JPS6246323B2 - - Google Patents
Info
- Publication number
- JPS6246323B2 JPS6246323B2 JP5666679A JP5666679A JPS6246323B2 JP S6246323 B2 JPS6246323 B2 JP S6246323B2 JP 5666679 A JP5666679 A JP 5666679A JP 5666679 A JP5666679 A JP 5666679A JP S6246323 B2 JPS6246323 B2 JP S6246323B2
- Authority
- JP
- Japan
- Prior art keywords
- veneer
- paper
- wood
- resin paper
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
この発明は、化粧単板等のような集成材の製法
に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for manufacturing laminated wood such as decorative veneer.
化粧合板等に使用する突板としては、これまで
天然銘木単板が使用されていた。しかしながら、
天然銘木単板の原木は次第に減少しており、かつ
原木から美しい木目模様をもつ天然銘木単板を製
造する際の歩留りが極端に低いため、天然銘木単
板は極めて高価格になつていた。そこで、天然銘
木を用いないで、低価格のレジンペーパーを用い
て天然銘木単板の木目模様に近似した木目膜様を
もつ化粧単板を製造することが考えられた。その
ような化粧単板の製造方法はつぎのとおりであ
る。すなわち、晒、半晒または未晒のクラフト紙
等を染液等に浸漬して所定の色(目標とする天然
銘木単板の春材部または夏材部の色)に染色し、
これに合成樹脂液を含浸したのち乾燥することに
より、春材色染色レジンペーパーおよび夏材色染
色レジンペーパーをつくり、これらに接着剤を塗
布して春材色染色レジンペーパーと夏材色染色レ
ジンペーパーとを交互に積み重ね、これを一対の
型版で挾んで圧締してフリツチ化し、これをスラ
イスすることにより天然銘木単板調の化粧単板を
製造していた。ところが、このようにして化粧単
板を製造する場合には、染色レジンペーパーが薄
いため、これに例えばロールコータを用いて接着
剤を塗布する場合に、レジンペーパーがロールコ
ータに巻きついたりして接着剤の塗布が困難であ
り、したがつて化粧単板の製造が困難になつてい
た。また、染色レジンペーパーは薄いため、運搬
時等の際の取り扱いが困難であり、かつ自動化工
程に乗せにくいという欠点があつた。 Until now, natural precious wood veneers have been used as veneers for decorative plywood and the like. however,
The raw wood for natural precious wood veneer is gradually decreasing, and the yield when manufacturing natural precious wood veneer with a beautiful grain pattern from raw wood is extremely low, so the price of natural precious wood veneer has become extremely high. Therefore, we thought of producing a decorative veneer with a grain pattern similar to that of natural precious wood veneer using low-cost resin paper instead of using natural precious wood. The method for producing such a decorative veneer is as follows. That is, bleached, semi-bleached, or unbleached kraft paper, etc. is dipped in a dye solution and dyed to a predetermined color (the color of the target spring wood or summer wood of the natural precious wood veneer).
By impregnating this with synthetic resin liquid and drying it, spring wood color dyed resin paper and summer wood color dyed resin paper are made, and adhesive is applied to these to create spring wood color dyed resin paper and summer wood color dyed resin paper. By stacking paper and paper alternately, sandwiching and pressing them between a pair of molds to form fritches, and slicing them, decorative veneers that look like natural precious wood veneers were manufactured. However, when manufacturing decorative veneers in this way, the dyed resin paper is thin, so when applying adhesive to it using a roll coater, for example, the resin paper may wrap around the roll coater. It has been difficult to apply the adhesive, making it difficult to manufacture decorative veneers. In addition, because dyed resin paper is thin, it is difficult to handle during transportation, and it is also difficult to incorporate into automated processes.
この発明は、このような事情に鑑みなされたも
ので、薄いシート状材としてレジンペーパーと素
材単板を用いてなる積層体をフリツチ成形し、ス
ライスして集成材を製造する方法であつて、前記
シート状のレジンペーパーは、予め素材単板と貼
着させた貼着体の形で用いることにより、化粧単
板等のような集成材を製造することをその要旨と
するものである。 This invention was made in view of the above circumstances, and is a method for producing laminated wood by frit-forming a laminate made of resin paper and a veneer of material as a thin sheet-like material, and slicing it. The gist of the sheet-shaped resin paper is to use it in the form of a bonded body that is previously bonded to a raw material veneer to produce a laminated wood such as a decorative veneer.
つぎに、この発明を詳しく説明する。 Next, this invention will be explained in detail.
この発明は、レジンペーパーと素材単板との貼
着体を用いて化粧単板を製造するものである。 This invention is for manufacturing a decorative veneer using a bonded body of resin paper and material veneer.
レジンペーパーとしては、厚さ数十ミルスから
数ミルスの紙、特に合成樹脂液が浸透しやすいク
ラフト紙またはリンター紙に、ユリア、メラミ
ン、ユリア−メラミン、フエノール、ポリビニル
アルコール等の合成樹脂を水または有機溶媒に溶
解したワニスを、含浸、乾燥させたものが用いら
れる。ワニスは、固形分濃度が10〜80重量%(以
下「%」と略す)、好ましくは20〜60%のものを
用いることが好ましい。このレジンペーパーは、
通常、目標とする天然銘木の夏材部の色と同一の
色をもつように設定される。そのような色をもつ
ようにすれば、レジンペーパーの原料紙として
着色剤を含んでいたり、染液のような着色剤液で
着色されたものを用い、これにワニスを含浸させ
るか、ワニス中に着色剤を含ませておき、これ
を無着色の原料紙に含浸させることにより行われ
る。そして、レジンペーパーの含水率(含水率=
(含水重量−乾燥重量)/(乾燥重量)×100)は
40〜100%に設定されることが、後工程における
スリツチのスライス性のから好ましい。 Resin paper is made of paper with a thickness of several tens of mils to several mils, especially kraft paper or linter paper that is easily penetrated by synthetic resin liquid, and synthetic resin such as urea, melamine, urea-melamine, phenol, polyvinyl alcohol, etc. A varnish dissolved in an organic solvent is impregnated and dried. It is preferable to use a varnish having a solid content concentration of 10 to 80% by weight (hereinafter abbreviated as "%"), preferably 20 to 60%. This resin paper is
Usually, the color is set to be the same as the color of the summer wood of the target natural tree. If you want to have such a color, you can use paper that contains a colorant as the raw material for resin paper, or use paper that has been colored with a colorant liquid such as dye liquid, and then impregnate it with varnish, or add it to the varnish. This is done by impregnating uncolored raw paper with a coloring agent. And the moisture content of resin paper (moisture content =
(Water weight - dry weight) / (dry weight) x 100) is
It is preferable to set it to 40 to 100% from the viewpoint of slicing performance of the slit in the subsequent process.
上記のレジンペーパーと貼り合わせる素材単板
としては、通常、低価格の原木を切削した原木単
板またはこれを脱色した脱色単板もしくは原木単
板、脱色単板を着色した着色単板が用いられる。
また、これらの単板を複数枚貼り合わせた合板を
用いてもよい。このような素材単板は、通常、目
標とする天然銘木の春材部の色と同一の色をもつ
ように設定される。そして、その含水率はレジン
ペーパーと同様に40〜100%に設定することが好
ましいのである。 The material veneer to be laminated with the above resin paper is usually a raw wood veneer cut from low-priced raw wood, a bleached veneer or raw wood veneer, or a colored veneer made from a bleached veneer. .
Furthermore, plywood made by laminating a plurality of these veneers together may also be used. Such material veneer is usually set to have the same color as the spring wood portion of the targeted natural wood. The moisture content is preferably set at 40 to 100%, similar to resin paper.
レジンペーパーと素材単板との貼り合わせは、
接着剤を素材単板の表面に塗布したのち、その上
にレジンペーパーを重ねて加圧して行う。すなわ
ち、素材単板は、腰が強いため、接着剤を塗布す
る際にロールコータ等に巻きつくことがないので
ある。そして、素材単板の上にレジンペーパーを
重ねたのちに行う加圧は、常温下でプレスした
り、重ね合わせたものをシートでカバーして加熱
プレスしたり、熱蒸気雰囲気下で熱ロールで加圧
することにより行われる。このようにこの発明に
よれば、レジンペーパーと素材単板とを貼り合わ
せる場合において、素材単板にのみ接着剤を塗布
し、レジンペーパーには接着剤を塗布しないた
め、従来のような接着剤塗布の際の問題が生ずる
ことがないのである。このようにして第1図のよ
うにレジンペーパー1と素材単板2とを貼り合わ
せることにより、1組の夏材部(レジンペーパー
部)と春材部(素材単板部)とをもつ貼着体3が
得られる。なお、この場合、素材単板2に代えて
素材単板端切れ材2aを用い、これを第2図のよ
うにレジンペーパー1の上に横継ぎ状態で貼るよ
うにすると、端切れ材2aの有効利用を図ること
ができる。 Laminating resin paper and material veneer,
After applying adhesive to the surface of the veneer, resin paper is placed on top of it and pressure is applied. In other words, since the material veneer is strong, it does not get wrapped around a roll coater or the like when applying adhesive. After layering the resin paper on top of the material veneer, pressure can be applied at room temperature, covered with a sheet and heated, or heated with a hot roll in a hot steam atmosphere. This is done by applying pressure. According to the present invention, when bonding resin paper and a material veneer, adhesive is applied only to the material veneer and not to the resin paper. No problems arise during application. By laminating the resin paper 1 and the material veneer 2 together as shown in Fig. 1 in this way, a paste having one set of summer material part (resin paper part) and spring material part (material veneer part) is bonded together. A fitted body 3 is obtained. In this case, if a material veneer scrap material 2a is used instead of the raw material veneer 2 and it is pasted on the resin paper 1 in a horizontal splice state as shown in Fig. 2, the scrap material 2a can be used effectively. can be achieved.
このようにして得られた貼着体3を複数枚用
い、通常のように接着剤を介して積層し、一対の
型版で圧締してフリツチ化したのちスライスする
ことにより化粧単板(図示せず)が得られる。こ
の場合、各貼着体3を構成するレジンペーパー1
および素材単板2の含水率が40〜100%に設定さ
れていると、スライスを容易に行うことができる
のである。 Using a plurality of adhesive bodies 3 thus obtained, they are laminated with adhesive in the usual manner, pressed with a pair of templates to form fritches, and then sliced to create a decorative veneer (Fig. (not shown) is obtained. In this case, the resin paper 1 constituting each adhesive body 3
If the moisture content of the raw material veneer 2 is set to 40 to 100%, slicing can be easily performed.
なお、このスライスの際に、スライス厚さを薄
くすると、化粧合板に用いることができる天然銘
木単板調の化粧単板集成材が得られ、それを厚く
すると、木目模様をもつ板状体集成材が得られる
ようになるのである。また、貼着体3のみでフリ
ツチを構成せずに、貼着体3と通常の素材単板と
を用いてフリツチを構成し、これをスライスして
集成材を製造するようにしてもよいのである。 In addition, when slicing, if the slice thickness is reduced, a decorative veneer laminated wood with a natural precious wood veneer look that can be used for decorative plywood is obtained, and if it is thickened, a plate-like laminated wood with a wood grain pattern is obtained. This will make it possible to obtain materials. Furthermore, instead of constructing the frit only with the adhesive body 3, it is also possible to construct the frit using the adhesive body 3 and a normal material veneer, and then slice this to produce laminated wood. be.
以上のように、この発明は、シート状のレジン
ペーパーと素材単板とを貼着した腰の強い貼着体
を用いるため、これを積層接着する際の接着剤塗
布が容易になる。すなわち、これまでの、レジン
ペーパーを単独で用いたときのように、ロールコ
ータに巻きつくことがない。また、この貼着体は
かなり厚手であるため、運搬時の取り扱りが容易
であり、かつ自動化工程に乗せやすいのである。
また、貼着体の含水率を40〜100%に設定する
と、フリツチのスライスが極めて容易になるとと
もに、取り扱い時に割れの発生することが回避さ
れるという効果がある。 As described above, since the present invention uses a strong adhesive body in which a sheet-like resin paper and a veneer of material are adhered, it is easy to apply an adhesive when laminating and bonding these together. That is, unlike when resin paper is used alone, it does not wrap around the roll coater. Moreover, since this adhesive body is quite thick, it is easy to handle during transportation and easy to put into an automated process.
Further, setting the moisture content of the adhesive body to 40 to 100% has the effect that slicing of the fritches is extremely easy and the occurrence of cracks during handling is avoided.
つぎに、実施例について説明する。 Next, examples will be described.
実施例 1
複数枚のクラフト紙(厚さ254μ(10ミルス)、
山陽国策パルプ社製、HL−10)に、ユリア−メ
ラミン樹脂水性液(固形物25%)100重量部に塩
化アンモニウム硬化剤0.8重量部添加して水溶性
染料で着色したワニスを含浸させ、ついで130℃
で乾燥して含水率60%のレジンペーパーをつくつ
た。このものの樹脂含有量は43%であつた。Example 1 Multiple sheets of kraft paper (thickness 254μ (10 mils),
Sanyo Kokusaku Pulp Co., Ltd., HL-10) was impregnated with a varnish colored with a water-soluble dye by adding 0.8 parts by weight of an ammonium chloride curing agent to 100 parts by weight of an aqueous urea-melamine resin liquid (25% solids), and then 130℃
It was dried to create resin paper with a moisture content of 60%. The resin content of this product was 43%.
他方、寸法が1800×300×1mm、のラブラ染色
単板(ローズ色)を乾燥して含水率を70%に調節
した。 On the other hand, a labra-dyed veneer (rose color) with dimensions of 1800 x 300 x 1 mm was dried and the moisture content was adjusted to 70%.
つぎに、これらのラブラ染色単板上にそれぞれ
湿気硬化型1液タイプウレタン系接着剤を塗布し
たのち、前記のレジンペーパーを重ね、常温でプ
レスして貼着体をつくつた。このようにして合計
300枚の貼着体をつくり、それぞれ上記のウレタ
ン系接着剤を塗布してレジンペーパー側が同じ方
向を向くようにして重ねた。つぎに、これを押圧
面に凹凸をもつ一対の型版で挾んで圧締すること
によりフリツチをつくり、これをスライスして化
粧単板を製造した。この場合、貼着体は腰が強く
厚手であるため、接着剤塗布およびその取り扱い
が容易であつた。また、貼着体の含水率が適正に
設定されているため、スライスの際に目ぼれ、割
れ等が生じなかつた。そして、得られた化粧単板
は、表面が平滑で、夏材部の幅が広く、天然調の
ものであつた。 Next, a moisture-curable one-component urethane adhesive was applied to each of these Labra-dyed veneers, and then the resin paper described above was layered and pressed at room temperature to produce a bonded body. In this way the total
300 adhesive sheets were made, each coated with the above urethane adhesive and stacked with the resin paper facing in the same direction. Next, this was sandwiched and pressed between a pair of templates with uneven pressing surfaces to create fritches, and this was sliced to produce decorative veneers. In this case, since the adhesive body was strong and thick, it was easy to apply the adhesive and handle it. Furthermore, since the moisture content of the adhesive body was set appropriately, no blemishes or cracks occurred during slicing. The obtained decorative veneer had a smooth surface, a wide summer wood part, and a natural appearance.
実施例 2
寸法が1800×100×1mmおよび1800×50×1mm
のラブラ染色単板端切れ材を用い、これを、実施
例1と同様にしてつくつたレジンペーパーに貼り
合わせて定尺(1800×300)の貼着体をつくつ
た。また、実施例1と同様に、寸法が1800×300
×1mmのラブラ染色単板を用い、これを、実施例
1と同様にしてつくつたレジンペーパーに貼り合
わせて定尺の貼着体をつくつた。このようにして
得られた2種類の貼着体を用い、実施例1と同様
にして化粧単板を製造した。得られた化粧単板
は、ラブラ染色単板端切れ材の横継ぎ部も目立た
なく、優れたものであり、かつ端切れ材を用いた
ため安価であつた。Example 2 Dimensions are 1800 x 100 x 1 mm and 1800 x 50 x 1 mm
Using scraps of Labra-dyed veneer, this was pasted onto resin paper made in the same manner as in Example 1 to make a fixed-sized (1800 x 300) adhered body. Also, as in Example 1, the dimensions are 1800 x 300
A 1 mm Labra dyed veneer was used and bonded to a resin paper made in the same manner as in Example 1 to make a regular-sized adhesive. Decorative veneers were manufactured in the same manner as in Example 1 using the two types of adhesive bodies thus obtained. The obtained decorative veneer was superior in that the horizontal joints of the Labra-dyed veneer scraps were not noticeable, and it was inexpensive because scraps were used.
第1図および第2図は、それぞれこの発明で用
いる貼着体の製造説明図である。
1……レジンペーパー、2……素材単板。
FIG. 1 and FIG. 2 are explanatory diagrams for manufacturing the adhesive body used in the present invention, respectively. 1...Resin paper, 2...Material veneer.
Claims (1)
単板を用いてなる積層体をフリツチ成形し、スラ
イスして集成材を製造する方法であつて、前記シ
ート状のレジンペーパーは、予め素材単板と貼着
させた貼着体の形で用いることを特徴とする集成
材の製法。1. A method of manufacturing laminated wood by frit-forming and slicing a laminate made of resin paper and a material veneer as a thin sheet-like material, wherein the sheet-like resin paper is bonded to the material veneer in advance. A method for producing laminated wood, characterized in that it is used in the form of a bonded body.