JPH0445928A - 自己消火性積層フィルム - Google Patents
自己消火性積層フィルムInfo
- Publication number
- JPH0445928A JPH0445928A JP2156101A JP15610190A JPH0445928A JP H0445928 A JPH0445928 A JP H0445928A JP 2156101 A JP2156101 A JP 2156101A JP 15610190 A JP15610190 A JP 15610190A JP H0445928 A JPH0445928 A JP H0445928A
- Authority
- JP
- Japan
- Prior art keywords
- film
- nylon
- fire retardant
- laminated film
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
め要約のデータは記録されません。
Description
、直しに自ら消火して燃え拡がることのない自己消火性
積層フィルムに関する。
用されて来たが、最近では、電子精密機器、輸送機器、
建材等の分野で用いられるようになって来た。このよう
な新規分野では、積層フィルムの難燃化が要求され、各
種の研究が進められており、例えば、少なくとも2枚の
プラスチックフィルムの間に難燃剤を含有した接着剤層
を介在させてなる難燃性積層フィルムが提案されている
(特開昭53−82887号公報参照)。この技術によ
れば、多量の難燃剤による接着剤層の接着性の低下を招
くので、これを防く為に、接着剤層に含有させる難燃剤
とj7て接着剤に不溶解で、且つ平均粒径が接着剤層厚
みの80%以下の粉体状難燃剤を接着剤100重量部に
対し60〜400重量部の範囲で添加すると共に、接着
剤層の厚みが2枚のプラスチックフィルムの総厚みに対
し20%乃至同一厚みの範囲とすることも提案されてい
る(特開昭62−240545号公報参照)。
れも、@燃性を付与する為には、多量の難燃剤を含有さ
せねばなCしず、然も、該難燃剤は、ハロゲン、燐、硫
黄、アンチモン等の元素を主体とする故に、焼却すると
を害気体を発生し、大気汚染の元凶となり、又、一方で
は燃焼炉の腐食や水質汚染をも惹起するという問題点が
あった。
解決する為になされたものであって、2枚以上の合成樹
脂フィルムからなる積層フィルムであって、このうち、
少なくとも1枚のフィルムは、ノルトフローレ−1・が
20 (g10j分)以上で、且つ難燃剤を含有する熱
可塑性樹脂製フィルムからなることを1寺徴とする自己
消火性積層フィルムをその要旨とするものである。
成するフィルムの−として、少量の難燃剤を含有すると
共に、熱によって極めて融り易い特定の熱可塑性樹脂か
らなるフィルム(以下「特定のフィルム」という)を採
用することによって、万一火炎に曝されても、逸速くこ
の特定のフィルムのみが先に溶融落下し、残りのフィル
ムへの延焼率を低く抑えることが出来、)容31!l!
落下した樹脂自体も自己消火性を有するので、結局火炎
は拡大しないという従来には見られなかった全く新しい
難燃機構に基くものである。
フィルムは、−・般に機械的強度に乏しく、これ自体で
は所期の物性が得られないので、通常の汎用樹脂からな
るフィルムからなるフィルムと積層することによって、
強度物性と難燃性とを兼備したものとするのである。
、燐、硫黄を含む有機系難燃剤、金属水酸化物、重炭酸
すトリウム等の無機系難燃剤が使用可能であるが、その
使用量は、前述の通り特定のフィルムのみで済むので、
ノイルJ・に塗布乃至含有したり、2枚のフィルム間に
介在させる接着剤中に練込んだりする従来一般に使用さ
れる難燃性フィルムでの使用量の半分以下で充分である
。
としては、ポリオレフィン系もしくはポリアミド系樹脂
が好適に用いられ、ポリオレフィン系樹脂としては、ポ
リエチレン、エチレン酢酸ビニル共重合体、エチレン−
エチルアクリレート共重合体等のエチレン共重合体、ポ
リプロピレン、プロピレンと他のモノマーとの共重合体
、低分子量ポリエチレン、低分子量ポリプロピレン等が
挙げられる。
ン6−6、ナイロン6−10、ナイロン]1、ナイロン
12及びこれらの共重合物等が、好適に使用される。尚
、これらの樹脂には、高級アルコール、ヒドロキシ安息
香酸エステル等の可塑剤が含まれていてもよい。
としては、上記ポリオレフィン系樹脂、ポリアミド系樹
脂のみに限定されない。
して、充填剤、顔料、抗酸化剤等を添加してもよい。
そのメル]・フローレートが20 (g/l、0分)以
−ヒのものでなりればならず、かがる樹脂は比較的分子
量の低いものから得られるのであって、20に満たない
場合は溶融落下し難く、又、熔融落下するとしても、そ
の前に他の積層フィルムに燃え移る危険性があり、所期
の機能を発揮し得ない。
2]、Or熱可塑性プラスチックの流れ試験方法」で測
定される値をいい、ポリエチI/ン系樹脂にあっては、
条件4(試験温度190’C5試験荷重2.16kg/
f) 、ポリプロピレン系樹脂及びポリアミド系樹脂に
あっては、条件]4(試験温度230°C1試験荷重2
.16kg/f)での測定値である。
体に対し重量比で50%以上になるよう構成されている
のが好ましく、これに満たない場合は、所期の効果が得
られない場合がある。
を構成する樹脂としては、ポリエチレン、エチレン−酢
酸ビニル共重合体、ポリプロピレン、ポリエチレンテレ
フタレート等のポリエステル、ポリアミド等が、好適に
使用され、好ましくは、特定のフィルムと同系統のもの
を選択するのがよい。
は、それ以外のフィルムの片面もしくは両面の何れに積
層されていてもよく、又、2枚の熱可塑性樹脂フィルJ
、の間に介在せしめられていてもよい。又、特定のフィ
ルムを、熱可塑性樹脂フィルムに積層する方法としては
、押出コーティング、ホソI−メルトコーティング、溶
液コーティング等の公知の方法が使用される。
フィルムからなる積層フィルムであって、このうら、少
なくとも1枚のフィルムは、メルI−フローレー1〜が
20 (g/10分)以」二で、且つ難燃剤を含量する
熱可塑性樹脂製フィルムからなるので、着火した場合に
は、火炎が拡大乃至延焼する前に、特定のフィルムが溶
出して滴下し、火源から離れると直ちに消火する。
実施例に限定されるものではない。
ン720」東ソー社製、メルI・フローレト150、酢
酸ビニル含量28%)95重量部と、難燃剤(商品名r
A F” R1002j旭硝子社製、臭素含量66%
)5重量部とを、120°Cの熱ロールにより5分間混
練して特定のフィルムを構成する月相を調製した後、厚
み20μの2枚の直鎖状低密度ポリエチレンフィルムに
挟んで、200μのスペーサーを入れた120°Cのブ
I/ス機で熱ブl/スして、厚みが200μの本発明積
層フィルムを得た。
して試験片とし、垂直に垂下して着火試験を行った。
した。
ラセン530」東ソー社製、メルト)じ7−レート75
、酢酸ビニル含量6%)を用いたこと以外は実施例]と
同様にして、厚みが200μの本発明積層フィルムを得
、着火試験を行った。
した。
ラセン541」東ソー社製、メルトフローレート9、酢
酸ビニル含量10%)を用いたごと以外は実施例]と同
様にして、厚みが200μの積層フィルムを得、着火試
験を行った。
続Jlだ。
ラセン63」」東ソー社製、ノルトフローレー) 1.
5、ff1=酸ビニルビニル含量20用いたこと以外は
実施例1と同様にして、厚みが200μの積層フィルム
を得、着火試験を行った。
続けた。
−1)J三洋化成工業社製、メルI・フローl/−1−
500以上)70重量部と、エチl/ンー酢酸ビニル共
重合体(商品名「ウルトラセン720」東ソーネ]−製
、メルトフ1−1−レート]502酢酸ビニル含!28
%)30重量部に、燐酸グアニジン(商品名「アビノン
301」三相ケミカル社製)10重量部を160 ’C
で加熱混合した後、厚み30μのポリプロピレンフィル
ムの片面に、ホノ]・メルトコーターにより、100μ
の厚みにコーティングして、厚みが130μの本発明積
層フィルムを得得られた積層フィルムを幅20c+nの
テープ状に切断して試験片とし、垂直に垂下して着火試
験を行った。
した。
ン681」東ソー社製、メルトフローレ−I−350、
酢酸ビニル含量20%)45重量部に、塩素化ポリエチ
レン(商品名「エラスレン301八」昭和電工社製)5
重量部と、[・ルエン50重景部を混合した後、厚み1
5μのポリエチレンテレフタレートフィルムの片面に、
ロールコーティングにより、200μの厚みにコーティ
ングし、その上面から厚み20μの低密度ポリエチレン
フィルムを圧着し、100°Cの熱ロールによりプレス
して、厚みが235μの積層フィルムを得た。
て試験片とし、垂直に垂下して着火試験を行った。
した。
成とされているので、難燃剤の含を量が少量で済み、廃
棄物の処理が容易であり、自動車内装材、電気用、建築
用、輸送梱包用に使用して好適なものである。
Claims (1)
- 1、2枚以上の合成樹脂フィルムからなる積層フィルム
であって、このうち、少なくとも1枚のフィルムは、メ
ルトフローレートが20(g/10分)以上で、且つ難
燃剤を含有する熱可塑性樹脂製フィルムからなることを
特徴とする自己消火性積層フィルム。