TW201217291A - Glass with photocatalytic function - Google Patents
Glass with photocatalytic function Download PDFInfo
- Publication number
- TW201217291A TW201217291A TW100133143A TW100133143A TW201217291A TW 201217291 A TW201217291 A TW 201217291A TW 100133143 A TW100133143 A TW 100133143A TW 100133143 A TW100133143 A TW 100133143A TW 201217291 A TW201217291 A TW 201217291A
- Authority
- TW
- Taiwan
- Prior art keywords
- glass
- acid
- sample
- photocatalytic ability
- hydrofluoric acid
- Prior art date
Description
201217291 六、發明說明: 【發明所屬之技術領域】 本發明係關於在廣泛波長區域中對光有所感應,用以將有 害有機物質分解並有效地無害化之光觸媒材料,以及使用光 觸媒材料作為其應用所構成之過濾器。 【先前技術】 已知有藉由光使原本必須賦予高能量否則不會進行之反 應知以進行的光觸媒反應,截至目前為止,作為光觸媒材 料已知有一氧化鈦、氧化鋅、硫化録、氧化嫣等之所謂半 導體觸媒,以及釕聯吡啶錯合物等之金屬錯合物。 該等之中,二氧化鈦係安定性最高且幾乎沒有生物毒性, 故廣泛被使用作為各種化學反應或用於環境淨化之光觸媒。 此光觸媒經由40〇nm附近的近紫外光之照射,位於占滿 能帶(filled band)之電子被激發至傳導帶(c〇nducd〇n band) ’藉此發生電荷分離’在如此產生之電荷位⑷⑹中產 生氫氧自由基或超氧化物陰離子,利用該等之強力氧化作 用,而將有機鹵化物或NOx等環境污染物質予以分解。 又’對半導體製造設備、手術室等之醫療設備、醫藥製造 〇又備、& no製造设備之设置現場的給氣’或者於核能設施之 排氣裝置中’係使用以玻璃纖維所構成之HEPA過滤器 (High Efficiency Particurate Air Filter,高效率空氣過请哭)。 根據ns,HEPA過濾器係「以定額風量對於粒徑〇 3μηι 100133143 3 201217291 之粒子具有99.97%以上之粒子捕集率,且具有初期損失為 245Pa以下之性能的氣體過濾器」。 HEPA過濾器之過濾器部分一般係使直徑1〜ΙΟμηι以下 之玻璃纖維具有數ΙΟμηι之空隙,並以10%左右之填充率進 行填充而構成。 在給排氣中,除了屬於ΗΕΡΑ過濾器捕集對象之粒徑為 0.3μηι以上的粒子以外,存在有各種液體狀或氣體狀之有機 物,該等係無法利用ΗΕΡΑ過濾器予以去除。 在無法利用ΗΕΡΑ過濾器予以去除之粒子等對於給氣對 象屬於有害物之情況,係與其他手段併用而將其無害化,但 給排氣設備會變得複雜且高價。 ΗΕΡΑ過濾器等之過濾器係大多使用玻璃纖維。 玻璃纖維係以二氧化矽作為主成分,但二氧化矽屬於安定 的物質,化學活性低,無法期待其可具有將有害物質予以無 害化之觸媒機能。 為了對屬於安定物質之二氧化矽賦予化學活性,目前為 止,提案有數個將幾乎為純二氧化矽結晶的人工水晶之細 粒,利用氫氟酸(HF)等之氫鹵酸予以處理,藉此賦予光觸媒 能力之技術。 於W02005/089941號公報、日本專利特開2006-511175 號公報、特開2007-098205號公報、特開2007-098206號公 報及特開2007-307430號公報中,揭示有對低價且屬於安定 100133143 201217291 物質之純二氧化石夕(Si〇2)結晶的人工水晶之細粒利用氮氣 酸(HF)予以處理,藉以取代二氧化鈦之光觸媒能力。 於日本專利特開丽_〇9議號公報中係揭月匕示有將天缺 水晶或人工水晶載持於粒狀無機物或有機物而成之光觸媒 材料。 於日本專利特開腦_29,號公報及特開顺·靡似 號中係揭示有㈣板狀、粒狀、粉末狀 '塊狀、纖維狀之石 英(二氧化石夕)玻璃,並經由氫氟酸、氫氣酸、氯漠酸進行函 化處理之光觸媒材料。 • 於日本專利特開2007-098206號中係揭示有使用天然矽 石、人工矽石、熔融石英、矽石溶膠等之粒狀二氧化矽,將 : 其細粒利用氫氟酸進行_化處理而成之光觸媒材料。 。亥文獻中亦揭示將天然矽石、人工矽石、熔融石英、矽石 /合膠等載持於粒狀之無機物或有機物而成之光觸媒材料。 於曰本專利特開2〇〇7_〇982〇5號公報中係揭示有使用天 然水曰曰或人工水晶,並將其細粒利用氫氟酸進行鹵化處理而 成之光觸媒材料。 «亥文獻中’係揭示將光觸媒材料載持於粒狀之無機物或有 機物。 於曰本專利特開2007-098206號公報中係揭示有使用天 然矽石、人工矽石、熔融石英、矽石溶膠等之粒狀二氧化矽, 將其細粒利用氫氟酸進行S化處理而成之光觸媒材料。 100133143 201217291 該文獻中,係揭示將誠觸媒材料麟於粒狀之無機物或 有機物。 於曰本專利特開2007-307430號公報中係揭示將人工水 晶之細粒載持於粒狀之無機物或有機物而成之光觸媒材料。 (先前技術文獻) (專利文獻) 專利文獻1 專利文獻2 專利文獻3 專利文獻4 專利文獻5 專利文獻6 專利文獻7 專利文獻8 【發明内容】 W02005/089941 號公報 曰本專利特開2004-290747號公報 曰本專利特開2004-290748號公報 曰本專利特開2006-511175號公報 曰本專利特開2007-098205號公報 曰本專利特開2007-0982〇6號公報 曰本專利特開2007-307430號公報 曰本專利特開2007-098205號公報 (發明所欲解決之問題) 本案之課題在於獲得低價之光觸媒能力材料。 本案之課題在於獲得具有細粒以外之形態的光觸媒。 本案之課題在於獲得可利用紫外線以外之光的光觸媒。 本案之課題在於獲得具有光觸媒能力之過濾器。 本案之課題在於獲得使用具光觸媒能力的過濾器之給排 氣用裝置。 100133143 201217291 (解決問題之手段) 本發明人等發現’將_麵、無驗玻璃、卿玻璃等含 有二氧切之材料進行氫_處理之材料,亦可獲得光觸媒 能力。 本^月人等發現,將鈉舞破蹲、無驗玻璃、卿玻璃等含 有氧化夕之材料進行氫氟酸處理之材料,可獲得光觸媒能 力。 本f明人等發現,將簡麵、無驗玻璃、财玻璃等含 有氧夕之材料進行氫i酸處理之材料,亦可獲得光觸媒 能力。 本發月人等發現,未經氫_處理之含有二氧化碎之材料 所形成的細粒以外之板或纖維狀的材料,係具有光觸媒能 力。 本發明人等發現,將使用於窗戶玻璃之_玻璃予以氫氟 酸處理所得之材料,係具有光觸媒能力。 根據此等發現,本發明人等提出以下構成之發明。 本案中,作為基於此事實而解決先前所述之發明課題的手 段,係提供將鈉鈣玻璃材料進行氫鹵酸處理而得之光觸媒。 本案中係提供以下手段,作為用以解決該等問題之手段。 一種光觸媒材料’係經氫S酸處理之納i弓破壤。 一種光觸媒材料’係經氫_酸處理之玻璃纖維。 一種具有光觸媒能力之過濾器,係由經氫_酸處理之玻璃 100133143 7 201217291 纖維所構成。 一種給排氣裝置,係使用具有光觸媒能力之過濾器,該過 濾器係由經氫i酸處理之鈉鈣玻璃纖維所構成。 更具體之構成如下。 (1) 一種具有光觸媒能力之玻璃,係將含有二氧化矽以外 之成分的玻璃以氫鹵酸進行處理。 (2) 如上述(1)之具有光觸媒能力之玻璃,其中,含有二氧 化石夕以外之成分的玻璃為鈉飼玻璃。 (3) 如上述(1)之具有光觸媒能力之玻璃,其中,含有二氧 化矽以外之成分的玻璃為無鹼玻璃。 (4) 如上述(1)之具有光觸媒能力之玻璃,其中,含有二氧 化矽以外之成分的玻璃為硼矽玻璃。 (5) 如上述(1)之具有光觸媒能力之玻璃,其中,氫齒酸為 氫氟酸。 (6) 如上述(1)之具有光觸媒能力之玻璃,其中,氫鹵酸為 氫氯酸。 (7) 如上述(1)之具有光觸媒能力之玻璃,其中,氫i酸為 氫溴酸。 (8) 如上述(1)之具有光觸媒能力之玻璃,其中,玻璃為粒 狀體。 (9) 如上述(1)之具有光觸媒能力之玻璃,其中,玻璃為纖 維狀體。 100133143 201217291 之坡璃,其中,坡璃為板 (9)如上述(1)之具有光觸媒能力 狀體。 (10) —種過濾器,係由將含二氣 ^ ^ ^ 匕石夕之玻故以虱南酸進行 處理的纖維狀體所形成。 (11) 一種給排氣料3,係使用由將含二氧⑽之玻璃以 氫鹵酸進行處理的纖維狀體所形成之過濾器。 (發明效果) “ 根據此專手段’可獲得以下效果。 經氩函酸處理之納妈玻璃若經光照射,則會分解有機污染 物質。 〜經氫_酸處理之玻璃纖維係藉由作成織布或不織布,而可 獲得具有光觸媒能力之過濾器。 、、二氫鹵齩處理之鈉鈣玻璃板若經紫外光或可見光照射,則 會分解有機物。 除此之外’經氫1s酸處理之鈉鈣玻璃即便在玻璃板表面為 平滑透明之狀態仍可發揮觸媒機能。 【實施方式】 光觸媒此力之量測係利用亞曱藍之褪色試驗而量測基本 事項’並利用屬於病態住宅症候群(Sick House Syndrome)成 因物質之一的乙醛之分解試驗’量測光觸媒能力。 (亞曱監褪色試驗方法) 亞甲藍掩色試驗係如下述般進行。 100133143
S 9 201217291 將試料洗淨、乾燥後,置入亞甲藍水溶液中,由黑光燈照 射24小時之波長為300〜400nm的紫外光,從吸光度相對 於波長664nm之光的前後變化,量測亞曱藍水溶液之褪色 率〇 又,將試料於暗處放置24小時,量測亞曱藍對試料之吸 附率。 作為亞曱藍水溶液,係於0.0374g之亞曱藍三水和物 (Mw=374)加入精製水成為lOOmL,對此亞曱藍水溶液5mL 添加精製水495mL,使濃度成為O.Olmmol/L而使用。 褪色率之測定於聚苯乙烯製容器中之亞曱藍試藥2〇mL 中置入試料,於暗室中,由黑光燈照射24小時之波長為300 〜400nm的紫外光,量測照射前與照射後亞曱藍試藥對於波 長664nm之光的吸光度變化。 根據吸光度測疋結果’由以下所不之Lambert-Beer式, 算出亞甲藍試藥之褪色率(%),獲得試料之亞曱藍試藥的分 解率。 100-Abs(24h)/Abs(0h) X100=褪色率) 其中,Abs(24h)係照射24小時後之吸光率,Abs(Oh)係照 射前之吸光率。 又’為了確認吸光度之變化,將試料於暗處下放置24小 時’量測亞曱藍對試料之吸附率(%),算出可視為真觸媒能 力之褪色率與吸附率的差(%)。 100133143 10 201217291 (乙醛分解試驗方法) 乙酸分解試驗係如下述般進行。 將s式料洗淨、乾燥後,置於浪度定為5.Oppm、氣體流量 定為1.0L/分之乙醛環境中,照射來自黑光燈之波長為3〇〇 〜400nm的紫外光,量測每單位時間之乙醛分解量及因乙醛 分解所產生之每單位時間的二氧化碳產生量。 利用實施例1、2、3,說明取代結晶性的水晶而使用非結 晶性的玻璃作為光觸媒之例。 [貫施例1 ] (納辑玻璃粒) 作為實施例1,係說明使用鈉鈣玻璃粒作為光觸媒之例。 試料1係省略含有量未滿1%之成分,基本組成係si〇2 為 71.9%、CaO 為 7.8%、Al2〇3 為 1.7%、MgO 為 4 〇%、
NasO為13.3%之一般所使用的鈉鈣玻璃所構成之玻璃纖 維,將此玻璃纖維於濃度10%之氫氟酸水溶液中浸潰處理5 分鐘’洗淨、乾燥並粉碎為粒徑〇.2mm者。 將如此所得之玻璃試料浸潰於亞曱藍水溶液中,針對照射 70小時之可見光或於暗處下靜置70小時者,量測照射或靜 置前後之亞甲藍的褪色率。 試料1之亞曱藍的褪色率,在經氫氟酸處理之情況係為 42%。 另外’在未經氫氟酸處理之情況係為22%。
S 100133143 201217291 由此數據可知’試料1之鈉鈣破螭係即便不經過氫氟酸處 理’對亞甲藍之褪色亦為有效,而在經氫氟酸處理之情況則 更為有效。 [實施例2] (無鹼玻璃) 試料2係省略含有量未滿1%之成分,基本組成係Si02 為 55.0%、CaO 為 23.0%、Al2〇3 為 14.2%、B2〇3 為 6.2% 之無鹼玻璃。 試料2之亞甲藍的褪色率’在經氫氟酸處理之情況係為 42% 〇 另外,在未經氫氟酸處理之情況係為16%。 由此數據可知’試料2之無鹼玻璃係即便不經過氫氟酸處 理,對亞甲藍之褪色亦為有效,而在經氳氟酸處理之情況則 更為有效。 [實施例3] (侧矽玻璃) 試料3係省略含有量未滿1%之成分,基本組成係§丨〇2 為 33.0%、CaO 為 6.8%、Al2〇3 為 1.3%、B2〇3 為 37.4%、
MgO為5.5%、Na2〇為16.0%之硼石夕玻璃。 試料3之亞甲藍的褪色率,在經氫氟酸處理之情況係為 26%。 另外,在未經氳氟酸處理之情況係為16%。 100133143 12 201217291 由此數據可知’試料3之硼矽玻璃係即便不經過氫氟酸處 理,對亞曱藍之褪色率亦為有效,而在經氫氟酸處理之情况 則更為有效。 [實施例4] (玻璃纖維) 針對取代粒狀玻璃而使用纖維狀玻璃之光觸媒進行說明。 (亞甲藍褪色試驗方法) 玻璃纖維所造成之褪色率的測定,係於石英玻璃製容器中 的亞甲監试藥100mL中置入經氫氟酸處理之玻璃纖維, 照射24小時之來自螢光燈的可見光,測定照射前與照射後 亞曱監試藥對於波長664nm之光的吸光度。 根據吸光度測疋結果’由上述Lambert-Beer式算出亞曱 藍試藥之褪色率(%),獲得試料之亞曱藍試藥的分解率。 試料4係屬於一般玻璃纖維之鈉鈣玻璃纖維,省略含有量 未滿1%之成分’基本組成係Si〇2為71.9%、CaO為7.8%、 八12〇3為1.7%、]^〇為4.0%、他2〇為13.3%之一般所使 用的鈉鈣玻璃,將由其所構成之玻璃纖維於濃度〇.〇5%、0.1 %、0.5%、1%之氫氟酸水溶液中浸潰處理5分鐘,益經洗 淨、乾燥者。 利用該試料4,獲得12%〜23%之亞曱藍褪色率。 另外,相同鈉鈣玻璃纖維在未進行氫氟酸浸潰處理之情 況,亞曱藍褪色率係7%。 100133143 13 201217291 [實施例5] (玻璃板) 說明取代粒狀或纖維狀而使用板狀玻璃之光觸媒進行說 明。 作為實施例5,針對使用上述鈉鈣玻璃板之例進行說明。 將厚度lmm之納妈玻璃板切出3〇x30mm2,浸潰於氫氟 酸溶液中,使其濃度及處理時間變化而進行浸潰處理後,進 行水洗並乾燥,以此作為試驗片。 以下,對於使氫氟酸溶液濃度及處理時間變化而進行處理 之試驗片試料5〜試料14,將褪色率(%)、吸附率(%)及差(%) 示如下。 試料5係於濃度5%之氫氟酸中浸漬處理5分鐘者。 試料5之褪色率為15%,吸附率為15%,其差為0%。 試料6係於濃度10%之氫氟酸中浸潰處理5分鐘者。 試料6之褪色率為14%,吸附率為15%,其差為-1%。 試料7係於濃度1%之氫氟酸中浸漬處理5分鐘者。 試料7之褪色率為16%,吸附率為15%,其差為1%。 試料8係於濃度10%之氫氟酸中浸潰處理10分鐘者。 試料8之褪色率為21%,吸附率為16%,其差為5%。 試料9係於濃度20%之氫氟酸中浸潰處理5分鐘者。 試料9之褪色率為19%,吸附率為14%,其差為5%。 針對試料5〜9之褪色率、吸附率及其差進行探討之結 100133143 14 201217291 果,褪色率21%、吸附率16%之試料8及褪色率19%、吸 附率14%之試料9係為有用。 此外,為了確認處理條件,係將氫氟酸濃度固定為20%, 準備改變浸潰處理時間之試料10〜試料14,進行同樣計測。 試料10係於氫氟酸中浸潰處理15分鐘者。 試料10之褪色率為22%,吸附率為11%,其差為11%。 試料11係於氫氟酸中浸潰處理15分鐘者。 試料11之褪色率為13%,吸附率為5%,其差為8%。 試料12係與試料7同樣地於氫氟酸中浸潰處理15分鐘 者。 此試料12之褪色率為13%,與試料7相同,但吸附率大 至11%,其差為2%。 試料13為對氫氟酸浸潰處理20分鐘者。 試料13之褪色率為15%,吸附率為8%,其差為7%。 另外,試料13之應特別註記事項係顯示推定為蓮花效應 (Lotus effect)的撥水性。 試料14係於氫氟酸中浸潰處理30分鐘者。 試料14之褪色率小至2%,但因吸附率為0%,其差為2 %。 試料11及試料12雖為相同處理條件,但仍顯示不同的吸 附率,故作為在相同條件下調查試料之誤差的目的,將以全 部於濃度20%中浸潰處理15分鐘之相同條件進行處理的試 100133143 15 201217291 料15〜試料19之褪色率、吸附率及其差示如下。 試料15之褪色率為22%,吸附率為11%,其差為11%。 試料16之褪色率為13%,吸附率為5%,其差為8%。 試料17之褪色率為13%,吸附率為11%,其差為2%。 試料18之褪色率為8%,吸附率為6%,其差為2%。 試料19之褪色率為8%,吸附率為8%,其差為0%。 雖有誤差,但明顯可知以上所示之試料係具有進行亞曱藍 分解之觸媒能力。 (參考例) 為了與經氫氟酸處理之青板玻璃的觸媒能力進行比較,將 二氧化鈦塗佈於鈉鈣玻璃基板上而作成銳鈦礦型二氧化 鈦,此比較試料之褪色率為29%,吸附率為25%,其差為 4%。 (乙醛分解試驗) 乙醛分解試驗所使用之試料20係與實施例1〜15之情況 同樣被普遍使用之納妈玻璃,省略含有量未滿1 %之成分, 基本組成係 Si02 為 71,9%、CaO 為 7.8%、A1203 為 1.7%、 MgO 為 4.0%、Na20 為 13.3%。 試料20係於與試料10〜12同樣為濃度20%的氫氟酸中 浸潰處理15分鐘後,水洗並乾燥,從厚度1mm之鈉妈玻璃 切出 5〇xlOOmm2 者。 試料20所得之乙醛的每單位時間分解量為0.98μιηο1/小 100133143 16 201217291 時,二氧化碳之每單位時間生成量為l 3—〇i/小時,乙酸 去除率為7.11%,二氧化碳之轉化率為5%。 由此結果可知,試料20之鈉鈣玻璃對於乙醛係具有可實 用之觸媒機能。 最後,為了得知在-般使用情況下之亞甲藍提色,係使用 與試料20之鈉鈣玻螭為相同條件的試料2卜照射6小時將 來自營光燈之紫外光以紫外線遮蔽過遽器去除後之波長 400〜710nm的可見光,獲得4%之褪色率。 由此結果可知,試料20之鈉鈣玻璃對於乙醛係具有可實 用之觸媒機能。 (產業上之可利用性) 經氫鹵酸處理之鈉鈣玻璃經由照射光而發揮分解有機物 之光觸媒能力。 此觸媒能力係與僅對紫外光具有觸媒能力之二氧化鈦不 同,經由可見光亦可發揮觸媒能力,故極為有效率且有用。 、經氫鹵酸處理之納辦玻璃纖維係藉由作成織布或不織 布,而可獲得聚光觸媒能力的過濾器^ > 使用由經氫i酸處理之玻璃纖維所構成 人i姆應is的給排 氣裝置,在要求去除有機物之設施中係有用。 本案發明之經氫s酸處理之鈉鈣板玻璃係為平滑透明,藉 由照射光而可發揮分解有機物之光觸媒能力。 此板玻璃係可使用於窗戶玻璃’與大氣接觸側的面係可將 100133143 17 201217291 大氣中之有機污染物質予以分解去除,於屋内側則可將病態 住宅症候群之原因物質乙醛、廚房之油煙、香菸之煙等予以 分解去除,作為建築物之窗戶材料係有用。 又,當使用作為汽車等車輛之窗戶玻璃的情況,可期待車 外排出氣體中之有機物質的分解去除、車内各種有機物質的 分解去除機能。 又,由於亦具有推定為蓮花效果之撥水效果,進而可期待 伴隨於此撥水效果之自我洗淨效果,故作為接觸於外界氣體 之建築物的窗戶玻璃、車輛等之輸送裝置的窗戶玻璃係有 用。 又,雖未進行定量測定,但亦可定性地觀察到對於氮氧化 物之光觸媒能力。 100133143 18
Claims (1)
- 201217291 七、申請專利範圍: 1. 一種具有光觸媒能力之玻璃,其特徵為,將含有二氧化 矽以外之成分的玻璃以氫鹵酸進行處理。 2. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述玻璃為鈉約玻璃。 3. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述玻璃為無驗玻璃。 4. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述玻璃為硼矽玻璃。 5. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述氫齒酸為氫氟酸。 6. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述氫_酸為氫氯酸。 7. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述氫鹵酸為氫溴酸。 8. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述玻璃為粒狀體。 9. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述玻璃為纖維狀體。 10. 如申請專利範圍第1項之具有光觸媒能力之玻璃,其 中,上述玻璃為板狀體。 11. 一種過濾器,係由將含二氧化矽之玻璃以氫i酸進行 100133143 19 201217291 處理之纖維狀體所形成。 12.—種給排氣用裝置,係使用由將含二氧化矽之玻璃以 氫鹵酸進行處理的纖維狀體所形成之過濾器。 100133143 20 201217291 四、指定代表圖: (一) 本案指定代表圖為:無 (二) 本代表圖之元件符號簡單說明: 無 五、本案若有化學式時,請揭示最能顯示發明特徵的化學式: 益 100133143 2