JP6971839B2 - 研磨パッド - Google Patents
研磨パッド Download PDFInfo
- Publication number
- JP6971839B2 JP6971839B2 JP2017252433A JP2017252433A JP6971839B2 JP 6971839 B2 JP6971839 B2 JP 6971839B2 JP 2017252433 A JP2017252433 A JP 2017252433A JP 2017252433 A JP2017252433 A JP 2017252433A JP 6971839 B2 JP6971839 B2 JP 6971839B2
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane resin
- polishing pad
- polishing
- resin foam
- pad according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
研磨面を有し、
該研磨面が、前記ポリウレタン樹脂発泡体の表面で構成され、
前記ポリウレタン樹脂発泡体は、25℃でのtanδが0.24〜0.60である。
また、本実施形態に係る研磨パッドは、研磨面を有し、該研磨面が、前記ポリウレタン樹脂発泡体の表面で構成されている。
なお、25℃でのtanδは、25℃での貯蔵弾性率E’に対する25℃での損失弾性率E’’の比を意味する。
測定温度範囲:0℃〜100℃
昇温速度:5℃/min
周波数:1Hz
ひずみ:0.5%
すなわち、ポリウレタン樹脂発泡体の測定対象範囲(例えば、0.7mm×1.6mm×1.6mm)に含まれている、各気泡の体積を測定し、この体積と同じ体積の真球の直径を各気泡の直径とする。
そして、各気泡の直径から直径の算術平均値を求め、これを気泡径の平均値とする。また、各気泡の直径から直径の変動係数を求め、これを気泡径の変動係数とする。
なお、「前記ポリウレタン樹脂発泡体では、気泡が、前記研磨面に垂直な断面において円形状となっている」とは、「前記ポリウレタン樹脂発泡体は、下記式(1)に示す気泡の長さのアスペクト比の平均値が、3/5〜5/3である。」ことを意味する。
気泡の長さのアスペクト比の平均値 = 研磨面に垂直な方向の気泡の長さ/研磨面に平行した方向の気泡の長さ ・・・(1)
なお、気泡の長さのアスペクト比の平均値は、X線CTスキャン装置(例えば、ヤマト科学株式会社製のTDM1000H−I)を用いて、以下のようにして求めることができる。
すなわち、まず、研磨面に垂直な方向のポリウレタン樹脂発泡体の断面画像を撮影し、この画像において観察される気泡を無作為に100個選んで、個々の気泡について、「研磨面に垂直な方向の気泡の長さ」、及び、「研磨面に平行した方向の気泡の長さ」を求め、気泡の長さのアスペクト比を求める。
そして、これらの気泡の長さのアスペクト比を算術平均し、この算術平均値を「気泡の長さのアスペクト比の平均値」とする。
なお、断面画像の気泡の外側輪郭線上において、研磨面に垂直な方向で相互の距離が最大となる2点を選び、この2点間の距離を「研磨面に垂直な方向の気泡の長さ」とする。また、断面画像の気泡の外側輪郭線上において、研磨面に平行な方向で相互の距離が最大となる2点を選び、この2点間の距離を「研磨面に平行した方向の気泡の長さ」とする。
なお、見掛け密度は、JIS K7222:2005に基づいて測定することができる。
また、前記ポリウレタン樹脂は、活性水素化合物とイソシアネート化合物とがウレタン結合して、活性水素化合物の第1の構成単位とイソシアネート化合物の第2の構成単位とが交互に繰り返した構造となっている。
なお、ポリオールポリマーとしては、ヒドロキシ基を分子中に3以上有する多官能ポリオールポリマーも挙げられる。
また、前記ポリウレタン樹脂は、ポリプロピレングリコール(PPG)を構成単位として含むことにより、比較的もろい構造を有することになり、その結果、研磨パッドのドレス時の切削速度が高まるという利点を有する。
さらに、本実施形態に係る研磨パッドは、前記ポリウレタン樹脂を100質量%としたときに、前記ポリウレタン樹脂の構成単位に含まれるポリプロピレングリコール(PPG)を、好ましくは30質量%以上、より好ましくは40〜70質量%、さらにより好ましくは60〜65質量%含有する。
まず、ポリウレタン樹脂発泡体を極性溶媒(重DMF、重DMSO等)に溶かして溶解物を得る。次に、該溶解物を1H−NMRで分析することより、ポリプロピレングリコール(PPG)を定量し、前記ポリプロピレングリコール(PPG)の含有割合を求める。
また、前記ポリプロピレングリコール(PPG)の含有割合の別の求め方としては、以下の方法がある。
まず、ポリウレタン樹脂発泡体をメタノールで化学分解して分解物を得る。次に、該分解物をゲル浸透クロマトグラフィー(GPC)等で分画し、各分取物を1H−NMR又はGC−MSで分析することより、ポリプロピレングリコール(PPG)を定量し、前記ポリプロピレングリコール(PPG)の含有割合を求める。
また、本実施形態に係る研磨パッドの製造方法では、末端基としてイソシアネート基を有するウレタンプレポリマーと、整泡剤とを混合することにより、空気が気泡として分散した分散液を得る。
そして、分散液と、活性水素を分子内に複数含む活性水素有機化合物たる硬化剤とを混合して重合することにより、ポリウレタン樹脂発泡体を有する研磨パッドを得ることができる。
前記整泡剤としては、シリコーン系界面活性剤、フッ素系界面活性剤、イオン性界面活性剤などが挙げられる。
すなわち、末端基としてイソシアネート基を有するウレタンプレポリマーと、水と、触媒とを混合することにより、ウレタンプレポリマーの末端基たるイソシアネート基と、水とを反応させてCO2を発生させ、CO2が気泡として分散した分散液を得る。
そして、分散液と、活性水素を分子内に複数含む活性水素有機化合物たる硬化剤とを混合して重合することにより、ポリウレタン樹脂発泡体を有する研磨パッドを得ることができる。
前記触媒は、イソシアネート基と、水との反応を促進させるためのものであり、前記触媒としては、3級アミン触媒、金属系触媒などが挙げられる。
また、本実施形態に係る研磨パッドは、仕上げ研磨、精密研磨等に好適に用いられる。
即ち、本実施形態に係る研磨パッドは、ポリウレタン樹脂発泡体を含む研磨パッドである。本実施形態に係る研磨パッドは、研磨面を有し、該研磨面が、前記ポリウレタン樹脂発泡体の表面で構成されている。前記ポリウレタン樹脂発泡体は、25℃でのtanδが0.24〜0.60である。
斯かる研磨パッドでは、前記tanδが大きい(0.24以上)ことにより、研磨時の被研磨物の微細振動を抑制でき、そして、研磨時の被研磨物のダンピングを抑制できる。その結果、研磨時において、研磨パッドと被研磨物とが密着しやすくなる。
よって、斯かる研磨パッドは、研磨速度を高めつつ、平坦性を高めることができる。
下記表1に示す、プレポリマーと、水と、触媒とを下記表1の配合割合で70℃下で混合することにより、プレポリマーの末端基たるイソシアネート基と、水とを反応させてCO2を発生させ、CO2が気泡として分散した分散液を得た。
次に、該分散液と、硬化剤とを混合して重合することにより、ポリウレタン樹脂発泡体たる研磨パッドを得た。
・プレポリマー1:ポリプロピレングリコール(PPG)と、トリレンジイソシアネート(TDI)とを反応させることで得られるウレタンプレポリマー(末端基としてイソシアネート基を有するウレタンプレポリマー)(NCOwt%:5.80)(タケネートL1150、三井化学社製)
・プレポリマー2:ポリテトラメチレンエーテルグリコール(PTMG)と、トリレンジイソシアネート(TDI)とを反応させることで得られるウレタンプレポリマー(末端基としてイソシアネート基を有するウレタンプレポリマー)(NCOwt%:6.00)(タケネートL2695、三井化学社製)
・プレポリマー3:ポリテトラメチレンエーテルグリコール(PTMG)と、トリレンジイソシアネート(TDI)とを反応させることで得られるウレタンプレポリマー(末端基としてイソシアネート基を有するウレタンプレポリマー)(NCOwt%:4.31)(タケネートL2690、三井化学社製)
・硬化剤:MOCA(4,4’−メチレンビス(2−クロロアニリン))
・整泡剤:シリコーン系界面活性剤(デコスターブB8465、エボニック社製)
・触媒:3級アミン系触媒(トヨキャットL33、東ソー社製)
また、下記表1のPPGの濃度は、ポリウレタン樹脂を100質量%としたときに、前記ポリウレタン樹脂の構成単位に含まれるポリプロピレングリコール(PPG)の濃度を意味する。
下記表1に示す材料及び配合にしたこと以外は、実施例1と同様にして、ポリウレタン樹脂発泡体たる研磨パッドを得た。
下記表1に示す、プレポリマーと、整泡剤とを下記表1の配合割合で70℃下で混合することにより、空気が気泡として分散した分散液を得た。
次に、該分散液と、硬化剤とを混合して重合することにより、ポリウレタン樹脂発泡体たる研磨パッドを得た。
下記表1に示す材料及び配合にしたこと以外は、実施例3と同様にして、ポリウレタン樹脂発泡体たる研磨パッドを得た。
市販のポリウレタン樹脂発泡体たる研磨パッドを用意した。
D硬度は、JIS K6253−1997に準拠して測定した。
具体的には、ポリウレタン発泡体を2cm×2cm(厚み:任意)の大きさに切り出したものを硬度測定用試料とし、該硬度測定用試料を温度23℃±2℃、湿度50%±5%の環境下に16時間静置した。
ここで、硬度測定用試料の厚みが6mm以上である場合には、この硬度測定用試料の硬度を硬度計(高分子計器社製、アスカーD型硬度計)で測定した。
一方で、硬度測定用試料の厚みが6mm未満である場合には、硬度測定用試料を複数厚み方向に重ね合わせて、重ね合せた硬度測定用試料の合計の厚みを6mm以上にし、重ね合せた硬度測定用試料の硬度を硬度計(高分子計器社製、アスカーD型硬度計)で測定した。
また、見掛け密度、tanδ、及び、E’については、上述した方法で測定した。
実施例及び比較例の研磨パッドを図1に示すようなドーナツ状に加工し(外径:240mm、内径:90mm、厚み:約2.0mm)、また、図1に点の位置を測定ポイント(12箇所)とし、この測定ポイントにφ約3mmの貫通孔を形成して、試験体を得た。
次に、両面テープを介して研磨装置(Ecomet2000)のプラテンに前記試験体を貼り付け、デプスゲージを用いて前記貫通孔において試験体の厚みを測定した。
そして、下記切削条件でパッドの表面を切削した。
パッドコンディショナー:AD3BI−100530−3(kinik社製のDiaGridφ4inch)
コンディション
Weight:35g/cm2
プラテンスピード:50rpm
ヘッドスピード:60rpm
ドレッシング時間:30min
水の流量:100mL/min
前記切削後に、デプスゲージを用いて前記貫通孔において試験体の厚みを測定した。
そして、各ポイントの切削前後の試験体の厚みの差から、各ポイントの切削速度(μm/hr)を求め、各ポイントの切削速度から切削速度の算術平均値を求めこれを研磨パッドの切削速度(μm/hr)とした。
実施例及び比較例の研磨パッドを用い、下記条件で被研磨物を研磨し、研磨レート(RR)、及び、研磨後における被研磨物の表面粗さの算術平均粗さ(Ra)を求めた。なお、研磨レート、及び、Raは、以下の方法で求めた。
結果を表2に示す。
被研磨物:シリコンベアウエハ(厚み:約760μm)
研磨機:ポリッシングマシンPNX332B、岡本工作機械製作所社製
ヘッドタイプ:ゴム
スラリーの流量:600mL/min
研磨回数:2回
スラリータイプ:NP7310x31
研磨時間:3min
プラテン/ガイドの圧力:(150g/cm2)/(200g/cm2)
ヘッドスピード:39rpm
プラテンスピード:40rpm
研磨レートは、研磨によって減少した厚みを研磨時間で割ることにより求めた。
なお、厚みは、Nano−metrics社製のnanospecAFT5100で測定した。
以下の条件でRaを測定した。なお、2回目の研磨後のRaを測定した。
装置:Bruker社製、Wyko NT9300
測定モード:PSI
内部レンズ:×1
対物レンズ:×50
視野範囲:94μm×125μm
Claims (7)
- ポリウレタン樹脂発泡体を含む研磨パッドであって、
研磨面を有し、
該研磨面が、前記ポリウレタン樹脂発泡体の表面で構成され、
前記研磨面を構成する前記ポリウレタン樹脂発泡体は、25℃でのtanδが0.24〜0.60であり、
前記ポリウレタン樹脂発泡体は、気泡径の平均値が60〜140μmである、研磨パッド。 - 前記ポリウレタン樹脂発泡体は、気泡径の変動係数が0.4〜0.6である、請求項1に記載の研磨パッド。
- 前記ポリウレタン樹脂発泡体では、気泡が、前記研磨面に垂直な断面において円形状となっている、請求項1又は2に記載の研磨パッド。
- 前記ポリウレタン樹脂発泡体は、見掛け密度が0.4〜0.6g/cm3である、請求項1〜3の何れか1項に記載の研磨パッド。
- 前記ポリウレタン樹脂発泡体は、45℃における貯蔵弾性率E’が0.5×107〜5.0×107Paである、請求項1〜4の何れか1項に記載の研磨パッド。
- 前記ポリウレタン樹脂発泡体は、65℃における貯蔵弾性率E’が0.3×107〜5.0×107Paである、請求項1〜5の何れか1項に記載の研磨パッド。
- 前記ポリウレタン樹脂発泡体が、ポリウレタン樹脂を含有し、
前記ポリウレタン樹脂が、ポリプロピレングリコールを構成単位として含む、請求項1〜6の何れか1項に記載の研磨パッド。