JP4766947B2 - 粘着シート - Google Patents
粘着シート Download PDFInfo
- Publication number
- JP4766947B2 JP4766947B2 JP2005227875A JP2005227875A JP4766947B2 JP 4766947 B2 JP4766947 B2 JP 4766947B2 JP 2005227875 A JP2005227875 A JP 2005227875A JP 2005227875 A JP2005227875 A JP 2005227875A JP 4766947 B2 JP4766947 B2 JP 4766947B2
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- film
- adhesive sheet
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、前記相溶可能成分は、カルボン酸エステルであることができる。
本発明においては、ポリオール成分として、ポリオキシアルキレン骨格を有するポリエーテルポリオールに、他のポリオール、例えば、ポリオキシテトラメチレングリコール、あるいはブタンジオール、ヘプタンジオール、ヘキサンジオール、シクロヘキサンジメタノール等のポリオールを一部混合して使用することができる。
以下に、バルク重合について具体的に説明する。反応容器にポリオールを投入し、温度が50〜80℃になるように調整し攪拌しつつ、ポリイソシアネートを添加してウレタン化を起こさせる。さらに鎖延長剤を添加して反応させた後、反応生成物をトレーに移動して、100〜150℃で4時間以上保持し、反応を完結させることによって、塊状のポリエーテルポリウレタンを得ることができる。
粘着シートを皮膚へ貼付する際に、皮膚の貼着部位を粘着シートの上から視覚的に確認することができるように、担持フィルム及びエラストマーフィルムは透明または半透明であることが好ましい。また、担持フィルムは、エラストマーフィルムに高い弾性率を付与することができるものであることが好ましく、例えば、常温常湿における引張り試験による50%伸張時のモジュラスが、2N/mm2以上、200N/mm2以下であることが好ましく、8N/mm2以上、50N/mm2以下であることがさらに好ましい。
なお、本発明において「フィルム」という場合には、シートを含み、「シート」という場合には、フィルムを含む概念とする。
ポリエーテルポリウレタン(大日精化工業(株)製、商品名レザミンP−210)を2軸スクリュー型の混練機で加熱溶融させた後、Tダイ式の押出し機を用いて厚みが30μmになるように押出し、ポリウレタンフィルムを形成した。
担持フィルムとして、ポリプロピレン、ポリエチレン及びエチレン−酢酸ビニル共重合体を主成分として含有する樹脂からなるフィルム(厚み40μm)に、形成されたポリウレタンフィルムを重ね、ゴムロールを用いて密着させて、ポリウレタンフィルムと担持フィルムとの積層体(支持体)を作製した。得られた積層体について、後述する評価試験に基づき、粘着剤層形成前の剥離強度(T形剥離)を測定したところ、0.22N/40mmであった。
実施例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの間の接着力を剥離強度(T形剥離)が0.42N/40mmとなるように変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの間の接着力を剥離強度(T形剥離)が0.14N/40mmとなるように変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの間の接着力(T形剥離)を剥離強度が0.17N/40mmとなるように変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの間の接着力を剥離強度(T形剥離)が0.22N/40mmとなるように変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの間の接着力を剥離強度(T形剥離)が0.29N/40mmとなるように変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの間の接着力を剥離強度(T形剥離)が0.35N/40mmとなるように変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを、エチレン−酢酸ビニル共重合体成分を除いたフィルム(40μm厚)に変更した以外は実施例1と同様にして、粘着シートを作製した。ただし、ポリウレタンフィルムと担持フィルムとの間の接着強度(T形剥離)は、粘着剤層形成前の剥離強度が0.20N/40mmであった。
比較例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの接着力を、粘着剤層形成前の剥離強度(T形剥離)が0.22N/40mmとなるように変更した以外は比較例1と同様にして、粘着シートを作製した。
比較例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの接着力を、粘着剤層形成前の剥離強度(T形剥離)が0.29N/40mmとなるように変更した以外は比較例1と同様にして、粘着シートを作製した。
比較例1において、担持フィルムのポリウレタンフィルムとの積層面へのコロナ放電処理の強度を変更すると共に、ポリウレタンフィルムの製膜時の湿度を調整することにより、ポリウレタンフィルムと担持フィルムとの接着力を、粘着剤層形成前の剥離強度(T形剥離)が0.15N/40mmとなるように変更した以外は比較例1と同様にして、粘着シートを作製した。
実施例1〜7、比較例1〜4で得られた粘着シートについて、下記に示す評価試験を行った。その結果を表1に示す。
粘着剤層を形成する前の積層体において、ポリウレタンフィルムと担持フィルムとの間の剥離力を日本工業規格JIS K6854−3(1999)に準じて測定した。すなわち、積層体を40mm×100mmの大きさに切断し、積層体のポリウレタンフィルムと担持フィルムとの端部をつかみ、常温常湿条件下で引張試験機を用いて剥離速度が300mm/minでT型剥離を行い、そのときの剥離力を測定した。
粘着剤層形成後の剥離シート付き粘着シートにおいて、ポリウレタンフィルムと担持フィルムとの間の剥離力を日本工業規格JIS K6854−1(1999)に準じて測定した。すなわち、製造後60℃で24時間保存した後の剥離シート付き粘着シートを20mm×100mmの大きさに切断し、剥離シートを剥がして粘着剤層面を表面が平滑なアルミニウム板の表面に貼付し固定した。次いで、固定した粘着シートにおける担持フィルムの端をつかみ、常温常湿条件下で引張試験機を用い、剥離速度が300mm/minでポリウレタンフィルムと剥離した担持フィルムとの角度が90度となるように90度剥離を行い、そのときの剥離力を測定した。
粘着シートについて製造加工性の評価を行った。すなわち、剥離シートの剥離処理面に実施例1と同様にして粘着剤層を形成し、この粘着剤層を、得られた積層体のポリウレタンフィルム面に重ね、ゴムロールを用いて粘着シートを形成した。このとき、ポリウレタンフィルム面から担持フィルムが浮き上がっているか否か目視観察した。ポリウレタンフィルム面から担持フィルムの浮き上がりが全く認められなかったものを記号「〇」、担持フィルムの浮き上がりが少しでも認められたものを記号「×」で示した。
粘着シートの使用時における剥離操作性の評価を行った。すなわち、剥離シート付き粘着シートを50mm×50mmの大きさに切断し、剥離シートを除去してから前腕内側に貼付した。次いで、貼付後すぐに担持フィルムを剥がした。担持フィルムの剥離のし易さを下記基準に基づき評価を行った。すなわち、担持フィルムが容易に剥離できたものを記号「〇」、担持フィルムが剥離できたものを記号「△」、ポリウレタンフィルムと密着していて剥離し難かったものを記号「×」で示した。
一方、比較例1〜3の粘着シートは、剥離操作性に劣ったものであることが分かった。なお、比較例4の粘着シートは、粘着剤層形成前と形成後で剥離力の変動が大きく、実用的には、操作性不良を生じる可能性を有するものである。
Claims (5)
- 担持フィルムの一方の面にポリウレタンフィルムを有し、該ポリウレタンフィルムの上に粘着剤層が設けられた粘着シートであって、該担持フィルムが、ポリプロピレン、ポリエチレン及びエチレン−酢酸ビニル共重合体を主成分として含有する樹脂からなることを特徴とする粘着シート。
- 前記粘着剤層が、アクリル系重合体を主成分とし、かつ、該アクリル系重合体に対して相溶可能であり、常温で液状もしくはペースト状である相溶可能成分を含有する組成物から形成されていることを特徴とする請求項1記載の粘着シート。
- 前記相溶可能成分が、カルボン酸エステルであることを特徴とする請求項1又は2記載の粘着シート。
- 前記ポリウレタンフィルムを形成する材料が、ポリエステルポリウレタン及び/又はポリエーテルポリウレタンであることを特徴とする請求項1から3のいずれか1項記載の粘着シート。
- 前記担持フィルムを形成する樹脂が、エチレン−酢酸ビニルを0.1質量%以上、1.0質量%以下含有することを特徴とする請求項1から4のいずれか1項に記載の粘着シート。