KR950032676A - 자동차 배기재료용 열연페라이트강 - Google Patents
자동차 배기재료용 열연페라이트강 Download PDFInfo
- Publication number
- KR950032676A KR950032676A KR1019950009472A KR19950009472A KR950032676A KR 950032676 A KR950032676 A KR 950032676A KR 1019950009472 A KR1019950009472 A KR 1019950009472A KR 19950009472 A KR19950009472 A KR 19950009472A KR 950032676 A KR950032676 A KR 950032676A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- weight
- formula
- hot
- automobile exhaust
- Prior art date
Abstract
본 발명은, 자동차의 배기가스재료, 특히 고온으로 가열되는 배기 다기관, 배기 파이프 등의 재료로서 열연소둔 상태로 이용될수 있는 페라이트강에 관한 것으로, 필수합금원소로서 Si : 0.4중량%∼2중량%, Cr : 6중량%∼17중량%, P : 0.025중량%∼0.10중량%, Nb : 0.35중량%∼0.60중량%를 함유하고, 불순물 원소가 하기의범위로 제한되어 있으며, C : 0.02중량%이하, Mn : 0.8주양% 이하, N : 0.015중량%이하, Al : 0.02중량% 이하, Ti : 0.02중량% 이하, Zr : 0.02중량% 이하 또 성분의 중량%가 하기식 (1) 및 (2)를 만족하고, 식 (1)Nb/(C+N)≥13식 (2) 11≤Cr+3Si+4Nb-50(C+N+P)-Mn-Ni-Co+Mo+Cu≤16.5 잔부는 Fe와 불가피적 불순물로 이루어지는 것을 특징으로 하는 자동차 배기재료용 열연페라이트강이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 열연소둔판, 또는 냉연소둔판의 신장에 미치는 Nb(C+N), Zr/(C+N), Al/(C+N)의 영향을 나타내는 그래프, 제2도는 열연소둔판의 신장 및 Cr의 영향을 나타내는 그래프.
제3A, B도는 열연소둔후의 압연방향의 금속조직을 나타내는 도면대용사진.
Claims (6)
- 필수합금원소로서Si : 0.4중량%-2중량% Cr : 6중량%∼17중량%P : 0.025중량%-0.10중량% Nb : 0.35중량%∼0.60중량%를 함유하고, 불순물 원소가 하기의 범위로 제한되어 있으며,C : 0.02중량% 이하 Mn : 0.8중량% 이하N : 0.015중량% 이하 Al : 0.02중량% 이하Ti : 0.02중량% 이하 Zr : 0.02중량% 이하또 성분의 중량%가 하기식 (1) 및 (2)를 만족하고, 식(1) Nb/(C+N)≥13 식(2) 11≤Cr+3Si+4Nb-50(C+N+P)-Mn-Ni-Co+Mo+Cu≤16.5 잔부는 Fe와 불가피적 불순물로 이루어지는 것을 특징으로 하는 자동차 배기재료용 열연페라이트강.
- 필수합금원소로서Si : 0.4중량%-2중량% Cr : 6중량%∼17중량%P : 0.025중량%-0.10중량% Nb : 0.35중량%∼0.60중량%를 함유하고, 불순물 원소가 하기의 범위로 제한되어 있으며,C : 0.02중량%이하 Mn : 0.8중량%이하N : 0.015중량%이하 Al : 0.02중량%이하Ti : 0.02중량%이하 Zr : 0.02중량%이하또한 최적합금원소로서Mo : 0.1중량%∼3.0중량% Cu : 0.1중량%∼1.0중량%의 1종 또는 2종을 함유하고, 또 성분의 중량%가 하기식 (1) 및 (2)를 만족하고,식(1) Nb/(C+N)≥13식(2) 11≤Cr+3Si+4Nb-50(C+N+P)-Mn-Ni-Co+Mo+Cu≤16.5잔부는 Fe와 불가피적 불순물로 이루어지는 것을 특징으로 하는 자동차 배기재료용 열연페라이트강.
- 필수합금원소로서Si : 0.4중량%-2중량% Cr : 6중량%∼17중량%P : 0.025중량%-0.10중량% Nb : 0.35중량%∼0.60중량%를 함유하고, 불순물 원소가 하기의 범위로 제한되어 있으며,C : 0.02중량%이하 Mn : 0.8중량%이하N : 0.015중량%이하 Al : 0.02중량%이하Ti : 0.02중량%이하 Zr : 0.02중량%이하또한 최적합금원소로서Ni : 1중량% 이하 Co : 0.5중량% 이하의 1종 또는 2종을 함유하고, 또 성분의 중량%가 하기식 (1) 및 (2)를 만족하고,식(1) Nb/(C+N)≥13식(2) 11≤Cr+3Si+4Nb-50(C+N+P)-Mn-Ni-Co+Mo+Cu≤16.5잔부는 Fe와 불가피적 불순물로 이루어지는 것을 특징으로 하는 자동차 배기재료용 열연페라이트강.
- 필수합금원소로서Si : 0.4중량%-2중량% Cr : 6중량%∼17중량%P : 0.025중량%-0.10중량% Nb : 0.35중량%∼0.60중량%를 함유하고, 불순물 원소가 하기의 범위로 제한되어 있으며,C : 0.02중량% 이하 Mn : 0.8중량% 이하N : 0.015중량% 이하 Al : 0.02중량% 이하Ti : 0.02중량% 이하 Zr : 0.02중량% 이하또한 최적합금원소로서Mo : 0.1중량%∼3.0중량% Cu : 0.1중량%∼1.0중량%의 1종 또는 2종 및,Ni : 1중량% 이하 Co : 0.5중량% 이하의 1종 또는 2종을 함유하고, 또 성분의 중량%가 하기식 (1) 및 (2)를 만족하고,식(1) Nb/(C+N)≥13식(2) 11≤Cr+3Si+4Nb-50(C+N+P)-Mn-Ni-Co+Mo+Cu≤16.5잔부는 Fe와 불가피적 불순물로 이루어지는 것을 특징으로 하는 자동차 배기재료용 열연페라이트강.
- 제1 내지 4항중 어느 한항에 있어서, 자동차의 배기 다기관용의 열연페라이트강.
- 제1 내지 4항중 어느 한항에 있어서, 자동차의 배기 파이프용의 열연페라이트강.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.