JP4212988B2 - 粘着シート及び粘着シートの製造方法 - Google Patents
粘着シート及び粘着シートの製造方法 Download PDFInfo
- Publication number
- JP4212988B2 JP4212988B2 JP2003302615A JP2003302615A JP4212988B2 JP 4212988 B2 JP4212988 B2 JP 4212988B2 JP 2003302615 A JP2003302615 A JP 2003302615A JP 2003302615 A JP2003302615 A JP 2003302615A JP 4212988 B2 JP4212988 B2 JP 4212988B2
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- adhesive sheet
- film
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
しかしながら、個別包装された粘着シートの端面から粘着剤がはみ出して包装材料の内面を汚したり、粘着シートの背面に粘着剤が回り込んで背面を汚したり、さらには、内面や背面に付着した粘着剤によって、粘着シートを包装材料から取り出し難くなったりすることがあった。特に、粘着剤層が液状成分等を含有する場合には、粘着剤層が粘着シートの端面から滲み出して、粘着シートの背面や包装材料の内側面を汚染しやすく、結果として、粘着シートを包装材料から取り出し難くなることが多かった。
また、前記エラストマーフィルムは、ポリエステルポリウレタン、ポリエーテルポリウレタン、ポリエーテルポリエステル及びポリエーテルポリアミドからなる群から選ばれる1つであることができる。
また、前記担持フィルムは、ポリエチレン、ポリプロピレン及びポリエステルからなる群から選ばれる1つであることができる。
また、前記相溶可能成分が、カルボン酸エステルであることができる。
本発明においては、ポリオール成分として、ポリオキシアルキレン骨格を有するポリエーテルポリオールに、他のポリオール、例えば、ポリオキシテトラメチレングリコール、あるいはブタンジオール、ヘプタンジオール、ヘキサンジオール、シクロヘキサンジメタノール等のポリオールを一部混合して使用することができる。
以下に、バルク重合について具体的に説明する。反応容器にポリオールを投入し、温度が50〜80℃になるように調整し攪拌しつつ、ポリイソシアネートを添加してウレタン化を起こさせる。さらに鎖延長剤を添加して反応させた後、反応生成物をトレーに移動して、100〜150℃で4時間以上保持し、反応を完結させることによって、塊状のポリエーテルポリウレタンを得ることができる。
粘着シートを皮膚へ貼付する際に、皮膚の貼着部位を粘着シートの上から視覚的に確認することができるように、担持フィルム及びエラストマーフィルムは透明または半透明であることが好ましい。また、担持フィルムは、エラストマーフィルムに高い弾性率を付与することができるものであることが好ましく、例えば、常温常湿における引張り試験による50%伸張時のモジュラスが、2N/mm2以上、200N/mm2以下であることが好ましく、8N/mm2以上、50N/mm2以下であることがさらに好ましい。
加熱収縮率(%)=[(L1−L2)/L1]×100
本発明においては、アクリル系重合体と、カルボン酸エステルと、架橋剤とを混合して少なくとも一部に架橋体を形成することによりゲル状の粘着剤層を得ることができる。このようにして得られた粘着剤層は、微小変形領域における弾性率を低下させることができ、皮膚面の凹凸に対して粘着剤層表面の密着性(濡れ性)を向上させて皮膚に対する良好な接着性を発揮することができる。しかも粘着シートを剥離する際には、皮膚面にかかる応力を緩和したり、分散させることができるので、剥離時に皮膚面に対して物理的刺激をほとんど与えることがなく、皮膚面の角質の剥離等もほとんど生じず、皮膚の損傷も極めて少ない、という効果を有する。
なお、本発明において「フィルム」という場合には、シートを含み、「シート」という場合には、フィルムを含む概念とする。
ここで使用される包装材料としては、通常、使用されるものと同様のものを使用することができるが、例えば、ポリエチレンシート、ポリプロピレンシート、ナイロンシート、金属箔等を使用することができる。
具体的には、ポリエチレンシート等からなる袋体に粘着シートを入れ、袋体の開口部をヒートシール等で塞ぎ、滅菌処理を施したもの等が挙げられる。
エラストマー樹脂として、ポリエーテルポリウレタン(大日精化工業(株)製、「レザミンP−210」)を2軸スクリュー型の混練機で加熱溶融させた後、Tダイ式の押出し機を用いて厚みが30μmになるように押出し、エラストマーフィルムを形成した。
担持フィルムとして、加熱収縮率が縦方向2.6%、横方向0.3%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)を用意し、この延伸ポリプロピレンフィルムと、形成したエラストマーフィルムとをゴムロールを用いて密着させ、支持体を得た。
実施例1において、担持フィルムを加熱収縮率が縦方向2.6%、横方向0.5%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向2.8%、横方向0.5%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向3.0%、横方向0.7%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向4.5%、横方向4.2%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向3.0%、横方向1.2%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向3.4%、横方向1.3%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1〜4、比較例1〜3で得られた粘着シートについて、下記に示す評価試験を行った。その結果を表1に示す。
剥離シート付きの粘着シートから剥離シートを剥がし、次に、この粘着シートの粘着剤層面をアルミニウム板に貼付した状態で、エラストマーフィルムから担持フィルムを剥離して担持フィルムのみを得る。この担持フィルムから30mm×40mmの大きさの試料片を切り出し、この試料片を50ccの酢酸エチルに24時間、常温で浸漬して抽出を行った。浸漬後の抽出液をキャピラリーガスクロマトグラフィー分析装置に注入し、クロマトグラムのピーク面積から、担持フィルムに移行した液状成分量を定量した。
架橋処理を施した粘着シートの粘着剤層とは反対側の最外層を肉眼で観察し、凹凸が形成されているか否か確認した。凹凸が形成されていた場合には記号「○」、凹凸が形成されていなかった場合には記号「×」で示す。
次に、この粘着シートを、ポリエチレンシートからなる包装材料で包装して開口部をヒートシールした。この包装材料内に密封された粘着シートを、60℃で72時間保存した後、包装材料から粘着シートを取り出し、下記基準に基づいて評価を行った。
評価基準:
「○」…粘着シートの粘着剤層とは反対側の最外層に、適度な凹凸が形成されており、包装材料から粘着シートをスムースに取り出すことができた場合
「×」…粘着シートの粘着剤層とは反対側の最外層に、適度な凹凸が形成されておらず、包装材料から粘着シートをスムースに取り出すことができなかった場合
Claims (7)
- 担持フィルムの一方の面にエラストマーフィルムを有し、該エラストマーフィルムの上に粘着剤層が設けられた粘着シートであって、該粘着剤層とは反対側の最外層に凹凸が形成されており、前記担持フィルムの加熱収縮率が、縦方向で3.0%以下であり、横方向で0.7%以下であり、かつ、該粘着剤層は架橋処理が施されていて架橋反応が完結していることを特徴とする粘着シート。
- 前記粘着剤層が、アクリル系重合体を主成分とし、かつ、該アクリル系重合体に対して相溶可能であり、常温で液状もしくはペースト状である相溶可能成分を含有する組成物から形成されていることを特徴とする請求項1記載の粘着シート。
- 前記エラストマーフィルムが、ポリエステルポリウレタン、ポリエーテルポリウレタン、ポリエーテルポリエステル及びポリエーテルポリアミドからなる群から選ばれる1つであることを特徴とする請求項1又は2記載の粘着シート。
- 前記担持フィルムが、ポリエチレン、ポリプロピレン及びポリエステルからなる群から選ばれる1つであることを特徴とする請求項1から3のいずれか1項記載の粘着シート。
- 前記相溶可能成分が、カルボン酸エステルであることを特徴とする請求項1から4のいずれか1項記載の粘着シート。
- 請求項1から5のいずれか1項記載の粘着シートを製造する方法であって、担持フィルムとエラストマーフィルムとを積層し、別途剥離シート上に形成した粘着剤層をエラストマーフィルム面に重ねて貼り合わせた後、架橋反応を施すことを特徴とする粘着シートの製造方法。
- 請求項1から5のいずれか1項に記載の粘着シートが、包装材料を用いて包装されていることを特徴とする包装粘着シート。