JP3142921B2 - Insulation panel for torch method - Google Patents
Insulation panel for torch methodInfo
- Publication number
- JP3142921B2 JP3142921B2 JP03295764A JP29576491A JP3142921B2 JP 3142921 B2 JP3142921 B2 JP 3142921B2 JP 03295764 A JP03295764 A JP 03295764A JP 29576491 A JP29576491 A JP 29576491A JP 3142921 B2 JP3142921 B2 JP 3142921B2
- Authority
- JP
- Japan
- Prior art keywords
- asphalt
- sheet
- glass fiber
- torch
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は建築物の屋根等のトーチ
工法に使用されるフェノールフォーム断熱パネルに関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a phenol foam insulation panel used in a torch method for building roofs and the like.
【０００２】[0002]
【従来の技術】従来、トーチ工法に使用される断熱材と
して、改質アスファルトシート防水トーチ工法施工指針
・同解説（日本建築学会編集発行 １９９０年６月５
日）に記載されているように、ポリスチレンフォームや
硬質ウレタンフォームが知られている。2. Description of the Related Art Conventionally, as a heat insulating material used in the torch method, a modified asphalt sheet waterproof torch method construction guideline and explanation (edited by the Architectural Institute of Japan, June 5, 1990)
As described in Japanese Patent Application Laid-Open (JP-A) No. 2000-216, polystyrene foam and rigid urethane foam are known.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、これら
の断熱材を使用したトーチ工法は、次のような問題があ
った。ポリスチレンフォームや硬質ウレンタンフォーム
等の断熱材は耐熱性が小さく、直接これらの断熱材にト
ーチバーナーをあてて防水シートを融着させようとする
と、断熱材が２次発泡を起こしたり、あるいは軟化点以
上の温度に達して大きく変形してしまったり、燃焼して
しまい断熱性能、防水性能が低下するので施工すること
ができない。そこで、前記の改質アスファルトシート防
水トーチ工法施工・同解説に記載されているように、断
熱材をセットしてから厚さ２ｍｍ以上の粘着層付シート
を断熱材の表面に接着させて、防水シートを融着させる
時にトーチバーナーの炎を間接的にうけるような工程を
とるようにしている。その為に断熱材を使用するトーチ
工法は工程数が多くなり施工性が悪いという問題があっ
た。また粘着層付シートと断熱材の接着は粘着層付シー
トの粘着剤によるもので接着力が小さく改善が望まれて
いた。However, the torch method using these heat insulating materials has the following problems. Insulation materials such as polystyrene foam and rigid urethane foam have low heat resistance. If a torch burner is directly applied to these insulation materials to fuse the waterproof sheet, the insulation material may cause secondary foaming or softening. It cannot be installed because it reaches a temperature above the point and is greatly deformed or burns, and the heat insulation performance and waterproof performance are reduced. Therefore, as described in the above description of the modified asphalt sheet waterproof torch method construction, the heat insulating material is set, and then a sheet with an adhesive layer having a thickness of 2 mm or more is adhered to the surface of the heat insulating material, and the waterproofing is performed. When the sheets are fused, a process is performed to indirectly receive the flame of the torch burner. Therefore, the torch method using a heat insulating material has a problem that the number of steps is increased and workability is poor. Further, the adhesion between the sheet with the adhesive layer and the heat insulating material is due to the adhesive of the sheet with the adhesive layer, and the adhesive force is small and improvement has been desired.
【０００４】本発明の目的は上記問題点に鑑み、耐熱性
が優れ防水シートをトーチバーナーにより直接融着する
ことが可能で、かつ、防水シートとの接着力が大きくズ
レや剥離が生じないトーチ工法用断熱パネルを提供する
ことにある。In view of the above problems, an object of the present invention is to provide a torch which has excellent heat resistance, can directly fuse a waterproof sheet with a torch burner, and has a large adhesive force with the waterproof sheet and does not cause displacement or peeling. An object of the present invention is to provide a heat insulating panel for a construction method.
【０００５】[0005]
【課題を解決するための手段】本発明は、フェノールフ
ォームのすくなくとも片面にアスファルト含浸ガラス繊
維シートが積層されていることを特徴とするトーチ工法
用断熱パネルである。本発明で言うフェノールフォーム
とは、フェノール類とアルデヒド類の反応によって生成
するフェノール樹脂の発泡体のことである。フェノール
フォームは、ポリスチレンフォームや硬質ウレタンフォ
ーム等と比べ、耐熱性、難熱性が格段に優れており、ア
スファルト含浸ガラス繊維シートをすくなくとも片面に
積層することにより、防水シートをトーチバーナーで直
接融着することが可能となる。フェノールフォームの厚
さは、屋根等に要求される断熱性能により定まるが、通
常、１０〜１００ｍｍの範囲が好ましい。SUMMARY OF THE INVENTION The present invention is a heat insulating panel for a torch method, wherein a glass fiber sheet impregnated with asphalt is laminated on at least one side of a phenol foam. The phenol foam referred to in the present invention is a phenol resin foam produced by a reaction between phenols and aldehydes. Phenol foam is remarkably superior in heat resistance and heat resistance compared to polystyrene foam or rigid urethane foam, etc., and the waterproof sheet is directly fused with a torch burner by laminating at least one side of an asphalt-impregnated glass fiber sheet. It becomes possible. The thickness of the phenol foam is determined by the heat insulating performance required for a roof or the like, but is usually preferably in the range of 10 to 100 mm.
【０００６】本発明で言うアスファルトを含浸したガラ
ス繊維シートとは、ガラス繊維の織布もしくは不織布に
アスファルトを含浸したものである。アスファルト含浸
ガラス繊維シートは、シートの骨格をなしている繊維部
分の耐熱性が良好であり、トーチバーナーの火が当たっ
てもめくれや著しい変形がなく、溶融するアスファルト
により防水シートと一体化するので大きな接着力が得ら
れる。また、アスファルトを含浸させることにより、ガ
ラス繊維による皮膚への刺激もなく、取扱い性にも優れ
る。The glass fiber sheet impregnated with asphalt according to the present invention is a glass fiber woven or nonwoven fabric impregnated with asphalt. Asphalt impregnated glass fiber sheet has good heat resistance of the fiber part that forms the skeleton of the sheet, does not turn up or noticeable deformation even when the torch burner is hit, and is integrated with the waterproof sheet by melting asphalt Great adhesion is obtained. In addition, by impregnating with asphalt, the skin is not irritated by the glass fiber and the handleability is excellent.
【０００７】アスファルト含浸ガラス繊維シートは、原
反であるガラス繊維の織布もしくは不織布に熱溶融した
アスファルトを浸漬や片面塗工あるいは両面塗工等の方
法により含浸させて製造することができる。アスファル
トは、ストレートアスファルト、ブローンアスファル
ト、防水工事用アスファルト、ポリマー改質アスファル
ト等種々なものが使用できるが、軟化点が５０℃以上の
ものが好ましい。軟化点が５０℃以下ではトーチバーナ
ー等で加熱しなくても軟化する場合があり、取扱い性が
悪く好ましくない。本発明のアスファルト含浸ガラス繊
維シートを製造するための量は、シートの強度をたもた
せることとアスファルトの含浸性が良好なことから、２
０ｇ／ｍ2 から２００ｇ／ｍ2 の範囲が好ましい。ま
た、アスファルト含浸ガラス繊維シートの坪量は、ガラ
ス繊維織布もしくは不織布の坪量の２倍から１０倍程度
にすることが好ましい。２倍以下ではアスファルトの含
浸量が少なすぎて防水シートとの接着性が小さくなり、
１０倍以上ではアスファルトの含浸量が多すぎてシート
の表面に厚いアスファルト層が生じ、耐ブロッキング性
能が悪くなり製造や運搬時の取扱いに支障をきたした
り、また、シートの屈曲性が低下し取扱い中に折れやす
くなる。アスファルト含浸ガラス繊維シートの坪量と厚
さは、パネルの切断加工性の点から、各々、４０ｇ／ｍ
2 から２０００ｇ／ｍ2 の範囲が、厚さは０．１ｍｍか
ら２ｍｍの範囲が好ましい。A glass fiber sheet impregnated with asphalt can be produced by impregnating a woven or nonwoven fabric of glass fiber as a raw fabric with hot melted asphalt by a method such as immersion, single-side coating or double-side coating. As the asphalt, various ones such as straight asphalt, blown asphalt, asphalt for waterproofing work, and polymer modified asphalt can be used, but those having a softening point of 50 ° C. or more are preferable. If the softening point is 50 ° C. or lower, the material may soften without heating with a torch burner or the like, and the handling property is poor, which is not preferable. The amount for producing the asphalt-impregnated glass fiber sheet of the present invention is 2% because the sheet has strength and the asphalt impregnation is good.
A range from 0 g / m 2 to 200 g / m 2 is preferred. The basis weight of the asphalt-impregnated glass fiber sheet is preferably about 2 to 10 times the basis weight of the glass fiber woven or nonwoven fabric. If it is less than twice, the amount of asphalt impregnation is too small, and the adhesion to the waterproof sheet will be small,
If it is more than 10 times, the amount of asphalt impregnated is too large and a thick asphalt layer is formed on the surface of the sheet, and the blocking resistance is deteriorated, which hinders the handling during manufacture and transportation, and the flexibility of the sheet is reduced and the handling is reduced. It breaks easily. The basis weight and thickness of the asphalt-impregnated glass fiber sheet are each 40 g / m2 from the viewpoint of panel cutability.
The thickness is preferably in the range of 2 to 2000 g / m 2 and the thickness is preferably in the range of 0.1 mm to 2 mm.
【０００８】以上詳述した本発明で使用するアスファル
ト含浸ガラス繊維シートをフェノールフォーム以外の断
熱材、例えばポリスチレンフォーム、硬質ウレタンフォ
ームあるいはイソシアヌレートフォーム等に積層して
も、これらの断熱材はフェノールフォームに比べ耐熱
性、難燃性が小さく、トーチバーナーの火が当たると変
形や燃焼が起こるので施工できなくなる。また、厚さの
大きいシートをこれらの断熱材に積層するとシートによ
り保護された部分の変形、燃焼は防ぐことはできるが、
パネルとパネルの継ぎ目やパラペット、役物との取り合
い等の隙間からトーチバーナーの火が小口にまわり、や
はり変形、燃焼が起こり施工できなくなる。フェノール
フォームの場合には耐熱性、難燃性が優れているので、
トーチバーナーの火が小口に当たっても表面が多少炭化
するだけであり、断熱性能、防水性能はなんら問題なく
施工することができる。[0008] Even if the asphalt-impregnated glass fiber sheet used in the present invention described above is laminated on a heat insulating material other than phenol foam, for example, polystyrene foam, hard urethane foam or isocyanurate foam, these heat insulating materials are phenol foam. Heat resistance and flame retardancy are smaller than those of the torch burner. In addition, when a sheet with a large thickness is laminated on these heat insulating materials, deformation and burning of the portion protected by the sheet can be prevented,
The fire of the torch burner circulates from the gaps between the panels, the joints between the panels, the parapets, the connection with the accessories, etc., leading to deformation and burning, which makes the construction impossible. Phenol foam has excellent heat resistance and flame retardancy,
Even if the fire of the torch burner hits the forehead, the surface is only slightly carbonized, and the insulation performance and waterproof performance can be implemented without any problem.
【０００９】フェノールフォームとアスファルト含浸ガ
ラス繊維シートは、フェノールフォームの発泡硬化時に
アスファルト含浸ガラス繊維シートをフェノールフォー
ムに接触させフェノールフォームの自己接着力により積
層することができる。また、あらかじめフェノールフォ
ーム発泡体を成型しておき、その後にアスファルト含浸
ガラス繊維シートを加熱しながら圧着し、アスファルト
の接着力により積層することもできる。また、接着剤に
よりフェノールフォームとアスファルト含浸ガラス繊維
シートを積層することもできる。この場合、使用する接
着剤は耐熱性のすぐれた無機系接着剤やフェノール系、
レゾルシノール系接着剤が好ましい。The phenol foam and the asphalt-impregnated glass fiber sheet can be laminated by bringing the asphalt-impregnated glass fiber sheet into contact with the phenol foam at the time of foaming and curing of the phenol foam, by the self-adhesive force of the phenol foam. Alternatively, a phenol foam foam may be molded in advance, and then the asphalt-impregnated glass fiber sheet may be pressure-bonded while being heated, and may be laminated by the asphalt adhesive force. Further, a phenol foam and an asphalt-impregnated glass fiber sheet can be laminated with an adhesive. In this case, the adhesive used is an inorganic adhesive with excellent heat resistance, a phenolic adhesive,
Resorcinol adhesives are preferred.
【００１０】アスファルト含浸ガラス繊維シートはフェ
ノールフォームの片面に積層してもよく、両面に積層し
てもよい。前者の場合、もう一方の片面は防水、防湿性
の高いシート例えば、ポリエチレンコート紙やポリマー
ラテックスコート紙等を積層することが好ましい。次に
本発明を図面により説明する。図１は、フェノールフォ
ーム層１とアスファルト含浸ガラス繊維シート２が積層
された本発明のトーチ工法用断熱パネルの断面図であ
る。図２は、本発明のトーチ工法用断熱パネルを用いた
屋根等の断熱防水の施工図である。まず屋根のコンクリ
ート４の上に、接着剤３を用いて本発明のトーチ工法用
断熱パネルを接着する。接着剤は、エポキシ系、ウレタ
ン系、合成ゴム系等のものが用いられる。次に、その上
にロール状に巻いた改質アスファルトからなる防水シー
ト５を巻き戻しながら、改質アスファルトからなる防水
シート５および本発明のトーチ工法用断熱パネルの表層
部のアスファルト含浸ガラス繊維シート２をトーチバー
ナー６であぶり、アスファルトを溶融し両者を押しつけ
て接着一体化させる。以下、実施例を挙げて、本発明を
更に具体的に説明する。The asphalt-impregnated glass fiber sheet may be laminated on one side of the phenol foam or on both sides. In the former case, the other side is preferably laminated with a sheet having high waterproof and moisture-proof properties, for example, polyethylene-coated paper or polymer latex-coated paper. Next, the present invention will be described with reference to the drawings. FIG. 1 is a sectional view of a heat insulation panel for a torch method according to the present invention in which a phenol foam layer 1 and an asphalt-impregnated glass fiber sheet 2 are laminated. FIG. 2 is a construction diagram of insulation and waterproofing of a roof or the like using the insulation panel for a torch method of the present invention. First, the insulating panel for the torch method of the present invention is bonded on the roof concrete 4 using the adhesive 3. As the adhesive, an epoxy-based, urethane-based, synthetic rubber-based adhesive, or the like is used. Next, while unwinding the waterproof sheet 5 made of the modified asphalt wound thereon, the waterproof sheet 5 made of the modified asphalt and the asphalt-impregnated glass fiber sheet of the surface layer portion of the heat insulating panel for the torch method of the present invention are used. 2 is blown with a torch burner 6, the asphalt is melted, and both are pressed to be bonded and integrated. Hereinafter, the present invention will be described more specifically with reference to examples.
【００１１】[0011]
【実施例】単位面積あたりの重量が５０ｇ／ｍ2 である
ガラス繊維不織布にアスファルト（防水工事用アスファ
ルト 軟化点１００℃）を溶融浸漬により含浸させ、単
位面積あたり２８０ｇ／ｍ2 のアスファルト含浸ガラス
繊維シート（厚さ０．３ｍｍ）を得た。これを５０×５
０×２ｃｍのステンレス製モールドの底部にセットし
た。そして、この中にレゾール樹脂、フロン系発泡剤、
硬化剤、整泡剤等の混合物を注入し、ただちに７０℃の
雰囲気中で３０分間養生して片面にアスファルト含浸ガ
ラス繊維シートが積層された断熱パネルを得た。EXAMPLE A glass fiber non-woven fabric having a weight per unit area of 50 g / m 2 is impregnated with asphalt (asphalt softening point 100 ° C. for waterproofing work) at a melting temperature of 100 ° C., and asphalt-impregnated glass fiber of 280 g / m 2 per unit area. A sheet (thickness 0.3 mm) was obtained. This is 50 × 5
It was set on the bottom of a stainless steel mold of 0 × 2 cm. And in this, resole resin, CFC-based foaming agent,
A mixture of a curing agent, a foam stabilizer and the like was injected, and the mixture was immediately cured in an atmosphere at 70 ° C. for 30 minutes to obtain a heat insulating panel having an asphalt-impregnated glass fiber sheet laminated on one surface.
【００１２】[0012]
【比較例１】実施例で用いた単位面積あたりの重量が５
０ｇ／ｍ2 であるガラス繊維不織布をそのままの状態で
実施例と同じ方法によりフェノールフォームの片面に積
層した。Comparative Example 1 The weight per unit area used in Examples was 5
A glass fiber nonwoven fabric of 0 g / m 2 was laminated as it was on one surface of the phenol foam in the same manner as in the example.
【００１３】[0013]
【比較例２】単位面積あたりの重量が４２０ｇ／ｍ2 の
市販のアスファルトフェルトを実施例と同じ方法により
フェノールフォームの片面に積層した。Comparative Example 2 A commercially available asphalt felt having a weight per unit area of 420 g / m 2 was laminated on one surface of a phenol foam in the same manner as in the example.
【００１４】[0014]
【比較例３】市販押出し発泡ポリスチレンの片面に、実
施例と同様な方法で製造した単位面積あたりの重量が２
８０ｇ／ｍ2 のアスファルト含浸ガラス繊維シートを市
販フェノール系接着剤で積層した。以上の方法により得
た断熱パネルの耐熱性および改質アスファルト防水シー
トとの接着強度を次に示す方法により調べた。結果を表
１に示す。Comparative Example 3 One side of commercially available extruded expanded polystyrene was weighed 2 per unit area, produced in the same manner as in the Example.
An asphalt-impregnated glass fiber sheet of 80 g / m 2 was laminated with a commercially available phenolic adhesive. The heat resistance of the heat insulating panel obtained by the above method and the adhesive strength with the modified asphalt waterproof sheet were examined by the following method. Table 1 shows the results.
【００１５】耐熱性；トーチ工法で用いるＬＰガスバー
ナーで断熱パネルのシート面を１０ｃｍ離れた位置から
約１０秒間あぶった。断熱パネルのフォームおよびシー
トの劣化状態を観察した。 接着強度；断熱パネルのシート面の上に、市販の改質ア
スファルト防水シートをＬＰガスバーナーで両者をあぶ
り接着させた。この試験体の中央部から１０×１０×２
ｃｍのサイズの供試体を切り出し、フォーム面と改質ア
スファルト防水シート面にエポキシ系の接着剤で鋼製引
っ張り治具を取付け、引っ張り強度を測定した。Heat resistance: The sheet surface of the heat insulating panel was blown for about 10 seconds with a LP gas burner used in the torch method from a position 10 cm away from the sheet surface. The deterioration state of the foam and sheet of the heat insulating panel was observed. Adhesive strength: A commercially available modified asphalt waterproof sheet was adhered to the heat-insulating panel sheet surface by LP gas burner. 10 × 10 × 2 from the center of this specimen
A test piece having a size of cm was cut out, and a steel pulling jig was attached to the foam surface and the modified asphalt waterproof sheet surface with an epoxy-based adhesive, and the tensile strength was measured.
【００１６】[0016]
【表１】 [Table 1]
【００１７】[0017]
【発明の効果】本発明の断熱パネルは、上記のとうりの
構成とすることにより優れた耐熱性を有し、屋根等のト
ーチ工法において、トーチバーナーにより直接防水シー
トを融着することが可能であり、施工性が大幅に向上す
る。また、本発明の断熱パネルは、改質アスファルト防
水シートとの接着力が優れ、長期にわたりズレ、剥離等
の問題を生じない。The heat insulating panel of the present invention has excellent heat resistance by adopting the above-mentioned rib structure, and can directly fuse a waterproof sheet with a torch burner in a torch method for a roof or the like. Therefore, the workability is greatly improved. In addition, the heat insulating panel of the present invention has excellent adhesive strength to the modified asphalt waterproof sheet, and does not cause problems such as displacement and peeling over a long period.
【図１】本発明のトーチ工法用断熱パネルの断面図。FIG. 1 is a sectional view of a heat insulation panel for a torch method according to the present invention.
【図２】本発明のトーチ工法用断熱パネルを用いた屋根
等の断熱防水の施工図。FIG. 2 is a construction diagram of insulation and waterproofing of a roof or the like using the insulation panel for a torch method of the present invention.
１ フェノールフォーム ２ アスファルト含浸ガラス繊維シート ３ 接着剤 ４ コンクリート ５ 改質アスファルト防水シート ６ トーチバナー DESCRIPTION OF SYMBOLS 1 Phenol foam 2 Asphalt impregnated glass fiber sheet 3 Adhesive 4 Concrete 5 Modified asphalt waterproof sheet 6 Torch banner
Claims (2)
ルフォームのすくなくとも片面に、軟化点が５０℃以上
のアスファルトを含浸させたアスファルト含浸ガラス繊
維シート（厚さ０．１ｍｍ〜２ｍｍ、坪量４０ｇ/ｍ 2 〜
２０００ｇ/ｍ 2 、該シート中のガラス繊維の重量２０ｇ
/ｍ 2 〜２００ｇ/ｍ 2 ）が積層されていることを特徴とす
るトーチ工法用断熱パネル。1. A phenol foam having a thickness of 10 to 100 mm having a softening point of at least 50 ° C. on at least one side.
Asphalt-impregnated glass fiber sheet impregnated with asphalt (thickness 0.1 mm to 2 mm, basis weight 40 g / m 2 to
2000 g / m 2 , weight of glass fiber in the sheet 20 g
/ m 2 -200 g / m 2 ) is laminated.
上に接着し、断熱パネルのアスファルト含浸ガラス繊維
シート上に、防水シートをトーチバーナーにより直接融
着させることを特徴とする防水トーチ工法。 2. The waterproofing torch method according to claim 1, wherein the insulating panel according to claim 1 is adhered to a roof member, and the waterproofing sheet is directly fused to an asphalt-impregnated glass fiber sheet of the insulating panel by a torch burner. .