JPH025979A - Golf club - Google Patents
Golf clubInfo
- Publication number
- JPH025979A JPH025979A JP63156714A JP15671488A JPH025979A JP H025979 A JPH025979 A JP H025979A JP 63156714 A JP63156714 A JP 63156714A JP 15671488 A JP15671488 A JP 15671488A JP H025979 A JPH025979 A JP H025979A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- whisker
- fiber
- golf club
- whiskers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔発明の目的〕
（産業上の利用分野）
本発明はゴルフクラブに関し、更に詳しくは、ウィスカ
ー（ｌｈｉｓｋｅｒ、ホイスカーともいわれる。）の強
度特性などを最大限に生かしたゴルフクラブに関するも
のである。[Detailed Description of the Invention] [Object of the Invention] (Industrial Field of Application) The present invention relates to a golf club, and more specifically, to a golf club that takes full advantage of the strength characteristics of whiskers (also called whiskers). It's about clubs.
（従来の技術とその問題点）
従来より、ゴルフクラブの構成部材、例えばクラブのヘ
ッド、インサート板、フェース、シャフトなどを強化す
るために、カーボン繊維（ＣＦ）、ポロン繊維、全芳香
族ポリアミド繊維などの補強用Ｈ＆雄を合成樹脂に混入
した繊維強化樹脂（ＦＲＰ）、あるいは金属に混入した
繊維強化金属（ＦＲＭ）などが使用されている。(Prior art and its problems) Conventionally, carbon fiber (CF), poron fiber, wholly aromatic polyamide fiber has been used to strengthen the constituent members of golf clubs, such as club heads, insert plates, faces, and shafts. Fiber-reinforced resin (FRP), which is a synthetic resin mixed with reinforcing H & male, or fiber-reinforced metal (FRM), which is a metal mixed with reinforcing H & male, is used.
しかしながら、これらの強化材料を用いても、ヘッド部
の破損や１１，１れ、あるいはシャフトの折れなどが生
じ、十分なものとはいえない。However, even if these reinforcing materials are used, damage to the head portion, 11,1 cracking, or breakage of the shaft may occur, and it cannot be said to be sufficient.
また、ＣＦＲＰなどは材質の硬度が硬いため、ゴルフポ
ールの打球感触が悪いという欠点もある。Furthermore, since CFRP is a hard material, it also has the disadvantage that the golf pole has a poor feel when hitting a ball.
一方、ウィスカー繊維を強化材料とする技術としては、
ウィスカーを混入した合成樹脂や金属を用いてゴルフク
ラブとするもの（実開昭５９−８３８８ ”ｔ ） 、
炭＞ｋ ＃ａｍ ナト１７） １ｉＡｍ ７ ）にウ
ィ゛ζカーを混合したエポキシ樹脂などの熱硬化性樹脂
を含浸してプリプレグを形成し、これを巻回硬化させて
釣竿などを製造するもの（特開昭５８−２１１４４２号
）、などがある。On the other hand, as a technology that uses whisker fibers as a reinforcing material,
A golf club made of synthetic resin or metal mixed with whiskers (Utility Model Publication No. 59-8388"t),
Charcoal > k #am Nat17) 1iAm 7) is impregnated with a thermosetting resin such as epoxy resin mixed with Wirζ car to form a prepreg, which is then rolled and cured to manufacture fishing rods, etc. JP-A No. 58-211442), etc.
しかしながら、前記したウィスカーを利用する技術は、
ウィスカーを樹脂中に混入分散させることを前提として
いるものであり、ウィスカーの特性を十分に生かした複
合材料であるとはいえない。However, the technology using whiskers described above is
It is based on the premise that whiskers are mixed and dispersed in a resin, so it cannot be said that it is a composite material that fully takes advantage of the characteristics of whiskers.
（発明が解決しようとする課題）
本発明者は、ウィスカー（ひげ結晶）の強度などにみら
れる優れた特性をゴルフクラブ用の複合材料に生かすべ
く鋭意検討した。その結果、炭素繊維やポロンｍ維など
のｔａ維シート上にウィスカーを均一に散布し、固着し
てシート状としたもの（以下、ウィスカーシートという
。）と、各種のｍ雄強化樹脂シートとを積層して複合材
料とした場合、ウィスカーシートにおいてウィスカーの
特性が十分に生かされることを見い出し、本発明を完成
するに至った。(Problems to be Solved by the Invention) The present inventor has made extensive studies to utilize the excellent properties of whiskers (beard crystals), such as their strength, in composite materials for golf clubs. As a result, whiskers were uniformly dispersed on a TA fiber sheet such as carbon fiber or Poron M fiber and fixed to form a sheet (hereinafter referred to as a whisker sheet), and various M male reinforced resin sheets. The present inventors have discovered that the characteristics of whiskers can be fully utilized in whisker sheets when laminated to form a composite material, leading to the completion of the present invention.
本発明は１前記したウィスカーシートとｆｆｌ！強化樹
脂シートとのｍ履体を用いて破損、割れ、折れなどに耐
性を有するゴルフクラブを提供することを目的とするも
のである。The present invention includes the above whisker sheet and ffl! The object of the present invention is to provide a golf club that is resistant to breakage, cracking, bending, etc. by using a shoe body made of reinforced resin sheets.
（課題を解決するための手段）
本発明を概説すれば、本発明はゴルフクラブの構成部材
が、繊維シートにウィスカーを付着してなるウィスカー
シートと繊維強化樹脂シートとの積層体から構成された
ものであることを特徴とするゴルフクラブに関するもの
である。(Means for Solving the Problems) To summarize the present invention, a component of a golf club of the present invention is constituted by a laminate of a whisker sheet formed by attaching whiskers to a fiber sheet and a fiber reinforced resin sheet. This invention relates to a golf club characterized by:
以下、本発明の構成ならびに実施例について図面に基づ
いて詳しく説明する。Hereinafter, the configuration and embodiments of the present invention will be described in detail based on the drawings.
本発明で使用するウィスカーシートは、炭素繊維、全芳
香族ポリアミドｍ維、ポロン繊維、ガラス繊維などの長
繊維より製作したｍ維シート上に、ウィスカーを均一に
散布し、バインダーで固めることによって得ることがで
きる。The whisker sheet used in the present invention is obtained by uniformly scattering whiskers on an m-fiber sheet made of long fibers such as carbon fiber, fully aromatic polyamide m-fiber, poron fiber, glass fiber, etc., and hardening it with a binder. be able to.
ウィスカーは太さが０．１μｍ〜１０ｐ、ｍ程度の針状
結晶（ひげ結晶）のもので非常に多くのものが知られて
いる。例えば、炭化珪素、炭化硼素などのセラミックス
系ウィスカー、あるいは金属系ウィスカーなど、多数の
ものが知られており１本発明においては、これらを特別
の制限なしに使用することができる。ウィスカーの使用
量は適宜法めればよく−１例えば全芳香族ポリアミド繊
＃３０〜４０重量％に対し、炭化珪素ウィスカー７０〜
６０重量％を用いてウィスカーシートを製作すればよい
。A large number of whiskers are known as needle-shaped crystals (beard crystals) with a thickness of about 0.1 μm to 10 μm. For example, many whiskers are known, such as ceramic whiskers such as silicon carbide and boron carbide, and metal whiskers, and these can be used in the present invention without any particular limitations. The amount of whiskers to be used may be determined as appropriate - 1 For example, 70 to 40% by weight of silicon carbide whiskers to fully aromatic polyamide fiber #30 to 40% by weight.
A whisker sheet may be manufactured using 60% by weight.
本発明で使用するＨ＆維強化樹脂シートは、炭素繊維、
全芳香族ポリアミド！ａ雄、ポロン繊維などの補強繊維
の織布、不織布にエポキシ樹脂、ポリエステル樹脂など
の通常の熱硬化樹脂を含浸させ、半硬化状態にしたプリ
プレグ、あるいはこれらの補強繊維を合成樹脂に混入し
た繊維強化樹脂（ＦＲＰ）のシート状物などである。The H & fiber reinforced resin sheet used in the present invention includes carbon fiber,
Fully aromatic polyamide! Woven fabrics made of reinforcing fibers such as poron fibers, prepregs made by impregnating non-woven fabrics with ordinary thermosetting resins such as epoxy resins and polyester resins to a semi-cured state, or fibers made by mixing these reinforcing fibers into synthetic resins. These include sheets of reinforced resin (FRP).
（実施例）
次に、前記したウィスカーシートと朦雄強化樹脂シート
の積層体より構成されるゴルフクラブの構成部材を説明
する。(Example) Next, a constituent member of a golf club composed of a laminate of the whisker sheet and the Atsuo reinforced resin sheet described above will be described.
第１図は、本発明の第１実施例になる前記したウィスカ
ーシートとカーボン繊維シートの積層体でＪ＃成したフ
ェースインサート板を有するヘッドの上方よりみた斜視
図である。FIG. 1 is a perspective view from above of a head having a J# face insert plate made of a laminate of the whisker sheet and carbon fiber sheet described above, according to a first embodiment of the present invention.
第２図は、第１図に示されるフェースインサート板のウ
ィスカーシートとカーボン繊維シートの蹟層状態を示す
説明図である。FIG. 2 is an explanatory diagram showing the state of the whisker sheet and carbon fiber sheet of the face insert plate shown in FIG. 1.
フェースインサート板は、熱硬化性樹脂としてエポキシ
樹脂を用いた未硬化のカーボンｉａ維プリプレグと、全
芳香族ポリアミドの繊維シ−ト１に炭化ケイ素ウィスカ
ーを均一に散布し （ポリアミド３６屯、！ｊ、％、ウ
ィスカー６４屯ニー％）、バインダーで固めたウィスカ
ーシートを第２図の如く積層、加圧−加熱成形する。そ
の際、プリプレグの未硬化状の熱硬化性樹脂がウィスカ
ーシートの＃ａ雄の隙間に含浸していき各シートが密Ｒ
硬化する。次に硬化した積層板をインサート形状に加工
し、ヘッドに装着する。The face insert plate is made of an uncured carbon IA fiber prepreg using epoxy resin as a thermosetting resin, and a fully aromatic polyamide fiber sheet 1 with silicon carbide whiskers evenly sprinkled on it (polyamide 36 tons,!j , %, whisker 64 tonne %), whisker sheets hardened with a binder are laminated as shown in FIG. 2, and then pressurized and heated. At that time, the uncured thermosetting resin of the prepreg impregnates the #a male gap of the whisker sheet, and each sheet is tightly rounded.
harden. Next, the cured laminate is processed into an insert shape and attached to the head.
以［−のようにして、ウィスカーシートによりフェース
インサート板が強化されるとともに、インパクト時にお
いてウィスカーシートがポールからの衝撃力を有効に吸
収するためソフトな打球感が得られる。As described above, the face insert plate is strengthened by the whisker sheet, and at the time of impact, the whisker sheet effectively absorbs the impact force from the pole, resulting in a soft hitting feeling.
第３１２１は、本発明の第２実施例になる前記したカー
ボン繊維シートとウィスカーシートの積層体で構成した
中空ヘッドの斜視図で、Ｊａ層履体各シートの積層状態
がヘッド上面の一部において、１スされている。No. 3121 is a perspective view of a hollow head constructed of a laminate of the above-described carbon fiber sheet and whisker sheet according to the second embodiment of the present invention, in which the laminated state of each sheet of the Ja layer footwear is shown in a part of the upper surface of the head. , has been passed once.
この中空ヘッドはコンプレッション成形により製造され
、積層体の比強度が大きいためヘッド形状を大きくする
ことができる。また、フェースインサート板と同様に、
ソフトな打球感が得られるとともに、ヘッドの破損やか
けを防止することができる。This hollow head is manufactured by compression molding, and since the laminate has a high specific strength, the head shape can be made large. Also, like the face insert plate,
Not only can you get a soft feel at impact, but you can also prevent the head from being damaged or chipped.
第４図は、本発明の第３実施例になる前記したカーボン
繊維シートとウィスカーシートの積層体で構成したシャ
フトの一部分の斜視図で、積層体の各シートの積層状態
が示されている。FIG. 4 is a perspective view of a portion of a shaft constructed from a laminate of carbon fiber sheets and whisker sheets described above according to a third embodiment of the present invention, showing the laminated state of each sheet of the laminate.
カーボンｍ雅シートとウィスカーシートの未硬化状４ｈ
の蹟層材をシートワインディング法により製造し、これ
からシャフトに成形、硬化される。ウィスカーシートに
よりシャフトが強化され、肉薄の軒端シャフトが製造さ
れる。Uncured 4h of carbon miya sheet and whisker sheet
This material is manufactured using the sheet winding method, which is then formed into a shaft and hardened. The whisker sheet strengthens the shaft and produces a thin-walled eave end shaft.
ｍ維シートにウィスカーを付着、固定してなるウィスカ
ーシートと、繊維強化樹脂シートとの積層体からゴルフ
クラブの構成部材を製造するという本発明により、次の
ような優れた効果を奏する。The present invention, in which a constituent member of a golf club is manufactured from a laminate of a whisker sheet formed by adhering and fixing whiskers to a m-fiber sheet and a fiber-reinforced resin sheet, has the following excellent effects.
（１）ゴルフクラブのヘット、イノサート、フェース、
シャフトなどの各構成部材に適用される材キ１の強度が
向」−するため、これら部材の破損、；’；ｌれ、折れ
などを防＋卜することができる。(1) Golf club head, inosert, face,
Since the strength of the material 1 applied to each component member such as the shaft is improved, damage, bending, bending, etc. of these members can be prevented.
（２）フェースインサート材、フェース面に使用する場
合、インパクト時において、ウィスカーシートがポール
からの衝撃力を吸収するため、ソフトな打球感が得られ
る。(2) When used as a face insert material on the face surface, the whisker sheet absorbs the impact force from the pole at the time of impact, resulting in a soft shot feel.
（３）中空ヘッドに使用する場合、高強Ｉｆであるため
肉厚を薄くでき、打ちやすい大きなヘッド形状とするこ
とができる。(3) When used in a hollow head, since it has a high strength If, the wall thickness can be reduced, and a large head shape that is easy to hit can be formed.
（４）シャフトに使用する場合、シャフトを軽星化する
ことができるため、ヘッドスピードを増大させることが
容易なりラブが得られる。(4) When used in a shaft, since the shaft can be made into a light star, the head speed can be easily increased and love can be obtained.
第１図は、本発明の第１実施例になるウィスカーシート
とカーボン繊維シートの積層体で構成したフェースイン
サート板を有するヘッドの斜視図である。第２図はフェ
ースインサート板のウィスカーシートとカーボン繊維シ
ートの積層状態を示す説明図である。
第３図は、本発明の第２実施例になるウィスカーシート
とカーボンｍ維シートの端層体で構成した中空ヘッドの
斜視図である。
第４図は、本発明の第３実施例になるウィスカーシート
とカーボン繊維シートの積層体で構成したシャフトの一
部分の斜視図である。FIG. 1 is a perspective view of a head having a face insert plate made of a laminate of a whisker sheet and a carbon fiber sheet according to a first embodiment of the present invention. FIG. 2 is an explanatory diagram showing a laminated state of a whisker sheet and a carbon fiber sheet of a face insert plate. FIG. 3 is a perspective view of a hollow head constructed of end layers of a whisker sheet and a carbon m-fiber sheet according to a second embodiment of the present invention. FIG. 4 is a perspective view of a portion of a shaft constructed of a laminate of a whisker sheet and a carbon fiber sheet according to a third embodiment of the present invention.
Claims (1)
ーを付着させたウィスカーシートと繊維強化樹脂シート
の積層体から構成されたものであることを特徴とするゴ
ルフクラブ。 ２、ウィスカーシートの繊維シートが全芳香族ポリアミ
ド繊維、ウィスカーが炭化ケイ素ウィスカーである請求
項１に記載のゴルフクラブ。 ３、繊維強化樹脂シートが、炭素繊維強化樹脂シートで
ある請求項１に記載のゴルフクラブ。 ４、ゴルフクラブの構成部材が、クラブヘッドである請
求項１に記載のゴルフクラブ。 ５、ゴルフクラブの構成部材が、フェースインサート板
である請求項１に記載のゴルフクラブ。 ６、ゴルフクラブの構成部材が、シャフトである請求項
１に記載のゴルフクラブ。[Scope of Claims] 1. A golf club characterized in that the constituent members of the golf club are composed of a laminate of a whisker sheet in which whiskers are attached to a fiber sheet and a fiber-reinforced resin sheet. 2. The golf club according to claim 1, wherein the fiber sheet of the whisker sheet is a wholly aromatic polyamide fiber and the whisker is a silicon carbide whisker. 3. The golf club according to claim 1, wherein the fiber reinforced resin sheet is a carbon fiber reinforced resin sheet. 4. The golf club according to claim 1, wherein the component of the golf club is a club head. 5. The golf club according to claim 1, wherein the component of the golf club is a face insert plate. 6. The golf club according to claim 1, wherein the component of the golf club is a shaft.