JPS59162087A - Thermal recording type releasable paper - Google Patents
Thermal recording type releasable paperInfo
- Publication number
- JPS59162087A JPS59162087A JP58037098A JP3709883A JPS59162087A JP S59162087 A JPS59162087 A JP S59162087A JP 58037098 A JP58037098 A JP 58037098A JP 3709883 A JP3709883 A JP 3709883A JP S59162087 A JPS59162087 A JP S59162087A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive layer
- base
- pressure
- sensitive adhesive
- sensitive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔技術分野〕
本発明はロイコ染料と顕色剤との間の発色反応を利用し
た感熱記録型剥離紙に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Technical Field] The present invention relates to a heat-sensitive recording type release paper that utilizes a color-forming reaction between a leuco dye and a color developer.
従来、シート状支持体の表面にロイコ染料と加熱により
該ロイコ染料を発色させる顕色剤を主成分として含有す
る感熱記録紙は知られており、この感熱記録紙を感熱記
録型の包装ラベルとして利用することが提案されている
。このような感熱記録型のラベルの場合、その印字方式
はサーマルヘッドによるものであるため、従来のインク
又はインクリボンによる印字方式のものに比して、簡単
かつ美麗に行い得るという利点を備えている。しかしな
がら、感熱記録紙の場合、その感熱発色層に、ジオクチ
ルフタレート（ＤＯＰ）やジオクチルアジペート（ＤＯ
Ａ）のようなプラスチックフィルムに適用されている可
塑剤や食用油等が浸透すると、印字部（発色部）が消色
するという問題があり、プラスチックフィルム包装品に
対するラベルとしては適用することができない。例えば
、スーパーなどの量販店においては、生鮮食品を販売す
るために、発泡スチロールのようなプラスチックトレー
に、魚、野菜、肉などを入れ、その全体をポリ塩化ビニ
ルなどのプラスチックフィルムによりオーバラップし、
更にそのラップ上に計量値の印字されてラベルを貼布す
ることが行われているが、この場合、ラベルとして従来
の感熱紙を用いると、包装品を積重ねたりなどして、ラ
ベルとラップフィルムとを密着させた時に、ラップフィ
ルム中の可塑剤がラベル表面の感熱発色層中に浸透し、
ある時間経過した後にはそのラベル表面の印字が消色し
、商品の販売に大きな支障をきたしてしまう。Conventionally, thermal recording paper has been known which contains a leuco dye and a color developer that develops color from the leuco dye when heated on the surface of a sheet-like support as a main component, and this thermal recording paper has been used as a thermal recording type packaging label. It is proposed to use. In the case of such heat-sensitive recording type labels, since the printing method is based on a thermal head, it has the advantage of being easier and more beautiful than conventional printing methods using ink or ink ribbon. There is. However, in the case of heat-sensitive recording paper, the heat-sensitive coloring layer contains dioctyl phthalate (DOP) and dioctyl adipate (DO).
If the plasticizers, edible oils, etc. applied to plastic films like A) penetrate, there is a problem that the printed part (colored part) will fade, so it cannot be used as a label for plastic film packaged products. . For example, in mass retailers such as supermarkets, in order to sell fresh foods, fish, vegetables, meat, etc. are placed in plastic trays such as Styrofoam, and the entire tray is covered with plastic film such as polyvinyl chloride.
In addition, a label is attached with the weight value printed on the wrap, but in this case, if conventional thermal paper is used as the label, the label and wrap film may be separated by stacking the packaged items. When the wrap film is brought into close contact with the label, the plasticizer in the wrap film penetrates into the heat-sensitive coloring layer on the label surface.
After a certain period of time, the printing on the surface of the label fades, causing a major hindrance to product sales.
このような剥離紙用の感熱記録材料としては、支持体上
にロイコ染料からなる発色剤と、該ロイコ染料を加熱時
発色させる顕色剤１例えば、有機酸やフェノール性化合
物等を含有する感熱発色層を設けると共に、該感熱発色
層の上面に保護層（水溶性高分子層、以下オーバコート
層ともいう）を設けたものが知られている。しかしなが
ら、プラスチックフィルムにラベルを長期間貼布してい
ると、ラベルの裏面より油や可塑剤が浸透し、消色現象
が表われサーマルヘッドとしては不充分であった。Such a heat-sensitive recording material for release paper includes a coloring agent made of a leuco dye on a support, and a color developer 1 that causes the leuco dye to develop color when heated, such as a heat-sensitive material containing an organic acid or a phenolic compound. It is known that in addition to providing a coloring layer, a protective layer (water-soluble polymer layer, hereinafter also referred to as an overcoat layer) is provided on the upper surface of the thermosensitive coloring layer. However, when a label is attached to a plastic film for a long period of time, oil and plasticizer permeate from the back side of the label, resulting in a decoloring phenomenon, making the label unsatisfactory as a thermal head.
一方、このような裏面からの油や可塑剤等の浸透による
影響を防止するために、支持体の裏面に水溶性高分子の
バックコート層を設けることが提案されているが、この
場合には、製品の生産性が低下する上に、バンクコート
層を設ける際の乾燥工程の採用により、地肌カブリの問
題が生じるという難点がある。On the other hand, in order to prevent the influence of penetration of oil, plasticizer, etc. from the back surface, it has been proposed to provide a back coat layer of water-soluble polymer on the back surface of the support. However, there are disadvantages in that not only the productivity of the product is reduced, but also the problem of background fogging occurs due to the use of a drying process when providing the bank coat layer.
本発明は、前記のような従来技術に見られる欠点を克服
し、特別のバックコート層を設けることなく、裏面から
浸透する油や可塑剤の影響を防止した感熱記録型剥離紙
を提供することを目的とする。The present invention overcomes the drawbacks seen in the prior art as described above, and provides a heat-sensitive recording type release paper that prevents the influence of oil and plasticizer penetrating from the back side without providing a special back coat layer. With the goal.
本発明によれば、支持体の表面にロイコ染料と顕色剤と
を含有する感熱発色層を設け、支持体の裏面に接着剤層
を介して剥離台紙を設けたものにおいて、該接着剤層と
して、カルボキシル基変性ポリビニルアルコールを添加
した水性アクリルエマルジョンから形成された感圧接着
剤層を用いることを特徴とする感熱記録型剥離紙が提供
される。According to the present invention, a heat-sensitive color forming layer containing a leuco dye and a color developer is provided on the surface of a support, and a release mount is provided on the back surface of the support with an adhesive layer interposed therebetween, in which the adhesive layer Accordingly, there is provided a heat-sensitive recording type release paper characterized by using a pressure-sensitive adhesive layer formed from an aqueous acrylic emulsion to which carboxyl group-modified polyvinyl alcohol is added.
本発明においては、支持体の裏面に剥離台紙と共に設け
る感圧接着剤層として、水性アクリルエマルジョンにカ
ルボキシル基変性ポリビニルアルコールを添加したもの
から形成された感圧接着剤層を用いる。感圧接着剤とし
て、水性アクリルエマルジョンを用いることは知られて
いるが、このものから形成された感圧接着剤層は、可塑
剤や油−３＝
等の浸透に対する遮断性が悪く、剥離紙をこの接着剤層
を介してラップフィルム等に貼布した場合。In the present invention, a pressure-sensitive adhesive layer formed from an aqueous acrylic emulsion to which carboxyl group-modified polyvinyl alcohol is added is used as the pressure-sensitive adhesive layer provided on the back surface of the support together with a release mount. It is known to use a water-based acrylic emulsion as a pressure-sensitive adhesive, but the pressure-sensitive adhesive layer formed from this has poor barrier properties against the penetration of plasticizers, oil, etc., and release paper When applied to a wrap film, etc. via this adhesive layer.
ラツプフイムに含まれる可塑剤がその接着剤を透過し、
さらに表面の感熱発色層まで浸透するため、感熱発色部
を消色させる。これに対し、本発明により、カルボキシ
ル基変性ポリビニルアルコールを添加した水性アクリル
エマルジョンから形成された接着剤層は、可塑剤や油等
の浸透に対する遮断性がよく、前記のような感熱発色部
の消色の問題を生じない。The plasticizer contained in Lapfim permeates through the adhesive,
Furthermore, since it penetrates into the heat-sensitive color forming layer on the surface, the heat-sensitive color forming area is decolored. In contrast, according to the present invention, an adhesive layer formed from an aqueous acrylic emulsion to which carboxyl group-modified polyvinyl alcohol has been added has good barrier properties against penetration of plasticizers, oils, etc. Does not cause color problems.
本発明で用いる水性アクリルエマルジョンとしては、例
えば、メタクリル酸メチル、メタクリル酸エチル、メタ
クリル酸ブチル、アクリル酸メチル、アクリル酸エチル
、アクリル酸２−エチルヘキシル、グリシジルメタクリ
レート、アクリル酸ヒドロキシプロピル等の単量体を主
成分として用いて形成したアクリル系重合体を含む水性
エマルジョンが用いられ、市販のもの、例えば、東洋イ
ンキ社製のＢ Ｐ Ｗ４７９２、Ｂ Ｐ Ｗ４６５５
（商品名）や、カネボウＮＳＣ社製のＡＱ−２１、ＡＱ
−３（商品名）、三井東圧社製のＸ −５０４５（商品
名）、昭和４−
高分子社製のＴ−５０ＯＡ （商品名）等が採用される
。また、カルボキシル基変性ポリビニルアルコールとは
、ポリビニルアルコールと、フマール酸、無水フタル酸
、無水トリメリット酸、無水イタコン酸等のカルボン酸
との反応物或いはこれらの反応物をエステル化したもの
、或いは酢酸ビニルと少量のマレイン酸、フマル酸、イ
タコン酸等のエチレン性不飽和カルボン酸との重合物を
ケン化したもの等が用いられる。このようなカルボキシ
ル基変性ポリビニルアルコールの製造法については特公
昭４５−２１３１２号、特開昭５３−９１９９５号、同
５４−２８３８９号並びに同５４−２８３９０号の各公
報に開示されている。Examples of the aqueous acrylic emulsion used in the present invention include monomers such as methyl methacrylate, ethyl methacrylate, butyl methacrylate, methyl acrylate, ethyl acrylate, 2-ethylhexyl acrylate, glycidyl methacrylate, and hydroxypropyl acrylate. An aqueous emulsion containing an acrylic polymer formed using as a main component is used, and commercially available emulsions such as B P W4792 and B P W4655 manufactured by Toyo Ink Co., Ltd.
(product name), AQ-21 manufactured by Kanebo NSC, AQ
-3 (trade name), X-5045 (trade name) made by Mitsui Toatsu Co., Ltd., and T-50OA (trade name) made by Koubunshi Co., Ltd. in 1920, etc. are adopted. Furthermore, carboxyl group-modified polyvinyl alcohol is a reaction product of polyvinyl alcohol and a carboxylic acid such as fumaric acid, phthalic anhydride, trimellitic anhydride, itaconic anhydride, or an esterified product of these reaction products, or acetic acid. A saponified polymer of vinyl and a small amount of ethylenically unsaturated carboxylic acid such as maleic acid, fumaric acid, and itaconic acid is used. Methods for producing such carboxyl group-modified polyvinyl alcohol are disclosed in Japanese Patent Publication Nos. 45-21312, 91995-1983, 28389-1989, and 28390-1989.
水性アクリルエマルジョンに対するカルボキシル基変性
ポリビニルアルコールの添加量は、固形分換算で、水性
アクリルエマルジョン１重量部に対し、０．０２〜０．
０５重量部の割合で充分である。The amount of carboxyl group-modified polyvinyl alcohol added to the aqueous acrylic emulsion is 0.02 to 0.02 to 1 part by weight of the aqueous acrylic emulsion in terms of solid content.
A proportion of 0.05 parts by weight is sufficient.
なお、本発明における感熱記録型剥離紙とは、その紙表
面に対する印字や画像の記録を加熱方式により行うこと
のでき、かつその裏面に貼着された剥離台紙を剥離する
ことにより、固体表面に対して接着することのできるシ
ー１−を意味し、番号札、値札、薬ビン札などの各種ラ
ベルやレッテルの他、ネームプレー１へ、シールなどが
包含される。Note that the heat-sensitive recording type release paper in the present invention is capable of printing or recording images on the surface of the paper using a heating method, and by peeling off the release mount attached to the back side, it can be printed on the solid surface. It refers to a label that can be adhered to a label, and includes various labels and labels such as number tags, price tags, and medicine bottle tags, as well as name plates and stickers.
本発明で用いるロイコ染料としては慣用のトリフェニル
メタン系、フルオラン系、フェノチアジン系、オーラミ
ン系、スピロピラン系のものが好ましく適用され、例え
ば、３−（Ｎ−（ｐ−トリルアミノ））−７−アニリノ
フルオラン、３−（Ｎ−（ｐ−１−リル）−Ｎ−メチル
アミノ）−７−アニリノフルオラン、３−（Ｎ−（ｐ−
トリル） −Ｎ−エチルアミノ）−７−アニリノフルオ
ラン、３−（Ｎ−（ｐ−トリル）−Ｎ−プロピルアミノ
）−７−アニリノフルオラン、３−（Ｎ−（ｐ−１〜リ
ル）−Ｎ−ブチルアミノ）−７−アニリノフルオラン、
３−ジメチルアミノ−６−メチル−７−アニリノフルオ
ラン、３−ジエチルアミノ−６−メチル−７−アニリノ
フルオラン、３−ジプロピルアミノ−６−メチル−７−
アニリノフルオラン、３−ジブチルアミノ−６−メチル
−７−アニリノフルオラン、３−ピロリジノ−６−メチ
ル−７一アニリノフルオラン、３−ピペリジノ−６−メ
チル−７−アニリノフルオラン、３−ピペラジノ−６−
メチル−７−アニリノフルオラン、３−Ｎ−（Ｎ’−メ
チルピペラジノ）−６−メチル−７−アニリノフルオラ
ン、３−モルホリノ−６−メチル−７−アニリノフルオ
ラン、３−ジベンジルアミノ−６−メチル−７−アニリ
ノフルオランなどが挙げられる。As the leuco dye used in the present invention, commonly used triphenylmethane-based, fluoran-based, phenothiazine-based, auramine-based, and spiropyran-based leuco dyes are preferably used, such as 3-(N-(p-tolylamino))-7-aniline dyes. Linofluorane, 3-(N-(p-1-lyl)-N-methylamino)-7-anilinofluorane, 3-(N-(p-
tolyl) -N-ethylamino)-7-anilinofluorane, 3-(N-(p-tolyl)-N-propylamino)-7-anilinofluorane, 3-(N-(p-1~ lyl)-N-butylamino)-7-anilinofluorane,
3-dimethylamino-6-methyl-7-anilinofluorane, 3-diethylamino-6-methyl-7-anilinofluorane, 3-dipropylamino-6-methyl-7-
Anilinofluorane, 3-dibutylamino-6-methyl-7-anilinofluorane, 3-pyrrolidino-6-methyl-7-anilinofluorane, 3-piperidino-6-methyl-7-anilinofluorane , 3-piperazino-6-
Methyl-7-anilinofluorane, 3-N-(N'-methylpiperazino)-6-methyl-7-anilinofluorane, 3-morpholino-6-methyl-7-anilinofluorane, 3-dibenzyl Examples include amino-6-methyl-7-anilinofluorane.
前記ロイコ染料に対する顕色剤としては、従来一般に用
いられているフェノール性物質、有機酸、無機酸又はそ
れらの塩、活性白土等の種々の電子受容性物質が適用さ
れるが、その具体例を示すと以下の通りである。As the developer for the leuco dye, various electron-accepting substances such as phenolic substances, organic acids, inorganic acids or their salts, and activated clay, which have been commonly used in the past, can be used. It is shown below.
フェノール性物質：
３．５−キシレノール、チモール、ｐ −ｔｅｒｔ−ブ
チルフェノール、４−ヒドロキシフェノキシド、メチル
−４−ヒドロキシベンゾエート、４−ヒドロキシアセト
フェノン、α−ナフトール、β−ナフトール、カテコー
ル、レゾルシン、ヒドロキノン、４−ｔｅｒｔ−オクチ
ルカテコール、４．４−ｓｅｅ−ブチリデンフェノール
、２，２′ −ジヒドロキシジフェニル、２，２−メチ
レンビス（４−メチル−６ｔｅｒｔ −ブチルフェノー
ル、２，２−ビス（４−ヒドロキシフェニル）プロパン
、４．４−ｓｅｅ−プチリデンジフエ７−
ノール、ピロガロール、フロログルシン、フロログルシ
ンカルボン酸、４−ｔｅｒｔ−オクチルフェノール、４
−フェニルフェノール、２，２−ビス（Ｐ−ヒドロキシ
フェニル）ブタン、４，４′ −シクロへキシリデンジ
フェノール、２，２−ビス（２，５−ジブロム−４−ヒ
ドロキシフェニル）プロパン、４，４′ −イソプロピ
リデンビス（２−ｔｅｒｔ−ブチルフェノール） 、２
．２’ −メチレンビス（４−クロロフェノール）等。Phenolic substances: 3.5-xylenol, thymol, p-tert-butylphenol, 4-hydroxyphenoxide, methyl-4-hydroxybenzoate, 4-hydroxyacetophenone, α-naphthol, β-naphthol, catechol, resorcinol, hydroquinone, 4 -tert-octylcatechol, 4,4-see-butylidenephenol, 2,2'-dihydroxydiphenyl, 2,2-methylenebis(4-methyl-6tert-butylphenol), 2,2-bis(4-hydroxyphenyl)propane , 4.4-see-butylidenediphen7-nol, pyrogallol, phloroglucin, phloroglucin carboxylic acid, 4-tert-octylphenol, 4
-phenylphenol, 2,2-bis(P-hydroxyphenyl)butane, 4,4'-cyclohexylidene diphenol, 2,2-bis(2,5-dibromo-4-hydroxyphenyl)propane, 4,4 '-isopropylidene bis(2-tert-butylphenol), 2
．． 2'-methylenebis(4-chlorophenol), etc.
酸性物質又はその塩：
安息香酸、没食子酸、サリチル酸、サリチル酸亜鉛、１
−ヒドロキシ−２−ナフトエ酸、０−ヒドロキシ安息香
酸、ｍ−ヒドロキシ安息香酸、Ｐ−ヒドロキシ安息香酸
ベンジル、２−ヒドロキシ−Ｐ−トルイル酸、酒石酸、
シュウ酸、マレイン酸、クエン酸、コハク酸、ステアリ
ン酸、４−オキシシフタル酸、ホウ酸等。Acidic substances or their salts: benzoic acid, gallic acid, salicylic acid, zinc salicylate, 1
-Hydroxy-2-naphthoic acid, 0-hydroxybenzoic acid, m-hydroxybenzoic acid, benzyl P-hydroxybenzoate, 2-hydroxy-P-toluic acid, tartaric acid,
Oxalic acid, maleic acid, citric acid, succinic acid, stearic acid, 4-oxycyphthalic acid, boric acid, etc.
これらの顕色剤は染料１重量部に対し１〜５重量部の割
合で用いるのが好ましい。These color developers are preferably used in an amount of 1 to 5 parts by weight per 1 part by weight of the dye.
感熱発色層を形成するにはこれらロイコ染料、顕色剤の
他に結着剤が用いられる。結着剤には広８−
く公知のものが使用できるが具体的には、ポリビニルア
ルコール
シセルロース、カルボキシメチルセルロース、カルボキ
シエチルセルロース、ポリビニルピロリドン、ポリアク
リルアミド、澱粉、ゼラチンなどが挙げられる。In addition to these leuco dyes and color developers, a binder is used to form the thermosensitive coloring layer. A wide variety of known binders can be used, and specific examples include polyvinyl alcohol cellulose, carboxymethyl cellulose, carboxyethyl cellulose, polyvinyl pyrrolidone, polyacrylamide, starch, and gelatin.
なお、これら水溶性結着剤との併用で、例えば、スチレ
ン−ブタジェン共重合体、塩化ビニル−酢酸ビニル共重
合体、ポリ酢酸ビニル、ポリアクリル酸エステル、ポリ
ブチルメタクリレートのようなポリメタクリル酸エステ
ルなどのラテックス類も使用できる。In addition, in combination with these water-soluble binders, for example, styrene-butadiene copolymer, vinyl chloride-vinyl acetate copolymer, polyvinyl acetate, polyacrylic ester, polymethacrylic ester such as polybutyl methacrylate. Latex such as can also be used.
更に、感熱発色層中には助剤として（増感剤、ヘッドマ
ツチング改良）セラックロウ、モンタンワックス、カル
ナバロウ等のワックス類、シリカ、タルク、炭酸カルシ
ウム、尿素ホルマリン樹脂等を添加してもよい。Furthermore, waxes such as shellac wax, montan wax, carnauba wax, silica, talc, calcium carbonate, urea-formalin resin, etc. may be added as auxiliary agents (sensitizer, head matching improvement) to the heat-sensitive coloring layer.
本発明においては、必要に応じ、水溶性高分子を含むオ
ーバコート層を感熱発色層の上に設けることができるが
、この場合に使用される水溶性高分子としては、例えば
、ポリビニルアルコール、ヒドロキシエチルセルロース
、メチルセルロース、カルボキシメチルセルロース、デ
ンプン及びその誘導体、カゼイン、アルギン酸ソーダ、
ポリビニルピロリドン、ポリアクリルアマイド、スチレ
ン−マレイン酸共重合体などが挙げられる。In the present invention, an overcoat layer containing a water-soluble polymer can be provided on the heat-sensitive coloring layer if necessary. Examples of the water-soluble polymer used in this case include polyvinyl alcohol, hydroxyl Ethylcellulose, methylcellulose, carboxymethylcellulose, starch and its derivatives, casein, sodium alginate,
Examples include polyvinylpyrrolidone, polyacrylamide, and styrene-maleic acid copolymer.
この水溶性高分子は、これを耐水化し得る慣用の耐水化
剤と共に用いることができ、この耐水化剤としてはホル
マリン、グリオキサゾール、クロム明パンメラミン、メ
ラミン−ホルマリン、ポリアミド樹脂、ポリアミド−エ
ピクロルヒドリン樹脂等が挙げられる。This water-soluble polymer can be used together with a conventional water-resistant agent that can make it water-resistant. Examples of the water-resistant agent include formalin, glyoxazole, chromium-light melamine, melamine-formalin, polyamide resin, and polyamide-epichlorohydrin resin. etc.
本発明の製品を得るには、支持体の表面に感熱発色層を
設けると共に、支持体の裏面に対して、本発明によるカ
ルボキシル基変性ポリビニルアルコールを添加した水性
アクリルエマルジョンを台紙の表面に塗布乾燥して形成
した感圧接着剤層を有する剥離台紙を、その感圧接着剤
層を介して貼付する。To obtain the product of the present invention, a heat-sensitive coloring layer is provided on the surface of the support, and an aqueous acrylic emulsion containing carboxyl group-modified polyvinyl alcohol according to the present invention is applied to the back surface of the support and dried. A release mount having a pressure-sensitive adhesive layer formed thereon is attached via the pressure-sensitive adhesive layer.
本発明の感熱記録型剥離紙は、前記のように、剥離台紙
と支持体裏面との間に介在させた感圧接着剤層に、可塑
剤や油等の浸透に対する遮断性を保持させたことにより
、従来必要とされていた支持体裏面に対するバックコー
ト層の形成が省略され、その分製品生産性が向上すると
共に、更にバックコート層を形成するのに必要とされた
加熱乾燥工程も省略されるので、その分地肌カブリが防
止される。As described above, the heat-sensitive recording type release paper of the present invention has a pressure-sensitive adhesive layer interposed between the release mount and the back surface of the support that maintains a barrier property against penetration of plasticizers, oil, etc. As a result, the formation of a back coat layer on the back side of the support, which was previously required, is omitted, which improves product productivity, and also eliminates the heat drying process required to form a back coat layer. Therefore, background fogging is prevented accordingly.
次に本発明を実施例により更に詳細に説明する。 Next, the present invention will be explained in more detail with reference to Examples.
実施例
下記２液を充分に攪拌混合して感圧接着剤液を形成し、
これを台紙（離型紙）上へ湿潤付着量３６ｇ ／ ｒｒ
？でワイヤーバー塗布し、乾燥して、感圧接着剤層を有
する台紙を作成した。次いでこの台紙を、その感圧接着
剤層を介して感熱記録紙（裏面バリヤ一層なし）の支持
体裏面に貼付して、感熱剥離紙Ａを得た。Example The following two liquids were sufficiently stirred and mixed to form a pressure-sensitive adhesive liquid,
Apply this onto the mount (release paper) with a wet adhesion amount of 36g / rr
? It was coated with a wire bar and dried to create a mount having a pressure-sensitive adhesive layer. Next, this mount was attached to the back side of a support of heat-sensitive recording paper (without a back barrier layer) via the pressure-sensitive adhesive layer to obtain heat-sensitive release paper A.
水性アクリルエマルジョン １０重量部（感圧接着
剤）
酢酸ビニル−イタコン酸変性ポリビニルアル−１１＝
コール１０％水溶液 ３重量部比較例
感圧接着剤液として水性アクリルエマルジョンのみを使
用した以外は実施例と同様な方法で感熱剥離紙Ｂを得た
。Water-based acrylic emulsion 10 parts by weight (pressure-sensitive adhesive) Vinyl acetate-itaconic acid-modified polyvinylal-11 = Cole 10% aqueous solution 3 parts by weight Comparative Example Same as the example except that only the water-based acrylic emulsion was used as the pressure-sensitive adhesive liquid. Heat-sensitive release paper B was obtained in a similar manner.
以上の方法で得た感熱剥離紙Ａ（実施例）及びＢ（比較
例）に対し、１５０℃、 ２ ｋｇ ／ ｃＪ 、 １
秒間熱ブロツクで印字発色させ、地肌部及び発色部の各
濃度をマクベス濃度計で測定後、台紙（離型紙）をはが
し、ラップシートへ貼り、４０℃の乾燥した環境中へ１
２時間放置後、発色部の濃度を測定した。その結果を次
表に示す。150°C, 2 kg/cJ, 1 for thermal release paper A (Example) and B (Comparative Example) obtained by the above method.
After printing and coloring using a heat block for seconds and measuring the density of the background and colored areas using a Macbeth densitometer, remove the backing paper (release paper), apply it to a wrap sheet, and place it in a dry environment at 40°C.
After standing for 2 hours, the density of the colored area was measured. The results are shown in the table below.
表 １ 特許出願人 株式会社 リ コ − 代理人弁理士池浦敏明 ＝１２−Table 1 Patent applicant Rico Co., Ltd. Representative Patent Attorney Toshiaki Ikeura =12-
Claims (1)
感熱発色層を設け、支持体の裏面に接着剤層を介して剥
離台紙を設けたものにおいて、該接着剤層として、カル
ボキシル基変性ポリビニルアルコールを添加した水性ア
クリルエマルジョンから形成された感圧接着剤層を用い
ることを特徴とする感熱記録型剥離紙。(1) A heat-sensitive color forming layer containing a leuco dye and a color developer is provided on the surface of the support, and a release mount is provided on the back surface of the support with an adhesive layer interposed therebetween, in which a carboxyl A heat-sensitive recording release paper characterized by using a pressure-sensitive adhesive layer formed from an aqueous acrylic emulsion to which base-modified polyvinyl alcohol is added.