JPS61183163A - アルミナ磁器組成物 - Google Patents
アルミナ磁器組成物Info
- Publication number
- JPS61183163A JPS61183163A JP60023792A JP2379285A JPS61183163A JP S61183163 A JPS61183163 A JP S61183163A JP 60023792 A JP60023792 A JP 60023792A JP 2379285 A JP2379285 A JP 2379285A JP S61183163 A JPS61183163 A JP S61183163A
- Authority
- JP
- Japan
- Prior art keywords
- alumina
- ceramic composition
- alumina ceramic
- weight
- mgo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
「産業上の利用分野」
本発明は、マイクロ波導波体、マイクロ波透過窓、マイ
クロ波集積回路基板等の電波媒体として高周波誘電損失
の小さい材料が要求される分野で好適に利用される。
クロ波集積回路基板等の電波媒体として高周波誘電損失
の小さい材料が要求される分野で好適に利用される。
「従来の技術」
高純度アルミナ磁器は耐熱性、耐化学的抵抗性、機械的
強度などにおいて優れ、高周波誘電損失が小さいことか
ら、広範囲で汎用されているが、焼結助剤等の添加物の
種類や量の微妙な変化によりその緒特性、就中電気的特
性が大きく変わるため、上記分野で利用される高周波誘
電材料としての実用に適さなかった。発明者等はアルミ
ナ磁器をこの種高周波誘電材料に利用するために添加物
を種々検討し、先に主成分アルミナにＣａＯ及びＴ １
（ｈを所、定量添加してなるアルミナ磁器組成物並び
に主成分アルミナにＭｇＯ及び＄１０２を所定量添加し
てなるアルミナ磁器組成物をそれぞれ特願昭５９−８２
１１８号並びに特願昭５８−１２５１８６号において提
案した。
強度などにおいて優れ、高周波誘電損失が小さいことか
ら、広範囲で汎用されているが、焼結助剤等の添加物の
種類や量の微妙な変化によりその緒特性、就中電気的特
性が大きく変わるため、上記分野で利用される高周波誘
電材料としての実用に適さなかった。発明者等はアルミ
ナ磁器をこの種高周波誘電材料に利用するために添加物
を種々検討し、先に主成分アルミナにＣａＯ及びＴ １
（ｈを所、定量添加してなるアルミナ磁器組成物並び
に主成分アルミナにＭｇＯ及び＄１０２を所定量添加し
てなるアルミナ磁器組成物をそれぞれ特願昭５９−８２
１１８号並びに特願昭５８−１２５１８６号において提
案した。
「発明が解決しようとする問題点」
近年、マイクロ波集積回路基板の電極ないし導体回路は
研磨された基板表面に薄膜で細線化されて形成される傾
向にあるため、断線不良を未然に防止するには気孔径の
小さい緻密な材料が必要となるが、上記特願昭５９−８
２１１８号発明及び特願昭５８−１２５１８６号発明は
緻本発明目的とせず、その他にも高周波誘電材料として
好適な緻密質アルミナ磁器は知られていない。
研磨された基板表面に薄膜で細線化されて形成される傾
向にあるため、断線不良を未然に防止するには気孔径の
小さい緻密な材料が必要となるが、上記特願昭５９−８
２１１８号発明及び特願昭５８−１２５１８６号発明は
緻本発明目的とせず、その他にも高周波誘電材料として
好適な緻密質アルミナ磁器は知られていない。
本発明は特願昭５９−８２１１．１号発明及び特願昭５
８−１２５１８６号発明よシ本発明波誘電損失が小さく
、緻密なアルミナ磁器組成物を提供することを目的とす
る。
８−１２５１８６号発明よシ本発明波誘電損失が小さく
、緻密なアルミナ磁器組成物を提供することを目的とす
る。
「問題点を解決するための手段」
重量基準でＡｌ２Ｏ３９９，４〜９９．９ ％と残部５
ｉ（ｈ。
ｉ（ｈ。
ＣａＯ及びＭｇＯとからなシ、５ｉＯｚ ＋ ＣａＯ及
びＭｇＯが別紙組成図の ５ｉＣｈ ＣａＯＭｇＯ 点Ａ ０．９００，０２５０，０７５点Ｂ ０
．６００．３００．１０ 点Ｃ０．６００，１２５０，２７５ 〔単位二重量分率〕 で囲まれる領域内の比率で含有することを特徴とするア
ルミナ磁器組成物である。
びＭｇＯが別紙組成図の ５ｉＣｈ ＣａＯＭｇＯ 点Ａ ０．９００，０２５０，０７５点Ｂ ０
．６００．３００．１０ 点Ｃ０．６００，１２５０，２７５ 〔単位二重量分率〕 で囲まれる領域内の比率で含有することを特徴とするア
ルミナ磁器組成物である。
「作用」
上記組成によシ
（イ）誘電率（以下「ε」と記載する）が１０以下、
（ロ）誘電体力率（以下ｒ ｔａｎＪ ｊと記載する）
が６×１０以下、 （ハ）鏡面仕上面の平均気孔径が２０〔μｍ〕以下とな
る。
が６×１０以下、 （ハ）鏡面仕上面の平均気孔径が２０〔μｍ〕以下とな
る。
実施例
アルミナ（昭和軽金属製ＵＡ−５０５５．純度９９．９
９９％ ） ５００Ｆと、無水ケイ酸（試薬特級）、炭
酸カルシウム（試薬特級）及び炭歳マグネシウム（試薬
特級）を酸化物換算で第１表に示す含有比率で１９種類
秤量した添加成分とをアルミナ含有率が鹸化物換算で第
２表、第８表、第４表、第５表又は第６表にそれぞれ示
すように９９．８重量％、９９．４重量％、９９．７重
量％、９９．９重量％又は９９．９５重量％となるよう
に配合し、配合物と脱イオン水４００ｍｆｌ 、ポリビ
ニルアルコール５ｆ及びポリエチレングリコール２ｆと
を内容積１Ωのポリエチレン容器へ入れ、純度９９．９
９重量％のアルミナ原石（２０ｍφ）２麺を用いて湿式
混合し凍結乾燥し、篩に通し、圧力１５００ ｂ／−で
金型プレスし、第２表〜第６表に示す焼成温度で焼成し
た後、両端面０．１ｓ、側面０．８ｓに研磨加工するこ
とＫよって供試片２０１〜６１９を製造した。供試片２
０１〜６１９について次の条件でε＋ ｔａｎＪ及び平
均気孔径を測定した結果を第２〜第６表に示す。
９９％ ） ５００Ｆと、無水ケイ酸（試薬特級）、炭
酸カルシウム（試薬特級）及び炭歳マグネシウム（試薬
特級）を酸化物換算で第１表に示す含有比率で１９種類
秤量した添加成分とをアルミナ含有率が鹸化物換算で第
２表、第８表、第４表、第５表又は第６表にそれぞれ示
すように９９．８重量％、９９．４重量％、９９．７重
量％、９９．９重量％又は９９．９５重量％となるよう
に配合し、配合物と脱イオン水４００ｍｆｌ 、ポリビ
ニルアルコール５ｆ及びポリエチレングリコール２ｆと
を内容積１Ωのポリエチレン容器へ入れ、純度９９．９
９重量％のアルミナ原石（２０ｍφ）２麺を用いて湿式
混合し凍結乾燥し、篩に通し、圧力１５００ ｂ／−で
金型プレスし、第２表〜第６表に示す焼成温度で焼成し
た後、両端面０．１ｓ、側面０．８ｓに研磨加工するこ
とＫよって供試片２０１〜６１９を製造した。供試片２
０１〜６１９について次の条件でε＋ ｔａｎＪ及び平
均気孔径を測定した結果を第２〜第６表に示す。
「測定条件」
１、ε及びｔａｎＪの場合
装置・方法：横河ヒューレットバッカード製モデル８４
０８Ｂ 誘電体円柱共振法 周 波 数：８ＧＨｚ 温 度： ２０℃ ２、平均気孔径の場合 供試片の鏡面を２００倍で写真撮影し、写真中５０■Ｘ
５０ｍ５＋視野内の５〔μｍ３以上の気孔の平均を算出
した。
０８Ｂ 誘電体円柱共振法 周 波 数：８ＧＨｚ 温 度： ２０℃ ２、平均気孔径の場合 供試片の鏡面を２００倍で写真撮影し、写真中５０■Ｘ
５０ｍ５＋視野内の５〔μｍ３以上の気孔の平均を算出
した。
第 １ 表
第１表〜第６表かられかるように本発明範囲内の供試片
はε≦１０、ｔａｎδ≦６×１０且つ平均気孔径≦２０
（μｍ〕となりていたが、本発明範囲外の供試片はε、
ｔａｎδ及び平均気孔径のうち少なくとも一つが所望値
を超えていた。
はε≦１０、ｔａｎδ≦６×１０且つ平均気孔径≦２０
（μｍ〕となりていたが、本発明範囲外の供試片はε、
ｔａｎδ及び平均気孔径のうち少なくとも一つが所望値
を超えていた。
「発明の効果」
高周波誘電損失が小さい。また、マイクロ波集積回路基
板に利用される場合、配線パターンの断線不良が未然に
防止される。
板に利用される場合、配線パターンの断線不良が未然に
防止される。
図面は５ｔ０２− ＣａＯＭｇＯ三成分系組成図である
。
。
Claims (1)
- 【特許請求の範囲】 重量基準でＡｌ＿２Ｏ＿３９９．４〜９９．９％と残部
ＳｉＯ＿２、ＣａＯ及びＭｇＯとからなり、ＳｉＯ＿２
、ＣａＯ及びＭｇＯが別紙組成図の ＳｉＯ＿２ ＣａＯ ＭｇＯ 点Ａ ０．９０ ０．０２５ ０．０７５ 点Ｂ ０．６０ ０．３０ ０．１０ 点Ｃ ０．６０ ０．１２５ ０．２７５ 〔単位：重量分率〕 で囲まれる領域内の比率で含有することを特徴とするア
ルミナ磁器組成物。