JP2547132B2 - Method for manufacturing pottery with flow pattern - Google Patents
Method for manufacturing pottery with flow patternInfo
- Publication number
- JP2547132B2 JP2547132B2 JP3228147A JP22814791A JP2547132B2 JP 2547132 B2 JP2547132 B2 JP 2547132B2 JP 3228147 A JP3228147 A JP 3228147A JP 22814791 A JP22814791 A JP 22814791A JP 2547132 B2 JP2547132 B2 JP 2547132B2
- Authority
- JP
- Japan
- Prior art keywords
- raw material
- sheet material
- liquid
- container
- decorative raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、タイル，屋根瓦などの
建材をはじめ、便器，洗面器などの衛生陶器、更には食
器、置物その他、焼物類全般を対象として、その表面に
大理石などに見られる流れ模様を具備させることができ
るようにした、焼物類の製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention is applied to building materials such as tiles and roof tiles, sanitary ware such as toilet bowls and washbasins, and tableware, figurines and other pottery, and to marble etc. The present invention relates to a method for producing a pottery product which can be provided with a visible flow pattern.
【０００２】[0002]
【従来の技術】従来、大理石製に見せ掛けた焼物類を製
造するには、その成形体（焼成前のもの）にボタ掛けに
よって施釉する手順を、発色が異なる複数種の釉薬につ
きそれぞれ繰り返し、これを焼成するといった手順を踏
んでいた。すなわち、焼成過程へ臨む段階にある成形体
には、発色の異なる釉薬が複数層に積層された状態とな
っているから、その焼成中に各釉薬が溶け出すと、ある
部分では釉薬相互が反応しあった融合色となり、他のあ
る部分では各釉薬単独の発色が現れるなどして複数色の
混在した流れ模様を形成することとなり、これが全体と
して大理石の如き様相を呈するものであった。2. Description of the Related Art Conventionally, in order to produce wares made to look like marble, the procedure of applying glaze to the molded body (before firing) by repeating fluttering is repeated for each of a plurality of glazes of different colors. I was taking steps such as baking. That is, since the glaze that is in the stage of going through the firing process is in a state where glazes of different colors are laminated in multiple layers, when each glaze melts out during firing, the glazes react with each other in some areas. It became a blended color, and in some other part, each glaze appeared alone and a flow pattern in which multiple colors were mixed was formed, and this had a marble-like appearance as a whole.
【０００３】[0003]
【発明が解決しようとする課題】従来における焼物類の
製造方法には次の如き欠点があった。すなわち、釉薬に
はその当初より種々様々なガスが溶解しているから、こ
れらが焼成によって噴出して、焼物類の模様表面にピン
ホールやブクなどを発生させ易かった。しかも、釉薬を
複数回にわたってボタ掛けしている関係上、各釉薬層の
相互間にも空気が巻き込まれ易くなっており、焼成を経
ることで、焼物類の模様表面に比較的大きな凹みを発生
させることもあった。これらを防止するには、釉薬の塗
布厚みを相当分厚くしなければならなかったが、それ故
に、施釉作業が面倒となりまたその所要時間も長引くよ
うになっていた。また、各発色の釉薬相互は、焼成中に
起こる流れが一方向的なものとなり易く、大理石調の模
様としてのバリエーションに乏しかった。The conventional methods for producing wares have the following drawbacks. That is, since various kinds of gases were dissolved in the glaze from the beginning, it was easy for these gases to be ejected by firing to generate pinholes, burrs and the like on the surface of the pattern of the pottery. Moreover, since the glaze is applied multiple times, it is easy for air to be trapped between the glaze layers, resulting in relatively large dents on the pattern surface of the pottery after firing. There was also something to do. In order to prevent these problems, the glaze coating thickness had to be made considerably thick, but therefore the glaze work was troublesome and the time required for it was prolonged. In addition, the glazes of the respective colors were unidirectional in the flow that occurred during firing, and there was little variation as a marble-like pattern.
【０００４】本発明は、上記の如き事情に鑑みてなされ
たものであって、ピンホールやブク及び比較的大きな凹
みの発生を防止することができると共に、模様付けのバ
リエーション（大理石調に限らない）を豊富にすること
ができる、流れ模様を具備した焼物類の製造方法（以
下、本発明方法と言う）を提供することを目的とする。The present invention has been made in view of the above circumstances, and it is possible to prevent the generation of pinholes, bumps, and relatively large dents, and to provide variations in patterning (not limited to marble tones). It is an object of the present invention to provide a method for producing a baked product having a flow pattern (hereinafter, referred to as a method of the present invention) capable of enriching a).
【０００５】[0005]
【課題を解決するための手段】本発明方法の要旨とする
ところは、焼物類の成形用坏土にバインダー液と顔料と
を混入してスラリー状とした装飾用原料液を顔料の色が
異なるものにつき複数種準備し、各装飾用原料液を容器
内へ注入してその液面上を各単独色又は渾融色のうち少
なくとも２色が残存する程度の混合状態にし、次に吸水
性のあるシート材を前記容器内の液面へ接面させて装飾
用原料液を吸着させ、該シート材を焼物類における焼成
前の成形体に対して表面形状に沿わせるように張り付
け、これを焼成する点にある。The gist of the method of the present invention is that the color of the pigment is different in the decorative raw material liquid which is made into a slurry by mixing the binder liquid and the pigment into the kneaded clay for forming the ware. Prepare a plurality of types for each item, inject each of the decorative raw material liquids into the container, and make the liquid surface of the mixed state such that at least two of the individual colors or the fusion colors remain, and A certain sheet material is brought into contact with the liquid surface in the container to adsorb the decorative raw material liquid, and the sheet material is attached to the molded product of the baked product so as to conform to the surface shape, and the product is baked. There is a point to do.
【０００６】また、本発明方法では、焼物類における焼
成前の成形体に対してシート材を張り付けた後、該シー
ト材に保持されている装飾用原料液が成形体側へ移行す
るのを待って、当該シート材を成形体から剥離し、得ら
れた成形体の表面に透明系釉薬を塗布してこれを焼成す
るようにしてもよい。In the method of the present invention, after the sheet material is attached to the unfired molded article of the pottery, the decorative raw material liquid held in the sheet material waits for the migration to the molded article side. Alternatively, the sheet material may be peeled off from the molded body, a transparent glaze may be applied to the surface of the molded body, and the transparent glaze may be baked.
【０００７】[0007]
【作用】装飾用原料液は、焼成によって発色する釉薬と
は異なり、その組成の一つである顔料自体によって色付
けられたものである。そのため、焼成を経ることによっ
ても、ピンホールやブクが発生する可能性は極めて低く
なっている。また、装飾用原料液は、成形体に対して複
数層に積層させるわけではないので、大きな凹みも発生
しない。ところで、装飾用原料液はスラリー（泥漿）状
をしたものであるから、顔料の色が異なる複数種を一つ
の容器内へ注入して混合させた場合、その混合した様相
は、恰も墨流しの如く自然的（非幾何学的）となり、ま
た幻想的図形を描くようになる。そのため、このような
混合状態にある装飾用原料液をシート材に吸着させ、こ
れを成形体の表面に張り付けることによって、該成形体
の表面へ自然的幻想的な図形をそのまま転写することが
できる。従って、該成形体を焼成すれば、流れ模様を具
備した極めて審美的な焼物が得られることとなる。装飾
用原料液の色選択や使用数及び混合状況を変更させるこ
とには無限の展開が期待できるから、得られる焼物のバ
リエーションも同様に無限の広がりを有することとな
る。FUNCTION The decorative raw material liquid is colored by the pigment itself which is one of its compositions, unlike the glaze which is colored by firing. Therefore, it is extremely unlikely that pinholes or burrs are generated even after firing. Further, since the decorative raw material liquid is not laminated in a plurality of layers on the molded body, no large dent is generated. By the way, since the decorative raw material liquid is in the form of slurry (slurry), when a plurality of types of pigments having different colors are poured into one container and mixed, the mixed appearance looks like a sumi-fashi. It becomes natural (non-geometric) and draws fantastical figures. Therefore, by adsorbing the above mixed raw material liquid for decoration on the sheet material and adhering it to the surface of the molded body, it is possible to transfer a natural and fantastic figure to the surface of the molded body as it is. it can. Therefore, when the molded body is fired, an extremely aesthetic fired product having a flow pattern can be obtained. Infinite development can be expected by changing the color selection, the number of uses, and the mixing state of the decorative raw material liquid, so that the variations of the obtained baked products also have infinite spread.
【０００８】なお、上記手順の中でシート材を成形体へ
張り付けた場合、該シート材に保持されている装飾用原
料液は成形体側へと移行してゆき、やがてはその全部が
成形体へ保持されることとなる。従って、この状熊で成
形体からシート材を剥離させることは可能であり、その
まま成形体を焼成してもよい。また、この焼成に先駆け
て、成形体の表面、即ち装飾用原料液による被膜表面へ
透明系（無色透明乃至着色誘明）の釉薬を塗布しておく
と、焼成後に得られる焼物も、流れ模様に深みや光沢が
付加するようになって一層審美的となる。When the sheet material is adhered to the molded body in the above procedure, the decorative raw material liquid held on the sheet material moves to the molded body side, and eventually all of it becomes the molded body. Will be retained. Therefore, it is possible to peel the sheet material from the molded body with this bear, and the molded body may be baked as it is. In addition, prior to this firing, if a transparent glaze (colorless transparent or coloring inducement) is applied to the surface of the molded article, that is, the surface of the coating film of the decorative raw material liquid, the fired product obtained after firing will also have a flow pattern. It becomes more aesthetic by adding depth and gloss.
【０００９】[0009]
【実施例】以下、本発明を、その実施例を示す図面に基
づいて説明すると次のとおりである。図１は、本発明方
法の手順が分り易くなるように描いた概略図である。ま
ず、図中最上部に示すように、澱粉糊１などを水２で溶
くことによってバインダー液３を準備しておく。そし
て、焼物類の成形体を成形する場合に用いるのと同質の
坏土５に対して、適宜色付けを有する顔料４と、上記の
如く準備したバインダー液３とを混入して装飾用原料液
６を製造する。該装飾用原料液６は、その粘度が２００
０センチポイズ程度のスラリー（泥漿）状にしておく必
要がある。但し、あまり粘度が低すぎると、後述するシ
ート材８への吸着時に保持不足が発生し、反対に粘度が
▲高▼すぎると保持不可能となるおそれがあるので注意
を要する。また、該装飾用原料液６としては、前記顔料
４の色付けが異なるものにつき、複数種（６Ａ，６Ｂ）
を準備しておく。The present invention will be described below with reference to the drawings showing the embodiments thereof. FIG. 1 is a schematic diagram drawn so that the procedure of the method of the present invention can be easily understood. First, as shown in the uppermost part of the figure, a binder liquid 3 is prepared by dissolving starch paste 1 and the like with water 2. Then, a pigment raw material 5 of the same quality as that used for forming a molded body of burned material, a pigment 4 having an appropriate coloring, and a binder liquid 3 prepared as described above are mixed to prepare a decorative raw material liquid 6 To manufacture. The decoration raw material liquid 6 has a viscosity of 200.
It is necessary to prepare a slurry (slurry) of about 0 centipoise. However, if the viscosity is too low, insufficient holding may occur during adsorption to the sheet material 8 which will be described later, and on the other hand, if the viscosity is too high, holding may be impossible, so caution is required. Further, as the decorative raw material liquid 6, a plurality of kinds (6A, 6B) of different coloring of the pigment 4 are used.
Be prepared.
【００１０】次に、これら各色（少なくとも２色とす
る）の装飾用原料液６Ａ，６Ｂを、それぞれにつき適量
づつ一つの容器７内へ注入する。注入後には、容器７に
対して回転や震動を与えたり、容器７内の装飾用原料液
６Ａ，６Ｂを直接的に軽く攪拌したり、圧搾空気の吹き
付けによって液面を波立たせたりするなどして、各単独
色が未だ残存する程度の混合状態とする。例えば、い
ま、装飾用原料液６Ａとして多量の白色を用い、同６Ｂ
として少量の赤色を用いたとする。この場合、双方の色
が渾融して容器７内の一部にピンク色の領域ができるの
は構わないが、容器７内の全領域がピンク色に染まって
しまっては模様とはなり得ない。そのため、容器７内で
は、その液面上において白色や赤色（いずれか一方だけ
でもよい）が、そのまま残存している領域が必要となる
のである。すなわち、白地に赤やピンクの縞模様乃至渦
巻模様が形成されたり、ピンク地に白や赤の縞模様乃至
渦巻模様が形成されたりした状態とする。Next, the decoration raw material liquids 6A and 6B of each of these colors (at least two colors) are poured into one container 7 in appropriate amounts. After the injection, the container 7 may be rotated or shaken, the decorative raw material liquids 6A and 6B in the container 7 may be directly and lightly stirred, or the liquid surface may be undulated by blowing compressed air. The mixed state is such that each individual color still remains. For example, a large amount of white is used as the decorative raw material liquid 6A
It is assumed that a small amount of red is used as. In this case, both colors may be melted to form a pink area in a part of the container 7, but if the entire area of the container 7 is dyed in pink, it may be a pattern. Absent. Therefore, in the container 7, a region where white or red (only one of them may be left) remains as it is on the liquid surface is required. That is, the state is such that a red or pink striped pattern or spiral pattern is formed on a white background, or a white or red striped pattern or spiral pattern is formed on a pink background.
【００１１】ここまでの作業が終わったら、織布，不織
布，紙その他より成る吸水性を有したシート材８を、前
記容器７内の液面へ静かに接面させる。実際には、シー
ト材８を液面上へ浮かべてしまえばよい。このことによ
り、容器７内の液面上で混合状態となっている装飾用原
料液（６Ａ及び６Ｂ）は、その混合状態がそのままの形
でシート材８に吸着保持されるものとなる。該装飾用原
料液（６Ａ及び６Ｂ）がシート材８の表面に１ｍｍ程度
付着すれば十分であるから、この時点でシート材８を容
器７内から取り出す。該シート材８は、保持された装飾
用原料液（６Ａ，６Ｂ）が適度な乾燥状態となるか又は
ならないうちに、焼物類における焼成前の成形体９に対
して、その表面形状に沿わせるように張り付ける。例え
ば本実施例では、成形体９が平板状をしたタイル生素地
などである場合を示してあるが、この場合にあって、シ
ート材８は成形体９の四周側面にまで密着するように張
り付けることができる。なお、装飾用原料液（６Ａ，６
Ｂ）の含浸したシート材８を乾燥させるにあたっては、
その乾燥度合が、成形体９自体に要求される含水率（通
常は４％程度）と同じとなるように合わせておくのが好
ましい。When the work up to this point is completed, the water-absorbing sheet material 8 made of woven cloth, non-woven cloth, paper or the like is gently brought into contact with the liquid surface in the container 7. In practice, the sheet material 8 may be floated on the liquid surface. As a result, the decorative raw material liquids (6A and 6B) in a mixed state on the liquid surface in the container 7 are adsorbed and held on the sheet material 8 in the mixed state as it is. It is sufficient that the decoration raw material liquid (6A and 6B) adheres to the surface of the sheet material 8 by about 1 mm, and thus the sheet material 8 is taken out from the container 7 at this point. The sheet material 8 is made to conform to the surface shape of the molded article 9 before firing in the pottery, before or after the retained decoration raw material liquid (6A, 6B) is brought to an appropriate dry state or not. Stick it on. For example, in the present embodiment, the case where the molded body 9 is a flat tile-shaped green body or the like is shown, but in this case, the sheet material 8 is attached so as to come into close contact with the four circumferential side surfaces of the molded body 9. You can The raw material liquid for decoration (6A, 6A
In drying the sheet material 8 impregnated in B),
It is preferable that the degree of dryness is adjusted so as to be the same as the water content required for the molded body 9 itself (usually about 4%).
【００１２】このようにして得られた成形体９は、その
肉厚や形状、素材に応じた焼成条件（方法や温度，時間
など）に基づいて焼成する。なお、該成形体９の表面に
シート材８が張り付いたままで焼成しても、該シート材
８は焼成によって焼失するものであり、焼成後の焼物に
は何ら悪影響を及ぼすものではない。The thus-obtained molded body 9 is fired on the basis of firing conditions (method, temperature, time, etc.) according to its thickness, shape and material. In addition, even if the sheet material 8 is fired with the surface of the molded body 9 stuck to the surface, the sheet material 8 is burned off by the firing, and the fired product after firing is not adversely affected.
【００１３】しかし、該シート材８は、焼成前の成形体
９から剥離しておくこともできる。すなわち、成形体９
に対して未乾燥状態にあるシート材８を張り付けると、
その後、シート材８に保持されている装飾用原料液（６
Ａ，６Ｂ）は徐々に成形体９中へと移行してゆくもので
あり、やがてはその全部が成形体９に保持されることと
なる。従ってこの時点では、シート材８をそれ単独とし
て剥離することが可能となる。シート材８を剥離した後
の成形体９は、これをそのまま焼成することも可能であ
るが、成形体９の表面（装飾用原料液の被膜表面）へ透
明系（無色透明乃至着色透明）の釉薬を塗布した後に焼
成することもできる。このようにすると、焼成後の焼物
に得られる流れ模様に深みや光沢が付加されたものとな
り、一層審美的となる。図２に示す如く、本発明方法に
よって得られた焼物１０（タイル）は、その表面全面に
自然的幻想的な流れ模様が表れたものとなっている。However, the sheet material 8 may be separated from the molded body 9 before firing. That is, the molded body 9
When the sheet material 8 in the undried state is attached to
After that, the decorative raw material liquid (6
A and 6B) gradually move into the molded body 9, and eventually all of them are held by the molded body 9. Therefore, at this time, the sheet material 8 can be peeled off by itself. The molded body 9 from which the sheet material 8 has been peeled off can be baked as it is, but the surface of the molded body 9 (the surface of the coating of the decorative raw material liquid) is transparent (colorless or transparent). It is also possible to bake after applying the glaze. In this way, the flow pattern obtained in the fired product after firing is added with depth and gloss, which makes it more aesthetic. As shown in FIG. 2, the ware 10 (tile) obtained by the method of the present invention has a natural and fantastic flow pattern on the entire surface thereof.
【００１４】本発明方法は、前述した如く、タイル（役
物を含む），屋根瓦などの建材をはじめ、便器，洗面器
などの衛生陶器、更には食器、置物その他、焼物類全般
を対象として実施できるものである。また、本発明方法
によって施される模様は、大理石調などの現存する模様
に限定されるものではなく、想像的空想的なものを含む
あらゆる流れ模様を可能としている。このように、本発
明方法の細部にわたる構成は、実施の態様に応じて適宜
変更可能である。As described above, the method of the present invention is applied to building materials such as tiles (including accessories) and roof tiles, sanitary ware such as toilet bowls and washbasins, and tableware, figurines and other pottery products in general. It can be implemented. Further, the pattern applied by the method of the present invention is not limited to the existing pattern such as a marble tone, but allows any flow pattern including an imaginary and fantasy pattern. As described above, the detailed configuration of the method of the present invention can be appropriately changed according to the embodiment.
【００１５】[0015]
【発明の効果】以上の説明で明らかなように、本発明に
係る焼物類の製造方法によれば、ピンホール，ブク，凹
みなどを発生させることなく、流れ模様を具備した焼物
類を製造することができるものである。また、色の異な
る装飾用原料液を相互に混合して得られる模様は、自然
的幻想的な縞模様乃至渦巻模様となるものであり、大理
石調などとして、より似せた感じを持たせられる。しか
も、該模様は、複雑な凹凸形状を有した如き焼物類に対
しても具備させることができるものであり、またその作
業性は平板材などの単純形状のものに模様を具備させる
場合と何等変わらない程に簡単なものとなっている。更
に、装飾用原料液の色選択や使用数及び混合状況などを
変更させることには無限の展開が期待できるから、得ら
れる装飾タイルの模様バリエーションも無限に広げられ
る等、幾多の優れた利点を有している。As is apparent from the above description, according to the method for producing a pottery product according to the present invention, a pottery product having a flow pattern is produced without generating pinholes, burrs, dents, and the like. Is something that can be done. Also, the pattern obtained by mixing the decorative raw material liquids of different colors with each other is a natural and fantastic striped pattern or swirl pattern, and gives a more similar feeling as a marble tone. Moreover, the pattern can be provided even for wares having a complicated uneven shape, and its workability is similar to that when a simple shape such as a flat plate is provided with the pattern. It's as easy as ever. In addition, since it is expected to have unlimited development in changing the color selection of the decorative raw material liquid, the number of uses, and the mixing status, the pattern variations of the obtained decorative tiles can be endlessly expanded, and many other excellent advantages are obtained. Have
【図１】本発明の手順を示す概略図である。FIG. 1 is a schematic diagram showing the procedure of the present invention.
【図２】本発明方法によって製造された焼物類の一例を
示す斜視図である。FIG. 2 is a perspective view showing an example of a burnt product produced by the method of the present invention.
３…バインダー液 ４…顔料 ５…成形用坏土
６…装飾用原料液７…容器 ８…シート材 ９…成
形体 １０…焼物3 ... Binder liquid 4 ... Pigment 5 ... Molding clay
6 ... Raw material liquid for decoration 7 ... Container 8 ... Sheet material 9 ... Molded body 10 ... Baked product
Claims (2)
料とを混入してスラリー状とした装飾用原料液を顔料の
色が異なるものにつき複数種準備し、各装飾用原料液を
容器内へ注入してその液面上を各単独色又は渾融色のう
ち少なくとも２色が残存する程度の混合状態にし、次に
吸水性のあるシート材を前記容器内の液面へ接面させて
装飾用原料液を吸着させ、該シート材を焼物類における
焼成前の成形体に対して表面形状に沿わせるように張り
付け、得られた成形体を焼成することを特徴とする流れ
模様を具備した焼物類の製造方法。1. A plurality of types of decorative raw material liquids, each having a different pigment color, are prepared by mixing a binder liquid and a pigment into a clay for forming a pottery product, and each of the decorative raw material liquids is a container. It is poured into the inside of the container to make a mixed state such that at least two of the individual colors or the fused colors remain on the liquid surface, and then a sheet material having water absorption is brought into contact with the liquid surface in the container. And adsorbing the decorative raw material liquid on the sheet material, adhering the sheet material to a molded article of a fired product before firing so as to conform to the surface shape, and firing the obtained molded article. For producing baked products.
料とを混入してスラリー状とした装飾用原料液を顔料の
色が異なるものにつき複数種準備し、各装飾用原料液を
容器内へ注入してその液面上を各単独色又は渾融色のう
ち少なくとも２色が残存する程度の混合状態にし、次に
吸水性のあるシート材を前記容器内の液面へ接面させて
装飾用原料液を吸着させ、該シート材を焼物類における
焼成前の成形体に対して表面形状に沿わせるように張り
付けると共に、該シート材に保持されている装飾用原料
液が成形体側へ移行するのを待って当該シート材を成形
体から剥離し、得られた成形体の表面に透明系釉薬を塗
布してこれを焼成することを特徴とする流れ模様を具備
した焼物類の製造方法。2. A plurality of kinds of decorative raw material liquids, each having a different pigment color, are prepared by mixing a binder liquid and a pigment into a clay for forming a pottery product, and each of the decorative raw material liquids is a container. It is poured into the inside of the container to make a mixed state such that at least two of the individual colors or the fused colors remain on the liquid surface, and then a sheet material having water absorption is brought into contact with the liquid surface in the container. Adsorbing the decorative raw material liquid and adhering the sheet material to the molded product of the fired product before firing so as to follow the surface shape, and the decorative raw material liquid held by the sheet material is on the molded product side. Production of burned products having a flow pattern characterized by peeling the sheet material from the molded body after waiting for the transition to, and coating the surface of the obtained molded body with a transparent glaze and firing it. Method.