JP2551408B2 - How to decorate items - Google Patents

How to decorate items

Info

Publication number
JP2551408B2
JP2551408B2 JP61081989A JP8198986A JP2551408B2 JP 2551408 B2 JP2551408 B2 JP 2551408B2 JP 61081989 A JP61081989 A JP 61081989A JP 8198986 A JP8198986 A JP 8198986A JP 2551408 B2 JP2551408 B2 JP 2551408B2
Authority
JP
Japan
Prior art keywords
image
layer
receiving layer
article
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP61081989A
Other languages
Japanese (ja)
Other versions
JPS62240588A (en
Inventor
正典 赤田
喜員 伊藤
純平 菅藤
満 多気田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP61081989A priority Critical patent/JP2551408B2/en
Priority to PCT/JP1987/000228 priority patent/WO1987006195A1/en
Priority to EP92120842A priority patent/EP0535718B1/en
Priority to EP87902719A priority patent/EP0266430B1/en
Priority to DE3751107T priority patent/DE3751107T2/en
Priority to US07/138,384 priority patent/US4923848A/en
Priority to DE3751484T priority patent/DE3751484T2/en
Publication of JPS62240588A publication Critical patent/JPS62240588A/en
Priority to US08/034,186 priority patent/US5451560A/en
Priority to JP5095055A priority patent/JPH068648A/en
Priority to US08/395,850 priority patent/US5629259A/en
Priority to US08/470,208 priority patent/US5707925A/en
Application granted granted Critical
Publication of JP2551408B2 publication Critical patent/JP2551408B2/en
Priority to US08/797,726 priority patent/US5940111A/en
Priority to US09/260,017 priority patent/US6392680B2/en
Priority to US10/112,932 priority patent/US6917375B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 （発明の属する技術分野） 本発明は、物品の装飾方法に関し、更に詳しくは昇華
性染料（熱移行性染料）により任意の画像を形成するこ
とか出来、且つ形成された画像を任意の物品に貼着する
ことが出来る物品の装飾方法を提供する。Description: TECHNICAL FIELD The present invention relates to a method for decorating an article, and more specifically, it can and can form an arbitrary image with a sublimation dye (heat transfer dye). Provided is a method of decorating an article, which can attach the image to an arbitrary article.

（従来の技術） 従来、昇華性染料による布帛の熱転写（昇華性転写）
方法は古くから行われており、この方法は昇華性染料を
担持する染料絵柄層を透明フイルム上に形成し、これを
布帛に重ねて加熱し、染料を布帛に移行させて布帛に画
像を形成する方法である。この技術を利用し、更に近年
の精密サーマルプリンター等の画像技術の発展と相まっ
て、昇華性染料を有する熱転写シートからプラスチック
フイルム上に写真に劣らない程度の精密な画像形成方法
が種々提案されている。この近年の方法によれば、例え
ば、ポリエステル層を有する紙等の透明フイルム上に、
カメラ、画像、テレビ画像或いはパソコンのグラフィッ
ク画像等を容易にハードコピー化出来るものであり、従
来の写真技術や精密印刷技術に十分に対抗し得るレベル
に達している。(Prior Art) Conventionally, thermal transfer of fabric by sublimation dye (sublimation transfer)
The method has been used for a long time, and this method forms a dye pattern layer carrying a sublimable dye on a transparent film, superimposes this on a cloth and heats it to transfer the dye to the cloth to form an image on the cloth. Is the way to do it. Utilizing this technology, in combination with the recent development of image technology such as precision thermal printers, various kinds of precise image forming methods have been proposed on a plastic film from a thermal transfer sheet having a sublimable dye so as not to be inferior to a photograph. . According to this recent method, for example, on a transparent film such as paper having a polyester layer,
It can easily make a hard copy of a camera, an image, a television image, or a graphic image of a personal computer, and has reached a level that can sufficiently oppose conventional photographic technology and precision printing technology.

（発明が解決しようとする課題） 上述の如き熱転写技術は簡便に任意の画像を形成し得
る利点を有するが、その被熱転写シートがポリエステル
等の如く昇華性染料によって染着可能な材料に限定され
るという問題があり、又、一方では、被転写物品は、フ
イルム状やシート状等のシート状物に形状が限定され、
例えば、木材、金属、ガラス、セラミックス等には画像
を形成することが出来ず、更に、ポリエステル等のプラ
スチックスであっても、それらの画像形成面が曲面であ
ったり、凹凸形状を有したり、更に平面状であってもシ
ート状物以外の立体的成形物には画像を形成することが
困難であるという問題がある。(Problems to be Solved by the Invention) Although the thermal transfer technique as described above has an advantage that any image can be easily formed, the thermal transfer sheet is limited to a material that can be dyed with a sublimable dye such as polyester. On the other hand, on the other hand, the transferred article is limited to a sheet-like material such as a film or a sheet,
For example, it is not possible to form an image on wood, metal, glass, ceramics, etc., and even if plastics such as polyester are used, their image forming surface may have a curved surface or an uneven shape. Further, there is a problem that it is difficult to form an image on a three-dimensional molded article other than the sheet-shaped article even if it is flat.

特に、近年のキャッシュカード等の各種のカードの種
類及び利用分野が拡大するに従って、これらカード類に
画像や記号を付与し、種々の機能や装飾を与えることが
必要であるが、これらのカードは平面状であるが柔軟性
が無かったり、或いは文字や記号等の凹凸部が形成され
ている為に、これらのカード類に上記の熱転写方法で画
像を付与することも困難である。In particular, with the expansion of the types and fields of use of various cards such as cash cards in recent years, it is necessary to add images and symbols to these cards to give them various functions and decorations. It is difficult to apply an image to these cards by the above-mentioned thermal transfer method because they are flat but have no flexibility or have irregularities such as characters and symbols.

従って、任意の材料からなり、任意の形状且つ任意の
表面形状を有する物品の表面に、所望の画像を容易に付
与することが出来、且つ画像と被装飾物品とが一体化す
る様な技術の開発が要望されている。Therefore, it is possible to easily provide a desired image on the surface of an article made of an arbitrary material and having an arbitrary shape and an arbitrary surface shape, and to integrate the image with the article to be decorated. Development is required.

（課題を解決する為の手段） 即ち、本発明は、昇華性染料層を全面に有する熱転写
シートの染料層面を、透明フイルムの一方の面に設けら
れた透明受像層からなる被熱転写シートの受像層面に対
向させて重ね合わせ、いずれかの側からサーマルヘッド
により、画像信号に従って熱エネルギーを付与すること
により、上記受像層に昇華性染料からなる所望の画像を
形成する工程、及び上記画像形成された被熱転写シート
の画像面を被装飾物品に対向させて被熱転写シート全体
を貼着する工程とを含むことを特徴とする物品の装飾方
法である。(Means for Solving the Problem) That is, the present invention provides an image-receiving material for a heat-transferable sheet, which comprises a transparent image-receiving layer provided on one surface of a transparent film, the dye layer surface of the thermal transfer sheet having a sublimable dye layer on the entire surface. A step of forming a desired image composed of a sublimable dye on the image receiving layer by applying thermal energy according to an image signal from either side by superimposing the layers facing each other and a thermal head, and forming the image. And a step of adhering the entire heat-transferable sheet with the image surface of the heat-transferable sheet facing the article to be decorated.

（発明の実施の形態） 次に実施の形態を図解的に示す添付図面を参照して本
発明を更に詳しく説明する。(Embodiments of the Invention) Next, the present invention will be described in more detail with reference to the accompanying drawings which schematically show embodiments.

第１図は、本発明で使用する被熱転写シートの基本的
な形態を図解的に示す図であり、第２〜３図は被熱転写
シートの好ましい実施の形態を示す図である。FIG. 1 is a diagram schematically showing a basic form of a heat-transferable sheet used in the present invention, and FIGS. 2 to 3 are diagrams showing a preferred embodiment of the heat-transferable sheet.

第１図に示す通り、本発明で使用する被熱転写シート
10の基本的な構成は、任意の透明フイルム１の一方の面
に受像層２を設けたことを特徴としている。被熱転写シ
ートをこの様な構成とすることによって、昇華性染料を
有する熱転写シートによりサーマルヘッドを用いて受像
層２に所望の画像を形成し、次いで画像を有する被熱転
写シートを任意の被装飾物品の貼着面に対抗させて、こ
れらの任意の物品に任意の手段により貼着することによ
って、前述の如き従来技術の欠点が基本的に解決され
る。As shown in FIG. 1, the heat transfer sheet used in the present invention
The basic constitution of 10 is characterized in that an image receiving layer 2 is provided on one surface of an arbitrary transparent film 1. By configuring the heat transferable sheet as described above, a desired image is formed on the image receiving layer 2 by using a thermal transfer sheet having a sublimable dye, and then the heat transferable sheet having the image is used as an arbitrary decorated article. The above-mentioned drawbacks of the prior art are basically solved by adhering to any of these articles by any means so as to oppose the adhering surface.

即ち、上記における受像層２は昇華性染料によって染
着可能な材料に限定されるが、画像を形成した被熱転写
シートは、これを反転させて、それぞれ被装飾物品の材
質に応じた接着方法により、ガラスでも、金属でも、木
材でも或いは昇華性染料によっては染着困難なプラスチ
ックス材料でも自由に貼着が可能である。又、この様な
画像は、十分な柔軟性を有する為、被装飾物品の表面形
状が曲面や凹凸形状面であってもそれらの表面形状に十
分に追従することが可能である為、被装飾物品の表面形
状によって貼着が制限されることがない。That is, the image receiving layer 2 in the above is limited to a material which can be dyed with a sublimable dye, but the image-formed heat-transferable sheet is turned over and is subjected to an adhesion method according to the material of the article to be decorated. Also, glass, metal, wood, or plastic material that is difficult to dye with sublimable dyes can be attached freely. Further, since such an image has sufficient flexibility, it is possible to sufficiently follow the surface shape of the article to be decorated even if the surface shape of the article is a curved surface or an uneven surface. Attachment is not limited by the surface shape of the article.

又、この様に貼着された画像は、その表面が透明フイ
ルムで被覆されている為、それ以上何らの手段も要する
ことなく、十分な耐摩擦性、耐水性、耐薬品性等を有す
るものとなる。In addition, since the surface of the image adhered in this way is covered with a transparent film, it has sufficient abrasion resistance, water resistance, chemical resistance, etc. without requiring any further means. Becomes

第２図は被熱転写シート10の好ましい１例を示すもの
であり、受像層２の表面に離型層３が設けられている。FIG. 2 shows a preferred example of the heat transferable sheet 10, in which a release layer 3 is provided on the surface of the image receiving layer 2.

離型層３は、図示していない熱転写シートからサーマ
ルヘッドを用いて昇華性染料を移行させて、受像層３に
画像を形成する際に熱転写シートと受像層２の熱による
粘着を防止する為にあるものであり、この様な粘着が生
じない場合や、熱転写シートの表面にこの様な離型層が
設けられている場合は不要である。The release layer 3 transfers the sublimable dye from a thermal transfer sheet (not shown) using a thermal head to prevent the thermal transfer sheet and the image receiving layer 2 from sticking to each other when an image is formed on the image receiving layer 3. It is not necessary when such adhesion does not occur or when such a release layer is provided on the surface of the thermal transfer sheet.

第３図に示す例は、被熱転写シート10の別の好ましい
例を示すものであり、受像層２と透明フイルム１との間
に中間層４が設けられている。The example shown in FIG. 3 shows another preferable example of the heat transferable sheet 10, in which an intermediate layer 4 is provided between the image receiving layer 2 and the transparent film 1.

ここで云う中間層４とは、受像層２に熱転写シートか
らサーマルヘッドを用いて昇華性染料を移行させて画像
を形成する際に、画像の形成を十分にするものであり、
例えば、クッション層や断熱層である。例えば、クッシ
ョン性のある層を中間層４として設けることにより、熱
転写シートと受像層２の密着性が改良され、サーマルヘ
ッドによる画像形成時の昇華性染料の移行が均一化され
て、画像信号に十分対応した画像を形成することが出来
る。The intermediate layer 4 referred to here is a layer for sufficiently forming an image when an image is formed by transferring a sublimable dye from the thermal transfer sheet to the image receiving layer 2 using a thermal head,
For example, a cushion layer or a heat insulating layer. For example, by providing a layer having a cushioning property as the intermediate layer 4, the adhesiveness between the thermal transfer sheet and the image receiving layer 2 is improved, and the transfer of the sublimable dye at the time of image formation by the thermal head is made uniform, so that an image signal is obtained. A sufficiently compatible image can be formed.

又、中間層４を断熱性のある材料から断熱層として形
成することによって、熱転写シートから昇華性染料を受
像層２に移行させるのに際して、付与される熱の放熱が
防止出来、熱利用効率が向上して十分な画像の形成が促
進される。勿論、これらのクッション層或いは断熱層は
別々に任意の順序で同時に設けてよい。Further, by forming the intermediate layer 4 from a heat-insulating material as a heat-insulating layer, when transferring the sublimable dye from the thermal transfer sheet to the image-receiving layer 2, it is possible to prevent the heat radiation of the applied heat and to improve the heat utilization efficiency. And the formation of a sufficient image is promoted. Of course, these cushion layers or heat insulating layers may be separately provided simultaneously in any order.

この様な中間層は、被熱転写シートが画像形成後、被
装飾物品に反転させて貼着するので、貼着後は、画像を
有する受像層より外側に来るので実質上透明であること
が必要である。Such an intermediate layer is necessary to be substantially transparent because it is placed on the article to be decorated after being inverted after the image is formed on the heat-transferable sheet, so that it comes outside the image-receiving layer having the image. Is.

以上が本発明で使用する被熱転写シートの主たる構成
であり、上記好ましい例示の外にも種々の態様が当業者
の自明であり、これらの自明の態様も当然本発明に包含
される。The above is the main constitution of the heat transferable sheet used in the present invention, and various modes other than the above preferable examples are obvious to those skilled in the art, and these obvious modes are naturally included in the present invention.

次に本発明の物品の装飾方法を説明すると、本発明の
方法は、上記の如き被熱転写シートを利用し、サーマル
ヘッドを用いて画像形成することを主たる特徴とするも
のである。Next, the method of decorating an article of the present invention will be described. The method of the present invention is mainly characterized in that an image is formed using a thermal head using the above-mentioned thermal transfer sheet.

基本的な態様として第４〜５図に図解的に示す方法に
より説明する。As a basic mode, a method illustrated in FIGS. 4 to 5 will be described.

第４図に示す例は、第１図に示す被熱転写シートを利
用するものであり、先ず、最初に昇華性染料を記録剤と
する従来公知の熱転写シート20を被熱転写シート10に、
熱転写シートの染料担持層21が被熱転写シート10の受像
層２に対向する様に重ね、熱転写シート20又は被熱転写
シート10のいずれかの側、好ましくは熱転写シート20側
からサーマルヘッドにより画像信号に従って熱エネルギ
ー（矢印）を付与することによって、受像層２に所望の
画像５が形成される。次いでこの様に形成された画像を
有する被熱転写シートを、被装飾物品30に対向させて重
ね合せ、適宜な接着手段により被装飾物品30に貼着させ
る（第５図）ことにより本発明の装飾方法が完了する。The example shown in FIG. 4 utilizes the heat-transferable sheet shown in FIG. 1. First, a conventionally known heat-transfer sheet 20 containing a sublimable dye as a recording material is first used as the heat-transferable sheet 10.
The dye-carrying layer 21 of the thermal transfer sheet is superposed so as to face the image receiving layer 2 of the thermal transfer sheet 10, and either side of the thermal transfer sheet 20 or the thermal transfer sheet 10, preferably the thermal transfer sheet 20 side, according to an image signal by a thermal head. A desired image 5 is formed on the image receiving layer 2 by applying thermal energy (arrow). Next, the heat-transferred sheet having the image thus formed is placed so as to face the article 30 to be decorated, and adhered to the article 30 to be decorated by an appropriate adhesive means (FIG. 5). The method is complete.

又、受像層２は一般に昇華性染料で染着可能な熱可塑
性樹脂から形成されているので、何らの接着剤を必要と
せずに、そのままプラスチックス成形物、布帛、金属、
その他に熱融着させることも可能である。Further, since the image receiving layer 2 is generally formed of a thermoplastic resin that can be dyed with a sublimable dye, it does not require any adhesive agent and can be directly used as a plastic molded product, cloth, metal,
Alternatively, heat fusion can be performed.

以上本発明の装飾方法を基本的な例で説明したが、第
２図以下に例示した被熱転写シートを使用して本発明の
装飾方法を実施する場合も同様である。Although the decorative method of the present invention has been described above with reference to a basic example, the same applies to the case of carrying out the decorative method of the present invention using the heat-transferable sheets illustrated in FIG.

次に以上の如き被熱転写シートを構成する材料及び構
成方法の面から本発明を更に詳細に説明する。Next, the present invention will be described in more detail in terms of the materials and the method of forming the heat transfer sheet as described above.

透明フイルムとしては、受像層に形成された画像を隠
蔽しない程度に透明であり、且つ耐摩耗性等の優れた表
面物性を有するフイルムであり、例えば、ポリオレフィ
ン、ポリ塩化ビニル、ポリエチレンテレフタレート、ポ
リスチレン、ポリメタクリレート、ポリカーボネート等
の各種のプラスチックスのフイルム若しくはこれらの表
面を種々処理したものが使用出来る。この様な透明フイ
ルムは、あまり厚いと物品に貼着したときに画像が盛り
上がり、物品との一体感が無くなるので、例えば、0.5
〜50μｍ程度の厚さのものが好ましい。The transparent film, which is transparent to the extent that it does not hide the image formed in the image receiving layer, and has excellent surface properties such as abrasion resistance, for example, polyolefin, polyvinyl chloride, polyethylene terephthalate, polystyrene, Films of various plastics such as polymethacrylate and polycarbonate, or those whose surface is variously treated can be used. If such a transparent film is too thick, the image will rise when attached to an article and the sense of unity with the article will be lost.
A thickness of about 50 μm is preferable.

受像層を構成する材質は、熱転写シートから移行する
昇華性染料、例えば、昇華性の分散染料を受容し、受容
により形成された画像を維持する為のものである。例え
ば、（イ）〜（ホ）の合成樹脂が単独若しくは２種以上
の混合により使用される。The material constituting the image receiving layer is for receiving a sublimable dye transferred from the thermal transfer sheet, for example, a sublimable disperse dye, and for maintaining an image formed by the reception. For example, the synthetic resins (a) to (e) are used alone or in combination of two or more.

（イ）エステル結合を有するもの。(A) Those having an ester bond.

ポリエステル樹脂、ポリアクリル酸エステル樹脂、ポ
リカーボネート樹脂、ポリ酢酸ビニル樹脂、スチレンア
クリレート樹脂、ビニルトルエンアクリレート樹脂等。Polyester resin, polyacrylic ester resin, polycarbonate resin, polyvinyl acetate resin, styrene acrylate resin, vinyl toluene acrylate resin, etc.

（ロ）ウレタン結合を有するもの。(B) Those having a urethane bond.

ポリウレタン樹脂等。 Polyurethane resin and the like.

（ハ）アミド結合を有するもの。(C) Those having an amide bond.

ポリアミド樹脂（ナイロン）。 Polyamide resin (nylon).

（ニ）尿素結合を有するもの。(D) Those having a urea bond.

尿素樹脂等。 Urea resin etc.

（ホ）その他極性の高い結合を有するもの。(E) Others having a highly polar bond.

ポリカプロラクトン樹脂、ポリスチレン樹脂、ポリ塩
化ビニル樹脂、ポリアクリロニトリル樹脂等。Polycaprolactone resin, polystyrene resin, polyvinyl chloride resin, polyacrylonitrile resin, etc.

又、受像層は飽和ポリエステルと塩化ビニル−酢酸ビ
ニル共重合体との混合樹脂により構成される。飽和ポリ
エステルとしては、例えば、バイロン200、バイロン29
0、バイロン600等（以上、東洋紡製）、KA−1038C（荒
川化学製）、TP220、TP235（以上、日本合成製）等が用
いられる。塩化ビニル−酢酸ビニル共重合体は塩化ビニ
ル成分含有率85〜97重量％で、重合度200〜800程度のも
のが好ましい。塩化ビニル−酢酸ビニル共重合体は、必
ずしも塩化ビニル成分と酢酸ビニル成分のみの共重合体
である場合に限らず、本発明の目的を妨げない範囲のビ
ニルアルコール成分、マレイン酸成分等を含むものであ
ってもよい。The image receiving layer is composed of a mixed resin of a saturated polyester and a vinyl chloride-vinyl acetate copolymer. As the saturated polyester, for example, Byron 200, Byron 29
0, Byron 600, etc. (manufactured by Toyobo), KA-1038C (manufactured by Arakawa Chemical), TP220, TP235 (manufactured by Nippon Gosei) and the like are used. The vinyl chloride-vinyl acetate copolymer preferably has a vinyl chloride component content of 85 to 97% by weight and a degree of polymerization of about 200 to 800. The vinyl chloride-vinyl acetate copolymer is not limited to the case where it is a copolymer of only a vinyl chloride component and a vinyl acetate component, and contains a vinyl alcohol component, a maleic acid component, etc. within a range not hindering the object of the present invention. May be

受像層は、又、ポリスチレン系の樹脂により構成され
てもよく、例えば、スチレン系モノマー、例えば、スチ
レン、α−メチルスチレン、ビニルトルエンの単独若し
くは共重合体からなるポリスチレン系樹脂、或いは前記
スチレン系モノマーと他のモノマー、例えば、アクリル
酸エステル、メタクリル酸エステル、アクリロニトリ
ル、メタクリロニトリル等のアクリル若しくはメタクリ
ル系モノマー若しくは無水マレイン酸との共重合体であ
るスチレン系共重合体樹脂が挙げられる。The image receiving layer may be composed of a polystyrene resin, for example, a styrene monomer, for example, styrene, α-methylstyrene, a polystyrene resin composed of a homo- or copolymer of vinyltoluene, or the styrene-based resin. A styrene copolymer resin which is a copolymer of a monomer and another monomer, for example, an acrylic or methacrylic monomer such as acrylate, methacrylate, acrylonitrile, methacrylonitrile, or maleic anhydride is exemplified.

以上の如き合成樹脂のうちで特に好適なものはポリエ
ステル系樹脂である。Among the above synthetic resins, polyester resins are particularly preferred.

上記いずれの態様においても、受像層の白色度を向上
させて転写画像を鮮明度を更に高めるとともに、被熱転
写シート表面に筆記性を付与し、且つ転写された画像の
再転写を防止する目的で受像層中に白色顔料を添加する
ことが出来る。白色顔料としては、酸化チタン、酸化亜
鉛、カオリンクレー、炭酸カルシウム、微粉末シリカ等
が用いられ、これは２種以上混合して用いることが出来
ることは前述した通りである。又、転写画像の耐光性を
更に高める為に、受像層中に紫外線吸収剤及び／又は光
安定化剤を添加することが出来る。In any of the above embodiments, for the purpose of improving the whiteness of the image-receiving layer to further improve the clarity of the transferred image, imparting writability to the surface of the heat-transferred sheet, and preventing retransfer of the transferred image. A white pigment can be added to the image receiving layer. As the white pigment, titanium oxide, zinc oxide, kaolin clay, calcium carbonate, fine powder silica and the like are used, and as described above, two or more kinds can be mixed and used. Further, in order to further enhance the light resistance of the transferred image, an ultraviolet absorber and / or a light stabilizer can be added to the image receiving layer.

これら紫外線吸収剤、光安定化剤の添加量は受像層を
構成する樹脂100重量部に対してそれぞれ0.05〜10重量
部、及び0.5〜３重量部が好ましい。The amounts of these ultraviolet absorbers and light stabilizers are preferably 0.05 to 10 parts by weight and 0.5 to 3 parts by weight, respectively, based on 100 parts by weight of the resin constituting the image receiving layer.

本発明で使用する被熱転写シートは、熱転写シートと
の離型性及び受像層と透明フイルムとの離型性を向上せ
しめる為に、受像層の一方の面又は両方の面に離型層を
形成したり、或いはこれに代えて受像層中に離型剤を含
有せしめることが出来る。離型剤としてはポリエチレン
ワックス、アミドワックス、テフロンパウダー等の固型
ワックス類；弗素系、隣酸エステル系の界面活性剤；シ
リコーンオイル等が挙げられるが、シリコーンオイルが
好ましい。The heat-transferable sheet used in the present invention has a release layer formed on one surface or both surfaces of the image-receiving layer in order to improve releasability between the heat-transfer sheet and the image-receiving layer and the transparent film. Alternatively, or in place of this, a release agent can be contained in the image receiving layer. Examples of the release agent include solid waxes such as polyethylene wax, amide wax, and Teflon powder; fluorine-based and phosphoric acid ester-based surfactants; silicone oil; and silicone oil is preferred.

上記シリコーンオイルとしては油状のものも用いるこ
とが出来るが、硬化型のものが好ましい。硬化型の上記
シリコーンオイルとしては、反応硬化型、光硬化型、触
媒硬化型等が挙げられるが、反応硬化型のシリコーンオ
イルが特に好ましい。As the silicone oil, an oily one can be used, but a curable type is preferred. Examples of the curable silicone oil include a reaction curable type, a photocurable type, and a catalyst curable type, and a reaction curable type silicone oil is particularly preferable.

反応硬化型のシリコーンオイルとしては、アミノ変性
シリコーンオイルとエポキシ変性シリコーンオイルとを
反応硬化させたものが好ましく、アミノ変性シリコーン
オイルとしては、KF−393、KF−857、KF−858、Ｘ−22
−3680、Ｘ−22−3810C（以上、信越化学工業（株）
製）等が挙げられ、エポキシ変性シリコーンオイルとし
ては、KF−100T、KF−101、KF−60−164、KF−103（以
上、信越化学工業（株）製）等が挙げられる。As the reaction-curable silicone oil, those obtained by reacting and curing an amino-modified silicone oil and an epoxy-modified silicone oil are preferable, and as the amino-modified silicone oil, KF-393, KF-857, KF-858, X-22
-3680, X-22-3810C (Shin-Etsu Chemical Co., Ltd.)
Examples of the epoxy-modified silicone oil include KF-100T, KF-101, KF-60-164, KF-103 (all manufactured by Shin-Etsu Chemical Co., Ltd.) and the like.

又、触媒硬化型或いは光硬化型シリコーンオイルとし
ては、KS−705F、KS−770（以上、触媒硬化型シリコー
ンオイル：信越化学工業（株）製）、KS−720、KS−774
（以上、光硬化型シリコーンオイル：信越化学工業
（株）製）等が挙げられる。これら硬化型シリコーンオ
イルの添加量は、受像層を構成する樹脂の0.5〜30重量
％が好ましい。Examples of the catalyst-curable or photocurable silicone oil include KS-705F and KS-770 (these are the catalyst-curable silicone oils manufactured by Shin-Etsu Chemical Co., Ltd.), KS-720 and KS-774.
(Above, a photo-curable silicone oil: manufactured by Shin-Etsu Chemical Co., Ltd.). The addition amount of these curable silicone oils is preferably 0.5 to 30% by weight of the resin constituting the image receiving layer.

又、受像層の表面の一部に、上記離型剤を適宜な溶媒
に溶解或いは分散させて塗布した後、乾燥させる等によ
って離型層を設けることも出来る。離型層を構成する離
型剤としては、前記したアミノ変性シリコーンオイルと
エポキシ変性シリコーンオイルとの反応硬化型が特に好
ましい。離型層の厚さは0.01〜５μｍ、特に0.05〜２μ
ｍが好ましい。Further, a release layer may be provided on a part of the surface of the image receiving layer by dissolving or dispersing the release agent in an appropriate solvent and applying the solution, followed by drying. As the release agent constituting the release layer, a reaction curing type of the above-mentioned amino-modified silicone oil and epoxy-modified silicone oil is particularly preferable. The thickness of the release layer is 0.01 to 5 μm, particularly 0.05 to 2 μm.
m is preferred.

尚、受像層を形成する再にシリコーンオイルを添加し
て形成すると、塗布後、シリコーンオイルが表面にブリ
ードしてくるので、ブリードさせた後に硬化させて離型
層を形成することが出来る。When silicone oil is added again to form the image receiving layer, the silicone oil bleeds to the surface after application, so the release layer can be formed by bleeding and curing.

受像層の形成は、透明フイルム上に、受像層を形成す
る材料を溶解ないし分散して得られる受像層形成用組成
物を使用して、公知の塗布若しくは印刷方法により行う
他に、受像層を透明フイルムとは別の一時的キャリアー
上に一旦形成した後に、改めて透明フイルム上に転写す
る方法により行ってもよい。The image-receiving layer is formed by a known coating or printing method using a composition for forming an image-receiving layer obtained by dissolving or dispersing a material for forming the image-receiving layer on a transparent film. It may be carried out by a method in which it is once formed on a temporary carrier different from the transparent film and then transferred again onto the transparent film.

一時的キャリアーとしては、表面が離型性のシートを
用いる。例えば、（１）セルロース繊維紙や合成紙等の
表面にアンダーコート層を施した後に離型用シリコーン
層を施したもの、（２）セルロース繊維紙の表面にポリ
オレフィン系樹脂若しくはポリエステル樹脂をエクスト
ルージョンコーティングしたもの、又は（３）ポリエス
テルフイルム等のプラスチックフイルムの表面に離型用
シリコーン層を施したもの等である。A sheet whose surface is releasable is used as the temporary carrier. For example, (1) an undercoat layer on a surface of cellulose fiber paper or synthetic paper followed by a release silicone layer, and (2) a polyolefin resin or polyester resin on the surface of the cellulose fiber paper by extrusion. It is coated or (3) a plastic film such as a polyester film having a release silicone layer on the surface.

一時的キャリアー上には、透明フイルム上に行うのと
同様にして受像層を形成した後、必要により接着層を形
成する。この接着層は透明フイルム上に受像層を転写さ
せるときに、透明フイルムと受像層との間の接着力を確
保する為のものである。この方法では、更に他の層、例
えば、クッション性等を付与する中間層を一時的キャリ
アー上に形成しておき、透明フイルム上に中間層と受像
層とを一度に転写する様にしてもよい。中間層が接着層
を兼ねているときは接着層を一時的キャリアー上に形成
しなくてもよい。尚、いずれの場合においても、接着層
は透明フイルムと、一時的キャリアー上の最上層との間
に介在すればよいから、接着層を透明フイルム上に形成
しておき、一時的キャリアー上には受像層のみ、或いは
受像層と中間層を順に形成しておいて転写してもよい。An image-receiving layer is formed on the temporary carrier in the same manner as on a transparent film, and then an adhesive layer is formed if necessary. This adhesive layer is for ensuring the adhesive force between the transparent film and the image receiving layer when the image receiving layer is transferred onto the transparent film. In this method, another layer, for example, an intermediate layer for imparting cushioning properties or the like may be formed on the temporary carrier, and the intermediate layer and the image receiving layer may be transferred at one time on the transparent film. . When the intermediate layer also serves as the adhesive layer, the adhesive layer may not be formed on the temporary carrier. In any case, since the adhesive layer may be interposed between the transparent film and the uppermost layer on the temporary carrier, the adhesive layer is formed on the transparent film and the temporary carrier is not formed on the temporary carrier. The image receiving layer alone or the image receiving layer and the intermediate layer may be sequentially formed and transferred.

受像層を一時的キャリアー上に一旦形成し、転写法に
より透明フイルム上に形成する方法を採用すると、透明
フイルム上に形成された受像層の表面は、一時的キャリ
アーの表面の状態が転写されている為に平滑性が非常に
優れており、透明フイルム上に直接に形成した受像層
は、転写法によるものと比べると平滑性が劣っており、
より鮮明で精緻な画像を得たいときは、転写法を採用す
るのがよい。When the method of forming the image receiving layer on the temporary carrier and then forming it on the transparent film by the transfer method is adopted, the surface state of the temporary carrier is transferred to the surface of the image receiving layer formed on the transparent film. Therefore, the smoothness is very excellent, and the image-receiving layer formed directly on the transparent film is inferior in smoothness to that obtained by the transfer method.
When a clearer and more detailed image is desired, the transfer method should be adopted.

接着剤としては受像層と透明フイルムとを接着出来る
ものであればよく、ポリエステル系、ポリアクリル酸エ
ステル系、ポリウレタン系、ポリ塩化ビニル系、ポリオ
レフィン系、エチレン−酢酸ビニル共重合体、合成ゴム
系等の有機溶剤溶液又はエマルジョンが使用出来る。接
着剤は熱接着タイプでも、常温粘着タイプでもよい。熱
接着タイプの場合には、ワックス、エチレン−酢酸ビニ
ル共重合体樹脂、ポリオレフィン、石油系樹脂等のホッ
トメルトタイプの接着剤による熱接着或いはポリオレフ
ィンフイルム等、エクストルージョンフイルムによるサ
ンドイッチラミネーションでもよい。Any adhesive can be used as long as it can bond the image-receiving layer and the transparent film, and is polyester-based, polyacrylic ester-based, polyurethane-based, polyvinyl chloride-based, polyolefin-based, ethylene-vinyl acetate copolymer, synthetic rubber-based Organic solvent solutions or emulsions such as The adhesive may be a heat bonding type or a room temperature adhesive type. In the case of the heat-bonding type, heat-bonding with a hot-melt type adhesive such as wax, ethylene-vinyl acetate copolymer resin, polyolefin, or petroleum resin, or sandwich lamination using an extrusion film such as a polyolefin film may be used.

中間層を兼ねる接着層として両面テープを用いてもよ
い。両面テープはレーヨンペーパーにアクリル系貼着剤
等を含浸乾燥したもので、乾燥後の両面テープには微細
空孔が出来ており、発泡層と等価の役割を果たすものと
思われる。A double-sided tape may be used as an adhesive layer that also serves as an intermediate layer. The double-sided tape is obtained by impregnating and drying an acrylic adhesive or the like in rayon paper. The dried double-sided tape has fine pores and is considered to play a role equivalent to a foamed layer.

中間層は、構成する材質によりクッション性、多孔性
のいずれかであり、或いは場合によっては接着層の役目
も兼ねている。The intermediate layer may be either cushioning or porous depending on the constituent material, or may also serve as an adhesive layer in some cases.

クッション性層はJIS−Ｋ−6301に規定される100％モ
ジュラスが100kg/cm2以下である樹脂を主とするもので
あり、ここで前記100％モジュラスが100kg/cm2を越える
と、剛性が高過ぎる為にこの様な樹脂を用いて中間層を
形成しても、熱転写シートと受像層の印字の際の十分な
密着性が保たれない。又、前記100モジュラスの下限
は、実際上0.5kg/cm2程度である。The cushioning layer is mainly made of a resin having a 100% modulus specified in JIS-K-6301 of 100 kg / cm 2 or less. If the 100% modulus exceeds 100 kg / cm 2 , the rigidity is reduced. Even if the intermediate layer is formed using such a resin, the adhesion between the thermal transfer sheet and the image receiving layer at the time of printing cannot be maintained sufficiently. Further, the lower limit of the 100 modulus is actually about 0.5 kg / cm 2 .

上記の条件に合致する樹脂としては次の様なものが挙
げられる ポリウレタン樹脂、ポリエステル樹脂、ポリブタジエ
ン樹脂、ポリアクリル酸エステル樹脂、エポキシ樹脂、
ポリアミド樹脂、ロジン変性フェノール樹脂、テルペン
フェノール樹脂、エチレン／酢酸ビニル共重合体樹脂
等。Resins that meet the above conditions include the following: polyurethane resin, polyester resin, polybutadiene resin, polyacrylate resin, epoxy resin,
Polyamide resin, rosin-modified phenol resin, terpene phenol resin, ethylene / vinyl acetate copolymer resin, etc.

上記の樹脂は、１種若しくは２種以上混合して使用す
ることが出来るが、上記の樹脂は比較的粘着性を有して
いるので、加工中に支障があるときは無機質の添加材、
例えば、シリカ、アルミナ、クレー、炭酸カルシウム
等、或いはステアリン酸アミド等のアミド系物質を添加
してもよい。The above resins can be used alone or in combination of two or more, but since the above resins are relatively tacky, if there is a problem during processing, an inorganic additive,
For example, silica, alumina, clay, calcium carbonate, or an amide-based substance such as stearic acid amide may be added.

クッション性層は上記した様な樹脂を必要に応じて他
の添加剤とともに溶剤・希釈剤等と混練して塗料若しく
はインキとし、公知の塗布方法若しくは印刷方法により
塗膜として乾燥させることにより形成出来、その厚みは
0.5〜50μｍ、より好ましくは２〜20μｍ程度である。
厚みが0.5μｍ未満では、設けた透明フイルムの表面の
粗さを吸収しきれず、従って効果がなく、逆に50μｍを
越えると効果の向上が見られないばかりか、受像層が厚
くなりすぎて突出し、巻き取ったり、重ねたりする際の
支障となるし、又、経済的でもない。The cushioning layer can be formed by kneading the above-mentioned resin with a solvent and a diluent together with other additives as necessary to form a paint or ink, and drying it as a coating film by a known coating method or printing method. , Its thickness is
The thickness is 0.5 to 50 μm, more preferably 2 to 20 μm.
If the thickness is less than 0.5 μm, the roughness of the surface of the provided transparent film cannot be absorbed, and therefore it is not effective. On the contrary, if the thickness exceeds 50 μm, the effect is not improved and the image receiving layer becomes too thick to project. , It becomes a hindrance when winding or stacking, and it is not economical.

この様な中間層を形成すると、熱転写シートと被熱転
写シートとの密着性が向上するのは、中間層自体が剛性
が低い為に印字に際に圧力により変形する為と考えられ
るが、更に前記した様な樹脂は通常ガラス転移点や軟化
点が低く、印字の際に与えられた熱エネルギーにより、
常温におけるよりも更に剛性が低下して変形し易くなる
ことも寄与しているものと推定される。When such an intermediate layer is formed, it is considered that the adhesion between the thermal transfer sheet and the thermal transfer sheet is improved because the intermediate layer itself has low rigidity and therefore is deformed by pressure during printing. Resins such as those usually have a low glass transition point and softening point, and due to the thermal energy given during printing,
It is presumed that this also contributes to the fact that the rigidity is further reduced and deformation is more likely than at room temperature.

多孔層は、１）ポリウレタン等の合成樹脂エマルジョ
ン、メチルメタクリレート−ブタジエン系等の合成ゴム
ラテックスを機械的攪拌により起泡させた液を透明フイ
ルム上に塗布し乾燥させた層、２）上記合成樹脂エマル
ジョン、上記合成ゴムラテックスに発泡剤を混合させた
液を透明フイルム上に塗布し乾燥させた層、３）塩化ビ
ニルプラスチックゾル、ポリウレタン等の合成樹脂又は
スチレン−ブタジエン系等の合成ゴムに発泡剤を混合し
た液を透明フイルム上に塗布し加熱することにより発泡
させた層、４）熱可塑性樹脂又は合成ゴムを有機溶剤に
溶解した溶液と、該有機溶媒に比べて蒸発しにくく該有
機溶媒に対し相溶性を有し、且つ熱可塑性樹脂又は合成
ゴムに対して溶解性を有しない非溶媒（水を主成分とす
るものも含む）との混合液を、透明フイルム上に塗布し
乾燥させることによりミクロ状に凝集した膜を形成して
なるミクロポーラス層等が用いられる。The porous layer is 1) a layer in which a synthetic resin emulsion such as polyurethane or a synthetic rubber latex such as methyl methacrylate-butadiene system is foamed by mechanical stirring and applied on a transparent film and dried, and 2) the above synthetic resin. A layer obtained by coating an emulsion, a liquid obtained by mixing a foaming agent with the above synthetic rubber latex on a transparent film and drying it. 3) A foaming agent for a synthetic resin such as vinyl chloride plastic sol or polyurethane, or a synthetic rubber such as styrene-butadiene system. A layer obtained by applying a mixed liquid on a transparent film and foaming it by heating, 4) a solution in which a thermoplastic resin or synthetic rubber is dissolved in an organic solvent, and an organic solvent which is less likely to evaporate than the organic solvent. With non-solvents (including those containing water as the main component) that are compatible with each other and that are insoluble in thermoplastic resins or synthetic rubbers Interleaf solution, the microporous layer or the like by forming a flocculated film microscopically form is used by coating and drying on a transparent film.

上記１）〜３）の層は起泡の大きさが大きい為、該層
上に受像層の形成用溶液を塗布し乾燥させた場合、乾燥
させて形成された受像層の表面に凹凸が生じる恐れがあ
る。その為に上記凹凸が小さく、又、均一性の高い画像
を転写せしめることが可能な受像層の表面を得る為に
は、多孔室として上記４）のミクロポーラス層を設ける
ことが好ましい。Since the layers 1) to 3) have a large amount of foaming, when the solution for forming the image receiving layer is applied on the layer and dried, the surface of the image receiving layer formed by drying is uneven. There is a fear. Therefore, in order to obtain a surface of the image receiving layer which has a small unevenness and is capable of transferring a highly uniform image, it is preferable to provide the microporous layer of 4) as a porous chamber.

上記ミクロポーラス層の形成に当たって用いられる熱
可塑性樹脂としては、飽和ポリエステル、ポリウレタ
ン、塩化ビニル−酢酸ビニル共重合体、セルロースアセ
トプロピオネート等が挙げられ、又、同様に用いられる
上記合成ゴムとしては、スチレン−ブタジエン系、イソ
プレン系、ウレタン系等が挙げられる。又、該ミクロポ
ーラス層の形成に当たって用いられる有機溶媒及び非溶
媒としては種々のものが可能であるが、通常、有機溶媒
としてはメチルエチルケトン、アルコール等の親水性溶
媒が用いられ、又、非溶媒としては水が用いられる。Examples of the thermoplastic resin used in the formation of the microporous layer include saturated polyester, polyurethane, vinyl chloride-vinyl acetate copolymer, cellulose acetopropionate, and the like. Styrene-butadiene-based, isoprene-based, urethane-based and the like. Further, various organic solvents and non-solvents can be used for forming the microporous layer, and as the organic solvent, a hydrophilic solvent such as methyl ethyl ketone and alcohol is usually used. Is water.

本発明における多孔層の厚みは、３μｍ以上のものが
好ましく、特に５〜20μｍ厚のものが好ましい。多孔層
の厚みが３μｍ未満のものは、クッション性、断熱性の
効果が発揮されない。The thickness of the porous layer in the present invention is preferably 3 μm or more, particularly preferably 5 to 20 μm. When the thickness of the porous layer is less than 3 μm, the cushioning and heat insulating effects are not exhibited.

説明で前後したが、中間層が接着層を兼ねる場合もあ
ることは受像層の形成方法において述べた通りである。As described above in the description of the method for forming the image-receiving layer, the intermediate layer may also serve as the adhesive layer, although the description was changed.

上記の中間層は被熱転写シートの背面に設けてもよい
し、一方の面に設けてもよい。The above intermediate layer may be provided on the back surface of the heat transferable sheet or on one surface thereof.

被熱転写シートの加工工程中又はプリンター内での走
行時に静電気の発生を抑える為に、少なくとも一方の面
の受像層中又は受像層の表面に帯電防止剤を含有させる
ことが出来る。帯電防止剤としては、界面活性剤、例え
ば、陽イオン型界面活性剤（例えば、第４級アンモニウ
ム塩、ポリアミン誘導体等）、陰イオン型界面活性剤
（例えば、アルキルスルホネート等）、両性イオン型界
面活性剤若しくは非イオン型界面活性剤が挙げられる。
帯電防止剤は、グラビアコーティング、バーコーティン
グ等により受像層表面に塗布形成してもよく、受像層樹
脂中に練り込んで受像層の塗工、乾燥時に受像層表面に
移行させてもよい。受像層樹脂と混合する帯電防止剤と
しては、カチオン型のアクリルポリマーを用いることが
出来る。An antistatic agent can be contained in at least one of the image receiving layers or on the surface of the image receiving layer in order to suppress the generation of static electricity during the processing of the heat transfer sheet or during traveling in the printer. Examples of the antistatic agent include surfactants, for example, cationic surfactants (for example, quaternary ammonium salts, polyamine derivatives, etc.), anionic surfactants (for example, alkyl sulfonates, etc.), amphoteric surfactants Surfactants or nonionic surfactants.
The antistatic agent may be applied to the surface of the image receiving layer by gravure coating, bar coating, or the like, or may be kneaded into the resin of the image receiving layer and transferred to the surface of the image receiving layer during coating and drying of the image receiving layer. A cationic acrylic polymer can be used as the antistatic agent mixed with the image-receiving layer resin.

本発明で使用する被熱転写シートは、いずれか一方の
面若しくは両方の面に、少なくとも一部に他の方法で記
録出来る様にしてもよい。代表的なものは水平ペンや鉛
筆等による筆記性層を設けることである。筆記性層は、
受像層を部分的に設けないことにより、透明フイルム表
面をそのまま利用してもよいが、体質顔料を含有する樹
脂層を受像層と並べるか、受像層の上に設けることによ
り形成してもよい。The heat transfer sheet used in the present invention may be configured to be able to record on at least one part or at least one part by another method. A typical example is to provide a writable layer with a horizontal pen or pencil. The writable layer is
By not providing the image receiving layer partially, the transparent film surface may be used as it is, but it may be formed by arranging a resin layer containing an extender pigment side by side with the image receiving layer or by providing it on the image receiving layer. .

以上が本発明で使用する被熱転写シートの構成である
が、この様な被熱転写シートに所望の画像を形成する好
ましい方法は、昇華性染料を有する層を透明フイルム上
に設けてなる熱転写シートを使用する方法である。この
方法で使用する熱転写シートそれ自体及び転写方法自体
はいずれも公知であり、これらの公知の熱転写シート及
び転写方法はいずれも本発明において有用である。又、
この様な転写方法によって、モノカラーでもフルカラー
の画像でもいずれも容易に形成することが出来る。The above is the constitution of the heat transferable sheet used in the present invention. A preferable method for forming a desired image on such a heat transferable sheet is a heat transfer sheet comprising a layer having a sublimable dye on a transparent film. Is the method to use. Both the thermal transfer sheet itself and the transfer method used in this method are known, and these known thermal transfer sheets and transfer methods are all useful in the present invention. or,
With such a transfer method, both a monochrome image and a full-color image can be easily formed.

例えば、従来公知の熱転写シートを前記の被熱転写シ
ートに重ねて従来公知のいずれかの転写装置、例えば、
サーマルプリンター（例えば、東芝製、サーマルプリン
ターTN−5400）等の装置によって５〜100mJ/mm2の熱エ
ネルギーを付与することによって、所望の画像を被熱転
写シートの受像層中に形成することが出来る。For example, a conventionally known thermal transfer sheet is overlaid on the thermal transfer sheet, and any conventionally known transfer device, for example,
A desired image can be formed in the image receiving layer of the heat transferable sheet by applying thermal energy of 5 to 100 mJ / mm 2 with an apparatus such as a thermal printer (for example, Toshiba thermal printer TN-5400). .

以上の如き画像が形成されたフイルムを用いる本発明
の装飾方法は、その画像面を被装飾物品に対向させて貼
着するものであり、この様な方法により、基材である透
明フイルムがそのまま画像の保護層として利用すること
が出来る。尚、本発明において上記の理由から形成する
画像は、予め鏡面関係にある画像として形成するのが好
ましい。The decorative method of the present invention using a film on which an image as described above is applied is such that the image surface of the film is pasted to the article to be decorated, and the transparent film as the base material remains as it is by such a method. It can be used as a protective layer for images. In the present invention, it is preferable that the image formed for the above-mentioned reason is formed as an image having a mirror surface relationship in advance.

本発明の装飾方法は、以上の通り、特定の被熱転写シ
ートを使用し、且つ画像を反転させて貼着する以外は、
その画像形成方法や被装飾物品に対する貼着方法はいず
れも従来公知の方法でよく、又、本発明の装飾方法の対
象となる被装飾物品もその材質、形状等、特に限定され
ず、例えば、カートン、容器、バッグ類、カセットケー
ス、カセットハーフ、フロッピーケース、包装紙等のパ
ッケージ；株券、小切手、手形、証券、証書、通帳類、
乗車券、車馬券、印紙、切手、鑑賞券等の金券類；キャ
ッシュカード、クレジットカード、メンバーズカード、
グリーティングカード、葉書、名刺、ICカード等のカー
ド類；その他、帳票類、封筒、タグ、シオリ、カレンダ
ー、ポスター、パンフレット、パスポート、POP用品、
コースター、ディスプレイ、ネームプレート、キーボー
ド、化粧品、装身具（時計、ライター）、文具類、建
材、ラジオ、テレビ、スピーカー、電卓、自動車のメー
ターパネル、エンブレム、キー、衣類、履物、装置類、
OA機器等、いずれの材質或いは形状のものでもよい。As described above, the decoration method of the present invention uses the specific heat-transferable sheet, and inverts the image and attaches it.
The image forming method and the sticking method for the article to be decorated may be any conventionally known method, and the article to be decorated which is a target of the decoration method of the present invention is not particularly limited in its material, shape, etc., for example, Packages such as cartons, containers, bags, cassette cases, cassette halves, floppy cases, wrapping paper; stock certificates, checks, bills, securities, certificates, passbooks,
Tickets, wagon tickets, stamps, stamps, appreciation tickets, etc .; cash cards, credit cards, members' cards,
Cards such as greeting cards, postcards, business cards, IC cards; other forms, envelopes, tags, Shiori, calendars, posters, brochures, passports, POP supplies,
Coasters, displays, name plates, keyboards, cosmetics, accessories (clocks, lighters), stationery, building materials, radios, TVs, speakers, calculators, car instrument panels, emblems, keys, clothing, footwear, devices,
Any material or shape such as OA equipment may be used.

（実施例） 次に実施例を挙げて本発明を更に具体的に説明する。
尚、文中、部又は％とあるのは特に断りにない限り重量
基準である。(Example) Next, an Example is given and this invention is demonstrated still more concretely.
In the text, "part" or "%" is based on weight unless otherwise specified.

実施例１ 基材としてポリエステルフイルム（厚み６μｍ）を用
い、その片面にポリエステル樹脂系プライマーを塗布及
び乾燥し、更にその上に下記組成の受像層形成用インキ
を用い、乾燥後重量が7g/m2となる様に塗布及び乾燥し
た。Example 1 A polyester film (thickness 6 μm) was used as a substrate, a polyester resin-based primer was applied to one side of the substrate and dried, and an image-receiving layer-forming ink having the following composition was further applied thereon, and the weight after drying was 7 g / m 2. It was applied and dried so as to be 2 .

受像層形成用インキ： ポリエステル樹脂（東洋紡製、バイロン200） 100部 アミノ変性シリコーン（信越化学工業製、KF−393） ５
部 エポキシ変性シリコーン（信越化学工業製、Ｘ−22−34
3） ５部 溶剤（メチルエチルケトン／トルエン／シクロヘキサノ
ン＝4/2/2） 900部 上記インキを塗布及び乾燥後、１日放置し、その後10
0℃の温度で30分間加熱し、シリコーンを表面にブリー
ドさせ、表面に硬化したシリコーン層を有する受像層と
した。Ink for forming image receiving layer: 100 parts polyester resin (manufactured by Toyobo, Byron 200) Amino-modified silicone (manufactured by Shin-Etsu Chemical Co., Ltd., KF-393) 5
Part Epoxy modified silicone (X-22-34 manufactured by Shin-Etsu Chemical Co., Ltd.
3) 5 parts Solvent (methyl ethyl ketone / toluene / cyclohexanone = 4/2/2) 900 parts After applying and drying the above ink, let it stand for 1 day, then 10
It was heated at a temperature of 0 ° C. for 30 minutes to cause silicone to bleed on the surface to form an image receiving layer having a cured silicone layer on the surface.

得られた受像層の上に、シアンの昇華性染料（分子量
は250以上）をバインダー樹脂で担持させた昇華転写フ
イルムを重ね、顔写真を色分解して得たシアン成分の電
気信号に連結したサーマルヘッドで熱エネルギーを付与
し、シアン画像を得た。次いで、マゼンタの昇華性染料
（分子量は250以上）を用いた昇華転写フイルム及びイ
エローの昇華性染料（分子量は250以上）を用いた昇華
転写フイルムにより同様にして昇華転写を行い、フルカ
ラーの顔写真とその他の文字、図形からなる表示画像を
形成した。A sublimation transfer film carrying a cyan sublimable dye (having a molecular weight of 250 or more) with a binder resin is superposed on the obtained image receiving layer, and connected to an electrical signal of a cyan component obtained by color separation of a face photograph. Thermal energy was applied by a thermal head to obtain a cyan image. Next, sublimation transfer is performed in the same manner using a sublimation transfer film using a magenta sublimation dye (molecular weight is 250 or more) and a sublimation transfer film using a yellow sublimation dye (molecular weight is 250 or more), and a full-color face photograph is obtained. And a display image composed of other characters and figures.

表示画像の形成されたフイルムの受像層側を、厚さ10
0μｍの白色不透明の硬質塩化ビニル樹脂シートからな
るカード基体上に重ねて200℃の熱ローラーで圧着し、
表示画像を有する受像層が貼合されたカードを得た。The image receiving layer side of the film on which the display image is formed is
Overlaid on a card substrate consisting of a 0 μm white opaque hard vinyl chloride resin sheet and pressure-bonded with a 200 ° C. heat roller,
A card to which an image receiving layer having a display image was attached was obtained.

このカードの表面は、全体的に平滑であり、画像部分
に何ら盛り上がりもなかった。更にこのカードの画像は
40℃の雰囲気に３ケ月間保持した促進試験においても、
画像の乱れや層間剥離は全く生じなかった。又、カーボ
ンアーク灯によるJISの耐光試験をしたところ、懸架はJ
IS 4〜５級であり、良好な性能を示した。表面の引っ掻
き等についても良好な耐久性を示した。The surface of this card was entirely smooth and there was no bulge in the image portion. Furthermore, the image of this card
Even in an accelerated test that was kept in an atmosphere of 40 ° C for 3 months,
No image distortion or delamination occurred. Also, a JIS light resistance test using a carbon arc lamp showed that the suspension was J
The grade was IS 4 to 5, and showed good performance. It also showed good durability against scratches on the surface.

実施例２ 実施例１において、顔写真画像を形成した被熱転写シ
ートの画像面にポリエステル系接着剤を塗布し、これを
電話機の曲面に貼着したところ、画像は電話機の曲面に
十分に追従し、曲面と一体化し、シールの様な貼着感を
与えず、直接画像を印刷した如き視感を与えた。Example 2 In Example 1, a polyester-based adhesive was applied to the image surface of the heat transfer sheet on which a facial photograph image was formed, and the polyester adhesive was attached to the curved surface of the telephone. The image sufficiently follows the curved surface of the telephone. It was integrated with a curved surface and gave a feeling as if an image was printed directly without giving a sticking feeling like a sticker.

実施例３ 実施例１における画像を形成した被熱転写シートの画
像面に、厚さ１μｍのポリアミド系粘着剤層を形成し、
これをガラス製コップの外面に貼着したところ、貼着感
を与えず、あたかも直接印刷した如き視感を与えた。Example 3 A polyamide-based pressure-sensitive adhesive layer having a thickness of 1 μm was formed on the image side of the heat-transferred sheet on which the image was formed in Example 1.
When this was stuck to the outer surface of a glass cup, it did not give a feeling of sticking and gave a feeling as if it was printed directly.

（発明の効果） 以上の如き本発明の物品の装飾方法によれば、従来
は、画像の形成及び付与が不可能或いは困難であった立
体成形物、曲面或いは複雑な凹凸形状等の表面を有する
物品、更にはこれらの物品の材質に拘らず、昇華性染料
により形成された画像を自由に付与することが出来る。(Effects of the Invention) According to the method for decorating an article of the present invention as described above, it has a surface such as a three-dimensional molded article, a curved surface or a complicated uneven shape, which has heretofore been impossible or difficult to form and impart an image. An image formed by a sublimable dye can be freely imparted regardless of the article and the material of the article.

しかも本発明によれば、従来の所謂絵付シールとは異
なり、本発明による画像を有するフイルムは薄いもので
ある為、被装飾物品に貼着しても、それらが十分に一体
化して、貼着感を与えず、優れた美観、機能及び耐久性
を有する。Further, according to the present invention, unlike the conventional so-called picture stickers, the film having the image according to the present invention is thin, so that even when the film is stuck to the article to be decorated, they are sufficiently integrated and stuck. It does not give a feeling and has excellent aesthetics, function and durability.

【図面の簡単な説明】[Brief description of drawings]

第１〜３図は、本発明で使用する被熱転写シートの断面
を図解的に示す図であり、第４図は、熱転写シートによ
る画像の形成を図解的に示す図であり、第５図は、物品
の装飾状態を図解的に示す図である。 1:透明フイルム 2:受像層 3:離型層 4:中間層 5:画像 6:接着剤 10:被熱転写シート 20:熱転写シート 21:染料担持層 30:被装飾物品1 to 3 are diagrams schematically showing a cross section of a heat transfer sheet used in the present invention, FIG. 4 is a diagram schematically showing formation of an image by the heat transfer sheet, and FIG. It is a figure which shows the decoration state of an article typically. 1: Transparent film 2: Image-receiving layer 3: Release layer 4: Intermediate layer 5: Image 6: Adhesive 10: Thermal transfer sheet 20: Thermal transfer sheet 21: Dye carrying layer 30: Decorative article

Claims (3)

(57)【特許請求の範囲】(57) [Claims] 【請求項１】昇華性染料層を全面に有する熱転写シート
の染料層面を、透明フイルムの一方の面に設けられた透
明受像層からなる被熱転写シートの受像層面に対向させ
て重ね合わせ、いずれかの側からサーマルヘッドによ
り、画像信号に従って熱エネルギーを付与することによ
り、上記受像層に昇華性染料からなる所望の画像を形成
する工程、及び上記画像形成された被熱転写シートの画
像面を被装飾物品に対向させて被熱転写シート全体を貼
着する工程とを含むことを特徴とする物品の装飾方法。1. A thermal transfer sheet having a sublimable dye layer over its entire surface, the dye layer surface of which is opposed to and superposed on an image receiving layer surface of a heat transferable sheet comprising a transparent image receiving layer provided on one surface of a transparent film. A step of forming a desired image of a sublimable dye on the image receiving layer by applying heat energy according to an image signal from the side of the thermal head, and the image surface of the image-formed heat-transferred sheet is decorated. A step of adhering the entire heat-transferable sheet so as to face the article, and a method for decorating the article. 【請求項２】被装飾物品が、カード類である特許請求の
範囲第（１）項に記載の物品の装飾方法。2. The method for decorating an article according to claim 1, wherein the article to be decorated is a card or the like. 【請求項３】被装飾物品が、容器類である特許請求の範
囲第（１）項に記載の物品の装飾方法。3. The method for decorating an article according to claim 1, wherein the article to be decorated is a container.
JP61081989A 1986-04-11 1986-04-11 How to decorate items Expired - Lifetime JP2551408B2 (en)