JPH0859918A - Phenolic resin composition - Google Patents

Abstract

PURPOSE: To obtain the subject composition having flame resistance, heat resistance, antistatic performance, etc., without deteriorating excellent properties such as moldability, flexibility and electric properties which are characteristic to polypropylene by melting and kneading the polypropylene with a powdery phenolic resin cured material. CONSTITUTION: This resin composition is obtained by melting and kneading (A) 100pts.wt. of polypropylene with (B) 5-50 pts.wt. of a powdery phenolic resin cured material (preferably, having an acetone-extraction rate of <10% and particle diameters of 1-100μm). Further, a preferable example of the component B is a material obtained by heating and curing a mixture obtained by compounding a phenolic novolak resin with a curing agent and/or a material obtained by thermosetting a resol-type phenolic resin. Heating temperature is preferably 100-180 deg.C for producing the cured material having cured structure whose acetone-extraction rate is <10%.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、ポリプロピレンの持っ
ている熱可塑性樹脂としての特性を損う事なく、かつフ
ェノール樹脂の優れた特長を活かして、良好な難燃性、
耐熱性、耐衝撃性、塗装性および制電性など与えるフェ
ノール樹脂組成物に関するもので、射出成形等により得
られる各種成形品、押出し成形等により得られる用途に
対して有用である。[Field of Industrial Application] The present invention does not impair the characteristics of polypropylene as a thermoplastic resin, and makes good use of the excellent characteristics of phenol resin, and has good flame retardance,
The present invention relates to a phenol resin composition that provides heat resistance, impact resistance, paintability, antistatic property, etc., and is useful for various molded articles obtained by injection molding and the like, and applications obtained by extrusion molding and the like.

【０００２】[0002]

【従来の技術】一般にポリプロピレンは、ポリエチレン
に比べて成形性が優れ、成形品の外観が良好であるが、
次の様な欠点がある。 （１）衝撃強度の温度依存性が大で、室温から０℃まで
の間に衝撃強度が急激に低下する。 （２）スチレン系樹脂、塩化ビニルなどと比較して、剛
性が不足している。 （３）透明性の不足。 （４）燃えやすい。 （５）紫外線により劣化しやすい。 （６）帯電しやすい。 （７）塗装、メッキ、蒸着などの二次加工性の不良。 （８）染色性不良 これに対して、幾つかの改良が行われている。2. Description of the Related Art Generally, polypropylene is superior in moldability to polyethylene and has a good appearance of molded articles.
It has the following drawbacks. (1) The impact strength has a large temperature dependency, and the impact strength sharply decreases from room temperature to 0 ° C. (2) Rigidity is insufficient as compared with styrene resin, vinyl chloride and the like. (3) Lack of transparency. (4) Easy to burn. (5) It is easily deteriorated by ultraviolet rays. (6) Easily charged. (7) Poor secondary workability such as painting, plating, vapor deposition. (8) Poor dyeability There have been some improvements made.

【０００３】例えば、低温における耐衝撃強度の改良と
して、エチレンとのブロックコポリマーが検討され、射
出成形用として大型雑貨、家庭電気製品、自動車部品お
よびコンテナなどの各種の分野に使用されている。ま
た、剛性の改良としてガラス繊維、タルクなどの各種無
機質充填材を添加する事で、剛性がポリスチレンと同等
もしくはそれ以上の製品が出来ている。不燃化の検討と
して、塩素化パラフィン、三酸化アンチモンおよび芳香
族系ハロゲン化合物による不燃グレードがあるが、不燃
化剤の価格が高い事および安全衛生上などに問題が残さ
れている。ポリプロピレンはポリエチレンと同様極めて
優れた絶縁抵抗を有しているが、一方この長所が帯電し
やすい原因となっている。そこで、帯電防止のためポリ
ビニルアルコールを始め各種の帯電防止剤が検討されて
いるが、耐老化性、価格、加工時の熱安定性などの問題
がある。For example, block copolymers with ethylene have been studied for improving impact resistance at low temperatures, and have been used in various fields such as large sundries, household electric appliances, automobile parts and containers for injection molding. In addition, by adding various inorganic fillers such as glass fiber and talc to improve rigidity, products with rigidity equal to or higher than polystyrene can be made. There are nonflammable grades made of chlorinated paraffin, antimony trioxide and aromatic halogen compounds as a nonflammable material, but there are problems such as high price of nonflammable agents and safety and hygiene. Polypropylene, like polyethylene, has an extremely excellent insulation resistance, but on the other hand, this advantage is a cause of being easily charged. Therefore, various antistatic agents such as polyvinyl alcohol have been studied to prevent static electricity, but there are problems such as aging resistance, cost, and thermal stability during processing.

【０００４】[0004]

【発明が解決しようとする課題】本発明はポリプロピレ
ンの持つ優れた特性の低下をほとんどまねくことなく、
ポリプロピレンと粉末状フェノール樹脂硬化物を溶融混
練してなるフェノール樹脂組成物を提供することにあ
る。DISCLOSURE OF THE INVENTION The present invention hardly causes deterioration of the excellent properties of polypropylene,
It is intended to provide a phenol resin composition obtained by melt-kneading polypropylene and a powdery phenol resin cured product.

【０００５】[0005]

【課題を解決するための手段】本発明者らは、長年フェ
ノール樹脂の研究に携わる中、検討した結果耐熱性、難
燃性、帯電性、耐摩耗性などのフェノール樹脂の特長を
付与した、ポリプロピレンと粉末状フェノール樹脂硬化
物を溶融混練してなるフェノール樹脂組成物を得る事が
できた。さらに鋭意検討した結果、粉末状フェノール樹
脂硬化物の内そのアセトン抽出率が１０％未満であり、
かつ粉末の粒径が１〜１００μｍの粉末状フェノール樹
脂硬化物を使用する事で、上記の特性に加えて耐衝撃
性、曲げ強度、帯電性などが向上する事を見出し、本発
明を完成させるに至った。[Means for Solving the Problems] The present inventors have been engaged in research on phenolic resins for many years, and as a result of examination, they have added the characteristics of phenolic resins such as heat resistance, flame retardancy, electrostatic properties and abrasion resistance, A phenol resin composition obtained by melt-kneading polypropylene and a powdery phenol resin cured product could be obtained. As a result of further intensive study, the acetone extraction rate of the powdery phenolic resin cured product was less than 10%,
In addition to the above-mentioned properties, it was found that impact resistance, bending strength, charging property and the like are improved by using a powdery phenol resin cured product having a powder particle size of 1 to 100 μm, and the present invention is completed. Came to.

【０００６】即ち本発明は、ポリプロピレン１００重量
部と粉末状フェノール樹脂硬化物５〜５０重量部を溶融
混練してなるフェノール樹脂組成物に関するものであ
り、好ましくはポリプロピレン１００重量部と粉末状フ
ェノール樹脂硬化物５〜３０重量部を溶融混練してなる
フェノール樹脂組成物、さらに好ましくはポリプロピレ
ン１００重量部と粉末状フェノール樹脂硬化物１０〜２
５重量部を溶融混練してなるフェノール樹脂組成物に関
するものである。ここで、ポリプロピレン１００重量部
に対する粉末状フェノール樹脂硬化物の配合量が５重量
部未満の場合、フェノール樹脂の持つ優れた特長が発現
しない。また、ポリプロピレン１００重量部に対する粉
末状フェノール樹脂硬化物の配合量が５０重量部を越え
た場合には、ポリプロピレンの持つ成形性や成形品の外
観などが損われる。That is, the present invention relates to a phenol resin composition obtained by melt-kneading 100 parts by weight of polypropylene and 5 to 50 parts by weight of a powdered phenol resin cured product, preferably 100 parts by weight of polypropylene and a powdered phenol resin. Phenolic resin composition obtained by melt-kneading 5 to 30 parts by weight of a cured product, more preferably 100 parts by weight of polypropylene and 10 to 2 powdered phenolic resin cured product.
The present invention relates to a phenol resin composition obtained by melt-kneading 5 parts by weight. Here, when the powdered phenolic resin cured product is blended in an amount of less than 5 parts by weight with respect to 100 parts by weight of polypropylene, the excellent characteristics of the phenolic resin are not exhibited. Further, when the amount of the powdery phenolic resin cured product mixed with 100 parts by weight of polypropylene exceeds 50 parts by weight, the moldability of polypropylene and the appearance of the molded product are impaired.

【０００７】また、本発明に使用するフェノール樹脂硬
化物は、粉砕、粉末化し、その粉末の粒径が１〜１００
μｍである事を特徴のひとつとする。ここで、粉末の粒
径が１μｍ未満の場合、極めて微粒のため溶融混練時の
作業性が落ち、粉末の粒径が１００μｍを越えた場合に
は、成形品の外観などが損われる。The phenol resin cured product used in the present invention is pulverized and powdered, and the particle size of the powder is 1 to 100.
One of the features is that it is μm. Here, if the particle size of the powder is less than 1 μm, the workability at the time of melt-kneading is deteriorated because it is extremely fine, and if the particle size of the powder exceeds 100 μm, the appearance of the molded product is impaired.

【０００８】[0008]

【作用】本発明で用いられるポリプロピレンは特に限定
される物でなく一般に市販されているものである。The polypropylene used in the present invention is not particularly limited and is generally commercially available.

【０００９】本発明に用いられる粉末状フェノール樹脂
硬化物を作製する時に使用するフェノール樹脂として
は、ノボラック型フェノール樹脂、レゾール型フェノー
ル樹脂、ベンジリックエーテル型フェノール樹脂などが
挙げられる。これらは、単独および２種以上を混合して
用いることもできる。また、ゴム変性、アルキルベンゼ
ン変性などの各種変性フェノール樹脂も使用する事が出
来る。好ましくは、ノボラック型フェノール樹脂と硬化
剤とを配合し、加熱により硬化させてなる粉末状フェノ
ール樹脂硬化物および／またはレゾール型フェノール樹
脂を加熱または酸により硬化させてなる硬化物である。Examples of the phenol resin used when preparing the powdery phenol resin cured product used in the present invention include novolac type phenol resin, resol type phenol resin and benzylic ether type phenol resin. These may be used alone or in combination of two or more. Further, various modified phenolic resins such as rubber modified and alkylbenzene modified can also be used. Preferably, a powdered phenol resin cured product obtained by mixing a novolac type phenol resin and a curing agent and curing by heating and / or a cured product obtained by curing a resol type phenol resin by heating or an acid.

【００１０】本発明に用いられるノボラック型フェノー
ル樹脂は、フェノール類（Ｐ）とアルデヒド類（Ｆ）を
配合モル比（Ｆ／Ｐ）が０．５〜１．０となる様な配合
比率で反応釜に仕込み、更に樹脂化触媒として塩酸、硫
酸、燐酸、パラトルエンスルフォン酸、ベンゼンスルフ
ォン酸、蓚酸、マレイン酸、蟻酸、酢酸などから選ばれ
た１種または２種以上を添加し、変性樹脂を得る場合は
変性剤を添加した後加熱し、適当な時間還流反応を行っ
た後、反応によって生成した縮合水を除去するため真空
脱水或いは常圧脱水し、更に残っている水と未反応のフ
ェノール類を除去する方法によって得る事が出来る。The novolac type phenol resin used in the present invention is a reaction of phenols (P) and aldehydes (F) in a compounding molar ratio (F / P) of 0.5 to 1.0. A modified resin is charged in a kettle, and one or more kinds selected from hydrochloric acid, sulfuric acid, phosphoric acid, paratoluenesulfonic acid, benzenesulfonic acid, oxalic acid, maleic acid, formic acid, acetic acid, etc. are added as a resinizing catalyst. When it is obtained, it is heated after adding a denaturing agent, and refluxed for an appropriate period of time, and then vacuum dehydration or atmospheric dehydration is performed to remove the condensed water produced by the reaction, and the remaining water and unreacted phenol are removed. It can be obtained by the method of removing the kind.

【００１１】本発明に用いられるレゾール型フェノール
樹脂は、フェノール類（Ｐ）とアルデヒド類（Ｆ）を配
合モル比（Ｆ／Ｐ）が１．０〜２．０となる様な配合比
率で反応釜に仕込み、更に樹脂化触媒として水酸化ナト
リウム、水酸化カリウム、水酸化バリウム、水酸化カル
シウムなどのアルカリ類、アンモニア、トリエチルアミ
ン等のアミン類の中から選ばれた１種または２種以上を
添加し、変性樹脂を得る場合は変性剤を添加した後加熱
し、適当な時間還流反応を行った後、反応によって生成
した縮合水を除去するため真空脱水或いは常圧脱水する
方法によって得る事が出来る。The resol type phenol resin used in the present invention reacts phenols (P) and aldehydes (F) at a compounding ratio such that the compounding molar ratio (F / P) is 1.0 to 2.0. It is charged in a kettle, and one or more kinds selected from alkalis such as sodium hydroxide, potassium hydroxide, barium hydroxide and calcium hydroxide and amines such as ammonia and triethylamine are added as a resin-forming catalyst. However, when a modified resin is obtained, it can be obtained by a method of adding a modifying agent, heating, refluxing for a suitable time, and then vacuum dehydration or atmospheric dehydration to remove condensed water generated by the reaction. .

【００１２】本発明で使用するフェノール樹脂の原料と
なるフェノール類としては、フェノール、オルソクレゾ
ール、メタクレゾール、パラクレゾール、ビスフェノー
ルＡ、ビスフェノールＦ、カテコール、レゾルシン、ハ
イドロキノン、プロピルフェノール、ブチルフェノー
ル、オクチルフェノール、ノニルフェノールなどから選
ばれた１種または２種以上である。アルデヒド類として
は、ホルムアルデヒド、パラホルムアルデヒド、トリオ
キサン、アセトアルデヒドなどが挙げられ、これらの中
から適宜選択して１種または２種以上が用いられる。ま
た、変性剤種としてはアルキルベンゼン（キシレン系樹
脂）、カシューオイル、ロジンなどのテルペン類および
ホウ酸が用いられる。The phenols used as raw materials for the phenol resin used in the present invention include phenol, orthocresol, metacresol, paracresol, bisphenol A, bisphenol F, catechol, resorcin, hydroquinone, propylphenol, butylphenol, octylphenol, nonylphenol. It is 1 type (s) or 2 or more types selected from the like. Examples of the aldehydes include formaldehyde, paraformaldehyde, trioxane, acetaldehyde and the like, and one or two or more kinds are appropriately selected from these. As the modifier species, alkylbenzene (xylene-based resin), cashew oil, terpenes such as rosin, and boric acid are used.

【００１３】本発明に用いられる粉末状フェノール樹脂
硬化物を作製する際の硬化方法としては、代表的には熱
および酸による方法が挙げられるが、特に熱による硬化
方法が好ましい。ノボラック型フェノール樹脂の場合、
ヘキサメチレンテトラミン等の硬化剤を目標とする架橋
構造の程度に合せて、ノボラック型フェノール樹脂１０
０重量部に対して、１〜２０重量部添加混合して硬化さ
せる。As a curing method for producing the powdery phenolic resin cured product used in the present invention, a method using heat and an acid is typically mentioned, and a curing method using heat is particularly preferable. In case of novolac type phenolic resin,
A novolac type phenolic resin 10 is prepared by adjusting the curing agent such as hexamethylenetetramine to the target degree of the crosslinked structure.
1 to 20 parts by weight is added to 0 parts by weight and mixed to cure.

【００１４】本発明において、粉末状フェノール樹脂硬
化物の硬化の程度は、アセトン抽出試験法により測定さ
れるアセトン抽出率の数値で示した。アセトン抽出試験
とは、フェノール樹脂の未硬化分をソックスレー抽出器
を用い、アセトンを溶媒として抽出する方法である。通
常、未硬化のフェノール樹脂はアセトンに溶解するが、
硬化が進むにつれて溶解しなくなる。完全に硬化した粉
末状フェノール樹脂硬化物はアセトンに対して全く溶解
しない。即ち、完全に硬化したフェノール樹脂硬化物は
アセトン抽出率０％となり、フェノール樹脂はアセトン
抽出率１００％なる。In the present invention, the degree of curing of the powdery phenolic resin cured product is shown by the numerical value of the acetone extraction rate measured by the acetone extraction test method. The acetone extraction test is a method of extracting the uncured portion of the phenol resin with a Soxhlet extractor using acetone as a solvent. Normally, uncured phenolic resin dissolves in acetone,
It does not dissolve as the curing progresses. A completely cured powdery phenol resin cured product does not dissolve in acetone at all. That is, the completely cured phenol resin cured product has an acetone extraction rate of 0%, and the phenol resin has an acetone extraction rate of 100%.

【００１５】ノボラック型フェノール樹脂とヘキサメチ
レンテトラミンの混合物およびレゾール型フェノール樹
脂を熱硬化させる際の温度は、目標とする硬化程度によ
り設定する。即ち、アセトン抽出率１０％未満の硬化構
造を有する粉末状フェノール樹脂硬化物を製造する場
合、加熱温度としては１００〜１８０℃が好ましい。The temperature at which the mixture of the novolac type phenol resin and hexamethylenetetramine and the resol type phenol resin are heat-cured is set according to the target degree of curing. That is, when a powdery phenolic resin cured product having a cured structure with an acetone extraction rate of less than 10% is produced, the heating temperature is preferably 100 to 180 ° C.

【００１６】粉末状フェノール樹脂硬化物の粉砕方法と
しては、ハンマーミル、自由ミル、パルペライザー、タ
ーボミル、ジェットミル等を用いる事が出来る。粉末の
粒径は使用する粉砕機により調整する事が出来る。特定
の範囲の粒径の樹脂粉末を得るためには粉砕後、ふるい
を掛けることにより容易に得る事が出来る。この際、粉
砕機への原料の供給速度、粉砕機の回転速度、粉砕機の
スクリーンのメッシュにより得られる粒径が異なってく
る。A hammer mill, a free mill, a pulverizer, a turbo mill, a jet mill or the like can be used for pulverizing the powdery phenol resin cured product. The particle size of the powder can be adjusted by the crusher used. In order to obtain a resin powder having a particle size in a specific range, it can be easily obtained by pulverizing and then sieving. At this time, the feed rate of the raw material to the crusher, the rotation speed of the crusher, and the particle size obtained depend on the mesh of the screen of the crusher.

【００１７】[0017]

【実施例】以下本発明を実施例により詳細に説明する
が、本発明は実施例によって限定されるものではない。
なお、実施例、比較例に記載されている「部」および
「％」は「重量部」および「重量％」を示す。EXAMPLES The present invention will be described in detail below with reference to examples, but the present invention is not limited to the examples.
In addition, "parts" and "%" described in Examples and Comparative Examples indicate "parts by weight" and "% by weight".

【００１８】《フェノール樹脂の合成》 〔合成例１〕撹拌機、熱交換器、温度計の付いた反応装
置にフェノール１，０００部および蓚酸８．０部を仕込
んだ。その後混合液を９０±２℃に昇温させた後、同温
度に保持して、かつ真空度を４４０Ｔｏｒｒに制御しな
がら、アルデヒドタンク内にいれておいた３７％ホルム
アルデヒド水溶液６５０部を３．０時間を要して混合液
に添加し、また添加後は同条件下で３．０時間保って前
段のアルデヒド類接触反応を行った。つづいて前段の反
応液を常圧下で１５０℃まで昇温させた後、真空度を６
０Ｔｏｒｒに保ちながら、液温が２３０℃になるまで昇
温して、残留水分と遊離モノマーを除去する事により、
融点８５℃、遊離モノマー量０．２％のノボラック型フ
ェノール樹脂（Ｂ１）を得た。<< Synthesis of Phenolic Resin >> [Synthesis Example 1] 1,000 parts of phenol and 8.0 parts of oxalic acid were charged in a reactor equipped with a stirrer, a heat exchanger and a thermometer. Then, the temperature of the mixed solution was raised to 90 ± 2 ° C., and while maintaining the same temperature and controlling the degree of vacuum to 440 Torr, 650 parts of the 37% formaldehyde aqueous solution placed in the aldehyde tank was added to 3.0. It was added to the mixed solution over a period of time, and after the addition, the former aldehyde-catalyzed reaction was carried out for 3.0 hours under the same conditions. Subsequently, the temperature of the reaction solution in the first stage was raised to 150 ° C. under normal pressure, and the degree of vacuum was adjusted to 6
By keeping the temperature at 0 Torr and raising the liquid temperature to 230 ° C to remove residual water and free monomers,
A novolac type phenol resin (B1) having a melting point of 85 ° C. and a free monomer amount of 0.2% was obtained.

【００１９】〔合成例２〕合成例１と同型の反応装置に
フェノール１，０００部、３７％ホルムアルデヒド水溶
液１，５１０部および２８％アンモニア水１００部を仕
込んだ。その後混合液を徐々に昇温し、内温８０℃にお
いて１５分間減圧還流を行った。内温５０℃まで冷却後
静置し、分離水を除去した後、６０℃で減圧脱水し、融
点６５℃、遊離モノマー量１％のレゾール型フェノール
樹脂（Ｂ２）を得た。Synthesis Example 2 A reactor of the same type as in Synthesis Example 1 was charged with 1,000 parts of phenol, 1,510 parts of 37% formaldehyde aqueous solution and 100 parts of 28% ammonia water. After that, the temperature of the mixed solution was gradually raised, and the mixture was refluxed under reduced pressure at 80 ° C. for 15 minutes. After cooling to an internal temperature of 50 ° C., the mixture was allowed to stand, the separated water was removed, and the mixture was dehydrated under reduced pressure at 60 ° C. to obtain a resol-type phenol resin (B2) having a melting point of 65 ° C. and a free monomer amount of 1%.

【００２０】《フェノール樹脂硬化物の作製》 〔作製例１〕合成例１で合成したノボラック型フェノー
ル樹脂（Ｂ１）１，０００部とヘキサメチレンテトラミ
ン１００部とを混合粉砕した後、１２０℃で６０分さら
に１６０℃で６０分加熱した。得られたノボラック樹脂
硬化物をハンマーミルで粗粉砕した後、パルペライザー
を用いて微粉砕した。得られた粉末状ノボラック樹脂硬
化物（Ｄ１）の平均粒径は４０μｍであり、アセトン抽
出率は７％であった。<Preparation of Phenolic Resin Cured Product> [Preparation Example 1] 1,000 parts of the novolac-type phenol resin (B1) prepared in Synthesis Example 1 and 100 parts of hexamethylenetetramine were mixed and pulverized, and then the mixture was crushed at 120 ° C. for 60 minutes. Minutes Further heated at 160 ° C. for 60 minutes. The obtained cured novolak resin was roughly pulverized with a hammer mill and then finely pulverized with a palpelizer. The obtained powdery novolac resin cured product (D1) had an average particle size of 40 μm and an acetone extraction rate of 7%.

【００２１】〔作製例２〕合成例１で合成したノボラッ
ク型フェノール樹脂（Ｂ１）１，０００部とヘキサメチ
レンテトラミン１００部とを混合粉砕した後、１１０℃
で２時間さらに１４０℃で９０分加熱した。得られたノ
ボラック樹脂硬化物をハンマーミルで粗粉砕した後、パ
ルペライザーを用いて微粉砕した。得られた粉末状ノボ
ラック樹脂硬化物（Ｄ２）の平均粒径は６０μｍであ
り、アセトン抽出率は９％であった。[Production Example 2] 1,000 parts of the novolac type phenol resin (B1) synthesized in Synthesis Example 1 and 100 parts of hexamethylenetetramine were mixed and pulverized, and then 110 ° C.
Heated for 2 hours at 140 ° C. for 90 minutes. The obtained cured novolak resin was roughly pulverized with a hammer mill and then finely pulverized with a palpelizer. The obtained powdery novolac resin cured product (D2) had an average particle size of 60 μm and an acetone extraction rate of 9%.

【００２２】〔作製例３〕合成例２で合成したレゾール
型フェノール樹脂（Ｂ２）を１５０℃で１時間加熱し
た。得られたレゾール樹脂硬化物をハンマーミルで粗粉
砕した後、パルペライザーを用いて微粉砕した。得られ
た粉末状レゾール樹脂硬化物（Ｄ３）の平均粒径は４５
μｍであり、アセトン抽出率は０．６％であった。[Production Example 3] The resol-type phenol resin (B2) synthesized in Synthesis Example 2 was heated at 150 ° C for 1 hour. The obtained resole resin cured product was roughly pulverized with a hammer mill and then finely pulverized with a palpelizer. The average particle size of the obtained powdery resol resin cured product (D3) is 45.
μm, and the acetone extraction rate was 0.6%.

【００２３】〔作製例４〕合成例２で合成したレゾール
型フェノール樹脂（Ｂ２）を１３０℃で９０分加熱し
た。得られたレゾール樹脂硬化物をハンマーミルで粗粉
砕した後、ジェットミルを用いて微粉砕した。得られた
粉末状レゾール樹脂硬化物（Ｄ４）の平均粒径は１５μ
ｍであり、アセトン抽出率は１．５％であった。[Production Example 4] The resol-type phenol resin (B2) synthesized in Synthesis Example 2 was heated at 130 ° C for 90 minutes. The obtained resol resin cured product was roughly pulverized with a hammer mill and then finely pulverized with a jet mill. The average particle diameter of the obtained powdery resol resin cured product (D4) is 15μ.
m, and the acetone extraction rate was 1.5%.

【００２４】〔作製例５〕合成例１で合成したノボラッ
ク型フェノール樹脂（Ｂ１）１，０００部とヘキサメチ
レンテトラミン１００部とを混合粉砕した後、１２０℃
で３０分さらに１６０℃で６０分加熱した。得られたノ
ボラック樹脂硬化物をハンマーミルで粗粉砕した後、パ
ルペライザーおよびジェットミルを用いて微粉砕した。
得られた粉末状ノボラック樹脂硬化物（Ｄ５）の平均粒
径は０．８μｍであり、アセトン抽出率は９％であっ
た。[Production Example 5] 1,000 parts of the novolac type phenol resin (B1) synthesized in Synthesis Example 1 and 100 parts of hexamethylenetetramine were mixed and pulverized, and then 120 ° C.
It was heated for 30 minutes at 160 ° C. for 60 minutes. The obtained novolak resin cured product was roughly pulverized with a hammer mill and then finely pulverized with a pulverizer and a jet mill.
The obtained powdery novolac resin cured product (D5) had an average particle size of 0.8 μm and an acetone extraction rate of 9%.

【００２５】〔作製例６〕合成例２で合成したレゾール
型フェノール樹脂（Ｂ２）を１４０℃で６０分加熱し
た。得られたレゾール樹脂硬化物をハンマーミルで粗粉
砕した後、パルペライザーを用いて微粉砕した。得られ
た粉末状レゾール樹脂硬化物（Ｄ６）の平均粒径は１５
０μｍであり、アセトン抽出率は６％であった。[Production Example 6] The resol-type phenol resin (B2) synthesized in Synthesis Example 2 was heated at 140 ° C for 60 minutes. The obtained resole resin cured product was roughly pulverized with a hammer mill and then finely pulverized with a palpelizer. The average particle diameter of the obtained powdery resol resin cured product (D6) is 15
It was 0 μm, and the acetone extraction rate was 6%.

【００２６】合成例１〜２で得られたノボラック型フェ
ノール樹脂およびレゾール型フェノール樹脂の配合と特
性値を表１に示した。また、作製例１〜６で得られた粉
末状フェノール樹脂硬化物の配合と特性値を表２に示し
た。Table 1 shows the composition and characteristic values of the novolac type phenol resin and the resol type phenol resin obtained in Synthesis Examples 1 and 2. Further, Table 2 shows the composition and characteristic values of the powdery phenolic resin cured products obtained in Production Examples 1 to 6.

【００２７】〔実施例１〕ポリプロピレン１００重量部
と作製例１で得られた粉末状ノボラック樹脂硬化物（Ｄ
１）１０重量部を加圧ニーダーにて１９０℃、３０分間
溶融混練する。得られたフェノール樹脂組成物を押出し
成形によりシートとし、各試験片を作製した。[Example 1] 100 parts by weight of polypropylene and the powdery novolac resin cured product (D
1) 10 parts by weight are melt-kneaded with a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００２８】〔実施例２〕ポリプロピレン１００重量部
と作製例２で得られた粉末状ノボラック樹脂硬化物（Ｄ
２）３０重量部を加圧ニーダーにて１９０℃、３０分間
溶融混練する。得られたフェノール樹脂組成物を押出し
成形によりシートとし、各試験片を作製した。[Example 2] 100 parts by weight of polypropylene and the powdery novolac resin cured product (D
2) Melt and knead 30 parts by weight with a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００２９】〔実施例３〕ポリプロピレン１００重量部
と作製例３で得られた粉末状レゾール樹脂硬化物（Ｄ
３）５重量部配合し、加圧ニーダーにて１９０℃、３０
分間溶融混練する。得られたフェノール樹脂組成物を押
出し成形によりシートとし、各試験片を作製した。[Example 3] 100 parts by weight of polypropylene and the powdery resol resin cured product (D
3) Mix 5 parts by weight, and press the kneader at 190 ° C for 30
Melt and knead for a minute. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００３０】〔実施例４〕ポリプロピレン１００重量部
と作製例４で得られた粉末状レゾール樹脂硬化物（Ｄ
４）４５重量部を加圧ニーダーにて１９０℃、３０分間
溶融混練する。得られたフェノール樹脂組成物を押出し
成形によりシートとし、各試験片を作製した。Example 4 100 parts by weight of polypropylene and the powdery resol resin cured product (D
4) Melt and knead 45 parts by weight with a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００３１】〔比較例１〕ポリプロピレン１００重量部
と作製例１で得られた粉末状ノボラック樹脂硬化物（Ｄ
１）３重量部を加圧ニーダーにて１９０℃、３０分間溶
融混練する。得られたフェノール樹脂組成物を押出し成
形によりシートとし、各試験片を作製した。[Comparative Example 1] 100 parts by weight of polypropylene and the powdery novolac resin cured product (D
1) Melt and knead 3 parts by weight with a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００３２】〔比較例２〕ポリプロピレン１００重量部
と作製例３で得られた粉末状レゾール樹脂硬化物（Ｄ
３）７０重量部を加圧ニーダーにて１９０℃、３０分間
溶融混練する。得られたフェノール樹脂組成物を押出し
成形によりシートとし、各試験片を作製した。[Comparative Example 2] 100 parts by weight of polypropylene and the powdery resol resin cured product (D
3) Melt and knead 70 parts by weight with a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００３３】〔比較例３〕ポリプロピレン１００重量部
と作製例５で得られた粉末状ノボラック樹脂硬化物（Ｄ
５）１０重量部を加圧ニーダーにて１９０℃、３０分間
溶融混練する。得られたフェノール樹脂組成物を押出し
成形によりシートとし、各試験片を作製した。[Comparative Example 3] 100 parts by weight of polypropylene and the powdery novolac resin cured product (D
5) 10 parts by weight are melt-kneaded in a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００３４】〔比較例４〕ポリプロピレン１００重量部
と作製例６で得られた粉末状レゾール樹脂硬化物（Ｄ
６）１０重量部を加圧ニーダーにて１９０℃、３０分間
溶融混練する。得られたフェノール樹脂組成物を押出し
成形によりシートとし、各試験片を作製した。Comparative Example 4 100 parts by weight of polypropylene and the powdery resol resin cured product (D
6) 10 parts by weight are melt-kneaded with a pressure kneader at 190 ° C. for 30 minutes. Each of the test pieces was prepared by extruding the obtained phenol resin composition into a sheet.

【００３５】〔比較例５〕ポリプロピレン１００重量部
を押出し成形によりシートとし、各試験片を作製した。[Comparative Example 5] 100 parts by weight of polypropylene was extruded into a sheet to prepare each test piece.

【００３６】〔比較例６〕エチレンブロックコポリマー
１００重量部を押出し成形によりシートとし、各試験片
を作製した。Comparative Example 6 100 parts by weight of the ethylene block copolymer was extruded into a sheet to prepare each test piece.

【００３７】（試験片の評価方法）メルトフローインデ
ックス（ＭＦＩ）はＡＳＴＭ Ｄ１２３８−６２Ｔ、軟
化点はＡＳＴＭ Ｄ１５２５−５８Ｔ、曲げ剛性度はＡ
ＳＴＭ Ｄ７９０、引張降伏強度はＡＳＴＭ Ｄ６３
８、アイゾット衝撃強度はＡＳＴＭ Ｄ２５６−５６、
熱変形温度はＡＳＴＭ Ｄ６４８、成形収縮率はＡＳＴ
Ｍ Ｄ９５５−５１、体積固有抵抗はＡＳＴＭ Ｄ２５
７、誘電率はＡＳＴＭ Ｄ１５０、燃焼試験はUnderwri
ters Laboratories社 の安全標準ＵＬ９４（○：燃焼時
間１０秒以内、△：１０秒以上燃焼、×：全焼）によっ
て測定した。これらの配合及び評価結果は表３に示し
た。(Evaluation method of test piece) Melt flow index (MFI) is ASTM D1238-62T, softening point is ASTM D1525-58T, flexural rigidity is A.
ASTM D790, tensile yield strength is ASTM D63
8, Izod impact strength is ASTM D256-56,
Heat distortion temperature is ASTM D648, molding shrinkage is AST
M D955-51, volume resistivity is ASTM D25
7. Dielectric constant: ASTM D150, Combustion test: Underwri
ters Laboratories safety standard UL94 (○: burning time within 10 seconds, Δ: burning for 10 seconds or more, ×: total burning). The formulations and the evaluation results are shown in Table 3.

【００３８】[0038]

【表１】 [Table 1]

【００３９】[0039]

【表２】 [Table 2]

【００４０】[0040]

【表３】 [Table 3]

【００４１】実施例１〜４で得られたポリプロピレンと
粉末状フェノール樹脂硬化物を溶融混練してなるフェノ
ール樹脂組成物は比較例１〜６で得られたものに比べ
て、アイゾット衝撃強度、熱変形温度、成形収縮率、難
燃性などの機械的、物理的特性が向上する事が確認され
た。また、ポリプロピレンは非極性炭化水素である事か
ら優れた電気的特性を有しているが、フェノール樹脂硬
化物をブレンドする事により更に電気的特性が向上し
た。The polypropylene resin compositions obtained by melt-kneading the polypropylene and the powdery phenolic resin cured products obtained in Examples 1 to 4 were better than those obtained in Comparative Examples 1 to 6 in Izod impact strength and heat resistance. It was confirmed that mechanical and physical properties such as deformation temperature, molding shrinkage and flame retardancy were improved. Further, polypropylene has excellent electrical properties because it is a non-polar hydrocarbon, but the electrical properties were further improved by blending a cured phenol resin.

【００４２】[0042]

【発明の効果】本発明によれば、従来からポリプロピレ
ンの持っている成形性、可撓性、電気的特性などの優れ
た特長を損う事なく、難燃性、耐熱性、耐衝撃性、塗装
性および制電性などのフェノール樹脂の持つ特長も付与
出来る。このため、従来からポリプロピレンが使用され
ている分野は勿論の事、難燃性、耐熱性、制電性が要求
される分野においても適応が可能である。EFFECTS OF THE INVENTION According to the present invention, flame retardancy, heat resistance, impact resistance, and polypropylene can be achieved without impairing the excellent characteristics of polypropylene such as moldability, flexibility, and electrical characteristics. Features such as paintability and antistatic property of phenolic resin can be added. Therefore, it can be applied not only in the field where polypropylene has been conventionally used but also in the field where flame retardancy, heat resistance and antistatic property are required.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 ポリプロピレン１００重量部と粉末状フ
ェノール樹脂硬化物５〜５０重量部を溶融混練してなる
フェノール樹脂組成物。1. A phenol resin composition obtained by melt-kneading 100 parts by weight of polypropylene and 5 to 50 parts by weight of a powdered phenol resin cured product. 【請求項２】 粉末状フェノール樹脂硬化物が、ノボラ
ック型フェノール樹脂と硬化剤とを配合し、加熱により
硬化させてなる粉末状フェノール樹脂硬化物および／ま
たはレゾール型フェノール樹脂を加熱または酸により硬
化させてなる粉末状フェノール樹脂硬化物である請求項
１記載のフェノール樹脂組成物。2. A powdery phenolic resin cured product is obtained by mixing a novolac type phenolic resin and a curing agent and curing the powdery phenolic resin cured product and / or a resol type phenolic resin by heating or acid. The phenol resin composition according to claim 1, which is a powdered phenol resin cured product obtained by the above. 【請求項３】 粉末状フェノール樹脂硬化物のアセトン
抽出率が１０％未満である請求項１又は２記載のフェノ
ール樹脂組成物。3. The phenol resin composition according to claim 1, wherein the powdery phenolic resin cured product has an acetone extraction rate of less than 10%. 【請求項４】 粉末状フェノール樹脂硬化物の粉末の粒
径が１〜１００μｍである請求項１、２又は３記載のフ
ェノール樹脂組成物。4. The phenol resin composition according to claim 1, 2 or 3, wherein the powder of the powdered phenol resin cured product has a particle size of 1 to 100 μm.