JP6582512B2 - Composite container and manufacturing method thereof, composite preform, plastic member, inner label member, and label - Google Patents
Composite container and manufacturing method thereof, composite preform, plastic member, inner label member, and label Download PDFInfo
- Publication number
- JP6582512B2 JP6582512B2 JP2015085099A JP2015085099A JP6582512B2 JP 6582512 B2 JP6582512 B2 JP 6582512B2 JP 2015085099 A JP2015085099 A JP 2015085099A JP 2015085099 A JP2015085099 A JP 2015085099A JP 6582512 B2 JP6582512 B2 JP 6582512B2
- Authority
- JP
- Japan
- Prior art keywords
- plastic member
- preform
- label
- composite
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、複合容器およびその製造方法、複合プリフォーム、プラスチック製部材、内側ラベル部材、ならびにラベルに関する。 The present invention relates to a composite container and a manufacturing method thereof, a composite preform, a plastic member, an inner label member, and a label.
近時、飲食品などの内容液を収容するボトルとして、プラスチック製のものが一般化してきており、このようなプラスチックボトルには内容液が収容される。 Recently, plastic bottles have been generalized as bottles for storing content liquids such as food and drink, and the content liquids are stored in such plastic bottles.
このような内容液を収容するプラスチックボトルは、金型内にプリフォームを挿入し、２軸延伸ブロー成形することにより製造される。 A plastic bottle containing such a content liquid is manufactured by inserting a preform into a mold and biaxially stretch-blow molding.
ところで、従来の２軸延伸ブロー成形法では、例えばＰＥＴやＰＰなどの単層材料、多層材料またはブレンド材料などを含むプリフォームを用いて容器形状に成形している。しかしながら、従来の２軸延伸ブロー成形法においては、単にプリフォームを容器形状に成形するだけであるのが一般的である。このため、容器に対して様々な機能や特性（バリア性や保温性など）を持たせる場合、例えばプリフォームを構成する材料を変更するなど、その手段は限定されてしまう。とりわけ、容器の部位（例えば胴部や底部）に応じて、異なる機能や特性を持たせることは難しい。 By the way, in the conventional biaxial stretch blow molding method, for example, a preform including a single layer material such as PET or PP, a multilayer material, or a blend material is used to mold into a container shape. However, in the conventional biaxial stretch blow molding method, the preform is generally simply formed into a container shape. For this reason, when various functions and characteristics (barrier property, heat retaining property, etc.) are given to the container, the means is limited, for example, the material constituting the preform is changed. In particular, it is difficult to have different functions and characteristics depending on the part of the container (for example, the trunk and the bottom).
本発明はこのような点を考慮してなされたものであり、容器に対して様々な機能や特性を付与することが可能な、ブロー成形方法、複合プリフォーム、複合容器、内側ラベル部材およびプラスチック製部材を提供することを目的とする。 The present invention has been made in view of the above points, and can provide a blow molding method, a composite preform, a composite container, an inner label member, and a plastic capable of imparting various functions and characteristics to the container. It aims at providing a manufacturing member.
本発明は、複合容器において、
プラスチック材料製の容器本体と、
前記容器本体の外面にプラスチック製部材と、を備え、
前記容器本体および前記プラスチック製部材は、ブロー成形により一体として膨張され、
前記プラスチック製部材に、ラベルが接着されており、
前記容器本体から、前記プラスチック製部材および前記ラベルを一体として分離回収することができることを特徴とする複合容器である。
The present invention relates to a composite container,
A container body made of plastic material;
A plastic member on the outer surface of the container body,
The container body and the plastic member are expanded integrally by blow molding,
A label is bonded to the plastic member,
The composite container is characterized in that the plastic member and the label can be separated and recovered as a unit from the container body.
本発明は、前記プラスチック製部材は、収縮チューブであることを特徴とする複合容器である。 The present invention is the composite container, wherein the plastic member is a shrinkable tube.
本発明は、前記プラスチック製部材および／または前記ラベルに印刷が施されていることを特徴とする複合容器である。 The present invention is the composite container, wherein the plastic member and / or the label is printed.
本発明は、前記容器本体の外側を取り囲むように密着して設けられた内側ラベル部材を更に備え、
前記プラスチック製部材は、前記内側ラベル部材の外側に密着して設けられていることを特徴とする複合容器である。
The present invention further comprises an inner label member provided in close contact so as to surround the outer side of the container body,
The plastic member is a composite container provided in close contact with the outside of the inner label member.
本発明は、複合容器の製造方法において、
プラスチック材料製のプリフォームを準備する工程と、
前記プリフォームの外側を取り囲むようにプラスチック製部材を設けることにより、前記プリフォームと、前記プリフォームの外側に密着された前記プラスチック製部材とを有する複合プリフォームを作製する工程と、
前記複合プリフォームを加熱するとともにブロー成形金型内に挿入する工程と、
前記ブロー成形金型内で前記複合プリフォームに対してブロー成形を施すことにより、前記複合プリフォームの前記プリフォームおよび前記プラスチック製部材を一体として膨張させることにより、容器本体と、前記容器本体の外側に密着して設けられたプラスチック製部材とを有する複合容器を製造する工程と、
前記複合容器の前記プラスチック製部材に、ラベルを接着する工程と、を備え、
前記プラスチック製部材および前記ラベルは一体として、前記容器本体から分離回収することができることを特徴とする複合容器の製造方法である。
The present invention relates to a method for producing a composite container,
Preparing a preform made of plastic material;
Providing a plastic member so as to surround the outside of the preform to produce a composite preform having the preform and the plastic member in close contact with the outside of the preform;
Heating the composite preform and inserting it into a blow mold; and
By subjecting the composite preform to blow molding with respect to the composite preform in the blow molding die, the preform and the plastic member of the composite preform are inflated integrally, and the container body and the container body Producing a composite container having a plastic member closely attached to the outside;
Adhering a label to the plastic member of the composite container,
In the method of manufacturing a composite container, the plastic member and the label can be separated and collected from the container main body as a unit.
本発明は、前記プラスチック製部材は、収縮チューブであることを特徴とする複合容器の製造方法である。 The present invention is the method for manufacturing a composite container, wherein the plastic member is a shrinkable tube.
本発明は、前記複合容器の前記プラスチック製部材に、ラベルを接着する工程の前に、前記プラスチック製部材に印刷を施す工程をさらに備えることを特徴とする複合容器の製造方法である。 The present invention is a method for manufacturing a composite container, further comprising a step of printing the plastic member before the step of bonding a label to the plastic member of the composite container.
本発明は、前記複合容器の前記プラスチック製部材に、ラベルを接着する工程の後に、前記プラスチック製部材および／または前記ラベルに印刷を施す工程をさらに備えることを特徴とする複合容器の製造方法である。 The present invention is a method for manufacturing a composite container, further comprising a step of printing the plastic member and / or the label after the step of adhering a label to the plastic member of the composite container. is there.
本発明は、前記プリフォームの外側を取り囲むように内側ラベル部材を設ける工程を更に備え、
前記プラスチック製部材は、前記内側ラベル部材の外側に設けられることを特徴とする複合容器の製造方法である。
The present invention further comprises a step of providing an inner label member so as to surround the outer side of the preform,
The plastic member is provided on the outside of the inner label member.
本発明は、上記複合容器の製造方法に用いられる複合プリフォームである。 This invention is a composite preform used for the manufacturing method of the said composite container.
本発明は、上記複合容器の製造方法に用いられるプラスチック製部材である。 This invention is a plastic member used for the manufacturing method of the said composite container.
本発明は、上記複合容器の製造方法に用いられる内側ラベル部材である。 This invention is an inner side label member used for the manufacturing method of the said composite container.
本発明は、上記複合容器の製造方法に用いられるラベルである。 This invention is a label used for the manufacturing method of the said composite container.
本発明によれば、ブロー成形金型内で複合プリフォームに対してブロー成形を施すことにより、複合プリフォームのプリフォームおよびプラスチック製部材を一体として膨張させる。このためプリフォーム（容器本体）とプラスチック製部材とを別部材から構成することができ、プラスチック製部材の種類や形状を適宜選択することにより、複合容器に様々な機能や特性を付与することができる。また、複合容器が備えるプラスチック製部材には、ラベルが接着されている。この、ラベルとプラスチック製部材とは、ラベルの分離回収の際、一体として回収することができ、分離回収工程を簡略化することができると共に、複合容器から、ラベルとプラスチック製部材とを分離回収した後の容器本体を従来通りリサイクルすることができる。 According to the present invention, the preform of the composite preform and the plastic member are expanded integrally by performing blow molding on the composite preform in the blow mold. For this reason, the preform (container body) and the plastic member can be formed of different members, and various functions and characteristics can be imparted to the composite container by appropriately selecting the type and shape of the plastic member. it can. Further, a label is bonded to the plastic member provided in the composite container. The label and the plastic member can be collected as a single unit when the label is separated and collected, the separation and collection process can be simplified, and the label and the plastic member are separated and collected from the composite container. After that, the container body can be recycled as usual.
第１の実施の形態
以下、図面を参照して本発明の第１の実施の形態について説明する。図１乃至図１１は本発明の第１の実施の形態を示す図である。
First Embodiment Hereinafter, a first embodiment of the present invention will be described with reference to the drawings. 1 to 11 are views showing a first embodiment of the present invention.
まず、図１および図２により、本実施の形態によるブロー成形方法によって作製される複合容器の概要について説明する。なお、本明細書中、「上」および「下」とは、それぞれ複合容器１０Ａを正立させた状態（図１参照）における上方および下方のことをいう。
First, an outline of a composite container produced by the blow molding method according to the present embodiment will be described with reference to FIGS. 1 and 2. In the present specification, “upper” and “lower” refer to the upper side and the lower side in a state where the
図１および図２に示す複合容器１０Ａは、後述するように、ブロー成形金型５０を用いてプリフォーム１０ａおよびプラスチック製部材４０ａを含む複合プリフォーム７０（図４参照）に対して２軸延伸ブロー成形を施すことにより、複合プリフォーム７０のプリフォーム１０ａおよびプラスチック製部材４０ａを一体として膨張させて得られたものである。
A
このような複合容器１０Ａは、内側に位置するプラスチック材料製の容器本体１０と、容器本体１０の外側に密着して設けられたプラスチック製部材４０とを備えており、さらにプラスチック製部材４０には、ラベル４３が接着されている。
Such a
このうち容器本体１０は、口部１１と、口部１１下方に設けられた首部１３と、首部１３下方に設けられた肩部１２と、肩部１２下方に設けられた胴部２０と、胴部２０下方に設けられた底部３０とを備えている。
Among these, the
他方、プラスチック製部材４０は、容器本体１０の外面に薄く延ばされた状態で密着されており、容器本体１０に対して容易に移動または回転しない状態で取付けられている。
On the other hand, the
次に容器本体１０について詳述する。容器本体１０は、上述したように口部１１と、首部１３と、肩部１２と、胴部２０と、底部３０とを有している。
Next, the
このうち口部１１は、図示しないキャップに螺着されるねじ部１４と、ねじ部１４下方に設けられたフランジ部１７とを有している。なお、口部１１の形状は、従来公知の形状であっても良い。
Of these, the
首部１３は、フランジ部１７と肩部１２との間に位置しており、略均一な径をもつ略円筒形状を有している。また、肩部１２は、首部１３と胴部２０との間に位置しており、首部１３側から胴部２０側に向けて徐々に径が拡大する形状を有している。
The
さらに、胴部２０は、全体として略均一な径をもつ円筒形状を有している。しかしながら、これに限られるものではなく、胴部２０が四角形筒形状や八角形筒形状などの多角形筒形状を有していても良い。あるいは、胴部２０が上方から下方に向けて均一でない水平断面をもつ筒形状を有していても良い。また、本実施の形態において、胴部２０は、凹凸が形成されておらず、略平坦な表面を有しているが、これに限られるものではない。例えば、胴部２０にパネルまたは溝などの凹凸が形成されていても良い。
Furthermore, the trunk | drum 20 has a cylindrical shape with a substantially uniform diameter as a whole. However, the present invention is not limited to this, and the
一方、底部３０は、中央に位置する凹部３１と、この凹部３１周囲に設けられた接地部３２とを有している。なお、底部３０の形状についても特に限定されるものではなく、従来公知の底部形状（例えばペタロイド底形状や丸底形状など）を有していても良い。
On the other hand, the
また胴部２０における容器本体１０の厚みは、これに限定されるものではないが、例えば５０μｍ〜２５０μｍ程度に薄くすることができる。さらに、容器本体１０の重量についても、これに限定されるものではないが、１０ｇ〜２０ｇとすることができる。このように容器本体１０の肉厚を薄くすることにより、容器本体１０の軽量化を図ることができる。
Moreover, although the thickness of the container
このような容器本体１０は、合成樹脂材料を射出成形して製作したプリフォーム１０ａ（後述）を二軸延伸ブロー成形することにより作製することができる。なおプリフォーム１０ａ、すなわち容器本体１０の材料としては熱可塑性樹脂、特に、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレンナフタレート（ＰＥＮ）、ポリカーボネート（ＰＣ）を使用することが好ましい。また、上述した各種樹脂をブレンドして用いても良い。容器本体１０は、赤色、青色、黄色、緑色、茶色、黒色、白色などの色に着色されていても良いが、リサイクルのしやすさを考慮した場合、無色透明であることが好ましい。さらに、容器本体１０の内面に、容器のバリア性を高めるために、例えばダイヤモンド状炭素膜や酸化珪素薄膜などの蒸着膜を形成しても良い。
Such a container
また、容器本体１０は、２層以上の多層成形ボトルとして形成することもできる。すなわち押し出し成形または射出成形により、例えば、中間層をＭＸＤ−６（ナイロン）、ＭＸＤ−６＋脂肪酸塩、ポリグリコール酸（ＰＧＡ）、エチレンビニルアルコール共重合体（ＥＶＯＨ）またはＰＥＮなどのガスバリア性および遮光性を有する樹脂（中間層）として３層以上からなるプリフォーム１０ａを押出成形後、ブロー成形することによりガスバリア性および遮光性を有する多層ボトルとして形成しても良い。なお、中間層としては、上述した各種樹脂をブレンドした樹脂を用いても良い。
The
また、熱可塑性樹脂の溶融物に不活性ガス（窒素ガス、アルゴンガス）を混ぜることで、０．５〜１００μｍの発泡セル径を持つ発泡プリフォームを成形し、この発泡プリフォームをブロー成形することによって、容器本体１０を作製しても良い。このような容器本体１０は、発泡セルを内蔵しているため、容器本体１０全体の遮光性を高めることができる。
Further, by mixing an inert gas (nitrogen gas, argon gas) with the thermoplastic resin melt, a foam preform having a foam cell diameter of 0.5 to 100 μm is formed, and this foam preform is blow-molded. Thus, the
このような容器本体１０は、例えば満注容量が１００ｍｌ〜２０００ｍｌのボトルからなっていても良い。あるいは、容器本体１０は、満注容量が例えば１０Ｌ〜６０Ｌの大型のボトルであっても良い。
Such a container
次にプラスチック製部材４０について説明する。プラスチック製部材４０（４０ａ）は後述するようにプリフォーム１０ａの外側を取り囲むように設けられ、プリフォーム１０ａの外側に密着された後、プリフォーム１０ａとともに２軸延伸ブロー成形されることにより得られたものである。
Next, the
プラスチック製部材４０は容器本体１０の外面に接着されることなく取付けられており、容器本体１０に対して移動または回転しないほどに密着されている。このプラスチック製部材４０は、容器本体１０の外面において薄く引き延ばされて容器本体１０を覆っている。また、図２に示すように、プラスチック製部材４０は、容器本体１０を取り囲むようにその周方向全域にわたって設けられており、略円形状の水平断面を有している。
The
この場合、プラスチック製部材４０は、容器本体１０のうち、口部１１および首部１３を除く、肩部１２、胴部２０および底部３０を覆うように設けられている。これにより、容器本体１０の肩部１２、胴部２０および底部３０に対して所望の機能や特性を付与することができる。
In this case, the
なお、プラスチック製部材４０は、容器本体１０のうち口部１１以外の全域または一部領域に設けられていても良い。例えば、プラスチック製部材４０は、容器本体１０のうち、口部１１を除く、首部１３、肩部１２、胴部２０および底部３０の全体を覆うように設けられていても良い。さらに、プラスチック製部材４０は１つに限らず、複数設けても良い。例えば、２つのプラスチック製部材４０を肩部１２の外面および底部３０の外面にそれぞれ設けても良い。
Note that the
また、プラスチック製部材４０には、開口４４（剥離用開口）を設けることができる。この開口４４は、複数設け、プラスチック製部材４０の長手方向に沿って切断領域４５が形成されていることが好ましい。プラスチック製部材４０がこのような複数の開口４４を有していることにより、ラベル４３およびプラスチック製部材４０を容器本体１０からさらに容易に分離回収することができる。また、複数の開口４４は、容器本体１０の胴部２０に対応する位置であって、プラスチック製部材４０のラベル４３が接着される位置に設けられていることが好ましい（図３参照）。これにより、開口４４を設けたことにより、分離回収工程前に誤ってプラスチック製部材４０が剥離してしまうことを防止できるとともに、ラベル４３およびプラスチック製部材４０を容器本体１０からさらに容易に分離回収することができる。
The
開口４４の形状としては、例えば、円形状、長方形状、楕円形状、角丸長方形状、菱形形状、三角形状、五角形状、矢羽根形状、六角形状等が挙げられるが、これに限定されるものではない。また、容器本体１０に装着された状態で、プラスチック製部材４０の開口４４の幅（径）は、１０ｍｍ以下となることが好ましい。なお、容器本体１０に装着された状態で、プラスチック製部材４０の隣接する開口同士の最短距離は、５ｍｍ以下とすることが好ましい。これにより、複数の開口を、プラスチック製部材４０を剥離する時のガイドとして用いることができる。
Examples of the shape of the
またプラスチック製部材４０の厚みは、これに限定されるものではないが、容器本体１０に取り付けられた状態で例えば５μｍ〜５０μｍ程度とすることができる。
Moreover, although the thickness of the
本実施の形態において、プラスチック製部材４０には、ラベル４３が接着されている。このように、プラスチック製部材にラベル４３が接着されており、その一方で、プラスチック製部材４０は、容器本体１０に対して溶着ないし接着されていないため、複合容器１０Ａからラベル４３を分離回収する際に、プラスチック製部材４０を合わせて回収することが可能となる。これにより、ラベル４３およびプラスチック製部材４０を容器本体１０から分離回収することができ、従来と同様に無色透明な容器本体１０をリサイクルすることができる。また、ラベル４３とプラスチック製部材４０とを一体として回収することができるため、分離回収工程を簡略化することができる。
In the present embodiment, a
一実施形態において、ラベル４３およびプラスチック製部材４０は、例えば刃物などを用いてラベル４３および／またはプラスチック製部材４０に切り込みを入れることにより、分離回収することができる。また、別の実施形態において、ラベル４３および／またはプラスチック製部材４０に予め図示しない切断線を設け、この切断線に沿ってラベル４３および／またはプラスチック製部材４０を剥離することにより、分離回収することができる。さらにラベル４３が、後述するロールラベル、ロールオンシュリンクラベルなどの場合には、プラスチック製部材４０に巻き付け、接着したラベル４３の端部に、プラスチック製部材４０とは接着されていない摘まみ片を設け、この摘まみ片を引っ張ることより、分離回収することもできる。さらに、ラベル４３がプラスチック製部材４０に対して強固に接着されているので、ラベル４３を引っ張ることによりラベル４３とともにプラスチック製部材４０を容器本体１０から剥離するようにしても良い。
In one embodiment, the
プラスチック製部材とラベル４３との接着に用いられる接着剤としては、プラスチック製部材４０とラベル４３とが一体として、容器本体１０から分離回収することができる程度にこれらを接着できるものであれば、特に限定されず、例えば、シアノアクリレート系接着剤、シリコーン系接着剤、エポキシ系接着剤、などが挙げられる。接着剤は、プラスチック製部材４０のうちラベル４３が設けられる領域全体に塗布されてもよく、一部に塗布されてもよい。
As an adhesive used for bonding the plastic member and the
接着剤を、プラスチック製部材４０のうちラベル４３が設けられる一部に塗布する場合、塗布箇所４６としては、以下のような態様が、より容易にラベル４３およびプラスチック製部材４０を容器本体１０から分離回収することができるため好ましい。（１）ラベル４３の周方向両端への塗布（図４参照）、（２）プラスチック製部材４０が複数の開口を有する場合、その開口に沿っての塗布（図５参照）。
In the case where the adhesive is applied to a part of the
ラベル４３には、印刷が施された印刷領域が設けられていることが好ましい。印刷領域に表示される事項としては、図柄や商品名などのほか、内容液の名称、製造者、原材料名などの文字情報であっても良い。ラベル４３は、一部または全域が、赤色、青色、黄色、緑色、茶色、黒色、白色などの色に着色されていても良く、さらに透明であっても不透明であっても良い。
The
ラベル４３を備える複合容器１０Ａとしては、例えば、図６（ａ）に示すように、プラスチック製部材４０の一部を覆うようにラベル４３が取り付けられたものを挙げることができる。また、図６（ｂ）に示すように、ラベル４３がプラスチック製部材４０の全域を覆うように取り付けられたものを挙げることができる。また、図６（ｃ）に示すように、ラベル４３がプラスチック製部材４０の全域を覆うように設けられ、さらにラベルの文字を表示する部分が透明となっており、プラスチック製部材４０が着色された構成のものを挙げることができる。また、これに限らず、プラスチック製部材４０と、ラベル４３とに互いに異なる絵柄を印刷しておき、これらプラスチック製部材４０およびラベル４３を互いに重ねることにより、一つの絵となる構成や、立体感を持たせた構成とすることもできる（図示せず。）。
As
ラベル４３としては、例えば、シュリンクラベル、ストレッチラベル、ロールラベル、ロールオンシュリンクラベルなどを挙げることができる。以下、各ラベルの態様について説明する。これらは、プラスチック製部材４０全域または一部を覆うように巻装させることができる。これらの中でも、ロールラベルおよびロールオンシュリンクラベルが好ましい。
Examples of the
一実施形態において、シュリンクラベルは、筒状のシュリンクラベル原反を、接着剤が塗布されたプラスチック製部材４０に装着し、温度８０〜９０度でシュリンク加工することにより得ることができる。
In one embodiment, the shrink label can be obtained by attaching a cylindrical shrink label raw material to a
筒状のシュリンクラベル原反は、ポリ乳酸系フィルム、ポリスチレン系フィルム、ポリエステル系フィルム、低密度ポリエチレンフィルム、中密度ポリエチレンフィルム、高密度ポリエチレンフィルム、低密度直鎖状ポリエチレンフィルム、環状ポリオレフィンフィルム、ポリプロピレンフィルム、エチレン−プロピレン共重合体、エチレン−酢酸ビニル共重合体、アイオノマー樹脂、エチレン−アクリル酸共重合体、エチレン−アクリル酸メチル共重合体などの樹脂から製膜された遠心ポリオレフィンフィルム、ポリエステル−ポリスチレン多層フィルム、不織布と収縮フィルムとのラミネートフィルム、ポリエステル−ポリスチレン共押出フィルム、６−ナイロンフィルム、６，６−ナイロンフィルムなどのポリアミドフィルム、塩素化ポリエチレン、塩素化ポリプロピレンなどの樹脂から製膜された変性ポリオレフィンフィルム、塩化ビニル−酢酸ビニル共重合体の樹脂から製膜されたフィルム、アクリル系樹脂フィルムなどの樹脂フィルムを用いて作製することができる。例えば、２枚の樹脂フィルムの長手方向の両端を重ねて、成形することで筒状のシュリンクラベル原反を作製することができる。 Raw material of cylindrical shrink label is polylactic acid film, polystyrene film, polyester film, low density polyethylene film, medium density polyethylene film, high density polyethylene film, low density linear polyethylene film, cyclic polyolefin film, polypropylene Film, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, ionomer resin, ethylene-acrylic acid copolymer, centrifugal polyolefin film formed from resin such as ethylene-methyl acrylate copolymer, polyester- Polystyrene multilayer film, laminated film of nonwoven fabric and shrink film, polyester-polystyrene coextruded film, polyamide film such as 6-nylon film, 6,6-nylon film, chlorination It can be prepared using a modified polyolefin film formed from a resin such as reethylene or chlorinated polypropylene, a film formed from a vinyl chloride-vinyl acetate copolymer resin, or a resin film such as an acrylic resin film. . For example, a cylindrical shrink label original fabric can be produced by stacking and molding both ends of two resin films in the longitudinal direction.
上記樹脂フィルムは、それを構成する樹脂の１種または２種以上を使用し、押し出し法、キャスト成形法、Ｔダイ法、切削法、インフレーション法、その他などの製膜化法を用いて単層で製膜したもの、または２種以上の樹脂を使用して共押し出しなどで多層製膜したもの、または２種以上の樹脂を混合使用して製膜し、テンター方式やチューブラー方式などで一軸または二軸方向に延伸してなる各種樹脂フィルムを使用することができるが、延伸フィルムであって、流れ方向の一軸延伸フィルムが好ましい。またこれらフィルムは、発泡フィルムであってもよい。 The above-mentioned resin film is a single layer using one or more kinds of resins constituting the resin film and using a film forming method such as an extrusion method, cast molding method, T-die method, cutting method, inflation method, etc. , Film formed by co-extrusion using two or more types of resin, or film formed using a mixture of two or more types of resin, and uniaxial with a tenter method or a tubular method, etc. Alternatively, various resin films obtained by stretching in the biaxial direction can be used, but a stretched film, preferably a uniaxially stretched film in the flow direction. These films may be foamed films.
本発明では、断熱性が高いという点から、延伸ポリエステル系フィルム、延伸ポリスチレン系フィルム、延伸ポリオレフィン系フィルム、ポリ乳酸系フィルム、発泡ポリオレフィン系フィルム、延伸ポリエステル−ポリスチレン共押出しフィルムまたは発泡ポリスチレン系フィルム、ポリエステル−ポリスチレン多層フィルムなどを好適に使用することができ、または不織布と前記フィルムとの積層フィルムであってもよい。なお、延伸フィルムは、一軸延伸であっても、二軸延伸であってもよく、一軸延伸フィルムの場合は、縦一軸延伸であっても、横一軸延伸であってもよい。 In the present invention, a stretched polyester film, a stretched polystyrene film, a stretched polyolefin film, a polylactic acid film, a foamed polyolefin film, a stretched polyester-polystyrene coextruded film or a foamed polystyrene film, because of its high heat insulation properties, A polyester-polystyrene multilayer film or the like can be suitably used, or a laminated film of a nonwoven fabric and the film may be used. The stretched film may be uniaxially stretched or biaxially stretched. In the case of a uniaxially stretched film, it may be longitudinally uniaxially stretched or laterally uniaxially stretched.
シュリンクラベルの厚みは、これに限定されるものではないが、プラスチック製部材４０に接着された状態で例えば１０μｍ〜８０μｍ程度とすることができる。
Although the thickness of a shrink label is not limited to this, For example, it can be about 10 micrometers-80 micrometers in the state adhere | attached on the
一実施形態において、ストレッチラベルは、周方向に引っ張られた状態で接着剤が塗布されたプラスチック製部材４０に被嵌され、その後、引っ張り力を取り除くことにより収縮し、プラスチック製部材４０に追従し、巻装させることにより得ることができる。
In one embodiment, the stretch label is fitted on the
ストレッチラベルは、適度な柔軟性を有する熱可塑性樹脂フィルム、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、低密度直鎖状ポリエチレン、ポリプロピレンなどのポリオレフィン樹脂からなる単層または多層樹脂フィルムを用いて作製することができる。その中でも、低密度直鎖状ポリエチレンからなる単層フィルム、低密度直鎖状ポリエチレンからなる層を備える多層フィルムを用いて作製することが好ましい。これらフィルムは上記した方法により作製することができる。 Stretch labels are thermoplastic resin films with moderate flexibility, such as single-layer or multilayer resin films made of polyolefin resins such as low-density polyethylene, medium-density polyethylene, high-density polyethylene, low-density linear polyethylene, and polypropylene. Can be used. Among these, it is preferable to produce using a single layer film made of low density linear polyethylene and a multilayer film provided with a layer made of low density linear polyethylene. These films can be produced by the method described above.
ストレッチラベルの厚みは、これに限定されるものではないが、プラスチック製部材４０に接着された状態で例えば５μｍ〜５０μｍ程度とすることができる。
The thickness of the stretch label is not limited to this, but can be, for example, about 5 μm to 50 μm in a state where the stretch label is adhered to the
一実施形態において、ロールラベルは、樹脂フィルムを接着剤を塗布したプラスチック製部材４０に巻き付け、さらに樹脂フィルムの両端部を接着または融着することにより得ることができる。
In one embodiment, the roll label can be obtained by winding a resin film around a
ロールラベルは、上記した樹脂フィルムを用いて作製することができる。樹脂フィルムの両端部を接着に用いる接着剤としては、例えば、ポリ酢酸ビニル系接着剤、ポリアクリル酸エステル系接着剤、シアノアクリレート系接着剤、エチレン共重合体接着剤、セルロース系接着剤、ポリエステル系接着剤、ポリアミド系接着剤、ポリイミド系接着剤、アミノ樹脂系接着剤、フェノール樹脂系接着剤、エポキシ系接着剤、ポリウレタン系接着剤、ゴム系接着剤、シリコーン系接着剤などが挙げられる。 The roll label can be produced using the resin film described above. Examples of the adhesive that uses both ends of the resin film for adhesion include, for example, polyvinyl acetate adhesive, polyacrylate adhesive, cyanoacrylate adhesive, ethylene copolymer adhesive, cellulose adhesive, and polyester. Adhesives, polyamide adhesives, polyimide adhesives, amino resin adhesives, phenol resin adhesives, epoxy adhesives, polyurethane adhesives, rubber adhesives, silicone adhesives, and the like.
ロールラベルの厚みは、これに限定されるものではないが、プラスチック製部材４０に接着された状態で、例えば５μｍ〜１００μｍ程度とすることができる。
Although the thickness of a roll label is not limited to this, In the state adhere | attached on the
一実施形態において、ロールオンシュリンクラベルは、筒状シュリンクラベル原反の作製に使用した樹脂フィルムを、接着剤を塗布したプラスチック製部材４０に巻き付け、次いで、樹脂フィルムの両端部をロールラベルの作製に使用した接着剤などを用いて接着または融着し、さらに、温度８０〜９０度でシュリンク加工することにより得ることができる。
In one embodiment, the roll-on-shrink label is obtained by winding a resin film used for producing a cylindrical shrink-label raw material around a
ロールラベルオンシュリンクラベルの厚みは、これに限定されるものではないが、プラスチック製部材４０に接着された状態で、例えば１０μｍ〜１００μｍ程度とすることができる。
Although the thickness of a roll label on shrink label is not limited to this, For example, it can be about 10 micrometers-100 micrometers in the state adhere | attached on the
次に図７により、本実施の形態による複合プリフォーム７０の構成について説明する。
Next, the configuration of the
図７に示すように、複合プリフォーム７０は、プラスチック材料製のプリフォーム１０ａと、プリフォーム１０ａの外側に設けられた有底円筒状のプラスチック製部材４０ａとを備えている。
As shown in FIG. 7, the
このうちプリフォーム１０ａは、口部１１ａと、口部１１ａに連結された胴部２０ａと、胴部２０ａに連結された底部３０ａとを備えている。このうち口部１１ａは、上述した容器本体１０の口部１１に対応するものであり、口部１１と略同一の形状を有している。また、胴部２０ａは、上述した容器本体１０の首部１３、肩部１２および胴部２０に対応するものであり、略円筒形状を有している。底部３０ａは、上述した容器本体１０の底部３０に対応するものであり、略半球形状を有している。
Among these, the
プラスチック製部材４０ａは、プリフォーム１０ａの外面に接着されることなく取付けられており、プリフォーム１０ａに対して移動または回転しないほどに密着されているか、または自重で落下しない程度に密着されている。プラスチック製部材４０ａは、プリフォーム１０ａを取り囲むようにその周方向全域にわたって設けられており、円形状の水平断面を有している。
The
この場合、プラスチック製部材４０ａは、胴部２０ａのうち容器本体１０の首部１３に対応する部分１３ａを除く全域と、底部３０ａの全域とを覆うように設けられている。
In this case, the
なお、プラスチック製部材４０ａは、口部１１ａ以外の全域または一部領域に設けられていても良い。例えば、プラスチック製部材４０ａは、口部１１ａを除く、胴部２０ａおよび底部３０ａの全体を覆うように設けられていても良い。さらに、プラスチック製部材４０ａは１つに限らず、複数設けても良い。例えば、２つのプラスチック製部材４０ａを胴部２０ａの外側２箇所にそれぞれ設けても良い。
The
このようなプラスチック製部材４０ａ（４０）としては、プリフォーム１０ａに対して収縮する作用をもたないものであっても良く、収縮する作用をもつものであっても良い。ブロー成形後において、容器本体１０と、プラスチック製部材４０との間に入り込む空気が少ない、即ち、密着性が高いという観点からは、プラスチック製部材４０ａは、プリフォーム１０ａに対して収縮する作用をもつもの（収縮チューブ）であることが好ましい。
Such a
前者の場合、プラスチック製部材４０ａ（４０）としては、例えばブロー成形により作製されたブローチューブ、シート成形により作製されたシート成形チューブ、押出成形により作製された押出チューブ、インフレーション成形により作製されたインフレーション成形チューブ、射出成形により作製された射出成形チューブなどを用いることができるが、これに限定されるものではなく、上記以外の成形方法を用いても良い。
In the former case, as the
一方、プラスチック製部材４０ａ（４０）が収縮する作用をもつ場合、プラスチック製部材４０ａ（４０）は、例えば、外的な作用（例えば熱）が加えられた際、プリフォーム１０ａに対して収縮（例えば熱収縮）するものが用いられても良い。あるいは、プラスチック製部材４０ａ（４０）は、それ自体が収縮性ないし弾力性を持ち、外的な作用を加えることなく収縮可能なものであっても良い。
On the other hand, when the
プラスチック製部材４０ａ（４０）は、上記したように多層からなるものであってもよく、例えば、最内面と最外面との層を構成する主成分が同じであっても、異なっていてもよい。具体的な層構成としては、最内面から、低密度ＰＥ／接着層／ＥＶＯＨ／接着層／低密度ＰＥのもの、ＰＰ／接着層／ＥＶＯＨ／接着層／ＰＰのものが挙げられる。接着層を構成する接着剤としては、例えば、ポリ酢酸ビニル系接着剤、ポリアクリル酸エステル系接着剤、シアノアクリレート系接着剤、エチレン共重合体接着剤、セルロース系接着剤、ポリエステル系接着剤、ポリアミド系接着剤、ポリイミド系接着剤、アミノ樹脂系接着剤、フェノール樹脂系接着剤、エポキシ系接着剤、ポリウレタン系接着剤、ゴム系接着剤、シリコーン系接着剤などが挙げられる。
The
プラスチック製部材４０ａ（４０）は、例えば、ＰＥ、ＰＰ、ＰＥＴ、ＰＥＮ、ポリ−４−メチルペンテン−１、ポリスチレン、ＡＳ樹脂、ＡＢＳ樹旨、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリ酢酸ビニル、ポリビニルアルコール、ポリビニルアセタール、ポリビニルブチラール、フタル酸ジアリル樹脂、フッ素系樹脂、ポリメタクリル酸メチル、ポリアクリル酸、ポリアクリル酸メチル、ポリアクリロニトリル、ポリアクリルアミド、ポリブタジエン、ポリブテン−１、ポリイソプレン、ポリクロロプレン、エチレンプロピレンゴム、ブチルゴム、ニトリルゴム、アクリルゴム、シリコーンゴム、フッ素ゴム、ナイロン６、ナイロン６，６、ＭＸＤ−６、芳香族ポリアミド、ＰＣ、ポリテレフタル酸エチレン、ポリテレフタル酸ブチレン、ポリナフタレン酸エチレン、Ｕポリマー、液晶ポリマー、変性ポリフェニレンエーテル、ポリエーテルケトン、ポリエーテルエーテルケトン、不飽和ポリエステル、アルキド樹脂、ポリイミド、ポリスルホン、ポリフェニレンスルフィド、ポリエーテルスルホン、シリコーン樹脂、ポリウレタン、フェノール樹脂、尿素樹脂、ポリエチレンオキシド、ポリプロピレンオキシド、ポリアセタール、エポキシ樹脂などを含んでなる樹脂材料を用いて作製することができる。このうち、ＰＥ、ＰＰ、ＰＥＴ、ＰＥＮなどの熱可塑性非弾性樹脂を含ませることが好ましい。また、樹脂材料は、上記した樹脂を構成する２以上のモノマー単位が重合した共重合体を含んでいても良い。さらに、樹脂材料は上記した樹脂を２種以上を含んでなるものであってよい。また、熱可塑性樹脂の溶融物に不活性ガス（窒素ガス、アルゴンガス）を混ぜることで、０．５〜１００μｍの発泡セル径を持つ発泡部材を使用し、この発泡プリフォームを成形することによって、遮光性を高めることができる。
The
また、プラスチック製部材４０ａ（４０）は、着色剤を含んでなることができる。着色剤の含有量は、プラスチック製部材４０ａ（４０）が単層である場合、樹脂材料の総量に対し、０．０１〜１０質量％であることが好ましく、０．１〜３．０質量％であることがより好ましく、０．５〜２．０質量％であることがさらに好ましい。また、プラスチック製部材４０ａ（４０）が多層からなる場合、着色剤を含む層が含む樹脂材料の総量に対し、０．０１〜１０質量％であることが好ましく、０．１〜３．０質量％であることがより好ましく、０．５〜２．０質量％であることがさらに好ましい。着色剤の含有量が上記数値範囲内であれば、樹脂性能の変化を極力抑えることができ、色調が安定的に成形できる。なお、プラスチック製部材４０ａ（４０）が多層からなる場合、着色剤を含む層が２以上であってもよい。
Further, the
着色剤は、茶色、黒色、緑色、白色、青色または赤色などの着色剤を使用することができる。着色剤は、顔料であっても、染料であってもよいが、耐光性という観点からは、顔料であることが好ましい。上記した着色剤の中でも、光反射性顔料である、チタンホワイト、アルミニウム粉、マイカ粉、硫化亜鉛、亜鉛華、炭酸カルシウム、カオリン、タルクなどの白色顔料、光吸収性顔料である、カーボンブラック、セラミックブラック、ボーンブラックなどの有色顔料が好ましい。着色層がこれらのような顔料を含んでなることにより、ブロー成形後のプラスチック製部材４０の可視光の透過率を低下させることができ、複合容器１０Ａに充填される内容液の品質変化を防止することができる。
As the colorant, a colorant such as brown, black, green, white, blue, or red can be used. The colorant may be a pigment or a dye, but is preferably a pigment from the viewpoint of light resistance. Among the colorants described above, light reflecting pigments such as titanium white, aluminum powder, mica powder, zinc sulfide, zinc white, calcium carbonate, kaolin, talc and other white pigments, light absorbing pigments, carbon black, Colored pigments such as ceramic black and bone black are preferred. By including such pigments in the colored layer, it is possible to reduce the visible light transmittance of the
またプラスチック製部材４０ａ（４０）は、その特性が損なわれない範囲において、主成分である上記の樹脂以外にも、各種の添加剤を添加してもよい。添加剤としては、例えば、可塑剤、紫外線安定化剤、着色防止剤、艶消し剤、消臭剤、難燃剤、耐候剤、帯電防止剤、糸摩擦低減剤、スリップ剤、離型剤、抗酸化剤、イオン交換剤、架橋剤、架橋助剤および着色顔料などを添加することができる。また、熱可塑性樹脂の溶融物に不活性ガス（窒素ガス、アルゴンガス）を混ぜることで、０．５〜１００μｍの発泡セル径を持つ発泡部材を使用し、この発泡プリフォームを成形することによって、遮光性を高めることができる。
In addition, the
またプラスチック製部材４０ａ（４０）がプリフォーム１０ａ（容器本体１０）と同一の材料を含んでいても良い。また、プラスチック製部材４０ａ（４０）が多層からなる場合、プラスチック製部材４０ａ（４０）は、プリフォーム１０ａ（容器本体１０）と同一の材料からなる層を備えていても良い。この場合、ブロー成形後、複合容器１０Ａにおいて、例えば強度を高めたい部分に重点的にプラスチック製部材４０ａを配置し、当該箇所の強度を選択的に高めることができる。例えば、容器本体１０の肩部１２周辺および底部３０周辺にプラスチック製部材４０を設け、この部分の強度を高めても良い。このような材料としては、熱可塑性樹脂、特にＰＥ、ＰＰ、ＰＥＴ、ＰＥＮ、ＰＣを挙げることができる。
The
またプラスチック製部材４０ａ（４０）は、酸素バリア性または水蒸気バリア性などのガスバリア性を有する材料を含んでいても良い。また、プラスチック製部材４０ａ（４０）が多層からなる場合、プラスチック製部材４０ａ（４０）は、酸素バリア性または水蒸気バリア性などのガスバリア性を有する材料からなる層を備えていても良い。この場合、プリフォーム１０ａとして多層プリフォームやブレンド材料を含むプリフォームなどを用いることなく、複合容器１０Ａのガスバリア性を高め、容器内への酸素の侵入を防ぎ、内容液が劣化することを防止し、また、容器内から外部への水蒸気の蒸散を防ぎ、内容量が減少することを防止することができる。例えば、容器本体１０のうち、肩部１２、首部１３、胴部２０および底部３０の全域にプラスチック製部材４０を設け、この部分のガスバリア性を高めても良い。このような材料としては、ＰＥ、ＰＰ、ＭＸＤ−６、ＥＶＯＨまたはこれらの材料に脂肪酸塩などの酸素吸収材を混ぜることも考えられる。
The
またプラスチック製部材４０ａ（４０）は、紫外線などの光線バリア性を有する材料を含んでいても良い。また、プラスチック製部材４０ａ（４０）が多層からなる場合、プラスチック製部材４０ａ（４０）は、紫外線などの光線バリア性を有する材料からなる層を備えていても良い。この場合、プリフォーム１０ａとして多層プリフォームやブレンド材料を含むプリフォームなどを用いることなく、複合容器１０Ａの光線バリア性を高め、紫外線などにより内容液が劣化することを防止することができる。例えば、容器本体１０のうち、肩部１２、首部１３、胴部２０および底部３０の全域にプラスチック製部材４０を設け、この部分の紫外線バリア性を高めても良い。このような材料としては、ブレンド材料、またはＰＥＴやＰＥ、ＰＰに遮光性樹脂を添加した材料が考えられる。また、熱可塑性樹脂の溶融物に不活性ガス（窒素ガス、アルゴンガス）を混ぜることにより作製された、０．５〜１００μｍの発泡セル径を持つ発泡部材を使用しても良い。
The
またプラスチック製部材４０ａ（４０）は、プリフォーム１０ａ（容器本体１０）を構成するプラスチック材料よりも保温性または保冷性の高い材料（熱伝導性の低い材料）を含んでいても良い。また、プラスチック製部材４０（４０ａ）が多層からなる場合、プラスチック製部材４０（４０ａ）は、プリフォーム１０ａ（容器本体１０）を構成するプラスチック材料よりも保温性または保冷性の高い材料（熱伝導性の低い材料）からなる層を備えていても良い。この場合、容器本体１０そのものの厚みを厚くすることなく、内容液の温度が複合容器１０Ａの表面まで伝達しにくくすることが可能となる。これにより、複合容器１０Ａの保温性または保冷性が高められる。例えば、容器本体１０のうち胴部２０の全部または一部にプラスチック製部材４０を設け、胴部２０の保温性または保冷性を高めても良い。また、使用者が複合容器１０Ａを把持した際、熱すぎたり冷たすぎたりすることにより複合容器１０Ａを持ちにくくなることが防止される。このような材料としては、発泡化したポリウレタン、ポリスチレン、ＰＥ、ＰＰ、フェノール樹脂、ポリ塩化ビニル、ユリア樹脂、シリコーン、ポリイミド、メラミン樹脂などが考えられる。また、熱可塑性樹脂の溶融物に不活性ガス（窒素ガス、アルゴンガス）を混ぜることにより作製された、０．５〜１００μｍの発泡セル径を持つ発泡部材を使用しても良い。これら樹脂を含んでなる樹脂材料に、中空粒子を混合することが好ましい。中空粒子の平均粒子径は、１〜２００μｍであることが好ましく、５〜８０μｍであることがより好ましい。なお、「平均粒子径」とは、体積平均粒子径を意味し、粒度分布・粒径分布測定装置（例えば、ナノトラック粒度分布測定装置、日機装株式会社製など）を用いて公知の方法により測定することができる。また、中空粒子としては、樹脂などから構成される有機系中空粒子であってもよく、ガラスなどから構成される無機系中空粒子であってもよいが、分散性が優れるという理由から、有機系中空粒子が好ましい。有機系中空粒子を構成する樹脂としては、例えば、架橋スチレン−アクリル樹脂などのスチレン系樹脂、アクリロニトリル−アクリル樹脂などの（メタ）アクリル系樹脂、フェノール系樹脂、フッ素系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、ポリカーボネート系樹脂、ポリエーテル系樹脂などを挙げることができる。また、ローペイクＨＰ−１０５５、ローペイクＨＰ−９１、ローペイクＯＰ−８４Ｊ、ローペイクウルトラ、ローペイクＳＥ、ローペイクＳＴ（ロームアンドハース（株）製）、ニポールＭＨ−５０５５（日本ゼオン（株）製）、ＳＸ８７８２、ＳＸ８６６（ＪＳＲ（株）製）などの市販される中空粒子を用いることもできる。中空粒子の含有量としては、プラスチック製部材４０ａが単層からなる場合、プラスチック製部材４０ａに含有される樹脂材料１００質量部に対して、０．０１〜５０質量部であることが好ましく、１〜２０質量部であることがより好ましい。プラスチック製部材４０ａが多層からなる場合、中空粒子を含有する層が含む樹脂材料１００質量部に対して、０．０１〜５０質量部であることが好ましく、１〜２０質量部であることがより好ましい。
Further, the
またプラスチック製部材４０ａ（４０）は、プリフォーム１０ａ（容器本体１０）を構成するプラスチック材料よりも滑りにくい材料を含んでいても良い。また、プラスチック製部材４０ａ（４０）が多層からなる場合、プラスチック製部材４０ａ（４０）は、プリフォーム１０ａ（容器本体１０）を構成するプラスチック材料よりも滑りにくい材料からなる層を最外層として備えていても良い。この場合、容器本体１０の材料を変更することなく、使用者が複合容器１０Ａを把持しやすくすることができる。例えば、容器本体１０のうち胴部２０の全部または一部にプラスチック製部材４０を設け、胴部２０を持ちやすくしても良い。
The
さらにプラスチック製部材４０ａ（４０）には、デザインまたは印字が施されていても良い。例えば、容器本体１０のうち胴部２０の全部または一部にプラスチック製部材４０を設け、胴部２０に画像や文字を表示しても良い。印刷は、例えばインクジェット法、グラビア印刷法、オフセット印刷法、フレキソ印刷法などの印刷法により、無地のプラスチック製部材４０ａにデザインまたは印字が施されて形成されても良い。例えば、インクジェット法を用いる場合、プラスチック製部材４０ａにＵＶ硬化型インクを塗布し、これにＵＶ照射を行い、硬化することにより印刷層を形成させることができる。この印刷は、プリフォーム１０ａに取り付けられる前のプラスチック製部材４０ａに対して施されても良く、プリフォーム１０ａの外側にプラスチック製部材４０ａを設けた状態で施されても良い。さらに、ブロー成形後であって、ラベル４３の接着前に複合容器１０Ａのプラスチック製部材４０に印刷を施しても良く、ラベル４３の接着後に印刷が施されてもよい。ラベル４３の接着後に印刷を施す場合、印刷の一部が、ラベル４３に掛かってしまってもよく、例えば、プラスチック製部材４０とラベル４３とを互いに重ねることにより、一つの絵となる構成や、立体感を持たせた構成としてもよい。
Further, the
プラスチック製部材４０の材料としては、容器本体１０と同一のものを用いても良く、容器本体１０と異なるものを用いても良い。また、プラスチック製部材４０ａは、一部または全域が、赤色、青色、黄色、緑色、茶色、黒色、白色などの色に着色されていても良く、さらに透明であっても不透明であっても良い。
As a material of the
次に、プラスチック製部材４０ａの形状について説明する。
Next, the shape of the
図７および図８（ａ）に示すように、プラスチック製部材４０ａは、全体として有底円筒形状からなり、円筒状の胴部４１と、胴部４１に連結された底部４２とを有していても良い。この場合、プラスチック製部材４０ａの底部４２がプリフォーム１０ａの底部３０ａを覆うので、複合容器１０Ａの胴部２０に加え、底部３０に対しても様々な機能や特性を付与することができる。このようなプラスチック製部材４０ａは、例えば上述したブローチューブやシート成形チューブ、射出成形チューブを挙げることができる。
As shown in FIGS. 7 and 8A, the
また、図８（ｂ）に示すように、プラスチック製部材４０ａは、全体として円管形状（無底円筒形状）からなり、円筒状の胴部４１を有していても良い。この場合、プラスチック製部材４０ａとしては、例えば上述したブローチューブ、押出チューブ、インフレーション成形チューブ、シート成形チューブ、射出成形チューブを用いることができる。
Further, as shown in FIG. 8B, the
また、図８（ｃ）および図８（ｄ）に示すように、プラスチック製部材４０ａは、フィルムを筒状に形成してその端部を貼り合わせることにより作製されても良い。この場合、図８（ｃ）に示すように、プラスチック製部材４０ａは、胴部４１を有する管形状（無底円筒形状）に構成されていても良く、図８（ｄ）に示すように、底部４２を貼り合わせることにより有底筒形状に構成されていても良い。この場合、プラスチック製部材４０ａとしては、例えばブローチューブ、押出チューブ、インフレーション成形チューブ、シート成形チューブを用いることができる。
Moreover, as shown in FIG.8 (c) and FIG.8 (d), the
次に、プラスチック製部材４０ａの製造方法について説明する。
Next, a method for manufacturing the
一実施形態において、プラスチック製部材４０ａは、樹脂材料を含んでなる樹脂シートを成形することにより製造することができる。成形方法としては、例えば、深絞り成形、または樹脂シートをチューブ状に成形し、その端部を融着、または接着する方法などが挙げられる。また、多層からなるプラスチック製部材４０ａは、２以上の樹脂シートを、上記した接着剤を介して積層させた積層樹脂シートを成形することにより得ることができる。
In one embodiment, the
上記樹脂シートは、市販品を用いてもよいし、従来公知の方法により製造することができる。本発明においては、押出成形により製造することが好ましく、押出成形が、Ｔダイ法またはインフレーション法により行われることが好ましい。 A commercial item may be used for the said resin sheet, and it can manufacture it by a conventionally well-known method. In this invention, it is preferable to manufacture by extrusion molding, and it is preferable that extrusion molding is performed by the T-die method or the inflation method.
例えば、以下の方法で、押出成形により樹脂シートを成形することができる。上記した樹脂材料を乾燥させた後、熱可塑性樹脂の融点以上の温度（Ｔｍ）〜Ｔｍ＋７０℃の温度に加熱された溶融押出機に供給して、樹脂材料を加熱溶融し、例えばＴダイなどのダイよりシート状に押出し、押し出されたシート状物を回転している冷却ドラムなどで急冷固化することにより樹脂シートを成形することができる。溶融押出機としては、一軸押出機、二軸押出機、ベント押出機、タンデム押出機などを目的に応じて使用することができる。 For example, a resin sheet can be formed by extrusion molding according to the following method. After drying the resin material described above, the resin material is supplied to a melt extruder heated to a temperature not lower than the melting point of the thermoplastic resin (Tm) to Tm + 70 ° C. to heat and melt the resin material. A resin sheet can be formed by extruding into a sheet form from a die and rapidly cooling and solidifying the extruded sheet form with a rotating cooling drum or the like. As the melt extruder, a single screw extruder, a twin screw extruder, a vent extruder, a tandem extruder, or the like can be used depending on the purpose.
加熱温度は、インフレーション法では、好ましくは１７０〜２３０℃、より好ましくは１８０〜２２０℃、Ｔダイ法では好ましくは１８０〜３００℃、より好ましくは２１０〜２７０℃である。
上記の樹脂材料は、例えば、０．３〜３０ｇ／１０分、インフレーション法では好ましくは０．３〜８ｇ／１０分、０．３〜６ｇ／１０分、Ｔダイ法では好ましくは０．３〜２０ｇ／１０分、より好ましくは４〜１５ｇ／１０分のメルトフローレート（ＭＦＲ）を有するものである。メルトフローレートとは、ＪＩＳ Ｋ７２１０−１９９５に規定された方法において、温度１９０℃、荷重２１．１８Ｎの条件で、Ａ法により測定される値である。樹脂材料のＭＦＲが０．３ｇ／１０分以上であれば、成形加工時の押出負荷を低減することができる。また、樹脂材料のＭＦＲが３０ｇ／１０分以下であれば、該樹脂材料からなる樹脂シートの機械的強度を高めることができる。
The heating temperature is preferably 170 to 230 ° C., more preferably 180 to 220 ° C. in the inflation method, and preferably 180 to 300 ° C., more preferably 210 to 270 ° C. in the T-die method.
The resin material is, for example, 0.3 to 30 g / 10 minutes, preferably 0.3 to 8 g / 10 minutes, 0.3 to 6 g / 10 minutes in the inflation method, and preferably 0.3 to 0.3 in the T-die method. It has a melt flow rate (MFR) of 20 g / 10 min, more preferably 4 to 15 g / 10 min. The melt flow rate is a value measured by the method A under the conditions of a temperature of 190 ° C. and a load of 21.18 N in the method defined in JIS K7210-1995. If the MFR of the resin material is 0.3 g / 10 min or more, the extrusion load during the molding process can be reduced. Moreover, if MFR of a resin material is 30 g / 10min or less, the mechanical strength of the resin sheet which consists of this resin material can be raised.
一実施形態において、プラスチック製部材４０ａは、加熱溶融した樹脂材料をチューブ状に押し出すことによっても製造することができる。多層からなるプラスチック製部材４０ａは、この樹脂材料を多層押し出しすることにより得ることができる。また、押し出しを金型内で行い、さらにその金型内において、金型の内面に沿って拡径するようにブロー成形することによっても、プラスチック製部材４０ａを得ることができる。
In one embodiment, the
また、さらに上記樹脂材料を押し出すことにより得られたチューブの一端を接着、溶着などにより閉鎖する。一端を閉鎖したチューブを、チューブの外径よりも大きい内径を有するチューブ状の金型内に配置し、チューブの他端にブロー装置を配置する。このとき、ブロー装置は、チューブと、これらの間からエアが漏れないよう密着させることが好ましい。次いで、このチューブ、金型およびブロー装置を、この配置のまま加熱炉に送り込み、加熱炉の内部で７０〜１５０℃に加熱する。加熱炉としては、その内部を均一な温度にするために、熱風循環式加熱炉を用いても良い。あるいはチューブ、金型およびブロー装置を、加熱した液体中を通過させることにより、これらを加熱しても良い。次に、チューブ、金型およびブロー装置を、加熱炉から取り出し、ブロー装置からチューブ内にエアを噴出することにより、チューブの内面を加圧延伸する。これにより、チューブは、膨張し、金型の内面形状に沿って拡径される。その後、ブロー装置からエアを噴出した状態のまま、チューブを冷水中で冷却し、チューブを金型から取り出す。これを所望の大きさにカットすることにより収縮性を有するプラスチック製部材４０ａが得られる。
Further, one end of the tube obtained by extruding the resin material is closed by adhesion, welding or the like. The tube closed at one end is placed in a tube-shaped mold having an inner diameter larger than the outer diameter of the tube, and a blow device is placed at the other end of the tube. At this time, it is preferable that the blow device is in close contact with the tube so that air does not leak from between them. Next, the tube, the mold and the blow device are fed into the heating furnace in this arrangement and heated to 70 to 150 ° C. inside the heating furnace. As the heating furnace, a hot-air circulating heating furnace may be used in order to make the inside uniform. Or you may heat these by making a tube, a metal mold | die, and a blowing apparatus pass in the heated liquid. Next, the tube, the mold and the blow device are taken out of the heating furnace, and air is blown into the tube from the blow device, whereby the inner surface of the tube is pressurized and stretched. Thereby, a tube expand | swells and diameter-expands along the inner surface shape of a metal mold | die. Thereafter, the tube is cooled in cold water while air is blown from the blow device, and the tube is taken out of the mold. By cutting this into a desired size, a
一実施形態において、収縮性を有するプラスチック製部材４０ａは、加熱溶融した樹脂材料および架橋剤または／および架橋助剤をチューブ状に押し出し、次いで、電子線を照射することにより架橋反応を行い、さらに加熱しつつ拡径したのちに冷却固定することにより得ることができる。また、所望により、電子線照射後、プラスチック製部材４０ａを拡径してもよい。ここで、電子線の線量は１〜１０００ｋＧｙであることが好ましく、５０〜２５０ｋＧｙであることがより好ましい。また、電子線の加速電圧は５０〜３０００ｋＶであることが好ましく、１００〜１５００ｋＶであることがより好ましい。また電子線以外の電離性放射線でもよく、ガンマ線等が挙げられる。
In one embodiment, the
また、一実施形態において、プラスチック製部材４０ａは、射出成形法によっても得ることができる。具体的には、まず、樹脂材料、着色剤および紫外線吸収剤の混合物を加熱溶融する。次いで、加熱溶融した混合物を金型内に射出する。これを冷却し、金型内から取り出すことによっても、プラスチック製部材４０ａを得ることができる。
In one embodiment, the
次に図９（ａ）〜（ｆ）により、本実施の形態による複合容器１０Ａの製造方法（ブロー成形方法）について説明する。
Next, a manufacturing method (blow molding method) of the
まず、プラスチック材料製のプリフォーム１０ａを準備する（図９（ａ）参照）。この場合、例えば図示しない射出成形機を用いて、射出成形法によりプリフォーム１０ａを作製しても良い。また、プリフォーム１０ａとして、従来一般に用いられるプリフォームを用いても良い。
First, a
次に、プリフォーム１０ａの外側にプラスチック製部材４０ａを設けることにより、プリフォーム１０ａと、プリフォーム１０ａの外側に密着されたプラスチック製部材４０ａとを有する複合プリフォーム７０を作製する（図９（ｂ）参照）。この場合、プラスチック製部材４０ａは、全体として有底円筒形状からなり、円筒状の胴部４１と、胴部４１に連結された底部４２とを有している。このプラスチック製部材４０ａは、胴部２０ａのうち容器本体１０の首部１３に対応する部分を除く全域と、底部３０ａの全域とを覆うように装着される。
Next, by providing a
この場合、プリフォーム１０ａの外径と同一またはわずかに小さい内径をもつプラスチック製部材４０ａを、プリフォーム１０ａに対して押し込むことにより、プリフォーム１０ａの外面に密着させても良い。あるいは、後述するように、熱収縮性をもつプラスチック製部材４０ａをプリフォーム１０ａの外面に設け、このプラスチック製部材４０ａを５０℃乃至１００℃に加熱することにより熱収縮させてプリフォーム１０ａの外面に密着させても良い。
In this case, a
このように、予めプリフォーム１０ａの外側にプラスチック製部材４０ａを密着させ、複合プリフォーム７０を作製しておくことにより、複合プリフォーム７０を作製する一連の工程（図９（ａ）〜（ｂ））と、複合容器１０Ａをブロー成形により作製する一連の工程（図９（ｃ）〜（ｆ））とを別々の場所（工場など）で実施することが可能になる。
In this manner, a series of steps for producing the composite preform 70 (FIGS. 9A to 9B) are performed by previously bringing the
次に、複合プリフォーム７０は、加熱装置５１によって加熱される（図９（ｃ）参照）。このとき、複合プリフォーム７０は、口部１１ａを下に向けた状態で回転しながら、加熱装置５１によって周方向に均などに加熱される。この加熱工程におけるプリフォーム１０ａおよびプラスチック製部材４０ａの加熱温度は、例えば９０℃乃至１３０℃としても良い。
Next, the
続いて、加熱装置５１によって加熱された複合プリフォーム７０は、ブロー成形金型５０に送られる（図９（ｄ）参照）。
Subsequently, the
複合容器１０Ａは、このブロー成形金型５０を用いて成形される。この場合、ブロー成形金型５０は互いに分割された一対の胴部金型５０ａ、５０ｂと、底部金型５０ｃとからなる（図９（ｄ）参照）。図９（ｄ）において、一対の胴部金型５０ａ、５０ｂ間は互いに開いており、底部金型５０ｃは上方に上がっている。この状態で一対の胴部金型５０ａ、５０ｂ間に、複合プリフォーム７０が挿入される。
The
次に図９（ｅ）に示すように、底部金型５０ｃが下がったのちに一対の胴部金型５０ａ、５０ｂが閉鎖され、一対の胴部金型５０ａ、５０ｂおよび底部金型５０ｃにより密閉されたブロー成形金型５０が構成される。次にプリフォーム１０ａ内に空気が圧入され、複合プリフォーム７０に対して２軸延伸ブロー成形が施される。
Next, as shown in FIG. 9 (e), after the
このことにより、ブロー成形金型５０内でプリフォーム１０ａから容器本体１０が得られる。この間、胴部金型５０ａ、５０ｂは３０℃乃至８０℃まで加熱され、底部金型５０ｃは５℃乃至２５℃まで冷却される。この際、ブロー成形金型５０内では、複合プリフォーム７０のプリフォーム１０ａおよびプラスチック製部材４０ａが一体として膨張される。これにより、プリフォーム１０ａおよびプラスチック製部材４０ａは、一体となってブロー成形金型５０の内面に対応する形状に賦形される。
As a result, the
このようにして、容器本体１０と、容器本体１０の外面に設けられたプラスチック製部材４０とを備えた複合容器１０Ａが得られる。
In this manner, a
次に図９（ｆ）に示すように、一対の胴部金型５０ａ、５０ｂおよび底部金型５０ｃが互いに離れ、ブロー成形金型５０内から複合容器１０Ａが取出される。
Next, as shown in FIG. 9 (f), the pair of
複合容器１０Ａの製造方法の変形例
次に、図１０（ａ）〜（ｆ）により、本実施の形態によるブロー成形方法（複合容器１０Ａの製造方法）の変形例について説明する。図１０（ａ）〜（ｆ）に示す変形例は、プラスチック製部材４０ａがプリフォーム１０ａに対して収縮する作用をもつもの（収縮チューブ）であり、他の構成は、図９（ａ）〜（ｆ）に示す形態と略同一である。図１０（ａ）〜（ｆ）において、図９（ａ）〜（ｆ）と同一部分には同一の符号を付して詳細な説明は省略する。
Modified Example of Manufacturing Method of
まず、プラスチック材料製のプリフォーム１０ａを準備する（図１０（ａ）参照）。
First, a
次に、プリフォーム１０ａの外側にプラスチック製部材４０ａを設ける（図１０（ｂ）参照）。この場合、プラスチック製部材４０ａは、全体として有底円筒形状からなり、円筒状の胴部４１と、胴部４１に連結された底部４２とを有している。このプラスチック製部材４０は、胴部２０ａのうち容器本体１０の首部１３に対応する部分を除く全域と、底部３０ａの全域とを覆うように装着される。
Next, a
次に、プリフォーム１０ａおよびプラスチック製部材４０ａは、加熱装置５１によって加熱される（図１０（ｃ）参照）。このとき、プリフォーム１０ａおよびプラスチック製部材４０ａは、口部１１ａを下に向けた状態で回転しながら、加熱装置５１によって周方向に均などに加熱される。この加熱工程におけるプリフォーム１０ａおよびプラスチック製部材４０ａの加熱温度は、例えば９０℃乃至１３０℃としても良い。
Next, the
このように、プラスチック製部材４０ａが加熱されることにより、プラスチック製部材４０ａが熱収縮し、プリフォーム１０ａの外側に密着する（図１０（ｃ）参照）。なお、プラスチック製部材４０ａ自体が収縮性を有する場合、プリフォーム１０ａの外側にプラスチック製部材４０ａを設けた時点（図１０（ｂ）参照）でプラスチック製部材４０ａがプリフォーム１０ａの外側に密着していても良い。
Thus, by heating the
続いて、加熱装置５１によって加熱されたプリフォーム１０ａおよびプラスチック製部材４０ａは、ブロー成形金型５０に送られる（図１０（ｄ）参照）。
Subsequently, the
プリフォーム１０ａおよびプラスチック製部材４０ａは、このブロー成形金型５０を用いて成形され、上述した図９（ａ）〜（ｆ）の場合と略同様にして、容器本体１０と、容器本体１０の外面に設けられたプラスチック製部材４０とを備えた複合容器１０Ａが得られる（図１０（ｄ）〜（ｆ）参照）。
The
次に図１１（ａ）〜（ｇ）により、本実施の形態による複合容器１０Ａの製造方法の他の変形例について説明する。図１１（ａ）〜（ｇ）に示す変形例は、プラスチック製部材４０ａがプリフォーム１０ａに対して収縮する作用をもち（収縮チューブ）、プリフォーム１０ａおよびプラスチック製部材４０ａを２段階で加熱するものであり、他の構成は、図９（ａ）〜（ｆ）に示す形態と略同一である。図１１（ａ）〜（ｇ）において、図９（ａ）〜（ｆ）と同一部分には同一の符号を付して詳細な説明は省略する。
Next, another modification of the method for manufacturing the
まず、プラスチック材料製のプリフォーム１０ａを準備する（図１１（ａ）参照）。
First, a
次に、プリフォーム１０ａの外側にプラスチック製部材４０ａを設ける（図１１（ｂ）参照）。この場合、プラスチック製部材４０ａは、全体として有底円筒形状からなり、円筒状の胴部４１と、胴部４１に連結された底部４２とを有している。このプラスチック製部材４０は、胴部２０ａのうち容器本体１０の首部１３に対応する部分を除く全域と、底部３０ａの全域とを覆うように装着される。
Next, a
次に、プリフォーム１０ａおよびプラスチック製部材４０ａは、第１の加熱装置５５によって加熱される（図１１（ｃ）参照）。このとき、プリフォーム１０ａおよびプラスチック製部材４０ａの加熱温度は、例えば５０℃乃至１００℃としても良い。
Next, the
プラスチック製部材４０ａが加熱されることにより、プラスチック製部材４０ａが熱収縮し、プリフォーム１０ａの外側に密着する。これにより、プリフォーム１０ａと、プリフォーム１０ａの外側に密着されたプラスチック製部材４０ａとを有する複合プリフォーム７０が得られる（図１１（ｃ）参照）。
When the
このように、第１の加熱装置５５を用いて予めプリフォーム１０ａの外側にプラスチック製部材４０ａを加熱密着させ、複合プリフォーム７０を作製しておくことにより、複合プリフォーム７０を作製する一連の工程（図１１（ａ）〜（ｃ））と、複合容器１０Ａをブロー成形により作製する一連の工程（図１１（ｄ）〜（ｇ））とを別々の場所（工場など）で実施することが可能になる。
In this way, a series of the
次に、複合プリフォーム７０は、第２の加熱装置５１によって加熱される（図１１（ｄ）参照）。このとき、複合プリフォーム７０は、口部１１ａを下に向けた状態で回転しながら、第２の加熱装置５１によって周方向に均などに加熱される。この加熱工程におけるプリフォーム１０ａおよびプラスチック製部材４０ａの加熱温度は、例えば９０℃乃至１３０℃としても良い。
Next, the
続いて、第２の加熱装置５１によって加熱された複合プリフォーム７０は、ブロー成形金型５０に送られる（図１１（ｅ）参照）。
Subsequently, the
複合プリフォーム７０は、このブロー成形金型５０を用いて成形され、上述した図９（ａ）〜（ｆ）の場合と略同様にして、容器本体１０と、容器本体１０の外面に設けられたプラスチック製部材４０とを備えた複合容器１０Ａが得られる（図１１（ｅ）〜（ｇ）参照）。
The
以上説明したように、本実施の形態によれば、ブロー成形金型５０内で複合プリフォーム７０に対してブロー成形を施すことにより、複合プリフォーム７０のプリフォーム１０ａおよびプラスチック製部材４０ａを一体として膨張させ、容器本体１０とプラスチック製部材４０とを備えた複合容器１０Ａを作製する。これにより、プリフォーム１０ａ（容器本体１０）とプラスチック製部材４０ａ（プラスチック製部材４０）とを別部材から構成することができる。したがって、プラスチック製部材４０の種類や形状を適宜選択することにより、複合容器１０Ａに様々な機能や特性を自在に付与することができる。
As described above, according to the present embodiment, the
また、本実施の形態によれば、複合容器１０Ａを作製する際、一般的なブロー成形装置をそのまま用いることができるので、複合容器１０Ａを作製するための新たな成形設備を準備する必要が生じない。
Further, according to the present embodiment, when the
変形例
次に図１２、図１３および図１４（ａ）〜（ｆ）により本発明の第１の実施の形態の変形例について説明する。
Modified Example Next, a modified example of the first embodiment of the present invention will be described with reference to FIGS. 12, 13 and 14A to 14F.
図１２、図１３および図１４（ａ）〜（ｆ）に示す変形例は、プラスチック製部材４０ａとして胴部と底部とを有するものではなく、円筒状のプラスチック製部材４０ａを用いたものである。
The modification shown in FIGS. 12, 13, and 14A to 14F does not have a body portion and a bottom portion as the
図１２に示す複合容器１０Ａにおいて、プラスチック製部材４０は、容器本体１０の肩部１２から胴部２０の下方部分まで延びているが、底部３０まで達していない。また、図１３に示す複合プリフォーム７０において、プラスチック製部材４０ａはプリフォーム１０ａの胴部２０ａのみを覆うように密着されており、より詳細には、胴部２０ａのうち容器本体１０の首部１３に対応する部分１３ａと胴部２０ａの下部に対応する部分とを除く領域を覆っている。
In the
図１２、図１３および図１４（ａ）〜（ｆ）において他の構成は、図１乃至図１１に示す実施の形態と略同一である。図１２、図１３および図１４（ａ）〜（ｆ）に示す変形例において、図１乃至図８に示す実施の形態と同一部分には同一符号を付して詳細な説明は省略する。 Other configurations in FIGS. 12, 13 and 14A to 14F are substantially the same as those in the embodiment shown in FIGS. In the modification shown in FIGS. 12, 13 and 14A to 14F, the same parts as those in the embodiment shown in FIGS.
このほか、複合容器１０Ａの構成および製造方法、ならびに複合プリフォーム７０の構成および製造方法については、図１乃至図１１に示す実施の形態と略同様であるので、詳細な説明を省略する。また、図１２、図１３および図１４（ａ）〜（ｆ）において、プラスチック製部材４０がプリフォーム１０ａに対して収縮する作用をもつもの（収縮チューブ）を用いても良い。
In addition, the configuration and manufacturing method of the
第２の実施の形態
次に、図面を参照して本発明の第２の実施の形態について説明する。図１５乃至図２４は本発明の第２の実施の形態を示す図である。図１５乃至図２４において、第１の実施の形態と同一部分には同一の符号を付して詳細な説明は省略する。
Second Embodiment Next, a second embodiment of the present invention will be described with reference to the drawings. 15 to 24 are views showing a second embodiment of the present invention. 15 to 24, the same parts as those of the first embodiment are denoted by the same reference numerals, and detailed description thereof is omitted.
まず、図１５および図１６により、本実施の形態によるブロー成形方法によって作製される複合容器の概要について説明する。 First, an outline of a composite container produced by the blow molding method according to the present embodiment will be described with reference to FIGS. 15 and 16.
図１５および図１６に示す複合容器１０Ａは、後述するように、ブロー成形金型５０を用いてプリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａを含む複合プリフォーム７０（図１７参照）に対して２軸延伸ブロー成形を施すことにより、複合プリフォーム７０のプリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａを一体として膨張させて得られたものである。
A
このような複合容器１０Ａは、内側に位置するプラスチック材料製の容器本体１０と、容器本体１０の外側に密着して設けられた内側ラベル部材６０と、内側ラベル部材６０の外側に密着して設けられたプラスチック製部材４０とを備えており、さらにプラスチック製部材４０には、ラベル４３が接着されている。
Such a
このうち容器本体１０は、口部１１と、口部１１下方に設けられた首部１３と、首部１３下方に設けられた肩部１２と、肩部１２下方に設けられた胴部２０と、胴部２０下方に設けられた底部３０とを備えている。
Among these, the
一方、内側ラベル部材６０は、容器本体１０の外面に薄く延ばされた状態で密着されており、容器本体１０に対して容易に移動または回転しないほどに密着されている。
On the other hand, the
また、プラスチック製部材４０は、容器本体１０の外面かつ内側ラベル部材６０の外面に薄く延ばされた状態で密着されており、容器本体１０に対して容易に移動または回転しないほどに密着されている。
The
プラスチック製部材４０は、その少なくとも一部が半透明または透明であることが考えられ、この場合、この半透明または透明な部分を介して、内側ラベル部材６０を外方から視認できる。なお、プラスチック製部材４０は、その全体が半透明または透明であっても良く、あるいは不透明な部分と半透明または透明な部分（例えば窓部）とを有していても良い。なお、本実施の形態ではプラスチック製部材４０の全体が透明である場合を例にとって説明する。
It is conceivable that at least a part of the
次に内側ラベル部材６０について説明する。内側ラベル部材６０（６０ａ）は後述するようにプリフォーム１０ａの外側を取り囲むように設けられ、このプリフォーム１０ａおよびプラスチック製部材４０ａと一体となって２軸延伸ブロー成形されることにより得られたものである。
Next, the
内側ラベル部材６０は容器本体１０の外面に接着されることなく取付けられており、容器本体１０に対して移動または回転しないほどに密着されている。この内側ラベル部材６０は、容器本体１０の外面において薄く引き延ばされて容器本体１０を覆っている。図１６に示すように、内側ラベル部材６０は、容器本体１０を取り囲むようにその周方向全域にわたって設けられており、略円形状の水平断面を有している。
The
この場合、内側ラベル部材６０は、容器本体１０のうち、口部１１および首部１３を除く、肩部１２、胴部２０および底部３０を覆うように設けられている。これにより、容器本体１０の肩部１２、胴部２０および底部３０に所望の文字、画像などを付与し、複合容器１０Ａに対して装飾性をもたせたり、情報を表示させたりすることができる。
In this case, the
なお、内側ラベル部材６０は、容器本体１０のうち口部１１以外の全域または一部領域に設けられていても良い。例えば、内側ラベル部材６０は、容器本体１０のうち、口部１１を除く、首部１３、肩部１２、胴部２０および底部３０の全体を覆うように設けられていても良い。さらに、内側ラベル部材６０は１つに限らず、複数設けても良い。なお、内側ラベル部材６０は、プラスチック製部材４０と同一の領域に設けられていても良く、プラスチック製部材４０よりも狭い領域に設けられていても良い。後者の場合、内側ラベル部材６０はプラスチック製部材４０によって完全に覆われることが好ましい。
The
また内側ラベル部材６０の厚みは、これに限定されるものではないが、容器本体１０に取り付けられた状態で例えば５μｍ〜５０μｍ程度とすることができる。
Further, the thickness of the
次に、プラスチック製部材４０について説明する。プラスチック製部材４０（４０ａ）は後述するように内側ラベル部材６０（６０ａ）の外側を取り囲むように設けられ、プリフォーム１０ａおよび内側ラベル部材６０ａと一体となって２軸延伸ブロー成形されることにより得られたものである。
Next, the
プラスチック製部材４０は内側ラベル部材６０の外面に接着されることなく取付けられており、容器本体１０に対して移動または回転しないほどに密着されている。このプラスチック製部材４０は、内側ラベル部材６０の外面において薄く引き延ばされて内側ラベル部材６０を覆っている。図１６に示すように、プラスチック製部材４０は、容器本体１０を取り囲むようにその周方向全域にわたって設けられており、略円形状の水平断面を有している。
The
このほか、容器本体１０、プラスチック製部材４０およびラベル４３の構成は、上述した第１の実施の形態の場合と略同様であるので、ここでは詳細な説明を省略する。
In addition, since the configurations of the
次に図１７により、本実施の形態による複合プリフォームの構成について説明する。 Next, the structure of the composite preform according to this embodiment will be described with reference to FIG.
図１７に示すように、複合プリフォーム７０は、プラスチック材料製のプリフォーム１０ａと、プリフォーム１０ａの外側に密着して設けられた有底円筒状の内側ラベル部材６０ａと、内側ラベル部材６０ａの外側に密着して設けられた有底円筒状のプラスチック製部材４０ａとを備えている。
As shown in FIG. 17, the
内側ラベル部材６０ａは、プリフォーム１０ａの外面に密着されており、プリフォーム１０ａに対して容易に移動または回転しない状態で密着されている。内側ラベル部材６０ａは、プリフォーム１０ａを取り囲むようにその周方向全域にわたって設けられており、略円形状の水平断面を有している。
The
内側ラベル部材６０ａには、予めデザインまたは印字が施されていても良い。例えば、図柄や商品名などのほか、内容液の名称、製造者、原材料名などの文字情報が記載されていても良い。例えば、プリフォーム１０ａのうち胴部２０ａの全部または一部に内側ラベル部材６０ａを設け、成形後に容器本体１０の胴部２０に画像や文字が表示されるようにしても良い。
The
このような内側ラベル部材６０ａとしては、ポリエステル系樹脂、ポリアミド系樹脂、ポリアラミド系樹脂、ポリプロピレン系樹脂、ポリカーボネート系樹脂、ポリアセタール系樹脂、フッ素系樹脂などのフィルムを用いることができる。内側ラベル部材６０ａは、プリフォーム１０ａ（容器本体１０）および／またはプラスチック製部材４０ａ（４０）と同一の材料からなっていても良く、異なる材料からなっていても良い。
As such an
また、内側ラベル部材６０ａとして、以下に説明する各種材料を用いることもできる。
Further, various materials described below can be used as the
例えば内側ラベル部材６０ａは、酸素バリア性または水蒸気バリア性などのガスバリア性を有する材料からなっていても良い。この場合、プリフォーム１０ａとして多層プリフォームやブレンド材料を含むプリフォームなどを用いることなく、複合容器１０Ａのガスバリア性を高め、酸素や水蒸気によって内容液が劣化することを防止することができる。このような材料としては、ＰＥ、ＰＰ、ＭＸＤ−６、ＥＶＯＨまたはこれらの材料に脂肪酸塩などの酸素吸収材を混ぜることも考えられる。
For example, the
また内側ラベル部材６０ａは、紫外線などの光線バリア性を有する材料からなっていても良い。この場合、プリフォーム１０ａとして多層プリフォームやブレンド材料を含むプリフォームなどを用いることなく、複合容器１０Ａの光線バリア性を高め、容器内への酸素の侵入を防ぎ、内容液が劣化することを防止し、また、容器内から外部への水蒸気の蒸散を防ぎ、内容量が減少することを防止することができる。このような材料としては、ブレンド材料、またはＰＥＴやＰＥ、ＰＰに遮光性樹脂を添加した材料が考えられる。
The
また内側ラベル部材６０ａは、プリフォーム１０ａ（容器本体１０）を構成するプラスチック材料よりも保温性または保冷性の高い材料（熱伝導性の低い材料）からなっていても良い。この場合、容器本体１０そのものの厚みを厚くすることなく、内容液の温度が複合容器１０Ａの表面まで伝達しにくくすることが可能となる。これにより、複合容器１０Ａの保温性または保冷性が高められる。このような材料としては、発泡化したポリウレタン、ポリスチレン、ＰＥ、ＰＰ、フェノール樹脂、ポリ塩化ビニル、ユリア樹脂、シリコーン、ポリイミド、メラミン樹脂などが考えられる。さらに中空粒子を含んでなることが好ましい。中空粒子の平均粒子径は、１〜２００μｍであることが好ましく、５〜８０μｍであることがより好ましい。また、中空粒子としては、樹脂などから構成される有機系中空粒子であってもよく、ガラスなどから構成される無機系中空粒子であってもよいが、分散性が優れるという理由から、有機系中空粒子が好ましい。有機系中空粒子を構成する樹脂としては、上記したものと同様のものを挙げることができる。また、上記市販される中空粒子を用いることもできる。中空粒子の含有量としては、内側ラベル部材６０ａに含有される樹脂１００質量部に対して、０．０１〜５０質量部であることが好ましく、１〜２０質量部であることがより好ましい。
Further, the
一方、プラスチック製部材４０ａは、内側ラベル部材６０ａの外面に接着されることなく取付けられており、プリフォーム１０ａに対して移動または回転しないほどに密着されている。プラスチック製部材４０ａは、プリフォーム１０ａを取り囲むようにその周方向全域にわたって設けられており、略円形状の水平断面を有している。
On the other hand, the
この場合、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、胴部２０ａのうち容器本体１０の首部１３に対応する部分１３ａを除く全域と、底部３０ａの全域とを覆うように設けられている。
In this case, the
なお、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、口部１１ａ以外の全域または一部領域に設けられていても良い。例えば、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、口部１１ａを除く、胴部２０ａおよび底部３０ａの全体を覆うように設けられていても良い。さらに、内側ラベル部材６０ａおよびプラスチック製部材４０ａはそれぞれ１つに限らず、複数設けても良い。例えば、２つの内側ラベル部材６０ａおよびプラスチック製部材４０ａを胴部２０ａの外側２箇所にそれぞれ設けても良い。
The
このようなプラスチック製部材４０ａとしては、プリフォーム１０ａに対して収縮する作用をもたないものであっても良く、収縮する作用をもつもの（収縮チューブ）であっても良い。
Such a
後者の場合、プラスチック製部材（収縮チューブ）４０ａとしては、プリフォーム１０ａに対して収縮する作用をもつものであれば良い。なお、プラスチック製部材４０ａは、外的な作用（例えば熱）が加えられた際、プリフォーム１０ａに対して収縮するもの（例えば熱収縮チューブ）が用いられることが好ましい。
In the latter case, any plastic member (shrinkable tube) 40a may be used as long as it has a function of shrinking the
このほか、プリフォーム１０ａおよびプラスチック製部材４０ａの構成は、上述した第１の実施の形態の場合と略同様であるので、ここでは詳細な説明を省略する。
In addition, since the configurations of the
次にプラスチック製部材４０ａおよび／または内側ラベル部材６０ａの形状について説明する。
Next, the shape of the
図１７および図１８（ａ）に示すように、プラスチック製部材４０ａ（内側ラベル部材６０ａ）は、全体として有底円筒形状からなり、円筒状の胴部４１（胴部６１）と、胴部４１（胴部６１）に連結された底部４２（底部６２）とを有していても良い。この場合、プラスチック製部材４０ａ（内側ラベル部材６０ａ）の底部４２（底部６２）がプリフォーム１０ａの底部３０ａを覆うので、複合容器１０Ａの胴部２０に加え、底部３０に対しても様々な機能や特性を付与することができる。
As shown in FIGS. 17 and 18A, the
また、図２３（後述）および図１８（ｂ）に示すように、プラスチック製部材４０ａ（内側ラベル部材６０ａ）は、全体として円管形状（無底円筒形状）からなり、円筒状の胴部４１（胴部６１）を有していても良い。この場合、プラスチック製部材４０ａ（内側ラベル部材６０ａ）としては、例えば押出チューブを用いることができる。
Further, as shown in FIGS. 23 (described later) and FIG. 18B, the
また、図１８（ｃ）および図１８（ｄ）に示すように、プラスチック製部材４０ａ（内側ラベル部材６０ａ）は、フィルムを筒状に形成してその端部を貼り合わせることにより作製されても良い。この場合、図１８（ｃ）に示すように、プラスチック製部材４０ａは、胴部４１（胴部６１）を有する管形状（無底円筒形状）に構成されていても良く、図１８（ｄ）に示すように、底部４２（底部６２）を貼り合わせることにより有底筒形状に構成されていても良い。
Further, as shown in FIGS. 18C and 18D, the
次に図１９（ａ）〜（ｆ）により、本実施の形態によるブロー成形方法（複合容器１０Ａの製造方法）について説明する。
Next, a blow molding method (a method for manufacturing the
まず、プラスチック材料製のプリフォーム１０ａを準備する（図１９（ａ）参照）。
First, a
次に、プリフォーム１０ａの外側に内側ラベル部材６０ａを設けるとともに、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設ける。これにより、プリフォーム１０ａと、プリフォーム１０ａの外側に密着された内側ラベル部材６０ａと、内側ラベル部材６０ａの外側に密着されたプラスチック製部材４０ａとを有する複合プリフォーム７０を作製する（図１９（ｂ）参照）。この場合、内側ラベル部材６０ａは、全体として有底円筒形状からなり、円筒状の胴部６１と、胴部６１に連結された底部６２とを有している。
Next, an
この際、プリフォーム１０ａの外径と同一またはわずかに小さい内径をもつ内側ラベル部材６０ａおよびプラスチック製部材４０ａを、それぞれプリフォーム１０ａに対して押し込むことにより、プリフォーム１０ａの外面に密着させても良い。あるいは、熱収縮性をもつ内側ラベル部材６０ａおよびプラスチック製部材４０ａをプリフォーム１０ａの外面に設け、この内側ラベル部材６０ａおよびプラスチック製部材４０ａを５０℃乃至１００℃に加熱することにより熱収縮させてプリフォーム１０ａの外面に密着させても良い。
At this time, even if the
また、予め内側ラベル部材６０ａの周囲にプラスチック製部材４０ａを設けておき、これら内側ラベル部材６０ａおよびプラスチック製部材４０ａを一体としてプリフォーム１０ａの外側に装着しても良い。あるいは、プリフォーム１０ａの外側に内側ラベル部材６０ａを設け、その後、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設けてもよい。
Alternatively, a
このように、予めプリフォーム１０ａおよび内側ラベル部材６０ａの外側にプラスチック製部材４０ａを密着させ、複合プリフォーム７０を作製しておくことにより、複合プリフォーム７０を作製する一連の工程（図１９（ａ）〜（ｂ））と、複合容器１０Ａをブロー成形により作製する一連の工程（図１９（ｄ）〜（ｆ））とを別々の場所（工場など）で実施することが可能になる。
In this way, a series of steps for producing the
次に、複合プリフォーム７０は、加熱装置５１によって加熱される（図１９（ｃ）参照）。
Next, the
続いて、加熱装置５１によって加熱された複合プリフォーム７０は、ブロー成形金型５０に送られる。複合容器１０Ａは、このブロー成形金型５０を用いて成形され、上述した第１の実施の形態の場合と略同様にして、容器本体１０と、容器本体１０の外面に設けられた内側ラベル部材６０と、内側ラベル部材６０の外側に設けられたプラスチック製部材４０とを備えた複合容器１０Ａが得られる（図１９（ｄ）〜（ｆ）参照）。
Subsequently, the
このほか、本実施の形態によるブロー成形方法（複合容器１０Ａの製造方法）は、上述した第１の実施の形態の場合と略同様であるので、ここでは詳細な説明を省略する。
In addition, the blow molding method (method for manufacturing the
ブロー成形方法の変形例
次に図２０（ａ）〜（ｆ）により、本実施の形態によるブロー成形方法（複合容器１０Ａの製造方法）の変形例について説明する。図２０（ａ）〜（ｆ）に示す変形例は、プラスチック製部材４０ａがプリフォーム１０ａに対して収縮する作用をもつもの（収縮チューブ）であり、他の構成は、図１９（ａ）〜（ｆ）に示す形態と略同一である。図２０（ａ）〜（ｆ）において、図１９（ａ）〜（ｆ）と同一部分には同一の符号を付して詳細な説明は省略する。
Modified Example of Blow Molding Method Next, a modified example of the blow molding method (manufacturing method of the
まず、プラスチック材料製のプリフォーム１０ａを準備する（図２０（ａ）参照）。
First, a
次に、プリフォーム１０ａの外側に内側ラベル部材６０ａを設けるとともに、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設ける（図２０（ｂ）参照）。内側ラベル部材６０ａおよびプラスチック製部材４０ａは、胴部２０ａのうち容器本体１０の首部１３に対応する部分を除く全域と、底部３０ａの全域とを覆うように装着される。このプラスチック製部材４０ａは、その少なくとも一部が半透明または透明になっていてもよい。
Next, an
この場合、予め内側ラベル部材６０ａの周囲にプラスチック製部材４０ａを設けておき、これら内側ラベル部材６０ａおよびプラスチック製部材４０ａを一体としてプリフォーム１０ａの外側に装着しても良い。あるいは、プリフォーム１０ａの外側に内側ラベル部材６０ａを設け、その後、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設けてもよい。
In this case, a
次に、プリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、加熱装置５１によって加熱される（図２０（ｃ）参照）。このとき、プリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、口部１１ａを下に向けた状態で回転しながら、加熱装置５１によって周方向に均などに加熱される。この加熱工程におけるプリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａの加熱温度は、例えば９０℃乃至１３０℃としても良い。
Next, the
このように、プラスチック製部材４０ａが加熱されることにより、プラスチック製部材４０ａが熱収縮し、プリフォーム１０ａの外側に密着する（図２０（ｃ）参照）。なお、プラスチック製部材４０ａ自体が収縮性を有する場合、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設けた時点（図２０（ｂ）参照）でプラスチック製部材４０ａが内側ラベル部材６０の外側に密着していても良い。
Thus, by heating the
続いて、加熱装置５１によって加熱されたプリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、ブロー成形金型５０に送られる（図２０（ｄ）参照）。
Subsequently, the
プリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、このブロー成形金型５０を用いて成形され、上述した図１９（ａ）〜（ｆ）の場合と略同様にして、容器本体１０と、容器本体１０の外面に設けられた内側ラベル部材６０と、内側ラベル部材６０の外側に設けられたプラスチック製部材４０とを備えた複合容器１０Ａが得られる（図２０（ｄ）〜（ｆ）参照）。
The
次に図２１（ａ）〜（ｇ）により、本実施の形態によるブロー成形方法（複合容器１０Ａの製造方法）の他の変形例について説明する。図２１（ａ）〜（ｇ）に示す変形例は、プラスチック製部材４０ａがプリフォーム１０ａに対して収縮する作用をもち（収縮チューブ）、プリフォーム１０ａおよびプラスチック製部材４０ａを２段階で加熱するものであり、他の構成は、図１９（ａ）〜（ｆ）に示す形態と略同一である。図２１（ａ）〜（ｇ）において、図１９（ａ）〜（ｆ）と同一部分には同一の符号を付して詳細な説明は省略する。
Next, with reference to FIGS. 21A to 21G, another modification of the blow molding method (a method for manufacturing the
まず、プラスチック材料製のプリフォーム１０ａを準備する（図２１（ａ）参照）。
First, a
次に、プリフォーム１０ａの外側に内側ラベル部材６０ａを設けるとともに、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設ける（図２１（ｂ）参照）。プラスチック製部材４０ａは、胴部２０ａのうち容器本体１０の首部１３に対応する部分を除く全域と、底部３０ａの全域とを覆うように装着される。このプラスチック製部材４０ａは、その少なくとも一部が半透明または透明になっていても良い。
Next, the
この場合、予め内側ラベル部材６０ａの周囲にプラスチック製部材４０ａを設けておき、これら内側ラベル部材６０ａおよびプラスチック製部材４０ａを一体としてプリフォーム１０ａの外側に装着しても良い。あるいは、プリフォーム１０ａの外側に内側ラベル部材６０ａを設け、その後、内側ラベル部材６０ａの外側にプラスチック製部材４０ａを設けてもよい。
In this case, a
次に、プリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａは、第１の加熱装置５５によって加熱される（図２１（ｃ）参照）。このとき、プリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａの加熱温度は、例えば５０℃乃至１００℃としても良い。
Next, the
プラスチック製部材４０ａが加熱されることにより、プラスチック製部材４０ａが熱収縮し、プリフォーム１０ａの外側に密着する。これにより、プリフォーム１０ａと、プリフォーム１０ａの外側に密着された内側ラベル部材６０ａと、内側ラベル部材６０ａの外側に密着されたプラスチック製部材４０ａとを有する複合プリフォーム７０が得られる（図２１（ｃ）参照）。
When the
このように、第１の加熱装置５５を用いて予めプリフォーム１０ａおよび内側ラベル部材６０ａの外側にプラスチック製部材４０ａを加熱密着させ、複合プリフォーム７０を作製しておくことにより、複合プリフォーム７０を作製する一連の工程（図２１（ａ）〜（ｃ））と、複合容器１０Ａをブロー成形により作製する一連の工程（図２１（ｄ）〜（ｇ））とを別々の場所（工場など）で実施することが可能になる。
In this way, the
次に、複合プリフォーム７０は、第２の加熱装置５１によって加熱される（図２１（ｄ）参照）。このとき、複合プリフォーム７０は、口部１１ａを下に向けた状態で回転しながら、第２の加熱装置５１によって周方向に均などに加熱される。この加熱工程におけるプリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａの加熱温度は、例えば９０℃乃至１３０℃としても良い。
Next, the
続いて、第２の加熱装置５１によって加熱された複合プリフォーム７０は、ブロー成形金型５０に送られる（図２１（ｅ）参照）。
Subsequently, the
複合プリフォーム７０は、このブロー成形金型５０を用いて成形され、上述した図１９（ａ）〜（ｆ）の場合と略同様にして、容器本体１０と、容器本体１０の外面に設けられた内側ラベル部材６０と、内側ラベル部材６０の外側に設けられたプラスチック製部材４０とを備えた複合容器１０Ａが得られる（図２１（ｅ）〜（ｇ）参照）。
The
以上説明したように、本実施の形態によれば、ブロー成形金型５０内で複合プリフォーム７０に対してブロー成形を施すことにより、複合プリフォーム７０のプリフォーム１０ａ、内側ラベル部材６０ａおよびプラスチック製部材４０ａを一体として膨張させ、容器本体１０と内側ラベル部材６０とプラスチック製部材４０とを備えた複合容器１０Ａを作製する。このためプリフォーム１０ａを用いて複合容器１０Ａを製造する段階で、予め複合容器１０Ａに内側ラベル部材６０を設けておくことができる。したがって、複合容器１０Ａに内容液を充填して密栓した後、ラベラーによってラベルを付与する工程を設ける必要がない。これにより、最終製品を製造するための製造コストを抑制することができる。
また、ラベラーの不具合などにより最終製品を製造する際に歩留まりが低下することを防止することができる。
As described above, according to the present embodiment, the
Further, it is possible to prevent the yield from being lowered when the final product is manufactured due to a labeler defect or the like.
また本実施の形態によれば、プリフォーム１０ａ（容器本体１０）とプラスチック製部材４０ａ（プラスチック製部材４０）とを別部材から構成することができる。したがって、プラスチック製部材４０の種類や形状を適宜選択することにより、複合容器１０Ａに様々な機能や特性を自在に付与することができる。
Moreover, according to this Embodiment, the
また、本実施の形態によれば、複合容器１０Ａを作製する際、一般的なブロー成形装置をそのまま用いることができるので、複合容器１０Ａを作製するための新たな成形設備を準備する必要が生じない。
Further, according to the present embodiment, when the
変形例
次に図２２、図２３および図２４（ａ）〜（ｆ）により本発明の変形例について説明する。
Modified Example Next, a modified example of the present invention will be described with reference to FIGS. 22, 23 and 24 (a) to (f).
図２２、図２３および図２４（ａ）〜（ｆ）に示す変形例は、内側ラベル部材６０ａおよびプラスチック製部材４０ａとして胴部と底部とを有するものではなく、円筒状の内側ラベル部材６０ａおよびプラスチック製部材４０ａを用いたものである。
The modified examples shown in FIGS. 22, 23, and 24 (a) to 24 (f) do not have the body portion and the bottom portion as the
図２２に示す複合容器１０Ａにおいて、内側ラベル部材６０およびプラスチック製部材４０は、容器本体１０の肩部１２から胴部２０の下方部分まで延びているが、底部３０まで達していない。また、図２３に示す複合プリフォーム７０において、内側ラベル部材６０ａおよびプラスチック製部材４０ａはプリフォーム１０ａの胴部２０ａのみを覆うように密着されており、より詳細には、胴部２０ａのうち容器本体１０の首部１３に対応する部分１３ａと胴部２０ａの下部に対応する部分とを除く領域を覆っている。
In the
図２２、図２３および図２４（ａ）〜（ｆ）において他の構成は、図１２乃至図１８に示す実施の形態と略同一である。図２２、図２３および図２４（ａ）〜（ｆ）に示す変形例において、図１５乃至図２１に示す実施の形態と同一部分には同一符号を付して詳細な説明は省略する。 Other configurations in FIGS. 22, 23 and 24A to 24F are substantially the same as those in the embodiment shown in FIGS. In the modification shown in FIGS. 22, 23 and 24A to 24F, the same parts as those in the embodiment shown in FIGS.
このほか、複合容器１０Ａの構成および製造方法、ならびに複合プリフォーム７０の構成および製造方法については、図１５乃至図２１に示す実施の形態と略同様であるので、詳細な説明を省略する。また、図２２、図２３および図２４（ａ）〜（ｆ）において、プラスチック製部材４０がプリフォーム１０ａに対して収縮する作用をもつもの（収縮チューブ）を用いても良い。
In addition, the configuration and manufacturing method of the
Claims (10)
プラスチック材料製の容器本体と、
前記容器本体の外面にプラスチック製部材と、を備え、
前記容器本体および前記プラスチック製部材は、ブロー成形により一体として膨張され、
前記プラスチック製部材に、ラベルが接着されており、
前記容器本体から、前記プラスチック製部材および前記ラベルを一体として分離回収することができ、
前記プラスチック製部材が、前記容器本体の胴部に対応する位置であって、ラベルが接着される位置に、複数の開口を有することを特徴とする複合容器。 In composite containers,
A container body made of plastic material;
A plastic member on the outer surface of the container body,
The container body and the plastic member are expanded integrally by blow molding,
A label is bonded to the plastic member,
From the container body, the plastic member and the label can be separated and recovered as a unit ,
The composite container , wherein the plastic member has a plurality of openings at positions corresponding to the body portion of the container main body and where the label is bonded .
プラスチック材料製のプリフォームを準備する工程と、
前記プリフォームの外側を取り囲むようにプラスチック製部材を設けることにより、前記プリフォームと、前記プリフォームの外側に密着された前記プラスチック製部材とを有する複合プリフォームを作製する工程と、
前記複合プリフォームを加熱するとともにブロー成形金型内に挿入する工程と、
前記ブロー成形金型内で前記複合プリフォームに対してブロー成形を施すことにより、前記複合プリフォームの前記プリフォームおよび前記プラスチック製部材を一体として膨張させることにより、前記プリフォームに対応する容器本体と、前記容器本体の外側に密着して設けられたプラスチック製部材とを作製する工程と、
前記複合容器の前記プラスチック製部材に、ラベルを接着する工程と、を備え、
前記プラスチック製部材および前記ラベルは一体として、前記容器本体から分離回収することができ、
前記プラスチック製部材が、前記容器本体の胴部に対応する位置であって、ラベルが接着される位置に、複数の開口を有することを特徴とする複合容器の製造方法。 In a method for manufacturing a composite container comprising a container body and a plastic member ,
Preparing a preform made of plastic material;
Providing a plastic member so as to surround the outside of the preform to produce a composite preform having the preform and the plastic member in close contact with the outside of the preform;
Heating the composite preform and inserting it into a blow mold; and
By subjecting the composite preform to blow molding in the blow molding die, the preform of the composite preform and the plastic member are inflated as one body, and thereby a container body corresponding to the preform And producing a plastic member provided in close contact with the outside of the container body;
Adhering a label to the plastic member of the composite container,
The plastic member and the label can be separated and recovered from the container body as a unit,
The method of manufacturing a composite container, wherein the plastic member has a plurality of openings at positions corresponding to the body portion of the container main body and where the label is bonded .
前記プラスチック製部材は、前記内側ラベル部材の外側に設けられることを特徴とする請求項５〜８のいずれか一項に記載の複合容器の製造方法。 A step of providing an inner label member so as to surround the outside of the preform;
The said plastic member is provided in the outer side of the said inner side label member, The manufacturing method of the composite container as described in any one of Claims 5-8 characterized by the above-mentioned.