TW200908046A - Tape for fixing aluminum electrolytic condenser elements windings, and aluminum electrolytic condenser - Google Patents
Tape for fixing aluminum electrolytic condenser elements windings, and aluminum electrolytic condenser Download PDFInfo
- Publication number
- TW200908046A TW200908046A TW097110849A TW97110849A TW200908046A TW 200908046 A TW200908046 A TW 200908046A TW 097110849 A TW097110849 A TW 097110849A TW 97110849 A TW97110849 A TW 97110849A TW 200908046 A TW200908046 A TW 200908046A
- Authority
- TW
- Taiwan
- Prior art keywords
- paper
- tape
- layer
- adhesive
- aluminum electrolytic
- Prior art date
Description
200908046 九、發明說明: 【發明所屬之技術領域】 ”上u六和在削增楫成之鋁電解電容 :器元件捲繞固定用料及使用上述膠帶而成之㈣解電: L无前技術】 著::::!解電容器之元件捲繞固定係使用接著劑或黏 /贡’可谷易地實施機械化等之黏著膠帶方式成為主 f。關於㈣電解電容㈣黏著膠帶,提出有將馬尼拉麻 、我、牛皮紙、合成纖維等用於支撐基材之銘電解電容 末端固定黏著膠帶(專利文獻!及2)。 〇 : 然而,將該等用於紹電解電容器之元件捲繞固定之情形 f 口支撐基材之基底為紙,故強度相對不足,例如,將 0 μηι以下之紙用作切基材之薄型黏著膠帶,在以捲繞 機貼附於電容器時會發生斷帶,…免斷帶,必須降低 速度(貼帶操作性)等,成為操作性降低之原因。又, -件捲繞固定膠帶之寬度為5 形時,操作性之降低尤為顯著。 士又,,:紙之厚度增厚,例如使用超過5〇_之情形 8τΓ 因膝▼強度相對變強,1 1 但捲完後之電容巧直,° 料操作性之降低’ 型電容器中。…不必要地變得過大’難以適用於小 利文獻】·日本專利特公昭62-62454號公報 和文獻2 ·日本專利特公昭62-62455號公報 13006I.doc 200908046 【發明内容】 發明所欲解決之問題 本發”於上述事實,*目的^提供—種紹電 。。電η捲繞固u黏著膝帶以及使用其之銘電解電容 益’該膠帶在用於鋁電解雷衮 屯解电合态之清形時,於捲繞該膠帶 時不發生斷帶,由此,不隆 雨—抑 +降低貼耶刼作性,可防止捲完後 電容器不必要地變得過大之不良現象。 解決問題之方法 本發明者等人為了達成上述目的而進行深入研究,结果 發現,、藉由使用下述銘電解電容器元件捲繞固定用膠;, 可達成上述目的,從而完成本發明。 7即’本發明之鋁電解電容器元件捲繞固定用膠帶,其特 徵在於’其係、於支撐基材之單面具有黏著劑層纟,其中, 上述支撐基材具有至少—層馬尼拉麻紙、牛皮紙、合成纖 、准紙或者包含該等之兩種以上之混抄紙之層,上述支撐基 材之密度大於G.9gW,上述支#基材之厚度為15〜5〇㈣。 本叙明之鋁電解電容器元件捲繞固定用膠帶,其特徵在 於’。其係於支撐基材之單面具有黏著劑層者,其中,上述 t:基材具有積層馬尼拉麻紙、牛皮紙、合成纖維紙或者 包含該等之兩種以上之混抄紙而成之兩層以上之多重層, 上述多重層中至少-層之密度大於0.9 gW,上述支撐基 材之厚度為15〜50 μηι。 、本發明之鋁電解電容器元件捲繞固定用膠帶,其特徵在 '至乂上述多重層之與黏著劑層相反之一側之最外層之 13006I.doc 200908046 密度大於0·9 g/cni3。 本發朋之I呂電解電容器,其特徵在於,其係使用本發明 之鋁電解電容器元件捲繞固定用膠帶而製成者。 發明之效果 本發明之鋁電解電容器元件捲繞固定用膠帶,作為支撐 =材,具有至少一層馬尼拉麻紙、牛皮紙、合成纖維紙: 者包含该等之兩種以上之混抄紙之層,支揮基材之穷产大 於〇一,支樓基材之厚度為15〜50_,藉此可二提 供如下1呂電解電容器:於捲繞該膝帶時不發生斷帶,由此 不降低貼帶操作性,可防止捲回後電容器不必要地變得過 大之不良現象。 【實施方式】 本!X明之Is電解電容||捲繞固定㈣著膠帶係由支撐基 材與黏著劑層構成。以下具體說明。 作為本發明所使用之支撐基材,其係由至少—層馬尼拉 麻紙、牛皮紙'合成纖維紙或者包含該等之兩種以上之混 抄紙之層構成。藉由佶用μ、+ /tci 楮由使用上述紙,可確保電解電容器之耐 熱性、電解液保持性。 又’作為本發明所使用之支撐基材,其係由積層馬尼拉 麻紙、牛皮紙、合成纖維紙或者包含該等之兩種以上之混 抄紙而成之兩層以上之多重層構成。藉由製成積層上料 而成之兩層以上之多重層而使用,與上述同樣,可確保電 解電容器之耐熱性及電解液保持性。 關於支撐基材之密度,於支撐基材具有至少一層馬尼拉 130061 .doc 200908046 麻紙、牛皮紙、合成纖維紙或者包含該等之兩種以上之混 抄紙之層之情形時’支撐基材之密度大於0.9 g/em3。若^ 述紙之密度為0.9 ,則有‘,、、法確保作為銘電解電 容器元件捲繞固定用之強度之虞。 又,關於支撐基材之密度,於支撐基材具有積層馬尼拉 麻紙、牛皮紙、合成纖維紙或者包含該等之兩種以上之混 抄紙而成之兩層以上之多重層之情形時,多重層之至少一& 層之密度大於G.9 g/em3’較好的是多重層之與:著制相 反之-側之3最外層之密度大於"一3。若上述紙之密度 為.^g/cni以下,則有無法確保作為銘電解電容器元件捲 繞固定用之強度之虞。 此處’說明上述密度(g/cm3)之測定方法。首先,自支撐 基材上’取出大小約1心爪或者額定尺寸之試驗片,測 定上述試驗片之長寬及厚度後,測定重量。由該重量Μ 分(%)依據下式計算出密度。再者,上述水分係指:將剛 以抄紙機抄過之後之卷紙立即以電阻式水分計測定;或 者,以乾燥法測定之情形時,取約2 g試驗片放入稱量 瓶,測^其重#,於1G5±3txl小時以上之條件下乾燥 後,於乾燥器内冷卻至大致常溫,成為怪量後,求出豆減 少量,將相對原來之重量之百分率作為水分。 密度(g/cm3)=[測定重量(g)x(1 —水分(%))/_/[長尺寸 (m)x寬尺寸(m)x厚度(m)] 支樓基材之厚度為15〜50 _,較好的是20〜4〇 若 支撐基材之厚度超過5〇 μπι ’則捲完後之電容器直徑變 J 3006!.doc 200908046 ,一 %分命-刀一乃曲,若不足15 μηι, 則支擇基材之強度過低,損及害實用性…支撐基材形 成多重層之情形時,多重層之與黏著劑層相反之-側之最 外層之厚度較好的是10 _以上,更好的是。〜川陶。若 不足10 μηι,則無法確保作為鋁電解電容器元件捲繞固 用膠帶所期望之支撐基材之強度。 、本發明之黏著膠帶之黏著劑層只要具有黏著性則其材質 或構成等並無特別限定’可使用通常使用之黏著劑,例如 丙烯I系黏著劑或橡膠系黏著劑、矽氧系黏著劑等常用之 感屋黏著劑。該等之中,較好的是使用丙烯酸系黏著劑。 作為丙烯酸系黏著劑,可使用賦予黏著性之低玻璃轉移 溫度(Tg)之丙烯酸系單體作為主單體。又,亦可使用:職 予黏著性、凝聚力之高Tg之共聚單體;或含有用於改善交 聯性和黏著性之官能基之單體、即單乙烯性不飽和單體 等。 作為上述主單體,可列舉將如下一種或兩種以上(曱基) 丙烯酸烷基酯用作單體成分之丙烯酸系聚合物等,該(甲 基)丙烯酸烷基酯例如為(甲基)丙烯酸甲酯、(甲基)丙稀酸 乙酷、(曱基)丙烯酸丁酯、(甲基)丙烯酸異戊酯、(甲基)丙 烯酸正己酯、(曱基)丙烯酸2-乙基己酯、(甲基)丙烯酸異 辛酯、(甲基)丙烯酸異壬酯、(甲基)丙烯酸癸酯、(曱基)丙 烯酸十二酯等。上述丙烯酸系黏著劑之耐熱性亦較高,係 本發明最適合之黏著劑。 作為上述共聚單體,可列舉例如,醋酸乙烯酯、丙酸乙 130061.doc 200908046 烯酯、乙烯基醚、苯乙烯、丙烯腈、甲基丙烯腈等含有乙 炸基之化合物。 作為上述含官能基單體,可列舉例如,丙烯酸、子基丙 烯酸、伊康酸、馬來酸、富馬酸、巴豆酸等含叛基單體; (曱基)丙烯酸2-羥乙酯、(甲基)丙烯酸2_經丙酯、(甲基)丙 烯酸4-羥丁酯、N-羥曱基丙烯醯胺、烯丙醇等含羥基單 體,(甲基)丙烯酸二曱胺基乙酯、(曱基)丙烯酸二乙胺基 乙酯、(甲基)丙烯酸二曱胺基丙酯等含三級胺基單體;丙 烯醯胺、曱基丙烯醯胺等含醯胺基單體;N_甲基(曱基)丙 烯醯胺、N-乙基(甲基)丙烯醯胺、N_曱氧基曱基(甲基)丙 烯醯胺、N-乙氧基曱基(甲基)丙烯醯胺' n-第三丁基(曱 基)丙烯醯胺、N-辛基(曱基)丙烯醯胺等含N_取代醯胺基單 體;曱基丙烯酸縮水甘油酯等含環氧基單體等。該等可共 聚合之單體成分可使用一種或兩種以上。該等可共聚合單 體之使用量為全部單體成分之70重量。/。以下,更好的是4〇 重量%以下。 上述丙烯酸系聚合物係將單一單體或兩種以上單體之混 合物加以聚合而獲得。聚合可採用溶液聚合、乳化聚合、 本體聚合、懸浮聚合等任一方式。丙烯酸系聚合物之重量 平均分子量(Mw)較好的是50萬〜15〇萬,更好的是川萬 〜120萬。重量平均分子量(Mw)和數量平均分子量之 分散度(Mw/Mn)較好的是6〜1 〇。 重S平均分子ϊ係以GPC法藉由標準聚苯乙烯換算之 值。作為GPC主機,使用T〇s〇h公司製之;hLC_812〇gP(:, 130061 .doc -10- 200908046 管柱溫度4(TC,泵流量0.5 ml/min,使用檢測器RI之資料 處理係使用分子量事先已知之標準聚苯乙烯之校線 (在分子量500〜2060萬之校正),藉由分子量換算求得分子 量。 使用管柱:TSKgel GMH-H(S)x2根(Tosoh公司製) 流動相:四氫。夫喃 注入量:100 μΐ f 樣品濃度:1 .〇 g/l(四氫呋喃溶液) 分散度係作A重量平均分子量與數量平均/分子量之比而 算出。數量平均分子量之測定,係以與重量平均分子量之 測定相同之方法實施。 上述丙烯酸系黏著劑可適宜含有交聯劑。可列舉例如, 異亂酸醋系交聯劑、環氧交聯劑、氮丙咬系交聯劑 物系交聯劑等。 发σ 交聯劑之使用量並無特別之限制,例如 酸系聚合物100重量份,# # M s 、上述丙烯 里知較好的是0.1〜15重量份,承虹 是1〜10重量份。若不足〇1 好的 足,若超過15重量份,則由於黏著:者劑之凝聚力不 著力不足等之原因。者劑之交聯過多而成為黏 上述黏著劑除上述成分外 各種起始劑m抗Mm 已知之 〜抗老化劑、填充存丨、益Α _ 移劑、塑化劑等添加劑。 、 者色训、鏈轉 用於調製上述黏著劑層之溶劑並 用有機溶劑。作為有機溶劑膜年之限制,通常使 獏時之塗骐穩定性之方 130061.doc 200908046 面而言,較好 •疋〇均勻溶解黏著劑組合物者。# $ # # 溶劑,可列舉例如t作為有機 苯、間二甲笨、針燒、己烧、庚燒'甲苯、鄰二甲 對二甲苯、環已烷、甲醇、乙St、显$ 醇、1-戊醇、環P _ 丁砰乙%、異丙 ^ %、2·甲基環己醇、二乙基醚、異丙x "、二丁基…喃、丙酮、甲= 酮、τ基異丁基τ基乙基 環己酮、甲基枣己 甲基戊基酮)、二異丁基酮、 酸乙脂、醋U = ㈣甲醋'醋 _)、心_1甲:、 土乙醒胺(DMAc)、Ν-尹美咐< & * 甲氧基乙醇、2_乙氣其… N歹基❸各烷酮、2- 有機溶劑,較好的 丁氧基乙醇等。作為上述 们戍“i車乂好的是醋酸乙酯、甲苯 劑,黏著劑組合物通常 、。藉由浴 …s “周製成固體成分濃度為5〜50重量 /。,較好的是5〜30重哥〇/„,审紅从θ , 里 m ^ ^ ^ ^ 更好的疋10〜25重量%之溶液。 斤形成之黏者劑層之厚度並無特別之限 疋2,〇叫左右,更好的是:較好的 】〇〜30 _。若不μ _左右,最好的是 足2 μηι,則有作為元件捲 捲繞^性降低之情況。另―方面,耀帶之 變得過厚而難以操作之情況。力起過10〇 μι則有 支:=: = :1層之形成方法係將黏著劑組合物塗佈於 ==二黏著劑組合物層。作為該形成方法,可 ::各種方法。例如’於黏著劑組合物層之形成中使用連 、’塗佈裝置之情形時,可列舉例如如 著南丨έ曰入、六、六、 r万忐·連續供給黏 :丄且5師合液)’藉由安裝於裝置前端之模具等喷出機 構而於溥片基材上連續擠出成薄層、 作為形成黏著劑 130061.doc 200908046 組合物層之方法,於採用批次方式之情形時,可列舉如下 μ·將黏著劑組合物(溶液)流延至支撐基材上,以敷料 為或絲棒(mayer bar)、到刀塗佈機進行成形之方法。如 此,將薄層化之黏著劑組合物積層至支撐基材上後,進行 加熱而除去溶劑。 本發月之黏著劑層於貼附至不鏽鋼板⑽zQ237)上之狀 :下’於剝離角度90。、拉伸速度5〇_/油下 好的是3.〇_贿以上,更好的是3.5卿麵以上。= 時’本發明之黏著膠帶可維持作為元件捲繞固定用 膠π所必需之黏著力。 」下’對本發明之銘電解電容器加以說明,該銘電解電 谷时包括·將陽極笛與陰極荡經由隔板捲繞而成之電容器 凡件,分別自陽極、陰極箱引出之端子,密封该等之封^ 材枓與外殼。此處’作為電容器元件之捲繞固定用膠帶, 使用上述鋁電解電容写、亓生 件捲繞固定用膠帶。藉由使用該 ^可獲付如下鋁電解電容器:於捲繞該膠帶時不發生 斷帶’由此不降低貼帶操作性,不會發生捲完後之電;, 不必要地變得過大之不良現象。 實施例 以下基於實施例說明太双αη 例兄月本發明,但本發明並不限定於古亥 等。再者,以下,份係指重量份。 …" 實施例1 J ”^ g/cm3、厚度為2〇陣之 早層牛皮紙(曰本高度紙工業製)。 130061.doc 200908046 黏著劑層使用以下之方法調製。首先,調製作為基礎聚 合物之丙烯酸系聚合物,其由包含1QG份丙稀酸正丁醋與5 份丙烯酸之單體混合溶液獲得。相對於1〇〇份該丙烯酸系 聚合物’添加2份異氰酸醋系交聯劑(商品名:c〇r〇nate L、日本聚胺酯製)' 5〇〇份作為溶劑之曱苯,調製丙烯酸 系黏著劑溶液°將該丙烯酸系黏著劑溶液塗佈至支撑基材 上並加以乾燥,使其成為厚度為2〇 μηι之黏著劑層,製作
黏著劑層。 實施例2 作為支撐基材’使用由密度為0.95 g/cm3、厚度為Η 之單層牛皮紙(日本高度紙工業製)與密度為〇 75 g/cm3、厚 度為15 μηι之單層牛皮紙(日本高度紙工業製)構成之雙層 牛皮紙(曰本高度紙工業製)。 黏著劑層使用以下之方法調製。首先,調製作為基礎聚 合物之丙烯酸系聚合物,其由包含7〇份丙烯酸正丁酯、h 份丙烯酸2-乙基己酯與5份丙烯酸之單體混合溶液獲得。 相對於1 00份該丙烯酸系聚合物,添加2份異氰酸酯系交聯 劑(商品名:CORONATE L、曰本聚胺酯製)、5〇〇份作為溶 劑之曱苯’調製丙烯酸系黏著劑溶液。將該丙稀酸系黏著 劑溶液塗佈至支樓基材上並加以乾燥,使其成為厚产為2〇 μιη之黏著劑層,製作黏著劑層。 比較例1 μηι之 於實施例1中,使用密度為0.75 g/cm3、厚度為2〇 單層牛皮紙(曰本高度紙工業製)作為支撐基材,除此以 130061.doc -14- 200908046 外,與實施例1同樣,製作黏著膠帶。 比較例2 於實施例2中’使用由密度為〇8m 夕黾显止+从/ ^^415 μπι 曰,,氏(日本高度紙工業製)與密度為〇75 度為1 5 μηι之單岸半由^士一 :層牛皮紙(曰本南度紙工業製)構成之雙層 牛皮紙(日本向度紙工掌製彳作盔土择i — 系表)作為支撐基材,除此以外,與 貫允例2同樣,製作黏著膠帶。 、下揭示實紅例與比較例中得到之黏著膠帶之評價方法 和評價結果。 、/ <貼帶操作性之評價> 將β著勝γ切割加工成寬2·5顏之磁帶狀,在假想為電 容器捲繞機之磁帶捲繞機中,確認以50 m/分鐘之速度移 打之情形時之黏著膠帶之移行狀態。 表1 --L~~~ -1__二丨一” P便將本發明之黏著膠帶用於鋁電解電容器元件固哀 达之b形日守,亦可確認該膠帶於捲繞時不發生斷帶,巧 -、占帀操作性,可防止捲完後之電容器不必要地變得这 之不I J. 水。乃一万面’於比較例中,可確認於捲繞瑪 時發生斷帶、貼帶操作性降低。 【圖式簡單說明】 圖Η系表示本發明之黏著膠帶之一例之概念圖。 130061 .d〇c •15- 200908046 圖2係表示本發明之黏著膠帶之一例之概念圖。 【主要元件符號說明】 1 支樓基材 1-1 支撐基材 1-2 支撐基材(最外層) 2 黏著劑層 3 鋁電解電容器元件固定用膠帶 130061.doc 16-
Claims (1)
- 200908046 、申請專利範圍·· 、電解電W %件捲繞固定用勝帶,其特徵在於, 、糸於支撐基材之單面具有黏著劑層者,其中, 上述支撐基材具有至少一屬馬尼拉麻紙、牛皮紙、人 成纖維紙或者包含該等之兩種以上之混抄紙之層,—— 上述支擇基材之密度大於0.9 g/cm3, 2. 上述支撐基材之厚度為15〜50 μιη。 種飽电解電谷器元件捲繞固定用膠帶,其特徵在於, 其係於支撐基材之單面具有黏㈣層者,其中, 上述支撐基材具有積層兩層以上之馬尼拉麻紙、牛皮 紙、合成纖維紙或者包含該等之兩種以上之混抄紙而成 之多重層, 上述夕重層中至少_層之密度大於9呂/⑽3, 上述支撐基材之厚度為15〜50 μπι。 3·如請求項2之㈣解電容器元件捲繞固定用膠帶,其中 至ν上述夕重層之與黏著劑層相反之一側之最外層之密 度大於0.9 g/cm3。 4· -種銘電解電容器’其係使用如請求項⑴中任一項之 I呂電解電容器兀件捲繞固定用膠帶而製成者。 130061.doc