JP2001057931A - Deodorizing antibacterial sheet - Google Patents
Deodorizing antibacterial sheetInfo
- Publication number
- JP2001057931A JP2001057931A JP11234830A JP23483099A JP2001057931A JP 2001057931 A JP2001057931 A JP 2001057931A JP 11234830 A JP11234830 A JP 11234830A JP 23483099 A JP23483099 A JP 23483099A JP 2001057931 A JP2001057931 A JP 2001057931A
- Authority
- JP
- Japan
- Prior art keywords
- antibacterial
- sheet
- nonwoven fabric
- water
- deodorizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、人や動物に使用さ
れるベッド用シーツ等の日用品に関するものである。さ
らに詳しくは、脱臭抗菌に効果が有るシートに関するも
のである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to daily necessities such as bed sheets used for humans and animals. More specifically, the present invention relates to a sheet effective for deodorizing and antibacterial.
【０００２】[0002]
【従来の技術】人あるいは動物が尿等を***した場合に
は、不快な臭気の発生原因となるばかりかベッド、床等
を汚染し、菌類の繁殖を促す源となっている。特に犬、
猫等の***物の臭気は大であり、床等に飛散しやすい。
従来の動物用シートや介護用シートは、粉末状の吸水性
ポリマー等を不織布、紙、フィルム等の支持基体上に、
層状に散布したもの、バインダーで支持基体に固定化し
たもの、支持基体間に封入したもの等が知られている。2. Description of the Related Art When humans or animals excrete urine or the like, they not only cause unpleasant odors but also contaminate beds and floors, and are a source of promoting the propagation of fungi. Especially dogs,
Excrement of cats and the like has a large odor and is easily scattered on floors and the like.
Conventional animal sheets and nursing care sheets are made of a powdery water-absorbing polymer or the like on a nonwoven fabric, paper, or a supporting substrate such as a film.
Known are those that are scattered in layers, those that are fixed to a support substrate with a binder, and those that are sealed between support substrates.
【０００３】従来のシートの問題点としては、単に粉末
状の吸水性ポリマーを基材に散布したものは運搬中や取
り扱い時に吸水性ポリマーが偏在化しやすい。バインダ
ーで固定したものは***物の吸収能が低下する場合が有
る。A problem with the conventional sheet is that when a powdery water-absorbing polymer is simply sprayed on a substrate, the water-absorbing polymer tends to be unevenly distributed during transportation or handling. Those fixed with a binder may reduce the ability to absorb excrement.
【０００４】又、従来のシートは脱臭機能が不十分なも
のが多く、***物の菌類による分解で発生するガスによ
る臭気が経時で周囲に充満する事が多々ある。例えば、
特開平６−２５３９６６号公報には水分移動上部布層、
水分分散中間部層、漏れ防止布層の下部布層を接合して
一体化したものが開示されているが、脱臭性、抗菌性は
考慮されていない。特開平９−１８７４８２号公報に
は、吸水加工された、抗菌性を有する熱可塑性繊維層と
防水層が積層された複合シートが開示されている。しか
しながら、抗菌性を有する熱可塑性繊維のみで吸着剤を
使用していないので初期の脱臭性に劣る。[0004] Further, many of the conventional sheets have an insufficient deodorizing function, and the surroundings are often filled with odor due to gas generated by decomposition of excrement by fungi. For example,
JP-A-6-253966 discloses a moisture transfer upper cloth layer,
Although the one in which the water dispersion intermediate layer and the lower cloth layer of the leakage prevention cloth layer are joined and integrated is disclosed, deodorizing properties and antibacterial properties are not considered. Japanese Patent Application Laid-Open No. Hei 9-187482 discloses a composite sheet in which a water-absorbing, antibacterial thermoplastic fiber layer and a waterproof layer are laminated. However, since only the thermoplastic fiber having antibacterial properties does not use an adsorbent, the initial deodorizing property is poor.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、充分な脱臭
機能を有し、抗菌により***物の分解を抑え、分解によ
るガスの発生を防止する、シート全面で均一で多量の液
体吸収性、脱臭抗菌特性を有する脱臭抗菌シートの提供
を可能ならしめたものである。DISCLOSURE OF THE INVENTION The present invention has a sufficient deodorizing function, suppresses the decomposition of excrement by antibacterial action, and prevents gas generation due to decomposition. It is possible to provide a deodorant antibacterial sheet having deodorant antibacterial properties.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、上記の問
題解決につき鋭意検討を重ねた結果、本発明に到達した
ものである。即ち、本発明は、抗菌防黴剤と吸着剤を含
有する少なくとも２枚の不織布の間に吸水性ポリマーを
熱エンボス加工で封入したシートを液体透過性のシート
と液体不透過性のシートとの間に入れ、少なくとも両端
部の全面ヒートシール加工により一体化したものであ
り、水中へ溶出する成分により抗菌防黴性が発現する脱
臭抗菌シートである。Means for Solving the Problems The present inventors have made intensive studies on solving the above problems, and as a result, have arrived at the present invention. That is, the present invention relates to a liquid-permeable sheet and a liquid-impermeable sheet in which a water-absorbing polymer is sealed between at least two nonwoven fabrics containing an antibacterial fungicide and an adsorbent by hot embossing. It is a deodorized antibacterial sheet which is interposed and integrated by heat sealing at least at both ends, and exhibits antibacterial and antifungal properties due to components eluted into water.
【０００７】本発明は、抗菌防黴剤が有機化合物の金属
塩である脱臭抗菌シートである。The present invention is a deodorizing antibacterial sheet wherein the antibacterial and fungicide is a metal salt of an organic compound.
【０００８】本発明は、有機化合物が、ベンズイミダゾ
ール化合物、メルカプトピリジン−Ｎ−オキシド化合
物、イソチアゾリン化合物、ベンゾチアゾール化合物も
しくはベンゾチアゾリン化合物から選ばれる少なくとも
１種の化合物である脱臭抗菌シートである。The present invention is the deodorizing antibacterial sheet wherein the organic compound is at least one compound selected from a benzimidazole compound, a mercaptopyridine-N-oxide compound, an isothiazoline compound, a benzothiazole compound and a benzothiazoline compound.
【０００９】本発明は、金属塩が銀塩、銅塩、亜鉛塩の
少なくとも１種を含有する脱臭抗菌シートである。The present invention is a deodorizing antibacterial sheet wherein the metal salt contains at least one of a silver salt, a copper salt and a zinc salt.
【００１０】本発明は、吸着剤がゼオライト系化合物で
ある脱臭抗菌シートである。[0010] The present invention is a deodorizing antibacterial sheet wherein the adsorbent is a zeolite compound.
【００１１】本発明は、不織布が、有機化合物の金属塩
よりなる抗菌防黴剤を含有する繊維状物質を含む脱臭抗
菌シートである。The present invention is a deodorizing antibacterial sheet in which the nonwoven fabric contains a fibrous substance containing an antibacterial and fungicide comprising a metal salt of an organic compound.
【００１２】本発明は、不織布が湿式不織布である脱臭
抗菌シートである。[0012] The present invention is a deodorizing antibacterial sheet in which the nonwoven fabric is a wet nonwoven fabric.
【００１３】本発明は、人の介護用シートとして使用さ
れる脱臭抗菌シートである。[0013] The present invention is a deodorizing antibacterial sheet used as a sheet for human care.
【００１４】本発明は、動物用シートとして使用される
脱臭抗菌シートである。[0014] The present invention is a deodorizing antibacterial sheet used as an animal sheet.
【００１５】[0015]
【発明の実施の形態】本発明における脱臭抗菌シート
は、抗菌防黴剤と吸着剤を含有する不織布の間に吸水性
ポリマーを熱エンボス加工で封入したシートと抗菌防黴
剤と吸着剤を含有する不織布が、液体透過性のシートと
液体不透過性のシートの間に入っており、少なくとも両
端部が全面にヒートシール加工で一体化されており、特
に抗菌防黴剤が有機化合物の金属塩よりなり、ペット用
トイレに敷いたり、ペット用の寝床に敷いたり、人の介
護用シートとして寝具上に敷いて使用する。BEST MODE FOR CARRYING OUT THE INVENTION The deodorizing antibacterial sheet of the present invention contains a sheet in which a water-absorbing polymer is encapsulated by heat embossing between a nonwoven fabric containing an antibacterial fungicide and an adsorbent, an antibacterial fungicide and an adsorbent. The nonwoven fabric to be inserted is interposed between the liquid-permeable sheet and the liquid-impermeable sheet, and at least both ends are integrated by heat sealing at least over the entire surface. It can be spread on pet restrooms, bedding on pets, or bedding on bedding as a sheet for human care.
【００１６】液体透過性のシートの役割は、液体をその
表面から吸収し、内部の不織布に渡す役割と、流動性の
***物を保持する役割を持っており、織物、編物、不織
布等が使用される。価格、液体透過性等で選択される
が、スパンボンド法、サーマルボンド法、カード法、エ
アーレイ法、湿式法等の不織布が挙げられる。液体透過
性の改良のためにシート表面に界面活性剤等で親水化処
理を行ったり、使用時の肌触りや柔らかさを出すために
高圧水流で処理したスパンレース加工不織布が好ましく
用いられる。シートを構成する繊維径はあまり小さいの
は液体透過性に劣るので、１〜８デニール程度が好まし
い。厚さは、液体透過性から薄いものがよいが、強度と
復元力等の使用感により選択される。通常は、目付は１
０〜５０ｇ／ｍ2、厚さは１０〜１００μｍ程度のもの
が使用される。好ましくはヒートシール性が良好なもの
が加工性が簡便であるので好ましく選択される。The liquid-permeable sheet has a function of absorbing liquid from its surface and passing it to the internal nonwoven fabric, and a function of retaining fluid excrement. Fabrics, knits, and nonwoven fabrics are used. Is done. Although it is selected according to the price, liquid permeability, etc., non-woven fabrics such as a spun bond method, a thermal bond method, a card method, an air lay method, and a wet method are exemplified. A spun lace nonwoven fabric is preferably used in which the sheet surface is subjected to a hydrophilic treatment with a surfactant or the like to improve the liquid permeability, or treated with a high-pressure water flow to give a soft or soft feel during use. It is preferable that the fiber diameter of the sheet is too small because the liquid permeability is inferior. The thickness is preferably thin in terms of liquid permeability, but is selected depending on the feeling of use such as strength and restoring force. Usually, the basis weight is 1
Those having a thickness of 0 to 50 g / m 2 and a thickness of about 10 to 100 μm are used. Preferably, those having good heat sealability are preferably selected because of easy workability.
【００１７】特に人の介護用として使用する場合には、
液体透過性のシートの表面を疎水性の繊維等とするほう
が患者との接触面の水分を出来るだけ少なくして不快感
を防止するのに効果的である。動物の場合でも同様に疎
水性にすることで足や体の表面に尿等が付着して周囲を
汚染するのを防止する効果が有る。In particular, when used for human care,
It is more effective to use a hydrophobic fiber or the like for the surface of the liquid-permeable sheet in order to minimize the moisture on the contact surface with the patient and prevent discomfort. Similarly, in the case of animals, by making them hydrophobic, there is an effect of preventing urine and the like from adhering to the surface of the feet and body and contaminating the surroundings.
【００１８】疎水性の繊維としてはポリエステルやポリ
プロピレン等が挙げられる。親水性の繊維としては、パ
ルプ、レーヨン、綿、親水性ナイロン等が挙げられる。
好ましくは疎水性不織布と親水性不織布をスパンレース
等で積層したシートが使用出来る。Examples of the hydrophobic fiber include polyester and polypropylene. Examples of the hydrophilic fiber include pulp, rayon, cotton, and hydrophilic nylon.
Preferably, a sheet obtained by laminating a hydrophobic nonwoven fabric and a hydrophilic nonwoven fabric with a spunlace or the like can be used.
【００１９】液体不透過性のシートとしては、液体を遮
断する効果の有るものであれば何でもよいが、例えばポ
リエチレン、ポリプロピレン、ポリ塩化ビニル、ポリエ
ステル等のフィルム、織布、不織布、紙等にラミネート
したラミネートシートが挙げられる。通常は、目付は１
０〜５０ｇ／ｍ2、厚さは１０〜１００μｍ程度のもの
が使用される。好ましくはヒートシール性の良好なもの
が加工性が簡便であるので好ましく選択される。Any liquid-impermeable sheet may be used as long as it has a liquid-blocking effect. For example, the sheet may be laminated to a film of polyethylene, polypropylene, polyvinyl chloride, polyester, or the like, woven fabric, nonwoven fabric, paper, or the like. Laminated sheet. Usually, the basis weight is 1
Those having a thickness of 0 to 50 g / m 2 and a thickness of about 10 to 100 μm are used. Preferably, a material having good heat sealability is preferably selected because the workability is simple.
【００２０】本発明で使用する吸着剤は、粘土系、ゼオ
ライト系、酸性白土系、活性白土系、ベントナイト系、
活性炭系等の無機化合物系や酸性基や塩基性基を有する
高分子化合物等が利用出来る。好ましいのは、アンモニ
ア、トリメチルアミン、硫化水素、エチルメルカプタン
等の吸着に有効である粘土系のアルミノケイ酸亜鉛系で
ある。具体的には水沢化学工業社製のミズカナイトＡ
Ｐ、ミズカナイトＡＧ、ミズカナイトＨＰ、ミズカナイ
トＨＧ、ミズカナイトＭＰが挙げられる。The adsorbent used in the present invention may be clay-based, zeolite-based, acid clay-based, activated clay-based, bentonite-based,
An inorganic compound such as an activated carbon or a polymer compound having an acidic group or a basic group can be used. Preferred are clay-based zinc aluminosilicates which are effective for adsorption of ammonia, trimethylamine, hydrogen sulfide, ethyl mercaptan and the like. Specifically, Mizucanite A manufactured by Mizusawa Chemical Industry Co., Ltd.
P, Mizukanite AG, Mizukanite HP, Mizukanite HG, and Mizukanite MP.
【００２１】本発明で使用する吸水性ポリマーには、架
橋ポリアクリル酸ソーダ、酢酸ビニル−アクリル酸エス
テル共重合体、酢酸ビニル−マレイン酸メチル共重合
体、イソブチレン−無水マレイン酸共重合体、デンプン
−アクリルニトリルグラフト共重合体、ポリエチレンオ
キサイド架橋物等が有る。The water-absorbing polymer used in the present invention includes crosslinked sodium polyacrylate, vinyl acetate-acrylate copolymer, vinyl acetate-methyl maleate copolymer, isobutylene-maleic anhydride copolymer, starch -An acrylonitrile graft copolymer, a crosslinked product of polyethylene oxide and the like.
【００２２】吸水性ポリマーの使用量は、特に限定され
ないが、一般的には脱臭抗菌シートに対して３〜１００
ｇ／ｍ2、好ましくは５〜５０ｇ／ｍ2になるような高吸
水性のポリマーが選択される。吸水性ポリマーの使用に
より尿の戻りを防止する機能、ウエットバック性が向上
するほか、吸収量が増えるので臭いの発生する菌類の増
殖防止に効果が大きい。The amount of the water-absorbing polymer used is not particularly limited, but is generally 3 to 100 with respect to the deodorizing antibacterial sheet.
g / m 2, and preferably is superabsorbent polymers such that 5 to 50 g / m 2 selection. The use of the water-absorbing polymer improves the function of preventing urine return and the wet-back property, and increases the amount of absorption, so that it is highly effective in preventing the growth of odor-producing fungi.
【００２３】抗菌防黴剤と吸着剤を含有する不織布は、
不織布同士の貼り合わせで不織布の間に抗菌防黴剤と吸
着剤をポリエチレンやポリ酢酸ビニル等のバインダー粒
子と併用して熱圧処理で封入したり、抗菌防黴剤と高分
子化合物を含有するする抗菌防黴剤の組成物を塗布、含
浸等で含有させた不織布と他の不織布の間に吸着剤とバ
インダー粒子を封入したものが使用出来る。吸着剤の量
は、その種類により異なるが、臭気物質の吸着効果から
は不織布の重量比で５％以上の使用が好ましく、より好
ましくは１０％以上である。不織布の使用方法は、封入
シート単独か、好ましくは重ねて使用される。The nonwoven fabric containing an antibacterial fungicide and an adsorbent is
An antibacterial and fungicidal agent and an adsorbent are used together with binder particles such as polyethylene and polyvinyl acetate, and sealed between the nonwoven fabrics by heat and pressure treatment. An adsorbent and binder particles are enclosed between a nonwoven fabric containing a composition of the antibacterial and fungicide to be applied, impregnated, and the like, and another nonwoven fabric. Although the amount of the adsorbent varies depending on the type, it is preferable to use 5% or more, more preferably 10% or more by weight of the nonwoven fabric from the viewpoint of the effect of adsorbing odorous substances. Regarding the method of using the nonwoven fabric, the encapsulating sheet is used alone or, preferably, stacked.
【００２４】不織布が湿式不織布の場合は、抗菌防黴剤
を含有する繊維状物質を抄造時に他の繊維と一緒に使用
し、吸着剤は内填することで不織布に含有させる事が出
来るので簡単であり好ましい。また、内填することで吸
着剤の有効面積の減少が少ないので脱臭効果の点でも好
ましい。吸着剤の量はその種類により異なるが、臭気物
質の吸着効果からは不織布の重量比で３％以上の含有量
が好ましく、より好ましくは１０％以上である。不織布
の使用方法は、重ねて複数枚で使用したり、クレープ加
工で不織布にしわを付けた方が表面積が増え、吸水量が
増える他にウエットバック性も向上するので好ましい。When the non-woven fabric is a wet non-woven fabric, a fibrous substance containing an antibacterial and fungicide is used together with other fibers at the time of papermaking, and the adsorbent can be contained in the non-woven fabric by being filled therein. Is preferable. Further, since the decrease in the effective area of the adsorbent is small by filling in, it is preferable in terms of the deodorizing effect. Although the amount of the adsorbent varies depending on the type, the content is preferably 3% or more, more preferably 10% or more by weight of the nonwoven fabric from the viewpoint of the adsorption effect of the odorant. It is preferable to use a plurality of non-woven fabrics by stacking them or wrinkling the non-woven fabric by creping because the surface area increases, the amount of water absorption increases, and the wet-back property also improves.
【００２５】吸水性ポリマーを封入する時の熱エンボス
加工は、例えば表面に凹凸を設けた金属ロールとエンボ
スロールや鏡面ロール、樹脂ロール間に不織布を通す事
で不織布表面に凹凸を付けたり不織布同士を一体化する
加工法である。エンボスロール表面の温度は、不織布や
シートに使用する繊維や樹脂で異なるが、７０〜２００
℃程度が一般的である。The hot embossing process for enclosing the water-absorbing polymer may be performed, for example, by passing a nonwoven fabric between a metal roll having an uneven surface and an embossing roll, a mirror roll, or a resin roll to make the nonwoven fabric uneven, This is a processing method that integrates The temperature of the embossing roll surface varies depending on the fiber or resin used for the nonwoven fabric or sheet.
The temperature is generally about ° C.
【００２６】抗菌防黴剤と吸着剤を含有する不織布の間
に吸水性ポリマーを熱エンボス加工により封入し、一体
化することで吸水性ポリマーの極近隣に抗菌防黴剤が存
在しやすくなり、尿等を介して両者が接触することで抗
菌剤が溶出して吸水性ポリマーが吸収している尿等の中
での菌類の繁殖が抑えられることになる。加えてエンボ
ス加工の方が全面熱加工よりも不織布表面の液体吸収速
度の低下が少ないという効果も有る。The water-absorbing polymer is sealed between the nonwoven fabric containing the antibacterial and fungicide and the adsorbent by hot embossing and integrated, so that the antibacterial and fungicide can be present very close to the water-absorbing polymer, When both come into contact with each other via urine or the like, the antibacterial agent is eluted and the growth of fungi in urine or the like absorbed by the water-absorbing polymer is suppressed. In addition, embossing has the effect that the rate of liquid absorption on the surface of the nonwoven fabric is less reduced than that of thermal processing.
【００２７】抗菌防黴剤と吸着剤を含有する不織布の間
に吸水性ポリマーを熱エンボス加工により封入して一体
化したシートを液体透過性のシートと液体不透過性のシ
ートの間に入れて一体化する時のヒートシール加工は、
鏡面金属ロール同士や鏡面金属ロールとエンボスロール
との間を通す事で複数のシートや不織布を一体化する加
工法である。ロール表面の温度は、不織布やシートに使
用する繊維や樹脂で異なるが、一般的には８０〜２００
℃程度である。A sheet in which a water-absorbing polymer is sealed by heat embossing between a nonwoven fabric containing an antibacterial fungicide and an adsorbent and integrated is put between a liquid-permeable sheet and a liquid-impermeable sheet. The heat sealing process when integrating
This is a processing method in which a plurality of sheets or nonwoven fabrics are integrated by passing between mirror-surface metal rolls or between a mirror-surface metal roll and an embossing roll. The temperature of the roll surface varies depending on the fiber or resin used for the nonwoven fabric or sheet, but is generally 80 to 200.
It is about ° C.
【００２８】本発明の抗菌防黴剤として金属塩で用いら
れる有機化合物は、好ましくは基本的に防黴性を有し、
特に以下の含窒素複素環、硫黄原子の少なくともいずれ
かを含む化合物から選択される。The organic compound used as a metal salt as the antibacterial and antifungal agent of the present invention preferably has basically fungicidal properties,
In particular, it is selected from the following compounds containing at least one of a nitrogen-containing heterocyclic ring and a sulfur atom.
【００２９】本発明で使用する抗菌防黴剤としては、現
在市販されているビグアナイド系、アルコール系、フェ
ノール系、アニリド系、ヨウ素系、イミダゾール系、チ
アゾール系、イソチアゾロン系、トリアジン系、ニトリ
ル系、フッ素系、トロポリン系、有機金属系、無機金属
系のものはいずれも使用可能である。The antibacterial and fungicidal agents used in the present invention include commercially available biguanides, alcohols, phenols, anilides, iodine, imidazoles, thiazoles, isothiazolones, triazines, nitriles, and the like. Any of fluorine-based, tropoline-based, organic metal-based, and inorganic metal-based ones can be used.
【００３０】例えば、ピロール系、ピリジン系、ピリミ
ジン系、ピラゾール系、イミダゾール系、ベンズイミダ
ゾール系、１，３，５−トリアジン系、ヘキサヒドロ−
１，３，５−トリアジン系、トリアゾール系、イソオキ
サゾール系、チアゾール系、ベンゾチアゾール系、チア
ゾロン系、ベンゾチアゾロン系、イソチアゾロン系、ベ
ンゾイソチアゾロン系、テトラヒドロチアジアジンチオ
ン系などを基本骨格とするものが挙げられ、さらに、そ
れらのアルキルアリル誘導体、メルカプト誘導体などが
挙げられるが、なかでも、ベンズイミダゾール化合物、
メルカプトピリジン−Ｎ−オキシド化合物、イソチアゾ
ロン化合物、ベンゾチアゾール化合物、ベンゾチアゾロ
ン化合物から選ばれる少なくとも一種の化合物が特に好
ましい。これらの具体例としては、例えば、２−（４−
チアゾリル）−ベンズイミダゾール、２−（カルボメト
キシアミノ）−ベンズイミダゾール、２−メルカルトピ
リジン−Ｎ−オキシド、１，２−ベンゾイソチアゾリン
−３−オン、５−クロロ−２−メチル−４−イソチアゾ
リン−３−オン、２−メチル−４−イソチアゾリン−３
−オン、２−ｎ−オクチル−４−イソチアゾリン−３−
オン、１，２−ベンゾチアゾロン、２−（４−チオシア
ノメチルチオ）ベンゾチアゾールなどを挙げることがで
きる。For example, pyrrole, pyridine, pyrimidine, pyrazole, imidazole, benzimidazole, 1,3,5-triazine, hexahydro-
1,3,5-triazine, triazole, isoxazole, thiazole, benzothiazole, thiazolone, benzothiazolone, isothiazolone, benzoisothiazolone, tetrahydrothiadiazinethione, etc. And further include their alkylallyl derivatives and mercapto derivatives, among which, among others, benzimidazole compounds,
At least one compound selected from mercaptopyridine-N-oxide compounds, isothiazolone compounds, benzothiazole compounds, and benzothiazolone compounds is particularly preferred. Examples of these are, for example, 2- (4-
Thiazolyl) -benzimidazole, 2- (carbomethoxyamino) -benzimidazole, 2-mercartopyridine-N-oxide, 1,2-benzisothiazolin-3-one, 5-chloro-2-methyl-4-isothiazoline-3 -One, 2-methyl-4-isothiazoline-3
-One, 2-n-octyl-4-isothiazoline-3-
On, 1,2-benzothiazolone, 2- (4-thiocyanomethylthio) benzothiazole and the like can be mentioned.
【００３１】特に、ベンズイミダゾール化合物、メルカ
プトピリジン−Ｎ−オキシド化合物、イソチアゾロン化
合物、ベンゾチアゾール化合物もしくはベンゾチアゾロ
ン化合物のうちの少なくとも１種類が効果の点で好まし
い。In particular, at least one of a benzimidazole compound, a mercaptopyridine-N-oxide compound, an isothiazolone compound, a benzothiazole compound and a benzothiazolone compound is preferable in terms of the effect.
【００３２】また、本発明の脱臭抗菌シートで使用され
る抗菌防黴剤の金属塩の例としては銀、銅、亜鉛、錫、
マンガン、コバルト、鉄塩等が挙げられる。効果の点で
好ましくは銀、銅、亜鉛塩から選択され、特に銀、銅、
亜鉛塩の３種が複合されたものがより好ましい。Examples of the metal salt of the antibacterial and antifungal agent used in the deodorizing antibacterial sheet of the present invention include silver, copper, zinc, tin, and the like.
Manganese, cobalt, iron salts and the like can be mentioned. Silver, copper, and zinc salts are preferred in terms of effect, and silver, copper,
A composite of three zinc salts is more preferred.
【００３３】本発明では、含窒素複素環、硫黄原子の少
なくともいずれかを含む有機化合物の金属塩である抗菌
防黴剤を繊維構造内もしくは表面に強固かつ密に形成さ
せ、有効に機能させる為には、繊維が適度な膨潤性、イ
オン浸透性、イオン捕獲性を有することが必要である。In the present invention, an antibacterial and fungicide, which is a metal salt of an organic compound containing at least one of a nitrogen-containing heterocyclic ring and a sulfur atom, is formed firmly and densely in a fiber structure or on a surface thereof so as to function effectively. It is necessary for the fiber to have a suitable swelling property, ion permeability and ion trapping property.
【００３４】このような繊維として、いわゆるイオン交
換繊維が用いられ、例えばポリスチレン、ポリアクリ
ル、ポリアミド、ポリエチレン、セルロース等のベース
ポリマーにスルホン酸基、ホスホン酸基、カルボン酸基
等を適度に導入する事によって得られる。As such fibers, so-called ion-exchange fibers are used. For example, sulfonic acid groups, phosphonic acid groups, carboxylic acid groups and the like are appropriately introduced into base polymers such as polystyrene, polyacryl, polyamide, polyethylene and cellulose. Gained by things.
【００３５】また通常パルプと称せられる天然のセルロ
ース系繊維を部分的に化学変性することにより好ましく
利用出来る。化学変性処理としては、硫酸化、リン酸
化、硝酸化、カルボキシメチル化、カルボキシエチル
化、カルボキシプロピル化処理が挙げられる。中でも、
カルボキシメチル化処理はプロセスが容易で、経済性、
安全性も良く、かつ膨潤性、イオン浸透性等に優れてお
り本発明の実施に極めて好適であり、特に該セルロース
系繊維の部変性物の置換度が０．５以下のものが好まし
い。Further, natural cellulose fibers usually referred to as pulp can be preferably used by partially chemically modifying them. Examples of the chemical denaturation treatment include sulfation, phosphorylation, nitration, carboxymethylation, carboxyethylation, and carboxypropylation. Among them,
The carboxymethylation process is easy, economical,
It is excellent in safety and excellent in swelling property, ion permeability and the like, and is very suitable for the practice of the present invention. In particular, it is preferable that the degree of substitution of the partially modified product of the cellulose fiber is 0.5 or less.
【００３６】本発明で好ましく使用されるカルボキシメ
チル変性繊維状物質の素材となるパルプとしては、適度
にカルボキシメチル化された木材パルプ（針葉樹パル
プ、広葉樹パルプなど）は、本発明の実施に好適である
が、この他、レーヨンなどの再生セルロースも同様に使
用可能である。さらには、前記主旨に沿って適度に変性
されたイオン交換能を有する合成繊維、アルギン酸繊維
や可溶性ポリマーの湿式紡糸繊維であっても良い。ま
た、本発明における抗菌・防黴能を有する有機金属複合
塩を含有するポリマー液から製造された湿式紡糸繊維で
あっても良い。As the pulp used as the material of the carboxymethyl-modified fibrous substance preferably used in the present invention, suitably carboxymethylated wood pulp (softwood pulp, hardwood pulp, etc.) is suitable for practicing the present invention. However, regenerated cellulose such as rayon can be used as well. Further, a synthetic fiber, an alginic acid fiber, or a wet-spun fiber of a soluble polymer, which is appropriately modified according to the above-mentioned purpose and has ion exchange ability, may be used. Further, a wet-spun fiber produced from a polymer solution containing an organic metal complex salt having antibacterial and antifungal properties according to the present invention may be used.
【００３７】本発明における繊維状物質の好ましい一具
体例としては、天然セルロース系繊維のカルボキシメチ
ル化加工によって達成される。A preferred specific example of the fibrous substance in the present invention is achieved by carboxymethylation of a natural cellulosic fiber.
【００３８】本発明で用いられる各種のカルボキシメチ
ル基置換度を持つ繊維状物質は、置換度が大きくなるに
つれて、金属イオン捕獲能は高まり、したがって、本発
明における抗菌・防黴能を有する有機金属複合塩の充填
密度は高くなるが、高置換度では膨潤が過度に進み、繊
維強度の低下および、ひいては可溶化に至る。一般的
に、置換度はおよそ０．６で可溶性となる。強度低下は
あるが置換度はおよそ０．５が繊維形状が維持できる上
限レベルである。The fibrous substances having various degrees of carboxymethyl group substitution used in the present invention have a higher metal ion-capturing ability as the degree of substitution increases, and therefore, the organic metal having antibacterial and antifungal properties according to the present invention. Although the packing density of the composite salt increases, the swelling proceeds excessively at a high degree of substitution, leading to a decrease in fiber strength and, consequently, to solubilization. Generally, the degree of substitution becomes soluble at around 0.6. Although the strength is reduced, the degree of substitution is about 0.5, which is the upper limit level at which the fiber shape can be maintained.
【００３９】このようにして作られた極度に高濃度化さ
れた抗菌防黴剤を含有する繊維状物質と吸着剤を用いた
本発明における不織布を封入した袋を適用した場合は、
抗菌防黴剤が適度に水溶解性が有り、優れた抗菌防黴機
能による腐敗防止効果や吸着剤の脱臭効果により悪臭が
軽減される。特に吸水性ポリマー近隣に存在する抗菌防
黴剤が効果的に尿中に溶解して菌類の繁殖を抑える。When the nonwoven fabric-sealed bag of the present invention using the fibrous substance containing the extremely concentrated antibacterial and fungicide thus prepared and the adsorbent is applied,
The antibacterial and antifungal agent has moderate water solubility, and the excellent antibacterial and antifungal function has a rot preventing effect and a deodorizing effect of the adsorbent, thereby reducing malodor. In particular, an antibacterial and fungicide existing near the water-absorbing polymer effectively dissolves in urine and suppresses the growth of fungi.
【００４０】本発明において、最も効果的に抗菌防黴機
能を発揮する有機化合物の複合塩の作製方法について述
べる。In the present invention, a method for producing a complex salt of an organic compound that exhibits the most effective antibacterial and antifungal function will be described.
【００４１】基本的には、カルボキシメチルセルロース
に対して添加する金属塩組成を、計算量配合することに
よって達成できるし、また、銀電極もしくは白金電極を
用いた電位計測により、各イオンとの反応をモニターで
きる。Basically, it can be achieved by mixing the composition of the metal salt added to carboxymethylcellulose in a calculated amount, and the reaction with each ion can be measured by measuring the potential using a silver electrode or a platinum electrode. Can be monitored.
【００４２】一例として、２−メルカプトピリジン−Ｎ
−オキシドの複合塩の作製方法を例示すれば、銀、銅、
亜鉛の複合系に２−メルカプトピリジン−Ｎ−オキシド
を添加することにより得られる。銀２５モル％、銅２５
モル％、亜鉛５０モル％と２−メルカプトピリジン−Ｎ
−オキシドの複合塩を形成させるための具体例を挙げれ
ば、 Ｎａ型カルボキシメチルセルロース（ＤＳ＝０．４）固形分 １００ｇ 水 ５０００ｇ 硝酸銀 １０ｍｍｏｌ 硫酸銅 １５ｍｍｏ ｌ 硝酸亜鉛 ３０ｍｍ ｏｌ 水 １０００ｇ ２−メルカプトピリジン−Ｎ−オキシドナトリウム0.1m/l溶液１０００ｇ となる。また、本発明の好ましい１実施態様として、硝
酸銀添加後、以下、２−メルカプトピリジン−Ｎ−オキ
シド化合物添加→硫酸銅添加→２−メルカプトピリジン
−Ｎ−オキシド化合物添加→硝酸亜鉛添加→２−メルカ
プトピリジン−Ｎ−オキシド化合物添加など、各種の添
加方法により行うことができる。As an example, 2-mercaptopyridine-N
Illustrating a method for producing a composite salt of an oxide, silver, copper,
It is obtained by adding 2-mercaptopyridine-N-oxide to a composite system of zinc. 25 mol% silver, 25 copper
Mol%, zinc 50 mol% and 2-mercaptopyridine-N
Specific examples for forming a complex salt of an oxide include: Na-type carboxymethylcellulose (DS = 0.4) solid content 100 g water 5000 g silver nitrate 10 mmol copper sulfate 15 mmol zinc nitrate 30 mmol water 1000 g 2-mercaptopyridine-N -1000 g of a 0.1 m / l solution of sodium oxide. As a preferred embodiment of the present invention, after addition of silver nitrate, addition of 2-mercaptopyridine-N-oxide compound → addition of copper sulfate → addition of 2-mercaptopyridine-N-oxide compound → addition of zinc nitrate → 2-mercapto It can be performed by various addition methods such as addition of a pyridine-N-oxide compound.
【００４３】含窒素有機複素環化合物およびチオール化
合物、チオン化合物などの含硫黄化合物の多くは、同様
の思想で形成できる。Many of nitrogen-containing organic heterocyclic compounds and sulfur-containing compounds such as thiol compounds and thione compounds can be formed with the same concept.
【００４４】イソチアゾリン−３−オン系化合物も同様
に可能であり、また、イミダゾール誘導体にも、それ自
身（抗菌）防黴作用があるものが多い。この場合、水へ
の溶解度は低く、水溶液の形で添加することはできない
が、水混和性の有機溶剤、例えば、アルコール類、グリ
コール類などの溶剤には可溶であり、それらの溶液とし
て添加することにより、金属塩を繊維状物質内に形成で
きる。Isothiazolin-3-one compounds are also possible, and many of the imidazole derivatives themselves have an antibacterial and antifungal action. In this case, the solubility in water is low and it cannot be added in the form of an aqueous solution, but it is soluble in water-miscible organic solvents, for example, solvents such as alcohols and glycols. By doing so, a metal salt can be formed in the fibrous material.
【００４５】本発明における抗菌防黴剤を含有する繊維
状物質は、そのもの自体や他の有機繊維や無機繊維と混
合して粒状物として適用することもできるが、繊維状物
質単独や、他の各種繊維と混抄して不織布にして使用す
ることが、より実用的である。さらに、前述したとお
り、本発明における繊維状物質中に、抗菌防黴剤を高濃
度に吸着させて、いわゆるマスターバッチ的に本発明に
おける繊維状物質を適用することは、より効果的であ
り、且つ、操業上でも大きな利点がある。The fibrous substance containing the antibacterial and antifungal agent of the present invention can be used as a granular substance by itself or as a mixture with other organic fibers or inorganic fibers. It is more practical to mix with various fibers to make a nonwoven fabric. Further, as described above, in the fibrous substance of the present invention, it is more effective to apply the fibrous substance of the present invention in a so-called master batch by adsorbing an antibacterial and fungicide at a high concentration. There is also a great advantage in operation.
【００４６】本発明における抗菌防黴剤を含有する繊維
状物質と併用される有機繊維や無機繊維は、有機繊維と
しては、植物繊維、動物繊維、再生繊維、半合成繊維お
よび合成繊維から選ばれる繊維を単独あるいは混合した
ものが使用され、無機繊維としては、ガラス繊維、炭素
繊維、セラミック繊維およびウイスカーから選ばれる繊
維を単独あるいは混合したものが使用される。The organic fibers and inorganic fibers used in combination with the fibrous substance containing the antibacterial and fungicide in the present invention are selected from the group consisting of plant fibers, animal fibers, regenerated fibers, semi-synthetic fibers and synthetic fibers. A single fiber or a mixture of fibers is used. As the inorganic fiber, a single fiber or a mixture of fibers selected from glass fiber, carbon fiber, ceramic fiber and whisker is used.
【００４７】植物繊維としては、針葉樹パルプ、広葉樹
パルプなどの木材パルプや藁パルプ、竹パルプ、ケナフ
パルプなどの木本類、草本類、綿、麻（亜麻、ラミー）
等を含み、吸水性からは好ましい。さらに、古紙、損紙
などから得られるパルプ繊維も含まれる。動物繊維とし
ては、絹、羊毛などの繊維が挙げられる。Examples of plant fibers include wood pulp such as softwood pulp and hardwood pulp, straw pulp, bamboo pulp, and kenaf pulp, woody plants, herbs, cotton, hemp (flax, ramie).
Etc., and is preferred from the viewpoint of water absorption. Further, pulp fibers obtained from waste paper, broke, and the like are also included. Animal fibers include fibers such as silk and wool.
【００４８】再生繊維としては、レーヨン、キュプラ
が、半合成繊維としては、アセテート、トリアセテー
ト、プロミックスが、合成繊維としては、ナイロン、ア
クリル、ビニロン、ビニリデン、ポリ塩化ビニル、ポリ
エステル、ポリエチレン、ポリプロピレン、ベンゾエー
ト、ポリクラール、フェノール系などの繊維が挙げられ
る。Regenerated fibers include rayon and cupra, semi-synthetic fibers include acetate, triacetate, and promix. Synthetic fibers include nylon, acrylic, vinylon, vinylidene, polyvinyl chloride, polyester, polyethylene, polypropylene, Fibers such as benzoate, polyclar, and phenol-based fibers are included.
【００４９】本発明における抗菌防黴剤を含有する繊維
状物質の比率は、含有する抗菌防黴剤の種類や比率によ
るが、粒状物や不織布を構成する全繊維状物質中で、
０．１〜１００重量部、好ましくは０．５〜７０重量部
である。０．１重量部未満であると、十分な抗菌防黴機
能が発揮されず、長期にわたる効果が得にくい。また、
７０重量部を超えるとコスト面から望ましくない。The ratio of the fibrous substance containing the antibacterial and fungicide in the present invention depends on the kind and ratio of the antibacterial and fungicide contained therein.
It is 0.1 to 100 parts by weight, preferably 0.5 to 70 parts by weight. If the amount is less than 0.1 part by weight, a sufficient antibacterial and antifungal function is not exhibited, and it is difficult to obtain a long-term effect. Also,
If it exceeds 70 parts by weight, it is not desirable from the viewpoint of cost.
【００５０】本発明における抗菌防黴剤を含有する繊維
状物質と併用される繊維の少なくとも３０％は針葉樹パ
ルプや広葉樹パルプ、レーヨン等の吸水性繊維が好まし
い。In the present invention, at least 30% of the fibers used in combination with the fibrous substance containing the antibacterial and fungicide are preferably water-absorbing fibers such as softwood pulp, hardwood pulp and rayon.
【００５１】本発明における抗菌防黴剤を含有する繊維
状物質を他の併用される各種繊維と混抄して使用する場
合、必要に応じて、各種の繊維状バインダーを用いるこ
とができる。When the fibrous substance containing the antibacterial and antifungal agent of the present invention is mixed with other various fibers to be used, various fibrous binders can be used if necessary.
【００５２】本発明に用いられる繊維状バインダーは、
芯鞘タイプ（コアシェルタイプ）、並列タイプ（サイド
バイサイドタイプ）などの複合繊維が挙げられる。例え
ば、ポリプロピレン（芯）とポリエチレン（鞘）の組み
合わせ（商品名：ダイワボウＮＢＦ−Ｈ：大和紡績社
製）、ポリプロピレン（芯）とエチレンビニルアルコー
ル（鞘）の組み合わせ（商品名：ダイワボウＮＢＦ−
Ｅ：大和紡績社製）、ポリプロピレン（芯）とポリエチ
レン（鞘）の組み合わせ（商品名：チッソＥＳＣ：チッ
ソ社製）、高融点ポリエステル（芯）と低融点ポリエス
テル（鞘）の組み合わせ（商品名：メルテイ４０８０：
ユニチカ社製）などが挙げられる。また、ビニロンバイ
ンダー繊維（ＶＰＢ１０７×１：クラレ社製）などの熱
水溶融タイプなども使用できる。The fibrous binder used in the present invention is:
Composite fibers such as a core-sheath type (core-shell type) and a side-by-side type (side-by-side type) are exemplified. For example, a combination of polypropylene (core) and polyethylene (sheath) (trade name: Daiwabo NBF-H: manufactured by Daiwa Spinning Co.), a combination of polypropylene (core) and ethylene vinyl alcohol (sheath) (trade name: Daiwabo NBF-)
E: Daiwa Spinning Co., Ltd.), a combination of polypropylene (core) and polyethylene (sheath) (trade name: Chisso ESC: made by Chisso), a combination of high melting polyester (core) and low melting polyester (sheath) (trade name: Melty 4080:
Unitika). Further, a hot water melting type such as vinylon binder fiber (VPB107 × 1: manufactured by Kuraray Co., Ltd.) can also be used.
【００５３】繊維状のバインダーの繊維径は特に限定さ
れないが、０．３〜５デニールであることが好ましく、
より好ましくは１〜２デニールである。The fiber diameter of the fibrous binder is not particularly limited, but is preferably from 0.3 to 5 deniers.
More preferably, it is 1-2 denier.
【００５４】良好な引張り強度、折り適性を抄造段階で
付与させるために繊維状のバインダーを配合することに
より、不織布の内部強度を強くでき、抄造後の接着剤の
付与工程、スリット工程でテンションが加わった際に起
こり易い断紙や、スリット工程、プリーツ加工工程でこ
すられた時に起こり易い面剥けを抑える役割を果たす。By adding a fibrous binder in order to impart good tensile strength and foldability at the papermaking stage, the internal strength of the nonwoven fabric can be increased, and the tension can be reduced in the adhesive applying step and the slitting step after the papermaking. It plays a role in suppressing the paper breakage that easily occurs when it is applied, and the surface peeling that easily occurs when it is rubbed in the slitting process and the pleating process.
【００５５】本発明における抗菌防黴剤を含有する繊維
状物質を使用した湿式不織布を湿式抄紙法で製造する
際、地合を良好にするためには、各種繊維をパルパーな
どの分散タンク内で分散水に均一に分散する必要があ
り、そのために界面活性剤を用いることが望ましい。In producing a wet nonwoven fabric using a fibrous substance containing an antibacterial and fungicide in the present invention by a wet papermaking method, in order to improve the formation, various fibers are placed in a dispersion tank such as a pulper. It is necessary to disperse uniformly in the dispersion water, and it is desirable to use a surfactant for that purpose.
【００５６】界面活性剤は、アニオン系、カチオン系、
ノニオン系、両性に分類される。アニオン系界面活性剤
としては、例えば、カルボン酸塩、硫酸エステル塩、ス
ルホン酸塩、リン酸エステル塩などが挙げられる。カチ
オン系界面活性剤としては、アミン塩、アンモニウム塩
などが挙げられる。ノニオン系界面活性剤としては、エ
ーテル型、エステル型、アミノエーテル型などが挙げら
れる。両性界面活性剤としては、ベタイン型などが挙げ
られる。The surfactant may be anionic, cationic,
Nonionic and amphoteric. Examples of the anionic surfactant include a carboxylate, a sulfate, a sulfonate, and a phosphate. Examples of the cationic surfactant include an amine salt and an ammonium salt. Examples of the nonionic surfactant include an ether type, an ester type, and an amino ether type. Examples of the amphoteric surfactant include a betaine type.
【００５７】均一に混合分散した繊維の分散安定性を向
上させるために、アニオン性のポリアクリルアミド系粘
剤を繊維分散液、または抄紙ヘッドに添加することによ
り、湿式抄造後のシートの地合はさらに向上する。In order to improve the dispersion stability of the uniformly mixed and dispersed fibers, an anionic polyacrylamide-based thickener is added to the fiber dispersion or the papermaking head to form a sheet after wet papermaking. Further improve.
【００５８】本発明の抗菌防黴剤と吸着剤を含有する湿
式不織布は、一般紙や湿式不織布を製造するための湿式
抄紙機、例えば、長網抄紙機、円網抄紙機、傾斜ワイヤ
ー式抄紙機を単独で１層であっても、同機種同士、異機
種を組み合わせた２層以上の多層であっても良い。又、
抄紙機のワイヤーに水不透過部分を設けて抄くことによ
り、孔を開けて水はけ性をコントロールすることもでき
る。特に不織布を積層で使用する場合には速やかに下層
の不織布まで液体が浸透するので好ましい。The wet nonwoven fabric containing the antibacterial antifungal agent and the adsorbent of the present invention is a wet paper machine for producing general paper and wet nonwoven fabric, for example, fourdrinier paper machine, circular net paper machine, inclined wire paper machine. The machine may be a single layer, or may be a multilayer of two or more layers of the same model or a combination of different models. or,
By providing a water-impermeable portion on the wire of the paper machine and making the paper, it is possible to control the drainage property by making holes. In particular, when the nonwoven fabric is used in the form of a laminate, the liquid quickly penetrates to the lower nonwoven fabric, which is preferable.
【００５９】乾燥には、シリンダードライヤー、エアー
ドライヤー、赤外線ドライヤーなどの乾燥機を用いるこ
とが可能である。また、水はけ性を改良させるために、
孔あけ加工を施しても良い。For drying, a dryer such as a cylinder dryer, an air dryer and an infrared dryer can be used. Also, to improve drainage,
Drilling may be performed.
【００６０】シリンダードライヤーでの乾燥時に不織布
を弛ませたクレープ状にすると見かけの表面積が増える
ので保持出来る液体や臭気の吸収性が増大し、好まし
い。It is preferable to make the non-woven fabric into a crepe shape in which the non-woven fabric is slackened at the time of drying with a cylinder dryer, since the apparent surface area increases and the absorbability of the liquid and odor that can be retained increases.
【００６１】本発明の抗菌防黴剤と吸着剤を含有する不
織布は、取り扱いのし易さなどの用途により、さらに強
度、腰を向上させるために、液体の吸収性を損なわない
範囲で各種バインダーを付与することが可能である。The nonwoven fabric containing the antibacterial antifungal agent and the adsorbent of the present invention can be used in various binders within the range not impairing the liquid absorbability in order to further improve strength and stiffness depending on applications such as easy handling. Can be provided.
【００６２】バインダーとしては、例えば、アクリル系
ラテックス、酢ビ系ラテックス、ウレタン系ラテック
ス、エポキシ系ラテックス、ポリエステル系ラテック
ス、ＳＢＲ系ラテックス、ＮＢＲ系ラテックス、エポキ
シ系バインダー、フェノール系バーンダー、ＰＶＡ、デ
ンプン、一般的に製紙工程で使用される紙力剤などが挙
げられ、これらを単独、もしくは架橋剤と併用して使用
できる。Examples of the binder include acrylic latex, vinyl acetate latex, urethane latex, epoxy latex, polyester latex, SBR latex, NBR latex, epoxy binder, phenol burner, PVA, starch, Examples include paper strength agents generally used in papermaking processes, and these can be used alone or in combination with a crosslinking agent.
【００６３】本発明の抗菌防黴剤と吸着剤を含有する不
織布の目付は特に限定しないが、加工のしやすさ、使い
やすさからは１５〜５００ｇ／ｍ2が一般的であり、好
ましくは２０〜３００ｇ／ｍ2である。使用に際して適
当に不織布を重ねての使用が吸水性の点で好ましい。The basis weight of the nonwoven fabric containing the antibacterial and antifungal agent of the present invention and the adsorbent is not particularly limited, but is generally 15 to 500 g / m 2 from the viewpoint of ease of processing and ease of use. 20 to 300 g / m 2 . In use, it is preferable to use an appropriately laminated nonwoven fabric from the viewpoint of water absorption.
【００６４】また、本発明の有機化合物の金属塩よりな
る抗菌防黴剤と接着剤としての高分子化合物と混合した
組成物を不織布に塗布か含浸することも可能である。接
着剤は市販の各種水溶性高分子化合物や水不溶性高分子
化合物が使用される。It is also possible to apply or impregnate a nonwoven fabric with a composition obtained by mixing an antibacterial fungicide comprising a metal salt of an organic compound of the present invention with a polymer compound as an adhesive. As the adhesive, various commercially available water-soluble polymer compounds and water-insoluble polymer compounds are used.
【００６５】水不溶性高分子化合物としては、ウレタン
系高分子化合物、スチレン−ブタジェン系高分子化合
物、アクリル系高分子化合物、アクリロニトリル−ブタ
ジェン系高分子化合物、エステル系高分子化合物、スチ
レン系高分子化合物、アミド系高分子化合物、塩化ビニ
ル系化合物、酢酸ビニル系化合物、フッソ系化合物、シ
リコン系化合物、エチレン系高分子化合物やプロピレン
系高分子化合物等のオレフィン系高分子化合物等が挙げ
られる。Examples of the water-insoluble polymer compound include urethane polymer compounds, styrene-butadiene polymer compounds, acrylic polymer compounds, acrylonitrile-butadiene polymer compounds, ester polymer compounds, and styrene polymer compounds. And amide-based polymer compounds, vinyl chloride-based compounds, vinyl acetate-based compounds, fluorine-based compounds, silicon-based compounds, and olefin-based polymer compounds such as ethylene-based polymer compounds and propylene-based polymer compounds.
【００６６】水溶性高分子化合物としてはポリビニルア
ルコール系、デンプン系、ポリ酢酸ビニル系、ポリエチ
レンオキサイド、変性セルロース等が挙げられる。Examples of the water-soluble polymer compound include polyvinyl alcohol-based, starch-based, polyvinyl acetate-based, polyethylene oxide, and modified cellulose.
【００６７】水不溶性高分子化合物に自己乳化性を付与
したり、乳化剤で水に分散させたものを乾燥した場合に
は膜の不連続部分が発生しやすく、抗菌防黴剤のような
異種のものを加えた場合には特に顕著であり、その不連
続部分より抗菌防黴剤の成分が移動しやすくなり、良好
な抗菌防黴性が発現すると予想される。When a self-emulsifying property is imparted to a water-insoluble polymer compound, or when a material dispersed in water with an emulsifier is dried, a discontinuous portion of the film is liable to occur, and different types of materials such as antibacterial and fungicides are used. It is particularly remarkable when a compound is added, and it is expected that the components of the antibacterial and antifungal agent will easily migrate from the discontinuous portion and that good antibacterial and antifungal properties will be exhibited.
【００６８】特に、好ましい自己乳化型の水不溶性高分
子化合物としては、ウレタン系高分子化合物、スチレン
−ブタジェン系高分子化合物、アクリル系高分子化合物
である。Particularly preferred self-emulsifying water-insoluble polymer compounds are urethane polymer compounds, styrene-butadiene polymer compounds, and acrylic polymer compounds.
【００６９】抗菌防黴剤に付与する接着剤量は、抗菌防
黴剤固形分に対して８０重量％未満が好ましい。８０重
量％を超えると、接着性は強くなるものの抗菌防黴性が
低下する。The amount of the adhesive provided to the antibacterial and fungicide is preferably less than 80% by weight based on the solid content of the antibacterial and fungicide. If it exceeds 80% by weight, the adhesiveness is increased but the antibacterial and antifungal properties are reduced.
【００７０】本発明における抗菌防黴剤の組成物には必
要に応じて各種の顔料、染料等を混合することが出来
る。Various pigments, dyes and the like can be mixed into the antibacterial and fungicide composition of the present invention, if necessary.
【００７１】本発明における抗菌防黴剤の組成物の作成
例として銀、銅、亜鉛の複合系の抗菌防黴剤およびポリ
ウレタン系高分子化合物について述べる。一例として、
自己乳化型ポリウレタン系高分子化合物を使った例を用
いて説明する。 １）水１００ｇを用意する。 ２）硝酸銀０．１ｍｏｌ相当量を添加する。 ３）硫酸銅０．０５ｍｏｌ相当量を添加する。 ４）硝酸亜鉛０．１ｍｏｌ相当量を添加する。 ５）室温下で十分に撹拌する。 ６）２−メルカプトピリジン−Ｎ−オキシドナトリウム
塩の０．４ｍｏｌ／ｌ液１０００ｇを撹拌しながら少し
ずつ添加する。銀電極もしくは白金電極を用いて、電位
計測すると、反応終了点を検知することができる。 ７）添加終了後、３０分間撹拌し、十分に反応させる。 ８）自己乳化型ポリウレタン系高分子化合物の４０重量
％水分散液を２００ｇ添加する。As an example of preparing the composition of the antibacterial and fungicide of the present invention, a complex antibacterial and fungicide of silver, copper and zinc and a polyurethane polymer compound will be described. As an example,
A description will be given using an example using a self-emulsifying polyurethane polymer compound. 1) Prepare 100 g of water. 2) Add 0.1 mol equivalent of silver nitrate. 3) Add 0.05 mol equivalent of copper sulfate. 4) Add an amount equivalent to 0.1 mol of zinc nitrate. 5) Stir well at room temperature. 6) 1000 g of a 0.4 mol / l solution of 2-mercaptopyridine-N-oxide sodium salt is added little by little with stirring. When the potential is measured using a silver electrode or a platinum electrode, the reaction end point can be detected. 7) After completion of the addition, the mixture is stirred for 30 minutes to be sufficiently reacted. 8) 200 g of a 40% by weight aqueous dispersion of a self-emulsifying polyurethane polymer compound is added.
【００７２】上記の手順により、本発明における抗菌防
黴剤組成物Ｄであるメルカプトピリジン−Ｎ−オキシド
の銀塩、銅塩および亜鉛塩と水不溶性高分子化合物より
なる分散液が得られる。そのままの液状でも抗菌防黴剤
組成物の塗料として不織布に含浸、塗布等が可能であ
る。According to the above procedure, a dispersion comprising a silver salt, a copper salt and a zinc salt of mercaptopyridine-N-oxide, which is the antibacterial and fungicide composition D of the present invention, and a water-insoluble polymer compound is obtained. Even when the liquid is used as it is, it can be impregnated and applied to the nonwoven fabric as a paint for the antibacterial and antifungal composition.
【００７３】本発明における抗菌防黴剤の不織布単位面
積当たりの含有量は、抗菌防黴剤の組成によるが、一般
的には０．０５ｇ／ｍ2以上であり、０．１ｇ／ｍ2以上
が好ましい。[0073] content per nonwoven unit area of the antibacterial antifungal agent according to the present invention, depending on the composition of the antimicrobial antifungal agent, generally at 0.05 g / m 2 or more, 0.1 g / m 2 or more Is preferred.
【００７４】抗菌防黴剤が０．０５ｇ／ｍ2より少ない
と使用の初期から充分な抗菌性、防黴性が得られにく
い。抗菌防黴性の必要持続期間により適宜含有量を選択
出来るが、数日以上の使用では０．１ｇ／ｍ2以上が必
要である。If the amount of the antibacterial and antifungal agent is less than 0.05 g / m 2 , it is difficult to obtain sufficient antibacterial and antifungal properties from the beginning of use. The content can be appropriately selected depending on the required duration of the antibacterial and antifungal properties, but when used for several days or more, 0.1 g / m 2 or more is required.
【００７５】本発明における抗菌防黴剤の組成物は、作
成したものをそのまま不織布に塗布又は含浸しても良い
が、抗菌防黴剤の組成物の安定性向上や接着性を高める
ために、塗布する前に各種接着剤を付与することや着色
のための少量の顔料や染料の付与も可能である。The composition of the antibacterial and antifungal agent of the present invention may be applied or impregnated as it is to the nonwoven fabric. However, in order to improve the stability and adhesiveness of the composition of the antibacterial and antifungal agent, It is also possible to apply various adhesives before application and to apply a small amount of pigment or dye for coloring.
【００７６】本発明における抗菌防黴剤の組成物を含浸
又は塗布する不織布は、カード法等による乾式不織布、
スパンボンド、メルトブローン等による不織布、湿式不
織布、及びそれらのスパンレース加工不織布が使用され
る。The nonwoven fabric impregnated with or coated with the antibacterial and fungicidal composition of the present invention may be a dry nonwoven fabric by a card method or the like.
Nonwoven fabrics, wet nonwoven fabrics, and spunlace nonwoven fabrics thereof made of spunbond, meltblown, or the like are used.
【００７７】使用される不織布の目付は特に制限は無い
が、２０〜５００ｇ／ｍ2が一般的であり、好ましくは
２０〜３００ｇ／ｍ2である。The basis weight of the nonwoven fabric used is not particularly limited, but is generally 20 to 500 g / m 2 , preferably 20 to 300 g / m 2 .
【００７８】本発明の脱臭抗菌シートの作成方法の一例
を挙げると、抗菌防黴剤と吸着剤を含有する、伸縮率１
０〜２０％でクレープ加工された、５０〜１００ｇ／ｍ
2の２枚の不織布の間に吸水性ポリマーを加熱エンボス
加工により封入したシートと抗菌防黴剤と吸着剤を含有
する、伸縮率１０〜２０％でクレープ加工された、３０
〜６０ｇ／ｍ2の１〜４枚の不織布を重ね合わせ、上下
に液体透過性のシートと液体不透過性のシートを重ねて
両端部の全面に加熱エンボス加工で一体化した後、適当
な長さでヒートシール、切断して脱臭抗菌シートを作成
する。吸水性ポリマー封入シートを液体透過性のシート
側にする方が瞬間吸水性から好ましい。One example of the method for producing the deodorized antibacterial sheet of the present invention is as follows.
50-100 g / m creped at 0-20%
2 , containing a sheet in which a water-absorbing polymer is encapsulated between two nonwoven fabrics by heating embossing, an antibacterial fungicide and an adsorbent, and creped at a stretch ratio of 10 to 20%.
1 to 4 nonwoven fabrics of up to 60 g / m 2 are stacked, a liquid-permeable sheet and a liquid-impermeable sheet are stacked on top and bottom, and integrated by heating embossing over the entire surface at both ends, and then the appropriate length is applied. Then heat seal and cut to create a deodorizing antibacterial sheet. It is preferable to make the water-absorbing polymer-enclosed sheet a liquid-permeable sheet side from the viewpoint of instantaneous water absorption.
【００７９】吸水性ポリマー封入する時や液体透過性の
シートと液体不透過性のシートの間に不織布を入れて一
体化する時の加熱エンボス加工での温度は、不織布やシ
ートに使用する繊維や樹脂で異なるが、８０〜２００℃
程度が一般的である。The temperature of the heat embossing when enclosing the water-absorbent polymer or when integrating the nonwoven fabric between the liquid-permeable sheet and the liquid-impermeable sheet depends on the fiber used for the nonwoven fabric and the sheet. 80-200 ° C, depending on resin
The degree is common.
【００８０】本発明の脱臭抗菌シートに適当な間隔で超
音波加熱器等で部分的に溶着することによりしわや不織
布の偏りを防止出来るので好ましい。It is preferable to partially weld the deodorant antibacterial sheet of the present invention at an appropriate interval with an ultrasonic heater or the like because wrinkles and unevenness of the nonwoven fabric can be prevented.
【００８１】本発明では、吸水性ポリマーの近隣に抗菌
防黴剤が存在するので吸水性ポリマーが吸収した尿と接
触している抗菌防黴剤の水可溶成分が尿中へ溶出して菌
類の繁殖を抑えるために臭いの発生が少なくなるが、更
に近辺に存在する吸着剤が一部で発生した臭いを吸着す
るので脱臭効果が大きくなると予想される。In the present invention, since the antibacterial and fungicide is present in the vicinity of the water-absorbing polymer, the water-soluble component of the antibacterial and fungicide in contact with the urine absorbed by the water-absorbing polymer elutes into the urine, and Although the generation of odor is reduced in order to suppress the propagation of the odor, the deodorizing effect is expected to be increased since the adsorbent present in the vicinity further adsorbs the odor generated partially.
【００８２】本発明の脱臭抗菌シートの用途として好ま
しくは人の介護用シートとして使用される場合であり、
臭気を抑え、患者の不快感を軽減するものである。The deodorant antibacterial sheet of the present invention is preferably used as a sheet for human care,
It reduces odor and reduces patient discomfort.
【００８３】本発明の脱臭抗菌シートの用途として好ま
しくは動物用シートとして使用される場合であり、臭気
や黴を抑え、動物に付着した液体が飛散するのを軽減す
るものである。The deodorant antibacterial sheet of the present invention is preferably used as an animal sheet, which suppresses odors and molds and reduces the scattering of liquid adhering to animals.
【００８４】[0084]
【実施例】以下に実施例を挙げて本発明を具体的に説明
するが、本発明は実施例に限定されるものではない。な
お、実施例中の「部」および「％」は、それぞれ「重量
部」および「重量％」を示す。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the examples. In the examples, “parts” and “%” indicate “parts by weight” and “% by weight”, respectively.
【００８５】製造例Ａ 前記の発明の実施の形態の記載に準じて、カルボキシメ
チル基置換度０．２２（ＤＳ＝０．２２）の変性ＮＢＫ
Ｐに、銀／２−メルカプトピリジン−Ｎ−オキシドより
なる抗菌防黴剤を含有する繊維状物質を作製した（以
下、ＣＰ２２ＡｇＭＰと略記する）。即ち、上記の変性
ＮＢＫＰ分散液（固形分１０００ｇ）に硝酸銀０．５ｍ
ｏｌを加え、ｐＨを５．５に調節してから、３０分間撹
拌する。０．１Ｍ／ｌの２−メルカプトピリジン−Ｎ−
オキシドナトリウム液を、変性ＮＢＫＰ分散液に加えら
れた硝酸銀と等モル相当量を添加した。３０分間撹拌し
てから、硫酸でｐＨを４まで下げた後、脱水した。脱水
パルプに、再び５００ｍｌの水を加え、撹拌水洗して脱
水した。これを、銀／２−メルカプトピリジン−Ｎ−オ
キシドよりなる抗菌防黴剤を含有するカルボキシメチル
基置換度０．２２（ＤＳ＝０．２２）の変性ＮＢＫＰと
した。Production Example A Modified NBK having a carboxymethyl group substitution degree of 0.22 (DS = 0.22) according to the description of the above embodiment of the invention.
For P, a fibrous substance containing an antibacterial and fungicide composed of silver / 2-mercaptopyridine-N-oxide was prepared (hereinafter abbreviated as CP22AgMP). That is, 0.5 m of silver nitrate was added to the above-mentioned modified NBKP dispersion (solid content: 1000 g).
and adjust the pH to 5.5, then stir for 30 minutes. 0.1 M / l 2-mercaptopyridine-N-
The sodium oxide solution was added in an equimolar amount to the silver nitrate added to the modified NBKP dispersion. After stirring for 30 minutes, the pH was lowered to 4 with sulfuric acid and then dehydrated. 500 ml of water was again added to the dehydrated pulp, and the mixture was washed with stirring water and dehydrated. This was used as modified NBKP having a carboxymethyl group substitution degree of 0.22 (DS = 0.22) containing an antibacterial and fungicide composed of silver / 2-mercaptopyridine-N-oxide.
【００８６】比較例１で使用する不織布 ２ｍ3 の分散タンクにアクリル酸ソーダ系アニオン性界
面活性剤（日本アクリル化学社製、プライマル８５０）
を全繊維に対して１％になるように添加し、ＮＢＫＰ
（カナダ標準濾水度４８０ｍｌ）、高叩解ＮＢＫＰ（カ
ナダ標準濾水度２００ｍｌ）、ポリエステル繊維（２デ
ニール×５ｍｍ：帝人社製）、水中溶解温度が７０℃の
ビニロンバインダー繊維（ＶＰＢ１０７；１デニール×
３ｍｍ：クラレ社製）を各々６０：５：３０：５の比率
で配合し、合成アルミノ珪酸亜鉛（水沢化学工業社製、
ミズカナイトＡ）を全繊維に対して２０％になるように
添加し、分散濃度０．２％で３０分間分散した後、乾燥
重量で６０g/ｍ2 になるように円網抄紙機で抄紙後、表
面温度１３０℃のシリンダードライヤーで乾燥、クレー
プ加工（伸縮率１０％）して比較例１で使用する湿式不
織布を作製した。同様にして乾燥重量が３０ｇ／ｍ2の
湿式不織布を作製した。In a dispersion tank of 2 m 3 of the non-woven fabric used in Comparative Example 1, sodium acrylate-based anionic surfactant (Primal 850, manufactured by Nippon Acrylic Chemicals, Inc.)
Is added so as to be 1% with respect to all fibers, and NBKP is added.
(Canada standard freeness: 480 ml), high-beaten NBKP (Canada standard freeness: 200 ml), polyester fiber (2 denier x 5 mm: manufactured by Teijin Limited), vinylon binder fiber having a water dissolution temperature of 70 ° C (VPB107; 1 denier x)
3mm: manufactured by Kuraray Co., Ltd.) in a ratio of 60: 5: 30: 5, respectively, and synthetic zinc aluminosilicate (manufactured by Mizusawa Chemical Industry Co., Ltd.)
Mizucanite A) was added so as to be 20% with respect to all the fibers, dispersed at a dispersion concentration of 0.2% for 30 minutes, and then paper-dried to a dry weight of 60 g / m 2 by a round paper machine. The wet nonwoven fabric used in Comparative Example 1 was prepared by drying with a cylinder dryer having a surface temperature of 130 ° C. and creping (10% expansion and contraction). Similarly, a wet nonwoven fabric having a dry weight of 30 g / m 2 was prepared.
【００８７】実施例１〜５で使用する不織布 比較例１のＮＢＫＰの一部を、上記製造例Ａで得られた
本発明における繊維状物質であるＣＰ２２ＡｇＭＰに、
表１記載の配合量で置き換えた外は、比較例１で使用す
る不織布と同様にして、実施例１〜５で抗菌防黴剤と吸
着剤を含有する不織布として使用する、乾燥重量が６０
ｇ／ｍ2と３０ｇ／ｍ2の湿式不織布を作製した。A portion of the NBKP of the nonwoven fabric of Comparative Example 1 used in Examples 1 to 5 was added to CP22AgMP which is the fibrous substance of the present invention obtained in Production Example A above.
Except for replacing with the compounding amount shown in Table 1, in the same manner as the nonwoven fabric used in Comparative Example 1, the nonwoven fabric containing the antibacterial and antifungal agent and the adsorbent in Examples 1 to 5 was used.
g / m 2 and 30 g / m 2 wet nonwoven fabrics were produced.
【００８８】製造例Ｂ 製造例Ａと同様であるが、前記の発明の実施の形態の記
載に準じて、ＣＰ２２ＡｇＭＰの代わりに、カルボキシ
メチル基置換度０・４０（ＤＳ＝０・４０）の変性ＮＢ
ＫＰに（銀、銅、亜鉛）／２−メルカプトピリジン−Ｎ
−オキシドよりなる抗菌防黴剤を含有する繊維状物質を
作製した（以下、ＣＰ４０Ａｇ２５Ｃｕ２５Ｚｎ５０Ｍ
Ｐと略記する。なお、金属原子の次の数字は、モル％比
を表わす）。即ち、上記の変性ＮＢＫＰ分散液（固形分
１０００ｇ）に硝酸銀０．２５ｍｏｌ、硫酸銅０．２５
ｍｏｌ、硝酸亜鉛０．５ｍｏｌを加え、ｐＨを５．５に
調節してから、３０分間撹拌する。０．１Ｍ／ｌの２−
メルカプトピリジン−Ｎ−オキシドナトリウム液を、
１．７５ｍｏｌ相当量を添加した。３０分間撹拌してか
ら、硫酸でｐＨを４まで下げた後、脱水した。脱水パル
プに、再び５００ｍｌの水を加え、撹拌水洗して脱水
し、ＣＰ４０Ａｇ２５Ｃｕ２５Ｚｎ５０ＭＰを得た。Preparation Example B The same as Preparation Example A, but according to the description of the above-mentioned embodiment of the invention, instead of CP22AgMP, modification with a carboxymethyl group substitution degree of 0.40 (DS = 0.40) NB
KP with (silver, copper, zinc) / 2-mercaptopyridine-N
A fibrous material containing an antibacterial and antifungal agent composed of an oxide was prepared (hereinafter referred to as CP40Ag25Cu25Zn50M).
Abbreviated as P. In addition, the number next to the metal atom represents a mol% ratio). That is, 0.25 mol of silver nitrate and 0.25 mol of copper sulfate were added to the above-mentioned modified NBKP dispersion (solid content: 1000 g).
mol and 0.5 mol of zinc nitrate, adjust the pH to 5.5, and then stir for 30 minutes. 0.1 M / l 2-
Mercaptopyridine-N-oxide sodium solution,
1.75 mol equivalent was added. After stirring for 30 minutes, the pH was lowered to 4 with sulfuric acid and then dehydrated. To the dehydrated pulp, 500 ml of water was added again, washed with stirring water, and dehydrated to obtain CP40Ag25Cu25Zn50MP.
【００８９】実施例６〜１０で使用する不織布 比較例１のＮＢＫＰの一部を、上記製造例Ｂで得られた
本発明における繊維状物質であるＣＰ４０Ａｇ２５Ｃｕ
２５Ｚｎ５０ＭＰに、表１記載の配合量で置き換えた外
は、比較例１と同様にして、実施例６〜１０で抗菌防黴
剤と吸着剤を含有する不織布として使用する、乾燥重量
が６０ｇ／ｍ2と３０ｇ／ｍ2の湿式不織布を作製した。Nonwoven fabric used in Examples 6 to 10 A part of the NBKP of Comparative Example 1 was replaced with the fibrous substance CP40Ag25Cu of the present invention obtained in Production Example B above.
25Zn50MP, except that it was replaced by the compounding amount shown in Table 1, in the same manner as in Comparative Example 1, and used as a nonwoven fabric containing an antibacterial antifungal agent and an adsorbent in Examples 6 to 10, having a dry weight of 60 g / m2. Wet nonwoven fabrics of 2 and 30 g / m 2 were prepared.
【００９０】製造例Ｃ 前記の発明の実施の形態の記載に準じて、銀／２−メル
カプトピリジン−Ｎ−オキシドを含有させた、有機化合
物の金属塩よりなる抗菌防黴剤とウレタン系高分子化合
物とアクリル系高分子化合物を含む抗菌防黴剤の組成物
を作製した（以下、ＡｇＭＰ−ＵＡ０．３と略記す
る）。即ち、水に硝酸銀０．１ｍｏｌを加え、攪拌す
る。０．１ｍｏｌ／ｌの２−メルカプトピリジン−Ｎ−
オキシドナトリウム液を、加えられた硝酸銀と等モル相
当量を添加し、３０分間撹拌する。これに自己乳化型ウ
レタン系高分子化合物（大日本インキ化学工業社製、ハ
イドランＨＷ−３５０）の水分散液を加え、５分間攪拌
した後、同重量の自己架橋型アクリル系高分子化合物
（大日本インキ化学工業社製、ボンコート３２５６）の
水分散液を加え、銀／２−メルカプトピリジン−Ｎ−オ
キシドの抗菌防黴剤のウレタン系高分子化合物に対する
重量比を０．３とした。尚、括弧内金属原子の次の数字
は、モル％比を表わし、最後尾の数字は水不溶性高分子
化合物に対する抗菌防黴剤の重量比を表わす。Production Example C An antibacterial fungicide comprising a metal salt of an organic compound containing silver / 2-mercaptopyridine-N-oxide and a urethane-based polymer according to the description of the above embodiment of the invention A composition of an antibacterial and fungicide containing the compound and the acrylic polymer compound was prepared (hereinafter, abbreviated as AgMP-UA0.3). That is, 0.1 mol of silver nitrate is added to water and stirred. 0.1 mol / l 2-mercaptopyridine-N-
The sodium oxide solution is added in an equimolar amount to the added silver nitrate and stirred for 30 minutes. To this was added an aqueous dispersion of a self-emulsifying urethane polymer compound (Hydran HW-350, manufactured by Dainippon Ink and Chemicals, Inc.), and the mixture was stirred for 5 minutes. An aqueous dispersion of Boncoat 3256) manufactured by Nippon Ink Chemical Industry Co., Ltd. was added, and the weight ratio of the antibacterial and antifungal agent of silver / 2-mercaptopyridine-N-oxide to the urethane polymer was 0.3. The number following the metal atom in the parenthesis indicates the mole% ratio, and the last number indicates the weight ratio of the antibacterial and fungicide to the water-insoluble polymer compound.
【００９１】製造例Ｄ 製造例Ｃと同様であるが、前記の発明の実施の形態の記
載に準じて、ＡｇＭＰ−ＵＡ０．３の代わりに、（銀、
銅、亜鉛）／２−メルカプトピリジン−Ｎ−オキシドの
抗菌防黴剤を含有した自己乳化型ウレタン系高分子化合
物（ハイドランＨＷ−３５０）と自己架橋型アクリル系
高分子化合物（ボンコート３２５６）の水分散液を作製
した。即ち、硝酸銀０．２５ｍｏｌ、硫酸銅０．２５ｍ
ｏｌ、硝酸亜鉛０．５ｍｏｌ及びそれらの総モル相当量
である１．７５ｍｏｌの２−メルカプトピリジン−Ｎ−
オキシドナトリウム水溶液を添加、攪拌し、自己乳化型
ウレタン系高分子化合物水分散液を添加、攪拌後、同重
量の自己架橋型アクリル系化合物水分散液を添加、攪拌
して、（銀、銅、亜鉛）／２−メルカプトピリジン−Ｎ
−オキシドの抗菌防黴剤と自己乳化型ウレタン系高分子
化合物と自己架橋型アクリル系高分子化合物との重量比
を０．３とした（以下、Ａｇ２５Ｃｕ２５Ｚｎ５０ＭＰ
−ＵＡ０．３と略記する）。尚、括弧内金属原子の次の
数字は、モル％比を表わし、最後尾の数字は水不溶性高
分子化合物に対する抗菌防黴剤の重量比を表す。Production Example D The same as Production Example C, but according to the description of the above-mentioned embodiment of the invention, instead of AgMP-UA0.3, (silver,
Water of a self-emulsifying urethane polymer (Hydran HW-350) and a self-crosslinking acrylic polymer (Boncoat 3256) containing an antibacterial and fungicidal agent of (copper, zinc) / 2-mercaptopyridine-N-oxide A dispersion was prepared. That is, 0.25 mol of silver nitrate and 0.25 m of copper sulfate
ol, 0.5 mol of zinc nitrate and 1.75 mol of 2-mercaptopyridine-N-
An aqueous sodium oxide solution is added and stirred, a self-emulsifying aqueous urethane polymer compound aqueous dispersion is added, and after stirring, an aqueous dispersion of the same weight of a self-crosslinking acrylic compound is added and stirred (silver, copper, Zinc) / 2-mercaptopyridine-N
-The weight ratio of the antibacterial antifungal agent of the oxide, the self-emulsifying urethane polymer and the self-crosslinking acrylic polymer was 0.3 (hereinafter, Ag25Cu25Zn50MP)
-UA0.3). The number following the metal atom in the parenthesis indicates the mole% ratio, and the last number indicates the weight ratio of the antibacterial and fungicide to the water-insoluble polymer compound.
【００９２】実施例１１、１２で使用する不織布 ５デニールのポリアクリル繊維５０重量％と６デニール
のポリエチレン−ポリプロピレン複合繊維５０重量％か
らなる混合ウエブを熱処理した乾式不織布（目付６０ｇ
／ｍ2、厚さ３００μｍ）に上記製造例Ｃ、Ｄで得られ
た本発明の抗菌防黴剤の組成物を抗菌防黴剤が５ｇ／ｍ
2の乾燥塗布量になるようにサイズプレス装置で含浸
し、１１０℃で乾燥して実施例１１、１２で使用する抗
菌防黴剤と吸着剤を含有する不織布を得た。尚、塗布適
性を向上させるために抗菌防黴剤の組成物にセルロース
エーテル（信越化学工業社製、メトローズＳＨ３０００
０）水溶液を適量添加して含浸した。以下の実施例、比
較例でも同様にしてセルロースエーテルを必要に応じて
適量添加して含浸した。Dry nonwoven fabric (60 g weight per unit area) obtained by heat-treating a mixed web composed of 50% by weight of 5 denier polyacrylic fiber and 50% by weight of 6 denier polyethylene-polypropylene composite fiber used in Examples 11 and 12
/ M 2 , thickness of 300 μm) and the composition of the antibacterial and fungicide of the present invention obtained in the above Production Examples C and D was added at 5 g / m2.
It was impregnated with a size press so that the dry coating amount was 2 and dried at 110 ° C. to obtain a nonwoven fabric containing the antibacterial fungicide and the adsorbent used in Examples 11 and 12. In order to improve the coating suitability, the composition of the antibacterial and fungicide was added to cellulose ether (manufactured by Shin-Etsu Chemical Co., Ltd., Metroose SH3000).
0) An appropriate amount of an aqueous solution was added for impregnation. In the following Examples and Comparative Examples, cellulose ether was similarly added in an appropriate amount as necessary and impregnated.
【００９３】実施例１３で使用する不織布 実施例１２で使用する不織布の製造で、Ａｇ２５Ｃｕ２
５Ｚｎ５０ＭＰ−ＵＡ０．３の代わりに、塩化ベンザル
コニウム含有アクリル系高分子化合物（ボンコート３２
５６）を使用して塩化ベンザルコニウムの含浸量が５ｇ
／ｍ2になるように含浸、乾燥して実施例１３で使用す
る抗菌防黴剤と吸着剤を含有する不織布を得た。なお、
塩化ベンザルコニウム含有アクリル系高分子化合物は、
製造例Ｃで用いた自己乳化型ウレタン系高分子化合物と
自己架橋型アクリル系高分子化合物を固形で１０ｇに対
して、０.１ｍｏｌ/ｌの塩化ベンザルコニウム液１２０
ｍｌを加え、ｐＨ５.５に調整後、撹拌して作製した。The nonwoven fabric used in Example 13 The production of the nonwoven fabric used in Example 12 was carried out using Ag25Cu2
Instead of 5Zn50MP-UA0.3, benzalkonium chloride-containing acrylic polymer compound (Boncoat 32
56) using 5 g of benzalkonium chloride
/ M 2 , and dried to obtain a nonwoven fabric containing the antibacterial fungicide and the adsorbent used in Example 13. In addition,
Benzalkonium chloride-containing acrylic polymer compound,
0.1 mol / l of a benzalkonium chloride solution 120 per 10 g of the self-emulsifying urethane polymer compound and the self-crosslinking acrylic polymer compound used in Production Example C
The mixture was adjusted to pH 5.5, stirred, and prepared.
【００９４】比較例２で使用する不織布 実施例１１で用いた乾式不織布（目付６０ｇ／ｍ2、厚
さ３００μｍ）を何も含浸しないでそのままで比較例２
の不織布とした。Non-woven fabric used in Comparative Example 2 The dry non-woven fabric (having a basis weight of 60 g / m 2 and a thickness of 300 μm) used in Example 11 was used without any impregnation.
Nonwoven fabric.
【００９５】比較例３で使用する不織布 実施例１１で得られた抗菌防黴剤を含浸した不織布上に
ポリエチレン−酢酸ビニル系バインダー粒子（平均粒子
経２０μｍ）を３０ｇ／ｍ２散布、赤外線ヒーターで１
２０℃に加熱後比較例１で使用する不織布を載せて加圧
して比較例３で使用する不織布を作製した。Nonwoven fabric used in Comparative Example 3 The nonwoven fabric impregnated with the antibacterial and fungicide obtained in Example 11 was sprayed with 30 g / m2 of polyethylene-vinyl acetate binder particles (average particle diameter: 20 μm),
After heating to 20 ° C., the nonwoven fabric used in Comparative Example 1 was placed thereon and pressurized to produce a nonwoven fabric used in Comparative Example 3.
【００９６】実施例１１〜１３で使用する不織布と比較
例２で使用する不織布上に吸着剤（ミズカナイトＭ）と
ポリエチレン−酢酸ビニル系バインダー粒子（平均粒子
径２０μｍ）の重量比１０：２０の混合物を３０ｇ／ｍ
2散布、赤外線ヒーターで１２０℃に加熱後各々に実施
例１１〜１３で使用する不織布と比較例２で使用する不
織布を載せて加圧して実施例１１〜１３、比較例２で使
用する抗菌防黴剤と吸着剤を含有する不織布を作製し
た。Mixture of adsorbent (Mizukanite M) and polyethylene-vinyl acetate binder particles (average particle diameter 20 μm) at a weight ratio of 10:20 on the nonwoven fabric used in Examples 11 to 13 and the nonwoven fabric used in Comparative Example 2. 30 g / m
(2) Spraying, heating to 120 ° C. with an infrared heater, the nonwoven fabric used in Examples 11 to 13 and the nonwoven fabric used in Comparative Example 2 were placed on each of them and pressurized, and the antibacterial protection used in Examples 11 to 13 and Comparative Example 2 was applied. A nonwoven fabric containing a fungicide and an adsorbent was prepared.
【００９７】実施例１〜１３、及び比較例１〜４ ポリプロピレン製乾式不織布（目付１５ｇ／ｍ2）、と
ポリエチレン製フルム（目付１５ｇ／ｍ2）の縦４２ｃ
ｍ×横６２ｃｍの長方形シートを重ねて、その３辺をヒ
ートシールして内寸が４１ｃｍ×６１ｃｍの袋（以下袋
Ａと記す）を作製した。実施例１〜１０、比較例１で使
用する目付６０ｇ／2の不織布２枚の間に吸水性ポリマ
ー（アクリル系、平均粒子径１００μｍ）を３０ｇ／ｍ
2全面に散布した後１１０℃エンボス加工により一体化
してシートにした。袋Ａの中に前記の吸水性ポリマーを
封入して一体化した４０ｃｍ×６０ｃｍのシート１枚と
実施例１〜１０で使用する目付３０ｇ／ｍ2の不織布４
０ｃｍ×６０ｃｍを４枚入れて４辺の端部（幅１．５ｃ
ｍ）を１２０℃ヒートシール加工して実施例１〜１０の
脱臭抗菌シートを得た。実施例１１〜１３で使用する抗
菌防黴剤と吸着剤を含有する不織布、比較例２で使用す
る吸着剤を含有する不織布および比較例３で使用する抗
菌防黴剤を含有する不織布各々２枚の間に吸水性ポリマ
ー（架橋ポリアクリル酸ソーダ系、平均粒子径１０μ
ｍ）を３０ｇ／ｍ2全面に散布した後エンボス加工によ
り一体化してシートにした。袋Ａの中に前記の吸水性ポ
リマーを封入して一体化した４０ｃｍ×６０ｃｍのシー
ト１枚と実施例１１〜１３で使用する抗菌防黴剤と吸着
剤を含有した不織布４０ｃｍ×６０ｃｍを２枚を入れて
４辺の端部（幅１．５ｃｍ）を１２０℃ヒートシール加
工して実施例１１〜１３の脱臭抗菌シートを得た。同様
にして比較例１で使用する、目付６０ｇ／ｍ2の不織布
の間に吸水性ポリマーを封入して一体化した４０ｃｍ×
６０ｃｍのシート１枚と比較例１で使用する目付３０ｇ
／ｍ2の不織布４０ｃｍ×６０ｃｍを４枚を袋Ａに入れ
て４辺の端部（幅１．５ｃｍ）を１２０℃ヒートシール
加工して比較例１の脱臭抗菌シートを得た。同様にして
比較例２で使用する不織布の間に吸水性ポリマーを封入
して一体化した４０ｃｍ×６０ｃｍのシート１枚と比較
例２で使用する不織布４０ｃｍ×６０ｃｍを２枚袋Ａに
入れて４辺の端部（幅１．５ｃｍ）を１２０℃ヒートシ
ール加工して比較例２の脱臭抗菌シートを得た。同様に
して比較例３で使用する吸水性ポリマーを封入して一体
化した４０ｃｍ×６０ｃｍのシート１枚と比較例３で使
用する不織布４０ｃｍ×６０ｃｍを２枚袋Ａに入れて４
辺の端部（幅１．５ｃｍ）を全面に１２０℃ヒートシー
ル加工して比較例３の脱臭抗菌シートを得た。比較例４
は実施例１１で使用する抗菌防黴剤と吸着剤を含有した
目付６０ｇ／ｍ2の不織布２枚の間に吸水性ポリマー３
０ｇ／ｍ2を散布しただけでエンボス加工せずに使用
し、抗菌防黴剤と吸着剤を含有した目付３０ｇ／ｍ2の
不織布を４枚と共に袋Ａに入れて４辺の端部（幅１．５
ｃｍ）を１２０℃ヒートシール加工して比較例４の脱臭
抗菌シートを得た。Examples 1 to 13 and Comparative Examples 1 to 4 Length 42c of dry nonwoven fabric made of polypropylene (having a basis weight of 15 g / m 2 ) and polyethylene film (having a basis weight of 15 g / m 2 )
A rectangular sheet measuring mx 62 cm in width was overlaid, and three sides thereof were heat-sealed to produce a bag having an inner size of 41 cm x 61 cm (hereinafter referred to as bag A). 30 g / m of a water-absorbing polymer (acrylic, average particle diameter 100 μm) between two nonwoven fabrics having a basis weight of 60 g / 2 used in Examples 1 to 10 and Comparative Example 1
2 After spraying the entire surface, the sheet was integrated by embossing at 110 ° C to form a sheet. One sheet of 40 cm × 60 cm in which the above-mentioned water-absorbing polymer is sealed and integrated in the bag A and the nonwoven fabric 4 having a basis weight of 30 g / m 2 used in Examples 1 to 10
Insert 4 pieces of 0cm × 60cm and the edge of 4 sides (width 1.5c
m) was heat-sealed at 120 ° C. to obtain deodorized antibacterial sheets of Examples 1 to 10. Nonwoven fabric containing the antibacterial fungicide and the adsorbent used in Examples 11 to 13, nonwoven fabric containing the adsorbent used in Comparative Example 2, and nonwoven fabric containing the antibacterial fungicide used in Comparative Example 3 each two Between water-absorbing polymer (crosslinked sodium polyacrylate, average particle size 10μ)
m) was sprayed over the entire surface at 30 g / m 2 and then integrated by embossing to form a sheet. One sheet of 40 cm × 60 cm in which the above-mentioned water-absorbing polymer is sealed and integrated in the bag A, and two sheets of nonwoven fabric 40 cm × 60 cm containing the antibacterial antifungal agent and the adsorbent used in Examples 11 to 13 And the four edges (width 1.5 cm) were heat-sealed at 120 ° C. to obtain deodorant antibacterial sheets of Examples 11 to 13. Similarly, a water-absorbing polymer was sealed between the nonwoven fabrics having a basis weight of 60 g / m 2 and used in Comparative Example 1, and 40 cm ×
One sheet of 60 cm and a basis weight of 30 g used in Comparative Example 1
/ M 2 nonwoven fabric of 40 cm × 60 cm was put in bag A, and the four edges (width 1.5 cm) were heat-sealed at 120 ° C. to obtain a deodorant antibacterial sheet of Comparative Example 1. Similarly, one 40 cm × 60 cm sheet in which a water-absorbing polymer is sealed and integrated between the nonwoven fabrics used in Comparative Example 2 and two nonwoven fabrics 40 cm × 60 cm used in Comparative Example 2 are placed in bag A. The end of the side (width 1.5 cm) was heat-sealed at 120 ° C. to obtain a deodorant antibacterial sheet of Comparative Example 2. Similarly, one sheet of 40 cm × 60 cm integrated with the water-absorbing polymer used in Comparative Example 3 and the nonwoven fabric of 40 cm × 60 cm used in Comparative Example 3 were placed in bag A, and
The end (width 1.5 cm) of the side was heat-sealed at 120 ° C. over the entire surface to obtain a deodorant antibacterial sheet of Comparative Example 3. Comparative Example 4
Is a water-absorbing polymer 3 between two 60 g / m 2 nonwoven fabrics containing the antibacterial fungicide and the adsorbent used in Example 11.
0 g / m 2 was sprayed but not embossed. Four non-woven fabrics having a basis weight of 30 g / m 2 containing an antibacterial and antifungal agent and an adsorbent were put into bag A together with four sheets, and the four edges (width) 1.5
cm) was heat-sealed at 120 ° C. to obtain a deodorant antibacterial sheet of Comparative Example 4.
【００９８】前記の実施例１〜１０で使用する抗菌防黴
剤と吸着剤を含有する不織布、実施例１１〜１３で使用
する抗菌防黴剤を含有する不織布、および比較例１〜４
で使用する不織布について、抗菌性を測定した。得られ
た結果を表１および表２に示す。The nonwoven fabric containing the antibacterial fungicide and the adsorbent used in Examples 1 to 10, the nonwoven fabric containing the antibacterial fungicide used in Examples 11 to 13, and Comparative Examples 1 to 4
The antibacterial property of the nonwoven fabric used in the above was measured. The obtained results are shown in Tables 1 and 2.
【００９９】実施例１〜１３、及び比較例１〜４で得ら
れた脱臭抗菌シートの脱臭性を犬の尿で評価した。得ら
れた結果を表１および表２に示す。The deodorizing antibacterial sheets obtained in Examples 1 to 13 and Comparative Examples 1 to 4 were evaluated for their deodorizing properties using dog urine. The obtained results are shown in Tables 1 and 2.
【０１００】実施例１〜１３、及び比較例１〜４で得ら
れた脱臭抗菌シートのウエットバック性を純水で評価し
た。得られた結果を表１および表２に示す。The deodorized antibacterial sheets obtained in Examples 1 to 13 and Comparative Examples 1 to 4 were evaluated for wetback properties with pure water. The obtained results are shown in Tables 1 and 2.
【０１０１】＜抗菌性＞大腸菌（Ｅ−ｃｏｌｉ ＩＦ０
３３０１）を液体培地（ペプトン・イースト）で２４時
間前培養し、希釈して２×１０8セル／ｍｌの試験液を
調整した。上記実施例および比較例で使用する不織布の
試験片２ｃｍ×２ｃｍを用意し、水道水で流水水洗後、
それぞれをペトリ皿上に配置し、上記試験液を５滴（約
０．１ｍｌ）滴下し、乾燥しないようにカバーをして３
８℃で２４時間経時した。経時後、試験片のそれぞれを
Ｎｕｔｒｉｅｎｔ Ｂｒｏｔｈ寒天培地上に押し当て、
試験片上の菌を転写させて剥離し、３８℃で２４時間培
養し、観察した。評価は、次のとおりとした。 評価グレード −− ほぼ完全に殺菌し、菌の成育がない。 − ２ｃｍ×２ｃｍ転写面に５コロニー以下の成育
はあるが、殆ど完全に殺菌。 ＋ ２ｃｍ×２ｃｍ転写面に100コロニー以下で良
好な抗・殺菌作用。 ＋＋ ２ｃｍ×２ｃｍ転写面に効果は認められるが、
弱いか、少ない。 ＋＋＋ ２ｃｍ×２ｃｍ転写面に実質的効果なし。<Antibacterial Property> E. coli IF0
3301) was pre-cultured for 24 hours in a liquid medium (peptone yeast) and diluted to prepare a test solution of 2 × 10 8 cells / ml. Prepare a test piece 2 cm x 2 cm of the non-woven fabric used in the above Examples and Comparative Examples, and wash it with running tap water,
Each was placed on a Petri dish, and 5 drops (approximately 0.1 ml) of the above test solution was dropped.
It was aged at 8 ° C. for 24 hours. After aging, each of the test pieces was pressed onto Nutrient Broth agar medium,
The bacteria on the test piece were transferred, peeled, cultured at 38 ° C. for 24 hours, and observed. The evaluation was as follows. Evaluation grade --- Almost completely sterilized, with no growth of bacteria. -There is growth of 5 colonies or less on the transfer surface of 2 cm x 2 cm, but almost completely sterilized. + Good anti-bacterial effect with less than 100 colonies on the 2cm x 2cm transfer surface. ++ 2cm × 2cm Although the effect is recognized on the transfer surface,
Weak or less. ++++ 2cm × 2cm No substantial effect on transfer surface.
【０１０２】＜犬尿での脱臭性＞実施例１〜１３、比較
例１〜３で得られた脱臭抗菌シートについて、各々４０
ｃｍ×３０ｃｍに切断して２枚の試験シートを作成し
た。一方の試験シートの中心部に犬の尿を各２０ｍｌし
み込ませ、ポリエチレン製ビニール袋に入れて３８℃、
２４時間静置した。他方の試験シートも同様にポリエチ
レン製ビニール袋に入れて同様に３８℃、２４時間静置
した。各試験シートについて２０名が下記の評価グレー
ドで脱臭性を評価し、その平均を最終評価とした。未処
理シートは全て○であった。 評価グレード ○ 臭い無し ○〜△ 殆ど臭い無し △ やや臭い有り × 臭い多い<Deodorizing property in dog urine> The deodorizing antibacterial sheets obtained in Examples 1 to 13 and Comparative Examples 1 to 3 were each subjected to 40
Two test sheets were prepared by cutting into cm × 30 cm. 20 ml of dog urine was impregnated into the center of one of the test sheets and placed in a polyethylene plastic bag at 38 ° C.
It was left standing for 24 hours. The other test sheet was similarly placed in a polyethylene plastic bag and left at 38 ° C. for 24 hours. For each test sheet, 20 persons evaluated the deodorizing properties according to the following evaluation grades, and the average was used as the final evaluation. All untreated sheets were ○. Evaluation grade ○ No odor ○ 〜 △ Almost no odor △ Some odor × Many odor
【０１０３】＜ウエットバック性＞実施例１〜１３、比
較例１〜４の脱臭抗菌シートの液体透過性不織布側を上
にして置き、半径５ｃｍの円内に純水５ｇを吸収させ
る。１０秒後に重量を測定した濾紙（５Ｃ；東洋濾紙社
製、１１ｃｍ径）を載せ、ポリ塩化ビニル板を介して１
０ｋｇの重りを載せて１分後に重りとポリ塩化ビニル板
を取り除いて濾紙の重量を測定する。試験前後の濾紙の
重量から吸水量を算出する。少ない方が良。<Wet back property> The deodorizing antibacterial sheets of Examples 1 to 13 and Comparative Examples 1 to 4 were placed with the liquid-permeable nonwoven fabric side facing upward, and 5 g of pure water was absorbed in a circle having a radius of 5 cm. After 10 seconds, a filter paper (5C; manufactured by Toyo Roshi Kaisha, Ltd., 11 cm diameter) whose weight was measured was placed on the filter paper, and placed on a polyvinyl chloride plate via a polyvinyl chloride plate.
One minute after placing a 0 kg weight, the weight and the polyvinyl chloride plate are removed, and the weight of the filter paper is measured. The amount of water absorption is calculated from the weight of the filter paper before and after the test. Less is better.
【０１０４】[0104]
【表１】 [Table 1]
【０１０５】[0105]
【表２】 [Table 2]
【０１０６】表１および表２の結果から、次のことが解
る。From the results in Tables 1 and 2, the following can be understood.
【０１０７】製造例Ａに記載した抗菌防黴剤（ＣＰ２２
ＡｇＭＰ）を含む本発明における繊維状物質を、不織布
の構成繊維の一つであるＮＢＫＰの一部に置き換えて使
用した実施例１〜５の場合、抗菌防黴剤を含まない比較
例１に比べて、抗菌性および犬尿での脱臭性とも優れて
いた。。その配合量は、５部置き換えで効果が認めら
れ、置き換え量が増えるに従って効果は大きくなる。効
果は２０部以上の置き換えで完全な抗菌性が得られる結
果である。The antibacterial fungicide described in Production Example A (CP22
In the case of Examples 1 to 5 in which the fibrous substance of the present invention containing AgMP) was replaced with a part of NBKP which is one of the constituent fibers of the nonwoven fabric, compared with Comparative Example 1 which did not contain the antibacterial and fungicide. Also, it was excellent in antibacterial property and deodorizing property in dog urine. . With respect to the compounding amount, an effect is recognized by replacing 5 parts, and the effect increases as the replacing amount increases. The effect is the result of obtaining complete antimicrobial properties by replacing 20 parts or more.
【０１０８】製造例Ｂに記載した抗菌防黴剤（ＣＰ４０
Ａｇ２５Ｃｕ２５Ｚｎ５０ＭＰ）を含む本発明における
繊維状物質を、不織布の構成繊維の一つであるＮＢＫＰ
の一部に置き換えて使用した実施例６〜１０の場合、抗
菌防黴剤を含まない比較例１に比べて、抗菌性および犬
尿での脱臭性に効果が有ることが解った。その配合量
は、５部置き換えでも充分に効果が認められ、１０部以
上で完全な抗菌性が得られる結果であり、製造例Ａの抗
菌防黴剤（ＣＰ２２ＡｇＭＰ）よりも少量でも効果の有
る結果であった。The antibacterial fungicide described in Production Example B (CP40
Ag25Cu25Zn50MP) of the present invention containing NBKP, one of the constituent fibers of the nonwoven fabric.
It was found that in the case of Examples 6 to 10 which were used by substituting a part of the above, there was an effect on the antibacterial property and the deodorizing property in dog urine as compared with Comparative Example 1 not containing the antibacterial and fungicide. A sufficient effect is observed even when 5 parts are replaced, and complete antibacterial properties are obtained when 10 parts or more are used, and a result in which even a smaller amount than the antibacterial antifungal agent of Production Example A (CP22AgMP) is effective. Met.
【０１０９】製造例Ｃ，Ｄで得られた抗菌防黴剤と水不
溶性高分子化合物からなる抗菌防黴剤組成物を不織布に
含浸した実施例１１、１２は、抗菌防黴剤の乾燥重量は
５．０ｇ／ｍ2である。水不溶性高分子化合物に対する
抗菌防黴剤の重量比が同じ０．３の銀系の抗菌防黴剤使
用の実施例１１は、銀、銅、亜鉛系抗菌防黴剤使用の実
施例１２と比較して明らかに抗菌性、犬尿での脱臭性は
劣っている結果であった。実施例１３は抗菌防黴剤とし
て塩化ベンザルコニウムを使用しており、実施例１１よ
りも更に抗菌性、犬尿での脱臭性が劣っており、実使用
で効果の得られる下限であった。抗菌防黴剤を使用して
いない比較例２は抗菌性、犬尿での脱臭性は無い結果で
あった。In Examples 11 and 12 in which the nonwoven fabric was impregnated with the antibacterial fungicide composition comprising the antibacterial fungicide obtained in Production Examples C and D and a water-insoluble polymer compound, the dry weight of the antibacterial fungicide was as follows. It is 5.0 g / m 2 . Example 11 using a silver-based antibacterial and fungicide having the same 0.3 weight ratio of the antibacterial and fungicide to the water-insoluble polymer compound was compared with Example 12 using a silver, copper and zinc-based antibacterial and fungicide. As a result, the antibacterial property and the deodorizing property in dog urine were inferior. Example 13 used benzalkonium chloride as an antibacterial and antifungal agent, and was inferior to Example 11 in antibacterial properties and inferior in deodorization in dog urine, and was a lower limit at which an effect was obtained in actual use. . Comparative Example 2, which did not use an antibacterial and fungicide, showed antibacterial properties and no deodorizing properties in dog urine.
【０１１０】比較例３は実施例１１で吸着剤を使用しな
い場合であるが、犬尿での脱臭性は、吸着剤が無いため
に液体中での菌の繁殖は殆ど抑えられるが、尿中の一部
の繁殖や固体状の排出物内部の菌の繁殖は抑えられず、
脱臭性は実施例１１より比較例３の方が劣る結果になっ
たと予想される。Comparative Example 3 is a case where the adsorbent is not used in Example 11, but the deodorizing property in dog urine is almost suppressed by the absence of the adsorbent. Breeding of bacteria and the breeding of bacteria inside solid effluent cannot be suppressed,
It is expected that Comparative Example 3 was inferior to Example 11 in terms of deodorization.
【０１１１】実施例１〜１０、比較例１はウエットバッ
ク性はすべて良好であり、実施例１１〜１３、比較例
２、３では、乾式不織布を使用していることと、不織布
の積層に用いたバインダー粒子の影響でウエットバック
性は低下した。In Examples 1 to 10 and Comparative Example 1, the wet-back properties were all good, and in Examples 11 to 13 and Comparative Examples 2 and 3, the dry nonwoven fabric was used and the The wet back property was reduced due to the influence of the binder particles.
【０１１２】比較例４は実施例１１で吸水性ポリマーを
エンボス加工しないで散布しただけの場合であるが、使
用する不織布の抗菌性は実施例１１と同等であるが、犬
尿での脱臭性は吸水性ポリマーと抗菌防黴剤との間隔が
広がった事や吸水性ポリマーが動きやすく偏在しやすい
事により悪くなっている。ウエットバック性も吸水性ポ
リマーが偏在しやすいので劣った。Comparative Example 4 is a case where the water-absorbing polymer was sprayed without embossing in Example 11, but the nonwoven fabric used has the same antibacterial properties as Example 11, but has a deodorizing property in dog urine. This is worsened because the distance between the water-absorbing polymer and the antibacterial and antifungal agent is widened and the water-absorbing polymer is easily moved and unevenly distributed. The wet-back property was also inferior because the water-absorbing polymer was easily unevenly distributed.
【０１１３】[0113]
【発明の効果】本発明に使用される抗菌防黴剤と吸着剤
を含有した不織布間に吸水性ポリマーを加熱エンボス加
工で一体化したシートと抗菌防黴剤を含有した不織布と
を封入した袋は抗菌性、脱臭性、ウエットバック性が良
好である。エンボス加工により吸水性ポリマーを覆って
いる不織布に含有されている抗菌防黴剤と吸水性ポリマ
ーが近接しているので吸水性ポリマーが吸収した尿中へ
抗菌防黴剤の一部が溶出して菌類の繁殖をおさえやすく
なっているためと予想される。又、吸着剤は、初期の臭
いを吸着するほかに一部の抗菌防黴剤と接触していない
尿中で菌類の繁殖により臭いの有るガスが発生した場合
に吸着する効果が有ると予想される。特に犬等のペット
に使用した場合には脱臭性に対する効果は良好である。
特に含窒素複素環か硫黄原子を含有する有機化合物の金
属塩である抗菌防黴剤を含有した繊維状物質を使用した
場合や抗菌防黴剤と水不溶性高分子化合物との組成物を
含有した不織布を使用した場合は抗菌性、脱臭性に効果
が大きい。また、本発明において、抗菌防黴剤を含有し
て最も効果的に機能を発揮する繊維状物質は、セルロー
ス系繊維の部分変性物がカルボキシメチル変性されたも
のである。このような繊維状物質よりなるパルプを用い
ると、パルプを構成するセルロース繊維中に高密度で充
填できるので、極めて抗菌防黴剤含有量の高いパルプが
得られ、優れた効果を発揮する。金属塩として銀、銅、
亜鉛塩を組み合わせて使用すると、連続して長期に抗菌
性や防黴性効果等を発揮する。その理由は、各金属塩は
水溶解度が異なるのでそれらの組み合わせで連続して効
果を発揮できる為と予想される。抗菌防黴剤と水不溶性
高分子化合物よりなる抗菌防黴剤組成物の場合は耐久性
をそれらの重量比や種類により好ましく設計することが
できる。According to the present invention, a bag in which a sheet in which a water-absorbing polymer is integrated by heating and embossing between a nonwoven fabric containing an antibacterial fungicide and an adsorbent and a nonwoven fabric containing an antibacterial fungicide is used. Has good antibacterial properties, deodorizing properties, and wetback properties. Since the antibacterial agent contained in the nonwoven fabric covering the water-absorbing polymer by embossing and the water-absorbing polymer are close to each other, some of the antibacterial agent is eluted into the urine absorbed by the water-absorbing polymer. It is expected that the growth of fungi is easier to control. In addition, the adsorbent is expected to have the effect of adsorbing the initial odor and also adsorbing odorous gas generated by the growth of fungi in urine that has not been in contact with some antibacterial and fungicide agents. You. Particularly when used for pets such as dogs, the effect on deodorization is good.
Especially when a fibrous substance containing an antibacterial fungicide which is a metal salt of an organic compound containing a nitrogen-containing heterocyclic ring or a sulfur atom is used, or a composition of an antibacterial fungicide and a water-insoluble polymer compound is contained. When a nonwoven fabric is used, it has a great effect on antibacterial properties and deodorizing properties. In the present invention, the fibrous substance containing an antibacterial and fungicide and exhibiting the most effective function is a substance obtained by modifying a partially modified cellulosic fiber with carboxymethyl. When pulp made of such a fibrous substance is used, the pulp can be filled at a high density into the cellulose fibers constituting the pulp, so that pulp having an extremely high antibacterial and fungicide content can be obtained, and excellent effects can be exhibited. Silver, copper,
When a zinc salt is used in combination, the antibacterial and antifungal effects are exhibited continuously for a long time. The reason is expected to be that each metal salt has a different solubility in water, so that the combination thereof can exert an effect continuously. In the case of an antibacterial fungicide composition comprising an antibacterial fungicide and a water-insoluble polymer compound, durability can be preferably designed by their weight ratio and type.
Claims (9)
も２枚の不織布の間に吸水性ポリマーを熱エンボス加工
により封入したシートを液体透過性のシートと液体不透
過性のシートとの間に入れ、少なくとも両端部の全面ヒ
ートシール加工により一体化したものであり、水中へ溶
出する成分により抗菌防黴性が発現することを特徴とす
る脱臭抗菌シート。1. A sheet in which a water-absorbing polymer is sealed by heat embossing between at least two nonwoven fabrics containing an antibacterial fungicide and an adsorbent, between a liquid-permeable sheet and a liquid-impermeable sheet. A deodorizing antibacterial sheet characterized by being integrated by heat sealing at least on both ends thereof, and exhibiting antibacterial and antifungal properties by components that elute into water.
ことを特徴とする請求項１記載の脱臭抗菌シート。2. The deodorizing antibacterial sheet according to claim 1, wherein the antibacterial antifungal agent is a metal salt of an organic compound.
物、メルカプトピリジン−Ｎ−オキシド化合物、イソチ
アゾリン化合物、ベンゾチアゾール化合物もしくはベン
ゾチアゾリン化合物から選ばれる少なくとも１種の化合
物である請求項２記載の脱臭抗菌シート。3. The deodorizing antibacterial sheet according to claim 2, wherein the organic compound is at least one compound selected from a benzimidazole compound, a mercaptopyridine-N-oxide compound, an isothiazoline compound, a benzothiazole compound and a benzothiazoline compound.
も１種を含有することを特徴とする請求項２記載の脱臭
抗菌シート。4. The deodorizing antibacterial sheet according to claim 2, wherein the metal salt contains at least one of a silver salt, a copper salt and a zinc salt.
を特徴とする請求項１記載の脱臭抗菌シート。5. The deodorant antibacterial sheet according to claim 1, wherein the adsorbent is a zeolite compound.
抗菌防黴剤を含有する繊維状物質を含むことを特徴とす
る請求項１記載の脱臭抗菌シート。6. The deodorizing antibacterial sheet according to claim 1, wherein the nonwoven fabric contains a fibrous substance containing an antibacterial and fungicide composed of a metal salt of an organic compound.
する請求項６記載の脱臭抗菌シート。7. The deodorizing antibacterial sheet according to claim 6, wherein the nonwoven fabric is a wet nonwoven fabric.
して使用されることを特徴とする請求項１〜７のいずれ
か１項に記載の脱臭抗菌シート。8. The deodorizing antibacterial sheet according to any one of claims 1 to 7, wherein the deodorizing antibacterial sheet is used as a sheet for human care.
使用されることを特徴とする請求項１〜７のいずれか１
項に記載の脱臭抗菌シート。9. The sheet according to claim 1, wherein the deodorizing antibacterial sheet is used as an animal sheet.
The deodorant antibacterial sheet according to the item.