塩;硝酸塩、 過塩素酸塩、 硫酸塩、 リン酸塩などの無機酸塩: メタンスルホン酸塩、 トリフルォロメタンス ルホン酸塩、 エタンスルホン酸塩のような低級アルキルスルホン酸塩;ベンゼン スルホン酸塩、 p —トルエンスルホン酸塩のようなァリールスルホン酸塩; フマ ール酸塩、 コハク酸塩、 クェン酸塩、 酒石酸塩、 シユウ酸塩、 マレイン酸塩など の有機酸塩;およびグルタミン酸塩、 ァスパラギン酸塩のようなアミノ酸塩を挙 げることができる。
上記の酸および酸誘導体において、 酸成分となる置換基数は、 分子の骨格を形 成する元素数 (当該置換基を除く) に対して、 5 Z 1 0 0以上であることが好ま しい。 ここに酸成分となる置換基とは、 カルボキシル基、 スルホン基などをいい、 酸誘導体においては、 誘導体化される前の酸を構成している酸成分となる基をい ■5 ο
また、 本発明においてウェハ貼付用拈着シート中に、 パッケージクラック防止 性化合物、 特に酸または酸誘導体を配合させる場合には、 架棕剤との反応を ぐ ためには、 例えば酸および または酸誘導体の酸部分を保護基で g換しておいて、 ダイシング後の例えば UV照射により保護基を脱雔させて元の酸とすることがで
き、 より少量で本発明の効果を奏することが可能である。 このような化合物とし ては、 具体的には、 ジァリルスルホニゥム塩、 トリアリルスルホニゥム塩、 ジァ ルキルフエナシルスルホニゥム塩、 ァリルジァゾニゥム塩、 芳香族テトラカルボ ン酸エステル、 芳香族スルホン酸エステル、 ニトロべンジルエステル、 芳香族ス ルファミ ド、 ナフトキノンジアジドー 4ースルホン酸エステルなどが用いられる。 これら化合物も本発明における酸または酸誘導体に包含される。
なお、 本発明におけるパッケージクラック防止性化合物としては、 界面活性作 用を有するものは好ましくない。
さらに、 本発明において下記の一般式 ( I )
た、 上記の構造式において、 アミノ基をカルボキシル基に置換したシロキサ ン誘導体が例示される。
さらに、 上記シロキサン誘導体をその構成要素の一部に持つ数平均分子量が 1 0 0 0 0以下の化合物 (但し、 その有効性の点から上記シロキサン誘導体を共 重合体比で 5 %以上、 好ましくは 2 0 %以上含んでいるものが望ましい。 ) を用 いてもよい。 また、 該化合物を構成する他の構成成分は特に限定されるものでは ないが、 該化合物を含む溶液を調製する際に使用される希釈媒体に可溶なものが 好ましい。 なお、 シロキサン誘導体をその構成要素の一部に持つとは、 拈着剤ポ リマー、 放射線重合性化合物等の粘着剤の構成材料の骨格中あるいは側鎖を形成 していることを意味する。
以上の反応性基を有する有機化合物、 酸、 酸誘導体、 および一般式 ( I ) で表 されるシロキサン誘導体、 シロキサン誘導体を持つ化合物は、 1種を単独で用い てもよいし、 2種以上を併用してもよく、 必要に応じて水または有機溶剤で希釈 することが可能である。 上記化合物を含有する希釈溶液の濃度は、 上記化合物お よび溶剤の種類により種々異なるが、 通常は 0 . 0 1 %〜 3 0 %、 好ましくは
0 . 0 5 %〜 1 0 %である。
本発明の半導体素子の製造方法においては、 リードフレームに接続された半導 体チップを封止樹脂にて封止する前に、 上記の反応性基を有する有機化合物、 酸、 酸誘導体、 および一般式 ( I ) で表されるシロキサン誘導体、 該シロキサン誘導 体をその構成要素の一部に持つ化合物からなる群から選ばれる少なくとも一の化 合物にて、 リードフレームおよび Zまたは半導体ウェハもしくは半導体チップを 処理する。 これら半導体チップなどを処理する段階は、 封止前であれば、 いずれ の段階でもよく、 ダイシング前の半導体ウェハ、 ダイシング後の半導体ウェハ ( 半導体チップ) などの面に、 上記化合物またはその希釈溶液をスピンコートなど のコ一ティング、 塗付、 噴霧テープまたはフィルム状物 (ウェハ貼付用拈着シ一 ト) からの転写などの方法により処理してパッケージクラック防止性化合物をこ れら半導体チップなどに付着させるものである。 即ち、 本発明における処理とは、 リードフレームおよび Zまたは半導体ウェハもしくは半導体チップの表面にパッ ケージクラック防止性化合物を付着させるための処理である。
前記にて説明したように、 半導体チップの裏面 (パターン形成面の反対面) に おけるパッケージクラックが特に問題となるので、 少なくとも半導体チッブの裏 面に上記の処理を行うことが望ましい。 また、 リードフレームに上記の処理を行 う場合には、 封止樹脂により封止されるリードフレームの部分は、 少なくとも処 理されることが望ましい。 その下限は 0 . 0 0 5 / m以上、 好ましくは 0 . 0 01 以上、 より好ましくは 0. 0 3 um以上であり、 これらの膜厚は、 特に、 全 面処理における場合に好ましい範囲である。
上記化合物またはその希釈溶液の処理後の膜厚は、 上記化合物の種類および溶 液の濃度などにより種々異なるが、 通常は l iim以下、 好ましくは 0 . 1 /im以 下とするのが望ましい。
なお、 本発明においては、 被処理面の全面に対して必ずしも処理することを要 せず、 スポット状に付着させてもよい。 この場合、 E S C Aによる半導体チップ の裏面の表面分析で検出される S i、 C, ◦の各元素のうち、 ブランク (未処理) の半導体チップに較べて、 C量が 4 %以上、 好ましくは 5 %以上とするのが望ま
しい。
本発明の半導体素子の製造方法に使用されるウェハ貼付用拈着シ一トについて 説明する。 該シートは、 ウェハに対するパッケージクラック防止性化合物の転写 処理に使用されるものである。
図 1は、 本発明のウェハ貼付用粘着シートの一実施例を示す断面図である。 図 1に示されるウェハ貼付用拈着シート (以下 「枯着シート」 と略す。 ) 1は、 基 材 2と、 この基材 2の一方面上に積層された拈着剤層 3とから構成されており、 粘着剤層 3にはパッケージクラック防止性化合物が含有されている。 本発明の粘 着シートの形状はテープ伏、 ラベル状などのあらゆる形状をとり得る。
基材 2としては、 耐水性および酎熱性に優れているものが適し、 特に合成樹脂 フィルムが適する。 本発明の拈着シートでは、 その使用に際し、 紫外線 (UV) あるいは電子線 (E B ) などの放射掠の照射が行われる場合には、 それぞれの放 射線を必要量は透過させる材料を用いる必要がある。
このような基材 2としては、 具体的には、 ポリエチレンフィルム、 ポリブロピ レンフィルム、 エチレン一プロピレン共重合体フィルム、 ボリ塩化ビニルフィル 厶、 ポリエチレンテレフ夕レートフィルム、 エチレン酢酸ビニルフィルム、 ボリ ウレタンフィルム、 ポリブチレンテレフ夕レートフィルム、 ポリメチルペンテン フィルム、 ボリブタジエンフィルムなどが用いられる。 ウェハのダイシング後に エキスバンデイング処理をする必要がある場合には、 ボリ塩化ビニル、 ボリォレ フィン、 ポリオレフイン誘導体などの延伸可能なフィルムを用いることが好まし レ、。 これらのフィルムは単独または多層に積層して用いられる。
基材 2の粘着剤塗付側表面 2 aには、 拈着剤の投錨性を向上させるために、 コ ロナ処理、 E B処理、 下塗りなどの既知の処理を行うことが可能である。 基材 2 のフィルムの厚みは、 強度、 放射線透過性の点から通常 2 5 u m〜3 0 0 // m、 好ましくは 3 0〃m〜 3 0 0 ^ より好ましくは 4 0 /z m〜l 8 0 /z mである。 ダイシング時にフルカツトする際は、 切り込んだ後の強度維持の観点から、 7 0 ju m〜 1 8 0 /z mが好ましい。
粘着剤層 3の基材 2との対向面側 3 aには、 必要に応じてシリコン処理などが
施された剝雜フィルム、 あるいは無処理のポリエチレン、 ポリプロピレン、 フッ 素系の剝雜フィルムを設けることが可能である。
粘着剤層 3を主として構成する粘着剤としては、 従来公知の粘着剤が用いられ るが、 例えば天然ゴムや各種の合成ゴムなどのゴム系ポリマー、 あるいは (メタ) ァクリル酸アルキルエステルとこのエステルに共重合可能な他の不飽和単量体と の共重合物などのァクリル系ボリマ一をベースポリマ一とし、 ボリイソシァネー ト化合物、 アルキルエーテル化メラミン化合物、 エポキシ系化合物、 シランカツ プリング剤などの架橋剤が配合されたものが例示される。 なお、 上記のベースポ リマーが放射線により分子内にて重合する炭素一炭素二重結合を持つものであつ てもよい。 また、 粘着剤層 3は異なる成分、 配合からなる多層状構造をとること も可能である。
接着力向上成分として、 パッケージクラック防止性化合物は、 1種を単独で用 いてもよいし、 2種以上を併用してもよく、 その使用量は、 ベースポリマー 100 重量部に対して、 酸および酸誘導体以外のものは 0 . 1重量部〜 1 0重量部、 好 ましくは 0 . 5重量部〜 4重量部の範囲とするのがよく、 酸および酸誘導体は 0 . 1〜1 5 0重量部、 好ましくは 0 . 1〜1 0 0重量部、 より好ましくは 0. 5 〜 5重量部の範囲とするのがよい。 拈着剤の架橋反応あるレ、は放射線硬化反応に おいて、 酸、 酸誘導体が反応する場合には、 未反応の酸、 酸誘導体、 あるいは酸、 酸誘導体と粘着剤成分とが反応して形成されたォリゴマーが粘着剤層 3中に残る ように、 酸、 酸誘導体を通常よりも多めに配合するのがよい。 特に、 放射線重合 性化合物である場合には 3 0〜 100重量部の範囲が好ましい。
粘着剤層 3中へのパッケージクラック防止性化合物の含有方法は、 粘着剤を配 合する際に混入して拈着剤層 3全体に含ませる、 あるいは、 パッケージクラック 防止性化合物を含有してなる粘着剤層を全体の粘着剤層中の表層部のみ設ける、 粘着剤曆表面に塗付するなど、 ゥェハ裏面に移行可能な形態ならばどのようなも のも可能である。
粘着剤が放射線硬化型粘着剤である場合には、 上記拈着剤に放射線により硬化 して三次元網状化し、 放射線にて重合する、 分子中に少なくとも 2個の炭素一炭
素二重結合を有する低分子量化合物 (以下 「放射線重合性化合物」 という。 ) を 配合し、 さらに硬化手段が U Vである場合には、 光重合開始剤を配合することが 好ましい。
放射線重合性化合物は、 その分子量が通常 10. 000以下程度であるのがよく、 よ り好ましくは、 放射線照射による拈着剤曆 3の三次元網状化が効率よくなされる ように、 その分子量が 5, 000 以下でかつ分子内の放射線重合性炭素一炭素二重結 合の数が 2〜6個のものを用いるのがよい。 例えばトリメチ ールプロパントリ ァクリレート、 テトラメチロールメタントリアタリレート、 テトラメチロールメ タンテトラアタリレート、 ベン夕エリスリ トールトリアタリレート、 ペン夕エリ スリ トールテトラァクリレート、 ジペン夕エリスリ トールモノヒドロキシペンタ アタリレート、 ジペン夕エリスリ トールへキサァクリレート、 1 , 4ーブチレン グリコールジァクリレート、 1 , 6—へキサンジオールジァクリレート、 ポリエ チレングリコールジァクリレート、 市販のオリゴエステルァクリレート、 下記の ウレタンァクリレート系オリゴマーなどのアタリレート系化合物、 特公平 5— 2 5 9 0 7号公報 (特に従来技術の攔) に開示されているようなオルガノノポリシ ロキサン組成物などが挙げられる。
ウレタンァクリレート系オリゴマ一はポリオール化合物と、 多価ィソシァネー トと、 ヒドロキシ (メタ) アタリレート等により合成される化合物である。
多価イソシァネートとしては、 例えばトルエンジイソシァネート、 フヱニレン ジイソシァネート、 へキサメチレンジイソシァネート、 ジフエニルメタンジイソ シァネート、 ジメチルジフエニルジイソシァネート、 ジシクロへキシルメタンジ イソシァネート、 キシレンジイソシァネートなどが挙げられる。
ポリオール化合物としては、 例えばエチレングリコール、 プロピレングリコー ノレ、 ジエチレングリコール、 ブタンジオール、 ペンタンジオール、 トリメチロー ルェタン、 トリメチロールプロパン、 ペン夕エリスリ トールなどが挙げられる。 ヒドロキシ (メタ) ァクリレートとしては、 例えば 2—ヒドロキシェチル (メ 夕) アタリレート、 ボリエチレングリコール (メタ) ァクリレート、 ペン夕エリ スリ トールトリァクリレートなどが挙げられる。
本発明において放射線重合性化合物としては、 アタリレート系化合物、 特にべ ン夕エリスリ トール類、 中でもジペンタエリスリ トールへキサァクリレートが好 ましい。
放射線重合性化合物としては、 上記の化合物のうちの 1種を単独で用いてもよ いし 2種以上を併用してもよく、 その使用量は、 ベースボリマ一 1 0 0重量部に 対して、 1重量部〜 1 2 0重量部、 好ましくは 1重量部〜 1 0 0重量部、 より好 ましくは 2 0〜1 0 0重量部の範囲とするのがよい。 1重量部未潢であると、 枯 着剤層 3の放射線照射による三次元網状化が不十分となり、 拈着シート 1のチッ ブに対する粘着力の低下の程度が小さ過ぎて好ましくない。 反対に、 1 2 0重量 部を超えると、 粘着力との相溶性が悪くなりテープとした時に白濁化するなどの 問題点がある。
上記の光重合開始剤としては、 例えばイソプロピルべンゾインエーテル、 イソ ブチルベンゾインエーテル、 ベンゾフエノン、 ミヒラーズケトン、 クロ口チォキ サントン、 ドデシルチオキサントン、 ジメチルチオキサントン、 ァセトフヱノン ジェチルケタール、 ベンジルジメチルケタール、 α—ヒドロキシシクロへキシル フエ二ルケトン、 2—ヒドロキシメチルフエニルプロパンなどが挙げられ、 これ らのうちの 1種を単独で、 あるいは 2種以上の混合で使用すればよい。
この光重合開始剤の使用量としては、 通常、 上記のベースボリマ一 1 0 0重量 部に対して 0 . 1重量部〜 1 0重量部、 好ましくは 0 . 1重量部〜 5重量部の範 囲とするのがよい。 0 . 1重量部未満であると、 粘着剤層 3の U V照射による三 次元網状化が不十分となり、 粘着シートのチップに対する粘着力の低下の程度が 小さ過ぎて好ましくない。 反対に、 10重量部を超えると、 それに見合う効果が得 られないばかりか、 チップ裏面にこの光重合開始剤が残留するため好ましくなレ、。 なお、 必要に応じてこの光重合開始剤とともにトリェチルァミン、 テトラエチル ペン夕アミン、 ジメチルアミノエ夕ノールなどのアミン化合物を光重合促進剤と して併用してもよい。
さらに必要に応じて被着体であるウェハとの粘着力をコントロールするために、 タツキファイア、 粘着調整剤、 界面活性剤、 あるいはその他の改質剤および慣用
成分を配合することができる。 ただし、 界面活性剤または界面活性を示す化合物 は本発明の目的を達成するために、 なるべく少ない方が好ましい。
上記の各成分が混合されてなる粘着剤組成物を用いて枯着剤層 3を形成するに は、 例えば放射線透過性の基材 2上にこの組成物を塗付し、 必要に応じて加熱す ればよい。 このようにして形成される拈着剤層 3の厚みとしては、 通常 5 ζ π!〜 4 0〃m、 好ましくは 5 π!〜 2 5 i mとするのがよい。
粘着剤層 3と、 拈着剤層 3上に載置されるウェハ Aとの間の 9 0度剝雜接着力 は、 ウェハ Aを切断分雜した後に、 拈着シート 1からの半導体チップのピックァ ッブを容易にするために、 3 0 0 gZ 2 5 mm以下、 好ましくは 2 5 0 2 5 mm以下に設定することが望ましい。 その下限は 1 5 gZ 2 5 mm以上、 好まし くは 2 5 g Z 2 5 mm以上であることが望ましい。 また、 放射線硬化型の坫着シ 一トである場合には、 1 2 5 g Z 2 5 mm以下、 好ましくは 1 0 0 2 0 mm 以下に設定することが望ましく、 その下限は 1 gZ 2 5 mm以上であることが好 ましい。 この剝雜接着力は、 坫着シート 1を幅 2 5 mmに切断し、 トルエンで洗 浄したウェハの裏面に貼付して 3 0分間放置した後、 2 3 'C、 相対湿度 6 5 %の 条件下、 3 0 O mm/分で 90度剝離することによって測定される。 なお、 粘着シ 一ト 1が放射線硬化型の粘着シートである場合には、 放射線を基材 2側から照射 して、 剝離接着力が低下した後に測定する。
次に、 本発明の拈着シ一トを用いた本発明の分離方法について説明する。
まず図 1に示されるように、 粘着シート 1の粘着剤層 3上にダイシングされる べきウェハ Aを載置し、 感圧接着して固定した後、 ウェハ Aをダイシング、 洗浄、 乾燥の各工程に付する。
その後、 図 2に示されるように、 粘着シート 1の基材 2側から粘着剤層 3に放 射線 Bを照射して、 拈着剤層 3の粘着力を低下させる。 本発明方法において、 放 射線 Bの照射手段および照射方法は特に限定されず、 表面処理、 放射線硬化性塗 料、 放射線硬化性接着剤などの技術分野において一般に実施されている常套手段、 方法が採用される。 次に、 枯着シ一ト 1をエキスパンディングして、 切断された 各半導体チップ A 1, A 2 , A 3 · · ·間をピックアップに充分な間隔とする。
なお、 粘着シート 1をエキスパンデイングした後に、 放射線 Bを照射するように してもよい。
放射線 Bの照射は、 粘着シートからの転写量を増やすために、 粘着剤層 3が完 全に硬化する前に終了することが可能である。 放射線重合性化合物に本発明の目 的の機能を持たせた場合には、 放射線 Bの照射は粘着剤層 3が完全に硬化する前 に終了することが好ましい。 かくして、 半導体チップの裏面に、 例えば酸および Zまたは酸誘導体と拈着剤成分とが反応して形成されたオリゴマーを主成分とす る付着物が付着する。 このときの付着物の量は、 粘着剤層が完全に硬化した際の 付着物の量よりも多くなるので、 付着物中に含まれる、 例えば酸および/または 酸誘導体を介して、 半導体チップの裏面と封止樹脂との間の粘着力が向上し、 パ ッケージクラックが防止される。 また、 半導体封止樹脂の成形用金型からの剝離 性および各半導体チッブとの間の接着性がともに向上するので、 半導体封止樹脂 の設計が容易となる。
適切な放射線 Bの照射量または時間は、 例えば、 レーザー表面検査装置、 各種 顕微鏡観察、 E S C Aなどの表面分析装置により、 放射線の照射量または時間と 拈着シートからのパーティクルの付着量の関係を測定し、 付着量が比較的多い ( 最大値または極小値あるいはそれらの近傍付近の値となる) 放射線照射量または 時間を選ぶことで決定することができる。 さらに、 適切な放射線 Bの照射量また は時間を決定する上で考慮すべき点は、 半導体チップ A 1 · · ·を枯着シート 1 からピックアップする際に、 粘着剤が半導体チップ A 1 · · ·の裏面に付着しな いように、 粘着シート 1と半導体チップ A 1 · · ' との間の粘着力を低下させる のに充分な照射量または時間とすることである。 なお、 完全に硬化する前の好ま しい伏態としては、 赤外吸収スペクトルで測定した際、 二重結合由来のピークが 減少を続けている状態である。
次に、 拈着シート 1を図示しないピックアップステーションへ移送し、 図 3に 示されるように、 基材 2側から突き上げ針扞 5によって、 ピックアップすべき半 導体チップ A 1 · · 'を突き上げ、 突き上げられた半導体チップ A 1 · · ·を例 えばエアピンセッ ト 6によってピックアップし、 所定の基板上にマウンティング
する。 なお、 放射線 Bの照射は、 ピックアップステーションにおいて行ってもよ い。
本発明の分雜方法においては、 拈着シ一ト 1をエキスパンディングする工程は 必須ではなく、 ウェハ Aをダイシング、 洗浄、 乾燥の各工程に付した後、 枯着シ ート 1に放射線 Bを照射し、 切断された各半導体チップ A 1 · · ·をピックアツ プしてもよい。
本発明の半導体素子の製造方法によれば、 接着力向上成分である上記化合物に てリードフレームおよび/または半導体チップ (もしくは半導体ウェハ) を処理 するので、 リードフレームと封止樹脂との間の接着力および Zまたは半導体チッ プと封止樹脂との間の接着力が向上し、 リードフレームおよび半導体チップを封 止樹脂にて封止した際に、 パッケージクラックが防止される。 半導体チップの裏 面に対して高価なボリイミ ド樹脂で被覆する必要がなく、 生産コストを抑えるこ とができる。 さらに、 半導体封止樹脂の成形用金型からの剝雜性および半導体チ ップとの間の接着性がともに向上するので、 半導体封止樹脂の設計が容易となる。 また、 本発明の枯着シートは本発明の半導体素子の製造方法に便宜的に使用でき るものである。
以下、 本発明を詳細に説明するため実施例を挙げるが、 本発明はこれら実施例 によって何ら限定されるものではない。
〔実施例 1〜 9〕
a . 引張剝雜カ
シリコンウェハをダイシングして得られた 7 . 5 mmC3の半導体チップの裏面 (パターン形成面の反対面) 側に、 表 1に示される化合物の 5 %トルエン溶液 0 . 1 m 1を滴下し、 スピンコータにて 8 0 0 r p m, 2 0秒処理して乾燥させ た。 図 4に示されるように、 7 . 5 mmC]の半導体チップ A 1上に直径 2 mmの 開口部 7を有する力ブトンテープ 8を貼付し、 この開口部 7にて半導体チップ A 1の裏面 1 0に接触するように、 半導体封止樹脂 (日東電工株式会社製: M P - 1 9 0 ML ) にて円维台状のモールド 9 aを成形し、 矢符 X, Y方向に剝雜速度 5 mm/m i nにて引っ張り、 各々の引張剝離カを測定した。 その結果を同じく
表 1に記載する。
b. パッケージクラック発生の有無
シリコンウェハをダイシングして得られた 7. 5mmClの半導体チップの裏面 (パターン形成面の反対面) 側に、 表 1に示される化合物の 5%トルエン溶液 0. 1m lを滴下し、 スピンコータにて 8 0 0 r pm, 20秒処理して乾燥させ た。 図 5に示されるように、 半導体チップ A 1を裏面 1 0が上となるように、 銀 ぺ一スト 1 1にてリードフレーム 1 2が接続されたダイパッド 1 3上に固定し、 半導体封止樹脂 (日東電工株式会社製: MP— 1 9 0 L) にて 8 0ピン一 QF Pのパッケージ 9 bを成形し、 半導体素子 Sを得た。 8 5° (、 85%RH中に 72 時間保存し、 遠赤外線加熱にて 240て、 1 0秒間加熱した。 半導体素子 Sには、 半導体チップ A 1の裏面 1 0と封止樹脂 (パッケージ) 9 bとの界面に起因する クラックは発生せず、 良好な結果が得られた。
〔比較例 1〕
表 1に示される化合物のトルエン溶液を塗付する代わりに、 トルエンにて半導 体チップの裏面を洗浄する以外は、 実施例と同様の操作を行って、 引張剝雜力お よびパッケージクラック発生の有無を調べ、 その結果を表 1に記載した。 半導体 素子には、 半導体チップの裏面と封止樹脂との界面に起因する面の剝雜が認めら れた。
表 1
* 1 : 日本ボリウレタン株式会社製、 コロネート L
* 2 :大日本インキ化学工業株式会社製、 スーパーべッカミ ン J 一 8 2 0
* 3 :三菱瓦斯化学株式会社製、 テトラッ ド C_ ―
* 4 :信越 学工業株式会社製、 シランカツブリング剤 K B M— 9 0 3
* 5 :信越化学工業株式会社製、 シランカップリング剤 K B P— 4 4
* 6 : ビス ( 3—ァミノプロピル) テトラメチレンジシロキサン
〔実施例 1 7〜 20〕
a. 剪断接着力
トリクロ口ェタンにて洗浄された銅のリードフレーム (26mmx 35mmx 0. 25 mm) を表 2に示される化合物の 0. 5 %トルエン溶液に浸漬した後、 速やかにスピンコ一夕にて 80 0 r pm, 20秒処理して乾燥させた。 図 6に示 されるように、 リードフレーム 1 2上に、 上面の直径が 3. 8 mm. 下面の直径 が 4. 4 mm. 高さが 3 mmの円錐台伏のモールド 9 aを半導体封止樹脂 (日東 電工株式会社製: MP— 1 90ML) にて成形した。 測定治具を用いてリードフ レーム 1 2を固定し、 ォートグラフ速度 5mm/m i nにてモールド 9 aに矢符 Z方向の荷重を負荷して、 剪断接着力を測定した。 その結果を同じく表 2に記載 する。
b. パッケージクラック発生の有無
リ一ドフレームを表 2に示される化合物の 0. 5 %トルエン溶液に浸漬した後、 速やかにスピンコ一夕にて 8 0 0 r pm, 20秒処理して乾燥させた。 パッケ一 ジを 8 0 L-QFP (1 4mmx 2 Ommx 0. 4 mm) 、 タブを 8 mm x 8 m m、 シリコンチップを 8mmC]、 リードフレームを 42ァロイ (0. 1 5 mm厚) ダイボンドを銀ペーストとして、 半導体素子を作製し、 8 5'C、 85%RH中に 72時間保存し、 遠赤外線加熱にて 24 0 eC、 1 0秒間加熱した。 半導体素子に は、 リードフレームと封止樹脂 (パッケージ) との界面に起因するクラックは発 生せず、 良好な結果が得られた。
〔比較例 2〕
表 2に示される化合物のトルェン溶液を塗付する代わりに、 トルェンにてリー ドフレームを洗浄する以外は、 実施例と同様の操作を行って、 剪断接着力および パッケージクラック発生の有無を調べ、 その結果を表 2に記載した。 半導体素子 には、 リ一ドフレームと封止樹脂との界面に起因するクラックが一部発生してい
表 2
* 1、 * 5は、 表 1のそれと同じである。
〔実施例 2 1〜 2 3 ·比較例 3〕
下記の粘着剤 a〜dを厚さ 5 0 mのポリエステルフィルム上に塗工して、 拈 着剤層の厚さが 2 0 // mであるウェハ貼付用粘着シートをそれぞれ作成した。 な お、 下記の粘着剤組成において部とあるのは重量部を意味する。
(実施例 2 1 )
粘着剤 a :ァクリル系粘着剤 1 0 0部
ウレタンァクリ レート 3 0部 光重合開始剤 3部 シランカップリング剤 2部
(信越化学工業株式会社製、 商品名: K B P - 4 4 )
(実施例 2 2 )
粘着剤 b :アタリル系拈着剤 1 0 0部
ウレタンァクリ レート 3 0部 光重合開始剤 3部 シランカップリング剤 0 . 5部
(信越化学工業株式会社製、 商品名: K B P - 4 4 )
(実施例 2 3 )
粘着剤 c :アクリル系粘着剤 1 0 0部 ウレタンァクリレート 3 0部
ビス (3—アミノブ口ピル) テトラメチレンジシロキサン 1部
(比較例 3 )
粘着剤 d :アクリル系粘着剤 1 00部 ウレタンァクリレート 3 0部 光重合開始剤 3部
〔90度剝雜接着力〕
実施例 2 1〜23 ·比較例 3の拈着シートの基材面側から、 空冷式高圧水銀灯 を用いて、 UV (4 6 m J/cm2 · s) を 1 0秒間照射し、 上述の 90度剝離 接着力を測定したところ、 実施例 2 1〜23では 1 9 gZ25 mm. 比較例 3で は 1 8 gノ 25 mmであった。
〔半導体チップの分離〕
実施例 2 1〜23 ·比較例 3の坫着シートにシリコンウェハをそれぞれ貼付し、 サイズが 5 mm X 5 mmのシリコンチップにフル力ットした。 ダイシング後に、 各粘着シートの基材面側から、 空冷式高圧水銀灯を用いて、 UV (4 6mJXc m2 · s) を 7秒間照射し、 シリコンチップをピックアップした。 これらチップ の半導体封止樹脂との引張剝雜カを以下のようにして測定し、 その結果を表 3に まとめた。
〔チップ引張剝雜力〕
図 4に示されるように、 5mmClサイズのシリコンチップ A 1上に直径 2 mm の開口部 7を有するカブトンテープ 8を貼付し、 この開口部 7にてシリコンチッ ブ A 1に接触するように、 半導体封止樹脂 (日東電工株式会社製: MP - 1 9 0 ML) にてモールド 9 aを成形し、 剝雜速度 5 mmZm i nにて、 矢印方向 X、 Yに引っ張り引張剝雜カを測定した。 なお、 粘着シートはウェハの裏面上に貼付 し、 ダイシングされたシリコンチップ A 1の裏面 1 0上に半導体封止樹脂層 (モ 一ルド) 9 aを成形した。
表 3
実施例 2 1 実施例 22 実施例 23 比較例 3
引張剝雜カ 5200 g 4360 g 4 850 g 2570 g
〔パッケージクラック発生の有無〕
実施例 2 1〜2 3 ·比較例 3の拈着シートを用いて 7 . 5 mmC]サイズにシリ コンウェハをダイシングして、 シリコンチップ A 1をそれぞれの粘着シートから 分離した。 図 5に示されるように、 シリコンチップ A 1の裏面 0が上となるよ うに、 銀ペースト 1 1にてリードフレーム 1 2が接続されたダイパッド 1 3上に チップ A 1を固定し、 半導体封止樹脂 (日東電工株式会社製: M P - 1 9 0 ML ) にて Q F P— 8 0のパッケージ 9 bを成形した。 8 5で、 8 5 % 11 中に7 2時 間保存し、 遠赤外線加熱にて 2 4 0で、 1 0秒間加熱した。
その結果、 実施例 2 1〜2 3の拈着シートから分離されたチップ A 1の半導体 パッケージには、 チップの裏面と封止樹脂との接触に起因するクラックは生じな かったのに対して、 比較例 3の場合、 面の剝離が認められ、 良好な結果は得られ なかった。
〔ウェハ貼付用粘着シ一トの製造例〕
2 4〜 3 1 ·比較例 4〕
下記の粘着剤 e〜mを厚さ 5 0〃mのポリエステルフィルム上に塗工して、 粘 着剤層の厚さが 2 0 t mであるウェハ貼付用拈着シ一トをそれぞれ作成した。 な お、 下記の粘着剤組成において部とあるのは重量部を意味する。
(実施例 2 4 )
粘着剤 e :アクリル系粘着剤 1 0 0部
ジペンタエリスリ トールへキサァクリレート 3 0部 光重合開始剤 3部
(実施例 2 5 )
粘着剤 f :アタリル系粘着剤 1 0 0部
ジペンタエリスリ トールへキサァクリレート 3 0部 光重合開始剤 3部 無水フタル酸 1部
(実施例 2 6 )
粘着剤 g :アクリル系粘着剤 1 0 0部
ウレタン了ク リ レート 3 0部 光重合開始剤 3部 無水マレイン酸 1部
(実施例 2 7 )
粘着剤 h :アクリル系粘着剤 1 0 0部
ウレタンアタリ レート 3 0部 光重合開始剤 3部 無水フタル酸 1部 (実施例 2 8 )
粘着剤 i :アタリル系粘着剤 1 0 0部
ウレタンァクリ レート 3 0部 光重合開始剤 3部 リ ン酸 1部 (実施例 2 9 )
粘着剤 j :アタリル系粘着剤 1 0 0部
テトラメチロールメタントリァクリ レート 3 0部 光重合開始剤 3部 (実施例 3 0 )
粘着剤 k :ァクリル系粘着剤 1 0 0部
ウレタンアタリ レート 3 0部 シランカツプリ ング剤 (K B P— 4 4 ) 2部 光重合開始剤 3部 (実施例 3 1 )
粘着剤^ : アクリル系粘着剤 1 0 0部
ウレタンァクリ レート 3 0部 シランカツプリ ング剤 (K B M— 9 0 3 ) 2部 光重合開始剤 3部
(比較例 4 )
粘着剤 m:アタリル系粘着剤 1 00部
ウレタンァクリレート 30部 光重合開始剤 3部 これら粘着シートを用いて半導体チップを分離するに際して、 粘着シートの拈 着剤曆に照射する U Vの照射時間を決定するために、 先ず粘着剤 eを用いた実施 例 24の粘着シ一トについて以下の試験を行った。
① UV照射による粘着シートとウェハとの粘着力の経時変化
ウェハの裏面 (パターン形成面の反対面) 上に、 幅 2 Omm, 長さ 1 00mm の短冊状の本粘着シートを貼付し、 UV照射時間を変化させた際のウェハの拈着 力の変化を調べた。 なお、 本拈着シートを貼付して 30分後に、 空冷式高圧水銀 灯を用いて UV (46m J/cm2 * s) を照射し、 23で、 55%RH中で、 剝雜速度 30 Omm/m i n、 剝離角度 90° にて粘着力を調べ、 その結果を図 7に示した。 UV硬化反応が進行するには、 UVの照射時間は約 1秒以上必要で あることが、 図 7のグラフから判る。
② UV照射によるパーティクル数の経時変化
4インチウェハの裏面 (パターン形成面の反対面) 上に本拈着シートを貼付し、 30分後に UV (46mJ/cm2 · s) を照射した後、 本粘着シートを剝雜し て、 レーザー表面検査装置を用いて、 裏面上に形成された 0. 28; πι以上のパ 一ティクル (オリゴマーを主成分とする付着物) の数を測定した。 UV照射時間 を変えて測定した結果を図 8に示す。 パーティクル数は、 UV照射を 2秒間行つ た際に最大となることが図 8のグラフから判る。 なお、 本拈着シートの粘着剤を 完全に硬化させるには、 UVを通常 7秒間程度照射する必要があり、 UV照射を 2秒間で終了させれば、 未反応の粘着剤成分 (ジペンタエリスリ トールへキサァ クリレートなど) 、 あるいは粘着剤成分が反応して形成されたオリゴマーが粘着 剤層中に残存することとなる。
以上、 ウェハの粘着力およびパーティクル数の UV照射による経時変化の試験 結果から、 粘着剤 eを用いた実施例 24の粘着シートにおける UV照射時間は 2 秒間が望ましいことが判る。 また、 粘着剤 f の組成は、 粘着剤 eの組成と略同様
であるので、 UVの照射時間は 2秒間が望ましいことが判る。
上記と同様の操作により、 坫着剤 gについて UVの最適な照射時間を求めたと ころ、 7秒間であることが判った。 なお、 粘着剤 h, i, mの組成は、 粘着剤 g の組成と略同様であるので、 UVの照射時間は 7秒間が望ましいことが判る。 〔半導体チッブの分雜〕
実施例 24〜3 1 ·比較例 4の粘着シートにシリコンウェハをそれぞれ貼付し、 サイズが 5 mm X 5 mmのシリコンチップにフルカツトした。 ダイシング後に、 各粘着シートの基材面側から、 空冷式高圧水銀灯 (4 6mJZcm2 · s ) を用 いて、 UVを 2秒間 (実施例 24、 25、 29〜3 1 ) または 7秒間 (実施例 2 6〜28 '比較例 4) 照射し、 シリコンチップをピックアップした。 これらチッ ブの半導体封止樹脂との引張剝離カを以下のようにして測定し、 その結果を表 4 にまとめた。
図 4に示されるように、 5mmC]サイズのシリコンチップ A 1上に直径 2mm の開口部 7を有するカブトンテープ 8を貼付し、 この開口部 7にてシリコンチッ プ A 1に接触するように、 半導体封止樹脂 (日東電工株式会社製: MP— 1 9 0 ML) にてモールド 9 aを成形し、 剝離速度 5mmZm i nにて引張剝雜カを測 定した。 なお、 粘着シートはウェハの裏面上に貼付し、 ダイシングされたシリコ ンチップ A 1の裏面 1 0上に半導体封止樹脂層 (モールド) 9 aを成形した。
表 4
〔パッケージクラック発生の有無〕
実施例 24〜3 1 '比較例 4の枯着シートを用いて 7. 5mmC]サイズにシリ コンウェハをダイシングして、 シリコンチップ A 1をそれぞれの拈着シ一トから 分雜した。 図 5に示されるように、 シリコンチップ A 1の裏面 1 0が上となるよ
うに、 銀ペースト 1 1にてリードフレーム 1 2が接続されたダイパッ ド 1 3上に チップ A 1を固定し、 半導体封止樹脂 (日東電工株式会社製: M P - 1 9 0ML) にて QFP— 80のパッケージ 9 bを成形した。 85°C、 8 5%1¾11中に72時 間保存し、 遠赤外線加熱にて 24 0で、 1 0秒間加熱した。
その結果、 実施例 24〜3 1の粘着シートから分離されたチップ A 1の半導体 パッケージには、 チップの裏面と封止樹脂との接触に起因するクラックは生じな かったのに対して、 比較例 4の場合、 面の剝離が認められ、 良好な結果は得られ なかった。
本発明を上述の明細書およびそれに含まれる実施例に -、り適切かつ十分に説明 したが、 それらは本発明の精神および範囲を逸脱することなく変更または修飾す ることができる。
Claims
1 . リードフレームおよび zまたはウェハ若しくは半導体チップを、 反応性基 を有する有機化合物 (但し、 下記の酸、 その酸としての特性を示す基における誘 導体は除く) 、 酸、 該酸の酸成分となる置換基における誘導体 (以下、 酸誘導体) 〔但し、 酸、 酸誘導体中、 一般式 ( I ) に含まれるものは除く〕 、 および式 ( I )
〔但し、 式中 R l、 R 2、 R 3および R 4は、 互いに同一または異なっていて もよい 1価の有機基であり、 nおよび mは、 それぞれ 0または 1以上の整数を示 し、 nと mとの和は、 1〜1 0 0 0である。 〕
で表されるシロキサン誘導体および該シロキサン誘導体をその構成中に含む数平 均分子量 1 0 0 0 0以下の化合物から選ばれる少なくとも一種よりなるパッケ一 ジクラック性防止化合物にての処理に付する工程を含むことを特徵とする半導体 素子の製造方法。
2 . 反応性基を有する化合物が水酸基との反応性基を有する有機化合物である 請求の範囲第 1項記載の半導体素子の製造方法。
3 . 水酸基との反応性基を有する有機化合物が分子量 1 0 0 0以下の化合物で ある請求の範囲第 2項記載の半導体素子の製造方法。
4 . 反応性基を有する有機化合物がシランカップリング剤、 イソシアナ一ト系 架橋剤、 エポキシ系架橋剤およびメラミン系架橋剤から選ばれる請求の範囲第 1 項記載の半導体素子の製造方法。
5 . 酸および酸誘導体が、 無機酸、 有機カルボン酸、 そのカルボキシル基にお ける誘導体、 スルホン酸、 またはそのスルホン基における誘導体である請求の範 囲第 1項記載の半導体素子の製造方法。
6 . 酸および酸誘導体が、 酸成分となる置換基数 (酸誘導体においては、 誘導 体化される前の酸を構成している酸成分となる置換基数) が、 分子の骨格を形成 する元素数 (該置換基を除く。 ) に対して、 5 / 1 0 0以上のものである請求の
範囲第 1項記載の半導体素子の製造方法。
7. 酸が、 リン酸、 無水フタール酸、 無水マレイン酸から選ばれる請求の範囲 第 1項記載の半導体素子の製造方法。
8 . パッケージクラック防止性化合物が粘着剤中に含有された態様で処理に付 される請求の範囲第 1項記載の半導体素子の製造方法。
9 . パッケージクラック防止性化合物が濃度 0. 0 1〜3 0重量 の溶液とされ た態様で処理に付される請求の範囲第 1項記載の半導体素子の製造方法。
1 0 . 処理が、 該ウェハまたは該半導体チップの少なくともパターンが形成さ れていない面に対する処理である請求の範囲第 1項記載の半導体素子の製造方法。
1 1 . 処理手段が、 パッケージクラック防止性化合物のコーティングおよび/ または転写である請求の範囲第 1項記載の半導体素子の製造方法。
1 2 . パッケージクラック防止性化合物にての処理が、 反応性基を有する化合 物 (但し、 下記の酸、 その酸としての特性を示す基における誘導体は除く) 、 酸、 酸誘導体 〔但し、 酸、 酸誘導体中、 一般式 ( I ) に含まれるものは除く〕 、 およ び式 ( I )
で表されるシロキサン誘導体または該シロキサン誘導体残基をその構成中に含む 数平均分子量 1 0 0 0 0以下の化合物から選ばれる少なくとも一種よりなるパッ ケージクラック防止性化合物を含む粘着剤からなる層が、 基材面上に積層されて なるゥェハ貼付用粘着シートの粘着剤層上に、 ゥェハを載置することによる転写 処理である請求の範囲第 1項記載の半導体素子の製造方法。
1 3 . 粘着剤が放射線硬化型粘着剤である請求の範囲第 1 2項記載の半導体素 子の製造方法。
1 4 . 基材面上に放射線硬化型粘着剤が積層されてなるウェハ貼付用拈着シ一 ト上にウェハを載置した後、 該ウェハを切断して複数の半導体チップを得、 該拈 着剤層に放射線を照射して、 該粘着剤層を硬化させた後、 切断された半導体チッ プを分離する工程を経る半導体素子の製造方法であって、 該粘着剤が完全に硬化 する前に放射線の照射を終了することを特徵とする請求の範囲第 1 3項記載の半 導体素子の製造方法。
1 5 . 半導体チップを半導体封止樹脂にて封止する工程を経ることを特徵とす る請求の範囲第 1 4項記載の半導体素子の製造方法。
1 6 . 反応性基を有する化合物 (但し、 酸、 その酸としての特性を示す基にお ける誘導体は除く) 、 酸、 酸誘導体 〔但し、 酸、 酸誘導体中、 一股式 ( I ) に含 まれるものは除く〕 、 および式 ( I ) R 1 - R 1 ( I )
〔但し、 式中 R l、 R 2、 R 3および R 4は、 互いに同一または異なっていて もよい 1価の有機基であり、 n及び mは、 それぞれ 0または 1以上の整数を示し、 nと mとの和は、 1〜1 0 0 0である。 〕
で表されるシロキサン誘導体および該シロキサン誘導体をその構成中に含む数平 均分子量 1 0 0 0 0以下の化合物から選ばれる少なくとも一種よりなるパッケ一 ジクラック性化合物を含有する粘着剤からなる層が、 基材面上に積層されてなる ウェハ貼付用粘着シート。
1 7 . 該粘着剤層と、 該粘着剤層上に載置されるウェハとの間の 9 0度剝離接 着力が、 3 0 0 gZ 2 5 mm以下である請求の範囲第 1 6項記載のシート。