JP2660143B2 - Carbon fiber and cement composite for cement reinforcement - Google Patents
Carbon fiber and cement composite for cement reinforcementInfo
- Publication number
- JP2660143B2 JP2660143B2 JP4318303A JP31830392A JP2660143B2 JP 2660143 B2 JP2660143 B2 JP 2660143B2 JP 4318303 A JP4318303 A JP 4318303A JP 31830392 A JP31830392 A JP 31830392A JP 2660143 B2 JP2660143 B2 JP 2660143B2
- Authority
- JP
- Japan
- Prior art keywords
- cement
- carbon fiber
- reinforcement
- fiber
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明はセメント補強用の炭素繊
維及びそれを用いたセメント複合体に関するものであ
る。さらに詳しくいえば、本発明は、セメントとの密着
性に優れ、かつダイレクトスプレーガンに対する工程通
過性がよく、しかも集束性が良好であって、特にダイレ
クトスプレー工法に適したセメント補強用の炭素繊維、
及びこのものを用いた曲げ強度の高いセメント複合体に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a carbon fiber for reinforcing cement and a cement composite using the same. More specifically, the present invention provides a carbon fiber for cement reinforcement that has excellent adhesion to cement, has good processability with a direct spray gun, and has good convergence, and is particularly suitable for the direct spray method. ,
And a cement composite having high flexural strength using the same.
【０００２】[0002]
【従来の技術】近年、炭素繊維は高強度及び高弾性率を
有し、かつ軽量であるなど、優れた特徴を有することか
ら、例えば航空機部品，自動車部品，スポーツ用具など
の種々の分野における素材、あるいは樹脂補強材やセメ
ント補強材などとして著しく需要が伸びている。2. Description of the Related Art In recent years, carbon fibers have excellent characteristics such as high strength, high elastic modulus and light weight. Therefore, carbon fibers are used in various fields such as aircraft parts, automobile parts and sports equipment. Demand for such materials as resin reinforcing materials and cement reinforcing materials is increasing remarkably.
【０００３】また、セメント類の水硬性粉体を用いた混
練物は、各種の建築材料や土木材料などに広く用いられ
ている。このような混練物を補強し、亀裂発生を防止す
るため、従来繊維材料を配合することが行われてきた。
しかしながら、補強繊維として石綿を用いることは発が
ん性の点から好ましくなく、また、ガラス繊維は耐アル
カリ性に劣るため、セメント中においてガラス繊維自体
の強度が劣化するという欠点を有している。そのため、
各種の有機繊維や耐アルカリガラス繊維などが強化材と
して使用されているが、有機繊維では耐火性の点で問題
があり、また、耐アルカリガラス繊維を用いてもセメン
トなどのアルカリ性環境下では、長期間使用すると強度
が低下するという問題が生じる。そこで、耐熱性，耐薬
品性に優れ、かつ高強度，高弾性率の炭素繊維が注目さ
れている。[0003] Also, kneaded materials using hydraulic powders of cements are widely used in various building materials and civil engineering materials. In order to reinforce such a kneaded material and prevent crack generation, a fiber material has conventionally been blended.
However, the use of asbestos as a reinforcing fiber is not preferable from the viewpoint of carcinogenicity, and has the disadvantage that the strength of the glass fiber itself is deteriorated in the cement because the glass fiber has poor alkali resistance. for that reason,
Various organic fibers and alkali-resistant glass fibers are used as reinforcing materials.However, organic fibers have a problem in terms of fire resistance.Also, even in the case of using alkali-resistant glass fibers in an alkaline environment such as cement, When used for a long time, there is a problem that the strength is reduced. Accordingly, attention has been paid to carbon fibers which are excellent in heat resistance and chemical resistance, and have high strength and high elastic modulus.
【０００４】しかしながら、炭素繊維をセメントに添加
混合した場合、石綿やガラス繊維に比べてセメントへの
付着性（あるいは密着性）が劣るため、補強材として充
分な効果が発揮されないという問題がある。したがっ
て、これまで炭素繊維のセメントに対する付着性を高
め、得られる炭素繊維強化セメント材の強度を高めるべ
く種々の工夫がなされてきた。例えばエポキシ樹脂など
の疎水性液体樹脂を含浸させた炭素繊維ストランドをセ
メント中に張設し、樹脂とセメントとを同時に硬化させ
る方法（特公昭５８−１９６２０号公報）、メチルセル
ロースなどの水溶性結合剤で相互に結着した炭素繊維を
セメント中に一方向あるいは交差する二方向に配向して
配する方法（特開昭５６−１２９６５７号公報）、アク
リルエマルジョンなどの水溶性合成樹脂エマルジョンを
含ませた炭素繊維シートを介してセメントスラリー層を
重ね合わせる方法（特開昭５８−２２３６５９号公
報）、ハチエック式抄造法で強化セメント材を製造する
際に繊維表面にポリアルキルアミノアクリレートなどの
ノニオン性、あるいはカチオン性高分子凝集剤を付着さ
せる方法（特開昭６０−８１０５２号公報）、炭素繊維
の表面にカチオン性ゴムラテックスを付着させたセメン
ト補強用繊維材（特開昭６２−１０８７５５号公報）な
どが提案されている。However, when carbon fibers are added to and mixed with cement, the adhesiveness (or adhesion) to cement is inferior to that of asbestos or glass fibers, so that there is a problem that a sufficient effect as a reinforcing material cannot be exhibited. Therefore, various devices have been devised to increase the adhesion of carbon fiber to cement and to increase the strength of the obtained carbon fiber reinforced cement material. For example, a method in which a carbon fiber strand impregnated with a hydrophobic liquid resin such as an epoxy resin is stretched in cement and the resin and the cement are simultaneously cured (Japanese Patent Publication No. 58-19620), a water-soluble binder such as methylcellulose. (Japanese Patent Application Laid-Open No. 56-129657) in which carbon fibers bonded to each other are oriented in one direction or two directions crossing each other in cement, and a water-soluble synthetic resin emulsion such as an acrylic emulsion is included. A method in which a cement slurry layer is overlapped via a carbon fiber sheet (Japanese Patent Application Laid-Open No. 58-223659), a nonionic property such as polyalkylaminoacrylate or the like on the fiber surface when a reinforced cement material is manufactured by the Hachiek-type papermaking method, A method of attaching a cationic polymer flocculant (JP-A-60-81052), a carbon fiber Surface cationic rubber latex the deposited cement reinforcing fiber material (JP 62-108755 JP) have been proposed.
【０００５】しかしながら、これらの従来技術は、使用
する炭素繊維の形態に限定があったり、施工方法に限定
があったり、対象セメント種が制限されたり、あるいは
セメントに対する付着性が充分でないなどの問題を有
し、必ずしも充分に満足しうるものではない。ところ
で、最近、各種繊維を強化材とするコンクリート複合体
の製造において、より長い繊維（２５〜３０ｍｍ以上）
を用いることができ、力学的特性を充分に発揮できるダ
イレクトスプレー法が注目され、ガラス繊維を用いて実
用化されている。また、繊維製造工程において、特殊な
集束剤を用いることにより集束性を高めたピッチ系炭素
繊維をダイレクトスプレー法に応用する提案（特開昭６
２−３０００８号公報）もなされているが、製造方法及
び炭素繊維の形態が限定されているため炭素繊維一般に
適用することは困難である。さらにこのダイレクトスプ
レー法を適用する場合、補強用炭素繊維は、セメントに
対する密着性が良好であるとともに、ダイレクトスプレ
ーガンに対する工程通過性に優れる、すなわち炭素繊維
と金属との摩擦性が低く、滑りやすいことが重要であ
る。[0005] However, these conventional techniques have problems such as a limitation in the form of the carbon fiber used, a limitation in the construction method, a limitation on the type of cement to be applied, and insufficient adhesion to the cement. Which is not always satisfactory. By the way, recently, in the production of a concrete composite using various fibers as a reinforcing material, longer fibers (25 to 30 mm or more) have been used.
The direct spray method, which can sufficiently exhibit mechanical properties, has attracted attention and has been put to practical use using glass fibers. Also, in a fiber manufacturing process, a proposal is made to apply a pitch-based carbon fiber having improved bunching properties by using a special sizing agent to a direct spray method (Japanese Patent Laid-Open No.
No. 2-30008), but it is difficult to apply to carbon fibers in general because the production method and the form of carbon fibers are limited. Furthermore, when this direct spray method is applied, the reinforcing carbon fiber has good adhesiveness to cement and has excellent processability to the direct spray gun, that is, low friction between the carbon fiber and the metal, and is slippery. This is very important.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、このような
事情のもとで、セメントとの密着性に優れ、かつダイレ
クトスプレーガンに対する工程通過性がよく、しかも集
束性が良好であって、特にダイレクトスプレー工法に適
したセメント補強用の炭素繊維、及びこのものを用いた
曲げ強度の高いセメント複合体を提供することを目的と
してなされたものである。SUMMARY OF THE INVENTION Under such circumstances, the present invention provides excellent adhesiveness to cement, good processability with a direct spray gun, and good convergence. In particular, it is an object of the present invention to provide a carbon fiber for cement reinforcement suitable for a direct spray method and a cement composite having high bending strength using the carbon fiber.
【０００７】[0007]
【課題を解決するための手段】本発明者らは、前記目的
を達成するために鋭意研究を重ねた結果、炭素繊維の表
面に、ポリオキシアルキレンビスフェノールエーテルか
らなるサイジング剤を塗布することにより、セメントと
の密着性に優れ、かつダイレクトスプレーガンに対する
工程通過性がよく、しかも集束性が良好なセメント補強
用の炭素繊維が得られること、そしてこの炭素繊維を特
定の長さかつ特定の割合で含有するセメント複合体は高
い曲げ弾性率を有することを見出した。本発明は、この
ような知見に基づいてなされたものである。すなわち、
本発明は、炭素繊維の表面に、ポリオキシアルキレンビ
スフェノールエーテルから成るサイジング剤を塗布した
ことを特徴とするセメント補強用炭素繊維を提供するも
のである。また本発明は、この炭素繊維を繊維長１０〜
５０ｍｍに切断し、セメントマトリックスに対して容積
混入率１〜５％の割合で含有させてなる曲げ強度３００
ｋｇｆ／ｃｍ2 以上のセメント複合体を提供するもので
ある。Means for Solving the Problems The present inventors have conducted intensive studies to achieve the above object, and as a result, by applying a sizing agent composed of polyoxyalkylene bisphenol ether to the surface of carbon fiber, Excellent cement adhesion, good processability with direct spray guns, and good convergence can be obtained carbon fiber for cement reinforcement, and this carbon fiber with a specific length and specific ratio It has been found that the contained cement composite has a high flexural modulus. The present invention has been made based on such findings. That is,
The present invention provides a carbon fiber for cement reinforcement, characterized in that a sizing agent composed of polyoxyalkylene bisphenol ether is applied to the surface of the carbon fiber. In addition, the present invention provides a carbon fiber having a fiber length of 10 to 10.
Bending strength 300 cut into 50 mm and contained at a rate of 1-5% by volume mixing ratio with cement matrix
It is intended to provide a cement composite of kgf / cm 2 or more.
【０００８】本発明において、炭素繊維としては、ピッ
チ系，ＰＡＮ系，レーヨン系等何れも使用可能であり、
公知の方法によって、紡糸，不融化（耐炎化），炭化，
黒鉛化された引張強度が１５０ｋｇｆ／ｍｍ2 以上で、
引張弾性率が１０×１０3 ｋｇｆ／ｍｍ2 以上のものが
好ましく使用出来る。またコストに比して弾性率の発現
しやすいメソフェーズピッチ系炭素繊維が特に好ましく
使用出来る。In the present invention, pitch-based, PAN-based and rayon-based carbon fibers can be used.
Spinning, infusibility (flame resistance), carbonization,
If the graphitized tensile strength is 150 kgf / mm 2 or more,
Those having a tensile modulus of 10 × 10 3 kgf / mm 2 or more can be preferably used. In addition, mesophase pitch-based carbon fibers, which easily exhibit an elastic modulus compared to the cost, can be particularly preferably used.
【０００９】本発明においては、上記炭素繊維の表面
に、サイジング剤を塗布するが、このサイジング剤は該
炭素繊維の表面に直接塗布してもよいし、所望により炭
素繊維の表面を公知の方法、例えば酸化剤による液相酸
化法、ヒートクリーニング法，気相酸化法，ウイスカラ
イジング法，電解酸化法などにより、処理したのち塗布
してもよい。該サイジング剤としては、ポリオキシアル
キレンビスフェノールエーテルが用いられる。このポリ
オキシアルキレンビスフェノールエーテルの代表例とし
ては一般式In the present invention, a sizing agent is applied to the surface of the carbon fiber. The sizing agent may be applied directly to the surface of the carbon fiber or, if desired, the surface of the carbon fiber may be coated by a known method. For example, it may be applied after being processed by a liquid phase oxidation method using an oxidant, a heat cleaning method, a gas phase oxidation method, a whiskering method, an electrolytic oxidation method, or the like. As the sizing agent, polyoxyalkylene bisphenol ether is used. As a typical example of the polyoxyalkylene bisphenol ether, a general formula
【００１０】[0010]
【化１】 Embedded image
【００１１】〔式中、ｍ及びｎはそれぞれ１〜２９の整
数であり、かつｍ＋ｎ＝３０である。〕で表わされるポ
リオキシエチレンビスフェノールエーテルを挙げること
ができる。このサイジング剤は一種用いてもよいし、二
種以上を組み合わせて用いてもよい。サイジング剤の塗
布方法については特に制限はなく、適当な溶剤に溶解し
た溶液又は水性媒体に乳化させたエマルジョンを調製
し、これに炭素繊維のストランドを接触若しくは浸漬さ
せたのち、従来公知の方法、例えば熱風乾燥，赤外線乾
燥，マイクロウエーブ乾燥などの手段により、脱溶媒し
て炭素繊維の表面をサイジング剤で被覆する。サイジン
グ剤の塗布量は炭素繊維に対して0.５〜１０重量％の範
囲にあるのが望ましい。この量が0.５重量％未満では本
発明の効果が充分に発揮されないし、１０重量％を超え
ると集束が過度に強固になりセメント中の分散度が劣
り、セメント複合体の物性が低下する傾向がみられる。
このようにして処理された炭素繊維束を構成するモノフ
ィラメント数は３０〜１2,０００本、好ましくは５０〜
6,０００本であるのが望ましい。このモノフィラメント
数が３０本未満のものは集束した繊維束を製造する際の
生産性に劣るし、１2,０００本を超えると一束状に集束
するのが困難となったり、セメント中での分散性が悪く
なったりする。このようにして得られたセメント補強用
の炭素繊維は、セメントとの密着性に優れ、かつ金属と
の摩擦性が低く、滑りやすいため、ダイレクトスプレー
ガンに対する工程通過性がよい上、集束性が良好であっ
て、特にダイレクトスプレー工法に適している。Wherein m and n are each an integer of 1 to 29, and m + n = 30. And a polyoxyethylene bisphenol ether represented by the following formula: One of these sizing agents may be used, or two or more of them may be used in combination. The method of applying the sizing agent is not particularly limited, and a solution dissolved in an appropriate solvent or an emulsion emulsified in an aqueous medium is prepared, and a carbon fiber strand is contacted or immersed in the emulsion. For example, the surface of the carbon fiber is coated with a sizing agent by removing the solvent by means such as hot-air drying, infrared drying, or microwave drying. The amount of the sizing agent applied is preferably in the range of 0.5 to 10% by weight based on the carbon fiber. When the amount is less than 0.5% by weight, the effect of the present invention is not sufficiently exerted. When the amount is more than 10% by weight, the convergence becomes excessively strong, the degree of dispersion in cement is poor, and the physical properties of the cement composite deteriorate. There is a tendency.
The number of monofilaments constituting the carbon fiber bundle thus treated is 30 to 12,000, and preferably 50 to 12,000.
Preferably, the number is 6,000. If the number of monofilaments is less than 30, the productivity in producing bundled fiber bundles is inferior. If it exceeds 12,000, it becomes difficult to bundle them into a bundle, or the dispersion in cement becomes difficult. Or worse. The carbon fiber for cement reinforcement obtained in this way has excellent adhesion to cement, low friction with metal, and is slippery. Good, especially suitable for direct spray method.
【００１２】本発明のセメント複合体は、上記のセメン
ト補強用の炭素繊維を、繊維長１０〜５０ｍｍに切断し
て、セメントマトリックスに対して容積混入率１〜５％
の割合で含有させたものである。該炭素繊維の切断の方
法については特に制限はなく、例えばギロチン式カッタ
ー，ロービングカッター、あるいはダイレクトスプレー
用のノズルガンなどを用いて切断することができる。該
繊維長が１０ｍｍ未満ではセメントとの混合時の分散性
はよいものの、充分な補強性能が得られず、また５０ｍ
ｍを超えると補強性は得られるものの、分散性が低下
し、均一な製品が得られにくい。また、炭素繊維の配合
量がセメントマトリックスに対し、容積混入率が１％未
満では補強効果が充分に発揮されないし、５％を超える
と混合しにくかったり、均一に分散できなかったりする
など、好ましくない事態を招来する。In the cement composite of the present invention, the carbon fiber for cement reinforcement is cut into a fiber length of 10 to 50 mm, and a volume mixing ratio of 1 to 5% with respect to a cement matrix.
In the ratio of There is no particular limitation on the method of cutting the carbon fiber, and the cutting can be performed using, for example, a guillotine-type cutter, a roving cutter, or a nozzle gun for direct spraying. If the fiber length is less than 10 mm, the dispersibility at the time of mixing with the cement is good, but sufficient reinforcing performance cannot be obtained, and
If it exceeds m, the reinforcing property can be obtained, but the dispersibility is reduced, and it is difficult to obtain a uniform product. Further, when the mixing ratio of the carbon fiber to the cement matrix is less than 1% by volume, the reinforcing effect is not sufficiently exhibited. When the mixing ratio is more than 5%, it is difficult to mix or cannot be uniformly dispersed. Invite no situation.
【００１３】セメントに上記炭素繊維を含有させてセメ
ント複合体を成形する方法については特に制限はなく、
従来慣用されている種々の方法、例えばダイレクトスプ
レー法やプレミックス法などを用いることができるが、
本発明においては特にダイレクトスプレー法が好適に用
いられる。このダイレクトスプレー法は、炭素繊維のロ
ービングを連続的に切断しながら圧縮空気ガンのノズル
より吹き出し、同時に他のノズルより吹き出すセメント
スラリーと一緒に吹きつけて成形する方法である。この
際用いられるセメントスラリーについては特に制限はな
く、従来炭素繊維強化セメント複合体の製造において慣
用されているものを使用することができる。該セメント
スラリーとしては、例えばポルトランドセメント，高炉
セメント，アルミナセメントなどの水硬性セメントに、
砂，ケイ砂，パーライト，ひる石，シラスバルーン，フ
ライアッシュ，超微粉シリカなどの骨材と、分散剤，減
水剤，消泡剤などの混和剤などを配合し、水を加えて混
合スラリー化したものを挙げることができる。スラリー
中の水／セメント比や、骨材／セメント比などの配合比
率は、使用する炭素繊維の形態や製造するセメント複合
体の成形性、施工性に応じて適宜選ばれる。このように
して得られた未硬化の成形体は、その後周知の水中養
生，気中養生，蒸気養生などの方法により養生し、固化
して所望の炭素繊維強化セメント複合体を製造すること
ができる。このようにして製造された本発明のセメント
複合体は、その曲げ強度が３００ｋｇｆ／ｃｍ2 以上と
高いものであって、建築・土木分野における種々の用途
に好適に用いられる。There is no particular limitation on the method of forming the cement composite by adding the carbon fiber to the cement.
Various methods conventionally used, for example, a direct spray method or a premix method can be used,
In the present invention, the direct spray method is particularly preferably used. The direct spray method is a method in which a roving of carbon fiber is blown out from a nozzle of a compressed air gun while being continuously cut, and simultaneously blown together with a cement slurry blown out from another nozzle to form. The cement slurry used at this time is not particularly limited, and those conventionally used in the production of carbon fiber reinforced cement composites can be used. Examples of the cement slurry include hydraulic cements such as Portland cement, blast furnace cement, and alumina cement.
Aggregates such as sand, silica sand, perlite, vermiculite, shirasu balloon, fly ash, and ultrafine silica are mixed with admixtures such as dispersants, water reducing agents, and defoamers, and water is added to form a mixed slurry. Can be mentioned. The mixing ratio such as the water / cement ratio or the aggregate / cement ratio in the slurry is appropriately selected according to the form of the carbon fiber used, the moldability of the cement composite to be produced, and the workability. The uncured molded body thus obtained is cured by a known method such as underwater curing, air curing, or steam curing, and then solidified to produce a desired carbon fiber reinforced cement composite. . The thus-produced cement composite of the present invention has a high flexural strength of 300 kgf / cm 2 or more and is suitably used for various applications in the fields of construction and civil engineering.
【００１４】[0014]
【実施例】次に実施例により本発明をさらに詳細に説明
する。 実施例１ 分子量１５００のビスフェノールＡエチレンオキシド付
加物の濃度が４ｗｔ％のエマルジョン水溶液を調製し、
この溶液中に、ストランド引張弾性率２１×１０3 ｋｇ
ｆ／ｍｍ2 及び引張強度２１６ｋｇｆ／ｍｍ2 を有する
２０００フィラメントからなるメソフェーズピッチ系炭
素繊維ストランドを浸漬したのち、乾燥して、サイジン
グ剤が1.０ｗｔ塗布されたセメント補強用の炭素繊維を
作成した。一方、セメント／砂重量比1.３３，水／セメ
ント重量比0.３５及びセメント混和剤／セメント重量比
0.００８のセメントモルタルを調製した。ダイレクトス
プレー法で用いられるスプレーガンにより、上記のセメ
ント補強用の炭素繊維束を長さ２５ｍｍに切断しなが
ら、上記セメントモルタルと同時に吹き付け、炭素繊維
強化セメントコンクリート成形体を得た。この際、炭素
繊維の供給量が３ｖｏｌ％になるように調整した。この
成形体を室温材齢７日で長さ２５０ｍｍ，幅５０ｍｍ，
厚さ１０ｍｍの曲げ試験用の供試体に切り出し、支点間
距離２００ｍｍで３点曲げ試験を行なった。その結果、
曲げ強度は３１５ｋｇｆ／ｃｍ2 であった。Next, the present invention will be described in more detail by way of examples. Example 1 An aqueous emulsion solution having a concentration of 4 wt% of bisphenol A ethylene oxide adduct having a molecular weight of 1500 was prepared.
In this solution, the strand tensile modulus is 21 × 10 3 kg.
After immersing a mesophase pitch-based carbon fiber strand consisting of 2000 filaments having a f / mm 2 and a tensile strength of 216 kgf / mm 2 , it was dried to prepare a carbon fiber for cement reinforcement coated with 1.0 wt. of a sizing agent. . Meanwhile, cement / sand weight ratio 1.33, water / cement weight ratio 0.35 and cement admixture / cement weight ratio
A 0.008 cement mortar was prepared. The carbon fiber bundle for cement reinforcement was cut to a length of 25 mm and sprayed simultaneously with the cement mortar by a spray gun used in a direct spray method to obtain a carbon fiber reinforced cement concrete molded body. At this time, the supply amount of the carbon fiber was adjusted to be 3 vol%. At room temperature, the molded body was 250 mm long, 50 mm wide, and 7 days old.
A 10-mm-thick bending test specimen was cut out and subjected to a three-point bending test at a distance between supporting points of 200 mm. as a result,
The bending strength was 315 kgf / cm 2 .
【００１５】比較例１ エピコート８２８及び硬化剤ＳＥ−１１を含有するエマ
ルジョンタイプのエポキシ系サイジング剤中に、実施例
１と同様のストランド引張弾性率２１×１０3ｋｇｆ／
ｍｍ2 及び引張強度２１６ｋｇｆ／ｍｍ2 を有する２０
００フィラメントからなるメソフェーズピッチ系炭素繊
維ストランドを浸漬したのち、乾燥して、エポキシ系サ
イジング剤が1.０ｗｔ％塗布されたセメント補強用の炭
素繊維を作成した。一方、セメント／砂重量比1.３３，
水／セメント重量比0.３５及びセメント混和剤／セメン
ト重量比0.００８のセメントモルタルを調製した。以
下、実施例１と同様にして実施した。その結果、室温材
齢７日のものの曲げ強度は、１８７ｋｇｆ／ｃｍ2 であ
った。COMPARATIVE EXAMPLE 1 In an emulsion type epoxy sizing agent containing Epicoat 828 and a curing agent SE-11, the same strand tensile modulus as in Example 1 was used, ie, 21 × 10 3 kgf /
20 having a tensile strength of 216 kgf / mm 2 and a tensile strength of 216 kgf / mm 2
A mesophase pitch-based carbon fiber strand composed of 00 filaments was immersed and dried to prepare a carbon fiber for cement reinforcement coated with 1.0% by weight of an epoxy sizing agent. On the other hand, cement / sand weight ratio 1.33,
A cement mortar having a water / cement weight ratio of 0.35 and a cement admixture / cement weight ratio of 0.008 was prepared. Hereinafter, it carried out similarly to Example 1. As a result, the flexural strength of the material having a room temperature material age of 7 days was 187 kgf / cm 2 .
【００１６】[0016]
【発明の効果】本発明のセメント補強用の炭素繊維は、
セメントとの密着性に優れ、かつダイレクトスプレーガ
ンに対する工程通過性がよく、しかも集束性が良好であ
って、特にダイレクトスプレー工法に適している。ま
た、このセメント補強用の炭素繊維を含有するセメント
複合体は曲げ強度が高く、建築・土木分野における種々
の用途に好適に用いられる。The carbon fiber for reinforcing cement of the present invention is:
It has excellent adhesion to cement, has good processability with a direct spray gun, and has good convergence, and is particularly suitable for the direct spray method. Further, the cement composite containing carbon fibers for cement reinforcement has a high flexural strength and is suitably used for various applications in the fields of construction and civil engineering.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 中嶋 秀行 茨城県鹿島郡神栖町東和田４番地 株式 会社ペトカ内 (72)発明者 大野 定俊 大阪府南河内郡美原町木材通３−１−８ 株式会社竹中工務店 技術研究所 大 阪支所内 (72)発明者 米澤 敏男 東京都江東区南砂２−５−14 株式会社 竹中工務店 技術研究所内 (72)発明者 位田 淳一 愛知県名古屋市天白区原５丁目2101番地 (72)発明者 岩田 正樹 愛知県名古屋市港区辰巳町29−11 (56)参考文献 特開 昭63−315671（ＪＰ，Ａ) 特開 昭60−246872（ＪＰ，Ａ) ──────────────────────────────────────────────────続 き Continuing from the front page (72) Inventor Hideyuki Nakajima 4 Towada, Kamisu-cho, Kashima-gun, Ibaraki Pref. (72) Inventor Toshio Yonezawa 2-5-14 Minamisuna, Koto-ku, Tokyo 2-7-14 Minamisuna, Takenaka Co., Ltd. No. 2101 (72) Inventor Masaki Iwata 29-11 Tatsumi-cho, Minato-ku, Nagoya-shi, Aichi (56) References JP-A-63-315671 (JP, A) JP-A-60-246872 (JP, A)
Claims (3)
て、一般式 【化１】 〔式中、ｍ及びｎはそれぞれ１〜２９の整数であり、か
つｍ＋ｎ＝３０である。〕で表されるポリオキシアルキ
レンビスフェノールエーテルを塗布したことを特徴とす
るセメント補強用炭素繊維。1. A sizing agent on the surface of carbon fiber
And the general formula [Wherein, m and n are each an integer of 1 to 29;
M + n = 30. A polyoxyalkylene represented by
A carbon fiber for cement reinforcement, which is coated with lenbisphenol ether .
して0.５〜１０重量％である請求項１記載のセメント補
強用炭素繊維。2. The carbon fiber for cement reinforcement according to claim 1, wherein the amount of the sizing agent applied is 0.5 to 10% by weight based on the carbon fiber.
素繊維を繊維長１０〜５０ｍｍに切断し、セメントマト
リックスに対して容積混入率１〜５％の割合で含有させ
てなる曲げ強度３００ｋｇｆ／ｃｍ2 以上のセメント複
合体。3. A bending strength of 300 kgf / cm, wherein the carbon fiber for cement reinforcement according to claim 1 or 2 is cut to a fiber length of 10 to 50 mm and contained in a cement matrix at a volume mixing ratio of 1 to 5%. cm 2 or more of the cement complex.