JP2020100724A - 親水性基材及び親水性基材作製方法 - Google Patents
親水性基材及び親水性基材作製方法 Download PDFInfo
- Publication number
- JP2020100724A JP2020100724A JP2018239543A JP2018239543A JP2020100724A JP 2020100724 A JP2020100724 A JP 2020100724A JP 2018239543 A JP2018239543 A JP 2018239543A JP 2018239543 A JP2018239543 A JP 2018239543A JP 2020100724 A JP2020100724 A JP 2020100724A
- Authority
- JP
- Japan
- Prior art keywords
- hydrophilic
- hydrophilic polymer
- alcohol
- treatment
- polymer layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記親水性基材において、前記アルコール処理は、アルコールと、水及び/又は前記アルコール以外の有機溶媒とを含む混合溶媒処理であることが好ましい。
前記親水性基材作製方法において、前記アルコール処理は、アルコールと、水及び/又は前記アルコール以外の有機溶媒とを含む混合溶媒処理であることが好ましい。
本明細書において、水の接触角は、後述の実施例に記載の方法で測定可能である。
なお、本明細書において、表面粗さRaは、JIS B0601−2001で規定される中心線表面粗さRaである。
(1)、(2)の保持、乾燥時間は、基材の大きさ、導入する液種、等により適宜設定すれば良い。保持時間は、10秒〜10時間が好ましく、1分〜5時間がより好ましく、5分〜2時間が更に好ましい。乾燥は、室温(約23℃)から80℃で行うことが好ましく、室温から40℃で行うことがより好ましい。また、減圧して乾燥しても良い。更に、保持して一定時間後、適宜、余分な親水性ポリマー溶液・分散液を排出し、乾燥してもよい。
AIBN(アゾビスイソブチロニトリル)12.5mg/mlトルエン溶液を用いて、2−メトキシエチルアクリレート(25wt%トルエン)を60℃で7時間熱重合し、ポリ2−メトキシエチルアクリレート(PMEA)を作製した。
未処理のスライドチャンバーに作製したPMEAの0.25%メタノール溶液を注入した。その後、直ぐに40℃のオーブン中で5分間真空乾燥させた。
その後、メタノールを注入して(処理温度:室温)、自然乾燥し、アルコール処理基材を作製した。
未処理のスライドチャンバーに作製したPMEAの0.35%メタノール溶液を注入した。その後、直ぐに40℃のオーブン中で5分間真空乾燥させた。
その後、メタノールを注入して(処理温度:室温)、自然乾燥し、アルコール処理基材を作製した。
1N NaOH水溶液をスライドチャンバー(底面:ソーダ石灰ガラス製)に加え、1時間放置した。その後、チャンバー表面を水で洗浄して自然乾燥した。
作製したPMEAの0.25%メタノール溶液を前記親水化処理をしたスライドチャンバーに注入した。その後、直ぐに40℃のオーブン中で5分間真空乾燥させた。
その後、メタノールを注入して(処理温度:室温)、自然乾燥し、アルコール処理基材を作製した。
1N NaOH水溶液をスライドチャンバー(底面:ソーダ石灰ガラス製)に加え、1時間放置した。その後、チャンバー表面を水で洗浄して自然乾燥した。
作製したPMEAの0.35%メタノール溶液を前記親水化処理をしたスライドチャンバーに注入した。その後、直ぐに40℃のオーブン中で5分間真空乾燥させた。
その後、メタノールを注入して(処理温度:室温)、自然乾燥し、アルコール処理基材を作製した。
1N NaOH水溶液をスライドチャンバー(底面:ソーダ石灰ガラス製)に加え、1時間放置した。その後、チャンバー表面を水で洗浄して自然乾燥した。
作製したPMEAの0.35%メタノール溶液を前記親水化処理をしたスライドチャンバーに注入した。その後、直ぐに40℃のオーブン中で5分間真空乾燥させた。
その後、エタノールを注入して(処理温度:室温)、自然乾燥し、アルコール処理基材を作製した。
未処理のスライドチャンバーに作製したPMEAの0.25%メタノール溶液を注入した。その後、直ぐに40℃のオーブン中で5分間真空乾燥させた。
作製されたアルコール処理基材の表面(親水性基材におけるアルコール処理済親水性ポリマー層の表面)に蒸留水2μlを滴下し、30秒後の接触角をθ/2法(室温)で測定した。
親水性基材の親水性ポリマー層(アルコール処理済親水性ポリマー層)の膜厚は、親水性ポリマー層の断面を、TEMを使用し、加速電圧15kV、1000倍で測定(撮影)した。
レーザー顕微鏡を用いて、非接触で表面粗さを1つの親水性基材(アルコール処理済親水性ポリマー層)で4箇所(第1ピーク)測定し、そのRaの4点の平均を表面粗さRaとした(JIS B 0601−2001で規定される中心線表面粗さRaの平均)。
Claims (12)
- 基材表面上の親水性ポリマー層にアルコール処理が施された親水性基材。
- 前記アルコール処理は、メタノール処理及び/又はエタノール処理である請求項1記載の親水性基材。
- 前記アルコール処理は、アルコールと、水及び/又は前記アルコール以外の有機溶媒とを含む混合溶媒処理である請求項1記載の親水性基材。
- 前記親水性ポリマー層は、親水性ポリマー溶液を用いて形成されたものである請求項1〜3のいずれかに記載の親水性基材。
- 前記親水性ポリマー層の厚みが10〜1000nmである請求項1〜5のいずれかに記載の親水性基材。
- 基材表面に親水性ポリマー層を形成した後、アルコール処理を施す親水性基材作製方法。
- 前記アルコール処理は、メタノール処理及び/又はエタノール処理である請求項7記載の親水性基材作製方法。
- 前記アルコール処理は、アルコールと、水及び/又は前記アルコール以外の有機溶媒とを含む混合溶媒処理である請求項7記載の親水性基材作製方法。
- 前記親水性ポリマー層は、親水性ポリマー溶液を用いて形成されたものである請求項7〜9のいずれかに記載の親水性基材作製方法。
- 前記親水性ポリマー層の厚みが10〜1000nmである請求項7〜11のいずれかに記載の親水性基材作製方法。