JP2022003268A - 伝動用vベルト - Google Patents
伝動用vベルト Download PDFInfo
- Publication number
- JP2022003268A JP2022003268A JP2021096808A JP2021096808A JP2022003268A JP 2022003268 A JP2022003268 A JP 2022003268A JP 2021096808 A JP2021096808 A JP 2021096808A JP 2021096808 A JP2021096808 A JP 2021096808A JP 2022003268 A JP2022003268 A JP 2022003268A
- Authority
- JP
- Japan
- Prior art keywords
- rubber layer
- belt
- layer
- ethylene
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明のローエッジタイプVベルト(ローエッジタイプの伝動用Vベルト)は、圧縮ゴム層の本体と表面層(内表面層)との特定の二層構造を有する圧縮ゴム層を含むローエッジタイプVベルトであれば、特に限定されない。ローエッジタイプVベルトには、ローエッジVベルト、ローエッジコグドVベルトが含まれる。さらに、ローエッジコグドVベルトは、ローエッジVベルトの内周側のみにコグが形成されたローエッジコグドVベルトと、ローエッジVベルトの内周側および外周側の双方にコグが形成されたローエッジダブルコグドVベルトとに大別できる。これらのうち、耐側圧性と耐屈曲疲労性とを高度なレベルで両立することを要求される点から、ローエッジコグドVベルトおよびローエッジダブルコグドVベルトが好ましく、より過酷な状況で利用され、高度なレベルを要求される点から、ローエッジダブルコグドVベルトが特に好ましい。
圧縮ゴム層は、エチレン−α−オレフィンエラストマーおよび有機過酸化物を含むゴム組成物の硬化物で形成された圧縮ゴム層の本体と、この本体のベルト内周側表面を被覆し、かつエチレン−α−オレフィンエラストマーおよび硫黄系架橋剤を含むゴム組成物の硬化物で形成された表面層(内表面層)とを有している。圧縮ゴム層は、圧縮ゴム層の本体と内表面層とを有していればよく、他の層(例えば、圧縮ゴム層の本体と内表面層との間に介在する他のゴム層など)を有していてもよいが、圧縮ゴム層の機械的特性や生産性などの点から、圧縮ゴム層の本体と内表面層との二層構造が好ましい。本発明では、圧縮ゴム層を本体と内表面層との二層構造に形成することにより、耐側圧性と耐屈曲疲労性とを両立できる。さらに、圧縮ゴム層がエチレン−α−オレフィンエラストマーを含むことで耐熱性に優れ、高温下での使用におけるローエッジVベルトの耐久性を向上できる。
本発明では、圧縮ゴム層の本体(圧縮ゴム層本体)がエチレン−α−オレフィンエラストマーおよび有機過酸化物を含むゴム組成物の硬化物で形成されており、圧縮ゴム層のゴム硬度を高くできるため、耐側圧性を向上できる。
エチレン−α−オレフィンエラストマーは、主鎖に二重結合を含まないため、耐熱性に優れている。そのため、圧縮ゴム層本体のゴム成分をエチレン−α−オレフィンエラストマーで形成すると、高温下での使用におけるローエッジVベルトの耐久性を向上できる。エチレン−α−オレフィンエラストマーは、構成単位として、エチレン単位、α−オレフィン単位を含んでいればよく、ジエン単位をさらに含んでいてもよい。エチレン−α−オレフィンエラストマーには、エチレン−α−オレフィン共重合体ゴム、エチレン−α−オレフィン−ジエン三元共重合体ゴムなどが含まれる。
本発明では、圧縮ゴム層本体の架橋剤(または加硫剤)として有機過酸化物を用いることにより、ゴム硬度を向上でき、耐側圧性を向上できる。
前記ゴム組成物は、エチレン−α−オレフィンエラストマーおよび有機過酸化物に加えて、共架橋剤をさらに含んでいてもよい。
前記ゴム組成物は、短繊維をさらに含んでいてもよい。短繊維としては、ポリアミド短繊維(ポリアミド6短繊維、ポリアミド66短繊維、ポリアミド46短繊維、アラミド短繊維など)、ポリアルキレンアリレート短繊維(例えば、ポリエチレンテレフタレート(PET)短繊維、ポリエチレンナフタレート短繊維など)、液晶ポリエステル短繊維、ポリアリレート短繊維(非晶質全芳香族ポリエステル短繊維など)、ビニロン短繊維、ポリビニルアルコール系短繊維、ポリパラフェニレンベンゾビスオキサゾール(PBO)短繊維などの合成短繊維;綿、麻、羊毛などの天然短繊維;カーボン短繊維などの無機短繊維などが挙げられる。これら短繊維は、単独でまたは二種以上組み合わせて使用できる。これらのうち、アラミド短繊維、PBO短繊維が好ましく、アラミド短繊維が特に好ましい。
前記ゴム組成物は、フィラーをさらに含んでいてもよい。フィラーとしては、例えば、カーボンブラック、シリカ、クレー、炭酸カルシウム、タルク、マイカなどが挙げられる。フィラーは、補強性フィラーを含む場合が多く、このような補強性フィラーは、カーボンブラック、補強性シリカなどであってもよい。これらのフィラーは、単独でまたは二種以上組み合わせて使用できる。圧縮ゴム層では、耐側圧性を向上できる点から、フィラーは少なくとも補強性フィラー(特に、カーボンブラック)を含むのが好ましい。
、さらに好ましくは15〜100nmであり、補強効果が高い点から、小粒径、例えば、
平均粒径が5〜38nm、好ましくは10〜35nm、さらに好ましくは15〜30nm
のカーボンブラックであってもよい。小粒径のカーボンブラックとしては、例えば、SA
F、ISAF−HM、ISAF−LM、HAF−LS、HAF、HAF−HSなどが例示
できる。これらのカーボンブラックは単独または組み合わせて使用できる。
前記ゴム組成物は、他の成分をさらに含んでいてもよい。他の成分としては、他のゴム成分[天然ゴム、イソプレンゴム、ブタジエンゴム、クロロプレンゴム、スチレンブタジエンゴム(SBR)、アクリロニトリルブタジエンゴム(ニトリルゴム)、水素化ニトリルゴムなどのジエン系ゴム;クロロスルホン化ポリエチレンゴム、アルキル化クロロスルホン化ポリエチレンゴム、エピクロロヒドリンゴム、アクリル系ゴム、シリコーンゴム、ウレタンゴム、フッ素ゴムなど]、他の架橋剤、架橋促進剤(または加硫促進剤)、金属酸化物(酸化亜鉛、酸化マグネシウム、酸化鉛、酸化カルシウム、酸化バリウム、酸化鉄、酸化銅、酸化チタン、酸化アルミニウムなど)、軟化剤または可塑剤(パラフィンオイルやナフテン系オイルなどのオイル類など)、加工剤または加工助剤(ステアリン酸などの脂肪酸、ステアリン酸金属塩などの脂肪酸金属塩、ステアリン酸アマイドなどの脂肪酸アマイド、ワックス、パラフィンなど)、老化防止剤(酸化防止剤、熱老化防止剤、屈曲き裂防止剤、オゾン劣化防止剤など)、着色剤、粘着付与剤、滑剤、カップリング剤(シランカップリング剤など)、安定剤(紫外線吸収剤、熱安定剤など)、難燃剤、帯電防止剤などが挙げられる。
圧縮ゴム層本体は、高いゴム硬度を有しており、ゴム硬度は、例えば90〜99度、好ましくは91〜98度、さらに好ましくは92〜98度、より好ましくは93〜97度、最も好ましくは94〜96度である。圧縮ゴム層本体のゴム硬度が小さすぎると、耐側圧性が低下する虞があり、大きすぎると、耐屈曲性疲労性および耐久性が低下する虞がある。
本発明では、前記圧縮ゴム層本体のベルト内周側表面は、ジエン単位を含むエチレン−α−オレフィンエラストマーおよび硫黄系架橋剤を含むゴム組成物の硬化物で形成された平均厚み0.3〜3.5mmの表面層(内表面層)で被覆されている。前記内表面層は、耐屈曲疲労性を向上させる機能を有しており、前記圧縮ゴム層本体と内表面層との組み合わせによって、耐熱性、耐側圧性および耐屈曲疲労性を向上できる。
圧縮ゴム層の内表面層を形成するゴム組成物において、エチレン−α−オレフィンエラストマーは、硫黄系架橋剤で架橋されるため、ジエン単位を含んでいる。すなわち、内表面層のエチレン−α−オレフィンエラストマーは、構成単位として、エチレン単位、α−オレフィン単位、ジエン単位を含んでおり、エチレン−α−オレフィン−ジエン三元共重合体ゴムであってもよい。
本発明では、圧縮ゴム層の内表面層における架橋剤として硫黄系架橋剤を用いることにより、圧縮ゴム層本体に比べて内表面層を低硬度に調整でき、耐屈曲疲労性(耐亀裂性)を向上できる。
前記ゴム組成物は、ジエン単位を含むエチレン−α−オレフィンエラストマーおよび硫黄系架橋剤に加えて、架橋促進剤をさらに含んでいてもよい。
前記ゴム組成物は、短繊維をさらに含んでいてもよい。短繊維は、好ましい態様も含めて、前記圧縮ゴム層本体における短繊維(A4)の項で例示された短繊維から選択できる。
前記ゴム組成物は、フィラーをさらに含んでいてもよい。フィラーは、好ましい態様も含めて、前記圧縮ゴム層本体におけるフィラー(A5)の項で例示されたフィラーから選択できる。
前記ゴム組成物は、他の成分をさらに含んでいてもよい。他の成分としては、前記圧縮ゴム層本体における他の成分(A6)として例示された他の成分に加えて、共架橋剤などを利用できる。
圧縮ゴム層の内表面層の硬度は、例えば70〜95度、好ましくは80〜94度、さらに好ましくは85〜94度(例えば85〜93度)、より好ましくは90〜94度(最も好ましくは92〜94度)である。内表面層のゴム硬度が小さすぎると、耐側圧性が低下する虞があり、大きすぎると、耐屈曲性疲労性が低下する虞がある。
伸張ゴム層は、エチレン−α−オレフィンエラストマーを含むゴム組成物の硬化物で形成されていればよく、架橋剤は、有機過酸化物であってもよく、硫黄系架橋剤であってもよい。これらのうち、耐久性の点から、硫黄系架橋剤が好ましい。さらに、伸張ゴム層の層構造は特に限定されず、単層構造であってもよく、二層構造であってもよい。工数を低減でき、ベルトの生産性を向上できる点からは、単層構造が好ましく、ベルト背面における亀裂を抑制できる点からは、二層構造が好ましい。
本発明のローエッジタイプVベルトは、接着ゴム層を含んでいなくてもよいが、芯体と圧縮ゴム層本体、芯体と伸張ゴム層(または伸張ゴム層本体)の接着力を高めて、芯体と前記層との剥離を抑制できる点から、接着ゴム層を含むのが好ましい。接着ゴム層は、エチレン−α−オレフィンエラストマーおよび架橋剤を含むゴム組成物で形成されていてもよい。
エチレン−α−オレフィンエラストマーは、好ましい態様も含めて、圧縮ゴム層の本体におけるエチレン−α−オレフィンエラストマー(A1)の項で例示されたエチレン−α−オレフィンエラストマーから選択できる。
架橋剤としては、圧縮ゴム層本体における有機過酸化物(A2)の項で例示された有機過酸化物、圧縮ゴム層の内表面層における硫黄系架橋剤(B2)の項で例示された硫黄系架橋剤などを利用できる。これらの架橋剤は、単独でまたは二種以上組み合わせて使用できる。これらのうち、有機過酸化物が好ましい。
共架橋剤としては、圧縮ゴム層本体における共架橋剤(A3)の項で例示された共架橋剤などを利用できる。架橋促進剤としては、圧縮ゴム層の内表面層における架橋促進剤(B3)の項で例示された架橋促進剤などを利用できる。これらの共架橋剤および架橋促進剤は、単独でまたは二種以上組み合わせて使用できる。これらのうち、共架橋剤が好ましく、(メタ)アクリル酸亜鉛などの不飽和カルボン酸の金属塩が特に好ましい。
前記ゴム組成物は、フィラーをさらに含んでいてもよい。フィラーとしては、例えば、カーボンブラック、シリカ、クレー、炭酸カルシウム、タルク、マイカなどが挙げられる。これらのフィラーは、単独でまたは二種以上組み合わせて使用できる。これらのうち、カーボンブラックとシリカとの組み合わせが好ましい。
前記ゴム組成物は、接着性改善剤をさらに含んでいてもよい。接着性改善剤としては、例えば、レゾルシン−ホルムアルデヒド共縮合物(RF縮合物)、アミノ樹脂(窒素含有環状化合物とホルムアルデヒドとの縮合物、例えば、ヘキサメチロールメラミン、ヘキサアルコキシメチルメラミン(ヘキサメトキシメチルメラミン、ヘキサブトキシメチルメラミンなど)などのメラミン樹脂、メチロール尿素などの尿素樹脂、メチロールベンゾグアナミン樹脂などのベンゾグアナミン樹脂など)、これらの共縮合物(レゾルシン−メラミン−ホルムアルデヒド共縮合物など)などが挙げられる。
前記ゴム組成物は、他の成分をさらに含んでいてもよい。他の成分としては、前記圧縮ゴム層本体における他の成分(A6)として例示された他の成分などを利用できる。
接着ゴム層は、圧縮ゴム層本体のゴム硬度よりも低い硬度が好ましく、圧縮ゴム層の内表面層(または伸張ゴム層の外表面層)のゴム硬度よりも低い硬度がさらに好ましい。接着ゴム層を、このような低硬度に調整することにより、せん断応力が作用した場合に大きく変形することが可能となり、芯体と圧縮ゴム層本体および伸張ゴム層本体との間の剥離を抑制できる。
芯体としては、特に限定されないが、通常、ベルト幅方向に所定間隔で配列した心線(撚りコード)を使用できる。心線は、ベルトの長手方向に延びて配設され、通常、ベルトの長手方向に平行に所定のピッチで並列的に延びて配設されている。心線は、少なくともその一部が接着ゴム層と接していればよく、接着ゴム層が心線を埋設する形態、接着ゴム層と伸張ゴム層との間に心線を埋設する形態、接着ゴム層と圧縮ゴム層との間に心線を埋設する形態のいずれの形態であってもよい。これらのうち、耐久性を向上できる点から、接着ゴム層が心線を埋設する形態が好ましい。
本発明のローエッジタイプVベルトは、圧縮ゴム層の内表面層によって耐屈曲疲労性が高められているために、補強布がなくても優れた耐屈曲疲労性を有する。そのため、本発明では、補強布を設けずに工数を低減して、生産性を向上することができる。一方で、前記内表面層や伸張ゴム層をさらに補強布と組み合わせることにより、耐屈曲疲労性をさらに向上させてもよい。
本発明のローエッジタイプVベルトの製造方法は、特に限定されず、各層の積層工程(ベルトスリーブの製造方法)に関しては、ベルトの種類に応じて、慣用の方法を利用できる。
EPDM1:JSR(株)製「EP93」、エチレン含量55質量%、ジエン含量2.7質量%
EPDM2:JSR(株)製「EP24」、エチレン含量54質量%、ジエン含量4.5質量%
短繊維(パラ系アラミド短繊維):帝人(株)製「トワロン(登録商標)」、平均繊維径14μm、平均繊維長3mm
カーボンブラック:キャボットジャパン(株)製「ショウブラックN550」
シリカ:エボニック・デグサ・ジャパン(株)製「ウルトラシルVN−3」、比表面積155〜195m2/g
可塑剤(パラフィン系オイル):出光興産(株)製「ダイアナプロセスオイルPW90」
酸化亜鉛:堺化学工業(株)製「酸化亜鉛2種」、平均粒子径0.55μm
ステアリン酸:日油(株)製「ステアリン酸つばき」
酸化マグネシウム:協和化学(株)製「キョーワマグ150」
老化防止剤:4,4'−ビス(α,α−ジメチルベンジル)ジフェニルアミン(大内新興化学工業(株)製「ノクラックCD」)
共架橋剤:メタクリル酸亜鉛(三新化学工業(株)製「サンエステルSK−30」)
有機過酸化物:1,3−ビス(t−ブチルパーオキシイソプロピル)ベンゼン、理論活性酸素量9.45%
硫黄:美源化学社製「硫黄」
架橋促進剤:テトラメチルチウラムジスルフィド(大内新興化学工業(株)製「ノクセラーTT」)
接着性改善剤(ヘキサメトキシメチルメラミン):Singh Plasticisers & Resins Pvt. Ltd.社製「POWERPLAST PP−1890S」
心線:1100dtexのPETマルチフィラメント糸を2×3の撚り構成で、上撚り係数3.0、下撚り係数3.0で諸撚りした総繊度6600dtexの撚りコードに接着処理を施した処理コード。
表1のゴム組成物は、それぞれ、バンバリーミキサーなどの公知の方法を用いてゴム練りを行い、この練りゴムをカレンダーロールに通して圧延ゴムシート(未架橋ゴムシート)を作製した。なお、短繊維は、RFL液(レゾルシンおよびホルムアルデヒドと、ラテックスとしてのビニルピリジン−スチレン−ブタジエンゴムラテックスとを含有)で接着処理し、固形分の付着率6質量%の短繊維を用いた。RFL液として、レゾルシン2.6質量部、37%ホルマリン1.4質量部、ビニルピリジン−スチレン−ブタジエン共重合体ラテックス17.2質量部、水29.0質量部を用いた。
凸部と凹部とが交互に配された平坦なコグ付き型に、圧縮ゴム層の内表面層を形成する未架橋ゴムシートと圧縮ゴム層の本体を形成する未架橋ゴムシートとを積層した後、100℃の加熱下でプレスして、コグ部が形成された半架橋状態のコグパッドを調製した。円筒状の金型に凸部と凹部とが交互に配された内母型を被せ、前記コグパッドを前記内母型に巻き付けて両端部をジョイントして装着した。装着したコグパッドに、接着ゴム層を形成する未架橋ゴムシート(R3)を巻き付けた後、心線を螺旋状にスピニングした。前記心線の上に、さらに接着ゴム層を形成する未架橋ゴムシート(R3)、伸張ゴム層を形成する未架橋ゴムシートを巻き付けて成形体を形成した。この成形体に、ベルト外周側にコグ形状を形成するための外母型および可撓性ジャケットを被せた後、金型を加硫缶に設置し、温度170℃、時間40分で架橋してベルトスリーブを得た。このベルトスリーブをカッターでV字状に切断して、ベルト内周側と外周側にコグを有する変速ベルトであるローエッジダブルコグドVベルト(サイズ:上幅20mm、厚み(内周側コグ山部から外周側コグ山部までの距離)12mm、V角度30度、コグ高さ(内周側)4.5mm、コグ高さ(外周側)3mm、ベルト外周長さ650mm)を作製した。
内周面のみにコグを有し、外周面にコグを有しないローエッジコグドVベルトを作製する場合は、成形体に外母型を被せることなく可撓性ジャケットのみを被せる以外は、ローエッジダブルコグドVベルトの作製と同様にして作製した。ローエッジコグドVベルトのサイズは、上幅19mm、厚み(内周側コグ山部からベルト外周までの距離)10mm、V角度30度、コグ高さ(内周側)4.5mm、ベルト外周長さ640mmであった。
ローエッジコグドVベルトをコグ頂部においてベルト幅方向と平行に切断し、その断面をマイクロスコープで20倍に拡大して観察し、内表面層および外表面層の厚みを測定した。厚みの測定は、ベルト長さ方向に約5等分となるように5箇所で測定し、その算術平均を当該ベルトの内表面層および外表面層の厚みとした。なお、ベルトの内周側、および外周側にコグ部を有しないローエッジVベルトの切断箇所はコグ頂部に限らず、ベルト長さ方向に約5等分となるような5箇所とする。
耐久走行試験は、図4に示すように、直径φ100mmの駆動(DR)プーリ22と、直径φ80mmの従動(DN)プーリ23とを備える2軸走行試験機を用いて行なった。各プーリにVベルト21を軸荷重0.6kNで掛架し、雰囲気温度100℃にて、ベルトの寿命まで走行させた。なお、駆動プーリの回転数は、0〜20秒は7,000rpmで一定、20〜40秒は7,000±350rpmで変動、40〜60秒は再び7,000rpmで一定とし、従動プーリの負荷は15Nmとした。この60秒を1つのサイクルとして、試験終了まで繰り返した。
伸張ゴム層として有機過酸化物を含むゴム組成物(R1)を使用し、圧縮ゴム層の本体として有機過酸化物を含むゴム組成物(R1)を使用し、かつ圧縮ゴム層の内表面層として硫黄を含むゴム組成物(R2)を使用し、伸張ゴム層が単層構造であり、かつ圧縮ゴム層が二層構造であるローエッジダブルコグドVベルトを製造した。得られたベルトにおいて、圧縮ゴム層の本体の厚みは6.2mm、内表面層の厚みは0.3mmであり、伸張ゴム層の厚みは3.5mmであった。
得られたベルトにおける圧縮ゴム層の本体の厚みを6.0mm、内表面層の厚みを0.5mmに変更する以外は実施例1と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは6.0mm、内表面層の厚みは0.5mmであり、伸張ゴム層の厚みは3.5mmであった。
得られたベルトにおける圧縮ゴム層の本体の厚みを5.5mm、内表面層の厚みを1.0mmに変更する以外は実施例1と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは5.5mm、内表面層の厚みは1.0mmであり、伸張ゴム層の厚みは3.5mmであった。
伸張ゴム層の本体として有機過酸化物を含むゴム組成物(R1)を使用し、かつ伸張ゴム層の外表面層として硫黄を含むゴム組成物(R2)を使用する以外は実施例3と同様の方法で、伸張ゴム層および圧縮ゴム層がいずれも二層構造であるローエッジダブルコグドVベルトを製造した。得られたベルトにおいて、圧縮ゴム層の本体の厚みは5.5mm、内表面層の厚みは1.0mmであり、伸張ゴム層の本体の厚みは3.0mmであり、外表面層の厚みは0.5mmであった。
得られたベルトにおける伸張ゴム層の本体の厚みを2.5mm、外表面層の厚みを1.0mmに変更する以外は実施例4と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは5.5mm、内表面層の厚みは1.0mmであり、伸張ゴム層の本体の厚みは2.5mmであり、外表面層の厚みは1.0mmであった。
圧縮ゴム層の本体を4.5mm、内表面層の厚みを2.0mmに変更する以外は実施例5と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは4.5mm、内表面層の厚みは2.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
圧縮ゴム層の本体の厚みを3.5mm、内表面層の厚みを3.0mmに変更する以外は実施例5と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは3.5mm、内表面層の厚みは3.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
伸張ゴム層の本体の厚みを1.5mm、外表面層の厚みを2.0mmに変更する以外は実施例4と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは5.5mm、内表面層の厚みは1.0mmであり、伸張ゴム層の本体の厚みは1.5mm、外表面層の厚みは2.0mmであった。
伸張ゴム層として有機過酸化物を含むゴム組成物(R1)を使用し、圧縮ゴム層として有機過酸化物を含むゴム組成物(R1)を使用し、伸張ゴム層および圧縮ゴム層がいずれも単層構造であるローエッジダブルコグドVベルトを製造した。
伸張ゴム層として硫黄を含むゴム組成物(R2)を使用し、圧縮ゴム層として硫黄を含むゴム組成物(R2)を使用し、伸張ゴム層および圧縮ゴム層がいずれも単層構造であるローエッジダブルコグドVベルトを製造した。
伸張ゴム層として有機過酸化物を含むゴム組成物(R1)を使用し、圧縮ゴム層の本体として硫黄を含むゴム組成物(R2)を使用し、かつ圧縮ゴム層の内表面層として有機過酸化物を含むゴム組成物(R1)を使用し、伸張ゴム層が単層構造であり、かつ圧縮ゴム層が二層構造であるローエッジダブルコグドVベルトを製造した。すなわち、実施例3において、圧縮ゴム層の本体と内表面層とのゴム組成物を入れ替えた。
圧縮ゴム層の内表面層の厚みを4.0mmに変更する以外は実施例5と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは2.5mm、内表面層の厚みは4.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
伸張ゴム層として硫黄を含むゴム組成物(R2)を使用する以外は実施例3と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは5.5mm、内表面層の厚みは1.0mmであり、伸張ゴム層の厚みは3.5mmであった。
伸張ゴム層の外表面層および圧縮ゴム層の内表面層として、硫黄を含み、ゴム硬度がゴム組成物(R2)よりも小さいゴム組成物(R6)を使用する以外は実施例6と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは4.5mm、内表面層の厚みは2.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
伸張ゴム層の外表面層および圧縮ゴム層の内表面層として、硫黄を含み、ゴム硬度がゴム組成物(R2)よりも大きいゴム組成物(R7)を使用する以外は実施例6と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは4.5mm、内表面層の厚みは2.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
伸張ゴム層の外表面層および圧縮ゴム層の内表面層として、硫黄を含み、ゴム硬度がゴム組成物(R7)よりも大きいゴム組成物(R8)を使用する以外は実施例6と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは4.5mm、内表面層の厚みは2.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
伸張ゴム層の本体および圧縮ゴム層の本体として、有機過酸化物を含み、ゴム硬度がゴム組成物(R1)よりも小さいゴム組成物(R4)を使用する以外は実施例11と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは4.5mm、内表面層の厚みは2.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
伸張ゴム層の本体および圧縮ゴム層の本体として、有機過酸化物を含み、ゴム硬度がゴム組成物(R1)よりも大きいゴム組成物(R5)を使用する以外は実施例11と同様の方法でローエッジダブルコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは4.5mm、内表面層の厚みは2.0mmであり、伸張ゴム層の本体の厚みは2.5mm、外表面層の厚みは1.0mmであった。
ベルトの形状をローエッジコグドVベルトとする以外は実施例9と同様の方法でローエッジコグドVベルトを製造した。すなわち、得られたベルトにおいて、圧縮ゴム層の本体の厚みは5.5mm、内表面層の厚みは1.0mmであり、伸張ゴム層の厚みは1.5mmであった。
2…伸張ゴム層の外表面層
3…伸張ゴム層の本体
4…接着ゴム層
4a…芯体
5…圧縮ゴム層の本体
6…圧縮ゴム層の内表面層
Claims (8)
- 内周面側に配設される圧縮ゴム層を含み、前記圧縮ゴム層が、エチレン−α−オレフィンエラストマーおよび有機過酸化物を含むゴム組成物の硬化物で形成された圧縮ゴム層の本体と、前記圧縮ゴム層の本体の内周側表面を被覆し、かつジエン単位を含むエチレン−α−オレフィンエラストマーおよび硫黄系架橋剤を含むゴム組成物の硬化物で形成された平均厚み0.3〜3.5mmの内表面層とを有するローエッジタイプVベルト。
- 外周面側に配設される伸張ゴム層をさらに含み、前記伸張ゴム層が、ジエン単位を含むエチレン−α−オレフィンエラストマーおよび硫黄系架橋剤を含むゴム組成物の硬化物で形成されている請求項1記載のローエッジタイプVベルト。
- 外周面側に配設される伸張ゴム層をさらに含み、前記伸張ゴム層が、エチレン−α−オレフィンエラストマーおよび有機過酸化物を含むゴム組成物の硬化物で形成された伸張ゴム層の本体と、前記伸張ゴム層の本体の外周側表面を被覆し、かつジエン単位を含むエチレン−α−オレフィンエラストマーおよび硫黄系架橋剤を含むゴム組成物の硬化物で形成された外表面層とを有する請求項1記載のローエッジタイプVベルト。
- ベルト全体の平均厚みが8〜18mmである請求項1〜3のいずれか一項に記載のローエッジタイプVベルト。
- 前記圧縮ゴム層の本体の硬度が90〜99度であり、かつ前記内表面層の硬度が70〜95度である請求項1〜4のいずれか一項に記載のローエッジタイプVベルト。
- 前記圧縮ゴム層の本体において、エチレン−α−オレフィンエラストマーのジエン含量が3.5質量%未満であり、前記内表面層において、ジエン単位を含むエチレン−α−オレフィンエラストマーのジエン含量が3.5質量%以上である請求項1〜5のいずれか一項に記載のローエッジタイプVベルト。
- 少なくとも内周面側にコグを有する請求項1〜6のいずれか一項に記載のローエッジタイプVベルト。
- 変速ベルトである請求項1〜7のいずれか一項に記載のローエッジタイプVベルト。