JP7375435B2 - 熱転写シート - Google Patents
熱転写シート Download PDFInfo
- Publication number
- JP7375435B2 JP7375435B2 JP2019181033A JP2019181033A JP7375435B2 JP 7375435 B2 JP7375435 B2 JP 7375435B2 JP 2019181033 A JP2019181033 A JP 2019181033A JP 2019181033 A JP2019181033 A JP 2019181033A JP 7375435 B2 JP7375435 B2 JP 7375435B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- transfer
- release layer
- thermal transfer
- transfer sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、上記の熱転写シートにおいて、前記離型層が、ポリビニルアルコールを含有しており、前記離型層の総質量に対する前記ポリビニルアルコールの質量が5質量%以上25質量%以下でもよい。
また、上記の熱転写シートにおいて、前記離型層が、シリコーンオイルを含有しており、前記離型層の総質量に対する前記シリコーンオイルの質量が1質量%以上4質量%以下でもよい。
以下、本開示の実施の形態に係る熱転写シート(以下、「本開示の熱転写シート」という場合がある。)について説明する。
本開示の熱転写シート100を構成する基材1は、基材1上に設けられる離型層2や、離型層2上に設けられる転写層10を保持する。基材1の材料としては、ポリエチレンテレフタレート等のポリエステル、ポリアリレート、ポリカーボネート、ポリウレタン、ポリイミド、ポリエーテルイミド、セルロース誘導体、ポリエチレン、エチレン-酢酸ビニル共重合体、ポリプロピレン、ポリスチレン、アクリル、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリビニルアルコール、ポリビニルブチラール、ナイロン、ポリエーテルエーテルケトン、ポリサルフォン、ポリエーテルサルフォン、テトラフルオロエチレン-パーフルオロアルキルビニルエーテル共重合体、ポリビニルフルオライド、テトラフルオロエチレン-エチレン共重合体、テトラフルオロエチレン-ヘキサフルオロプロピレン共重合体、ポリクロロトリフルオロエチレン、ポリビニリデンフルオライド等の各種プラスチックフィルム、シート、カード等を例示できる。
各図に示すように、基材1上には、直接的に、又は任意の層を介して間接的に離型層2が設けられている(図示する形態では、基材1と離型層2とが直接的に接している)。離型層2上には、当該離型層2と直接的に接するように転写層10が設けられている。
各図に示すように、離型層2上には、転写層10が設けられている。また、本開示の熱転写シート100では、転写層10は、離型層2と直接的に接しており、離型層2から剥離可能に設けられている。転写層10は、図1(a)、図3、図4に示すように、1つの層からなる単層構造を呈していてもよく、図1(b)、図2に示すように、複数の層が積層された積層構造を呈していてもよい。
また、基材1の離型層2が設けられた面とは反対側の面に、背面層(図示しない)を設けてもよい。背面層の厚みは、0.1μm以上5μm以下が好ましく、0.3μm以上2μm以下がより好ましい。
基材として、厚さ5μmのポリエチレンテレフタレートフィルムを用い、この基材上に、下記組成の離型層用塗工液1を、乾燥時の厚みが0.2μmになるように塗布・乾燥し離型層を形成した。次いで、離型層上に、下記組成の保護層用塗工液1を乾燥時の厚みが1μmになるように塗布・乾燥し、保護層を形成することで、基材上に、離型層、保護層がこの順で設けられた実施例1の熱転写シートを得た。なお、保護層は、本開示の印画物の熱転写シートでいう転写層を構成する。
・アルキルペンダント系樹脂 5部
(アシオレジン(登録商標)RA-585S アシオ産業(株))
・トルエン 95部
・アクリル樹脂(酸価0mgKOH/g) 20部
(ダイヤナール(登録商標)BR-83 三菱ケミカル(株))
・メチルエチルケトン 40部
・トルエン 40部
離型層用塗工液1を、下記組成の離型層用塗工液2に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例2の熱転写シートを得た。
・アルキルペンダント系樹脂 5部
(アシオレジン(登録商標)RA-95H アシオ産業(株))
・トルエン 95部
離型層用塗工液1を、下記組成の離型層用塗工液3に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例3の熱転写シートを得た。
・アルキルペンダント系樹脂 4.95部
(アシオレジン(登録商標)RA-95H アシオ産業(株))
・シリコーンオイル 0.05部
(KP-368 信越シリコーン(株))
・トルエン 95部
離型層用塗工液1を、下記組成の離型層用塗工液4に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例4の熱転写シートを得た。
・アルキルペンダント系樹脂 4.75部
(アシオレジン(登録商標)RA-95H アシオ産業(株))
・シリコーンオイル 0.25部
(KP-368 信越シリコーン(株))
・トルエン 95部
離型層用塗工液1を、下記組成の離型層用塗工液5に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例5の熱転写シートを得た。
・アルキルペンダント系樹脂 5部
(ピーロイル(登録商標)1010 ライオン・スペシャリティ・ケミカル(株))
・トルエン 95部
離型層用塗工液1を、下記組成の離型層用塗工液6に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例6の熱転写シートを得た。
・アルキルペンダント系樹脂 33.3部
(ピーロイル(登録商標)406(固形分15%) ライオン・スペシャリティ・ケミカル(株))
・水 19.2部
・イソプロピルアルコール 47.5部
離型層用塗工液1を、下記組成の離型層用塗工液7に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例7の熱転写シートを得た。
・アルキルペンダント系樹脂 30部
(ピーロイル(登録商標)406(固形分15%) ライオン・スペシャリティ・ケミカル(株))
・ポリビニルアルコール 0.5部
(ゴーセノール(登録商標)KH-20 日本合成化学工業(株))
・水 22部
・イソプロピルアルコール 47.5部
離型層用塗工液1を、下記組成の離型層用塗工液8に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例8の熱転写シートを得た。
・アルキルペンダント系樹脂 23.3部
(ピーロイル(登録商標)406 ライオン・スペシャリティ・ケミカル(株))
・ポリビニルアルコール 1.5部
(ゴーセノール(登録商標)KH-20 日本合成化学工業(株))
・水 27.7部
・イソプロピルアルコール 47.5部
離型層用塗工液1を、下記組成の離型層用塗工液9に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例9の熱転写シートを得た。
・アルキルペンダント系樹脂 28部
(ピーロイル(登録商標)HT(固形分18%) ライオン・スペシャリティ・ケミカル(株))
・トルエン 72部
離型層用塗工液1を、下記組成の離型層用塗工液10に変更して離型層を形成した以外は、全て実施例1と同様にして、実施例10の熱転写シートを得た。
・アルキルペンダント系樹脂 26.4部
(ピーロイル(登録商標)HT(固形分18%) ライオン・スペシャリティ・ケミカル(株))
・シリコーンオイル 0.25部
(KP-368 信越シリコーン(株))
・トルエン 73.4部
離型層用塗工液1を、下記組成の離型層用塗工液11に変更して離型層を形成した以外は、全て実施例1と同様にして、比較例1の熱転写シートを得た。
・シリコーン変性樹脂 16部
(KS-847(固形分30%) 信越シリコーン(株))
・メチルエチルケトン 42部
・トルエン 42部
離型層用塗工液1を、下記組成の離型層用塗工液12に変更して離型層を形成した以外は、全て実施例1と同様にして、比較例2の熱転写シートを得た。
・ポリウレタン 22.2部
(ハイドラン(登録商標)AP-40(F)(固形分22.5%) DIC(株))
・水 30.3部
・イソプロピルアルコール 47.5部
離型層用塗工液1を、下記組成の離型層用塗工液13に変更して離型層を形成した以外は、全て実施例1と同様にして、比較例2の熱転写シートを得た。
・ポリウレタン 15.5部
(ハイドラン(登録商標)AP-40(F)(固形分22.5%) DIC(株))
・ポリビニルアルコール 1.5部
(ゴーセノール(登録商標)KH-20 日本合成化学工業(株))
・水 12.05部
・イソプロピルアルコール 47.5部
離型層を設けることなく、基材上に直接に保護層を形成したこと以外は、全て実施例1と同様にして、比較例4の熱転写シートを得た。
カード用ラミネータ(大日本印刷(株))を用い、塩化ビニル製のカード基材(大日本印刷(株))上に、各実施例、及び比較例の熱転写シートの転写層を転写し、各実施例、及び比較例の転写物を得た。転写層の転写は下記の3つの条件(下記転写条件1、2、3)にて、それぞれ行った。
転写条件1:160℃、20mm/sec.
転写条件2:140℃、20mm/sec.
転写条件3:120℃、20mm/sec.
上記条件で転写層の転写を行ったときの、転写の状態を確認し、下記評価基準に基づいて転写性評価を行った。評価結果を表1に示す。
A・・・転写条件1で転写できた。
B・・・転写条件1では融着してしまうが、転写条件2で転写できた。
C・・・転写条件1、2では融着してしまうが、転写条件3で転写できた。
NG・・・転写条件1~3の何れの条件でも融着してしまう。
各実施例、及び比較例の熱転写シートを折り曲げたときの、転写層の箔落ちの有無を目視で確認し、下記評価基準に基づいて転写層の箔持ち評価を行った。評価結果を表1に示す。
A・・・転写層の箔落ちが全くない。
B・・・部分的に転写層の箔落ちがみられるが使用上問題ないレベルである。
C・・・転写層の箔落ちが大きくみられ使用上問題が懸念されるレベルである。
上記転写層の転写で得られた各実施例、及び比較例の転写物の端部の尾引きの状態を確認し、以下の評価基準に基づいて箔切れ性の評価を行った。評価結果を表2に示す。
A・・・尾引きの発生なし。
B・・・尾引きの長さが0.2mm以下。
C・・・尾引きの長さが0.2mmより長く1mm未満。
NG・・・尾引きの長さが1mm以上。
2・・・離型層
5・・・保護層
6・・・接着層
7・・・受容層
8・・・ヒートシール層
9・・・溶融インキ層
10・・・転写層
100・・・熱転写シート
Claims (7)
- 基材、離型層、転写層がこの順で積層された熱転写シートであって、
前記転写層は、前記離型層と直接的に接しており、且つ、離型層から剥離可能に構成され、
前記離型層が、融点が30℃以上100℃以下のアルキルペンダント系樹脂を含有している、熱転写シート。 - 前記転写層が保護層を含む、請求項1に記載の熱転写シート。
- 前記転写層が受容層を含む、請求項1または2に記載の熱転写シート。
- 前記転写層がヒートシール層を含む、請求項1~3のいずれか一項に記載の熱転写シート。
- 前記転写層が溶融インキ層を含む、請求項1~4のいずれか一項に記載の熱転写シート。
- 前記離型層が、ポリビニルアルコールを含有しており、
前記離型層の総質量に対する前記ポリビニルアルコールの質量が5質量%以上25質量%以下である、請求項1~5のいずれか一項に記載の熱転写シート。 - 前記離型層が、シリコーンオイルを含有しており、
前記離型層の総質量に対する前記シリコーンオイルの質量が1質量%以上4質量%以下である、請求項1~6のいずれか一項に記載の熱転写シート。