JP4773887B2 - 防刃衣料用布帛 - Google Patents
防刃衣料用布帛 Download PDFInfo
- Publication number
- JP4773887B2 JP4773887B2 JP2006153482A JP2006153482A JP4773887B2 JP 4773887 B2 JP4773887 B2 JP 4773887B2 JP 2006153482 A JP2006153482 A JP 2006153482A JP 2006153482 A JP2006153482 A JP 2006153482A JP 4773887 B2 JP4773887 B2 JP 4773887B2
- Authority
- JP
- Japan
- Prior art keywords
- blade
- aromatic polyamide
- wholly aromatic
- boehmite alumina
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(1)ベーマイトアルミナを含む全芳香族ポリアミド系フィラメントから構成されることを特徴とする防刃衣料用布帛。
(2)全芳香族ポリアミド系フィラメントにおけるベーマイトアルミナの含有率が、該全芳香族ポリアミド系フィラメントの重量を基準にして1〜10重量%(好ましくは1〜8重量%)であることを特徴とする上記(1)記載の防刃衣料用布帛。
(3)全芳香族ポリアミド系フィラメント中のベーマイトアルミナのアスペクト比が、3〜100(好ましくは3〜50)であることを特徴とする上記(1)〜(2)のいずれかに記載の防刃衣料用布帛。
(4)全芳香族ポリアミドフィラメントが、パラ型全芳香族ポリアミド系フィラメントであることを特徴とする上記(1)〜(3)のいずれかに記載の防刃衣料用布帛。
(5)ベーマイトアルミナの全芳香族ポリアミド系フィラメントの繊維軸に対する配向角度の平均が、20°以下(好ましくは0°〜10°)であり、かつ標準偏差が10°以下(好ましくは0°〜10°)であることを特徴とする上記(1)〜(4)のいずれかに記載請求項1記載の防刃衣料用布帛。
[ここで、配向角度とは、ベーマイトアルミナを含有する芳香族ポリアミド繊維の繊維軸に平行な方向の断面を透過電子顕微鏡(以下、TEMと略記)により倍率70000倍にて観察した際の、ベーマイトアルミナの繊維軸に対する傾きの角度のことである。このときの観察条件は、無作為に選んだ任意の箇所2μm×2μmで200サンプルについて測定し、それらの平均値をもって配向角度とする。]
(6)下記式で表される布帛のカバーファクター(CF)が、2500〜3500(好ましくは2800〜3200)であることを特徴とする上記(1)〜(5)のいずれかに記載の防刃衣料用布帛。
(A)全芳香族ポリアミドの溶液にベーマイトアルミナを加える方法、
(B)全芳香族ポリアミドの溶液とベーマイトアルミナの溶液とを混合する方法、
(C)ベーマイトアルミナの溶液に全芳香族ポリアミドを添加し溶解する方法、
(D)全芳香族ポリアミドの重合時にベーマイトアルミナを添加する方法、
などが挙げられる。
ベーマイトアルミナを含有する全芳香族ポリアミド系フィラメントの繊維軸に平行な方向の断面をTEMにて倍率は70000倍で観察し、無作為に選んだ箇所2μm×2μmで200サンプル測定した繊維軸に対するベーマイトアルミナの傾きの角度の平均値を配向角度とする。
十分な量の粘土層(縦×横×高さ=20×20×10cm)、上面が平坦な工作用油粘土)の上面に、複数層積層した布帛サンプルを置く。一方、引張圧縮試験機(株式会社インテスコ製、タイプ2005)のロードセルの下部にアイスピックを下向きに固定する。アイスピックの先端が布帛サンプルの上部約5mmとなるようにクロスヘッドの高さを調整し、次いで、2mm/分のクロスヘッド速度で圧縮を開始する。防刃性能は、アイスピックがサンプルを全層貫通した時、すなわち、アイスピックの先端がサンプルの最後層布帛を貫通した時の応力で表示した。したがって、この値が大きいほど防刃性能が良好であることを示す。
(全芳香族ポリアミド系フィラメントの製造)
全芳香族ポリアミド系フィラメントに添加するベーマイトアルミナとして、巴工業(株)製の短径15nm、アスペクト比11のものを使用した。このベーマイトアルミナの分散は、浅田鉄工株式会社製ビーズミル(Nano Grain Mill)を用いて行い、N−メチル−2−ピロリドン(以下、NMPと略す)中にベーマイトアルミナ含量が6重量%となるように、NMP分散体を調製した。この時、メディアとして、0.3mmのジルコニアビーズを使用した。
このパラ型全芳香族ポリアミド系フィラメントを用い、経・緯の織密度を45本/inchとして、目付け288g/m2の平織物を作成した。この織物を、10枚重ね、防刃試験を行なった。その結果、防刃性能は50.2kgであった。これらの結果を表1の実施例1欄に示す。
添加するベーマイトアルミナの含有量が全芳香族ポリアミドフィラメントの全重量を基準として3重量%又は7重量%となる割合で添加する以外は実施例1と同様にして、ベーマイトアルミナ添加原糸を製造し、その織物の防刃性能評価を実施した。また、得られたパラ型芳香族ポリアミド繊維中ベーマイトアルミナの配向角度の平均は、それぞれ11°及び14°であり、配向角度の標準偏差は、それぞれ3.2°及び3.8°であった。両者の結果を表1の実施例2、実施例3の欄に示す。
アスペクト比が11のベーマイトアルミナを使用するかわりに、アスペクト比が6のベーマイトアルミナを使用する以外は、実施例1と同様にしてベーマイトアルミナを含む芳香族ポリアミドフィラメントを製造し、その織物の防刃性能評価を実施した。また、得られたパラ型芳香族ポリアミド繊維中ベーマイトアルミナの配向角度の平均は14°であり、配向角度の標準偏差は7.6°であった。その結果を表1の実施例4欄に示す。
比較例として、ベーマイトアルミナを添加しないこと以外は、実施例1と同様にして原糸を作成し、その織物の防刃性能評価を実施した。その結果を表1の比較例1欄に示す。
Claims (6)
- ベーマイトアルミナを含む全芳香族ポリアミド系フィラメントから構成されていることを特徴とする防刃衣料用布帛。
- 全芳香族ポリアミド系フィラメントにおけるベーマイトアルミナの含有率が該全芳香族ポリアミド系フィラメントの重量を基準にして1〜10重量%であることを特徴とする請求項1記載の防刃衣料用布帛。
- 全芳香族ポリアミド系フィラメント中のベーマイトアルミナのアスペクト比が3〜100であることを特徴とする請求項1又は請求項に記載の防刃衣料用布帛。
- 全芳香族ポリアミドフィラメントがパラ型全芳香族ポリアミド系フィラメントであることを特徴とする請求項1〜請求項3のいずれかに記載の防刃衣料用布帛。
- ベーマイトアルミナの全芳香族ポリアミド系フィラメントの繊維軸に対する配向角度の平均が20°以下であり、かつ配向角度の標準偏差が10°以下であることを特徴とする請求項1〜請求項4のいずれかに記載の防刃衣料用布帛。