JP4636263B2 - 熱可塑性フィルムの製造方法 - Google Patents
熱可塑性フィルムの製造方法 Download PDFInfo
- Publication number
- JP4636263B2 JP4636263B2 JP2005323979A JP2005323979A JP4636263B2 JP 4636263 B2 JP4636263 B2 JP 4636263B2 JP 2005323979 A JP2005323979 A JP 2005323979A JP 2005323979 A JP2005323979 A JP 2005323979A JP 4636263 B2 JP4636263 B2 JP 4636263B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- stretching
- cellulose acylate
- thermoplastic film
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
る熱緩和処理と、を連続して行うことを特徴とする。
Rth(nm)=|{(n(MD)+n(TD))/2}−n(TH)|×T(nm)
式中のn(MD)、n(TD)、n(TH)は長手方向、幅方向、厚み方向の屈折率を示し、Tはnm単位で表した厚みを示す。
本発明で用いるセルロースアシレートは以下の特徴を有するものが好ましい。
1.25≦B<3
である。より好ましくは、
Bの1/2以上がプロピオニル基の場合に、
2.6≦A+B≦2.95
2.0≦B≦2.95
Bの1/2未満がプロピオニル基の場合に、
2.6≦A+B≦2.95
1.3≦B≦2.5
である。さらに好ましくは、
Bの1/2以上がプロピオニル基の場合に、
2.7≦A+B≦2.95
2.4≦B≦2.9
Bの1/2未満がプロピオニル基の場合に、
2.7≦A+B≦2.95
1.3≦B≦2.0である。
(1) 乾燥
セルロースアシレート樹脂は粉体のまま用いても良いが、製膜の厚み変動を少なくするためにはペレット化したものを用いるのがより好ましい。
190℃以上240℃以下、より好ましくは195℃以上235℃以下、さらに好ましくは200℃以上230℃以下で混練し溶融する。この時、溶融温度は一定温度で行ってもよく、いくつかに分割して制御しても良い。好ましい混練時間は2分以上60分以下であり、より好ましくは3分以上40分以下であり、さらに好ましくは4分以上30分以下である。さらに、押出機内を不活性(窒素等)気流中、あるいはベント付き押出機を用い真空排気しながら実施するのも好ましい。
溶融したセルロースアシレート樹脂をギヤポンプに通し、押出機の脈動を除去した後、金属メッシュフィルター等でろ過を行い、この後ろに取り付けたT型のダイから冷却ドラム上にシート状に押し出す。押出しは単層で行ってもよく、マルチマニホールドダイやフィードブロックダイを用いて複数層押出しても良い。この時、ダイのリップの間隔を調整することで幅方向の厚みむらを調整することができる。
上述の方法で製膜したセルロースアシレートフィルムを、上述の方法で1軸または2軸に延伸し、延伸セルロースアシレートフィルムを作成する。これは単独で使用してもよく、これらと偏光板を組み合わせて使用してもよく、これらの上に液晶層や屈折率を制御した層(低反射層)やハードコート層を設けて使用しても良い。これらは以下の工程により達成できる。
セルロースアシレートフィルムは表面処理を行うことによって、各機能層(例えば、下塗層およびバック層)との接着を向上させることができる。例えばグロー放電処理、紫外線照射処理、コロナ処理、火炎処理、酸またはアルカリ処理を用いることができる。ここでいうグロー放電処理とは、10-3〜10-20 Torrの低圧ガス下でおこる低温プラズマでもよく、更にまた大気圧下でのプラズマ処理も好ましい。プラズマ励起性気体とは上記のような条件においてプラズマ励起される気体をいい、アルゴン、ヘリウム、ネオン、クリプトン、キセノン、窒素、二酸化炭素、テトラフルオロメタンの様なフロン類及びそれらの混合物などがあげられる。これらについては、詳細が発明協会公開技報(公技番号2001−1745、2001年3月15日発行、発明協会)にて30頁〜32頁に詳細に記載されている。なお、近年注目されている大気圧でのプラズマ処理は、例えば10〜1000Kev下で20〜500Kgyの照射エネルギーが用いられ、より好ましくは30〜500Kev下で20〜300Kgyの照射エネルギーが用いられる。
これらの中でも特に好ましくは、アルカリ鹸化処理である。
本発明のセルロースアシレートフィルムに、発明協会公開技報(公技番号 2001−1745、2001年3月15日発行、発明協会)にて32頁〜45頁に詳細に記載されている機能性層を組み合わせることが好ましい。中でも好ましいのが、偏光層の付与(偏光板)、光学補償層の付与(光学補償シート)、反射防止層の付与(反射防止フィルム)である。
(イ−1)使用素材
現在、市販の偏光層は、延伸したポリマーを、浴槽中のヨウ素もしくは二色性色素の溶液に浸漬し、バインダー中にヨウ素、もしくは二色性色素を浸透させることで作製されるのが一般的である。偏光膜は、Optiva Inc.に代表される塗布型偏光膜も利用できる。偏光膜におけるヨウ素および二色性色素は、バインダー中で配向することで偏向性能を発現する。二色性色素としては、アゾ系色素、スチルベン系色素、ピラゾロン系色素、トリフェニルメタン系色素、キノリン系色素、オキサジン系色素、チアジン系色素あるいはアントラキノン系色素が用いられる。二色性色素は、水溶性であることが好ましい。二色性色素は、親水性置換基(例、スルホ、アミノ、ヒドロキシル)を有することが好ましい。例えば、発明協会公開技法、公技番号2001−1745号、58頁(発行日2001年3月15日)に記載の化合物が挙げられる。
偏光膜は、偏光膜を延伸するか(延伸法)、もしくはラビングした(ラビング法)後に、ヨウ素、二色性染料で染色することが好ましい。
延伸に先立ち、PVAフィルムを膨潤させる。膨潤度は1.2〜2.0倍(膨潤前と膨潤後の重量比)である。この後、ガイドロール等を介して連続搬送しつつ、水系媒体浴内や二色性物質溶解の染色浴内で、15〜50℃、就中17〜40℃の浴温で延伸する。延伸は2対のニップロールで把持し、後段のニップロールの搬送速度を前段のそれより大きくすることで達成できる。延伸倍率は、延伸後/初期状態の長さ比(以下同じ)に基づくが前記作用効果の点より好ましい延伸倍率は1.2〜3.5倍、就中1.5〜3.0倍である。この後、50℃から90℃において乾燥させて偏光膜を得る。
これには特開2002−86554号公報に記載の斜め方向に傾斜め方向に張り出したテンターを用い延伸する方法を用いることができる。この延伸は空気中で延伸するため、事前に含水させて延伸しやすくすることが必用である。好ましい含水率は5%以上100%以下、より好ましくは10%以上100%以下である。
上記鹸化後のセルロースアシレートフィルムと、延伸して調製した偏光層を貼り合わせ偏光板を調製する。張り合わせる方向は、セルロースアシレートフィルムの流延軸方向と偏光板の延伸軸方向が45度になるように行うのが好ましい。
光学異方性層は、液晶表示装置の黒表示における液晶セル中の液晶化合物を補償するためのものであり、セルロースアシレートフィルムの上に配向膜を形成し、さらに光学異方性層を付与することで形成される。
上記表面処理したセルロースアシレートフィルム上に配向膜を設ける。この膜は、液晶性分子の配向方向を規定する機能を有する。しかし、液晶性化合物を配向後にその配向状態を固定してしまえば、配向膜はその役割を果たしているために、本発明の構成要素としては必ずしも必須のものではない。即ち、配向状態が固定された配向膜上の光学異方性層のみを偏光子上に転写して本発明の偏光板を作製することも可能である。
配向膜は、有機化合物(好ましくはポリマー)のラビング処理、無機化合物の斜方蒸着、マイクログルーブを有する層の形成、あるいはラングミュア・ブロジェット法(LB膜)による有機化合物(例、ω- トリコサン酸、ジオクタデシルメチルアンモニウムクロライド、ステアリル酸メチル)の累積のような手段で設けることができる。さらに、電場の付与、磁場の付与あるいは光照射により、配向機能が生じる配向膜も知られている。
棒状液晶性分子としては、アゾメチン類、アゾキシ類、シアノビフェニル類、シアノフェニルエステル類、安息香酸エステル類、シクロヘキサンカルボン酸フェニルエステル類、シアノフェニルシクロヘキサン類、シアノ置換フェニルピリミジン類、アルコキシ置換フェニルピリミジン類、フェニルジオキサン類、トラン類およびアルケニルシクロヘキシルベンゾニトリル類が好ましく用いられる。
円盤状(ディスコティック)液晶性分子には、C.Destradeらの研究報告、Mol.Cryst.71巻、111頁(1981年)に記載されているベンゼン誘導体、C.Destradeらの研究報告、Mol.Cryst.122巻、141頁(1985年)、Physicslett,A,78巻、82頁(1990)に記載されているトルキセン誘導体、B.Kohneらの研究報告、Angew.Chem.96巻、70頁(1984年)に記載されたシクロヘキサン誘導体及びJ.M.Lehnらの研究報告、J.Chem.Commun.,1794頁(1985年)、J.Zhangらの研究報告、J.Am.Chem.Soc.116巻、2655頁(1994年)に記載されているアザクラウン系やフェニルアセチレン系マクロサイクルが含まれる。
上記の液晶性分子と共に、可塑剤、界面活性剤、重合性モノマー等を併用して、塗工膜の均一性、膜の強度、液晶分子の配向性等を向上することが出来る。液晶性分子と相溶性を有し、液晶性分子の傾斜角の変化を与えられるか、あるいは配向を阻害しないことが好ましい。
光学異方性層は、液晶性分子および必要に応じて後述の重合性開始剤や任意の成分を含む塗布液を、配向膜の上に塗布することで形成できる。
配向させた液晶性分子を、配向状態を維持して固定することができる。固定化は、重合反応により実施することが好ましい。重合反応には、熱重合開始剤を用いる熱重合反応と光重合開始剤を用いる光重合反応とが含まれる。光重合反応が好ましい。
ことが好ましい。通常の傾斜角度は45゜である。しかし、最近は、透過型、反射型および半透過型LCDにおいて必ずしも45゜でない装置が開発されており、延伸方向はLCDの設計にあわせて任意に調整できることが好ましい。
このような光学補償フィルムが用いられる各液晶モードについて説明する。
カラーTFT液晶表示装置として最も多く利用されており、多数の文献に記載がある。TNモードの黒表示における液晶セル中の配向状態は、セル中央部で棒状液晶性分子が立ち上がり、セルの基板近傍では棒状液晶性分子が寝た配向状態にある。
棒状液晶性分子を液晶セルの上部と下部とで実質的に逆の方向に(対称的に)配向させるベンド配向モードの液晶セルである。ベンド配向モードの液晶セルを用いた液晶表示装置は、米国特許4583825号、同5410422号の各明細書に開示されている。棒状液晶性分子が液晶セルの上部と下部とで対称的に配向しているため、ベンド配向モードの液晶セルは、自己光学補償機能を有する。そのため、この液晶モードは、OCB(Optically Compensatory Bend) 液晶モードとも呼ばれる。
電圧無印加時に棒状液晶性分子が実質的に垂直に配向しているのが特徴であり、VAモードの液晶セルには、(1)棒状液晶性分子を電圧無印加時に実質的に垂直に配向させ、電圧印加時に実質的に水平に配向させる狭義のVAモードの液晶セル(特開平2−176625号公報記載)に加えて、(2)視野角拡大のため、VAモードをマルチドメイン化した(MVAモードの)液晶セル(SID97、Digest of tech. Papers(予稿集)28(1997)845記載)、(3)棒状液晶性分子を電圧無印加時に実質的に垂直配向させ、電圧印加時にねじれマルチドメイン配向させるモード(n−ASMモード)の液晶セル(日本液晶討論会の予稿集58〜59(1998)記載)および(4)SURVAIVALモードの液晶セル(LCDインターナショナル98で発表)が含まれる。
電圧無印加時に棒状液晶性分子が実質的に面内に水平に配向しているのが特徴であり、これが電圧印加の有無で液晶の配向方向を変えることでスイッチングするのが特徴である。具体的には特開2004−365941号公報、特開2004−12731号公報、特開2004−215620号公報、特開2002−221726号公報、特開2002−55341号公報、及び特開2003−195333号公報に記載のものなどを使用できる。
ECBモードおよびSTNモードに対しても、上記と同様の考え方で光学的に補償することができる。
反射防止膜は、一般に、防汚性層でもある低屈折率層、及び低屈折率層より高い屈折率を有する少なくとも一層の層(即ち、高屈折率層、中屈折率層)とを透明基体上に設けて成る。
基体上に少なくとも中屈折率層、高屈折率層、低屈折率層(最外層)の順序の層構成から成る反射防止膜は、以下の関係を満足する屈折率を有する様に設計される。
反射防止膜の高い屈折率を有する層は、平均粒径100nm以下の高屈折率の無機化合物超微粒子及びマトリックスバインダーを少なくとも含有する硬化性膜から成る。
低屈折率層は、高屈折率層の上に順次積層して成る。低屈折率層の屈折率は1.20〜1.55である。好ましくは1.30〜1.50である。
ハードコート層は、反射防止フィルムに物理強度を付与するために、透明支持体の表面に設ける。特に、透明支持体と前記高屈折率層の間に設けることが好ましい。
前方散乱層は、液晶表示装置に適用した場合の、上下左右方向に視角を傾斜させたときの視野角改良効果を付与するために設ける。上記ハードコート層中に屈折率の異なる微粒子を分散することで、ハードコート機能と兼ねることもできる。
例えば、前方散乱係数を特定化した特開11−38208号公報、透明樹脂と微粒子の相対屈折率を特定範囲とした特開2000−199809号公報、ヘイズ値を40%以上と規定した特開2002−107512号公報等が挙げられる。
上記の層以外に、プライマー層、帯電防止層、下塗り層や保護層等を設けてもよい。
反射防止フィルムの各層は、ディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、グラビアコート、マイクログラビア法やエクストルージョンコート法(米国特許2681294号明細書)により、塗布により形成することができる。
反射防止膜は、外光を散乱させるアンチグレア機能を有していてもよい。アンチグレア機能は、反射防止膜の表面に凹凸を形成することにより得られる。反射防止膜がアンチグレア機能を有する場合、反射防止膜のヘイズは、3〜30%であることが好ましく、5〜20%であることがさらに好ましく、7〜20%であることが最も好ましい。
サンプルフィルムを温度5℃、湿度60%rhに3時間以上調湿後、自動複屈折計(KOBRA-21ADH/PR:王子計測器(株)製)を用いて、25℃、60%rhにおいて、サンプルフィルム表面に対し垂直方向および、フィルム面法線から±40°傾斜させて方向から波長550nmにおけるレターデーション値を測定する。垂直方向から面内のレターデーション(Re)、垂直方向、±40°方向の測定値から厚み方向のレターデーション(Rth)を算出する。
(1)MD方向サンプリング
フィルムの長手方向に0.5m間隔で100点、1cm正方形の大きさに切り出す。
フィルムの製膜全幅にわたり、1cm正方形の大きさに50点、等間隔で切り出す。
サンプルフィルムを温度5℃、湿度60%rhに3時間以上調湿後、自動複屈折計(KOBRA-21ADH/PR:王子計測器(株)製)を用いて、25℃、60%rhにおいて、サンプルフィルム表面に対し垂直方向および、フィルム面法線から±40°傾斜させて方向から波長550nmにおけるレターデーション値を測定する。垂直方向から面内のレターデーション(Re)、垂直方向、±40°方向の測定値から厚み方向のレターデーション(Rth)を算出する。
これらの、上記MD方向100点、TD方向50点の各最大値と最小値の差を、各平均値で割り、百分率で示したものをRe,Rth変動とした。
東洋精機製、加熱テンシロンを用い、それぞれのサンプルのTg+10℃に加熱したオーブン中で1分間予熱した後、チャック間100mm、引っ張り速度100mm/min条件にて破断するまで延伸し、破断伸度を求めた。
セルロースアシレートのアシル置換度は、Carbohydr.Res.273(1995)83−91(手塚他)に記載の方法で13C−NMRにより求めた。
島津製作所製 DSC−50を用い昇温速度10℃/minで測定し、Tg直後に現 れる吸熱ピークの熱量をJ/gで算出した。同時にTgも測定した。
日本電色工業(株)製、濁度計 NDH−1001DPを用いて測定した。
Z−II OPTICAL SENSOR を用い(JIS K7105 6.3)に 従い黄色味(YI;イエローネスインデックス)を測定した。
さらにフィルムのYI値は上記式にて算出したYI値を、そのフィルムの厚みで割り、1mm当たりに換算して比較した。
フイルムサンプルをジクロロメタンに溶解し、GPCを用いて測定した。
絶乾したセルロースアシレート約0.2gを精秤し、メチレンクロリド:エタノール=9:1(質量比)の混合溶剤100mlに溶解した。これをオストワルド粘度計にて25℃で落下秒数を測定し、重合度を以下の式により求めた。
[η]=(1nηrel )/C
DP=[η]/Km
ただし、T:測定試料の落下秒数、T0 :溶剤単独の落下秒数、C:濃度(g/l)、Km:6×10-4とする。
DSCの測定パンにサンプルを20mg入れる。これを窒素気流中で、10℃/分で30℃から250℃まで昇温した後(1st-run)、30℃まで−10℃/分で冷却する。この後、再度30℃から250℃まで昇温する(2nd-run)。2nd-runでベースラインが低温側から偏奇し始める温度をガラス転移温度(Tg)とした。また、全水準に二酸化珪素部粒子(アエロジルR972V)0.05質量%を添加した。
(1)サンプルフィルムを25cm×5cmに裁断後、25℃60%RHに3時間以上調湿し、20cm基長のピンゲージで測定する。その値をXcmとする。
セルロースアシレートの調製は、触媒として硫酸(セルロース100重量部に対し7.8重量部)を添加し、アシル置換基の原料となるカルボン酸を添加し40℃でアシル化反応を行った。この時、カルボン酸の種類、量を調整することで、アシル基の種類、置換度を調整した。また、アシル化後の40℃で熟成を行った。
上記セルロースアシレート樹脂を直径3mm長さ5mmの円柱状のペレットに成形した。この際、可塑剤は以下の中から選定し、ペレットに混練した。これを110℃の真空乾燥機で乾燥し、含水率を0.1%以下とした後、Tg−10℃になるように調整してホッパーに投入した。可塑剤の種類としては、TPP:トリフェニルフォスフェート、BDP:ビフェニルジフェニルフォスフェート、DOA:ビス(2−エチルヘキシル)アジペート、PTP:1,4−フェニレン−テトラフェニルリン酸エステルを選択して用いた。
上記溶融製膜で製造されたセルロースアシレートフィルムを、Tg+5℃で縦方向に1.2倍延伸した後、表1(図5)に記載の延伸倍率で横延伸した。そして、横延伸したセルロースアシレートフィルムを冷却した後、熱緩和処理した。その際の予熱処理、延伸処理、冷却処理、熱緩和処理の時間やゾーン長さ等の延伸条件を表1に記載した。
表1から分かるように、実施例1〜10は、延伸処理の後にTg未満の冷却処理と、Tg以上の熱緩和処理を行っており、これによって、熱寸法率、ボーイングともに良好なセルロースアシレートフィルムが得られた。
(1)表面処理
延伸後の延伸セルロースアシレートフィルムを下記のいずれかの方法で鹸化を行った。
iso- プロパノール80重量部に水20重量部を加え、これにKOHを1.5規定となるように溶解し、これを60℃に調温したものを鹸化液として用いた。これを60℃のセルロースアシレートフィルム上に10g/m2 塗布し、1分間鹸化した。この後、50℃の温水をスプレーを用い、10L/m2 ・分で1分間吹きかけて洗浄した。
NaOHの1.5規定水溶液を鹸化液として用いた。これを60℃に調温し、セルロースアシレートフィルムを2分間浸漬した。この後、0.1Nの硫酸水溶液に30秒浸漬した後、水洗浴を通した。
特開平2001−141926号公報の実施例1に従い、2対のニップロール間に周速差を与え、長手方向に延伸したで厚み20μmの偏光層を調製した。この時、製膜、延伸直後のものと、80℃で1カ月経時後のものを作成した。なお、特開平2002−86554号公報の実施例1のように延伸軸が斜め45度となるように延伸した偏光層も同様に作成したが、以降の評価結果は上述のものと同様な結果が得られた。
このようにして得た延伸直後のもの(フレッシュ品)と80℃で1カ月経時(経時品)したもので作成した偏光層を、上記鹸化処理した延伸セルロースアシレートフィルム(位相差板)と鹸化処理した偏光板保護フィルム(商品名:フジタック)の間に挟み込んだ。この際、位相差板と偏光層の接着は、位相差板がセルロースアシレートの場合はPVA((株)クラレ製PVA−117H)3%水溶液を接着剤とし、位相差板がこれ以外の場合はエポキシ系接着剤を用いて貼り合わせた。またフジタックと偏光層の間は上述のPVA水溶液を接着剤として貼り合わせた。貼り合わせ方向は、偏光軸と位相差板の長手方向が45度となるようした。このようにして得た偏光板は位相差板を液晶側に、フジタックを外側(目視側)になるようにして、特開2000−154261号公報の図2〜9に記載の20インチVA型液晶表示装置液晶表示装置に取り付けた。これをフレッシュ品の偏光板を用いたものと、経時品の偏光板を用いたものを比較し、目視評価し、色むらの発生領域の全面積に占める割合を調べたところ、本発明を実施したものは良好な性能が得られた。
特開平11−316378号公報の実施例1の液晶層を塗布したセルロースアセテートフィルムの代わりに、本発明の延伸セルロースアシレートフィルムを使用した。この時、製膜、延伸直後のもの(フレッシュ品)を用いた場合と80℃で1カ月経時させたもの(経時品)を用いたもので作成し、両者比較し色むらの発生している領域を目視評価し、全面積に占める割合で示した。その結果、本発明セルロースアシレートフィルムを使用して製造した延伸セルロースアシレートフィルムを用いたものは良好な光学補償フィルムを作成できた。
本発明の延伸セルロースアシレートフィルムを発明協会公開技報(公技番号2001−1745号公報)の実施例47に従い本発明の延伸セルロースアシレートフィルムを用いて低反射フィルムを作成したところ、良好な光学性能が得られた。
上記本発明の偏光板を、特開平10−48420号公報の実施例1に記載の液晶表示装置、特開平9−26572号公報の実施例1に記載のディスコティック液晶分子を含む光学的異方性層、ポリビニルアルコールを塗布した配向膜、特開2000−154261号公報の図2〜9に記載の20インチVA型液晶表示装置、特開2000−154261号公報の図10〜15に記載の20インチOCB型液晶表示装置、特開2004−12731の図11に記載のIPS型液晶表示装置に用いた。さらに、本発明の低反射フィルムをこれらの液晶表示装置の最表層に貼り評価を行ったところ、良好な液晶表示素子を得るこ
とができた。
Claims (8)
- 熱可塑性フィルムを幅方向に延伸する延伸工程を有する熱可塑性フィルムの製造方法において、
前記延伸工程は、
前記熱可塑性フィルムを延伸する延伸処理と、該延伸処理した熱可塑性フィルムをガラス転移温度Tg未満で冷却する冷却処理と、該冷却処理した熱可塑性フィルムをTg以上で熱緩和する熱緩和処理と、を連続して行うことを特徴とする熱可塑性フィルムの製造方法。 - 前記延伸処理を行う延伸ゾーンの前記熱可塑性フィルムの走行方向の長さをL1、前記冷却処理を行う冷却ゾーンの前記熱可塑性フィルムの走行方向の長さをL2とした際に、L2/L1が0.2以上20以下であることを特徴とする請求項1に記載の熱可塑性フィルムの製造方法。
- 前記熱緩和処理は、前記熱可塑性フィルムの幅寸法を0〜30%収縮させることを特徴とする請求項1又は2に記載の熱可塑性フィルムの製造方法。
- 前記熱緩和処理後の熱可塑性フィルムは、温度60℃、相対湿度90%の状態で24時間保持した際の寸法変化率が、幅方向、長手方向ともに±1%以下であることを特徴とする請求項1〜3のいずれか1に記載の熱可塑性フィルムの製造方法。
- 前記熱可塑性フィルムは飽和ノルボルネン系フィルムであることを特徴とする請求項1〜4のいずれか1に記載の熱可塑性フィルムの製造方法。
- 前記熱可塑性フィルムはセルロースアシレート樹脂を用いて製膜したセルロースアシレートフィルムであることを特徴とする請求項1〜4のいずれか1に記載の熱可塑性フィルムの製造方法。
- 前記セルロースアシレート樹脂は、Aをアセチル基の置換度、Bをプロピオニル基、ブチリル基、ペンタノイル基、ヘキサノイル基の置換度の総和としたときに、アシレート基が下記の置換度、
2.0≦A+B≦3.0、
0≦A≦2.0、
1.2≦B≦2.9
を満足することを特徴とする請求項6に記載の熱可塑性フィルムの製造方法。 - 前記延伸処理は、前記熱可塑性フィルムの幅方向の端部を把持し、少なくとも1倍以上2.5倍以下に延伸することを特徴とする請求項1〜7のいずれか1に記載の熱可塑性フィルムの製造方法。