JP4953277B2 - 難燃性樹脂組成物 - Google Patents
難燃性樹脂組成物 Download PDFInfo
- Publication number
- JP4953277B2 JP4953277B2 JP2006053405A JP2006053405A JP4953277B2 JP 4953277 B2 JP4953277 B2 JP 4953277B2 JP 2006053405 A JP2006053405 A JP 2006053405A JP 2006053405 A JP2006053405 A JP 2006053405A JP 4953277 B2 JP4953277 B2 JP 4953277B2
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- flame retardant
- resin composition
- wax
- retardant resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、エチレン系樹脂の好ましい物性を維持しながら難燃性を改善した難燃性エチレン系樹脂組成物を提供するものである。
本発明はさらに、エチレン系樹脂に難燃性を維持しながら、機械物性および流動性加工性を向上させた難燃性エチレン系樹脂組成物を提供するものである。
本発明によって提供されるエチレン系樹脂組成物は、難燃性を保持しながら、機械物性および流動性加工性が改善された難燃性樹脂組成物である。
本発明によって、エチレン系樹脂の本来的特長である好ましい物性を維持しながら、難燃性、機械物性および加工性を付与して、電線被覆や建材などの難燃性が求められる用途に好適に使用できる難燃性樹脂組成物が提供される。
本発明で使用されるエチレン系樹脂(A)としては、エチレンの単独重合体、エチレンと他のα−オレフィンとの共重合体、エチレンと極性モノマーの共重合体、またはこれらの混合物を挙げることができる。
上記α−オレフィンとしては、炭素数3以上、好ましくは3〜20、より好ましくは3〜8のα−オレフィンが好ましく、具体的にはプロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテン、1−オクテンなどを挙げることができる。
不飽和エステルの好ましい具体例としては、酢酸ビニル、プロピオン酸ビニルなどのビニルエステル、アクリル酸メチル、アクリル酸エチル、アクリル酸イソブチル、アクリル酸n−ブチル、メタクリル酸メチル、メタクリル酸グリシジル、マレイン酸ジメチルなどの不飽和カルボン酸エステルなどを挙げることができる。
不飽和カルボン酸の塩の好ましい例としては、前記不飽和カルボン酸のNa、Li、K、Zn、Mg、Caなどの塩を挙げることができる。
オレフィン系ワックス としては、高分子量ポリオレフィンの熱分解によって得られるワックス、オレフィンの単独重合または他のオレフィンとの共重合によって得られるワックスなどがあり、適宜選択して使用することができるが、相溶性の点から本発明の目的にはエチレン系ワックスが好ましい。
本発明で使用される無機難燃剤としては、水酸化アルミニウム、水酸化マグネシウム、ハイドロタルサイト、塩基性炭酸マグネシウム、炭酸カルシウム、シリカ、タルク、クレイ、ゼオライトなどを例示することができる。中でも水酸化アルミニウム、水酸化マグネシウム、ハイドロタルサイトのような金属水和物が好ましい。
実施例及び比較例において使用した原料は、以下のとおりである。
(2)オレフィン系ワックス1(WAX−1)
粘度平均分子量:4000、密度:980kg/m3、融点:128℃
(三井化学社製 商品名エクセレックス HW40800)
(3)オレフィン系ワックス2(WAX−2)
粘度平均分子量:4100、密度:942kg/m3、融点:113℃
(三井化学社製 商品名エクセレックス HW41420P)
(4)オレフィン系ワックス3(WAX−3)
粘度平均分子量:4600、密度:902kg/m3、融点:90℃
(三井化学社製 商品名エクセレックス HW48070B)
(5)オレフィン系ワックス4(WAX−4)
粘度平均分子量:2600、密度:947kg/m3、融点:85℃、酸価19
(三井化学社製 商品名エクセレックス HW26502PE)
(6)難燃剤:商品名 キスマ5A(協和化学工業社製 水酸化マグネシウム)
(7)酸化防止剤:イルガノックス1010(チバスペシャルティケミカルズ社製)
(i)ストランド外観
JIS K 7210に従い、190℃、10kg荷重でストランドを押出し、その表面状態を観察して、下記の判定基準で評価を行った。
○:肌荒れは認められなかった。
△:若干の肌荒れが認められた。
×:肌荒れが著しかった。
JIS K6760法に従い測定した(ただし、試験片は、JIS K6301の3号ダンベル、試料厚1mmを用い、引張速度200mm/minで測定した)。
UL94耐炎性試験:3.0mm厚みのプレスシートにつき、UL94燃焼試験機(スガ試験機社製)を用いて、UL94垂直テストによる難燃性評価を行った。
o−ジクロルベンゼンを溶媒とし、クロス分別クロマトグラフを用いて測定した。
(v)密度(単位:kg/m3)
JIS K7112−1999法を用いて測定した。
(vi)融点(単位:℃)
示差走査熱量計(DSC)による融点を用いて測定した。
試料の調製
150℃に設定した6インチロールを用いて、EVA100重量部と、WAX−1 2重量部、難燃剤150重量部に、酸化防止剤0.2重量部とを、予めメルトブレンドした。さらに160℃に設定した加圧ニーダーを用いて20分間溶融混練した。
次に、得られたコンパウンドを、熱板160℃に設定したプレス成形機を用いて圧力100kg/cm2(ゲージ圧)の条件で10分間プレス成形し、所定のプレスシートを作製した。
評価
得られたプレスシートについて、前期方法にしたがって各物性を測定した。測定の結果を評に示した。
実施例1において、オレフィン系ワックスの使用を省略するほかは、同様にして試料を作成し、得られたプレスシートの評価を行った。結果を表1に示した。
本発明によって提供されるエチレン系樹脂組成物は、難燃性を保持しながら、機械物性および流動性加工性が改善された難燃性樹脂組成物である。
本発明により、本来的特徴である好ましい物性を維持しながら、難燃性、機械物性および加工性が付与された組成物であって、良好な難燃性とともに、すぐれた機械物性、流動性を示すので、電線や通信線の被覆材、建材その他の難燃性が求められる用途に好適な難燃性樹脂組成物が提供される。
Claims (6)
- 酢酸ビニル含量が33〜47重量%、メルトフローレイト(JIS K 7210−1999、190℃、2,160g荷重)が0.01〜0.15g/10分であるエチレン・酢酸ビニル共重合体100重量部に対して、メタロセン系触媒によって製造された粘度平均分子量が8,000以下で、密度が880〜980kg/m3で、融点が60〜160℃であるエチレン系ワックス0.01〜10重量部、および無機難燃剤50〜300重量部、さらに必要に応じて酸化防止剤、耐光安定剤、紫外線吸収剤、顔料、カーボンブラックから選ばれる添加剤からなり、該エチレン・酢酸ビニル共重合体、エチレン系ワックス、無機難燃剤及び添加剤とをエチレン・酢酸ビニル共重合体の融点以上の温度で混練して得られる、難燃性樹脂組成物。
- 前記エチレン系ワックスの粘度平均分子量が8,000以下で、密度が880〜980kg/m3で、融点が60〜130℃であることを特徴とする請求項1に記載の難燃性樹脂組成物。
- 前記無機難燃剤が、金属水和物であることを特徴とする請求項1または2に記載の難燃性樹脂組成物。
- 前記金属水和物が、水酸化アルミニウム、水酸化マグネシウムおよびハイドロタルサイトから選ばれた少なくとも1種であることを特徴とする請求項3に記載の難燃性樹脂組成物。
- 前記エチレン系ワックスが、変性されたワックスであることを特徴とする請求項1〜4のいずれか1項に記載の難燃性樹脂組成物。
- UL94耐炎試験に従って厚さ3mmの試験片で測定した難燃性が、V−0である請求項1〜5のいずれか1項に記載の難燃性樹脂組成物。