JP6086159B2 - 尿素scr筐体用フェライト系ステンレス鋼板 - Google Patents
尿素scr筐体用フェライト系ステンレス鋼板 Download PDFInfo
- Publication number
- JP6086159B2 JP6086159B2 JP2015546352A JP2015546352A JP6086159B2 JP 6086159 B2 JP6086159 B2 JP 6086159B2 JP 2015546352 A JP2015546352 A JP 2015546352A JP 2015546352 A JP2015546352 A JP 2015546352A JP 6086159 B2 JP6086159 B2 JP 6086159B2
- Authority
- JP
- Japan
- Prior art keywords
- less
- content
- urea scr
- steel sheet
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]質量%で、C:0.020%以下、Si:0.01〜0.50%、Mn:0.01〜0.50%、P:0.040%以下、S:0.010%以下、Al:0.01〜0.20%、Cr:20.5〜24.0%、Cu:0.40〜0.80%、Ni:0.05〜0.6%、N:0.020%以下、を含有し、Ti:0.01〜0.40%、Nb:0.01〜0.55%から選ばれる1種または2種をさらに含有し、残部Fe及びその他不可避的不純物からなり、Ti+Nb×48/93≧8×(C+N) ・・・(1)
(式(1)中のTi、Nb、CおよびNは、各元素の含有量(質量%)を示す。)
を満たす尿素SCR筐体用フェライト系ステンレス鋼板。
[2]さらに、質量%で、Mo:0.01〜0.25%を含有する前記[1]に記載の尿素SCR筐体用フェライト系ステンレス鋼板。
[3]さらに、質量%で、V:0.01〜0.20%、Zr:0.01〜0.20%、Ca:0.0002〜0.0020%の1種または2種以上を含有する前記[1]または[2]に記載の尿素SCR筐体用フェライト系ステンレス鋼板。
Cは、鋼板の加工性および靱性を低下させる元素であり、C含有量が0.020%を超えると、その悪影響が顕著となるので、C含有量は0.020%以下に限定する。特に、加工性および靱性の観点から、C含有量は0.017%以下とすることが好ましい。また、C含有量は0.012%以下とすることがより好ましい。
Siは、脱酸剤として必要な元素である。その効果は、Siを0.01%以上含有させることで得られる。しかし、冷延板焼鈍時に酸化して表面にSiO2皮膜を形成し、酸洗性を低下させることから、Si含有量は0.50%を上限とする。酸洗性の観点からは、Si含有量は0.20%以下とすることが好ましい。
Mnは、脱酸剤として必要な元素である。その効果は、Mnを0.01%以上含有させることで得られる。しかし、過剰に添加すると鋼板の加工性を低下させることから、Mn含有量は0.50%以下に限定する。鋼板の加工性の観点からは、Mn含有量は0.30%以下とすることが好ましく、また、0.20%以下とすることがより好ましい。
Pは、鋼板の加工性および靭性を低下させる元素であり、出来る限り低い方が好ましく、P含有量は0.040%以下とする。より好ましくは、P含有量は0.030%以下である。
Sは、靭性を低下させる元素であり、出来る限り低い方が好ましく、S含有量は0.010%以下とする。靭性の観点からは、S含有量を0.006%以下にすることが好ましい。
Alは脱酸剤として有効な元素である。その効果はAlを0.01%以上含有させることで得られる。しかし、Alを過剰に含有すると、Al2O3介在物の過度の生成によりヘゲ疵等が発生し表面品質が低下するため、Al含有量は0.20%以下に限定する。表面品質の観点からは、Al含有量は0.05%以下とすることが好ましい。
Crは、ステンレス鋼板の表面に生成する不動態皮膜を強化させて腐食の発生を抑制し、本発明の特徴である尿素SCR環境下でのアンモニウムカーバメイトに対する耐食性の向上に有効な元素成分である。十分な耐食性を得るためには、20.5%以上のCr含有量が必要であり、Cr含有量は20.5%を下限とする。さらに好ましくは、Cr含有量は21.0%以上である。一方、Crは、鋼板の靱性を低下させ、特に24.0%を超えてCrを含有すると靱性の低下が著しくなるため、Cr含有量は24.0%以下に限定する。靱性の観点から、Cr含有量は22.0%以下とすることが好ましい。
Cuは、腐食により孔食が発生した場合に孔食の拡大(腐食の進行)を抑制する作用があり、尿素SCR環境下でのアンモニウムカーバメイトに対する耐食性向上に特に有効な元素成分である。その効果は、Cuを0.40%以上含有させることで得られる。一方、Cuを0.80%を超えて含有すると靱性を低下させるため、Cuは0.80%以下含有させる。靭性の観点からは、Cuは0.60%以下含有させることが好ましい。
Niは、耐食性および靭性を向上させる効果を持ち、その効果は、Niを0.05%以上含有させることで得られる。しかし、原料コストが高いため、Ni含有量は0.6%以下とする。
Nは、Cと同様に加工性および靱性を低下させる元素であり、N含有量が0.020%を超えるとその悪影響が顕著となるので、0.020%以下に限定する。特に、加工性および靱性の観点から、N含有量は0.015%以下とすることが好ましく、0.012%以下とすることがより好ましい。
TiおよびNbは炭窒化物を形成し、Crが炭素および窒素と結びついて耐食性を低下させる鋭敏化現象を抑制する。その効果は、Ti含有量あるいはNb含有量を0.01%以上とし、
Ti+Nb×48/93≧8×(C+N) ・・・(1)
を満たすようにすることで得られる(式(1)中のTi、Nb、CおよびNは、各元素の含有量(質量%)を示す。)。また、鋭敏化抑制の観点からは、(1)式を満たすとともに、Ti含有量を0.20%以上とするか、Nb含有量を0.30%以上とすることが好ましい。しかし、Ti、Nbを過度に含有しても、鋭敏化抑制効果が飽和するだけでなく、靭性の低下を招くため、Ti含有量は0.40%以下、Nb含有量は0.55%以下とする。靭性の観点からはTi含有量は0.35%以下、Nb含有量は0.45%以下とすることが好ましい。
Moは耐食性の向上に有効な元素であり、その効果は、Moの0.01%以上の含有で得られる。しかし、0.25%を超えてMoを含有させると靱性を低下させることがあるため、Moを含有させる場合には、Mo含有量は0.01〜0.25%とする。
Vは含有させることにより加工性を高くする元素である。その効果は、Vを0.01%以上含有させることで得られる。しかし、0.20%を超えてVを含有させると表面欠陥が発生し、表面性状を低下させる場合があるので、Vを含有させる場合には、V含有量は0.01〜0.20%とする。
Zrは含有させることにより加工性を高くする元素である。その効果は、Zrを0.01%以上含有させることで得られる。しかし、0.20%を超えてZrを含有させると表面欠陥が発生し、表面性状を低下させる場合があるので、Zrを含有させる場合は、Zr含有量は0.01〜0.20%とする。
Caは、脱酸効果があり、必要に応じて含有させる。その効果を得るためには、Ca含有量は、0.0002%以上とし、好ましくは0.0005%以上とする。しかしながら、0.0020%を超えてCaを含有しても脱酸効果が飽和するばかりでなく、Caが介在物となり、ヘゲ疵を発生させ表面性状を低下させる場合があるため、Caを含有する場合は、Ca含有量は、0.0020%以下とする。
本発明の尿素SCR筐体用フェライト系ステンレス鋼板を製造する方法は、溶鋼の段階で上述のように溶鋼の組成を成分調整する以外は、特に限定されず、フェライト系ステンレス鋼板の製造に一般的に採用されている方法を適用することができる。
Z 0573(ステンレス鋼の65%硝酸腐食試験方法)に準拠した試験を行い、48時間の腐食速度(g/m2/h)を求めた。腐食速度が0.35g/m2/h以下のものを合格と判定した。結果を表1に示す。
Claims (3)
- 質量%で、
C:0.020%以下、
Si:0.01〜0.50%、
Mn:0.01〜0.50%、
P:0.040%以下、
S:0.010%以下、
Al:0.01〜0.20%、
Cr:20.5〜24.0%、
Cu:0.40〜0.80%、
Ni:0.05〜0.6%、
N:0.020%以下、
を含有し、
Ti:0.01〜0.40%、Nb:0.01〜0.55%から選ばれる1種または2種をさらに含有し、
残部Fe及びその他不可避的不純物からなり、
Ti+Nb×48/93≧8×(C+N) ・・・(1)
(式(1)中のTi、Nb、CおよびNは、各元素の含有量(質量%)を示す。)
を満たす尿素SCR筐体用フェライト系ステンレス鋼板。 - さらに、質量%で、Mo:0.01〜0.25%を含有する請求項1に記載の尿素SCR筐体用フェライト系ステンレス鋼板。
- さらに、質量%で、
V:0.01〜0.20%、
Zr:0.01〜0.20%、
Ca:0.0002〜0.0020%の1種または2種以上を含有する請求項1または2に記載の尿素SCR筐体用フェライト系ステンレス鋼板。