JPH0882020A - Manufacture of heat insulating panel - Google Patents
Manufacture of heat insulating panelInfo
- Publication number
- JPH0882020A JPH0882020A JP6241831A JP24183194A JPH0882020A JP H0882020 A JPH0882020 A JP H0882020A JP 6241831 A JP6241831 A JP 6241831A JP 24183194 A JP24183194 A JP 24183194A JP H0882020 A JPH0882020 A JP H0882020A
- Authority
- JP
- Japan
- Prior art keywords
- phenol resin
- heat insulating
- insulating panel
- reinforcing structure
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、高強度で、防火、耐火
性に優れていて、特に内外壁、間仕切り、ドア、天井用
等に好適な断熱パネルの製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a heat-insulating panel which has high strength, excellent fire resistance and fire resistance, and is particularly suitable for inner and outer walls, partitions, doors, ceilings and the like.
【０００２】[0002]
【従来の技術】内外壁、間仕切り、ドア、天井等に使用
する断熱パネルとしては、従来、ウレタンフォームを芯
材として、それに表皮材を貼付したパネルが主に使用さ
れている。しかしながら、ウレタンフォームは、断熱性
に優れる反面、可燃性であるため、これを建築物等に使
用した場合には、火災防止等のために消防法によって建
築物の敷地面積や建設地域が規制される場合がある。2. Description of the Related Art As a heat insulating panel used for inner and outer walls, partitions, doors, ceilings, etc., conventionally, a panel having urethane foam as a core material and a skin material attached thereto has been mainly used. However, while urethane foam has excellent heat insulation properties, it is flammable, so when it is used in buildings, etc., the site area and construction area of buildings are regulated by the Fire Service Act to prevent fires. There is a case.
【０００３】このため、上記規制を受ける場所では、防
火、耐火性を考慮して、ウレタンフォームに難燃剤を添
加した断熱パネル、押出し発泡ポリスチレンボードの両
面に石こうボードを貼付した断熱パネル、又はイソシア
ヌレートフォームを芯材にして表皮材を貼付した断熱パ
ネル等が使用されているが、防火、耐火性がまだ十分で
はなく、さまざまな消火設備の設置が必要とされてい
る。For this reason, in places subject to the above regulations, in consideration of fire protection and fire resistance, a heat insulating panel made by adding a flame retardant to urethane foam, a heat insulating panel made by sticking a plaster board on both sides of an extruded expanded polystyrene board, or isocyanate. Insulation panels and the like with nureto foam as a core material and affixed with a skin material are used, but fire protection and fire resistance are not yet sufficient, and it is necessary to install various fire extinguishing equipment.
【０００４】また、有機系フォームとして最も不燃性が
高いものにフェノール樹脂フォームが知られているが、
単独では芯材としての強度が劣り、表皮材との接着性も
低いため、フェノール樹脂フォーム単独では断熱パネル
の芯材としては利用できないという欠点を有している。
この欠点を解消する手段として、特開平３−１０９１４
５号、特開平４−３１９４２８号、及び特開平５−２２
２７８４号には、断熱パネル等の芯材として、フェノー
ル樹脂フォームとハニカム体との複合体を用いたものが
開示されている。Phenolic resin foam is known as the most incombustible organic foam.
The phenol resin foam alone has a drawback that it cannot be used as a core material of a heat insulating panel because it has poor strength as a core material and low adhesiveness to a skin material.
As means for solving this drawback, Japanese Patent Laid-Open No. 3-109914
5, JP-A-4-319428, and JP-A-5-22.
No. 2784 discloses a core material of a heat insulating panel or the like, which uses a composite of a phenol resin foam and a honeycomb body.
【０００５】これらのうち、特開平３−１０９１４５
号、特開平４−３１９４２８号には、ハニカム体の両面
に、ガラス繊維等のマット状繊維物に発泡性フェノール
樹脂を加熱融着させた複合物を積層し、加熱加圧するこ
とにより発泡成形した芯材が開示されている。Of these, JP-A-3-109145
In Japanese Patent Laid-Open No. 4-319428, on both surfaces of a honeycomb body, a composite material in which a foamable phenol resin is heat-fused to a mat-like fiber material such as glass fiber is laminated, and foam-molded by heating and pressing. A core material is disclosed.
【０００６】しかしながら、マット状繊維物に発泡性フ
ェノール樹脂を加熱融着させた後、冷却固化させたもの
は、非常にもろいという欠点を有している。そのため、
マット状繊維状物と発泡性フェノール樹脂との複合物を
ハニカム体の両面に配置する際に、上記複合物をフラッ
トな状態に保っておかないと、発泡性フェノール樹脂が
脱落しやすく、ハニカム体のコア内に発泡したフェノー
ル樹脂が均一に充填されず、したがって、断熱性にムラ
を生じるという問題を有していた。However, the one obtained by heating and melting the foamable phenolic resin on the mat-like fiber material and then cooling and solidifying it has a drawback that it is very brittle. for that reason,
When arranging the composite of the mat-like fibrous material and the expandable phenol resin on both surfaces of the honeycomb body, if the composite is not kept in a flat state, the expandable phenol resin tends to fall off, and the honeycomb body There was a problem that the foamed phenolic resin was not uniformly filled in the core, and therefore the heat insulation was uneven.
【０００７】また、上記欠点のため、マット状繊維状物
と発泡性フェノール樹脂との複合物を、フラットな板状
の状態で、折り曲げないように注意して取り扱わなけれ
ばならず、長いままロール状にして保管することができ
ないという問題があった。この場合、長いままロール状
にして保管できるなら、必要に応じて所望の長さに切り
出すことができるので、フラットな板状の状態で保管す
る場合より、歩留が向上する。Due to the above-mentioned drawbacks, the composite of the mat-like fibrous material and the expandable phenol resin must be handled with care not to bend it in a flat plate-like state, and it should be rolled as it is for a long time. There was a problem that it could not be stored in the form. In this case, if it can be stored in a roll form while it is long, it can be cut out to a desired length as needed, so that the yield is improved as compared with the case of storage in a flat plate state.
【０００８】更に、上記の断熱パネルの芯材の、フェノ
ール樹脂フォームとマット状繊維物の剥離強度は、マッ
ト状繊維物のアンカー効果により多少改善されるもの
の、ウレタンフォームの剥離強度と比較すると半分程度
にすぎず、十分とはいえない。なお、一般建築物にパネ
ルだけで自立させて用いられる耐力外壁用パネルの剥離
強度は、少なくともウレタンフォーム芯材並みの２kg/c
m2以上が要求される。Further, the peeling strength of the phenol resin foam and the mat-like fiber material of the core material of the heat insulating panel is slightly improved by the anchoring effect of the mat-like fiber material, but is half that of the urethane foam. It's just a degree, not enough. In addition, the peeling strength of the outer wall panel, which is used by making the panel stand alone in a general building, has a peel strength of at least 2 kg / c, which is equivalent to the urethane foam core
m 2 or more is required.
【０００９】一方、特開平５−２２２７８４号公報に
は、ハニカム体にフェノール樹脂フォームを充填してな
る芯材の片面又は両面に、鉱物質繊維ボードを積層し、
更にその外側を表皮材で被覆してなる断熱パネルが開示
されている。この断熱パネルは、芯材の外側に高密度の
鉱物質繊維ボードを配置し、断熱パネル全体の厚さに対
する、鉱物質繊維ボードの厚さと表皮材の厚さとの合計
が占める割合を高くしているため、防火、耐火性に優れ
ている。On the other hand, in Japanese Unexamined Patent Publication (Kokai) No. 5-222784, a mineral fiber board is laminated on one or both sides of a core material obtained by filling a honeycomb body with phenol resin foam,
Further, a heat insulating panel having the outer surface thereof covered with a skin material is disclosed. In this heat insulation panel, a high-density mineral fiber board is arranged on the outside of the core material, and the total of the thickness of the mineral fiber board and the skin material accounts for a large proportion of the total thickness of the heat insulation panel. Therefore, it has excellent fire protection and fire resistance.
【００１０】しかしながら、この場合もフェノール樹脂
フォームと鉱物質繊維ボードとの剥離強度が、不十分で
あるという問題を有していた。However, also in this case, there is a problem that the peel strength between the phenol resin foam and the mineral fiber board is insufficient.
【００１１】[0011]
【発明が解決しようとする課題】本発明は、従来技術が
有する前述の問題点を解消するためになされたものであ
り、その目的は、成形の際の作業性に優れ、均一な断熱
性を有し、高強度で、防火、耐火性に優れるとともに、
パネルにした際の引張剥離強度に優れた断熱パネルの製
造方法を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems of the prior art, and its object is to provide excellent workability in molding and uniform heat insulation. It has high strength, excellent fire resistance and fire resistance,
An object of the present invention is to provide a method for manufacturing a heat insulating panel having excellent tensile peel strength when formed into a panel.
【００１２】[0012]
【課題を解決するための手段】上記目的を達成するた
め、本発明の断熱パネルの製造方法の一つは、補強用構
造体の両面に、発泡性フェノール樹脂と無機質繊維シー
トとの複合物を積層し、更にその両外側に、ホットメル
トフィルム又は熱硬化性樹脂の層を介して表皮材を積層
した後、加熱加圧して前記発泡性フェノール樹脂を発泡
硬化させる断熱パネルの製造方法であって、前記発泡性
フェノール樹脂と無機質繊維シートとの複合物の、前記
補強用構造体に接する面を熱可塑性物質で被覆しておく
ことを特徴とする。To achieve the above object, one of the methods for producing a heat insulating panel of the present invention is to provide a composite of an expandable phenol resin and an inorganic fiber sheet on both sides of a reinforcing structure. A method for producing a heat insulating panel, comprising laminating and further laminating a skin material on both outer sides thereof via a layer of a hot melt film or a thermosetting resin, followed by heat and pressure to foam and cure the foamable phenol resin. The surface of the composite of the expandable phenolic resin and the inorganic fiber sheet, which is in contact with the reinforcing structure, is coated with a thermoplastic material.
【００１３】また、本発明の断熱パネルの製造方法のも
う一つは、補強用構造体の両面に、発泡性フェノール樹
脂と無機質繊維シートとの複合物を積層した後、加熱加
圧して前記発泡性フェノール樹脂を発泡硬化させて芯材
とし、この芯材の両面に表皮材を貼付する断熱パネルの
製造方法であって、前記発泡性フェノール樹脂と無機質
繊維シートとの複合物の、前記補強用構造体に接する面
を熱可塑性物質で被覆しておくことを特徴とする。Another method of producing the heat insulating panel of the present invention is to laminate the composite of the expandable phenolic resin and the inorganic fiber sheet on both sides of the reinforcing structure, and then heat and pressurize the foam. A method for producing a heat insulating panel, comprising foaming and curing a phenolic phenolic resin to form a core material, and applying a skin material to both surfaces of the core material, wherein the composite of the foamable phenolic resin and an inorganic fiber sheet is used for the reinforcement. It is characterized in that the surface in contact with the structure is coated with a thermoplastic material.
【００１４】以下、本発明について好ましい態様を挙げ
て更に詳細に説明する。本発明において、補強用構造体
としては、例えば、ハニカム体、波形構造体、図３に示
されるような卵パック状の多数の凹部３２と凸部３３と
を有する構造体３１等が好ましく用いられる。発泡性フ
ェノール樹脂が両面から発泡したとき、それぞれの面か
ら発泡したフェノール樹脂フォームが、補強用構造体の
内部の少なくとも半分に至って、内部に完全に充填され
るような構造体を用いるのが好ましく、特にハニカム体
を用いるのが好ましい。The present invention will be described in more detail below with reference to preferred embodiments. In the present invention, as the reinforcing structure, for example, a honeycomb body, a corrugated structure, a structure 31 having a large number of egg pack-shaped concave portions 32 and convex portions 33 as shown in FIG. 3, and the like are preferably used. . When the expandable phenolic resin is foamed from both sides, it is preferable to use a structure in which the phenolic resin foam foamed from each surface reaches at least half of the inside of the reinforcing structure and is completely filled inside. It is particularly preferable to use a honeycomb body.
【００１５】上記ハニカム体としては、特に限定され
ず、公知のものを使用することができる。ハニカム体の
セル形状の例としては、ハニカムコア、ロールコア、コ
ルゲートコア等を挙げることができ、材質の例として
は、クラフト紙、セミ中芯紙等のペーパーハニカム、ア
ルミニウム等の金属ハニカム等を挙げることができる。
しかし、断熱パネルの断熱性を低下させないため、熱伝
導率が小さいペーパーハニカムが好ましい。また、ペー
パーハニカムの場合には、難燃性等を向上させる目的
で、フェノール樹脂、水酸化アルミニウム等を含浸させ
てあってもよい。The honeycomb body is not particularly limited, and known ones can be used. Examples of the cell shape of the honeycomb body include a honeycomb core, a roll core, a corrugated core, and the like, and examples of the material include a paper honeycomb such as kraft paper and semi-core paper, and a metal honeycomb such as aluminum. be able to.
However, a paper honeycomb having a small thermal conductivity is preferable because it does not deteriorate the heat insulating property of the heat insulating panel. Further, in the case of a paper honeycomb, it may be impregnated with a phenol resin, aluminum hydroxide or the like for the purpose of improving flame retardancy and the like.
【００１６】本発明におけるフェノール樹脂としては、
従来使用されているフェノール樹脂を使用することがで
きるが、硬化剤による表皮材の腐食が発生しないノボラ
ック型のフェノール樹脂を使用することが好ましい。こ
のフェノール樹脂に発泡剤を添加混合することで、発泡
性フェノール樹脂を得ることができる。発泡剤として
は、加熱によって熱分解してガスを発生する無機系及び
有機系発泡剤が使用され、特にジニトロソペンタメチレ
ンテトラミン等の有機系発泡剤が好ましく使用される。The phenol resin in the present invention includes
Although a conventionally used phenol resin can be used, it is preferable to use a novolac type phenol resin which does not cause corrosion of the skin material by the curing agent. A foaming phenol resin can be obtained by adding and mixing a foaming agent to this phenol resin. As the foaming agent, inorganic and organic foaming agents that thermally decompose to generate gas are used, and particularly, an organic foaming agent such as dinitrosopentamethylenetetramine is preferably used.
【００１７】上記発泡性フェノール樹脂には、発泡硬化
後の不燃性を向上させるために、フェノール樹脂に対し
て１〜70重量％、望ましくは10〜60重量％の難燃剤を添
加してもよい。上記添加量が１重量％未満では難燃剤の
効果が十分でなく、添加量が70重量％を超える場合には
発泡性フェノール樹脂の発泡を大きく阻害し、断熱性能
を低下させ、断熱パネルの重量の大幅な増加を招くので
好ましくない。難燃剤としては、ハロゲン系難燃剤、り
ん系難燃剤、三酸化アンチモン、又は水酸化アルミニウ
ムや水酸化マグネシウム等の無機水酸化物を使用するこ
とができるが、難燃剤がその分解脱水による吸熱効果を
有するという点で無機水酸化物を使用することが好まし
い。To the foamable phenol resin, a flame retardant may be added in an amount of 1 to 70% by weight, preferably 10 to 60% by weight, based on the phenol resin, in order to improve the incombustibility after foaming and curing. . If the addition amount is less than 1% by weight, the effect of the flame retardant is not sufficient, and if the addition amount exceeds 70% by weight, the foaming of the foamable phenol resin is greatly hindered, the heat insulation performance is lowered, and the weight of the heat insulation panel is reduced. Is not preferable because it causes a large increase in As the flame retardant, a halogen-based flame retardant, a phosphorus-based flame retardant, antimony trioxide, or an inorganic hydroxide such as aluminum hydroxide or magnesium hydroxide can be used, but the flame retardant has an endothermic effect due to its decomposition and dehydration. It is preferable to use an inorganic hydroxide in that it has
【００１８】本発明における無機質繊維シートとして
は、ガラス繊維、岩綿、アルミナ繊維等の織布、不織
布、紙、又は繊維を堆積させて樹脂バインダーによって
固着させたマット等を使用することができ、中でも、価
格や、発泡性フェノール樹脂が担持されやすいという点
で、ガラスチョップドストランドマットが好ましく使用
される。また、無機質繊維シートは、フェノール樹脂フ
ォームとの接着性を向上させるために表面処理を施して
あってもよい。As the inorganic fiber sheet in the present invention, woven cloth, non-woven cloth, paper such as glass fiber, rock wool, alumina fiber, or a mat in which fibers are deposited and fixed by a resin binder can be used. Among them, the glass chopped strand mat is preferably used because of its price and the ease with which the expandable phenol resin is supported. Further, the inorganic fiber sheet may be surface-treated in order to improve the adhesiveness with the phenolic resin foam.
【００１９】更に、無機質繊維シートは、厚さが0.1 〜
５mmであることが好ましく、特に0.2 〜３mmであること
が好ましい。厚さが0.1 mm未満の場合は、シートの面方
向に沿った通気性が低く、表皮材に塗布した接着剤等が
シート全体に浸透して、上記通気性がより低下するの
で、発泡性フェノール樹脂の発泡時に発生する発泡剤の
余剰ガス及びハニカム体のセル内の空気がパネル外へ抜
けにくくなり、ハニカム体のセル内へフェノール樹脂フ
ォームが完全に充填されず空隙が残る。厚さが５mmより
大きい場合には、無機質繊維シート内の、フェノール樹
脂フォーム及び表皮材に塗布した接着剤等が浸透してい
ない層の厚さが大きくなり、この層からの層間剥離が問
題となる。また、無機質繊維シートが断熱層となり、一
体成形時に発泡性フェノール樹脂の加熱発泡の所要時間
が極端に長くなるので実用的ではない。Further, the inorganic fiber sheet has a thickness of 0.1 to
It is preferably 5 mm, particularly preferably 0.2 to 3 mm. If the thickness is less than 0.1 mm, the air permeability along the surface direction of the sheet is low, the adhesive applied to the skin material penetrates the entire sheet, and the air permeability is further reduced, so that the foamable phenol Excess gas of the foaming agent generated during foaming of the resin and air in the cells of the honeycomb body are less likely to escape to the outside of the panel, and the phenol resin foam is not completely filled in the cells of the honeycomb body, leaving voids. If the thickness is greater than 5 mm, the thickness of the layer in the inorganic fiber sheet where the adhesive applied to the phenolic resin foam and the skin material does not penetrate becomes large, and delamination from this layer poses a problem. Become. In addition, the inorganic fiber sheet serves as a heat insulating layer, and the time required for the foaming of the expandable phenolic resin by heating during the integral molding becomes extremely long, which is not practical.
【００２０】また、無機質繊維シートは、単位面積重量
が30〜1500g/m2であることが好ましい。単位面積重量が
30g/m2未満では発泡性フェノール樹脂が担持されにく
く、また複合物としたときの強度も低いので取扱性に劣
る。単位面積重量が1500g/m2より大きい場合には、通気
性が低くなる。The unit weight of the inorganic fiber sheet is preferably 30 to 1500 g / m 2 . Unit area weight is
If it is less than 30 g / m 2 , the expandable phenol resin is difficult to be supported, and the strength of the composite is low, resulting in poor handleability. If the unit area weight is more than 1500 g / m 2 , the air permeability will be low.
【００２１】本発明において熱可塑性物質としては、溶
融又は軟化する温度が150 ℃以下である熱可塑性物質を
用いるのが好ましく、フィルムにした際に強度が優れて
いることから、熱可塑性樹脂あるいは熱可塑性エラスト
マーを用いるのが好ましい。熱可塑性樹脂としては、例
えば、ポリオレフィン系、ポリアミド系、ポリエステル
系の樹脂等を用いるのが好ましい。また、熱可塑性エラ
ストマーとしては、例えば、合成ゴム系等のホットメル
トパウダー、ホットメルトフィルム等を用いるのが好ま
しい。なお、これらはいずれも市販もされている。As the thermoplastic material in the present invention, it is preferable to use a thermoplastic material having a melting or softening temperature of 150 ° C. or lower. Since it has excellent strength when formed into a film, it is preferable to use a thermoplastic resin or a thermoplastic resin. It is preferable to use a plastic elastomer. As the thermoplastic resin, it is preferable to use, for example, a polyolefin-based resin, a polyamide-based resin, a polyester-based resin, or the like. As the thermoplastic elastomer, it is preferable to use, for example, hot melt powder or hot melt film of synthetic rubber or the like. All of these are commercially available.
【００２２】また、熱可塑性物質は、無機質繊維シート
に発泡性フェノール樹脂を付着させた面であって、発泡
性フェノール樹脂と無機質繊維シートとの複合物の、補
強用構造体に接する面に、フィルム状に被覆される。そ
の厚さは、0.02〜１mmが好ましく、0.03〜0.5 mmがより
好ましい。こうして熱可塑性物質で被覆することによ
り、発泡性フェノール樹脂の脱落が防止されるととも
に、発泡性フェノール樹脂と無機質繊維シートとの複合
物と、補強用構造体との接着性が向上する。なお、上記
熱可塑性物質の厚さが、0.02mmより薄いと、これらの効
果が十分に発揮されず、１mmより厚いと、成形時に発泡
性フェノール樹脂の発泡を阻害するとともに、補強用構
造体によって構成されている空間の空気が逃げにくくな
り、そのために防火、耐火性が低くなる。The thermoplastic material is a surface of the inorganic fiber sheet to which the expandable phenol resin is adhered, and a surface of the composite of the expandable phenol resin and the inorganic fiber sheet, which is in contact with the reinforcing structure, It is covered with a film. The thickness is preferably 0.02 to 1 mm, more preferably 0.03 to 0.5 mm. By coating with the thermoplastic material in this way, the foamable phenol resin is prevented from falling off, and the adhesiveness between the composite of the foamable phenol resin and the inorganic fiber sheet and the reinforcing structure is improved. If the thickness of the thermoplastic material is less than 0.02 mm, these effects are not sufficiently exerted, and if it is more than 1 mm, the foaming of the expandable phenol resin is hindered during molding, and the reinforcing structure causes The air in the constructed space is less likely to escape, which reduces fire protection and fire resistance.
【００２３】本発明の断熱パネルでは、表皮材が断熱パ
ネルの表裏両面ともに金属板であるか、あるいは一方の
面が金属板でもう一方の面が無機質ボードであること
が、防火、耐火性を向上させ、更に、透湿による結露や
芯材の劣化及び断熱性能の低下を防止するために好まし
い。表皮材として用いる金属板としては、鋼板、アルミ
ニウム板等を使用することができ、金属板は、外観向
上、腐食防止等のために、塗装又は表面処理を施してあ
ってもよい。また、無機質ボードとしては、石こうボー
ド、石綿セメント板、けい酸カルシウム板、スラグ石こ
う板、ＡＬＣ板等を使用することができる。In the heat insulation panel of the present invention, the skin material is a metal plate on both the front and back sides of the heat insulation panel, or one side is a metal plate and the other side is an inorganic board, which is fireproof and fireproof. It is preferable in order to improve and further prevent dew condensation due to moisture permeation, deterioration of the core material and deterioration of the heat insulating performance. As the metal plate used as the skin material, a steel plate, an aluminum plate or the like can be used, and the metal plate may be coated or surface-treated in order to improve the appearance and prevent corrosion. As the inorganic board, gypsum board, asbestos cement board, calcium silicate board, slag gypsum board, ALC board and the like can be used.
【００２４】また、本発明において、表皮材の接着手段
としてのホットメルトフィルムとしては、軟化点が50〜
200 ℃の接着性を有するホットメルトフィルムを使用す
ることが好ましい。軟化点が50℃より低い場合には、断
熱パネルの保管、輸送時に表皮材が剥離するおそれがあ
り、軟化点が200 ℃より高い場合には、断熱パネルの一
体成形が困難となる。このようなホットメルトフィルム
としては、例えば、市販のポリオレフィン系、ポリアミ
ド系、又はポリエステル系等のホットメルトフィルムが
挙げられる。In the present invention, the hot melt film as a means for adhering the skin material has a softening point of 50 to 50.
It is preferable to use a hot melt film having an adhesive property of 200 ° C. If the softening point is lower than 50 ° C, the skin material may peel off during storage and transportation of the heat insulating panel, and if the softening point is higher than 200 ° C, it becomes difficult to integrally form the heat insulating panel. Examples of such hot melt film include commercially available polyolefin-based, polyamide-based, or polyester-based hot-melt films.
【００２５】また、表皮材の接着手段として表皮材に塗
布する熱硬化性樹脂としては、エポキシ樹脂、ウレタン
樹脂等の接着性を有する樹脂が好ましく使用される。こ
のうち、接着力及び耐久性の面から、特にエポキシ樹脂
に硬化剤を添加した組成物が好ましい。As the thermosetting resin applied to the skin material as a means for adhering the skin material, an adhesive resin such as epoxy resin or urethane resin is preferably used. Among these, from the viewpoint of adhesive strength and durability, a composition obtained by adding a curing agent to an epoxy resin is particularly preferable.
【００２６】本発明の断熱パネルの製造方法において
は、まず、無機質繊維シートに発泡性フェノール樹脂を
加熱融着させ、更に補強用構造体に接する面を熱可塑性
物質で被覆した複合物を製造する。この複合物の製造方
法の一つとしては、無機質繊維シート上に粉体の発泡性
フェノール樹脂を散布し、その上に、同じく粉体の熱可
塑性物質を散布した後、それぞれの樹脂が溶融する温度
以上で、かつ、発泡性フェノール樹脂が発泡硬化する温
度以下に加熱して、無機質繊維シートへ発泡性フェノー
ル樹脂を融着させるとともに、熱可塑性物質を溶融させ
てフィルム状とする方法がある。また、他の製造方法と
して、無機質繊維シート上に粉体の発泡性フェノール樹
脂を散布し、その上に、予めフィルム状とした熱可塑性
物質を載置し、それぞれの樹脂が溶融する温度以上で、
かつ、発泡性フェノール樹脂が発泡硬化する温度以下に
加熱して、これらを一体化させる方法もある。In the method for producing a heat insulating panel of the present invention, first, a foamable phenol resin is heat-fused to an inorganic fiber sheet, and a surface of the inorganic fiber sheet in contact with the reinforcing structure is coated with a thermoplastic material to produce a composite. . One of the methods for producing this composite is to spray a powdery expandable phenolic resin on an inorganic fiber sheet, and then spray a powdery thermoplastic material on it, and then melt each resin. There is a method in which the foamable phenol resin is heated to a temperature not lower than the temperature at which the foamable phenol resin is foamed and hardened to fuse the foamable phenol resin to the inorganic fiber sheet and to melt the thermoplastic substance to form a film. Further, as another manufacturing method, a powdery expandable phenolic resin is sprinkled on an inorganic fiber sheet, on which a film-shaped thermoplastic substance is placed, and at a temperature at which each resin melts or above. ,
In addition, there is also a method in which these are integrated by heating them to a temperature at which the expandable phenol resin is foamed and cured.
【００２７】本発明の断熱パネルの製造方法の一つは、
次のような一体成形法によるものである。すなわち、図
２に示すように、補強用構造体１の両面に、補強用構造
体１に接する面が熱可塑性物質４で被覆された、発泡性
フェノール樹脂２と無機質繊維シート３との複合物５を
積層し、更にその両外側に表皮材６を、ホットメルトフ
ィルムを配した面、あるいは熱硬化性樹脂を塗布した面
が無機質繊維シート３の方へ向くように積層する。One of the methods for manufacturing the heat insulating panel of the present invention is as follows:
It is based on the following integral molding method. That is, as shown in FIG. 2, a composite of a foamable phenolic resin 2 and an inorganic fiber sheet 3 in which the surfaces in contact with the reinforcing structure 1 are coated with the thermoplastic material 4 on both sides of the reinforcing structure 1. 5 is laminated, and the skin material 6 is laminated on both outer sides so that the surface on which the hot melt film is arranged or the surface on which the thermosetting resin is applied faces the inorganic fiber sheet 3.
【００２８】続いて、この積層体７を、上型８及び下型
９を有するプレス装置にセットし、加熱加圧して発泡性
フェノール樹脂２を発泡硬化させ、上記各層を一体成形
する方法によって断熱パネルを得ることができる。スペ
ーサー１０はプレス装置の上型８と下型９との間隔を、
目的とする断熱パネルの厚さに合わせるために使用され
る。また、複数の積層体７と積層体７との間に面状ヒー
ターを挿入することによって、複数の断熱パネルの多段
プレス成形を行うことも可能である。Subsequently, the laminated body 7 is set in a pressing device having an upper mold 8 and a lower mold 9, heated and pressed to foam and cure the foamable phenol resin 2, and the layers are integrally heat-insulated by a method. You can get a panel. The spacer 10 keeps the space between the upper die 8 and the lower die 9 of the press device,
Used to match the desired thickness of the insulation panel. It is also possible to perform multi-stage press molding of a plurality of heat insulation panels by inserting a sheet heater between the plurality of laminates 7 and the laminate 7.
【００２９】本発明において、断熱パネルの一体成形
は、一般に使用される加熱機能を備えたプレス装置で行
うことができる。一体成形時の温度は、150 〜200 ℃が
好ましい。上記温度が150 ℃未満であると、発泡性フェ
ノール樹脂の発泡が不十分となるか、又は、成形時間が
長くなって経済的ではない。また、上記温度が200 ℃を
超えると、フェノール樹脂が徐々にではあるが熱分解を
おこして断熱パネルの品質が低下するので好ましくな
い。In the present invention, the integral molding of the heat insulating panel can be carried out by a generally used press device having a heating function. The temperature at the time of integral molding is preferably 150 to 200 ° C. If the temperature is lower than 150 ° C, foaming of the expandable phenol resin will be insufficient, or the molding time will be long, which is not economical. On the other hand, if the temperature exceeds 200 ° C., the phenol resin will be gradually thermally decomposed and the quality of the heat insulating panel will be deteriorated, which is not preferable.
【００３０】また、本発明のもう一つの製造方法は、次
のようにして行うことができる。すなわち、補強用構造
体の両面に、この補強用構造体に接する面が熱可塑性物
質で被覆された、発泡性フェノール樹脂と無機質繊維シ
ートとの複合物を積層し、この積層物を加熱加圧して、
発泡性フェノール樹脂を発泡硬化させて芯材を形成す
る。その後、得られた芯材の両外側に、表皮材を貼付す
る。Further, another manufacturing method of the present invention can be carried out as follows. That is, on both sides of the reinforcing structure, the surface in contact with the reinforcing structure is coated with a thermoplastic material, a composite of a foamable phenolic resin and an inorganic fiber sheet is laminated, and the laminate is heated and pressed. hand,
A foamable phenol resin is foamed and cured to form a core material. After that, the skin material is attached to both outer sides of the obtained core material.
【００３１】加熱加圧して芯材を成形する際に用いる装
置、及び温度は、上記一体成形による製造方法に用いる
装置、及び温度と同様とするのが好ましい。It is preferable that the apparatus and temperature used when the core material is molded by heating and pressurizing are the same as the apparatus and temperature used in the manufacturing method by the integral molding.
【００３２】また、芯材に、表皮材を貼付する方法は、
エポキシ樹脂等の接着剤を表皮材に塗布した後、常温又
は加熱下で、芯材に接着する等の方法によるのが好まし
い。The method of attaching the skin material to the core material is as follows.
It is preferable to apply an adhesive such as an epoxy resin to the skin material and then bond it to the core material at room temperature or under heating.
【００３３】図１に示すように、こうして得られた断熱
パネル１１は、補強用構造体１の内部空間に、発泡した
フェノール樹脂フォームが充填されてなるコア１２と、
その外側両面に接合された無機質繊維シート３と、更に
その外側両面に接合された表皮材６とで構成されてい
る。なお、熱可塑性物質４は、補強用構造体１の両面か
ら発泡して充填されたフェノール樹脂フォームの間に挟
まれる。As shown in FIG. 1, the heat insulating panel 11 thus obtained has a core 12 in which the foamed phenol resin foam is filled in the internal space of the reinforcing structure 1.
It is composed of an inorganic fiber sheet 3 bonded to both outer surfaces thereof, and a skin material 6 further bonded to both outer surfaces thereof. The thermoplastic substance 4 is sandwiched between phenol resin foams that are foamed and filled from both sides of the reinforcing structure 1.
【００３４】本発明の製造方法により得られる断熱パネ
ルの厚さは、特に限定されないが、外壁材等の特に防
火、耐火性が必要とされる場合には、40mm以上が好まし
い。厚さが40mm未満の場合には、断熱性が不十分であ
り、また防火、耐火性も十分ではない。The thickness of the heat insulation panel obtained by the production method of the present invention is not particularly limited, but is preferably 40 mm or more when the outer wall material and the like require fire protection and fire resistance. If the thickness is less than 40 mm, the heat insulation is insufficient, and the fire resistance and fire resistance are not sufficient.
【００３５】[0035]
【作用】本発明の断熱性パネルの製造方法によれば、発
泡性フェノール樹脂と無機質繊維シートとの複合物の補
強用構造体に接する面を熱可塑性物質で被覆したので、
熱可塑性物質からなる被膜によって発泡性フェノール樹
脂の脱落が防止されることから、作業性が向上する。ま
た、発泡性フェノール樹脂の脱落が防止されるので、補
強用構造体の内部空間にフェノール樹脂フォームが均一
に充填され、パネルとした際に均一な断熱性が得られ
る。また、熱可塑性物質は、発泡性フェノール樹脂と無
機質繊維シートとの複合物と、補強用構造体との接着性
を向上させる役割も果たすので、得られたパネルは、剥
離強度に優れており、防火、耐火性が要求される一般建
築物の耐力外壁用パネルとしても使用可能となる。According to the method for producing a heat insulating panel of the present invention, since the surface of the composite of the expandable phenolic resin and the inorganic fiber sheet in contact with the reinforcing structure is coated with the thermoplastic material,
The workability is improved because the foaming phenol resin is prevented from falling off by the coating film made of a thermoplastic material. Further, since the foamable phenol resin is prevented from falling off, the phenol resin foam is uniformly filled in the internal space of the reinforcing structure, and uniform heat insulation is obtained when the panel is formed. Further, since the thermoplastic material also plays a role of improving the adhesiveness between the composite of the expandable phenolic resin and the inorganic fiber sheet, and the reinforcing structure, the obtained panel has excellent peel strength, It can also be used as a panel for bearing outer walls of general buildings that require fire protection and fire resistance.
【００３６】また、本発明の断熱パネルの製造方法にお
いて、無機質繊維シートは、発泡性フェノール樹脂を担
持するだけではなく、発泡性フェノール樹脂が発泡する
際に発生する発泡剤の余剰な分解ガス及び補強用構造体
によって構成されている空間内の空気を外へ逃がすため
の通路としての役割も果す。このように、余剰の分解ガ
ス等が断熱パネルの内部に残ることがないため、補強用
構造体によって構成されている空間内にフェノール樹脂
フォームが完全に充填し、断熱パネルの断熱性が向上
し、全面にわたって均一となる。In addition, in the method for producing a heat insulating panel of the present invention, the inorganic fiber sheet not only carries the expandable phenol resin, but also an excessive decomposition gas of the foaming agent generated when the expandable phenol resin foams and It also serves as a passage for letting air in the space formed by the reinforcing structure escape to the outside. In this way, excess decomposition gas, etc. does not remain inside the heat insulation panel, so the phenol resin foam is completely filled in the space formed by the reinforcing structure, improving the heat insulation of the heat insulation panel. , Becomes uniform over the entire surface.
【００３７】[0037]
実施例１ 無機質繊維シートとして、単位面積重量が300 g/m2のガ
ラスチョップドストランドマットを用い、このマット上
に、発泡性フェノール樹脂（ノボラック型）の粉体を単
位面積あたりの散布量が1000g/m2となるように散布し、
その上に、熱可塑性物質としての、融点85℃、厚さ0.05
mmのポリオレフィン系ホットメルトフィルムである「Ｅ
ＸＫ」（商品名、ダイアボンド工業社製）を２枚重ねて
乗せた後、95℃で加熱加圧して、発泡性フェノール樹脂
を溶融、融着させて、発泡性フェノール樹脂側をフィル
ム状の熱可塑性物質で被覆した発泡性フェノール樹脂と
無機質繊維シートとの複合物を得た。得られた複合物
は、折り曲げても発泡性フェノール樹脂の脱落がなく、
作業性に優れたものであった。Example 1 As the inorganic fiber sheet, a glass chopped strand mat having a unit area weight of 300 g / m 2 was used, and a powder of an expandable phenolic resin (novolak type) was applied on the mat at an amount of 1000 g per unit area. Scatter so that it is / m 2 ,
On top of that, as a thermoplastic, melting point 85 ℃, thickness 0.05
mm polyolefin hot melt film "E
XK "(trade name, manufactured by Diabond Industrial Co., Ltd.) is placed on top of it, and then heated and pressed at 95 ° C to melt and fuse the foamable phenol resin, and the foamable phenol resin side is formed into a film. A composite of expandable phenolic resin coated with a thermoplastic and an inorganic fiber sheet was obtained. The obtained composite does not drop the expandable phenolic resin even when bent,
The workability was excellent.
【００３８】次に、補強用構造体として、厚さ50mmのペ
ーパーハニカム（昭和飛行機工業製、品番25−Ｓ−10）
を用い、その両面に、上記の複合物を、熱可塑性物質で
被覆された面がペーパーハニカムの方へ向くように積層
し、更にその両外側に、２液性のエポキシ樹脂組成物
（日本チバガイギー社製、主剤ＸＮＲ3312と硬化剤ＸＮ
Ｈ3312を20：11の比で混合）を、単位面積あたりの塗布
量が300 g/m2となるように塗布した厚さ0.4 mmのカラー
鋼板を、エポキシ樹脂組成物の塗布面がガラスチョップ
ドストランドマットの方へ向くように積層して、一体成
形用の積層体を作成した。Next, as a reinforcing structure, a paper honeycomb having a thickness of 50 mm (manufactured by Showa Aircraft Industry Co., Ltd., product number 25-S-10)
On both sides thereof, the above-mentioned composite is laminated so that the surface coated with the thermoplastic material faces the paper honeycomb, and the two-component epoxy resin composition (Japan Ciba Geigy Manufactured by the main agent XNR3312 and hardener XN
H3312 mixed at a ratio of 20:11) was applied to a coated steel plate with a thickness of 0.4 mm so that the coating amount per unit area would be 300 g / m 2, and the surface coated with the epoxy resin composition was glass chopped strands. The laminate was laminated so as to face the mat, and a laminate for integral molding was prepared.
【００３９】次に、加熱機能を備えたプレス装置の温度
を170 ℃とし、上記積層体をセットし、その両脇に高さ
52mmのアルミニウム製のスペーサーを配置し、１０分間
加熱加圧してパネルを得た。Next, the temperature of a pressing device having a heating function is set to 170 ° C., the above-mentioned laminated body is set, and heights are set on both sides of the laminated body.
A 52 mm aluminum spacer was placed and heated and pressed for 10 minutes to obtain a panel.
【００４０】実施例２ 実施例１において、発泡性フェノール樹脂に、難燃剤と
しての水酸化アルミニウムを、樹脂に対して２：１で添
加し、それ以外は実施例１と同様にしてパネルを得た。Example 2 A panel was obtained in the same manner as in Example 1 except that aluminum hydroxide as a flame retardant was added to the foamable phenol resin at a ratio of 2: 1 with respect to the resin. It was
【００４１】実施例３ 実施例１において、熱可塑性物質を、融点95℃、厚さ0.
05mmのポリアミド系ホットメルトフィルムである「ＰＡ
Ｙ」（商品名、ダイアボンド社製）に替え、それ以外は
実施例１と同様にしてパネルを得た。Example 3 In Example 1, the thermoplastic material was used, with a melting point of 95 ° C. and a thickness of 0.1.
05mm polyamide hot melt film "PA
Y ”(trade name, manufactured by Diabond Co.) was used, and a panel was obtained in the same manner as in Example 1 except for the above.
【００４２】比較例１ 実施例１において、複合物を製造する際に、熱可塑性物
質を用いず、それ以外は実施例１と同様にしてパネルを
得た。Comparative Example 1 A panel was obtained in the same manner as in Example 1 except that the thermoplastic material was not used in producing the composite in Example 1.
【００４３】このパネルは、成形時に、発泡性フェノー
ル樹脂の脱落があり、得られたパネルを分解したとこ
ろ、ハニカムのセル内の一部に、フェノール樹脂フォー
ムが完全に充填されずに空隙を有しているところがあっ
た。更に、熱伝導率を測定したところ、測定位置によっ
て0.033 〜0.040kcal/mh℃と大きなバラツキがあった。In this panel, the foamable phenolic resin dropped out during molding, and when the obtained panel was disassembled, some of the cells in the honeycomb were not completely filled with the phenolic resin foam and had voids. There was a place that was doing. Furthermore, when the thermal conductivity was measured, there was a large variation of 0.033 to 0.040 kcal / mh ° C. depending on the measurement position.
【００４４】比較例２ 表皮材として厚さ0.4 mmのカラー鋼板を使用し、２枚の
表皮材の間に、ウレタンフォームである「スリースーパ
ーウレタンフォームＳ−20」（商品名、東京エアゾル社
製）を注入し、発泡させて、全体の厚さが52mmのパネル
を得た。Comparative Example 2 A 0.4 mm thick colored steel plate was used as the skin material, and the urethane foam "Three Super Urethane Foam S-20" (trade name, manufactured by Tokyo Aerosol Co., Ltd.) was used between the two skin materials. ) Was injected and foamed to give a panel with an overall thickness of 52 mm.
【００４５】実験例 実施例１〜３及び比較例１、２で得たパネルについて、
熱伝導率測定、強度試験、表面試験、及び防火、耐火試
験を行った。なお、試験方法は表１に示す方法とした。
熱伝導率については、比較例１のみ測定場所によってバ
ラツキがあったのでその平均値を示した。その結果を表
２に示す。Experimental Examples Regarding the panels obtained in Examples 1 to 3 and Comparative Examples 1 and 2,
A thermal conductivity measurement, a strength test, a surface test, and a fireproof and fireproof test were performed. The test method was as shown in Table 1.
Regarding the thermal conductivity, only Comparative Example 1 had variations depending on the measurement location, and therefore the average value was shown. The results are shown in Table 2.
【００４６】[0046]
【表１】 [Table 1]
【００４７】[0047]
【表２】 表２中、＊は測定場所によりバラツキがあったことから平均値を示す。[Table 2] In Table 2, * indicates an average value because there was variation depending on the measurement location.
【００４８】表２の結果から、実施例１〜３はいずれも
高い断熱性と、防火、耐火性とを兼ね備え、パネルとし
ての圧縮強度、曲げ強度が高く、剥離強度も比較例２の
ウレタンフォームを芯材としたパネルと同等に高いこと
がわかる。From the results shown in Table 2, all of Examples 1 to 3 have high heat insulating properties, fire protection and fire resistance, high compressive strength and bending strength as a panel, and peel strength of Comparative Example 2. It can be seen that it is as high as the panel with the core material.
【００４９】これに対して、比較例１は測定場所によっ
て熱伝導率にバラツキがあり、したがって、断熱性の均
一性に劣り、剥離強度が低いことがわかる。また、比較
例２は、可燃性で、防火、耐火性が不合格であり、パネ
ルとしての曲げ強度に劣ることがわかる。On the other hand, in Comparative Example 1, the thermal conductivity varies depending on the measurement location, and therefore, the uniformity of heat insulation is poor and the peel strength is low. Further, Comparative Example 2 is flammable, fails in fire protection and fire resistance, and is inferior in bending strength as a panel.
【００５０】[0050]
【発明の効果】以上説明したように、本発明の断熱性パ
ネルの製造方法によれば、熱可塑性物質の被膜によっ
て、発泡性フェノール樹脂と無機質繊維シートとの複合
物から発泡性フェノール樹脂が脱落するのが防止される
ので、成形時の作業性が向上するとともに、複合物をロ
ール状にして保存し、必要に応じて所望の長さに切断し
て使用することもできるので、歩留が向上する。As described above, according to the method for producing a heat insulating panel of the present invention, the foamable phenol resin is removed from the composite of the foamable phenol resin and the inorganic fiber sheet by the coating of the thermoplastic material. Since it is prevented, the workability at the time of molding is improved, and the composite can be stored in a roll shape and can be cut into a desired length and used as necessary, so that the yield is improved. improves.
【００５１】また、発泡性フェノール樹脂の脱落が防止
されるので、補強用構造体の内部空間にフェノール樹脂
フォームが均一に充填され、パネルとした際に均一な断
熱性が得られる。更に、熱可塑性物質によって、パネル
とした際の剥離強度も向上するので、防火、耐火性が要
求される一般建築物の耐力外壁用パネルとしても使用可
能となる。Further, since the foamable phenol resin is prevented from falling off, the phenol resin foam is uniformly filled in the inner space of the reinforcing structure, and uniform heat insulation is obtained when the panel is formed. Further, since the thermoplastic material also improves the peel strength when formed into a panel, it can be used as a panel for a load bearing outer wall of a general building that requires fire protection and fire resistance.
【００５２】更にまた、無機質繊維シートによって、発
泡性フェノール樹脂が発泡する際に発生する発泡剤の余
剰な分解ガス及び補強用構造体の内部空間の空気が外へ
逃がされるため、これらのガスが断熱パネルの内部に残
ることがなく、補強用構造体の内部空間にフェノール樹
脂フォームが完全に充填されて、断熱パネルの断熱性が
向上し、全面にわたって均一となる。Furthermore, since the excessive decomposition gas of the foaming agent generated when the expandable phenol resin foams and the air in the internal space of the reinforcing structure are released to the outside by the inorganic fiber sheet, these gases are discharged. The phenol resin foam is completely filled in the inner space of the reinforcing structure without remaining inside the heat insulating panel, and the heat insulating property of the heat insulating panel is improved and becomes uniform over the entire surface.
【００５３】したがって、本発明の製造方法によれば、
高強度で、防火、耐火性に優れた断熱パネルを得ること
ができる。Therefore, according to the manufacturing method of the present invention,
It is possible to obtain a heat-insulating panel having high strength and excellent fire resistance and fire resistance.
【図１】本発明の断熱パネルの製造方法の一実施例によ
り製造される断熱パネルを示す断面図である。FIG. 1 is a cross-sectional view showing a heat insulating panel manufactured by an embodiment of the heat insulating panel manufacturing method of the present invention.
【図２】同実施例の一工程を示す側面図である。FIG. 2 is a side view showing one step of the same embodiment.
【図３】本発明の断熱パネルの製造方法に用いる補強用
構造体の一例である卵パック状構造体を示す部分斜視図
である。FIG. 3 is a partial perspective view showing an egg pack-shaped structure which is an example of a reinforcing structure used in the method for manufacturing a heat insulating panel of the present invention.
１ 補強用構造体 ２ 発泡性フェノール樹脂 ３ 無機質繊維シート ４ 熱可塑性物質 ５ 複合物 ６ 表皮材 ７ 積層体 ８ 上型 ９ 下型 １０ スペーサー １１ 断熱パネル １２ コア 1 Reinforcement Structure 2 Expandable Phenolic Resin 3 Inorganic Fiber Sheet 4 Thermoplastic Material 5 Composite 6 Skin Material 7 Laminated Body 8 Upper Mold 9 Lower Mold 10 Spacer 11 Insulation Panel 12 Core
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｅ０４Ｃ 2/36 Ｊ // Ｂ２９Ｋ 61:04 105:04 105:08 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display area E04C 2/36 J // B29K 61:04 105: 04 105: 08
Claims (5)
ル樹脂と無機質繊維シートとの複合物を積層し、更にそ
の両外側に、ホットメルトフィルム又は熱硬化性樹脂の
層を介して表皮材を積層した後、加熱加圧して前記発泡
性フェノール樹脂を発泡硬化させる断熱パネルの製造方
法であって、前記発泡性フェノール樹脂と無機質繊維シ
ートとの複合物の、前記補強用構造体に接する面を熱可
塑性物質で被覆しておくことを特徴とする断熱パネルの
製造方法。1. A skin material comprising a composite of a foamable phenol resin and an inorganic fiber sheet laminated on both sides of a reinforcing structure, and a hot melt film or a thermosetting resin layer on both outer sides thereof. A method of manufacturing a heat insulating panel in which the expandable phenol resin is foamed and hardened by heating and pressurizing, and a surface of the composite of the expandable phenol resin and the inorganic fiber sheet, which is in contact with the reinforcing structure. A method for producing a heat insulating panel, characterized in that the above is coated with a thermoplastic material.
ル樹脂と無機質繊維シートとの複合物を積層した後、加
熱加圧して前記発泡性フェノール樹脂を発泡硬化させて
芯材とし、この芯材の両面に表皮材を貼付する断熱パネ
ルの製造方法であって、前記発泡性フェノール樹脂と無
機質繊維シートとの複合物の、前記補強用構造体に接す
る面を熱可塑性物質で被覆しておくことを特徴とする断
熱パネルの製造方法。2. A core material obtained by laminating a composite of an expandable phenolic resin and an inorganic fiber sheet on both sides of a reinforcing structure and then heating and pressurizing the expandable phenolic resin to foam and cure it into a core material. A method for manufacturing a heat insulating panel in which a skin material is attached to both surfaces of a material, wherein a surface of the composite of the expandable phenolic resin and the inorganic fiber sheet, which is in contact with the reinforcing structure, is coated with a thermoplastic material. A method for manufacturing an insulating panel, which is characterized in that
ク型フェノール樹脂である請求項１又は２記載の断熱パ
ネルの製造方法。3. The method for producing a heat insulating panel according to claim 1, wherein the foamable phenol resin is a novolac type phenol resin.
又は軟化する熱可塑性樹脂あるいは熱可塑性エラストマ
ーである請求項１〜３のいずれか一つに記載の断熱パネ
ルの製造方法。4. The method for producing a heat insulating panel according to claim 1, wherein the thermoplastic substance is a thermoplastic resin or a thermoplastic elastomer that melts or softens at 150 ° C. or lower.
請求項１〜４のいずれか一つに記載の断熱パネルの製造
方法。5. The method for manufacturing a heat insulating panel according to claim 1, wherein the reinforcing structure is a honeycomb body.