JPH11107501A - Tatami mat and underlay sheet having antibacterial and mildewproof function - Google Patents

Tatami mat and underlay sheet having antibacterial and mildewproof function

Info

Publication number
JPH11107501A
JPH11107501A JP27120097A JP27120097A JPH11107501A JP H11107501 A JPH11107501 A JP H11107501A JP 27120097 A JP27120097 A JP 27120097A JP 27120097 A JP27120097 A JP 27120097A JP H11107501 A JPH11107501 A JP H11107501A
Authority
JP
Japan
Prior art keywords
antibacterial
tatami
tatami mat
mat
salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP27120097A
Other languages
Japanese (ja)
Inventor
Haruyoshi Funae
晴芳 船江
Munetomo Nakamura
宗知 中村
Yasuo Tsubakii
靖雄 椿井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Paper Mills Ltd
Original Assignee
Mitsubishi Paper Mills Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Paper Mills Ltd filed Critical Mitsubishi Paper Mills Ltd
Priority to JP27120097A priority Critical patent/JPH11107501A/en
Publication of JPH11107501A publication Critical patent/JPH11107501A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a superior antibacterial and mildewproof effects from the initial stage for a long time by carrying antibacterial and mildewproof agent composed of organic compound metallic salt containing a prescribed rate of a prescribed metal in a tatami facing, a tatami mat, a border material, and an underlay sheet. SOLUTION: Synthetic resin fiber or a rush is dipped in solution where antibacterial and mildewproof agent composed of metallic salt of organic compound, which contains at least one kind of nitrogen containing heterocycle and sulfur atom, and binder are dispersed, dried to be carried, woven, and made into a tatami facing. The constitution of the metallic salt is set to silver 10-40%, zinc 20-60%, and copper the rest (>0) in terms of the mole ratio. Dispersion liquid of the antibacterial and mildewproof agent is sprayed or injected by needle into the tatami mat formed by laminating plate materials having cushion performances which are formed by tightening a straw mat or a styrene foam plate, straw chips, wood chips, and cotton. The tatami is so formed that the tatami mat is covered with the tatami facing, and reinforcing materials are stacked on the end parts to be sewn. The antibacterial and mildewproof agent is slightly water-soluble, has high stability, has less falling and pollution, and exhibits superior antibacterial and mildewproof effects from the initial state for a long time.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、抗菌防黴機能を有
する畳に関し、抗菌防黴機能を有する畳表、マット状物
（畳床）、畳表とマット状物の間に設ける抗菌防黴機能
のあるシート、畳表を設ける側と反対側のマット状物を
覆う抗菌防黴機能のあるシート、畳端部に用いる帯状の
当て材、及び畳と床の間に敷くための抗菌防黴機能のあ
る畳の下敷き用シートに関するものである。さらに詳し
くは、本発明の畳、及び畳を構成する各部材、並びに畳
のための下敷き用シートは、菌の繁殖、黴臭などが抑制
され、速効性があり、長期間に亘って抗菌防黴機能が良
く発揮され、必要により、畳の内部、及び床から発生す
る異臭を除去するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tatami mat having an antibacterial and fungicide function, and more particularly to a tatami mat having a antibacterial and fungicide function, a mat-like material (tatami floor), and an antibacterial and fungicide function provided between the tatami mat and the mat-like material. A sheet, a sheet with an antibacterial and antifungal function covering the mat-shaped material on the side opposite to the side where the tatami mat is provided, a band-shaped patch material used at the end of the tatami, and a tatami with an antibacterial and antifungal function to lay between the tatami and the floor The present invention relates to an underlay sheet. More specifically, the tatami mat according to the present invention, the members constituting the tatami mat, and the underlay sheet for the tatami mat are capable of suppressing the growth of bacteria, moldy odor, etc., have a quick effect, and have an antibacterial action for a long period of time. It exhibits a good mold function and removes off-flavors generated from the inside of the tatami and the floor as needed.

【０００２】[0002]

【従来の技術】近年、衛生面の関心が高まり、長時間生
活の場としての畳表および畳に、抗菌防黴機能を持たせ
た畳表および畳を希望する消費者が増加している。特
に、高温多湿の環境下で長期に室内を締め切っていると
畳が黴臭を帯びたり、生活の多様化により、多種の栄養
物が溶解している水溶液をこぼして畳に滲み込み、黴が
発生したり、菌が繁殖したりする。また、環境面からゴ
ミをできるだけ出さないよう、畳表や畳にできるだけ耐
久性を持たせる必要が出てきている。2. Description of the Related Art In recent years, there has been an increasing interest in hygiene, and an increasing number of consumers desire tatami mats and tatami mats having an antibacterial and antifungal function as tatami mats and tatami mats as places for long-term living. In particular, if the room is closed for a long time in a high-temperature and high-humidity environment, the tatami will have a moldy smell, and due to diversification of life, spills an aqueous solution in which various nutrients are dissolved, and seeps into the tatami. They start up and multiply. In addition, it is necessary to make the tatami mats and tatami mats as durable as possible in order to minimize the amount of garbage from the environment.

【０００３】従来から、フェンチオン等の防虫機能を持
たせた畳の部材が知られているが、ダニなどの発生を防
止するだけで、抗菌防黴性は期待できない。特開平６−
２５７０６７号公報は、畳表の少なくとも表面に、セラ
ミックスと、銀イオンまたは銅イオンとを含むコーティ
ング層を形成した敷物を開示している。同公報は金属酸
化物の活性を利用して銀イオンまたは銅イオンを触媒に
して抗菌性と消臭性を持たせるものである。しかしなが
ら、同公報は金属無機酸化物に金属イオンを担持するの
で、防黴効果は期待できず、金属無機酸化物に脱臭機能
があるといっても防黴性によるものではなく、従って十
分な消臭性を得ることができない。また、銀イオンまた
は銅イオンとを併用した系は遅効性であって、最初に菌
や黴が増殖する初期の段階で発生を抑制する効果に乏し
く、即効性、且つ、持続性のある抗菌防黴剤ではない。Hitherto, a tatami member having an insect repellent function such as fenthion has been known. However, antibacterial and antifungal properties cannot be expected only by preventing the occurrence of ticks and the like. JP-A-6
Japanese Patent No. 257067 discloses a rug in which a coating layer containing ceramics and silver ions or copper ions is formed on at least the surface of a tatami mat. In this publication, antibacterial properties and deodorizing properties are imparted by using silver ions or copper ions as catalysts utilizing the activity of metal oxides. However, the publication discloses that a metal ion is carried on a metal inorganic oxide, so that a fungicidal effect cannot be expected. No odor can be obtained. In addition, a system in which silver ions or copper ions are used in combination is slow-acting, has little effect of suppressing the outbreak at the initial stage of the initial growth of bacteria and fungi, and has an immediate-acting and long-lasting antibacterial effect. Not a fungicide.

【０００４】特開平５‐７６１７号公報は、酸性基を有
するポリマーからなる脱臭素材であって、Ｚｎ2+，Ｃｕ
2+，Ｎｉ+，Ｍｎ2+，Ａｇ+，Ｆｅ2+からなる群より選ば
れた少なくとも一種の金属イオンで置換された酸性基を
有する脱臭素材を開示する。同公報は、金属イオンと結
合するポリマーは単に金属イオンをキレート結合などに
より担持する機能を有するのみで、抗菌防黴性は開示さ
れていない。同公報の脱臭素材は、脱臭性能の他に抗菌
性を同時に付与する場合には、必要に応じ酸性基を第４
アンモニウムイオンで置換すると良い旨、記載されてお
り、比較的安定性の悪い第４アンモニウムイオンを使用
するために、長期的な抗菌効果については疑問である。
また、第４アンモニウムイオンの対イオンがハロゲンイ
オンであるために、焼却廃棄する際、環境汚染のおそれ
がある。Japanese Patent Application Laid-Open No. Hei 5-7617 discloses a deodorizing material comprising a polymer having an acidic group, comprising Zn 2+ , Cu
Disclosed is a deodorizing material having an acidic group substituted by at least one metal ion selected from the group consisting of 2+ , Ni + , Mn2 + , Ag + , and Fe2 + . This publication does not disclose antibacterial and antifungal properties, since a polymer that binds to a metal ion merely has a function of supporting the metal ion through chelate bonding or the like. The deodorizing material disclosed in the same publication may have an acid group if necessary, when imparting antibacterial properties in addition to deodorizing performance.
It is described that it is better to substitute with ammonium ions, and it is questionable about the long-term antibacterial effect due to the use of quaternary ammonium ions having relatively low stability.
In addition, since the counter ion of the quaternary ammonium ion is a halogen ion, there is a risk of environmental pollution when incinerated and disposed.

【０００５】特開平７−１３３４４４号公報は、抗菌剤
とビヒクルとを含有する抗菌性塗料組成物において、抗
菌剤が分子内に金属イオンに配位可能な配位基とアルコ
キシシリル基とを有する配位化合物を銀イオン、銅イオ
ン、亜鉛イオン、錫イオンまたはクロムイオンに配位さ
せてなる金属錯体である抗菌性塗料組成物を開示する。
同公報は、水性塗料などに用いるもので、抗菌効果はあ
るが、防黴効果は不十分である。JP-A-7-133444 discloses an antibacterial coating composition containing an antibacterial agent and a vehicle, wherein the antibacterial agent has a coordinating group capable of coordinating to a metal ion and an alkoxysilyl group in a molecule. Disclosed is an antibacterial coating composition which is a metal complex obtained by coordinating a coordination compound with silver, copper, zinc, tin or chromium ions.
This publication is used for water-based paints and the like, and has an antibacterial effect but an insufficient antifungal effect.

【０００６】このような背景から、従来から使用されて
きた畳および下敷き用シートではあきたらず、要求に合
致した抗菌・防黴の両機能を十分備えた畳および下敷き
用シートの提供を求める消費者および生産者が増加して
いるが、抗菌・防黴の両機能について、速効性および長
期間に亘る両面の効果を満足する畳および下敷き用シー
トはまだない。[0006] Against this background, tatami and underlay sheets conventionally used are not satisfactory, and there is a demand for the provision of tatami and underlay sheets that are sufficiently provided with both antibacterial and antifungal functions that meet the requirements. However, there is still no tatami or underlay sheet that satisfies both the antibacterial and antifungal functions in a fast-acting and long-term effect on both sides.

【０００７】[0007]

【発明が解決しようとする課題】本発明は、抗菌・防黴
の両機能が初期及び長期に十分発揮された畳および下敷
き用シートの提供を目的とする。SUMMARY OF THE INVENTION It is an object of the present invention to provide a tatami mat and an underlay sheet in which both antibacterial and antifungal functions are sufficiently exhibited in the initial and long term.

【０００８】[0008]

【課題を解決するための手段】本発明者らは、上記の問
題解決につき、鋭意検討を重ねた結果、これまでに例を
みない画期的な手段、すなわち、畳表や畳床（マット状
物）そのものに抗菌防黴剤を含有させたり、畳および下
敷き用シートを構成する畳部材として用いる繊維状物質
そのものに抗菌防黴剤を含有させたものであって、長期
間に亘って抗菌防黴機能が良く発揮された畳および下敷
き用シートの提供に成功したものである。The inventors of the present invention have conducted intensive studies on solving the above-mentioned problems, and as a result, have found epoch-making means, such as tatami mats and tatami floors (mat-like mats). Product) itself contains an antibacterial and fungicide, or a fibrous substance itself used as a tatami member constituting a tatami mat and an underlay sheet contains an antibacterial and fungicide, which is used for a long period of time. It has succeeded in providing a tatami mat and an underlay sheet that exhibit a good mold function.

【０００９】１．本発明は、マット状物の上を畳表で覆
い、好ましくは端部に帯状の当て材を重ねて端部を縫合
した畳であって、該マット状物、畳表および帯状の当て
材の少なくとも１以上の部材に、有機化合物の金属塩よ
りなる抗菌防黴剤が含まれている畳の発明である。1. The present invention relates to a tatami mat covering a mat-like material with a tatami mat surface, and preferably lapping a band-like patch material at an end and suturing the end, wherein at least one of the mat-like material, the tatami mat and the band-like patch material is provided. The invention of a tatami mat includes the above member containing an antibacterial and fungicide made of a metal salt of an organic compound.

【００１０】２．本発明は、マット状物の上を畳表で覆
い、好ましくは端部に帯状の当て材を重ねて端部を縫合
した畳であって、該マット状物と畳表の間に、有機化合
物の金属塩よりなる抗菌防黴剤を含むシート状物を設け
た畳の発明である。[0010] 2. The present invention relates to a tatami mat covering a mat-like material with a tatami mat surface, preferably overlapping a band-shaped patch material at an end portion and suturing the end portion. It is an invention of a tatami mat provided with a sheet-like material containing an antibacterial and fungicide made of salt.

【００１１】３．本発明は、マット状物の上を畳表で覆
い、好ましくは端部に帯状の当て材を重ねて端部を縫合
した畳であって、畳表が設けられる反対側のマット状物
が、有機化合物の金属塩よりなる抗菌防黴剤を含むシー
トで覆われた畳の発明である。3. The present invention is a tatami mat covering the mat-like material with a tatami mat surface, and preferably suturing the end by overlapping a band-shaped patch at the end, and the mat-shaped material on the opposite side where the tatami mat is provided is an organic compound. Of the present invention is a tatami covered with a sheet containing an antibacterial and antifungal agent comprising a metal salt.

【００１２】４．上記の発明２または３において、マッ
ト状物、畳および下敷き用シート好ましくは端部に帯状
の当て材の少なくとも１以上の部材に、有機化合物の金
属塩よりなる抗菌防黴剤が含まれている畳の発明であ
る。4. In the above invention 2 or 3, at least one member of the mat-like material, the tatami mat and the underlaying sheet, preferably a band-shaped patch at the end, contains an antibacterial and fungicide made of a metal salt of an organic compound. It is the invention of the tatami mat.

【００１３】５．本発明は、有機化合物の金属塩よりな
る抗菌防黴剤を含むシートであって、畳と床の間に敷く
ための畳の下敷き用シートの発明である。5. The present invention relates to a sheet including an antibacterial and fungicide comprising a metal salt of an organic compound, and an underlay sheet for laying between a tatami and a floor.

【００１４】６．上記の発明１〜４において、有機化合
物が含窒素複素環、硫黄原子の少なくとも１種を含有す
る化合物である畳の発明である。6. In the above inventions 1 to 4, a tatami invention in which the organic compound is a compound containing at least one of a nitrogen-containing heterocyclic ring and a sulfur atom.

【００１５】７．上記の発明６において、含窒素複素
環、硫黄原子の少なくとも１種を含む有機化合物が、ベ
ンズイミダゾール化合物、メルカプトピリジン−Ｎ−オ
キシド化合物、イソチアゾロン化合物、ベンゾチアゾー
ル化合物もしくはベンゾチアゾロン化合物から選ばれる
少なくとも１種の化合物である畳の発明である。[0015] 7. In the above invention 6, the organic compound containing at least one of a nitrogen-containing heterocyclic ring and a sulfur atom is at least one selected from a benzimidazole compound, a mercaptopyridine-N-oxide compound, an isothiazolone compound, a benzothiazole compound and a benzothiazolone compound. The invention of the tatami mat, which is a compound of

【００１６】８．上記の発明１〜４において、金属塩が
銀塩、銅塩、亜鉛塩の少なくとも１種を含有する畳の発
明である。8. In the inventions 1 to 4, the invention is a tatami mat in which the metal salt contains at least one of a silver salt, a copper salt and a zinc salt.

【００１７】９．上記の発明８において、金属塩が銀
塩、銅塩、亜鉛塩の２種以上が複合されたものを含有す
る畳の発明である。9. In the above invention 8, the invention is a tatami mat containing a metal salt in which two or more of a silver salt, a copper salt and a zinc salt are combined.

【００１８】１０．上記の発明９において、金属塩が銀
塩、銅塩および亜鉛塩の３種が複合されたものを含有す
る畳の発明である。10. In the ninth aspect of the present invention, the invention relates to a tatami mat according to the ninth aspect, wherein the metal salt contains a complex of three kinds of silver salt, copper salt and zinc salt.

【００１９】１１．上記の発明１０において、銀塩、銅
塩および亜鉛塩３種について、銀、銅および亜鉛の組成
比が、モル比で合計１００としたときに、それぞれ、銀
１０〜４０、亜鉛２０〜６０、残りが銅である（ただ
し、銅が０になることはない）畳の発明である。11. In the above invention 10, when the composition ratio of silver, copper and zinc is set to a total of 100 in terms of a molar ratio of three kinds of silver salt, copper salt and zinc salt, silver 10 to 40 and zinc 20 to 60, respectively. This is a tatami invention in which the remainder is copper (but the copper never goes to zero).

【００２０】１２．上記の発明１〜４において、有機化
合物の金属塩よりなる抗菌防黴剤を含有する繊維状物質
を含む畳の発明である。[12] In the above inventions 1 to 4, it is a tatami invention including a fibrous substance containing an antibacterial and fungicide comprising a metal salt of an organic compound.

【００２１】１３．上記の発明１２において、繊維状物
質がセルロース系繊維の部分変性物である畳の発明であ
る。13. In the twelfth aspect, the invention relates to a tatami mat in which the fibrous substance is a partially modified cellulosic fiber.

【００２２】１４．上記の発明１３において、セルロー
ス系繊維の部分変性物がカルボキシメチル変性されたも
のである畳の発明である。14. A tatami invention according to the above invention 13, wherein the partially modified cellulose fiber is carboxymethyl modified.

【００２３】１５．上記の発明１４において、セルロー
ス系繊維の部分変性物の置換度が、０．５以下である畳
の発明である。[15] In the above invention 14, a tatami invention in which the degree of substitution of the partially modified cellulosic fiber is 0.5 or less.

【００２４】１６．上記の発明１〜４において、有機化
合物の金属塩よりなる抗菌防黴剤を含有する繊維状物質
と有機繊維または無機繊維の少なくとも１種を含む畳の
発明である。16. In the above inventions 1-4, there is provided a tatami invention comprising a fibrous substance containing an antibacterial and fungicide comprising a metal salt of an organic compound and at least one kind of organic fiber or inorganic fiber.

【００２５】１７．上記の発明１６において、有機繊維
が再生繊維、半合成繊維および合成繊維から選ばれる繊
維を単独あるいは複合したものである畳の発明である。17. A tatami invention according to the above invention 16, wherein the organic fiber is a fiber selected from recycled fiber, semi-synthetic fiber and synthetic fiber, alone or in combination.

【００２６】１８．上記の発明１〜４または１５におい
て、少なくとも有機化合物の金属塩よりなる抗菌防黴剤
を含有する繊維状物質と、吸着機能を有する物質とから
なる畳の発明である。18. In the above inventions 1 to 4 or 15, a tatami invention comprising a fibrous substance containing an antibacterial and antifungal agent comprising at least a metal salt of an organic compound and a substance having an adsorption function.

【００２７】１９．上記の発明１８において、吸着機能
を有する物質が、活性炭または活性炭素繊維の少なくと
も１種である畳の発明である。19. In the above invention 18, the tatami mat according to the present invention, wherein the substance having an adsorption function is at least one kind of activated carbon or activated carbon fiber.

【００２８】[0028]

【発明の実施の形態】以下、本発明における抗菌防黴機
能を有する畳を構成する各部材並びに畳と床の間に敷く
ための畳の下敷き用シートについて、詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, members constituting a tatami having an antibacterial and antifungal function and a sheet for laying a tatami underlay between a tatami and a floor in the present invention will be described in detail.

【００２９】本発明における畳表は、繊維状の合成樹脂
物を編成したり、いぐさを編成してなる。防菌防黴機能
を付与するには、編成前の繊維状の合成樹脂物やいぐさ
に金属塩よりなる抗菌防黴剤をバインダーとともに付着
させ、しかる後、編成したり、有機化合物の金属塩より
なる抗菌防黴剤とバインダーを分散した水溶液に該畳表
を浸漬し、乾燥し担持せしめる。また、有機化合物の金
属塩よりなる抗菌防黴剤を含有する繊維状物質と一緒
に、上記の繊維状の合成樹脂物あるいはいぐさを編成す
ることも可能である。さらには、それ以外に補強材とし
て、あるいは消臭材として他の有機繊維を混合し編成し
てもよい。The tatami mat in the present invention is formed by knitting a fibrous synthetic resin material or knitting an rush. In order to impart antibacterial and antifungal functions, an antibacterial fungicide made of a metal salt is attached to a fibrous synthetic resin material or knitted fabric together with a binder before knitting, and then knitted, or from a metal salt of an organic compound. The tatami mat is immersed in an aqueous solution in which an antibacterial fungicide and a binder are dispersed, dried and supported. It is also possible to knit the above-mentioned fibrous synthetic resin or rush together with a fibrous substance containing an antibacterial and fungicide consisting of a metal salt of an organic compound. Further, other organic fibers may be mixed and knitted as a reinforcing material or a deodorant material.

【００３０】本発明におけるマット状物（畳床と同じ）
は、藁床であってもよいし、発泡スチロール板上に、も
しくは発泡スチロール板の上下に、藁または木くずや綿
を固めたクッション性のある板状にした物を積層してな
る。防菌防黴機能を付与するには、畳表とともに縫合す
る前に、発泡スチロール板、藁くずや木くずや綿を固め
たクッション性のある板状物に、有機化合物の金属塩よ
りなる抗菌防黴剤の分散液をスプレーをして付与する
か、内部にニードル注入法により、含有させてもよい。
または、予め有機化合物の金属塩よりなる抗菌防黴剤を
含有せしめたパルプなどのセルロース系繊維状物質を混
合して用いるか、あるいは、これらを組合せてなる。さ
らには、マット状物を構成する段階で、消臭効果を出す
ために活性炭、無機活性繊維を混合して成型するとよ
い。Mat-like material in the present invention (same as a tatami floor)
May be a straw floor, or a laminate made of a cushion-like plate made of hardened straw or wood chips or cotton laminated on a styrofoam plate or above and below the styrofoam plate. An antibacterial agent consisting of a metal salt of an organic compound on a styrofoam plate, a cushion-like plate made of solidified straw, wood chips, or cotton before sewing with a tatami mat May be applied by spraying, or may be contained therein by a needle injection method.
Alternatively, a cellulose-based fibrous substance such as pulp previously containing an antibacterial and antifungal agent comprising a metal salt of an organic compound is used in combination, or a combination thereof. Furthermore, at the stage of composing the mat-like material, it is preferable to mix activated carbon and inorganic active fibers to form a deodorant effect.

【００３１】本発明おいて、必要により用いられる畳の
端に用いる帯状の当て材は、合成繊維を編成したものか
らなるが、防菌防黴機能の付与は、畳表の付与手段と同
様に行われる。また、芯材として腰のある帯状の紙など
も用いられるが、以下に示すシートと同様にして構成さ
れる。In the present invention, the band-shaped patch used at the end of the tatami mat, which is used if necessary, is made of a knitted synthetic fiber. Will be Further, although a waist band-shaped paper or the like is used as the core material, it is configured in the same manner as the sheet shown below.

【００３２】本発明における畳表とマット状物の間に設
けられるシート状物、畳表の反対側のマット面を覆うシ
ート、および、畳と床との間に敷く畳の下敷き用シート
は、基本的には、通常用いられる木材パルプ、草本系パ
ルプ、合成パルプまたは古紙パルプ、有機繊維、無機繊
維などからなる紙や、不織布で構成される。また、必要
により、クッション性を上げるために、発泡性のマット
状シートと貼り合せて用いたり、防水性や強度を上げる
ために、フィルムを貼り合せて用いたり、あるいは、紙
と不織布を張り合わせたり、粗く織った布を組合せて用
いられる。In the present invention, the sheet-like material provided between the tatami mat and the mat-like material, the sheet covering the mat surface on the opposite side of the tatami mat, and the tatami underlay sheet laid between the tatami mat and the floor are basically used. Is composed of commonly used wood pulp, herbaceous pulp, synthetic pulp or waste paper pulp, paper made of organic fiber, inorganic fiber, or the like, or nonwoven fabric. Also, if necessary, it may be used by laminating with a foamed mat-like sheet to improve cushioning properties, or by laminating a film to increase waterproofness or strength, or by laminating paper and nonwoven fabric. Used in combination with a coarsely woven cloth.

【００３３】かかる芯材、畳とマット状物の間に設ける
シート状物、マット面を覆うシートおよび下敷き用シー
ト（これらをまとめてシート類と呼称することがある）
に、防菌防黴機能を付与するには、シート形成前のパル
プや合成繊維など繊維状物質、あるいは、填料に金属塩
よりなる抗菌防黴剤をバインダーとともに付着させ、し
かる後、シート形成したり、有機化合物の金属塩よりな
る抗菌防黴剤とバインダーを分散した水溶液にシートを
浸漬し、乾燥して担持せしめるとよい。具体的には、有
機化合物の金属塩よりなる抗菌防黴剤を含有する繊維状
物質とともに、上記の合成繊維、パルプ、無機繊維、必
要により無機填料を湿式抄紙して、紙や不織布を形成し
たり、あるいは、乾式法で不織布を形成したりする。あ
るいは、乾式法や湿式法により、通常の方法でシートを
形成し、ロールコート、サイズプレス、タブサイズプレ
ス、スプレーなど、各種塗工方法により付与する。ある
いは、湿式法のスラリーに有機化合物の金属塩よりなる
抗菌防黴剤を分散し、そのまま抄紙し、防黴剤が内添さ
れているシートを形成する。また、これらの組合せによ
り、抗菌防黴機能のあるシートが形成される。Such a core material, a sheet-like material provided between a tatami mat and a mat-like material, a sheet covering a mat surface, and an underlay sheet (these may be collectively referred to as sheets).
In order to provide a fungicidal and fungicidal function, a fibrous substance such as pulp or synthetic fiber before sheet formation, or an antibacterial and fungicide consisting of a metal salt is attached to a filler together with a binder, and then the sheet is formed. Alternatively, the sheet may be immersed in an aqueous solution in which an antibacterial fungicide made of a metal salt of an organic compound and a binder are dispersed, dried, and supported. Specifically, together with a fibrous substance containing an antibacterial and antifungal agent comprising a metal salt of an organic compound, the above synthetic fibers, pulp, inorganic fibers, and if necessary, inorganic fillers are wet-formed to form paper or nonwoven fabric. Or a non-woven fabric is formed by a dry method. Alternatively, a sheet is formed by an ordinary method by a dry method or a wet method, and applied by various coating methods such as roll coating, size press, tab size press, and spray. Alternatively, an antibacterial and fungicide consisting of a metal salt of an organic compound is dispersed in a slurry of a wet method, and the paper is made as it is to form a sheet to which the fungicide is internally added. Further, a sheet having an antibacterial and antifungal function is formed by these combinations.

【００３４】本発明に用いられる有機化合物の金属塩よ
りなる抗菌防黴剤を含有する繊維状物質は、通常、直径
が０．１〜１００μｍの糸状の形状を有するもので、フ
ィラメントであってもパルプであってもよい。The fibrous substance containing an antibacterial and fungicide consisting of a metal salt of an organic compound used in the present invention is usually in the form of a thread having a diameter of 0.1 to 100 μm, and may be a filament. It may be pulp.

【００３５】本発明では、過酷な使用に耐えねばならな
い畳に該繊維状物質を適用するのであるから、本発明を
好ましく実施するには、本発明における抗菌防黴剤を繊
維構造内、もしくは、表面に強固かつ密に形成させねば
ならない。また、菌黴が適度の湿度で繁殖することか
ら、防菌防黴剤を有効に機能させるためには、イオン浸
透性、イオン捕獲性を有することが必要である。In the present invention, the fibrous substance is applied to a tatami mat that must withstand severe use. Therefore, in order to preferably carry out the present invention, the antibacterial and fungicide of the present invention is used in a fiber structure or It must be firmly and densely formed on the surface. In addition, since fungi proliferate at an appropriate humidity, in order for the fungicide / fungicide to function effectively, the fungicide must have ion permeability and ion trapping properties.

【００３６】このような繊維として、いわゆるイオン交
換繊維が用いられ、例えばポリスチレン、ポリアクリ
ル、ポリアミド、ポリエチレン、セルロースなどのベー
スポリマーにスルホン酸基、ホスホン酸基、カルボン酸
基等を適度に導入することによって得られる。As such a fiber, a so-called ion exchange fiber is used. For example, a sulfonic acid group, a phosphonic acid group, a carboxylic acid group and the like are appropriately introduced into a base polymer such as polystyrene, polyacryl, polyamide, polyethylene and cellulose. Obtained by:

【００３７】また、通常パルプと称せられる天然のセル
ロース系繊維を部分的に化学変性することにより、好ま
しく利用出来る。化学変性処理としては、硫酸化、リン
酸化、硝酸化、カルボキシメチル化、カルボキシエチル
化、カルボキシプロピル化処理が挙げられる。中でも、
カルボキシメチル化処理は、プロセスが容易で、経済
性、安全性も良く、かつ膨潤性、イオン浸透性などに優
れており、本発明の実施に極めて好適である。Further, natural cellulose fibers usually called pulp can be preferably used by partially chemically modifying them. Examples of the chemical denaturation treatment include sulfation, phosphorylation, nitration, carboxymethylation, carboxyethylation, and carboxypropylation. Among them,
The carboxymethylation treatment is very suitable for the practice of the present invention because the process is easy, the economy is good, the safety is good, and the swelling property and ion permeability are excellent.

【００３８】本発明で好ましく使用されるカルボキシメ
チル変性繊維状物質の素材となるパルプとしては、適度
にカルボキシメチル化された木材パルプ（針葉樹パル
プ、広葉樹パルプなど）は、本発明の実施に好適である
が、この他、レーヨンなどの再生セルロースも同様に使
用可能である。さらには、前記主旨に沿って、適度に変
性されたイオン交換能を有する合成繊維、アルギン酸繊
維や可溶性ポリマーの湿式紡糸繊維であっても良い。ま
た、本発明における抗菌・防黴能を有する有機金属複合
塩を含有するポリマー液から製造された湿式紡糸繊維で
あっても良い。As the pulp used as the material of the carboxymethyl-modified fibrous substance preferably used in the present invention, suitably carboxymethylated wood pulp (such as softwood pulp and hardwood pulp) is suitable for the practice of the present invention. However, regenerated cellulose such as rayon can be used as well. Further, in accordance with the above-mentioned gist, a synthetic fiber having a moderately modified ion exchange ability, an alginate fiber or a wet-spun fiber of a soluble polymer may be used. Further, a wet-spun fiber produced from a polymer solution containing an organic metal complex salt having antibacterial and antifungal properties according to the present invention may be used.

【００３９】本発明の畳および下敷き用シートに使用さ
れる本発明における繊維状物質の好ましい一具体例とし
ては、天然セルロース系繊維のカルボキシメチル化加工
によって達成される。One preferred specific example of the fibrous substance of the present invention used in the tatami mat and underlay sheet of the present invention is achieved by carboxymethylation of natural cellulosic fibers.

【００４０】カルボキシメチル化パルプの製造法は、既
に技術確立されており、例えばシーエムシー社、１９８
５．８．３０出版の「機能性セルロースの開発」６０〜
６１頁に記載されている水媒法、溶媒法のいずれの方法
によっても実施可能である。The method for producing carboxymethylated pulp is already established in the art, for example, CMC 198
5.8.30 Publication "Development of Functional Cellulose" 60-
It can be carried out by any of the aqueous medium method and the solvent method described on page 61.

【００４１】所望のカルボキシメチル基置換度を持つ繊
維状物質を得るには、基本的には、セルロース系繊維に
対するモノクロル酢酸ナトリウム量、アルカリ量および
水の量、その他反応条件を調整することによって可能で
ある。A fibrous substance having a desired degree of carboxymethyl group substitution can be basically obtained by adjusting the amount of sodium monochloroacetate, the amount of alkali and water with respect to the cellulosic fiber, and other reaction conditions. It is.

【００４２】一般的に、カルボキシメチル基置換度は、
グルコース単位当たりのカルボキシメチル基の置換度
（ＤＳ）で定義され、その置換率は、一旦、酸型カルボ
キシメチルセルロースに変換後、過剰量のアルカリを加
えて中和した後、酸で逆滴定することによって求められ
る。In general, the degree of carboxymethyl group substitution is
It is defined as the degree of substitution of carboxymethyl groups per glucose unit (DS). The degree of substitution is to convert to acid-type carboxymethylcellulose, neutralize it by adding an excess amount of alkali, and then back titrate with acid. Required by

【００４３】本発明の畳および下敷き用シートに用いら
れる各種のカルボキシメチル基置換度を持つ繊維状物質
は、置換度が大きくなるにつれて、金属イオン捕獲能は
高まり、したがって、本発明における抗菌・防黴能を有
する有機金属複合塩の充填密度は高くなるが、高置換度
では膨潤が過度に進み、繊維強度の低下および、ひいて
は可溶化に至り、本発明の実施には好ましくない。一般
的に、置換度はおよそ０．６で可溶性となる。強度低下
はあるが置換度はおよそ０．５が繊維形状が維持できる
上限レベルである。The fibrous materials having various degrees of carboxymethyl group substitution used in the tatami mat and underlay sheet of the present invention have a higher metal ion-capturing ability as the degree of substitution increases. Although the packing density of the organometallic composite salt having a fungal ability becomes high, the swelling proceeds excessively at a high degree of substitution, leading to a decrease in fiber strength and eventually to solubilization, which is not preferable for the practice of the present invention. Generally, the degree of substitution becomes soluble at around 0.6. Although the strength is reduced, the substitution degree is about 0.5, which is the upper limit level at which the fiber shape can be maintained.

【００４４】本発明における繊維状物質の好ましい態様
としてのセルロース繊維の置換度の下限値を規定するこ
とは、比較的難しい。例えば、置換度が０．４のカルボ
キシメチル化繊維状物質は、２．５ｍｍｏｌ／ｇの１価
金属イオンを捕獲できるが、本発明によれば、現実的に
有効な捕獲量、およびその後の有機化合物との反応で、
繊維内および少なくとも表面付近に、脱落の少ない形で
複合塩を形成させるには、イオン交換容量の５０％程度
に見積るのが妥当との実験結果がある。It is relatively difficult to define the lower limit of the degree of substitution of the cellulose fiber as a preferred embodiment of the fibrous substance in the present invention. For example, a carboxymethylated fibrous material having a degree of substitution of 0.4 can capture 2.5 mmol / g of monovalent metal ions, but according to the present invention, a practically effective capture amount and subsequent organic In the reaction with the compound,
There is an experimental result that it is appropriate to estimate about 50% of the ion exchange capacity in order to form a complex salt in the fiber and at least in the vicinity of the surface in a form with less falling off.

【００４５】したがって、置換度が０．５のカルボキシ
メチル化繊維状物質で、１〜１．５ｍｍｏｌ／ｇ相当の
有機金属複合塩が形成できる。これは、仮に有機金属塩
の分子量を１５０〜２５０に見積もれば、固形分として
約１５〜４０％の固形分（抗菌防黴剤）が形成されるこ
とを示し、抗菌防黴能を得るに十分な量である。Therefore, a carboxymethylated fibrous substance having a substitution degree of 0.5 can form an organometallic complex salt equivalent to 1 to 1.5 mmol / g. This indicates that if the molecular weight of the organometallic salt is estimated to be 150 to 250, a solid content (antibacterial and antifungal agent) of about 15 to 40% is formed as a solid content, which is sufficient for obtaining the antibacterial and antifungal ability. Amount.

【００４６】このようにして造られた本発明に用いられ
る繊維状物質は、そのままの状態、例えばパルプ形態の
ものを、例えば耐久性の大きい合成繊維と混抄するなど
して、シート状にして畳表やシート類に用いることがで
きる。The fibrous substance used in the present invention thus produced is used as it is, for example, a pulp form is mixed with a highly durable synthetic fiber, for example, to be made into a sheet form to form a tatami mat. And sheets.

【００４７】畳表がいぐさである場合、編成された小さ
な隙間に湿気がたまり、黴や菌が繁殖しやすいので、該
いぐさと有機化合物の金属塩よりなる抗菌防黴剤を含有
する繊維状物質とを含む畳表とする。例えば、いぐさを
畳表に編成する際には、本発明における繊維状物質を糸
状にして、一緒に編み込めばよい。また、いぐさと本発
明の繊維状物質を強固に結合させるには、例えば、本発
明の繊維状物質をＰＶＡ溶液中に含浸させ、接着性を高
めた後、いぐさと共に編み込めばよい。When the tatami mat is made of rush, moisture accumulates in the small gaps formed, and fungi and fungi easily propagate, so that the gusset and the fibrous material containing an antibacterial and antifungal agent made of a metal salt of an organic compound can be used. And a tatami table containing For example, when knitting rushes on a tatami mat, the fibrous substance of the present invention may be formed into a thread and knitted together. Further, in order to firmly bond the fibrous substance of the present invention with the rush, for example, the fibrous substance of the present invention may be impregnated in a PVA solution to improve the adhesiveness, and then knitted together with the rush.

【００４８】有機化合物の金属塩よりなる抗菌防黴剤を
含有する繊維状物質をシート類に用いる場合は、該繊維
状物質そのものをシート状物として用いてもよいが、耐
久性を高めるために、各種の合成繊維を併用してもよ
く、さらに耐久性を高めるためには、これに熱融着性の
有るバインダー繊維を併用してもよい。When a fibrous substance containing an antibacterial and fungicide consisting of a metal salt of an organic compound is used for sheets, the fibrous substance itself may be used as a sheet. Various types of synthetic fibers may be used in combination, and in order to further increase the durability, a binder fiber having heat-fusibility may be used in combination.

【００４９】マット状物に、有機化合物の金属塩よりな
る抗菌防黴剤を含有する畳の場合は、例えば、マット状
物の表面部、裏面部、内部の少なくとも１部に、本発明
の有機化合物の金属塩よりなる抗菌防黴剤を含有させれ
ばよい。In the case of a tatami mat containing an antibacterial and fungicide consisting of a metal salt of an organic compound, for example, at least one part of the front, back and inside of the mat is provided with the organic compound of the present invention. An antibacterial and fungicide consisting of a metal salt of the compound may be contained.

【００５０】床材として畳を用いて日常生活を送る上で
は、畳表の間隙、マット状物と畳表の間隙、あるいは畳
の裏側に、生活上の栄養物が入り込むことは避け難く、
そのため各種の菌や黴が生え易く、また著しく成長する
ことになる。又、高温多湿の状態で室内をしめきってお
くと、菌や黴が生長しやすい状態となる。また、畳と床
との間は何年間も掃除しない場合が有り、床下から上が
る湿気などにより、菌や黴が生長しやすい。In daily life using tatami mats as flooring, it is inevitable that daily nutrients enter the gaps between mats, mats and mats, or the back of tatami mats.
Therefore, various bacteria and fungi tend to grow and grow remarkably. If the room is closed in a hot and humid state, bacteria and fungi are likely to grow. Further, there is a case where the space between the tatami mat and the floor is not cleaned for many years, and bacteria and fungi easily grow due to humidity rising from under the floor.

【００５１】上述の本発明は、このような現象に対し
て、畳の各構成部材、および畳の下に敷く下敷き用シー
トに、本発明における抗菌防黴機能を付与すると、極め
て効果的に抗菌・防黴機能を発揮するものである。The above-mentioned present invention is extremely effective against the above-mentioned phenomena by imparting the antibacterial and antifungal function of the present invention to each component member of the tatami mat and the underlaying sheet laid under the tatami mat. -It exhibits a fungicidal function.

【００５２】本発明における繊維状物質の抗菌防黴能
は、前記の固形分で１％程度、あるいはそれ以下でも十
分な作用を発揮するので、それのみでみればかなり低い
置換度の変性でも利用可能であるが、例えば、このよう
にして加工された抗菌防黴繊維状物質を、樹脂業界で言
われている、いわゆるマスターバッチとして一部用い、
他の未加工繊維と混抄して用いる実施態様は、産業的に
は種々の畳表、畳および下敷き用シートへの応用が可能
となり、また、管理も容易で実用性が高く、各種の畳
表、畳および下敷き用シートに好適に用いられる。The antibacterial and fungicidal activity of the fibrous substance in the present invention is sufficient even when the solid content is about 1% or less. Although it is possible, for example, the antibacterial and antifungal fibrous material thus processed is partially used as a so-called master batch, which is said in the resin industry,
The embodiment used in combination with other unprocessed fibers is industrially applicable to various types of tatami mats, tatami mats and sheets for underlaying, and is easy to manage and has high practicability. And it is suitably used for underlay sheets.

【００５３】このような用途に供するには、少なくとも
５％以上、好ましくは１０％以上の抗菌防黴剤を含有さ
せ得る程度の置換率が必要であり、そのためには、置換
度で表せば、少なくとも０．２以上、好ましくは０．３
５以上のものが好ましい。In order to provide such a use, it is necessary to have a substitution rate at which at least 5% or more, preferably 10% or more, of the antibacterial and fungicide can be contained. At least 0.2, preferably 0.3
Five or more are preferred.

【００５４】しかしながら、金属イオン置換処理、有機
化合物処理を単一ではなく、複数回繰り返すこともで
き、それは、より高い密度での抗菌防黴剤の充填を可能
にする。したがって、上記範囲より下限の領域を決して
排除するものではない。However, the metal ion substitution treatment and the organic compound treatment can be repeated not a single time but a plurality of times, which makes it possible to fill the antibacterial and fungicide at a higher density. Therefore, a region lower than the above range is not excluded.

【００５５】抗菌防黴剤を高密度に充填した繊維状物質
を一部用いることの利点について述べる。抗菌防黴剤を
低密度に充填した繊維状物質を均一に分布させたもの
と、高密度に充填した繊維状物質を島状に分布させたも
のとを比較すると、少なくとも高濃度菌汚染耐性、耐久
性において、後者の方が明らかに優位性を示した。The advantage of partially using a fibrous substance filled with an antibacterial and fungicide at a high density will be described. Comparing the one in which the fibrous material filled with the antibacterial and fungicide at a low density is uniformly distributed and the one in which the fibrous material filled with a high density is distributed in an island form, at least high resistance to bacterial contamination with high concentration, The latter clearly showed superiority in durability.

【００５６】自然界においては、雑多な菌が共存してお
り、また、各種の耐性菌の存在も良く知られている事実
である。それらを含めて、全体的な有効性を発揮させる
には、極度に高濃度化された抗菌防黴剤分布を有する島
状構造は、経済的にも非常に有効な手段である。It is a fact that various bacteria coexist in nature and the existence of various resistant bacteria is well known. In order to achieve their overall effectiveness, including these, island structures with extremely concentrated antimicrobial and fungicide distribution are economically very effective means.

【００５７】このようにして作られた極度に高濃度化さ
れた抗菌防黴剤を含有する本発明における繊維状物質
を、各種の畳および下敷き用シートに適用した場合は、
優れた抗菌防黴機能を有しており、長期間に亘って抗菌
・防黴双方の機能が良く発揮される畳および下敷き用の
提供を可能ならしめたものである。When the fibrous substance of the present invention containing the extremely concentrated antibacterial and fungicide thus prepared is applied to various tatami and underlay sheets,
It has an excellent antibacterial and antifungal function, and can be used for tatami mats and underlays that exhibit both antibacterial and antifungal functions over a long period of time.

【００５８】本発明における繊維状物質と併用される有
機繊維または無機繊維として、有機繊維としては、再生
繊維、半合成繊維および合成繊維から選ばれる繊維を単
独あるいは混合したものが使用され、無機繊維として
は、炭素繊維、セラミック繊維およびウイスカーから選
ばれる繊維を単独あるいは混合したものが使用される。As the organic fibers or inorganic fibers used in combination with the fibrous substance in the present invention, as the organic fibers, fibers selected from regenerated fibers, semi-synthetic fibers and synthetic fibers, alone or in combination, are used. As the material, a fiber selected from carbon fibers, ceramic fibers and whiskers is used alone or in combination.

【００５９】再生繊維としては、例えばレーヨン、キュ
プラが、半合成繊維としては、例えばアセテート、トリ
アセテート、プロミックスが、合成繊維としては、例え
ばナイロン、アクリル、ビニロン、ビニリデン、ポリ塩
化ビニル、ポリエステル、ポリエチレン、ポリプロピレ
ン、ベンゾエート、ポリクラール、フェノール系などの
繊維が挙げられる。Regenerated fibers include, for example, rayon and cupra, semi-synthetic fibers include, for example, acetate, triacetate, and promix. Synthetic fibers include, for example, nylon, acryl, vinylon, vinylidene, polyvinyl chloride, polyester, and polyethylene. , Polypropylene, benzoate, polyclar, phenol-based fibers and the like.

【００６０】本発明における繊維については、繊維ハン
ドブック（１９９３年度版）に拠った。The fibers in the present invention are based on the Fiber Handbook (1993 edition).

【００６１】なお、本発明においては、上記の繊維の他
に、針葉樹パルプ、広葉樹パルプなどの木材パルプや藁
パルプ、竹パルプ、ケナフパルプなどの木本類、草本類
を含むものとする。さらに、古紙、損紙などから得られ
るパルプ繊維も含まれる。In the present invention, in addition to the above fibers, woody plants and herbs such as softwood pulp, hardwood pulp and other wood pulp, straw pulp, bamboo pulp, and kenaf pulp are included. Further, pulp fibers obtained from waste paper, broke, and the like are also included.

【００６２】本発明でいう吸着機能を有する物質とは、
気体、液体、臭気などを吸着する機能を有するものを指
す。例えばゼオライト、モンモリロナイト、アルミノ珪
酸亜鉛、ベントナイト、活性白土、シリカ、シリカゲル
など、また、活性炭、活性炭素繊維などが挙げられる。
特に活性炭、活性炭素繊維などは、臭気、湿気などを吸
着する機能を有するので、有利に用いることができる。The substance having an adsorption function referred to in the present invention is:
A substance that has the function of adsorbing gas, liquid, odor, etc. For example, zeolite, montmorillonite, zinc aluminosilicate, bentonite, activated clay, silica, silica gel, and the like, activated carbon, activated carbon fiber, and the like can be given.
In particular, activated carbon and activated carbon fiber can be advantageously used because they have a function of adsorbing odor, moisture, and the like.

【００６３】本発明の畳および下敷き用シートは、従来
技術の前記問題点を解決し、下記のような種々の優れた
効果を発揮するものである。 （１）黴の発生を防止し、黴臭を抑制する。 （２）高濃度菌汚染にも良好に機能する。 （３）安定性が高く、抗菌防黴剤の溶出が適度であり、
使用中に抗菌防黴剤が脱落汚染することが少ない。 （４）耐久性に優れており、長期間に亘って抗菌・防黴
双方の機能が良く発揮される。 （５）抗菌防黴剤の揮散性が非常に低く、しかも特筆す
べきは抗菌、防黴の双方に極めて有効な畳および下敷き
用シートが得られる。 （６）本発明における繊維状物質を含む畳および下敷き
用シートは、廃棄は焼却処理すれば良く、その際、塩素
系化合物を含まない繊維を使用することにより、環境汚
染をほとんどなくすことができる。The tatami mat and underlay sheet of the present invention solve the above-mentioned problems of the prior art and exhibit various excellent effects as described below. (1) Prevent the generation of mold and suppress the mold odor. (2) Works well for high concentration bacterial contamination. (3) High stability, moderate dissolution of the antibacterial and fungicide,
The antibacterial and antifungal agent is less likely to fall off and contaminate during use. (4) It is excellent in durability and exhibits both antibacterial and antifungal functions well over a long period of time. (5) A tatami and underlay sheet which is extremely low in volatility of an antibacterial and antifungal agent and, more particularly, is extremely effective for both antibacterial and antifungal. (6) The tatami and underlay sheet containing a fibrous substance in the present invention may be disposed of by incineration. At that time, by using fibers containing no chlorine-based compound, environmental pollution can be almost eliminated. .

【００６４】次に、本発明の畳および下敷き用シートに
用いられる部分カルボキシメチル化繊維状物質の金属イ
オン置換処理と抗菌防黴有機化合物について述べる。一
例として、置換度が０．４のＮａ型カルボキシメチルセ
ルロースを使った例を用いて説明する。 １）上記パルプ固形分１００ｇ相当量に攪拌が可能な程
度に水を加える。 ２）硝酸銀１００ｍｍｏｌ／相当量（１７ｇ）を添加す
る。 ３）系のｐＨが５．５〜６．０となるようにアルカリを
添加する。 ４）室温下で３０分攪拌し、十分に置換（吸着）させ
る。 ５）２−メルカプトピリジン−Ｎ−オキシドナトリウム
塩の０．１Ｍ／ｌ液１０００ｍｌを攪拌しながら少しず
つ添加する。銀電極もしくは白金電極を用いて、電位計
測すると、反応終了点を検知することができる。 ６）添加終了後、３０分間攪拌し、十分に反応させる。 ７）０．１Ｍ／ｌの硫酸液を加えて、系のｐＨを約４ま
で下げた後、脱水プレスにて脱水する。Next, the metal ion replacement treatment and the antibacterial and antifungal organic compound of the partially carboxymethylated fibrous substance used in the tatami mat and underlay sheet of the present invention will be described. As an example, a description will be given using an example using Na-type carboxymethylcellulose having a degree of substitution of 0.4. 1) Add water to an amount equivalent to 100 g of the above pulp solid content to such an extent that stirring is possible. 2) Add 100 mmol / equivalent (17 g) of silver nitrate. 3) Add alkali so that the pH of the system is 5.5 to 6.0. 4) Stir at room temperature for 30 minutes to allow sufficient displacement (adsorption). 5) 1000 ml of a 0.1 M / l solution of sodium 2-mercaptopyridine-N-oxide is added little by little with stirring. When the potential is measured using a silver electrode or a platinum electrode, the reaction end point can be detected. 6) After completion of the addition, the mixture is stirred for 30 minutes to allow a sufficient reaction. 7) The pH of the system is lowered to about 4 by adding a 0.1 M / l sulfuric acid solution, and then the system is dehydrated by a dehydration press.

【００６５】上記の手順により、メルカプトピリジン−
Ｎ−オキシド銀塩を含有するパルプが得られる。必要な
らば、再度水中に分散し、水洗することにより、脱落分
をあらかじめ除くことができる。実験結果によれば、一
部脱落はするが９０％以上の高収率で繊維内および表面
固着の形で塩が形成されていることが認められた。According to the above procedure, mercaptopyridine-
A pulp containing a silver N-oxide salt is obtained. If necessary, the fallout can be removed in advance by dispersing in water again and washing with water. According to the results of the experiment, it was confirmed that salts were formed in the form of in-fiber and surface fixation at a high yield of 90% or more, although they were partially removed.

【００６６】メルカプトピリジン−Ｎ−オキシド銀塩を
繊維内もしくは表面に収率良く形成させるには、ｐＨコ
ントロール、攪拌、薬品添加濃度および速度などの最適
化が必要である。In order to form the mercaptopyridine-N-oxide silver salt in the fiber or on the surface in a high yield, it is necessary to optimize pH control, stirring, concentration and rate of addition of chemicals, and the like.

【００６７】本発明において、最も効果的に抗菌防黴機
能を発揮する有機化合物の複合塩の作製方法について述
べる。In the present invention, a method for producing a complex salt of an organic compound that exhibits the most effective antibacterial and antifungal function will be described.

【００６８】基本的には、前記の単一金属塩の場合と同
様に、カルボキシメチルセルロースに対して添加する金
属塩組成を、計算量配合することによって達成できる
し、また、銀電極もしくは白金電極を用いた電位計測に
より、各イオンとの反応をモニターできる。Basically, as in the case of the above-mentioned single metal salt, the composition of the metal salt to be added to carboxymethylcellulose can be achieved by blending in a calculated amount. The reaction with each ion can be monitored by the potential measurement used.

【００６９】一例として、２−メルカプトピリジン−Ｎ
−オキシドの複合塩の繊維状物質の作製方法を例示すれ
ば、銀、銅、亜鉛の複合系に２−メルカプトピリジン−
Ｎ−オキシドを添加することにより得られる。銀２５モ
ル％、銅２５モル％、亜鉛５０モル％と２−メルカプト
ピリジン−Ｎ−オキシドの複合塩を形成させるための具
体例を挙げれば、 Ｎａ型カルボキシメチルセルロース（ＤＳ＝０．４）固形分 １００ｇ 水 ５０００ｇ 硝酸銀 ２５ｍｍｏｌ 硫酸銅 １５ｍｍｏｌ 硝酸亜鉛 ３０ｍｍｏｌ 水 １０００ｇ を加えた後、アルカリでｐＨ５．５〜６．０として、２
−メルカプトピリジン−Ｎ−オキシドナトリウム０．１
Ｍ/ｌ溶液１１５０ｇを添加した後、酸でｐＨ４．０ま
で下げる。また、本発明の好ましい１実施態様として、
硝酸銀添加後、以下、２−メルカプトピリジン−Ｎ−オ
キシド化合物添加→硫酸銅添加→２−メルカプトピリジ
ン−Ｎ−オキシド化合物添加→硝酸亜鉛添加→２−メル
カプトピリジン−Ｎ−オキシド化合物添加など、各種の
添加方法により行うことができる。As an example, 2-mercaptopyridine-N
-If an example of a method for producing a fibrous substance of a complex salt of an oxide is given, 2-mercaptopyridine is used in a complex system of silver, copper, and zinc.
Obtained by adding N-oxide. Specific examples for forming a complex salt of 2-molcaptopyridine-N-oxide with 25 mol% of silver, 25 mol% of copper, and 50 mol% of zinc include: Na-type carboxymethylcellulose (DS = 0.4) 100 g Water 5000 g Silver nitrate 25 mmol Copper sulfate 15 mmol Zinc nitrate 30 mmol Water 1000 g was added, and the pH was adjusted to 5.5 to 6.0 with alkali.
-Sodium mercaptopyridine-N-oxide 0.1
After addition of 1150 g of M / l solution, the pH is lowered to 4.0 with acid. Further, as one preferred embodiment of the present invention,
After the addition of silver nitrate, various types of 2-mercaptopyridine-N-oxide compound addition → copper sulfate addition → 2-mercaptopyridine-N-oxide compound addition → zinc nitrate addition → 2-mercaptopyridine-N-oxide compound addition It can be performed by an addition method.

【００７０】抗菌防黴剤の作製も同様にして行うことが
できる。すなわち、上記の記載からＮａ型カルボキシメ
チルセルロースを除いた形態で行えばよい。The preparation of an antibacterial and antifungal agent can be carried out in the same manner. That is, it may be performed in a form excluding the Na-type carboxymethyl cellulose from the above description.

【００７１】含窒素有機複素環化合物およびチオール化
合物、チオン化合物などの含硫黄化合物の多くは、同様
の思想で形成できる。イソチアゾリン−３−オン系化合
物も同様に可能であり、また、イミダゾール誘導体に
も、それ自身（抗菌）防黴作用があるものが多い。この
場合、水への溶解度は低く、水溶液の形で添加すること
はできないが、水混和性の有機溶剤、例えば、アルコー
ル類、グリコール類、ＤＭＳＯなどの溶剤には可溶であ
り、それらの溶液として添加することにより、金属塩を
繊維状物質内に形成できる。Many of nitrogen-containing organic heterocyclic compounds and sulfur-containing compounds such as thiol compounds and thione compounds can be formed with the same concept. Isothiazolin-3-one compounds are also possible, and many of the imidazole derivatives themselves have an (antibacterial) antifungal action. In this case, the solubility in water is low and it cannot be added in the form of an aqueous solution, but it is soluble in water-miscible organic solvents such as alcohols, glycols, and DMSO. By adding as a metal salt, a metal salt can be formed in the fibrous substance.

【００７２】本発明における繊維状物質は、そのもの自
体のみでシート類として、使用することができるが、他
の併用される各種繊維と共存させて使用することが、よ
り実用的である。さらに、前述したとおり、本発明にお
ける繊維状物質中に、抗菌防黴剤を高濃度に吸着させ
て、いわゆるマスターバッチ的に本発明における繊維状
物質を適用することは、より効果的であり、且つ、操業
上でも大きな利点がある。The fibrous substance in the present invention can be used as a sheet by itself, but it is more practical to use it together with various other fibers used in combination. Further, as described above, in the fibrous substance of the present invention, it is more effective to apply the fibrous substance of the present invention in a so-called master batch by adsorbing an antibacterial and fungicide at a high concentration. There is also a great advantage in operation.

【００７３】本発明の畳中に含まれる抗菌防黴剤の畳１
枚当たりの含有量は、０．１〜７０ｇ、好ましくは０．
２〜３０ｇである。０．１ｇ未満であると、十分な抗菌
防黴機能が発揮されず、また、７０ｇを超えて使用して
も、比較的効果の向上は低く、経済的にも不利である。
また、下敷き用シートの場合は、０．０５〜４０ｇ/ｍ2
である。Tatami 1 of the antibacterial and antifungal agent contained in the tatami of the present invention
The content per sheet is 0.1 to 70 g, preferably 0.1 to 70 g.
2 to 30 g. If the amount is less than 0.1 g, a sufficient antibacterial and antifungal function is not exhibited, and even if the amount exceeds 70 g, the improvement of the effect is relatively low and it is economically disadvantageous.
In the case of an underlay sheet, 0.05 to 40 g / m 2
It is.

【００７４】本発明における抗菌防黴剤を他の併用され
る各種繊維と混抄して使用する場合、必要に応じて、各
種のバインダーを用いることができる。When the antibacterial and fungicidal agent of the present invention is used as a mixture with other fibers used in combination, various binders can be used as necessary.

【００７５】本発明に用いられるバインダー繊維は、芯
鞘タイプ（コアシェルタイプ）、並列タイプ（サイドバ
イサイドタイプ）などの複合繊維が挙げられる。例え
ば、ポリプロピレン（芯）とポリエチレン（鞘）の組み
合わせ（商品名：ダイワボウＮＢＦ−Ｈ：大和紡績
製）、ポリプロピレン（芯）とエチレンビニルアルコー
ル（鞘）の組み合わせ（商品名：ダイワボウＮＢＦ−
Ｅ：大和紡績製）、ポリプロピレン（芯）とポリエチレ
ン（鞘）の組み合わせ（商品名：チッソＥＳＣ：チッソ
製）、高融点ポリエステル（芯）と低融点ポリエステル
（鞘）の組み合わせ（商品名：メルテイ４０８０：ユニ
チカ製）などが挙げられる。また、ビニロンバインダー
繊維（ＶＰＢ１０７×１：クラレ製）などの熱水溶融タ
イプなども使用できる。The binder fibers used in the present invention include conjugate fibers such as a core-sheath type (core-shell type) and a side-by-side type (side-by-side type). For example, a combination of polypropylene (core) and polyethylene (sheath) (trade name: Daiwabo NBF-H: manufactured by Daiwa Spinning), a combination of polypropylene (core) and ethylene vinyl alcohol (sheath) (trade name: Daiwabo NBF-)
E: manufactured by Daiwa Spinning Co., Ltd., a combination of polypropylene (core) and polyethylene (sheath) (trade name: Chisso ESC: made by Chisso), a combination of high melting polyester (core) and low melting polyester (sheath) (trade name: Melty 4080) : Made by Unitika Ltd.). Further, a hot water melting type such as vinylon binder fiber (VPB107 × 1: made by Kuraray) or the like can also be used.

【００７６】バインダー繊維の繊維径は特に限定されな
いが、０．３〜５デニールであることが好ましく、より
好ましくは１〜２デニールである。The fiber diameter of the binder fiber is not particularly limited, but is preferably from 0.3 to 5 denier, more preferably from 1 to 2 denier.

【００７７】本発明における抗菌防黴剤をシート類とし
て用いる場合には、良好な引張り強度、折り適性を抄造
段階で付与させるために、バインダー繊維を配合するこ
とにより、シート状物の内部強度を強くでき、抄造後の
バインダーの付与工程、スリット工程でテンションが加
わった際に起こり易い断紙や、スリット工程、プリーツ
加工工程でシート状物がこすられた時に起こり易い面剥
けを抑える役割を果たす。When the antibacterial and fungicide of the present invention is used as a sheet, the internal strength of the sheet is reduced by adding a binder fiber in order to impart good tensile strength and foldability in the papermaking stage. It can be made strong and plays a role in suppressing surface breakage, which is likely to occur when sheet-like material is rubbed in the application of binder after papermaking, tension is applied in the slitting process, and when the sheet is rubbed in the slitting process, pleating process. .

【００７８】本発明における抗菌防黴剤を使用したシー
ト類を湿式抄紙法で製造する際、地合を良好にするため
には、各種繊維をパルパーなどの分散タンク内で分散水
に均一に分散する必要があり、そのために界面活性剤を
用いることが望ましい。When the sheets using the antibacterial and fungicide of the present invention are produced by a wet papermaking method, in order to improve the formation, various fibers are uniformly dispersed in a dispersion tank such as a pulper in a dispersion water. It is desirable to use a surfactant for this purpose.

【００７９】界面活性剤は、アニオン系、カチオン系、
ノニオン系、両性に分類される。アニオン系界面活性剤
としては、例えば、カルボン酸塩、硫酸エステル塩、ス
ルホン酸塩、リン酸エステル塩などが挙げられる。カチ
オン系界面活性剤としては、アミン塩、アンモニウム塩
などが挙げられる。ノニオン系界面活性剤としては、エ
ーテル型、エステル型、アミノエーテル型などが挙げら
れる。両性界面活性剤としては、ベタイン型などが挙げ
られる。これらの中から、繊維の分散性の良好なものを
適宜選択して用いればよい。また、これら例示したもの
から外れるものであっても、繊維の分散性の良好なもの
であれば問題ない。Surfactants include anionic, cationic and
Nonionic and amphoteric. Examples of the anionic surfactant include a carboxylate, a sulfate, a sulfonate, and a phosphate. Examples of the cationic surfactant include an amine salt and an ammonium salt. Examples of the nonionic surfactant include an ether type, an ester type, and an amino ether type. Examples of the amphoteric surfactant include a betaine type. From these, those having good fiber dispersibility may be appropriately selected and used. In addition, even if it deviates from those exemplified above, there is no problem as long as it has good fiber dispersibility.

【００８０】均一に混合分散した繊維の分散安定性を向
上させるために、アニオン性のポリアクリルアミド系粘
剤を繊維分散液、または抄紙ヘッドに添加することによ
り、湿式抄造後のシート類の地合はさらに向上する。In order to improve the dispersion stability of the uniformly mixed and dispersed fibers, an anionic polyacrylamide-based thickener is added to the fiber dispersion or the papermaking head to form a sheet after wet papermaking. Is further improved.

【００８１】本発明におけるシート類は、一般紙や湿式
不織布を製造するための湿式抄紙機、例えば、長網抄紙
機、円網抄紙機、傾斜ワイヤー式抄紙機を単独で１層で
あっても、同機種同士、異機種を組み合わせた２層以上
の多層であっても良い。The sheets in the present invention may be a single-layer wet paper machine for producing ordinary paper or wet nonwoven fabric, such as a fourdrinier paper machine, a circular net paper machine, or an inclined wire paper machine. Alternatively, two or more layers of the same model or a combination of different models may be used.

【００８２】本発明におけるシート類の坪量は、１０〜
４００g/m2程度が一般的である。The basis weight of the sheets in the present invention is 10 to
About 400 g / m 2 is common.

【００８３】乾燥には、シリンダードライヤー、エアー
ドライヤー、赤外線ドライヤーなどの乾燥機を用いるこ
とが可能である。For drying, a dryer such as a cylinder dryer, an air dryer and an infrared dryer can be used.

【００８４】本発明におけるシート類は、湿式抄紙後乾
燥した時点で、強度および腰が良好であるが、取り扱い
のし易さなどの用途により、さらに強度、腰を向上させ
るために、湿式抄紙し、乾燥した後、各種バインダーを
付与することが可能である。The sheets in the present invention have good strength and stiffness at the time of drying after wet papermaking, but are subjected to wet papermaking to further improve strength and stiffness depending on applications such as easy handling. After drying, it is possible to apply various binders.

【００８５】バインダーとしては、例えば、アクリル系
ラテックス、酢ビ系ラテックス、ウレタン系ラテック
ス、エポキシ系ラテックス、ポリエステル系ラテック
ス、ＳＢＲ系ラテックス、ＮＢＲ系ラテックス、エポキ
シ系バインダー、フェノール系バインダー、ＰＶＡ、デ
ンプン、一般的に製紙工程で使用される紙力剤などが挙
げられ、これらを単独、もしくは架橋剤と併用して使用
できる。Examples of the binder include acrylic latex, vinyl acetate latex, urethane latex, epoxy latex, polyester latex, SBR latex, NBR latex, epoxy binder, phenolic binder, PVA, starch, Examples include paper strength agents generally used in papermaking processes, and these can be used alone or in combination with a crosslinking agent.

【００８６】[0086]

【実施例】以下に実施例を挙げて本発明を具体的に説明
するが、本発明は実施例に限定されるものではない。な
お、実施例中の「部」および「％」は、それぞれ「重量
部」および「重量％」を示す。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the examples. In the examples, “parts” and “%” indicate “parts by weight” and “% by weight”, respectively.

【００８７】＜抗菌防黴剤の作製＞ 「２−メルカプトピリジン−Ｎ−オキシドの銀、銅及び
亜鉛塩の複合塩の作製」下記の薬品を次の順番で添加し
て、組成の銀２５モル％、銅２５モル％、亜鉛５０モル
％と２−メルカプトピリジン−Ｎ−オキシドの複合塩を
作成した。 硝酸銀添加→硫酸銅添加→硝酸亜鉛添加→２−メルカプ
トピリジン−Ｎ−オキシド化合物添加。 ＜配合薬品＞ 水 ５０００ｇ 硝酸銀 ２５ｍｍｏｌ 硫酸銅 １５ｍｍｏｌ 硝酸亜鉛 ３０ｍｍｏｌ ０．１Ｍ／ｌの２−メルカプトピリジン−Ｎ−オキシドナトリウム液 １１５ｍｍｏｌ 相当量を添加<Preparation of antibacterial and antifungal agent> [Preparation of composite salt of silver, copper and zinc salts of 2-mercaptopyridine-N-oxide] The following chemicals were added in the following order, and 25 mol of silver having the composition %, 25 mol% of copper, 50 mol% of zinc and a complex salt of 2-mercaptopyridine-N-oxide. Silver nitrate addition → copper sulfate addition → zinc nitrate addition → 2-mercaptopyridine-N-oxide compound addition. <Combined chemicals> Water 5000 g Silver nitrate 25 mmol Copper sulfate 15 mmol Zinc nitrate 30 mmol 0.1 M / l 2-molcaptopyridine-N-oxide sodium solution 115 mmol An equivalent amount was added.

【００８８】＜抗菌防黴剤を含有した繊維状物質の作製
＞以下の方法で、銀、銅及び亜鉛塩の３種類の抗菌防黴
剤を含有した繊維状物質を作製した。<Preparation of fibrous substance containing antibacterial and fungicide> A fibrous substance containing three kinds of antibacterial and fungicide of silver, copper and zinc salt was prepared by the following method.

【００８９】「抗菌防黴剤を含有した繊維状物質Ａの作
製」前記の発明の実施の形態の記載に準じて、カルボキ
シメチル基置換度０．２２（ＤＳ＝０．２２）の変性Ｎ
ＢＫＰに、銀／２ーメルカプトピリジン−Ｎ−オキシド
よりなる抗菌防黴剤を含有する繊維状物質Ａを作製し
た。すなわち、上記の変性ＮＢＫＰ分散液（固形分１０
００ｇ）に硝酸銀０．５ｍｏｌを加え、ｐＨを５．５に
調節してから、３０分間攪拌する。０．１Ｍ／ｌの２−
メルカプトピリジン−Ｎ−オキシドナトリウム液を、変
性ＮＢＫＰ分散液に加えられた硝酸銀と等モル相当量を
添加した。３０分間攪拌してから、硫酸でｐＨを４まで
下げた後、脱水した。脱水パルプに、再び５００ｍｌの
水を加え、攪拌水洗して脱水し、繊維状物質Ａを得た。"Preparation of fibrous substance A containing antibacterial and antifungal agent" Modified N having a carboxymethyl group substitution degree of 0.22 (DS = 0.22) according to the description of the embodiment of the present invention.
Fibrous substance A containing BKP and an antibacterial and fungicide composed of silver / 2-mercaptopyridine-N-oxide was prepared. That is, the above modified NBKP dispersion (solid content of 10
Then, 0.5 mol of silver nitrate was added to the mixture (00 g), the pH was adjusted to 5.5, and the mixture was stirred for 30 minutes. 0.1 M / l 2-
A sodium mercaptopyridine-N-oxide solution was added in an equimolar amount to silver nitrate added to the modified NBKP dispersion. After stirring for 30 minutes, the pH was reduced to 4 with sulfuric acid and then dehydrated. To the dehydrated pulp, 500 ml of water was added again, and the mixture was washed with stirring water and dehydrated to obtain a fibrous substance A.

【００９０】「抗菌防黴剤を含有した繊維状物質Ｂの作
製」上記の「抗菌防黴剤を含有した繊維状物質Ａの作
製」と同様であるが、前記の発明の実施の形態の記載に
準じて、繊維状物質Ａの代わりに、カルボキシメチル基
置換度０．４０（ＤＳ＝０．４０）の変性ＮＢＫＰに
（銀、銅）／２−メルカプトピリジン−Ｎ−オキシドよ
りなる抗菌防黴剤を含有する繊維状物質Ｂを作製した。
すなわち、上記の変性ＮＢＫＰ分散液（固形分１０００
ｇ）に硝酸銀０．５ｍｏｌ、硫酸銅０．５ｍｏｌを加
え、ｐＨを５．５に調節してから、３０分間攪拌する。
０．１Ｍ／ｌの２ーメルカプトピリジン−Ｎ−オキシド
ナトリウム液を１．５ｍｏｌ相当量を添加した。３０分
間攪拌してから、硫酸でｐＨを４まで下げた後、脱水し
た。脱水パルプに、再び５００ｍｌの水を加え、攪拌水
洗して脱水し、繊維状物質Ｂを得た。"Preparation of fibrous substance B containing antibacterial and fungicide" The same as "Preparation of fibrous substance A containing antibacterial and fungicide", but the description of the embodiment of the present invention is made. In place of fibrous substance A, an antibacterial and fungicide consisting of (silver, copper) / 2-mercaptopyridine-N-oxide was added to modified NBKP having a carboxymethyl group substitution degree of 0.40 (DS = 0.40) A fibrous substance B containing the agent was prepared.
That is, the above modified NBKP dispersion (solid content: 1000
0.5 g of silver nitrate and 0.5 mol of copper sulfate are added to g), and the pH is adjusted to 5.5, followed by stirring for 30 minutes.
1.5 mol equivalent of 0.1 M / l sodium 2-mercaptopyridine-N-oxide solution was added. After stirring for 30 minutes, the pH was reduced to 4 with sulfuric acid and then dehydrated. To the dehydrated pulp, 500 ml of water was added again, and the mixture was washed with stirring water and dehydrated to obtain a fibrous substance B.

【００９１】「抗菌防黴剤を含有した繊維状物質Ｃの作
製」上記の「抗菌防黴剤を含有した繊維状物質Ａの作
製」と同様であるが、前記の発明の実施の形態の記載に
準じて、ＣＰ２２ＡｇＭＰの代わりに、カルボキシメチ
ル基置換度０．４０（ＤＳ＝０．４０）の変性ＮＢＫＰ
に（銀、銅、亜鉛）／２−メルカプトピリジン−Ｎ−オ
キシドよりなる抗菌防黴剤を含有する繊維状物質Ｃを作
製した。すなわち、上記の変性ＮＢＫＰ分散液（固形分
１０００ｇ）に硝酸銀０．２５ｍｏｌ、硫酸銅０．２５
ｍｏｌ、硝酸亜鉛０．５ｍｏｌを加え、ｐＨを５．５に
調節してから、３０分間攪拌する。０．１Ｍ／ｌの２−
メルカプトピリジン−Ｎ−オキシドナトリウム液を１．
７５ｍｏｌ相当量を添加した。３０分間攪拌してから、
硫酸でｐＨを４まで下げた後、脱水した。脱水パルプ
に、再び５００ｍｌの水を加え、攪拌水洗して脱水し、
繊維状物質Ｃを得た。"Preparation of fibrous substance C containing antibacterial and fungicide" The same as "Preparation of fibrous substance A containing antibacterial and fungicide", but in the description of the embodiment of the present invention. Modified NBKP having a carboxymethyl group substitution degree of 0.40 (DS = 0.40) instead of CP22AgMP
To prepare a fibrous substance C containing an antibacterial and fungicide consisting of (silver, copper, zinc) / 2-mercaptopyridine-N-oxide. That is, 0.25 mol of silver nitrate and 0.25 mol of copper sulfate were added to the above-mentioned modified NBKP dispersion (solid content: 1000 g).
mol and 0.5 mol of zinc nitrate, adjust the pH to 5.5, and then stir for 30 minutes. 0.1 M / l 2-
1. Mercaptopyridine-N-oxide sodium solution
An amount equivalent to 75 mol was added. After stirring for 30 minutes,
After the pH was lowered to 4 with sulfuric acid, it was dehydrated. To the dehydrated pulp, add 500 ml of water again, wash with stirring water and dehydrate,
Fibrous substance C was obtained.

【００９２】参考例１ 畳表の作製 上記で作製した抗菌防黴剤とポリビニールアルコールと
を３：１となるように混合し３％溶液とした。更に、ア
クリル酸ソーダ系アニオン性界面活性剤０．１％、アク
リル系ラテックス１％添加した。この溶液にいぐさ及び
編み糸を、畳１枚相当の畳表に含有される量が固形分で
１ｇとなるように浸漬し、乾燥して抗菌防黴処理をし、
畳表を編成した。Reference Example 1 Preparation of Tatami Table The antibacterial fungicide prepared above and polyvinyl alcohol were mixed at a ratio of 3: 1 to prepare a 3% solution. Further, 0.1% of sodium acrylate-based anionic surfactant and 1% of acrylic latex were added. The rush and knitting yarn are immersed in this solution so that the amount contained in the tatami mat equivalent to one tatami mat becomes 1 g in solid content, dried, and subjected to antibacterial and fungicide treatment.
We organized a tatami table.

【００９３】参考例２ マット状物の作製 木くず及びパルプが９：１の割合の混合物中に抗菌防黴
剤を含有した繊維状物質Ｃを０．１％混合し、ポリビニ
ルアルコールとともに加熱圧縮し、厚さ１cmのクッショ
ン性のある板状に固め、畳１枚相当の大きさにした。こ
れに畳１枚当たり固形分で１ｇとなるように、参考例１
と同様に作製した溶液をスプレーし、乾燥して抗菌防黴
処理をし、厚さ２cmの発泡ポリスチロールの板の両面に
重ねて、マット状物とした。Reference Example 2 Preparation of mat-like material A mixture of wood chips and pulp at a ratio of 9: 1 was mixed with 0.1% of fibrous material C containing an antibacterial and fungicide, and heated and compressed together with polyvinyl alcohol. It was solidified into a 1 cm thick cushion-like plate and made into a size equivalent to one tatami mat. Reference example 1 so that the solid content per tatami becomes 1 g.
The solution prepared in the same manner as described above was sprayed, dried and subjected to an antibacterial and fungicidal treatment, and overlaid on both sides of a foamed polystyrene plate having a thickness of 2 cm to obtain a mat-like material.

【００９４】参考例３ 塗布シート類の作製 (1)帯状の当て材の芯材となる紙、マット状物と畳表の
間に設ける紙、畳表が設けられる反対側のマット状物を
覆う紙、畳と床の間に敷くための畳の下敷き用紙 ＬＢＫＰ１００部、アルキルケテンダイマー０．３部、
カチオン系アクリルアミド０．０６部、カチオン化澱粉
０．８部、硫酸バンド０．４部をスラリーとして調製
し、調製後長網抄紙機を用いて坪量１００g/m2の紙を抄
造し、参考例１と同様に作製した溶液を、固形分で１．
５g/m2抄紙工程でサイズプレスし、抗菌防黴処理した帯
状の当て材の芯材となる紙、マット状物と畳表の間に設
ける紙、畳表が設けられる反対側のマット状物を覆う
紙、及び畳と床の間に敷くための畳の下敷き用紙を作成
した。 (2)マット状物と畳表の間に設ける不織布、畳表が設け
られる反対側のマット状物を覆う不織布、畳と床の間に
敷くための畳の下敷き用不織布 アクリル酸ソーダ系アニオン性界面活性剤を全繊維に対
して１％になるように添加し、ＮＢＫＰ（カナダ標準濾
水度４３０ｍｌ）、繊維径２デニール×５ｍｍポリエス
テル繊維状バインダー（メルテイ４０８０、ユニチカ社
製）を各々４０：６０の比率で配合し、乾燥重量で１０
０g/m2になるように、円網抄紙機で抄紙し１００℃で乾
燥後、参考例１と同様に作成した溶液を、固形分で１．
５g/m2抄紙工程でサイズプレスし、表面温度１３０℃の
シリンダードライヤーで乾燥して抗菌防黴処理した湿式
不織布を作製した。Reference Example 3 Preparation of Coated Sheets (1) Paper serving as a core material of a band-shaped patch, paper provided between a mat and a mat, paper covering the mat on the opposite side where a mat is provided, Underlay paper for laying between the tatami and the floor: 100 parts of LBKP, 0.3 parts of alkyl ketene dimer,
0.06 parts of cationic acrylamide, 0.8 parts of cationized starch and 0.4 part of sulfuric acid band were prepared as a slurry, and after preparation, paper having a basis weight of 100 g / m 2 was formed using a fourdrinier paper machine. A solution prepared in the same manner as in Example 1 was obtained by solid content of 1.
5g / m 2 Size press in the paper making process, covers the core paper of the band-shaped backing material that has been subjected to antibacterial and antifungal treatment, the paper provided between the mat and the tatami mat, and the mat on the opposite side where the tatami mat is provided Paper and tatami underlay paper for laying between the tatami and the floor were created. (2) Non-woven fabric to be provided between the mat and the tatami mat, non-woven fabric covering the mat on the opposite side where the tatami mat is provided, non-woven underlay for the tatami mat to be laid between the tatami and the floor, sodium acrylate-based anionic surfactant NBKP (standard Canadian freeness: 430 ml) and a fiber diameter of 2 denier × 5 mm polyester fibrous binder (Melty 4080, manufactured by Unitika Ltd.) are added at a ratio of 40:60 for each of the total fibers. Mix, dry weight 10
Paper was made with a round paper machine so as to be 0 g / m 2 , dried at 100 ° C., and a solution prepared in the same manner as in Reference Example 1 was added to a solid content of 1.
In a papermaking step of 5 g / m 2, the paper was subjected to size press and dried with a cylinder dryer having a surface temperature of 130 ° C. to produce a wet nonwoven fabric treated with antibacterial and antifungal treatment.

【００９５】参考例４ 内添シート類の作成 参考例３における紙で用いたパルプ１００部のうちの５
部を上記の抗菌防黴剤を含有した繊維状物質Ａ、Ｂ及び
Ｃにそれぞれ置き換え、スラリーとして混合して、３種
類の紙を抄造した。参考例３と同様の帯状の当て材の芯
材となる紙、マット状物と畳表の間に設けるシート状物
である紙、畳表が設けられる反対側のマット状物を覆う
シートである紙、並びに畳と床の間に敷くための畳の下
敷き用紙を得た。尚、シートの上には、抗菌防剤を塗布
しなかった。Reference Example 4 Preparation of Internally Added Sheets 5 out of 100 parts of pulp used for paper in Reference Example 3
The parts were respectively replaced with fibrous substances A, B and C containing the above-mentioned antibacterial and fungicide, and mixed as a slurry to produce three types of paper. Paper serving as a core material of a band-shaped patch similar to that of Reference Example 3, paper serving as a sheet provided between a mat and a tatami mat, paper serving as a sheet covering an opposite mat having a tatami mat provided thereon, In addition, tatami underlay paper for laying between the tatami and the floor was obtained. The sheet was not coated with an antibacterial agent.

【００９６】実施例１ 参考例１で作製した畳表と参考例２で作製したマット状
物の間とマット状物の裏に参考例３で作製した塗布紙を
重ね、且つ、畳の端に紙芯として参考例３で作成した紙
をテープ状に切り、これをポリエチレン繊維を編んだリ
ボン状の当て材に重ね、畳の端部に当て、各部材を一体
化するように縫合して、畳を作成した。６畳敷きの部屋
の床に、参考例３で作製した紙を下敷き用シートとして
床面に敷きつめ、その上に畳を敷き、大人３人が寝室と
して一週間使用した。その後、相対湿度７５％、温度３
０℃で３日間及び１月間部屋を密閉した状態にして、使
用前、使用後、３日間密閉後及び１月間密閉後の室内の
空気の状態、畳及び各部材の状態、及び畳をまくって、
畳の裏及び下敷き用シートの抗菌性能、防黴性能を総合
評価した。尚、部屋を密閉する前に一カ所だけ、大腸菌
（Ｅ−ｃｏｌｉ ＩＦＯ３３０１）が２×１０8セル／
ｍｌの試験液を畳の上と下敷き用紙の上に１ＣＣ／ｍ2
スプレーで散布乾燥し、更に畳と畳の隙間に湿る程度に
２０ＣＣ注入し、観察ポイントを作った。抗菌性及び防
黴性の評価には下の試験法を参考までに併用した。Example 1 The coated paper prepared in Reference Example 3 was placed between the tatami mat prepared in Reference Example 1 and the mat-shaped material prepared in Reference Example 2 and the back of the mat-shaped material, and paper was placed on the end of the tatami mat. The paper made in Reference Example 3 was cut into a tape shape as a core, and this was overlaid on a ribbon-shaped patch material woven of polyethylene fibers, applied to the end of the tatami mat, and sewed together so that each member was integrated. It was created. The paper prepared in Reference Example 3 was spread on the floor as a sheet for underlaying on the floor of a room with 6 tatami mats, and tatami was laid thereon, and three adults used the bedrooms for one week. After that, relative humidity 75%, temperature 3
Keep the room closed at 0 ° C for 3 days and 1 month, and before use, after use, after 3 days and after 1 month, the air condition in the room, the state of the tatami and each member, and the tatami ,
The antibacterial performance and the antifungal performance of the back and underlay sheets of the tatami mat were comprehensively evaluated. Before closing the room, E. coli (E-coli IFO3301) contained 2 × 10 8 cells / cell in only one place.
ml of the test solution on the tatami mat and on the underlying paper at 1 CC / m 2
It was spray-dried with a spray, and 20 CC was injected into the gap between the tatami mats so that the humid mats became wet. The following test methods were used for evaluation of antibacterial and antifungal properties.

【００９７】｛試験法｝ ＜抗菌性＞畳の構成部材の目的とする箇所を２ｃｍ×２
ｃｍにカットして、それぞれをＮｕｔｒｉｅｎｔ Ｂｒ
ｏｔｈ寒天培地上に押し当て、試験片上の菌を転写させ
て剥離し、３８℃で２４時間培養し、観察した。 ＜防黴性＞部屋全体の黴臭を官能試験により評価した。
また、各部材を切り取り黴の発生状態をルーペで観察し
た。必要により、１．５％の寒天を加えたＧＰ培地（日
本製薬社製）を作り、畳の各部材を２ｃｍ×２ｃｍにカ
ットした試料片を乗せ、十分に圧着させ、２８℃で２４
時間培養し観察した。その結果、実施例１の畳は一週間
使用した後も畳表の菌の発生が抑制されており使用前と
全く変化はなく、３日間及び１ケ月間密閉状態にあった
部屋の中の空気にも黴臭はなかった。畳の各部材につい
ても密閉前後で菌数の増加はなく抗菌効果が認められ
た。また、畳をめくって、試験水を畳の隙間に注いだ所
の下敷き用シートの抗菌効果も十分働いていており、変
化は見られなかった。{Test Method} <Antibacterial Property> The intended location of the component of the tatami mat is 2 cm × 2
cm and cut each into Nutrient Br
The bacterium on the test piece was transferred and peeled off by pressing on an oth agar medium, cultured at 38 ° C. for 24 hours, and observed. <Mold resistance> The mold odor of the whole room was evaluated by a sensory test.
Each member was cut off and the state of mold generation was observed with a loupe. If necessary, a GP medium (manufactured by Nippon Pharmaceutical Co., Ltd.) to which 1.5% agar was added was prepared, and a sample piece in which each member of the tatami was cut into 2 cm × 2 cm was placed thereon, sufficiently pressed, and pressed at 28 ° C.
The cells were cultured for a time and observed. As a result, the tatami mat of Example 1 was suppressed in the generation of bacteria on the tatami mat even after using it for one week, and there was no change from before use. There was no moldy smell. As for each member of the tatami mat, the number of bacteria did not increase before and after sealing, and an antibacterial effect was observed. In addition, the antibacterial effect of the underlaying sheet where the test water was poured into the gaps of the tatami mats when turning over the tatami mats worked well, and no change was observed.

【００９８】比較例１ いずれの部材にも抗菌防黴処理をしないで、実施例１に
準じて畳をつくり、実施例１と同様の条件で試験した。
その結果、一週間使用後には既に畳表及び畳とマット状
物との間の紙に、使用前に比較して菌の増加が認められ
た。３日間密閉した後の部屋の空気に黴臭があり、畳表
の菌もほぼ無数の状態になっていた。また、畳の隙間に
試験水を注いだ所は、下敷き用シートに黴が生え、菌の
増加があり、試験水を注いだ畳の縁にも黴が生えてい
た。Comparative Example 1 A tatami mat was made in the same manner as in Example 1 without any antibacterial and fungicide treatment, and the test was conducted under the same conditions as in Example 1.
As a result, after one week of use, an increase in bacteria was already observed on the tatami surface and on the paper between the tatami mat and the mat-like material as compared to before use. There was a moldy smell in the air in the room after being closed for 3 days, and the bacteria on the tatami surface were almost innumerable. Where the test water was poured into the gaps between the tatami mats, molds grew on the underlaying sheet, increasing the number of bacteria, and molds grew on the edges of the tatami mats with the test water.

【００９９】実施例２、３、４ 実施例１における参考例３で作成した塗布紙の代わりに
参考例４で作成した紙を用いて実施例１と同様に試験を
行った。抗菌防黴剤を含有した繊維状物質Ａを含む紙を
用いた畳を実施例２とし、抗菌防黴剤を含有した繊維状
物質Ｂを含む紙を用いた畳を実施例３とし、抗菌防黴剤
を含有した繊維状物質Ｃを用いた畳を実施例４とする。
その結果、防黴性については、抗菌防黴剤を含有した繊
維状物質Ａを含む紙を用いた畳（実施例２）、抗菌防黴
剤を含有した繊維状物質Ｂを含む紙を用いた畳（実施例
３）及び抗菌防黴剤を含有した繊維状物質Ｃを含む紙
（実施例４）とも実施例１と同様の効果があった。抗菌
性については、実施例２の畳の間に注いだ所の３日後の
状態は抗菌性はあるものの十分でなく、１カ月後の検査
でも実施例４には到らない。実施例４の畳の抗菌性は実
施例１と同様の効果があった。また、実施例３の畳の場
合はその中間であった。畳をめくって下敷き用紙の状態
を検査したが、同様の結果であった。即効性の抗菌効果
は大きい順に実施例４、３、２であった。Examples 2, 3, 4 A test was conducted in the same manner as in Example 1 except that the paper prepared in Reference Example 4 was used instead of the coated paper prepared in Reference Example 3 in Example 1. The tatami mat using the paper containing the fibrous substance A containing the antibacterial and fungicide is referred to as Example 2, and the tatami mat using the paper containing the fibrous substance B containing the antibacterial and fungicide is referred to as Example 3. Example 4 is a tatami mat using the fibrous substance C containing a fungicide.
As a result, regarding the antifungal property, a tatami mat using the paper containing the fibrous substance A containing the antibacterial and fungicide (Example 2) and a paper containing the fibrous substance B containing the antifungal and the fungicide were used. Tatami (Example 3) and paper containing fibrous substance C containing an antibacterial and fungicide (Example 4) also had the same effects as Example 1. Regarding the antibacterial property, the state after 3 days of pouring between the tatami mats of Example 2 is not sufficient although the antibacterial property is sufficient, and the test after one month does not reach Example 4. The antibacterial property of the tatami mat of Example 4 had the same effect as that of Example 1. In the case of the tatami mat of Example 3, it was in the middle. The condition of the underlying paper was inspected by turning over the tatami mats, and the same result was obtained. The immediate antibacterial effects were Examples 4, 3, and 2 in descending order.

【０１００】実施例５ 実施例４において、参考例４のスラリー中に活性炭素粒
子を２０重量％添加し、活性炭内添紙を抄造し、実施例
４と同様に実験した結果、抗菌防黴性は実施例４と同様
な効果を得た。マット状物の材質から出る臭い及び床か
ら出る臭いも取り除けた。Example 5 In Example 4, 20% by weight of activated carbon particles were added to the slurry of Reference Example 4 to form an activated carbon paper, and the same experiment as in Example 4 was carried out. Obtained the same effect as in Example 4. The odor from the mat-like material and the odor from the floor were also eliminated.

【０１０１】実施例６ 実施例１の塗布紙の代りに、参考例３で作製した湿式不
織布を用いて実施例１と同様の実験を行ったが、実施例
１と同様の効果を得た。Example 6 The same experiment as in Example 1 was performed using the wet nonwoven fabric prepared in Reference Example 3 instead of the coated paper of Example 1, and the same effect as in Example 1 was obtained.

【０１０２】実施例７ 活性炭素繊維２０重量部、ＮＢＫＰ（カナダ標準濾水度
４３０ｍｌ）４０重量部および繊維径２デニール×５ｍ
ｍポリエステル繊維状バインダー（メルテイ４０８０、
ユニチカ社製）３０重量部と上記の抗菌防黴繊維状物質
Ｃを１０重量部をパルプスラリーとして乾燥重量で１０
０g/m2になるように円網抄紙機で抄紙し、表面温度１３
０℃のシリンダードライヤーで乾燥し、シートを作製
し、実施例６と同様に実験した。１カ月間部屋を密閉し
た後で、試験水を滲み込ませた所のシートの内部におけ
る抗菌性については、実施例６の不織布よりも効果があ
ったが、実施例５とほぼ同じ防黴性を得た。このシート
を用いた畳は、マット状物の材質から出る臭い及び床か
ら出る臭いも取り除く効果もあった。Example 7 20 parts by weight of activated carbon fiber, 40 parts by weight of NBKP (Canada standard freeness 430 ml) and fiber diameter 2 denier × 5 m
m polyester fibrous binder (Melty 4080,
Unitica) (30 parts by weight) and 10 parts by weight of the above antibacterial and fungicidal fibrous substance C as a pulp slurry in a dry weight of 10
Paper was made with a mesh paper machine so that the surface temperature became 0 g / m 2 , and the surface temperature was 13
The sheet was dried with a cylinder dryer at 0 ° C. to prepare a sheet, and an experiment was performed in the same manner as in Example 6. After the room was sealed for one month, the antibacterial property inside the sheet where the test water was infiltrated was more effective than the nonwoven fabric of Example 6, but was almost the same as the antifungal property of Example 5. I got The tatami mat using this sheet also has an effect of removing the odor from the mat-like material and the odor from the floor.

【０１０３】比較例２ 実施例１の抗菌防黴剤の代わりに、二酸化チタンに銀イ
オンと銅イオンを担持した微粒子を用いて実験したが、
３日間部屋を閉め切った後の抗菌性について、比較例１
よりもやや効果を有するが、上記の実施例には及ばなか
った。また、防黴性は認められなかった。また、畳表が
初期の段階でザラツキがあり靴下との適度な滑り性がな
く生活適性が劣った。Comparative Example 2 An experiment was conducted using fine particles of titanium dioxide carrying silver ions and copper ions instead of the antibacterial and fungicide of Example 1.
About antibacterial property after closing a room for 3 days, Comparative Example 1
Although it has a slightly better effect, it did not reach the level of the above-mentioned embodiment. No antifungal properties were observed. In addition, the tatami mat was rough at an early stage, and did not have a suitable sliding property with socks, so that the living suitability was poor.

【０１０４】[0104]

【発明の効果】本発明に使用される抗菌防黴剤を含有し
た畳および下敷き用シートは、菌捕捉性が良く、また、
水分維持機能も有しており、各種のイオン拡散性も良好
である。さらに、本発明で使用される抗菌防黴剤は、水
難溶性であり、また適度な解離性を有しているために、
徐放性である。それ故、抗菌防黴の初期的効果ととも
に、長期に亘る効果も優れていて、ポットライフが長
く、耐久性に優れている。また、本発明における抗菌防
黴剤を含有した繊維状物質は、セルロース系繊維の部分
変性物がカルボキシメチル変性されたものであって、さ
らにその置換度（ＤＳ）が０．５以下である繊維状物質
を用いた場合である。このような繊維状物質よりなるパ
ルプを用いると、パルプを構成するセルロース繊維中に
高密度で充填できるので、極めて抗菌防黴剤含有量の高
いパルプが得られる。したがって、本発明に使用される
抗菌防黴剤及び該抗菌防黴剤を含有した繊維状物質を含
む本発明の畳および下敷き用シートは、抗菌防黴効果が
よく発現し、極めて良好な抗菌・防黴効果が得られた。
また、本発明に使用される抗菌防黴剤は、水難溶性で、
安定性が高いために、脱落汚染が著しく少ない。The tatami mat and underlay sheet containing the antibacterial and fungicide used in the present invention have good bacteria-trapping properties,
It also has a function of maintaining moisture and has good ion diffusivity. Furthermore, the antibacterial and antifungal agent used in the present invention is poorly water-soluble and has a moderate dissociation property.
It is sustained release. Therefore, the antibacterial and antifungal effects are excellent as well as the long-term effects, and the pot life is long and the durability is excellent. The fibrous substance containing an antibacterial and fungicide in the present invention is a fiber obtained by partially modifying a cellulosic fiber with carboxymethyl modification and further having a degree of substitution (DS) of 0.5 or less. This is the case when a substance is used. If pulp made of such a fibrous substance is used, the pulp can be filled at a high density into the cellulose fibers constituting the pulp, so that pulp having an extremely high antibacterial and fungicide content can be obtained. Therefore, the tatami mat and underlay sheet of the present invention containing the antibacterial and fungicide used in the present invention and the fibrous substance containing the antibacterial and fungicide exhibit excellent antibacterial and fungicidal effects, and exhibit extremely good antibacterial and antifungal properties. An antifungal effect was obtained.
Further, the antibacterial and antifungal agent used in the present invention is hardly water-soluble,
Due to the high stability, falling contamination is extremely low.

Claims (19)

【特許請求の範囲】[Claims] 【請求項１】 マット状物の上を畳表で覆い、好ましく
は端部に帯状の当て材を重ねて端部を縫合した畳であっ
て、該マット状物、畳表および帯状の当て材の少なくと
も１以上の部材に、有機化合物の金属塩よりなる抗菌防
黴剤が含まれている畳。1. A tatami mat which covers a mat-like material with a tatami mat surface, preferably overlaps a band-like patch material at an end thereof, and stitches the end portions thereof. A tatami mat in which at least one member contains an antibacterial fungicide made of a metal salt of an organic compound. 【請求項２】 マット状物の上を畳表で覆い、好ましく
は端部に帯状の当て材を重ねて端部を縫合した畳であっ
て、該マット状物と畳表の間に、有機化合物の金属塩よ
りなる抗菌防黴剤を含むシート状物を設けた畳。2. A mat having a mat-like material covered with a tatami mat surface, preferably a band-shaped patch material is overlapped on an end portion and the end is sewn. A tatami mat provided with a sheet material containing an antibacterial and fungicide made of a metal salt. 【請求項３】 マット状物の上を畳表で覆い、好ましく
は端部に帯状の当て材を重ねて端部を縫合した畳であっ
て、畳表が設けられる反対側のマット状物が、有機化合
物の金属塩よりなる抗菌防黴剤を含むシートで覆われた
畳。3. A tatami mat covering a mat-like material with a tatami mat surface, preferably a band-shaped patch material on the end portion and suturing the end portion, wherein the mat mat material on the opposite side where the tatami mat mat is provided is an organic material. Tatami covered with a sheet containing an antibacterial and fungicide consisting of a metal salt of a compound. 【請求項４】 マット状物、畳表および好ましくは端部
に帯状の当て材の少なくとも１以上の部材に、有機化合
物の金属塩よりなる抗菌防黴剤が含まれている請求項２
または３記載の畳。4. An antibacterial and antifungal agent comprising a metal salt of an organic compound is contained in at least one member of a mat-like material, a tatami mat surface, and preferably a band-like patch at an end.
Or the tatami according to 3. 【請求項５】 有機化合物の金属塩よりなる抗菌防黴剤
を含むシートであって、畳と床の間に敷くための畳の下
敷き用シート。5. A sheet for laying under a tatami mat to be laid between a tatami mat and a floor, the sheet comprising an antibacterial and fungicide comprising a metal salt of an organic compound. 【請求項６】 有機化合物が含窒素複素環、硫黄原子の
少なくとも１種を含有する化合物である請求項１、２、
３または４記載の畳。6. The compound according to claim 1, wherein the organic compound is a compound containing at least one of a nitrogen-containing heterocyclic ring and a sulfur atom.
The tatami mat according to 3 or 4. 【請求項７】 含窒素複素環、硫黄原子の少なくとも１
種を含む有機化合物が、ベンズイミダゾール化合物、メ
ルカプトピリジン−Ｎ−オキシド化合物、イソチアゾロ
ン化合物、ベンゾチアゾール化合物もしくはベンゾチア
ゾロン化合物から選ばれる少なくとも１種の化合物であ
る請求項６記載の畳。7. A nitrogen-containing heterocyclic ring and at least one of sulfur atoms
The tatami mat according to claim 6, wherein the organic compound containing the seed is at least one compound selected from a benzimidazole compound, a mercaptopyridine-N-oxide compound, an isothiazolone compound, a benzothiazole compound, and a benzothiazolone compound. 【請求項８】 金属塩が銀塩、銅塩、亜鉛塩の少なくと
も１種を含有する請求項１、２、３、または４記載の
畳。8. The tatami mat according to claim 1, wherein the metal salt contains at least one of a silver salt, a copper salt and a zinc salt. 【請求項９】 金属塩が銀塩、銅塩、亜鉛塩の２種以上
が複合されたものを含有する請求項８記載の畳。9. The tatami mat according to claim 8, wherein the metal salt contains a complex of two or more of silver salt, copper salt and zinc salt. 【請求項１０】 金属塩が銀塩、銅塩および亜鉛塩の３
種が複合されたものを含有する請求項９記載の畳。10. The metal salt is a silver salt, a copper salt or a zinc salt.
10. The tatami mat according to claim 9 wherein the species comprises a complex. 【請求項１１】 銀塩、銅塩および亜鉛塩３種につい
て、銀、銅および亜鉛の組成比が、モル比で合計１００
としたときに、それぞれ、銀１０〜４０、亜鉛２０〜６
０、残りが銅である（ただし、銅が０になることはな
い）請求項１０記載の畳。11. The composition ratio of silver, copper and zinc in the three kinds of silver salt, copper salt and zinc salt is 100 in total in molar ratio.
And silver 10-20 and zinc 20-6, respectively.
The tatami mat according to claim 10, wherein 0 is copper and the remainder is copper (but copper does not become 0). 【請求項１２】 有機化合物の金属塩よりなる抗菌防黴
剤を含有する繊維状物質を含む請求項１、２、３、また
は４記載の畳。12. The tatami mat according to claim 1, further comprising a fibrous substance containing an antibacterial and antifungal agent comprising a metal salt of an organic compound. 【請求項１３】 繊維状物質がセルロース系繊維の部分
変性物である請求項１２記載の畳。13. The tatami mat according to claim 12, wherein the fibrous substance is a partially modified cellulosic fiber. 【請求項１４】 セルロース系繊維の部分変性物がカル
ボキシメチル変性されたものである請求項１３記載の
畳。14. The tatami mat according to claim 13, wherein the partially modified cellulosic fiber is carboxymethyl-modified. 【請求項１５】 セルロース系繊維の部分変性物の置換
度が０．５以下である請求項１４記載の畳。15. The tatami mat according to claim 14, wherein the degree of substitution of the partially modified cellulosic fiber is 0.5 or less. 【請求項１６】 有機化合物の金属塩よりなる抗菌防黴
剤を含有する繊維状物質と有機繊維または無機繊維の少
なくとも１種を含む請求項１、２、３または４記載の
畳。16. The tatami mat according to claim 1, comprising a fibrous substance containing an antibacterial and fungicide comprising a metal salt of an organic compound and at least one of organic fibers and inorganic fibers. 【請求項１７】 有機繊維が再生繊維、半合成繊維およ
び合成繊維から選ばれる繊維を単独あるいは複合したも
のである請求項１６記載の畳。17. The tatami mat according to claim 16, wherein the organic fiber is a fiber selected from recycled fiber, semi-synthetic fiber and synthetic fiber, alone or in combination. 【請求項１８】 少なくとも有機化合物の金属塩よりな
る抗菌防黴剤を含有する繊維状物質と、吸着機能を有す
る物質とからなる請求項１、２、３、４または１５記載
の畳。18. The tatami mat according to claim 1, comprising a fibrous substance containing an antibacterial and fungicide comprising at least a metal salt of an organic compound, and a substance having an adsorption function. 【請求項１９】 吸着機能を有する物質が、活性炭また
は活性炭素繊維の少なくとも１種である請求項１８記載
の畳。19. The tatami mat according to claim 18, wherein the substance having an adsorption function is at least one of activated carbon and activated carbon fiber.
JP27120097A 1997-10-03 1997-10-03 Tatami mat and underlay sheet having antibacterial and mildewproof function Pending JPH11107501A (en)