JP6935564B1 - 電子レンジ用グラビアインキ組成物、電子レンジ用印刷物、積層体、電子レンジ用印刷物の製造方法、積層体の製造方法、包装袋、蓋材及びラベル - Google Patents
電子レンジ用グラビアインキ組成物、電子レンジ用印刷物、積層体、電子レンジ用印刷物の製造方法、積層体の製造方法、包装袋、蓋材及びラベル Download PDFInfo
- Publication number
- JP6935564B1 JP6935564B1 JP2020161920A JP2020161920A JP6935564B1 JP 6935564 B1 JP6935564 B1 JP 6935564B1 JP 2020161920 A JP2020161920 A JP 2020161920A JP 2020161920 A JP2020161920 A JP 2020161920A JP 6935564 B1 JP6935564 B1 JP 6935564B1
- Authority
- JP
- Japan
- Prior art keywords
- microwave oven
- resin
- acid
- acetate copolymer
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
近年では、スーパー・コンビニエンスストアなどで販売されている軟包装製品に入れられた冷凍食品・レトルト・弁当類は、電子レンジにより加熱されることが一般的となってきた。しかし、電子レンジによる加熱はマイクロ波が用いられるため、軟包装製品に金属意匠を付与する目的でアルミ箔またはアルミ蒸着フィルムを用いると、金属の表面に反射したマイクロ波によるスパークが生じ、包装材が収縮する問題があった。この問題に対し、アルミニウム顔料のインキを印刷をすることにより、電子レンジ使用時のスパークを抑えた包装材が提案されている。
(1) 電子レンジ用グラビアインキ組成物が、プラスチック基材フィルムの少なくとも一方の面に、0.1〜3μmの膜厚でインキ層を積層してなる電子レンジ用印刷層を形成する電子レンジ用印刷物であって、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする、電子レンジ用印刷物。
(2) (1)に記載の電子レンジ用印刷物の電子レンジ用印刷層上に、シーラント層またはシール層を積層してなることを特徴とする積層体、
(3) プラスチック基材フィルムを準備する工程と、
該プラスチック基材フィルムの少なくとも一方に、電子レンジ用グラビアインキ組成物を0.1〜3μmの膜厚で印刷してなる電子レンジ用印刷層を形成するグラビア印刷工程と、を含む電子レンジ用印刷物の製造方法であって、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする電子レンジ用印刷物の製造方法、
(4) プラスチック基材フィルムを準備する工程と、
該プラスチック基材フィルムの少なくとも一方に、電子レンジ用グラビアインキ組成物を0.1〜3μmの膜厚で印刷してなる電子レンジ用印刷層を形成するグラビア印刷工程と、
シーラント層を積層するラミネート工程またはシール層を積層する塗工工程と、
を含む積層体の製造方法であって、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする積層体の製造方法、
(5) 外層から順に、プラスチック基材フィルムと、0.1〜3μmの膜厚の電子レンジ用印刷層と、シーラント層とを必須とする包装袋において、
前記電子レンジ用印刷層が、電子レンジ用グラビアインキ組成物にて形成され、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする包装袋、
(6) 外層から順に、プラスチック基材フィルムと、0.1〜3μmの膜厚の電子レンジ用印刷層と、シーラント層とを必須とする蓋材において、前記電子レンジ用印刷層が電子レンジ用グラビアインキ組成物にて形成され、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする蓋材、
(7) 外層から順に、プラスチック基材フィルムと、0.1〜3μmの膜厚の電子レンジ用印刷層と、シーラント層あるいはシール層とを必須とするラベルにおいて、前記電子レンジ用印刷層が電子レンジ用グラビアインキ組成物にて形成され、前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とするラベル、
に関するものである。
インキ組成物中に溶剤は45〜98質量%の範囲内であることが好ましい。45質量%より少ないと固形分が多くなり、流動性が悪くなり、インキ製造適性が劣り、98質量%を超えると、インキ膜厚が局部的に不均一になり、印刷面上に、不定形の濃淡(泳ぎ現象)が生じたり、粘度が低くなり、顔料が沈降しやすくなるおそれがある。
顔料としては、例えば、二酸化チタン、弁柄、硫酸バリウム、炭酸カルシウム、シリカ、酸化亜鉛、硫化亜鉛、マイカ、タルク、パールなどの無機顔料、フタロシアニン系、不溶性アゾ系、縮合アゾ系、ジオキサジン系、アントラキノン系、キナクリドン系、ペリレン系、ペリノン系、チオインジゴ系、カーボンブラックなどの有機顔料、その他各種蛍光顔料、金属粉顔料、体質顔料などが挙げられる。これらの顔料は、一種類または二種類類以上組み合わせて使用してもよい。染料としては、溶剤に溶解または分散するものが好ましく、一種類または二種類以上組み合わせて使用してもよい。なかでも、耐久性の観点から、顔料を用いることが好ましい。特に、黄色有機顔料を含有するとゴールド調の色相になり、高級感を付与することができる。
シーラント層の厚みは、特に制限はないが、シーラントフィルムでは2〜200μm、押出ラミネート法による樹脂コーティングでは1〜100μmの厚みであることが好ましい。
中間層としては、印刷適性、巻き取り適性などに支障のない範囲内であればよく、5〜300μmの厚みが好ましく、6〜250μmの厚みがより好ましい。
前記シーラント層を積層する工程は、例えば、ヒートシール性を付与した積層体や公知のシーラントフィルムの貼り合わせ、押出ラミネート加工による樹脂コーティングなどによる工程が挙げられ、前記シール層を積層する塗工工程は、ヒートシール剤やホットメルト剤の塗工などによる工程であってもよい。
前記印刷層、前記シーラント層またはシール層の他に、剛性、腰、ガスバリア性、保香性、防湿性、耐ピンホール性、デッドホール性、遮光性、直線カット性などの性能を付与または強化するための中間層を積層する工程を含んでもよい。
前記容器は、有底筒状の容器であることがさらに好ましい。この場合、蓋材が有底筒状の容器の開口部を覆い、密閉されていることが好ましく、ヒートシールによる密閉であることがさらに好ましい。
前記容器に用いられる樹脂は、ポリエチレン系、ポリプロピレン系、ポリエチレンテレフタレート、ポリ塩化ビニル、ポリスチレン、ポリアクリロニトリルなどの熱可塑性樹脂などが挙げられる。
さらに、電子レンジ用印刷層を形成した他方の面のプラスチック基材フィルムや他の基材上に粘着層や接着層を積層し、さらに離型層を積層することによりラベルとすることもできる。粘着層や接着層はゴム系粘着材料やアクリル樹脂系接着材料などプラスチック基材フィルムや他の基材と離型層に密着し、かつ離型層が容易に剥離することができるものであればいずれでもよい。離型層はポリエチレンフィルムやポリエステルフィルムあるいは紙(離型紙)などいずれでもよい。
カルボキシル基変性含有塩化ビニル・酢酸ビニル共重合体樹脂(ソルバインM5、酸価5.9mgKOH/g、日信化学工業(株)製) 20部、メチルエチルケトン(MEK) 80部を、ビーカーに入れ、600rpmで30分間攪拌し、固形分20%のカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂CL1を100部得た。
同様に、カルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂(カネビニールT5DA、酸価6.5mgKOH/g、(株)カネカ製)を用いて、固形分20%のカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂CL2、水酸基含有塩化ビニル・酢酸ビニル共重合体樹脂(ソルバインTAO、酸価0mgKOH/g、水酸基価98mgKOH/g、日信化学工業(株)製)を用いて、固形分20%の水酸基含有塩化ビニル・酢酸ビニル共重合体樹脂CL3、変性していない塩化ビニル・酢酸ビニル共重合体樹脂(ソルバインCL、酸価0mgKOH/g、日信化学工業(株)製)を用いて、固形分20%の塩化ビニル・酢酸ビニル共重合体樹脂CL4をそれぞれ得た。
アトマイズ法で製造された原料アルミニウム粉100g、オレイン酸3g、ミネラルスピリット500mLを原料として、これを3.2φのベアリングボール5kgと共に、ボールミル内に仕込み粉砕を行い、スラリーを得た。
粉砕終了後、スラリーを37μmの篩にかけて粗粒子を取り除いた後、フィルタープレスにより余分の溶剤を除去して固形分90% のケーキを得た。
得られたケーキを縦型ミキサー内に移し、ミネラルスピリットを加え、15分撹拌し、未処理アルミニウム顔料を含むアルミペーストA1を得た。該アルミペースト中の未処理アルミニウム顔料はノンリーフィングタイプであり、固形分70%であった。
(実施例1)
カルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂CL1 25部、ポリウレタン樹脂(固形分30%、東京インキ(株)製) 30部、アルミペーストA1(未処理アルミニウム顔料 70%) 5部、酢酸プロピル 40部を、ビーカーに仕込み、600rpmで30分攪拌させて、実施例1の電子レンジ用インキG1を100部得た。
同様に、表1および表2の配合に従い、実施例2〜6、比較例1〜6及び比較例8の各電子レンジ用インキG2〜G12及びG14を作製した。
カルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂CL1 25部、ポリウレタン樹脂(固形分30%、東京インキ(株)製) 30部、アルミペーストA2(樹脂コートアルミニウム顔料44%:BP−280PA、東洋アルミニウム株式会社 製) 5部、酢酸プロピル 40部を、ビーカーに仕込み、600rpmで30分攪拌させて、比較例7の電子レンジ用インキG13を100部得た。
グラビア校正機GRAVO−PROOF (品番:CM−W、(株)日商グラビア製)に彫刻ヘリオ版(コンプレスト スタイラス130°、70L/cm)を取り付け、電子レンジ用インキG1を希釈溶剤(MEK 40部、酢酸プロピル 40部、イソプロピルアルコール 20部)にて、ザーンカップNo.3で粘度17秒に調整した後、PETフィルム(E−5102、12μ、東洋紡(株)製)に膜厚1.1μmで印刷し、電子レンジ用印刷物PR1を得た。同様に、表3の通り、電子レンジ用インキと膜厚を変更し、それぞれ電子レンジ用印刷物PR5、PR6、PR7、PR8、PR9、PR12を得た。
電子レンジ用印刷物PR1の印刷層上にタケラックA−525/タケネートA−52(略称:DL、三井化学(株)製)をA−Bar OSP−10(オーエスジーシステムプロダクツ(株)製)により塗工して、厚み15μmのナイロンフィルムのエンブレムONMB−RT(ユニチカ(株)製)を貼り合わせ、さらに同様に、厚み60μmのCPPのトレファンNO ZK93KM(東レフィルム加工(株)製)を貼り合わせた後、50℃で72時間エージングを行って、積層体LAM1を得た。同様に、電子レンジ用印刷物PR5〜9、PR12に代えて、それぞれ積層体LAM5〜9、LAM12を得た。
前記電子レンジ用印刷物10cm×10cmにカットしたサンプルを、電子レンジ(品番:HMN−18B、HOSHIZAKI(株)製、高周波出力:1800W、丸皿:200mm)に入れて2分間加熱したときのサンプルを評価した。評価は目視による表面の状態観察と、レンジアップ後のサンプルを電子レンジから取り出した際の感触で熱さを評価した。これらの作業を、10人のパネラーで10回繰り返し行った。表面状態に変化がなく、マイクロ波による温度上昇が見られないものを1点、加熱後に印刷物が温まっているもしくは、加熱中に印刷物がスパークしたものを0点として、合計点を算出した。評価は、〇:合計点が90点以上、×:合計点が90点未満、の2段階で評価した。
前記電子レンジ用印刷物を用いて、サンプル表面にセロハンテープ(18mm、ニチバン(株)製)を貼り付けて、セロハンテープを剥がしたときの、印刷面のセロハンテープへの取られ具合を目視にて観察し、密着性を評価した。印刷面が剥離しないものを密着性が良好と判断した。密着性について、○:まったく剥がれない、×:少しでも剥がれる、の2段階で評価した。
標準光源(型式:Macbeth judgeII、X−Rite社製)下で、レンジアップ後のサンプルを用いて観察し、意匠性を評価した。金属光沢の意匠が認められるものを1点、金属光沢の意匠が認められないものを0点として、10人のパネラーが評価を行い、合計点を算出した。
評価は、〇:合計点が7以上、×:7未満、の2段階で評価した。
各積層体を15mm幅の短冊状にして、試験片とし、この試験片を5つ用意し、万能型引張試験機(RTE−1210、(株)オリエンテック製)にて、T型剥離、引張速度300mm/分にて、引っ張り、それぞれの試験片のラミネート強度を5回測定し、その平均値を算出した。印刷していない印刷物の積層体(ブランク試験片)についても、同様の試験を行ない、平均値を算出した。ラミネート強度について、〇:ブランク試験片の平均値に対し、80%以上のラミネート強度である、×:ブランク試験片の平均値に対し、80%未満の平均荷重である、の2段階で評価した。
特許文献1に類似の比較例1の電子レンジ用インキを使用した電子レンジ用印刷物(PR7)及び積層体(LAM7)は、レンジアップ性、意匠性、密着性、及びラミネート強度のいずれも劣ることが明確である。
特許文献2に類似の比較例7の電子レンジ用インキを使用した電子レンジ用印刷物(PR13)及び積層体(LAM13)は、意匠性が劣ることが明確である。
比較例2〜6の電子レンジ用インキを使用した電子レンジ用印刷物(PR8〜12)及び積層体(LAM8〜12)は、レンジアップ性、密着性、ラミネート強度、あるいは意匠性、のいずれかが劣ることが明確である。
また、膜厚が範囲外である電子レンジ用印刷物(PR14、PR15)及び積層体(LAM14、LAM15)は、レンジアップ性、意匠性、密着性、あるいはラミネート強度のいずれかが劣ることが明確である。
Claims (7)
- 電子レンジ用グラビアインキ組成物が、プラスチック基材フィルムの少なくとも一方の面に、0.1〜3μmの膜厚でインキ層を積層してなる電子レンジ用印刷層を形成する電子レンジ用印刷物であって、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする、電子レンジ用印刷物。 - 請求項1に記載の電子レンジ用印刷物の電子レンジ用印刷層上に、シーラント層またはシール層を積層してなることを特徴とする積層体。
- プラスチック基材フィルムを準備する工程と、
該プラスチック基材フィルムの少なくとも一方に、電子レンジ用グラビアインキ組成物を0.1〜3μmの膜厚で印刷してなる電子レンジ用印刷層を形成するグラビア印刷工程と、を含む電子レンジ用印刷物の製造方法であって、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする電子レンジ用印刷物の製造方法。 - プラスチック基材フィルムを準備する工程と、
該プラスチック基材フィルムの少なくとも一方に、電子レンジ用グラビアインキ組成物を0.1〜3μmの膜厚で印刷してなる電子レンジ用印刷層を形成するグラビア印刷工程と、
シーラント層を積層するラミネート工程またはシール層を積層する塗工工程と、
を含む積層体の製造方法であって、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする積層体の製造方法。 - 外層から順に、プラスチック基材フィルムと、0.1〜3μmの膜厚の電子レンジ用印刷層と、シーラント層とを必須とする包装袋において、
前記電子レンジ用印刷層が、電子レンジ用グラビアインキ組成物にて形成され、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする包装袋。 - 外層から順に、プラスチック基材フィルムと、0.1〜3μmの膜厚の電子レンジ用印刷層と、シーラント層とを必須とする蓋材において、前記電子レンジ用印刷層が電子レンジ用グラビアインキ組成物にて形成され、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とする蓋材。 - 外層から順に、プラスチック基材フィルムと、0.1〜3μmの膜厚の電子レンジ用印刷層と、シーラント層あるいはシール層とを必須とするラベルにおいて、前記電子レンジ用印刷層が電子レンジ用グラビアインキ組成物にて形成され、
前記電子レンジ用グラビアインキ組成物が、アトマイズ法で得られ重合処理のされていないアルミニウム顔料(A)と、熱可塑性樹脂(B)を含み、
前記熱可塑性樹脂(B)が、酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と、ポリウレタン樹脂(b2)とを含み、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)と前記ポリウレタン樹脂(b2)の固形分重量比が、(b1)/(b2)=5/95〜95/5であり、
前記酸変性塩化ビニル・酢酸ビニル共重合体樹脂(b1)が、酸価3〜30mgKOH/gのカルボキシル基変性塩化ビニル・酢酸ビニル共重合体樹脂であり、前記重合処理のされていないアルミニウム顔料(A)と熱可塑性樹脂(B)の固形分重量比が、(A)/(B)=60/40〜1/99であることを特徴とするラベル。