JP3023109B2 - Heat transfer sheet - Google Patents
Heat transfer sheetInfo
- Publication number
- JP3023109B2 JP3023109B2 JP63065238A JP6523888A JP3023109B2 JP 3023109 B2 JP3023109 B2 JP 3023109B2 JP 63065238 A JP63065238 A JP 63065238A JP 6523888 A JP6523888 A JP 6523888A JP 3023109 B2 JP3023109 B2 JP 3023109B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- receiving layer
- image receiving
- molecular weight
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、熱転写シートと組み合わせて用いることに
より熱転写画像を形成することのできる被熱転写シート
に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] The present invention relates to a heat transfer sheet which can form a heat transfer image when used in combination with a heat transfer sheet.
被熱転写シートは、その受像層面を熱移行性染料を含
む色材層を有する転写シートの該色材層と対向させて重
ね合わせ、熱転写シートの背面から画像情報に応じて電
気信号により制御されるサーマルヘッド等の加熱手段に
て熱転写シートを加熱することによって、色材層中の染
料を受像層に移行させて転写画像を形成することができ
る。The heat-receiving sheet is superposed with its image-receiving layer surface facing the color material layer of a transfer sheet having a color material layer containing a heat-migrating dye, and is controlled by an electric signal according to image information from the back of the heat transfer sheet. By heating the thermal transfer sheet with a heating means such as a thermal head, the dye in the color material layer can be transferred to the image receiving layer to form a transferred image.
しかしながら、従来の被熱転写シートは熱転写記録に
より転写画像を形成する際に良好な画像感度を有し、し
かも画像形成後においては優れた画像安定性を有すると
いう、この両特性を同時に併せ持つ充分なものが存在し
なかった。即ち、従来の被熱転写シートは例えば、画像
安定性には優れているものの画像記録時の感度が不十分
なために再現性良好な転写画像を所望通りに記録形成す
ることができなかったり、或いは画像感度は良好である
ものの画像形成後に画像が滲んだりボケたりし、また受
像層に染着した染料が他へ再移行（再転写）して接触物
の相手側を汚染してしまい、また積載保管等においてブ
ロッキングが生じる等の問題点があった。However, conventional thermal transfer sheets have good image sensitivity when forming a transferred image by thermal transfer recording, and have excellent image stability after image formation. Was not present. That is, the conventional heat-transferable sheet, for example, is not excellent in image stability, but cannot record and form a transfer image with good reproducibility as desired due to insufficient sensitivity at the time of image recording, or Although the image sensitivity is good, the image bleeds or blurs after image formation, and the dye dyed on the image receiving layer re-migrate (re-transfer) to the other side, thereby contaminating the other side of the contacted object, and also loading. There were problems such as blocking during storage and the like.
本発明は上記課題に鑑みなされたもので、良好な画像
感度及び優れた画像安定性の両特性を兼備する被熱転写
シートを提供することを目的とするものである。The present invention has been made in view of the above problems, and an object of the present invention is to provide a heat transfer sheet having both characteristics of good image sensitivity and excellent image stability.
即ち本発明は、〔１〕シート基材と、該基材上に形成
され且つ熱転写シートから加熱により移行する染料を受
容する受像層からなる被熱転写シートにおいて、上記受
像層が高分子量受像層形成用樹脂と低分子量受像層形成
用樹脂を併用して形成されてなり、高分子量受像層形成
用樹脂と低分子量受像層形成用樹脂の混合割合が、高分
子量受像層形成用樹脂／低分子量受像層形成用樹脂＝80
/20〜20/80であることを特徴とする被熱転写シート、但
し、高分子量受像層形成用樹脂の高分子量とは、ポリエ
ステルは15,000以上、ポリスチレンは20,000以上、ポリ
アクリル酸は200,000以上、ポリ塩化ビニルは100,000以
上、ポリ酢酸ビニルは100,000以上、ポリアミドは15,00
0以上であり、低分子量受像層形成用樹脂の低分子量と
は、ポリエステルは5,000以下、ポリスチレンは10,000
以下、ポリアクリル酸は100,000以下、ポリ塩化ビニル
は30,000以下、ポリ酢酸ビニルは50,000以下、ポリアミ
ドは5,000以下であり、上記分子量は重量平均分子量で
表したものである、〔２〕シート基材と受像層の間に中
間層を設けた上記〔１〕記載の被熱転写シート、〔３〕
受像層表面に離型剤層を設けた上記〔１〕又は〔２〕記
載の被熱転写シート、を要旨とするものである。That is, the present invention relates to [1] a heat transfer sheet comprising a sheet base and an image receiving layer formed on the base and receiving a dye transferred from the heat transfer sheet by heating, wherein the image receiving layer is formed of a high molecular weight image receiving layer. Resin and the resin for forming the low molecular weight image receiving layer are formed in combination, and the mixing ratio of the resin for forming the high molecular weight image receiving layer and the resin for forming the low molecular weight image receiving layer is such that the resin for forming the high molecular weight image receiving layer / the low molecular weight image receiving layer is used. Layer forming resin = 80
/ 20 ~ 20/80, wherein the high molecular weight of the resin for forming a high molecular weight image-receiving layer is 15,000 or more for polyester, 20,000 or more for polystyrene, 200,000 or more for polyacrylic acid, poly 100,000 or more for polyvinyl chloride, 100,000 or more for polyvinyl acetate, 15,000 for polyamide
0 or more, and the low molecular weight of the resin for forming a low molecular weight image receiving layer, polyester is 5,000 or less, polystyrene is 10,000
Hereinafter, polyacrylic acid is 100,000 or less, polyvinyl chloride is 30,000 or less, polyvinyl acetate is 50,000 or less, polyamide is 5,000 or less, and the molecular weight is represented by weight average molecular weight. The heat transfer sheet according to the above [1], wherein an intermediate layer is provided between the image receiving layers, [3].
The heat transfer sheet according to the above [1] or [2], wherein a release agent layer is provided on the surface of the image receiving layer.
本発明において使用されるシート基材としてはプラス
チックフィルム、合成紙、セルロース繊維紙等が挙げら
れる。プラスチックフィルムとしてはポリエステル、ポ
リ塩化ビニル、ポリプロピレン、ポリエチレン、ポリカ
ーボネート、ポリアミド等の樹脂からなるフィルムが使
用でき、またこれらのフィルムに充填剤を加えて製膜し
た白色フィルムや微細な発泡を行わせた発泡フィルムも
使用できる。合成紙としては、ポリオレフィン樹脂若し
くはその他の合成樹脂を樹脂成分として、これに無機質
充填剤などを添加して混合し、押出して製造したもの、
又はポリスチレン樹脂、ポリエステル樹脂、ポリオレフ
ィン樹脂等のフィルムの表面に体質顔料を塗工して製造
したもの等が用いられる。セルロース繊維紙としては、
上質紙、コート紙、キャストコート紙、合成ゴムラテッ
クス又は合成樹脂エマルジョン含浸紙等を使用すること
ができる。Examples of the sheet substrate used in the present invention include a plastic film, synthetic paper, cellulose fiber paper and the like. As a plastic film, a film made of a resin such as polyester, polyvinyl chloride, polypropylene, polyethylene, polycarbonate, or polyamide can be used, and a white film or fine foam formed by adding a filler to these films. Foamed films can also be used. As synthetic paper, a polyolefin resin or other synthetic resin as a resin component, to which inorganic fillers and the like are added, mixed and extruded,
Alternatively, a film produced by applying an extender to the surface of a film of a polystyrene resin, a polyester resin, a polyolefin resin, or the like is used. As cellulose fiber paper,
Fine paper, coated paper, cast-coated paper, synthetic rubber latex or synthetic resin emulsion impregnated paper can be used.
また、シート基材として透明性を要する用途（オーバ
ーヘッドプロジェクター用等）又はカード、布等の物品
に熱で転写させる用途の場合には、透明なプラスチック
フィルムの受像層と反対側面に粘着剤などを塗布した支
持体又は遮蔽性付与材として、白色フィルム、発泡フィ
ルム、合成又はセルロース繊維紙を貼合わせることもで
きる。更にプラスチックフィルムどうし、合成紙どうし
又はセルロース繊維紙どうしを接着剤により貼合わせた
シート基材を使用できる。For applications requiring transparency as a sheet substrate (such as for an overhead projector) or applications where heat is transferred to an article such as a card or cloth, use an adhesive or the like on the side opposite to the image receiving layer of a transparent plastic film. A white film, a foamed film, a synthetic or cellulose fiber paper may be attached as the applied support or the material for imparting shielding properties. Further, a sheet substrate in which plastic films, synthetic papers, or cellulose fiber papers are bonded together with an adhesive can be used.
受像層は、熱転写記録の際に熱転写シートから移行し
てくる染料を受容することができる受像層形成用樹脂に
て構成され、該染料が染着されて転写画像が形成される
ものである。上記受像層形成用樹脂はこの種受像層を形
成するために使用されている樹脂を用いることができ
る。具体的には以下のような合成樹脂を単独又は２種以
上の混合により使用できる。The image receiving layer is formed of an image receiving layer forming resin capable of receiving a dye transferred from a thermal transfer sheet during thermal transfer recording, and the dye is dyed to form a transferred image. As the resin for forming the image receiving layer, a resin used for forming this kind of image receiving layer can be used. Specifically, the following synthetic resins can be used alone or in combination of two or more.
（ａ） エステル結合を有するもの。(A) Those having an ester bond.
ポリエステル樹脂、ポリアクリル酸エステル樹脂、ポ
リカーボネート樹脂、ポリ酢酸ビニル樹脂、スチレンア
クリレート樹脂、ビニルトルエンアクリレート樹脂な
ど。Polyester resin, polyacrylate resin, polycarbonate resin, polyvinyl acetate resin, styrene acrylate resin, vinyl toluene acrylate resin, etc.
（ｂ） ウレタン結合を有するもの。(B) Those having a urethane bond.
ポリウレタン樹脂など。 Polyurethane resin etc.
（ｃ） アミド結合を有するもの。(C) Those having an amide bond.
ポリアミド樹脂など。 Polyamide resin etc.
（ｄ） 尿素結合を有するもの。(D) Those having a urea bond.
尿素樹脂など。 Urea resin and the like.
（ｅ） その他極性の高い結合を有するもの。(E) Others having a highly polar bond.
ポリカプロラクトン樹脂、スチレン−無水マレイン酸
樹脂、ポリ塩化ビニル樹脂、ポリアクリロニトリル樹脂
など。Polycaprolactone resin, styrene-maleic anhydride resin, polyvinyl chloride resin, polyacrylonitrile resin and the like.
その他にも、受像層形成用樹脂として飽和ポリエステ
ルと塩化ビニル／酢酸ビニル共重合体が用いられる。塩
化ビニル／酢酸ビニル共重合体は塩化ビニル成分含有量
85〜97重量％で、重合度200〜800程度のものが好まし
い。塩化ビニル／酢酸ビニル共重合体は必ずしも塩化ビ
ニル成分と酢酸ビニル成分のみの共重合体である場合に
限らず、ビニルアルコール成分、マレイン酸成分等を含
むものであってもよい。In addition, a saturated polyester and a vinyl chloride / vinyl acetate copolymer are used as the resin for forming the image receiving layer. Vinyl chloride / vinyl acetate copolymer contains vinyl chloride component
Those having 85 to 97% by weight and a degree of polymerization of about 200 to 800 are preferred. The vinyl chloride / vinyl acetate copolymer is not necessarily limited to a copolymer of only a vinyl chloride component and a vinyl acetate component, but may include a vinyl alcohol component, a maleic acid component, and the like.
本発明における受像層は、上述の如き受像層形成用樹
脂のうち、高分子量受像層形成用樹脂と低分子量受像層
形成用樹脂を併用して形成される。ここで、高分子量受
像層形成用樹脂とは比較的に高分子量からなり、転写画
像の染料に対する保持性、保存性に優れた受像層形成が
可能な受像形成用樹脂をいい、一方、低分子量受像層形
成用樹脂とは比較的に低分子量からなり、染料の染着性
に優れた受像層形成が可能な受像層形成用樹脂をいう。
従って、本発明においてはこの高分子量受像層形成用樹
脂と低分子量受像層形成用樹脂を適宜ブレンドして受像
層を形成することにより、染料染着性及び染料の保持
性、保存性に優れた受像層が得られる。The image receiving layer in the present invention is formed by using a resin for forming a high molecular weight image receiving layer and a resin for forming a low molecular weight image receiving layer among the resins for forming an image receiving layer as described above. Here, the high molecular weight image-receiving layer forming resin is relatively high in molecular weight, and refers to an image-receiving resin capable of forming an image-receiving layer with excellent retention and transferability of a transferred image to a dye. The resin for forming an image receiving layer is a resin having a relatively low molecular weight and capable of forming an image receiving layer having excellent dyeing properties.
Therefore, in the present invention, by appropriately blending the resin for forming a high-molecular-weight image-receiving layer and the resin for forming a low-molecular-weight image-receiving layer to form an image-receiving layer, the dye-dyeing property and the dye-holding property and storage stability are excellent. An image receiving layer is obtained.
上記高分子量受像層形成用樹脂と低分子量受像層形成
用樹脂は、互いに同種の樹脂であっても或いは異種の樹
脂であってもよい。また両分子量の樹脂はそれぞれ２種
以上の分子量のものを使用しても、又、それぞれ２種以
上の樹脂材質のものを使用してもよい。また両分子量か
らなる樹脂の混合割合は、 高分子量受像層形成用樹脂／低分子量受像層形成用樹
脂＝80/20〜20/80、 である。この混合割合の範囲を外れる場合は、染料の
染着性と保持、保存性のどちらか一方の特性に劣った受
像層となる。The resin for forming a high molecular weight image receiving layer and the resin for forming a low molecular weight image receiving layer may be the same type of resin or different types of resins. The resins having both molecular weights may use two or more kinds of molecular weights, or may use two or more kinds of resin materials. The mixing ratio of the resins having both molecular weights is as follows: high molecular weight image receiving layer forming resin / low molecular weight image receiving layer forming resin = 80/20 to 20/80. If the mixing ratio is out of this range, the resulting image receiving layer is inferior in either one of the dyeing properties and the retention and storage properties.
本発明において使用される受像層形成用樹脂における
“高分子量”と“低分子量”の数値は、その樹脂材質に
より異なるものであり、それらを考慮しながら両分子量
の受像層形成用樹脂を適宜選択して併用する。各受像層
形成用樹脂における高分子量と低分子量の具体的数値を
下記に示す。尚、この分子量数値は重量平均分子量で表
したものである。The numerical values of “high molecular weight” and “low molecular weight” in the resin for forming an image receiving layer used in the present invention are different depending on the resin material, and the resins for forming the image receiving layer having both molecular weights are appropriately selected in consideration of these. Use together. Specific numerical values of the high molecular weight and the low molecular weight of each resin for forming an image receiving layer are shown below. In addition, this molecular weight numerical value is represented by the weight average molecular weight.
受像層の形成に当たっては、高分子量及び低分子量の
受像層形成用樹脂を適宜混合したものを溶剤等にて調整
した受像層形成用インキ組成物を従来周知の塗布手段に
てシート基材上に塗布し、乾燥することにより形成す
る。受像層の厚さは１〜50μｍである。 In forming the image receiving layer, an ink composition for forming an image receiving layer prepared by appropriately mixing a high molecular weight and a low molecular weight resin for forming an image receiving layer with a solvent or the like is applied onto a sheet substrate by a conventionally known coating means. It is formed by coating and drying. The thickness of the image receiving layer is 1 to 50 μm.
本発明の被熱転写シートはシート基材と受像層との間
にクッション層、多孔層等からなる中間層が設けられ、
この中間層を設けるとノイズが少なく画像情報に対応し
た画像を再現性良く転写記録することができる。中間層
を構成する材質としては例えばウレタン樹脂、アクリル
樹脂、エチレン系樹脂、ブタジエンラバー、エポキシ樹
脂等が挙げられる。中間層の厚さは２〜20μｍ程度が好
ましい。The heat transfer sheet of the present invention is provided with an intermediate layer comprising a cushion layer, a porous layer, and the like between the sheet substrate and the image receiving layer,
By providing this intermediate layer, an image corresponding to image information with little noise can be transferred and recorded with good reproducibility. Examples of the material constituting the intermediate layer include urethane resin, acrylic resin, ethylene-based resin, butadiene rubber, and epoxy resin. The thickness of the intermediate layer is preferably about 2 to 20 μm.
また本発明の被熱転写シートは、熱転写シートとの剥
離性を向上せしめるために受像層中に離型剤を含有せし
めることができる。離型剤としてはポリエチレンワック
ス、アミドワックス、テフロンパウダー等の固型ワック
ス類；弗素系、燐酸エステル系の界面活性剤；シリコー
ンオイル等が挙げられるがシリコーンオイルが好まし
い。Further, the heat transfer sheet of the present invention can contain a release agent in the image receiving layer in order to improve the releasability from the heat transfer sheet. Examples of the release agent include solid waxes such as polyethylene wax, amide wax and Teflon powder; fluorine-based and phosphoric acid ester-based surfactants; silicone oil; and silicone oil is preferred.
上記シリコーンオイルとしては油状のものも用いるこ
とができるが、硬化型のものが好ましい。硬化型のシリ
コーンオイルとしては、反応硬化型、光硬化型、触媒硬
化型等が挙げられるが、反応硬化型のシリコーンオイル
が特に好ましい。反応硬化型シリコーンオイルとして
は、アミノ変性シリコーンオイルとエポキシ変性シリコ
ーンオイルとを反応硬化させたものが好ましく、アミノ
変性シリコーンオイルとしてはKF-393（信越化学工業
（株）製）等が挙げられ、エポキシ変性シリコーンオイ
ルとしては、X-22-343（信越化学工業（株）製）等が挙
げられる。また触媒硬化型あるいは光硬化型シリコーン
オイルとしてはKS-705F-PS（触媒硬化型シリコーンオイ
ル、信越化学工業（株）製）、KS-720（光硬化型シリコ
ーンオイル、信越化学工業（株）製）等が挙げられる。
これらの硬化型シリコーンオイルの添加量は受像層を構
成する樹脂100重量部に対し0.5〜30重量部程度が好まし
い。As the silicone oil, an oily oil can be used, but a curable oil is preferable. Examples of the curable silicone oil include a reaction curable type, a photocurable type, and a catalyst curable type, and a reaction curable type silicone oil is particularly preferable. As the reaction-curable silicone oil, those obtained by reacting and curing an amino-modified silicone oil and an epoxy-modified silicone oil are preferable. Examples of the amino-modified silicone oil include KF-393 (manufactured by Shin-Etsu Chemical Co., Ltd.). Examples of the epoxy-modified silicone oil include X-22-343 (manufactured by Shin-Etsu Chemical Co., Ltd.). KS-705F-PS (catalyst-curable silicone oil, manufactured by Shin-Etsu Chemical Co., Ltd.) and KS-720 (photo-curable silicone oil, manufactured by Shin-Etsu Chemical Co., Ltd.) ) And the like.
The addition amount of these curable silicone oils is preferably about 0.5 to 30 parts by weight based on 100 parts by weight of the resin constituting the image receiving layer.
また、受容層の表面に上記離型剤を適当な溶媒に溶解
或いは分散させて塗布した後、乾燥させる等によって離
型剤層を設けることもできる。離型剤層を構成する離型
剤としては前記したアミノ変性シリコーンオイルとエポ
キシ変性シリコーンオイルとの反応硬化物が特に好まし
い。離型剤層の厚さは0.01〜５μｍ、特に0.05〜２μｍ
が好ましい。Further, the release agent layer may be provided by dissolving or dispersing the release agent in an appropriate solvent on the surface of the receiving layer, applying the solution, followed by drying. As the release agent constituting the release agent layer, the above-mentioned cured product of the amino-modified silicone oil and the epoxy-modified silicone oil is particularly preferable. The thickness of the release agent layer is 0.01 to 5 μm, particularly 0.05 to 2 μm
Is preferred.
尚、本発明の被熱転写シートはシート基材の裏面に滑
性層を設けることができる。被熱転写シートは積み重ね
て１枚ずつ送り出して転写を行う場合があり、この場合
滑性層を設けるとシートどうしの滑りが円滑となり、１
枚ずつ正確に送り出すことができる。滑性層の材質とし
ては、メチルメタクリレート等のメタクリレート樹脂若
しくは対応するアクリレート樹脂、塩化ビニル−酢酸ビ
ニル共重合体等のビニル系樹脂等が挙げられる。The heat transfer sheet of the present invention may have a slip layer on the back surface of the sheet substrate. In some cases, the sheets to be transferred are stacked and sent out one by one to perform the transfer. In this case, if a slip layer is provided, the slip between the sheets becomes smoother.
It can be sent out one sheet at a time. Examples of the material of the lubricating layer include a methacrylate resin such as methyl methacrylate or a corresponding acrylate resin, and a vinyl resin such as a vinyl chloride-vinyl acetate copolymer.
また、被熱転写シートに帯電防止剤を含有せしめるこ
ともできる。帯電防止剤を含有せしめることにより、被
熱転写シートのほこりの付着を防止する効果がある。帯
電防止剤はシート基材或いは受像層中に含有せしめても
よいし、或いは帯電防止剤層としてシート基材裏面等に
設けることができるが、シート基材裏面に帯電防止層と
して設けることが好ましい。Further, an antistatic agent can be added to the heat transfer sheet. The inclusion of an antistatic agent has the effect of preventing dust from adhering to the heat transfer sheet. The antistatic agent may be contained in the sheet substrate or the image receiving layer, or may be provided as an antistatic agent layer on the back surface of the sheet substrate, but is preferably provided as an antistatic layer on the back surface of the sheet substrate. .
更に、被熱転写シートに検知マークを設けることも可
能である。検知マークは熱転写シートと被熱転写シート
との位置決めを行う際等に極めて便利であり、例えば光
電管検知装置により検知し得る検知マークをシート基材
裏面等に印刷等により設けることができる。Further, it is possible to provide a detection mark on the heat transfer sheet. The detection mark is extremely convenient when positioning the thermal transfer sheet and the heat transfer target sheet. For example, a detection mark that can be detected by a photoelectric tube detection device can be provided on the back surface of the sheet base by printing or the like.
以下、実施例を挙げて本発明を更に詳細に説明する。
尚、下記の“部”は重量部を示す。Hereinafter, the present invention will be described in more detail with reference to examples.
The following "parts" indicate parts by weight.
実施例 （被熱転写シートの作成） シート基材として厚み150μｍの合成紙（王子油化
製：ユポFPG-150）を用い、表面に下記組成の受像層形
成用インキ組成物をワイヤーバーコーティングにより乾
燥後の厚みが５μｍとなるように塗布して被熱転写シー
トを作成した。Example (Preparation of Thermal Transfer Sheet) Using a 150 μm-thick synthetic paper (manufactured by Oji Yuka: YUPO FPG-150) as a sheet base material, drying the ink composition for forming an image receiving layer having the following composition on the surface by wire bar coating. Thereafter, coating was performed so that the thickness became 5 μm, to prepare a heat transfer sheet.
受像層形成用インキ組成物 ・受像層形成用樹脂 ポリエステル樹脂（Mn＝約22,000） （荒川化学製:KA1039U18） …50部 ポリエステル樹脂（Mn＝約2,900） （荒川化学製:KA1078B） …50部 ・離型剤 アミノ変性シリコーンオイル …７部 （信越化学工業製:X-22-3050C） エポキシ変性シリコーンオイル …７部 （信越化学工業製:X-22-3000E） ・溶剤 メチルエチクケトン／トルエン＝1/1 …400部 （熱転写シートの作成） 支持体として片面にコロナ処理が施された厚さ６μｍ
のポリエチレンテレフタレートフィルム（東洋紡製:S-P
ET）を使用し、フィルムのコロナ処理面上に、下記組成
の色材層形成用塗料組成物をワイヤーバーコーティング
により、乾燥時の厚みが１μｍとなるよう塗布形成し、
背面にシリコーンオイル（信越シリコーン製:X-41・400
3A）をスポイトにて１、２滴垂らした後、全面に広げ背
面処理コートを行い熱転写シートとした。Ink composition for forming image receiving layer ・ Resin for forming image receiving layer Polyester resin (Mn = about 22,000) (Arakawa Chemical: KA1039U18) ... 50 parts Polyester resin (Mn = about 2,900) (Arakawa Chemical: KA1078B) ... 50 parts Release agent Amino-modified silicone oil ... 7 parts (Shin-Etsu Chemical: X-22-3050C) Epoxy-modified silicone oil ... 7 parts (Shin-Etsu Chemical: X-22-3000E) ・ Solvent Methyl ethyl ketone / toluene = 1/1… 400 parts (preparation of thermal transfer sheet) 6 μm thick with corona treatment on one side as support
Polyethylene terephthalate film (Toyobo: SP
Using ET), on the corona-treated surface of the film, a coating composition for forming a colorant layer having the following composition is applied by wire bar coating so as to have a dry thickness of 1 μm,
Silicone oil on the back (Shin-Etsu Silicone: X-41.400
After dropping one or two drops of 3A) with a dropper, it was spread over the entire surface and subjected to a backside treatment coating to obtain a thermal transfer sheet.
色材層形成用塗料組成物 分散染料 …４部 （日本化薬製：カヤセットブルー714） エチルヒドロキシエチルセルロース樹脂 （ハーキュレス製） …５部 メチルエチルトケン／トルエン …90部 ＝1/1 上記のようにして得られた被熱転写シートと熱転写シ
ートとを、色材層と受像層とが接するようにして重ね合
わせ、熱転写シートの支持体側からサーマルヘッドを使
用し、サーマルヘッドの出力1W/ドット、パルス幅0.3〜
0.45msec、ドット密度３ドット/mmの条件で印字を行
い、被熱転写シートの受像層に転写画像を形成した。Coloring material layer forming coating composition Disperse dye 4 parts (Nippon Kayaku: Kayaset Blue 714) Ethyl hydroxyethyl cellulose resin (Hercules) 5 parts Methyl ethyl token / toluene 90 parts = 1/1 As above The heat transfer sheet and the heat transfer sheet obtained in this manner are overlapped so that the color material layer and the image receiving layer are in contact with each other, and a thermal head is used from the support side of the heat transfer sheet, and the output of the thermal head is 1 W / dot, pulse. Width 0.3 ~
Printing was performed under the conditions of 0.45 msec and a dot density of 3 dots / mm, and a transfer image was formed on the image receiving layer of the heat transfer sheet.
上記印字による画像形成の感度はO.D値（光学反射濃
度）で従来の被熱転写シートのO.D値に比べて0.1〜0.3
向上した優れたものであることが確認できた。また、画
像をけいせいした被熱転写シートを積み重ね、60℃の温
度で24時間経過後のシート状態を調べたところ、ブロッ
キングは発生しなかった。The sensitivity of image formation by the above printing is 0.1 to 0.3 in OD value (optical reflection density) compared to the OD value of the conventional heat transfer sheet.
It was confirmed that it was improved and excellent. Further, when the heat transfer sheets having the images formed thereon were stacked and the state of the sheet after a lapse of 24 hours at a temperature of 60 ° C. was examined, no blocking occurred.
比較例１ 実施例の受像層形成用インキ組成物における受像層形
成用樹脂のうち、Mn＝22,000のポリエステル樹脂（荒川
化学製:KA1039U18）のみを100部使用した他は、実施例
と同様にして被熱転写シートを作成した。Comparative Example 1 In the same manner as in Example except that only 100 parts of a polyester resin having Mn = 22,000 (KA1039U18 manufactured by Arakawa Chemical Co., Ltd.) was used among the resin for forming an image receiving layer in the ink composition for forming an image receiving layer of Example. A heat transfer sheet was prepared.
得られた被熱転写シートを実施例と同様の熱転写シー
トを用いて画像形成を行った。Using the obtained thermal transfer sheet, an image was formed using the same thermal transfer sheet as in the example.
この被熱転写シートでは画像形成の感度が若干低くな
り、高濃度が必要な画像形成には不適当なものであっ
た。また実施例と同様の積み重ねを行ったところ、ブロ
ッキングは殆どなかった。With this heat transfer sheet, the sensitivity of image formation was slightly lowered, and was unsuitable for image formation requiring high density. When stacking was performed in the same manner as in the example, there was almost no blocking.
比較例２ 実施例の受像層形成用インキ組成物における受像層形
成用樹脂のうち、Mn＝2,900のポリエステル樹脂（荒川
化学製:KA1078B）のみを100部使用した他は、実施例と
同様にして被熱転写シートを作成した。Comparative Example 2 In the same manner as in Example except that only 100 parts of a polyester resin having Mn = 2,900 (Arakawa Chemical: KA1078B) was used among the resin for forming the image receiving layer in the ink composition for forming an image receiving layer of Example. A heat transfer sheet was prepared.
得られた被熱転写シートを実施例と同様の熱転写シー
トを用いて画像形成を行った。Using the obtained thermal transfer sheet, an image was formed using the same thermal transfer sheet as in the example.
この被熱転写シートでは、画像形成の感度のO.D値は
従来品と同等のものであったものの、実施例と同様の積
み重ねを行ったところ、ブロッキングが発生してしまっ
た。In this heat transfer sheet, although the OD value of the sensitivity of image formation was equivalent to that of the conventional product, blocking occurred when stacking was performed in the same manner as in the example.
以上説明したように、本発明被熱転写シートは受像層
を高分子量受像層形成用樹脂と低分子量受像層形成用樹
脂を併用して形成してなるため、優れた染料染着性及び
染料の保持、保存性の両特性を兼備したものとなり、そ
の結果、画像形成の感度に優れ。画像安定性に優れたも
のである。特に高分子量受像層形成用樹脂と低分子量受
像層形成用樹脂の混合割合が、高分子量受像層形成用樹
脂／低分子量受像層形成用樹脂＝80/20〜20/80であるた
め、受像層の染料の染着性と保持、保存性の両方の特性
に優れたものが得られ、どちらか一方が劣った受像層と
なるのを避けることができる。As described above, the heat-receiving sheet of the present invention is formed by using the resin for forming the high-molecular weight image-receiving layer and the resin for forming the low-molecular weight image-receiving layer in combination with the image-receiving layer. , Which has both characteristics of storage stability and, as a result, excellent image formation sensitivity. It has excellent image stability. In particular, the mixing ratio of the resin for forming the high molecular weight image receiving layer and the resin for forming the low molecular weight image receiving layer is such that the resin for forming the high molecular weight image receiving layer / the resin for forming the low molecular weight image receiving layer is 80/20 to 20/80. A dye excellent in both the dyeing property and the retention and preservation properties of the dye is obtained, and it is possible to avoid an image receiving layer in which one of them is inferior.
従って、本発明によれば画像形成において優れた感度
の画像形成を行うことができ、一方、画像形成後におい
ては画像の滲み、損傷等がなく、ブロッキングの発生等
の虞れもない。Therefore, according to the present invention, it is possible to form an image with excellent sensitivity in image formation. On the other hand, after image formation, there is no bleeding or damage of the image, and there is no risk of occurrence of blocking.
また本発明によれば、シート基材と受像層の間に中間
層を設けることにより、ノイズが少ない画像を再現性よ
く転写記録することができる。更に、受像層表面に離型
剤層を設けることにより、特に熱転写記録時における熱
転写シートとの剥離性を向上せしめることができる。Further, according to the invention, by providing an intermediate layer between the sheet substrate and the image receiving layer, it is possible to transfer and record an image with less noise with good reproducibility. Further, by providing a release agent layer on the surface of the image receiving layer, it is possible to improve the releasability from the thermal transfer sheet particularly during thermal transfer recording.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭62−294595（ＪＰ，Ａ) 特開 昭62−189195（ＪＰ，Ａ) 特開 昭62−240588（ＪＰ，Ａ) 特開 昭63−7971（ＪＰ，Ａ) 特開 昭63−7972（ＪＰ，Ａ) 特開 昭63−7973（ＪＰ，Ａ) ──────────────────────────────────────────────────続 き Continuation of front page (56) References JP-A-62-294595 (JP, A) JP-A-62-189195 (JP, A) JP-A-62-240588 (JP, A) JP-A-63-294 7971 (JP, A) JP-A-63-7792 (JP, A) JP-A-63-7793 (JP, A)
Claims (3)
転写シートから加熱により移行する染料を受容する受像
層からなる被熱転写シートにおいて、上記受像層が高分
子量受像層形成用樹脂と低分子量受像層形成用樹脂を併
用して形成されてなり、高分子量受像層形成用樹脂と低
分子量受像層形成用樹脂の混合割合が、高分子量受像層
形成用樹脂／低分子量受像層形成用樹脂＝80/20〜20/80
であることを特徴とする被熱転写シート。但し、高分子
量受像層形成用樹脂の高分子量とは、ポリエステルは1
5,000以上、ポリスチレンは20,000以上、ポリアクリル
酸は200,000以上、ポリ塩化ビニルは100,000以上、ポリ
酢酸ビニルは100,000以上、ポリアミドは15,000以上で
あり、低分子量受像層形成用樹脂の低分子量とは、ポリ
エステルは5,000以下、ポリスチレンは10,000以下、ポ
リアクリル酸は100,000以下、ポリ塩化ビニルは30,000
以下、ポリ酢酸ビニルは50,000以下、ポリアミドは5,00
0以下であり、上記分子量は重量平均分子量で表したも
のである。1. A heat transfer sheet comprising a sheet substrate and an image receiving layer formed on the substrate and receiving a dye transferred from the thermal transfer sheet by heating, wherein the image receiving layer comprises a resin for forming a high molecular weight image receiving layer. The resin for forming a low molecular weight image receiving layer is formed in combination with the resin for forming a high molecular weight image receiving layer and the resin for forming a low molecular weight image receiving layer. Resin = 80/20-20/80
A heat transfer sheet, characterized in that: However, the high molecular weight of the resin for forming a high molecular weight image receiving layer means that polyester is 1
5,000 or more, polystyrene is 20,000 or more, polyacrylic acid is 200,000 or more, polyvinyl chloride is 100,000 or more, polyvinyl acetate is 100,000 or more, polyamide is 15,000 or more.The low molecular weight of the resin for forming the low molecular weight image receiving layer is polyester. 5,000 or less, polystyrene 10,000 or less, polyacrylic acid 100,000 or less, polyvinyl chloride 30,000
Below, polyvinyl acetate is 50,000 or less, polyamide is 5,000
0 or less, and the molecular weight is represented by a weight average molecular weight.
請求項１記載の被熱転写シート。2. The heat transfer sheet according to claim 1, wherein an intermediate layer is provided between the sheet substrate and the image receiving layer.
は２記載の被熱転写シート。3. The heat transfer sheet according to claim 1, wherein a release agent layer is provided on the surface of the image receiving layer.