US20170103249A1 - Glass-based substrate with vias and process of forming the same - Google Patents
Glass-based substrate with vias and process of forming the same Download PDFInfo
- Publication number
- US20170103249A1 US20170103249A1 US15/286,803 US201615286803A US2017103249A1 US 20170103249 A1 US20170103249 A1 US 20170103249A1 US 201615286803 A US201615286803 A US 201615286803A US 2017103249 A1 US2017103249 A1 US 2017103249A1
- Authority
- US
- United States
- Prior art keywords
- glass
- substrate
- vias
- major surface
- maximum diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/36—Removing material
- B23K26/38—Removing material by boring or cutting
- B23K26/382—Removing material by boring or cutting by boring
-
- G06K9/00013—
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C15/00—Surface treatment of glass, not in the form of fibres or filaments, by etching
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/0006—Working by laser beam, e.g. welding, cutting or boring taking account of the properties of the material involved
-
- B23K26/0057—
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/36—Removing material
- B23K26/362—Laser etching
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/36—Removing material
- B23K26/38—Removing material by boring or cutting
- B23K26/382—Removing material by boring or cutting by boring
- B23K26/386—Removing material by boring or cutting by boring of blind holes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/36—Removing material
- B23K26/38—Removing material by boring or cutting
- B23K26/382—Removing material by boring or cutting by boring
- B23K26/389—Removing material by boring or cutting by boring of fluid openings, e.g. nozzles, jets
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/36—Removing material
- B23K26/40—Removing material taking account of the properties of the material involved
- B23K26/402—Removing material taking account of the properties of the material involved involving non-metallic material, e.g. isolators
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/50—Working by transmitting the laser beam through or within the workpiece
- B23K26/53—Working by transmitting the laser beam through or within the workpiece for modifying or reforming the material inside the workpiece, e.g. for producing break initiation cracks
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B33/00—Severing cooled glass
- C03B33/02—Cutting or splitting sheet glass or ribbons; Apparatus or machines therefor
- C03B33/0222—Scoring using a focussed radiation beam, e.g. laser
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3649—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer made of metals other than silver
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
- C03C17/36—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal
- C03C17/3602—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer
- C03C17/3668—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions at least one coating being a metal the metal being present as a layer the multilayer coating having electrical properties
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
- C03C21/001—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions
- C03C21/002—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions to perform ion-exchange between alkali ions
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C23/00—Other surface treatment of glass not in the form of fibres or filaments
- C03C23/0005—Other surface treatment of glass not in the form of fibres or filaments by irradiation
- C03C23/0025—Other surface treatment of glass not in the form of fibres or filaments by irradiation by a laser beam
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/078—Glass compositions containing silica with 40% to 90% silica, by weight containing an oxide of a divalent metal, e.g. an oxide of zinc
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K1/00—Printed circuits
- H05K1/02—Details
- H05K1/03—Use of materials for the substrate
- H05K1/0306—Inorganic insulating substrates, e.g. ceramic, glass
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K1/00—Printed circuits
- H05K1/02—Details
- H05K1/11—Printed elements for providing electric connections to or between printed circuits
- H05K1/115—Via connections; Lands around holes or via connections
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K3/00—Apparatus or processes for manufacturing printed circuits
- H05K3/0011—Working of insulating substrates or insulating layers
- H05K3/0017—Etching of the substrate by chemical or physical means
- H05K3/002—Etching of the substrate by chemical or physical means by liquid chemical etching
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K3/00—Apparatus or processes for manufacturing printed circuits
- H05K3/0011—Working of insulating substrates or insulating layers
- H05K3/0017—Etching of the substrate by chemical or physical means
- H05K3/0026—Etching of the substrate by chemical or physical means by laser ablation
- H05K3/0029—Etching of the substrate by chemical or physical means by laser ablation of inorganic insulating material
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K3/00—Apparatus or processes for manufacturing printed circuits
- H05K3/22—Secondary treatment of printed circuits
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K3/00—Apparatus or processes for manufacturing printed circuits
- H05K3/40—Forming printed elements for providing electric connections to or between printed circuits
- H05K3/4038—Through-connections; Vertical interconnect access [VIA] connections
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K5/00—Casings, cabinets or drawers for electric apparatus
- H05K5/0017—Casings, cabinets or drawers for electric apparatus with operator interface units
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2101/00—Articles made by soldering, welding or cutting
- B23K2101/36—Electric or electronic devices
- B23K2101/42—Printed circuits
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2103/00—Materials to be soldered, welded or cut
- B23K2103/50—Inorganic material, e.g. metals, not provided for in B23K2103/02 – B23K2103/26
- B23K2103/54—Glass
-
- B23K2203/54—
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
- H05K2201/09—Shape and layout
- H05K2201/09209—Shape and layout details of conductors
- H05K2201/095—Conductive through-holes or vias
- H05K2201/09509—Blind vias, i.e. vias having one side closed
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
- H05K2201/10—Details of components or other objects attached to or integrated in a printed circuit board
- H05K2201/10007—Types of components
- H05K2201/10151—Sensor
Definitions
- the disclosure relates generally to glass-based substrate materials, and specifically to glass-based substrate materials having through holes of sufficient size to allow for metallization as may be used in a sensor arrangement, such as a fingerprint sensor on a portable electronic device.
- Finger print sensors have seen increased use in portable electronic devices, such as smart phones.
- Such sensors typically use a substrate layer supporting conductive layers that connect a sensing device (e.g., a capacitance sensor) to a processing circuit (e.g., a fingerprint application specific integrated circuit (ASIC)) configured to receive and process the sensing signal from the sensing device.
- a sensing device e.g., a capacitance sensor
- a processing circuit e.g., a fingerprint application specific integrated circuit (ASIC)
- One embodiment of the disclosure relates to a process for forming a glass sensor substrate including metallizable through vias.
- the process includes providing a glass substrate, and the glass substrate has a first major surface, a second major surface opposing the first major surface and an average thickness of greater than 0.3 mm.
- the process includes creating a plurality of etch paths through the glass substrate by directing a laser at the substrate in a predetermined pattern.
- the process includes etching a plurality of through vias through the glass substrate along the etch paths using a hydroxide based etching material.
- the hydroxide based etching material preferentially etches the substrate along the etch path such that an etch rate of the etching material along the etch path is at least 12 times greater than an etch rate of the etching material outside of the etch paths.
- Each of the plurality of through vias are long compared to their diameter such that a ratio of the thickness of the glass substrate to a maximum diameter of each of the through vias is greater than 8 to 1.
- An additional embodiment of the disclosure relates to a glass sensor substrate configured to support a sensing element and electrically conductive material that couples the sensing element to a processing circuit.
- the glass sensor substrate includes a first major surface and a second major surface opposite the first major surface.
- the glass sensor substrate includes an interior region located between the first and second major surfaces.
- the glass sensor substrate includes a plurality of chemically etched through holes extending between the first and second major surfaces through the interior region.
- Each of the through holes has a maximum diameter and a minimum diameter, and the substrate has an average thickness of greater than 0.3 mm.
- the maximum diameter of each of the plurality of through holes is less than 100 ⁇ m.
- the through holes do not substantially narrow along their lengths such that a ratio of the minimum diameter to the maximum diameter of each of the through holes is greater than 0.5 such that the electrically conductive material is permitted to fill the through holes providing a conductive path between the first major surface and the second major surface.
- An additional embodiment of the disclosure relates to a glass substrate.
- the glass substrate includes a first major surface and a second major surface opposite the first major surface.
- the glass substrate includes a plurality of through holes extending between the first and second major surfaces, and each of the through holes has a maximum diameter and a minimum diameter.
- the glass substrate is a multicomponent glass material including 50-75% SiO 2 and 10-20% alkali metal oxide, where the alkali metal oxide is at least one of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O.
- the average distance between the first major surface and the second major surface is greater than 0.3 mm.
- a ratio of the average distance between the first major surface and the second major surface to a maximum diameter of each of the plurality of through holes is greater than 8 to 1.
- a ratio of the minimum diameter to the maximum diameter of each of the through holes is greater than 0.5.
- FIG. 1 shows a diagram of a process for forming a glass-based substrate according to an exemplary embodiment.
- FIG. 2 is a perspective view of a substrate according to an exemplary embodiment.
- FIG. 3 is a schematic representation showing formation of laser damage tracks on a substrate according to an exemplary embodiment.
- FIG. 4 is a plot showing etch rates vs. preferential etch rates for two substrate material types and two etching materials.
- FIG. 5 is an image of a substrate with through vias following etching according to another exemplary embodiment.
- FIG. 6 is shows a device incorporating a sensor substrate in a fingerprint sensor according to an exemplary embodiment.
- FIG. 7 shows a schematic view of a finger print sensor according to an exemplary embodiment.
- glass-based means both glasses and glass-ceramics.
- through via means a via that extends through a thickness of a substrate from a first surface to a second surface.
- blind via means a via that extends only partially through a thickness of a substrate from one of first surface or second surface but not to all the way to the other of first surface or second surface.
- a glass-based substrate with vias and a related process for forming the glass substrate with vias are shown and described.
- the glass-based substrate may be used in an application where a substrate with vias may be leveraged, including, but not limited to sensors, for example a fingerprint sensor; semiconductor devices; radio-frequency (RF) devices, such as antennae, switches, and the like; interposer devices; microelectronic devices; optoelectronic devices; and microelectronic mechanical system (MEMS) devices.
- RF radio-frequency
- MEMS microelectronic mechanical system
- high length to width/diameter ratio vias to be formed in relatively thick glass substrate materials (e.g., having a thickness greater than 0.3 mm) via a hydroxide based etching process.
- the glass-based substrate discussed herein is relatively thick and capable of being strengthened (e.g., chemically tempered, heat tempered, etc.) which provides a robust, strong and drop resistant substrate.
- the high aspect ratio vias discussed herein are sufficiently wide and/or have highly consistent widths along their lengths to allow for filling the vias with an electrically conductive material, for example, metallization, which allows the relatively thick and robust substrate discussed herein to be used in sensing applications and allows for relatively high signal to noise ratios.
- metallized through holes are utilized to allow sufficient sensor signal to be communicated from the sensing device through the substrate and to a processing circuit associated with the sensor.
- the process starts with directing a laser (such as a picosecond laser) to a plurality of positions on the substrate.
- the laser interacts with the substrate to form a plurality of etch paths or damage paths through the substrate.
- the laser interaction with the substrate is believed to differentially change the structure and/or chemistry of the substrate along the path of the laser, as compared to adjacent sections of the substrate that did not interact with the laser.
- An exemplary process for forming the etch paths/damage paths is described in U.S. Pub. No. 2015/0166395, which is hereby incorporated by reference in its entirety.
- a variety of hydroxide based etchants preferentially etch the substrate along the laser damage tracks at a highly preferential etch rate.
- This highly preferential etching forms long, relatively wide holes/vias with a highly consistent width/diameter along the length of the hole (e.g., the hole has a low degree of taper, does not significant constrict toward its center, etc.), which allows for metallization, through favorable, low-cost processes such as metallization through metal paste application. It is believed that minimum hole diameter to maximum hole diameter differentials as low as 5 ⁇ m can be achieved using the process discussed herein. In comparison, minimum hole diameter to maximum hole diameter differentials achieved using conventional hydrofluoric acid based etching can be as much as 35 ⁇ m.
- the hydroxide based etchants discussed herein are also capable of etching at high absolute etch rates such that through holes of a desired diameter may be formed in relatively low etch times.
- the hydroxide based etching process discussed herein provides a process that is relatively safe, as compared to conventional hydrofluoric acid based etching techniques, because the hydroxide based etchants tend to be less toxic, less volatile and less caustic than hydrofluoric acid.
- the process discussed herein also provides improved etch performance as discussed herein while also utilizing a less complex and a less expensive etching system compared to conventional hydrofluoric acid etching systems.
- the hydroxide based etching system discussed herein does not utilize ultrasonic or mechanical agitation/vibration to achieve preferential etch rates.
- a flow chart showing a process of forming a glass-based substrate is shown according to an exemplary embodiment.
- a glass-based substrate such as a glass-based sheet or a glass-based wafer
- a plurality of etch paths through the glass-based substrate is formed by directing a laser at the substrate in a predetermined pattern.
- a plurality of vias through the glass-based substrate is formed by etching along the etch paths using a hydroxide based etching material.
- the vias are all through vias; in other embodiments, the vias are all blind vias; and in still other embodiments, the vias are a combination of blind and through vias.
- FIG. 2 shows a glass-based substrate, shown as glass-based substrate 20 .
- Glass-based substrate 20 includes a first major surface, shown as lower surface 22 , a second major surface, shown as upper surface 24 .
- Glass substrate 20 has a thickness, such as an average thickness, shown as Ti.
- T 1 is greater than 0.3 mm, and more specifically greater than 0.5 mm.
- T 1 is greater than 0.3 mm and less than 1.1 mm, and specifically greater than 0.5 mm and less than 1.1 mm.
- T 1 is 0.7 mm.
- the average thickness is determined by measuring the thickness of the glass-based substrate at least three points with an interferometer and averaging the measurements.
- glass-based substrate 20 may be formed from any glass or glass-ceramic material suitable for through hole formation via etching.
- the substrate can be glass and the glass can include fused silica, alkali containing glass (for example alkalialuminosilicate glasses), alkali-free glass (for example an alkali-free alkaline aluminoborosilicate glass), or laminated glass pieces with layers containing different glass compositions.
- glass substrate 20 is a multi-component glass material.
- glass substrate 20 is a multicomponent glass material including 50-75 mol % SiO 2 and 10-20 mol % alkali metal oxide, where the alkali metal oxide is at least one of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O.
- such multicomponent glass is capable of being tempered through ion-exchange processes, as discussed in more detail below.
- glass substrate 20 may be any of the strengthened glass materials described in US Published Patent Application No. 2012/0111057, which is incorporated herein by reference in its entirety.
- glass substrate 20 may be any of the strengthened glass materials described in US Published Patent Application No. 2005/0142364, which is incorporated herein by reference in its entirety.
- glass-based substrate 20 described herein may comprise numerous compositions.
- glass-based substrate 20 comprises an alkali aluminosilicate glass.
- the alkali aluminosilicate glass comprises, consists essentially of, or consists of: 60-70 mol % SiO 2 ; 6-14 mol % Al 2 O 3 ; 0-15 mol % B 2 O 3 ; 0-15 mol % Li 2 O; 0-20 mol % Na 2 O; 0-10 mol % KO; 0-8 mol % MgO; 0-10 mol % CaO; 0-5 mol % ZrO 2 ; 0-1 mol % SnO 2 ; 0-1 mol % CeO 2 ; less than 50 ppm As 2 O 3 ; and less than 50 ppm Sb 2 O 3 ; wherein 12 mol % ⁇ Li 2 O+Na 2 O+K 2 O ⁇ 20 mol % and
- the alkali aluminosilicate glass comprises, consists essentially of, or consists of 64 mol % ⁇ SiO 2 ⁇ 68 mol %; 12 mol % ⁇ Na 2 O ⁇ 16 mol %; 8 mol % ⁇ Al 2 O 3 ⁇ 12 mol %; 0 mol % ⁇ B 2 O 3 ⁇ 3 mol %; 2 mol % ⁇ K 2 O ⁇ 5 mol %; 4 mmol % ⁇ MgO ⁇ 6 mol %; and 0 mol % ⁇ CaO ⁇ 5 mol %, wherein: 66 mol % ⁇ SiO 2 +B 2 O 3 +CaO ⁇ 69 mol %; Na 2 O+K 2 O+B 2 O 3 +MgO+CaO+SrO>10 mol %; 5 mol % ⁇ MgO+CaO+SrO ⁇ 8 mol %; (Na 2 O+B 2 O 3 )—Al 2 O
- the alkali aluminosilicate glass comprises, consists essentially of, or consists of: 5-50 wt % SiO 2 ; 2-20 wt % Al 2 O 3 ; 0-15 wt % B 2 O 3 ; 1-20 wt % Na 2 O; 0-10 wt % Li 2 O; 0-10 wt % K 2 O; and, 0-5 wt % (Mg)+CaO+SrO+BaO); 0-3 wt % (SrO+BaO); and 0-5 wt % (ZrO 2 +TiO 2 ), wherein 0 ⁇ (Li 2 O+K 2 O)/Na 2 O ⁇ 0.5.
- glass-based substrate 20 is formed from a glass composition comprising the following composition when calculated in mol percent and calculated from the batch on an oxide basis: 55-80 SiO 2 , 12-30 Al 2 O 3 , and 2-15 P 2 O 5 . In some embodiments, glass-based substrate 20 is formed from a glass composition comprising a modifying oxide.
- At least one modify ing oxide is selected from the group consisting of Y 2 O 3 , ZrO 2 , HfO 2 , MgO, CaO, SrO, BaO, As 2 O 3 , SnO 2 , Li 2 O, La 2 O 3 GeO 2 , GaO 3 , Sb 2 O 3 , Na 2 O, K 2 O, Rb 2 O Cs 2 O, BeO, Sc 2 O 3 , TiO 2 , Nb 2 O 5 , Ta 2 O 5 , ZnO, CdO, PbO, Bi 2 O 3 , Gd 2 O 31 Lu 2 O 3 and/or B 2 O 3 in a total amount not exceeding 15 mol %.
- the at least one modifying oxide is selected from the group consisting of Y 2 O 3 , ZrO 2 , HfO 2 , MgO, CaO, SrO, BaO, As 2 O 3 , SnO 2 , Li 2 O, La 2 O 3 GeO 2 , Ga 2 O 3 , Sb 2 O 3 , Na 2 O, K 2 O, Rb 2 O, Cs 2 O, BeO, Sc 2 O 3 , TiO 2 , Nb 2 O 5 , Ta 2 O 5 , ZnO, CdO, PbO, Bi 2 O 3 , Gd 2 O 3 , Lu 2 O 3 and/or B 2 O 3 in a total amount not exceeding 7 mol %.
- substrate 20 has a width or diameter (e.g., the width or diameter of surface 22 and/or 24 ) of a size sufficient for use as a sensor substrate.
- the width or diameter (in the case of a circular wafer) of substrate 20 is between 25 mm and 500 mm, specifically between 50 mm and 300 mm and more specifically between 100 mm and 200 mm.
- substrate 20 is a disc having a diameter of about 150 mm and a thickness of about 0.7 mm.
- a schematic view of the creation of etch paths at step 14 is shown according to an exemplary embodiment.
- a laser device 30 is moved, aimed or otherwise controlled to direct laser 32 in a predetermined pattern onto substrate 20 .
- Laser 32 interacts with the material of substrate 20 and is believed to form physical or chemical changes through substrate 20 at the path of laser interaction forming a plurality of etch paths, shown as laser damage tracks 34 .
- Damage tracks 34 extend through a portion or an entirety of substrate 20 at the path of transmission of laser 32 , and as discussed in more detail below, damage tracks 34 provide the site for the preferential etching of substrate 20 to form vias (blind and/or through vias) in substrate 20 .
- the pattern of damage tracks 34 (and consequently, the location of through vias following etching) is selected based on the configuration of the particular sensor components and processing circuit for the sensor that substrate 20 will be used with.
- damage tracks 34 have a diameter or width that is relatively small compared to the eventual size of the vias following etching. In various embodiments, damage tracks 34 have a diameter between 0.05 ⁇ m and 1 ⁇ m and specifically about 0.3 ⁇ m (e.g., 0.3 ⁇ m plus or minus 10%).
- laser 32 may be a wide variety of lasers suitable for forming damage tracks 34 .
- one or more parameter (e.g., power, wavelength, timing, etc.) of laser 32 is selected or controlled to form damage tracks 34 based on one or more characteristic of substrate 20 , such as thickness or glass type, and/or based on the particular type of etchant used to form through vias in step 16 .
- laser 32 is a picosecond line-focused laser, and specifically is a picosecond line-focused laser having a laser wavelength of 1064 nm.
- the etching step 16 is shown and described.
- substrate 20 is placed into an etchant bath following formation of damage tracks 34 .
- the etching material is a hydroxide etching material that preferentially etches substrate 20 at the site of damage tracks 34 as compared to areas outside of damage tracks 34 .
- various hydroxide based etching materials have a high preferential etch rate.
- preferential etch rate refers to the etch rate of the glass-based material at the site of the damage tracks 34 .
- “undamaged etch rate” refers to the etch rate of the glass-based material that was not subjected to the laser damage (e.g., the areas of the glass-based material not at the side of a damage track/etch path).
- the hydroxide based etching materials discussed herein have a preferential etch rate at which the etching material removes material from the substrate) along damage tracks 34 that is at least 12 times greater than the undamaged etch rate experienced by portions of the substrate outside of damage tracks 34 .
- the hydroxide based etching materials discussed herein have a preferential etch rate along the damage tracks 34 that is at between 30 and 70 times greater that the undamaged etch rate experienced by portions of the substrate outside of damage tracks 34 .
- the high preferential etch rate discussed herein allows for the formation of vias in relatively thick substrate 20 and also allows for the formation of through vias that do not narrow substantially at the midpoint through substrate 20 .
- the high preferential etch rate allows for the fast formation of vias in substrate 20 without the unnecessary removal of undue amounts of substrate material from areas outside of damage tracks 34 .
- the hydroxide etching materials discussed herein also have a relatively high undamaged etch rate.
- the hydroxide based etching materials discussed herein have undamaged etch rates outside the area of damage tracks 34 between 0.02 ⁇ m/min and 0.25 ⁇ m/min.
- the hydroxide based etching material may be any hydroxide material.
- the hydroxide based etching material is at least one of sodium hydroxide, potassium hydroxide and tetramethylammonium hydroxide, and in specific embodiments, these materials are formed in an aqueous mixture with at least one of a diol and an alcohol.
- the etching material has a hydroxide concentration of at least 0.5 M.
- the etching material may be sodium hydroxide or potassium hydroxide having a concentration between 1 M and 19.5 M.
- the etching material is maintained at a temperature of greater than 60 degrees C. during etching, specifically between 60 and 175 degrees C. during etching, and more specifically between 60 and 120 degrees C. during etching.
- the process of the present disclosure forms a high aspect ratio through vias through a relatively thick substrate while maintaining total processing time at a satisfactorily low level.
- the total etching time of the process discussed herein is less than 24 hours, specifically less than 20 hours and in at least some embodiments, less than 10 hours.
- through vias can be formed through substrate 20 in as little as 3 hours using the process discussed herein without the need for mechanical agitation or sonication.
- total etching time of the process discussed herein is between two weeks and 3 hours, and in a specific embodiment, total etching time of the process discussed herein is four days.
- FIG. 4 shows plots of undamaged etch rate in ⁇ m/min versus preferential etch rate in ⁇ m/min for two etching materials and two different substrate materials.
- material Comp A represents a composition having the following on an oxide basis: 69.11 mol % SiO 2 ; 10.19 mol % Al 2 O 3 ; 15.09 mol % Na 2 O; 0.01 mol % K 2 O; 5.48 mol % MgO; 0.005 mol % TiO 2 ; 0.01 mol % Fe 2 O 3 ; 0.01 mol % ZrO 2 ; and 0.13 mol % SnO 2
- material code EXG represents Corning® Eagle XG® Glass.
- FIG. 4 shows that generally in the process of the present application, as undamaged etch rates decrease preferential etch rates increase, as shown by the curves in FIG. 4 .
- process 10 may include two etching steps.
- the first etching step is a hydroxide based etching step, such as step 16 discussed above.
- a low etch rate is used providing a very high preferential etch rate, as shown by the relationship between undamaged etch rate and preferential etch rate in FIG. 4 .
- This first high preferential etch rate step is utilized to open up through holes along damage tracks 34 .
- the undamaged etch rate is increased to quickly expand the through hole to the desired diameter.
- the undamaged etch rate during the second etching step is increased by increasing hydroxide etchant concentration and/or temperature.
- the second etching step may utilize an etchant with a higher etch rate, such as hydrofluoric acid.
- substrate 20 includes a plurality of via, shown as through vias 40 , that extend all of the way through substrate 20 between surfaces 22 and 24 and through substrate interior region 44 .
- vias 40 can be through vias, blind vias, or a combination thereof.
- through vias 40 have a relatively high aspect ratio (e.g., the ratio of their length and their maximum diameter). In various embodiments, the aspect ratio of vias 40 is greater than 8 to 1, specifically is greater than 10 to 1, and more specifically is greater than 12 to 1.
- the length of through vias 40 is substantial the same as the different thicknesses, Ti, discussed herein.
- the length of the via will be less than the thickness of the substrate.
- the length of the via is measured with an interferometer.
- the diameter of the via is measured by imaging the via with an optical microscope and calculating a least-squares best fit circle to the edges of the via.
- that diameter of vias 40 at various points along its length is large enough to accommodate an electrically conductive material such as a metallizing material such as a metallizing paste but is also small enough to not substantially compromise the integrity or strength of the substrate.
- the vias may be filled with an electrically conductive material using any known technique including, but not limited to, sputtering, electroless and/or electrolytic plating, chemical vapor deposition, etc.
- the electrically conductive material may be, for example, copper, silver, aluminum, titanium, gold, platinum, nickel, tungsten, magnesium, or any other suitable material.
- vias 40 have a maximum diameter, shown as D 1 , that is less than 100 ⁇ m and a minimum diameter, shown as D 2 that is greater than or equal to 40 ⁇ m.
- vias 40 are formed such that their diameter at different points along their length is relatively consistent. In some embodiments, vias 40 do not substantially narrow or taper along their lengths between surfaces 22 and 24 , and this structure is the result of the etching rates of the process as discussed herein. In various embodiments, vias 40 are not substantially tapered such that a ratio of D 2 to D 1 is greater than 0.5. In specific embodiments, through vias 40 are structured such that the ratio of D 2 to D 1 is between 0.8 and 1, specifically is between 0.9 and 1 and more specifically is between 0.92 and 0.98.
- vias 40 are defined by an interior surface 42 .
- interior surface 42 has one or more surface characteristics that are different from the surfaces of a hole formed by hydrofluoric acid, by a mechanical drill or by a laser drill.
- interior surfaces 42 of vias 40 are substantially smooth, such that interior surfaces 42 have a peak to valley differential of less than 6 ⁇ m, and more specifically between 3-6 ⁇ m.
- interior surfaces 42 of vias 40 are not substantially tapered such that a degree of taper along the length of vias 40 is less than 20%.
- interior surfaces 42 are hydroxyl rich surfaces, at least compared to surfaces etched by hydrofluoric acid.
- substrate 20 may also be tempered to provide increased strength and shatter resistance that is desirable in certain applications, such as in smartphone sensor applications.
- substrate 20 is tempered such that regions of the substrate adjacent to surfaces 22 and 24 are under compressive stress and, in some such embodiments, a central region of substrate 20 is under tensile stress. As will be understood, these differential stresses increase the strength and shatter resistance of substrate 20 .
- the compressive stress at the surfaces 22 and 24 of substrate 20 is greater 100 MP, and in a specific embodiment is greater than 500 MPa.
- substrate 20 may be thermally tempered via a process of heating and rapid cooling.
- substrate 20 may be chemically tempered such as through a process of surface ion exchange. As will be understood, chemical tempering swaps small ions, e.g., Na ions, in the substrate near the surface for larger ions, e.g., K ions, and the presence of the larger ions creates a surface compressive stress.
- the compressive stress layers have depths of at least 10 ⁇ m from surfaces 22 and 24 , and in some such embodiments, the surface compressive stress at each surface is greater than 500 MPa. In at least some embodiments, it is believed that interior surfaces 42 defining vias 40 and the adjacent regions are under compressive stress in addition to the compressive stress formed at surfaces 22 and 24 . Such compressive stress may provide strengthening and/or durability to vias 40 , in at least some embodiments. Compressive stress at the surface is measured by surface stress meter (FSM) using commercially available instruments such as the FSM-6000, manufactured by Orihara Industrial Co., Ltd. (Japan).
- FSM surface stress meter
- SOC stress optical coefficient
- ASTM standard C770-16 entitled “Standard Test Method for Measurement of Glass Stress-Optical Coefficient,” the contents of which are incorporated herein by reference in their entirety.
- the depth of the compressive stress layer may be measured by FSM or a scattered light polariscope (SCALP) depending on the ion exchange treatment. Where the stress in the glass-based article is generated by exchanging potassium ions into the glass-based article, FSM is used to measure the depth of the compressive stress layer.
- SCALP is used to measure the depth of the compressive stress layer.
- the depth of the compressive stress layer is measured by SCALP, since it is believed the exchange depth of sodium indicates the depth of the compressive stress layer and the exchange depth of potassium ions indicates a change in the magnitude of the compressive stress (but not the change in stress from compressive to tensile); the exchange depth of potassium ions in such glass-based articles is measured by FSM.
- Substrate 20 as discussed herein may be used for a wide variety of electronics substrate applications, and specifically sensor substrate applications.
- substrate 20 may be used as the substrate for a fingerprint sensor 50 , for an electronic device 52 (such as mobile phones, tablets, laptops, computers, navigation systems, and the like).
- FIG. 6 shows a consumer electronic device 52 including a housing 53 having front 54 , back 55 , and side surfaces 56 ; electrical components (not shown) that are at least partially inside or entirely within the housing and including at least a controller, a memory, a fingerprint sensor or touchscreen and a display 58 at or adjacent to the front surface of the housing; and a cover substrate 59 at or over the front surface of the housing such that it is over the display.
- fingerprint sensor 50 includes a metal containing electrically conductive material located within through vias 40 of substrate 20 .
- First and second redistribution layers are located on surfaces 22 and 24 , and a capacitance sensing array is coupled to the first redistribution layer.
- a fingerprint sensing ASIC is coupled to the second redistribution layer such that the signals generated by the sensing array are communicated through the substrate and to the ASIC.
- substrate 20 may support a wide variety of additional layers or coatings as desired for a particular application.
- substrate 20 may support one or more color layers, electrostatic discharge layer and a hard coating layer.
- sensor 60 uses a glass-based substrate, such as substrate 20 .
- Various layers 62 are located on a finger side 64 of substrate 20
- various layers 66 are located on a circuit side 68 of substrate 20 . Details of layers 62 and 66 are shown in FIG. 7 , and a single exemplary metallized through via 40 is shown electrically connecting layers 62 and 66 .
- An ASIC chip 70 configured to process signals related to a sensed finger print is connected via a conductor or cable 72 to layers 66 .
- substrate 20 provides a robust substrate for supporting layers 62 and 66 while at the same allowing for vias 40 to provide conduction between layers 62 and 66 .
- substrate 20 is believed to be stronger, stiffer and more scratch and crack-resistant than a polymer substrate, and in addition, the strength of substrate 20 allows for use of a thinner hard coating layer on the finger side of the sensor which achieves a better signal-to-noise ratio for the fingerprint sensor.
- substrate 20 also is believed to have a lower cost relative to sapphire sensor substrates. Because substrate 20 is formed from a glass-based material it may be tempered (either thermally or chemically), improving the drop performance of the sensor.
- the high aspect ratio, relatively wide through vias 40 allow for use of low cost metallizing by metal paste application instead of metallizing through extensive vapor deposition or multi-step electro-deposition.
- the combination laser damage and hydroxide etching process discussed herein allows for formation of a sensor substrate from a multicomponent glass material (as opposed to pure silica materials such as fused silica).
- the process discussed herein avoids the use of hazardous hydrofluoric acid. Further, it is believed that the process discussed herein is more efficient and/or has lower capital costs than a system using mechanical or laser drilling.
- damage tracks are initially formed in 0.7 mm thick, 150 mm diameter glass wafers formed of Comp A listed above using the picosecond laser technology described above.
- the damage pattern is based on the sensor array and/or ASIC of the sensor that the wafer is to be used with.
- These wafers are then placed in a process carrier with a pitch of 6.4 mm.
- the process carrier is then immersed in a bath of 6 M sodium hydroxide at 85 degrees C. for 3 days.
- the carrier is then removed from the alkaline bath and rinsed with large amounts of deionized water.
- the wafers are subsequently ion-exchanged for 3.5 hours at a temperature of 390 degrees C. using 100% KNO 3 .
- the remaining sensor components are then patterned onto the substrate using thin film and coating technologies to create the desired product.
- through vias of eleven micron diameter were formed in 0.7 mm thick sections of Comp A glass by etching in 6 M NaOH at 90 degrees C. for 8 hours. These vias have an aspect ratio of over 60:1 and can subsequently be etched to form vias of a waist ratio greater than 95%. The waist ratio is calculated with respect to the minimum diameter of the via (the “waist”) and the maximum diameter of the via.
- a first aspect includes process for forming vias in a glass-based substrate having a first major surface and an opposing second major surface, the process comprising creating a plurality of etch paths extending from the first major surface of the glass substrate by directing a laser at the substrate in a predetermined pattern; and etching a plurality of vias extending from the first major surface of the glass substrate along the etch paths using a hydroxide based etching material, wherein the hydroxide based etching material preferentially etches the substrate along the etch path such that an etch rate of the etching material along the etch path is at least 12 times greater than an etch rate of the etching material outside of the etch paths.
- each of the plurality of vias have a ratio of the length of the via to a maximum diameter of the via is greater than 8 to 1.
- the glass-based substrate includes 50-75 mol % SiO2 and 10-20 mol % alkali metal oxide, where the alkali metal oxide is at least one of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O.
- a ninth aspect according to any one of the first through eighth aspects further comprising tempering the glass substrate following etching such that the first major surface and the second major surface are under compressive stress, wherein the compressive stress at one or both of the first and major surfaces is at least 100 MPa.
- the tempering step comprises chemically tempering the glass substrate through ion exchange such that chemically strengthened layers extend from the first and second major surfaces, wherein a depth of each chemically strengthened layer is greater than 10 ⁇ m, and wherein the compressive stress at one or both of the first and major surfaces is at least 500 MPa.
- the hydroxide based etching material has a hydroxide concentration of at least 0.5 M and is maintained at a temperature of greater than 60 degrees C. during the etching step, and wherein the hydroxide based etching material preferentially etches the substrate along the etch path such that the etch rate of the etching material along the etch path is at least 30 times greater than the etch rate of the etching material outside of the etch paths.
- hydroxide based etching material includes at least one of sodium hydroxide, potassium hydroxide and tetramethylammonium hydroxide in an aqueous mixture with at least one of a diol and an alcohol.
- a sixteenth aspect includes a glass-based substrate comprising: a first major surface; a second major surface opposite the first major surface; an interior region located between the first and second major surfaces; and a plurality of vias extending from the first major surface into the interior region, each of the vias having a maximum diameter and a minimum diameter; wherein the substrate has an average thickness of greater than 0.3 mm; wherein the maximum diameter of each of the plurality of vias is less than 100 ⁇ m; and wherein a ratio of the minimum diameter to the maximum diameter of each of the vias is greater than 0.5.
- a seventeenth aspect according to the sixteenth aspect wherein the minimum diameter of each of the vias is greater than or equal to 40 ⁇ m, and wherein the ratio of the minimum diameter to the maximum diameter of each of the through holes is greater than 0.8 and less than 1.
- a nineteenth aspect according to the eighteenth aspect wherein the length of each via is greater than 0.5 mm and less than 1.1 mm, and wherein the ratio of the length of each via to the maximum diameter of each of via is greater than 10 to 1.
- the substrate is a includes 50-75 mol % SiO2 and 10-20 mol % alkali metal oxide, where the alkali metal oxide is at least one of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O.
- the substrate is a chemically tempered glass material having chemically strengthened layers extending from the first and second major surfaces, wherein the depths of the chemically strengthened layers are greater than 10 ⁇ m, and wherein the compressive stress at one or both of the first and major surfaces is at least 500 MPa.
- a twenty-fourth aspect according to any one of the sixteenth through twenty-third aspects, wherein at least one the plurality of vias is a through-via.
- a twenty-fifth aspect according to any one of the sixteenth through twenty-fourth aspects, wherein at least one of the plurality of vias is a blind via.
- a twenty-sixth aspect including a glass substrate comprising: a first major surface; a second major surface opposite the first major surface; a plurality of through vias extending between the first and second major surfaces, each of the through holes having a maximum diameter and a minimum diameter; and a multicomponent glass material including 50-75 mol % SiO2 and 10-20 mol % alkali metal oxide, where the alkali metal oxide is at least one of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O; wherein the average distance between the first major surface and the second major surface is greater than 0.3 mm; wherein a ratio of the average distance between the first major surface and the second major surface to a maximum diameter of each of the plurality of through vias is greater than 8 to 1; wherein a ratio of the minimum diameter to the maximum diameter of each of the vias is greater than 0.5.
- a twenty seventh aspect according to the twenty-sixth aspect wherein the average distance between the first major surface and the second major surface is greater than 0.5 mm and less than 1.1 mm, wherein the maximum diameter of the through holes is less than 100 ⁇ m, and wherein the ratio of the average distance between the first major surface and the second major surface to the maximum diameter of each of the through vias is greater than 10 to 1.
- the substrate is a chemically tempered glass material having chemically strengthened layers extending from the first and second major surfaces, wherein a depth of each chemically strengthened layer is greater than 10 ⁇ m, and wherein the first major surface and the second major surfaces are under compressive stress and the compressive stress at the surface of one or both of the first and second major surfaces is at least 100 MPa.
- a twenty ninth aspect including a consumer electronic product, comprising: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, a fingerprint sensor, and a display, the display being provided at or adjacent the front surface of the housing; and the glass-based substrate any one of the sixteenth through twenty fifth aspects disposed over the display, wherein the plurality of vias are filled with an electrical conductive material that provides a conductive pathway for the fingerprint sensor.
- a thirtieth aspect including a consumer electronic product, comprising: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, a fingerprint sensor, and a display, the display being provided at or adjacent the front surface of the housing; and the glass substrate of any one of the twenty sixth through twenty eighth aspects disposed over the display, wherein the plurality of through vias are filled with an electrical conductive material that provides a conductive pathway for the fingerprint sensor.
Landscapes
- Engineering & Computer Science (AREA)
- Chemical & Material Sciences (AREA)
- General Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Optics & Photonics (AREA)
- Physics & Mathematics (AREA)
- Life Sciences & Earth Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Microelectronics & Electronic Packaging (AREA)
- Plasma & Fusion (AREA)
- Mechanical Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Inorganic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Toxicology (AREA)
- Ceramic Engineering (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Glass Compositions (AREA)
- Surface Treatment Of Glass (AREA)
- Devices For Indicating Variable Information By Combining Individual Elements (AREA)
- Production Of Multi-Layered Print Wiring Board (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US15/286,803 US20170103249A1 (en) | 2015-10-09 | 2016-10-06 | Glass-based substrate with vias and process of forming the same |
US16/131,247 US10438039B2 (en) | 2015-10-09 | 2018-09-14 | Glass-based substrate with vias and process of forming the same |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201562239528P | 2015-10-09 | 2015-10-09 | |
US15/286,803 US20170103249A1 (en) | 2015-10-09 | 2016-10-06 | Glass-based substrate with vias and process of forming the same |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/131,247 Division US10438039B2 (en) | 2015-10-09 | 2018-09-14 | Glass-based substrate with vias and process of forming the same |
Publications (1)
Publication Number | Publication Date |
---|---|
US20170103249A1 true US20170103249A1 (en) | 2017-04-13 |
Family
ID=57227085
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/286,803 Abandoned US20170103249A1 (en) | 2015-10-09 | 2016-10-06 | Glass-based substrate with vias and process of forming the same |
US16/131,247 Expired - Fee Related US10438039B2 (en) | 2015-10-09 | 2018-09-14 | Glass-based substrate with vias and process of forming the same |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/131,247 Expired - Fee Related US10438039B2 (en) | 2015-10-09 | 2018-09-14 | Glass-based substrate with vias and process of forming the same |
Country Status (7)
Country | Link |
---|---|
US (2) | US20170103249A1 (zh) |
EP (1) | EP3359496A1 (zh) |
JP (1) | JP2018531205A (zh) |
KR (1) | KR20180067568A (zh) |
CN (1) | CN108137375A (zh) |
TW (1) | TW201722606A (zh) |
WO (1) | WO2017062798A1 (zh) |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10292275B2 (en) * | 2016-04-06 | 2019-05-14 | AGC Inc. | Method of manufacturing glass substrate that has through hole, method of forming through hole in glass substrate and system for manufacturing glass substrate that has through hole |
US20200130105A1 (en) * | 2018-10-30 | 2020-04-30 | AGC Inc. | Method of producing glass substrate having hole and glass laminate for annealing |
US10756003B2 (en) | 2016-06-29 | 2020-08-25 | Corning Incorporated | Inorganic wafer having through-holes attached to semiconductor wafer |
WO2020190489A1 (en) * | 2019-03-21 | 2020-09-24 | Corning Incorporated | Systems for and methods of forming micro-holes in glass-based objects using an annular vortex laser beam |
US20200354267A1 (en) * | 2019-05-10 | 2020-11-12 | Corning Incorporated | Silicate glass compositions useful for the efficient production of through glass vias |
US20200361812A1 (en) * | 2019-05-17 | 2020-11-19 | Corning Incorporated | Method of modifying a textured glass substrate with a region under compressive stress to increase strength of the glass substrate |
CN112312654A (zh) * | 2020-08-14 | 2021-02-02 | 珠海越亚半导体股份有限公司 | 一种嵌埋在玻璃介质中的无源器件结构及其制造方法 |
US20210147279A1 (en) * | 2019-11-18 | 2021-05-20 | AGC Inc. | Supporting glass substrate and laminated body |
US11062986B2 (en) | 2017-05-25 | 2021-07-13 | Corning Incorporated | Articles having vias with geometry attributes and methods for fabricating the same |
US11078112B2 (en) | 2017-05-25 | 2021-08-03 | Corning Incorporated | Silica-containing substrates with vias having an axially variable sidewall taper and methods for forming the same |
US11114309B2 (en) | 2016-06-01 | 2021-09-07 | Corning Incorporated | Articles and methods of forming vias in substrates |
CN113825732A (zh) * | 2019-05-15 | 2021-12-21 | 康宁股份有限公司 | 在高温下用高浓度碱性氢氧化物减小纹理化玻璃、玻璃陶瓷以及陶瓷制品的厚度的方法 |
US20220112123A1 (en) * | 2020-10-14 | 2022-04-14 | Schott Ag | Method for processing glass by alkaline etching |
WO2022076247A1 (en) * | 2020-10-05 | 2022-04-14 | Corning Incorporated | Methods of forming a foldable apparatus |
US11554984B2 (en) | 2018-02-22 | 2023-01-17 | Corning Incorporated | Alkali-free borosilicate glasses with low post-HF etch roughness |
US20230021394A1 (en) * | 2021-07-19 | 2023-01-26 | Komico Ltd. | Method for large surface coating base on control of thin film stress and coating structure useof |
EP4201903A1 (en) * | 2021-12-24 | 2023-06-28 | INTEL Corporation | Plate-up hybrid structures using modified glass patterning processes |
US11774233B2 (en) | 2016-06-29 | 2023-10-03 | Corning Incorporated | Method and system for measuring geometric parameters of through holes |
WO2024035078A1 (ko) * | 2022-08-08 | 2024-02-15 | 삼성전자 주식회사 | 패턴이 형성된 하우징을 포함하는 전자 장치 및 상기 패턴을 형성하는 방법 |
WO2024068290A1 (de) * | 2022-09-27 | 2024-04-04 | Schott Ag | Glaswafer sowie verfahren zu dessen herstellung |
Families Citing this family (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9321677B2 (en) | 2014-01-29 | 2016-04-26 | Corning Incorporated | Bendable glass stack assemblies, articles and methods of making the same |
JP6885161B2 (ja) * | 2016-04-06 | 2021-06-09 | Agc株式会社 | 貫通孔を有するガラス基板の製造方法およびガラス基板に貫通孔を形成する方法 |
WO2019195305A1 (en) * | 2018-04-03 | 2019-10-10 | Corning Incorporated | Methods for making high density vias in a glass article |
US11152294B2 (en) | 2018-04-09 | 2021-10-19 | Corning Incorporated | Hermetic metallized via with improved reliability |
WO2020149040A1 (ja) * | 2019-01-17 | 2020-07-23 | 日本板硝子株式会社 | 微細構造付ガラス基板及び微細構造付ガラス基板の製造方法 |
JP7492969B2 (ja) | 2019-02-21 | 2024-05-30 | コーニング インコーポレイテッド | 銅金属化貫通孔を有するガラスまたはガラスセラミック物品およびその製造方法 |
JPWO2020184175A1 (zh) * | 2019-03-08 | 2020-09-17 | ||
EP3916772A4 (en) | 2019-03-12 | 2023-04-05 | Absolics Inc. | PACKAGING SUBSTRATE AND SEMICONDUCTOR DEVICE WITH IT |
US11981501B2 (en) | 2019-03-12 | 2024-05-14 | Absolics Inc. | Loading cassette for substrate including glass and substrate loading method to which same is applied |
EP3916771A4 (en) | 2019-03-12 | 2023-01-11 | Absolics Inc. | PACKAGING SUBSTRATE AND EQUIPPED SEMICONDUCTOR DEVICE COMPRISING SUBSTRATE |
JP7087205B2 (ja) | 2019-03-29 | 2022-06-20 | アブソリックス インコーポレイテッド | 半導体用パッケージングガラス基板、半導体用パッケージング基板及び半導体装置 |
JP7116926B2 (ja) | 2019-04-23 | 2022-08-12 | 日本電気硝子株式会社 | ガラス板の製造方法、及びガラス板、並びにガラス板集合体 |
WO2020241805A1 (ja) * | 2019-05-30 | 2020-12-03 | 日本板硝子株式会社 | 微細構造付ガラス基板、導電層付ガラス基板、及び微細構造付ガラス基板を製造する方法 |
WO2021020241A1 (ja) * | 2019-08-01 | 2021-02-04 | 日本電気硝子株式会社 | ガラスフィルム及びこれを用いたガラスロール |
WO2021040178A1 (ko) | 2019-08-23 | 2021-03-04 | 에스케이씨 주식회사 | 패키징 기판 및 이를 포함하는 반도체 장치 |
WO2021041037A1 (en) * | 2019-08-30 | 2021-03-04 | Corning Incorporated | Display protector assemblies having vias |
CN112894146A (zh) * | 2019-12-04 | 2021-06-04 | 大族激光科技产业集团股份有限公司 | 玻璃基板通孔的激光加工方法和装置 |
CN111037125A (zh) * | 2019-12-26 | 2020-04-21 | 江苏汇鼎光学眼镜有限公司 | 一种防紫外线镜片的加工设备及其制备方法 |
JP7028418B2 (ja) * | 2020-04-27 | 2022-03-02 | 株式会社Nsc | 貫通孔を有するガラス基板製造方法および表示装置製造方法 |
JP7251704B2 (ja) * | 2020-09-16 | 2023-04-04 | 株式会社Nsc | ガラス用エッチング液およびガラス基板製造方法 |
CN112266178B (zh) * | 2020-11-09 | 2022-07-22 | 泰极微技术(苏州)有限公司 | 一种玻璃蚀刻方法 |
CN117295696A (zh) * | 2021-02-04 | 2023-12-26 | 康宁股份有限公司 | 用于增进的可制造性的低模量可离子交换玻璃 |
CN113105236B (zh) * | 2021-04-15 | 2022-06-14 | 贵州大学 | 基于飞秒激光加工的无铅压电陶瓷制备方法及无铅压电陶瓷 |
CN116535099A (zh) * | 2022-01-26 | 2023-08-04 | 华为技术有限公司 | 电子设备外壳的制备方法、电子设备外壳及电子设备 |
DE102022110353A1 (de) | 2022-04-28 | 2023-11-02 | Trumpf Laser- Und Systemtechnik Gmbh | Verfahren zur Trennung eines Werkstücks |
CN115432919A (zh) * | 2022-10-25 | 2022-12-06 | 深圳市益铂晶科技有限公司 | 一种玻璃激光切割的浸蚀裂片方法 |
Family Cites Families (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5166493A (en) | 1989-01-10 | 1992-11-24 | Canon Kabushiki Kaisha | Apparatus and method of boring using laser |
JP2004537175A (ja) | 2001-08-02 | 2004-12-09 | エスケーシー カンパニー,リミテッド | レーザーを使用した化学的機械的研磨パッドの製造方法 |
JP4702794B2 (ja) | 2003-10-06 | 2011-06-15 | Hoya株式会社 | 感光性ガラス基板の貫通孔形成方法 |
JP2007516932A (ja) | 2003-12-30 | 2007-06-28 | コーニング インコーポレイテッド | 高歪み点ガラス |
KR101277390B1 (ko) * | 2005-05-31 | 2013-06-20 | 히다치 비아 메카닉스 가부시키가이샤 | 프린트 배선판의 제조방법 및 그것에 이용되는 동박을 붙인 적층판 및 처리액 |
JP4410159B2 (ja) | 2005-06-24 | 2010-02-03 | 三菱電機株式会社 | 交流回転電機 |
JP5115476B2 (ja) * | 2006-05-18 | 2013-01-09 | 旭硝子株式会社 | 透明電極付きガラス基板とその製造方法 |
US8075999B2 (en) | 2008-08-08 | 2011-12-13 | Corning Incorporated | Strengthened glass articles and methods of making |
WO2011132600A1 (ja) | 2010-04-20 | 2011-10-27 | 旭硝子株式会社 | 半導体デバイス貫通電極用のガラス基板 |
JP5574866B2 (ja) * | 2010-07-26 | 2014-08-20 | 浜松ホトニクス株式会社 | レーザ加工方法 |
KR101940334B1 (ko) * | 2010-07-26 | 2019-01-18 | 하마마츠 포토닉스 가부시키가이샤 | 레이저 가공 방법 |
KR101940333B1 (ko) * | 2010-07-26 | 2019-01-18 | 하마마츠 포토닉스 가부시키가이샤 | 기판 가공 방법 |
US8584354B2 (en) | 2010-08-26 | 2013-11-19 | Corning Incorporated | Method for making glass interposer panels |
CN106425129B (zh) | 2010-11-30 | 2018-07-17 | 康宁股份有限公司 | 在玻璃中形成高密度孔阵列的方法 |
US8894868B2 (en) | 2011-10-06 | 2014-11-25 | Electro Scientific Industries, Inc. | Substrate containing aperture and methods of forming the same |
CN105246850B (zh) | 2012-11-29 | 2018-01-30 | 康宁股份有限公司 | 通过激光损坏和蚀刻制造玻璃制品的方法 |
EP2925482A1 (en) * | 2012-11-29 | 2015-10-07 | Corning Incorporated | Sacrificial cover layers for laser drilling substrates and methods thereof |
US9745220B2 (en) | 2013-06-21 | 2017-08-29 | Corning Incorporated | Etch rate enhancement at low temperatures |
US9296646B2 (en) | 2013-08-29 | 2016-03-29 | Corning Incorporated | Methods for forming vias in glass substrates |
US10293436B2 (en) | 2013-12-17 | 2019-05-21 | Corning Incorporated | Method for rapid laser drilling of holes in glass and products made therefrom |
US9558390B2 (en) | 2014-07-25 | 2017-01-31 | Qualcomm Incorporated | High-resolution electric field sensor in cover glass |
US9832868B1 (en) | 2015-08-26 | 2017-11-28 | Apple Inc. | Electronic device display vias |
-
2016
- 2016-10-06 US US15/286,803 patent/US20170103249A1/en not_active Abandoned
- 2016-10-07 WO PCT/US2016/056042 patent/WO2017062798A1/en active Application Filing
- 2016-10-07 CN CN201680059027.5A patent/CN108137375A/zh active Pending
- 2016-10-07 TW TW105132510A patent/TW201722606A/zh unknown
- 2016-10-07 JP JP2018517805A patent/JP2018531205A/ja active Pending
- 2016-10-07 KR KR1020187012586A patent/KR20180067568A/ko unknown
- 2016-10-07 EP EP16790775.7A patent/EP3359496A1/en not_active Withdrawn
-
2018
- 2018-09-14 US US16/131,247 patent/US10438039B2/en not_active Expired - Fee Related
Cited By (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10292275B2 (en) * | 2016-04-06 | 2019-05-14 | AGC Inc. | Method of manufacturing glass substrate that has through hole, method of forming through hole in glass substrate and system for manufacturing glass substrate that has through hole |
US11114309B2 (en) | 2016-06-01 | 2021-09-07 | Corning Incorporated | Articles and methods of forming vias in substrates |
US10756003B2 (en) | 2016-06-29 | 2020-08-25 | Corning Incorporated | Inorganic wafer having through-holes attached to semiconductor wafer |
US11774233B2 (en) | 2016-06-29 | 2023-10-03 | Corning Incorporated | Method and system for measuring geometric parameters of through holes |
US11972993B2 (en) | 2017-05-25 | 2024-04-30 | Corning Incorporated | Silica-containing substrates with vias having an axially variable sidewall taper and methods for forming the same |
US11062986B2 (en) | 2017-05-25 | 2021-07-13 | Corning Incorporated | Articles having vias with geometry attributes and methods for fabricating the same |
US11078112B2 (en) | 2017-05-25 | 2021-08-03 | Corning Incorporated | Silica-containing substrates with vias having an axially variable sidewall taper and methods for forming the same |
US11554984B2 (en) | 2018-02-22 | 2023-01-17 | Corning Incorporated | Alkali-free borosilicate glasses with low post-HF etch roughness |
US20200130105A1 (en) * | 2018-10-30 | 2020-04-30 | AGC Inc. | Method of producing glass substrate having hole and glass laminate for annealing |
US11541482B2 (en) * | 2018-10-30 | 2023-01-03 | AGC Inc. | Method of producing glass substrate having hole and glass laminate for annealing |
WO2020190489A1 (en) * | 2019-03-21 | 2020-09-24 | Corning Incorporated | Systems for and methods of forming micro-holes in glass-based objects using an annular vortex laser beam |
CN113613825A (zh) * | 2019-03-21 | 2021-11-05 | 康宁股份有限公司 | 使用环形涡旋激光束在基于玻璃的物体中形成微孔的***及方法 |
US20200354267A1 (en) * | 2019-05-10 | 2020-11-12 | Corning Incorporated | Silicate glass compositions useful for the efficient production of through glass vias |
US11952310B2 (en) * | 2019-05-10 | 2024-04-09 | Corning Incorporated | Silicate glass compositions useful for the efficient production of through glass vias |
CN113825732A (zh) * | 2019-05-15 | 2021-12-21 | 康宁股份有限公司 | 在高温下用高浓度碱性氢氧化物减小纹理化玻璃、玻璃陶瓷以及陶瓷制品的厚度的方法 |
US20200361812A1 (en) * | 2019-05-17 | 2020-11-19 | Corning Incorporated | Method of modifying a textured glass substrate with a region under compressive stress to increase strength of the glass substrate |
US11905202B2 (en) * | 2019-05-17 | 2024-02-20 | Corning Incorporated | Method of modifying a textured glass substrate with a region under compressive stress to increase strength of the glass substrate |
US20210147279A1 (en) * | 2019-11-18 | 2021-05-20 | AGC Inc. | Supporting glass substrate and laminated body |
CN112312654A (zh) * | 2020-08-14 | 2021-02-02 | 珠海越亚半导体股份有限公司 | 一种嵌埋在玻璃介质中的无源器件结构及其制造方法 |
WO2022076247A1 (en) * | 2020-10-05 | 2022-04-14 | Corning Incorporated | Methods of forming a foldable apparatus |
US11891326B2 (en) * | 2020-10-14 | 2024-02-06 | Schott Ag | Method for processing glass by alkaline etching |
US20220112123A1 (en) * | 2020-10-14 | 2022-04-14 | Schott Ag | Method for processing glass by alkaline etching |
US20230021394A1 (en) * | 2021-07-19 | 2023-01-26 | Komico Ltd. | Method for large surface coating base on control of thin film stress and coating structure useof |
EP4201903A1 (en) * | 2021-12-24 | 2023-06-28 | INTEL Corporation | Plate-up hybrid structures using modified glass patterning processes |
WO2024035078A1 (ko) * | 2022-08-08 | 2024-02-15 | 삼성전자 주식회사 | 패턴이 형성된 하우징을 포함하는 전자 장치 및 상기 패턴을 형성하는 방법 |
WO2024068290A1 (de) * | 2022-09-27 | 2024-04-04 | Schott Ag | Glaswafer sowie verfahren zu dessen herstellung |
Also Published As
Publication number | Publication date |
---|---|
EP3359496A1 (en) | 2018-08-15 |
WO2017062798A1 (en) | 2017-04-13 |
US10438039B2 (en) | 2019-10-08 |
KR20180067568A (ko) | 2018-06-20 |
JP2018531205A (ja) | 2018-10-25 |
CN108137375A (zh) | 2018-06-08 |
TW201722606A (zh) | 2017-07-01 |
WO2017062798A8 (en) | 2018-05-03 |
US20190012514A1 (en) | 2019-01-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10438039B2 (en) | Glass-based substrate with vias and process of forming the same | |
JP2018531205A6 (ja) | ビアを有するガラス系基板およびそれを形成するプロセス | |
JP7198560B2 (ja) | イオン交換可能な混合アルカリアルミノケイ酸塩ガラス | |
US11062986B2 (en) | Articles having vias with geometry attributes and methods for fabricating the same | |
JP7479549B2 (ja) | 特別な面取り部の形状および高強度を有する超薄ガラス | |
US20190177215A1 (en) | Strengthened glass-based articles having filled holes and method of making the same | |
US9422188B2 (en) | Thin substrates having mechanically durable edges | |
TW201925121A (zh) | 具有低過量改質劑含量的玻璃 | |
KR20220008278A (ko) | 상승된 온도에서 고농도 알칼리 수산화물을 갖는 텍스쳐링된 유리, 유리-세라믹, 및 세라믹 물품의 두께를 감소시키는 방법 | |
TW202108534A (zh) | 改良具有處於壓應力下的區域之紋理化玻璃基板以增加玻璃基板強度的方法 | |
KR20210046026A (ko) | 재인발 및 화학적 박형화 공정의 조합에 의한 유리의 향상된 강도 | |
JP2019199400A (ja) | 電子部品における板ガラスの使用 | |
US20190157107A1 (en) | Low surface roughness substrate having a via and methods of making the same | |
TWI794417B (zh) | 具有低hf蝕刻後粗糙度之無鹼硼矽酸鹽玻璃 | |
CN108290780B (zh) | 抗紫外光的制品及其制造方法 | |
WO2021041036A1 (en) | Ion exchange process for ultra-thin glass | |
WO2023034014A1 (en) | Glass compositions and glass laminate articles comprising the same | |
TW202312375A (zh) | 具有穿玻璃通孔之玻璃陶瓷基板 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CORNING INCORPORATED, NEW YORK Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:JIN, YUHUI;WILHELM, MATTHEW EVAN;SIGNING DATES FROM 20170202 TO 20170203;REEL/FRAME:041455/0710 |
|
STCB | Information on status: application discontinuation |